Open access

Irradiation Effects in Optical Fibers

Written By

Sporea Dan, Agnello Simonpietro and Gelardi Franco Mario

Published: 01 February 2010

DOI: 10.5772/39550

From the Edited Volume

Frontiers in Guided Wave Optics and Optoelectronics

Edited by Bishnu Pal

Chapter metrics overview

5,562 Chapter Downloads

View Full Metrics

1. Introduction

Intrinsic and extrinsic optical fiber-based sensors are promising devices to be used in very different and complex environments, by their very nature: capabilities to work under electromagnetic fields; possibility to carry multiplexed signals (time, wavelength multiplexing); small size and low mass; ability to handle multi-parameter measurements in distributed configuration; possibility to monitor sites far away from the controller. In the case of the optical fibers, the possibility to be incorporated into various types of sensors and actuators, free of additional hazards (i.e. fire, explosion), made them promising candidates to operate in adverse conditions as those required by space applications and terrestrial nuclear facilities (Alam et. al., 2006a, Alam et al., 2006b, Berghmans et al., 2008, Ott, 2002). In nuclear environments optical fibers found an application niche in optical communication links, embedded into various all-fiber or hybrid sensors or as light-guides for control and diagnostics (Alfeeli et al., 2007, Ahrens et al., 2001, Fernando et al., 2005, Fielder et al., 2005, Florous et al., 2007, Gan et al. 2008, Henschel et al., 2001, Kimurai et al. 2002, O'Keeffe et al. 2008, Reichle et al., 2007, Troska et al., 2003). For applications related to fusion installations the requirements are quite demanding because of the exposure to (Campbell, 2005, Griscom, 1998, Hodgson, 2006, ITER Physics Expert Group on Diagnostics, 1999, Shikama, 2003, Zabezhailov, 2005): ionising radiation, high temperature, and high electromagnetic disturbances.

One of the major drawbacks for optical fibers use under ionizing radiation is related to the development of colour centres, which affect dramatically the optical transmission in UV-visible-NIR spectral ranges (Griscom, 1998, Karlitschek, 1995). For this reason, optical fibers are by more than 30 years in the focus of colour centres research (Friebele, 1976, Kaiser, 1974).

Research on radiation induced colour centres in pure and doped bulk silica materials has a long history of over 50 years (Weeks, 1956), but it is still actual (Radiation effects, 2007, Devine et al., 2000, Pacchioni et al., 2000), as new materials and devices (optical fibers, waveguides, multiplexers, or fiber lasers) are continuously devised and evaluated. Apart from the diversity of the investigated materials and devices new challenges are presented by the various irradiation conditions to which such materials and devices are subjected.

The complexity of the colour centres dynamics lead to the use of complementary methods to individuate these centres (electron paramagnetic resonance: EPR, luminescence) besides the traditional optical absorption spectroscopy. New insights are also provided by in-situ experiments, when optical absorption changes are monitored during the irradiation, aiming to evaluate the irradiation effects disentangled from post irradiation relaxation and with the target to go deeper into the mechanisms of defects generation.

This chapter reports original results concerning the investigations carried out on optical fibers irradiated by gamma-ray, beta-ray, and neutron, using comparative measurements of optical absorption, EPR and luminescence. The optical measurements were performed mostly in the UV spectral range as the most effective colour centres are generated there. The EPR measurements were used to detect the presence of the intrinsic point defects E’ centers (Devine et al., 2000, Pacchioni et al., 2000), as well as H related paramagnetic point defects typically observed in H loaded fibers (Li et al, 1996, Karlitschek et al., 1998). Finally, the photoluminescence measurements were applied to reveal the presence of oxygen deficient defects (ODC(II)) induced by irradiation (Skuja, 1998, Skuja et al.; 2005).


2. The physics of colour centres

Up to now, most of the investigations on the use of optical fibers in radiation environments were done in relation to their use for sensing and data transfer. One approach of interest is related to the use of optical fibers for periscopes (light transmitting pipe-lights) for plasma diagnostics in fusion installations. Within such a task, the spectral behaviour of optical fibers in the UV-visible spectral range is of interest (Brichard, 2005).

Many years of study on bulk silica and on preforms or silica fibers have enabled to evidence optical absorption effects from IR up to vacuum-UV induced by the devices manufacturing or by their subsequent use during high intensity light propagation or in irradiation environments (Devine et al., 2000, Pacchioni et al., 2000, Skuja, 1998). The relevant role of the absorption in affecting the optical efficiency of the devices has lead to isolate the contributions of various absorption bands. Many efforts have been done also to assign these bands to given point defects and to determine specific procedures that could enable to prevent the same defect formation and/or could let their conversion into optically inactive species. A short review of the main intrinsic absorption bands occurring in the UV spectral range will be given in the following.

The ubiquitous and most easily induced absorption features in the UV range is the band at about 213 nm (5.8 eV), attributed to the E’ centers (Pacchioni et al., 2000, Skuja, 1998). This band is characterized by an oscillator strength, f, of about 0.2, and can be well described by a Gaussian profile with full width at half maximum (FWHM) of about (0.70.1) eV. The point defect responsible for this absorption is characterized by a microscopic structure consisting in an unpaired electron in an approximately sp3 hybrid orbital of a dangling bond of a threefold coordinated silicon atom: OSi, where the symbol represents single bonds to three oxygen atoms and the symbol stays for the unpaired electron (Pacchioni et al., 2000).

The electronic excitation process associated to this absorption band has been strongly debated and, recently, support to its attribution to an electronic transition from the defect related bonding states to the unpaired electron level has been given (Agnello et al., 2008).

It is noteworthy to observe that this defect is also paramagnetic and is characterized by an EPR signal (Weeks 1956) well correlated to the optical absorption (Weeks et al., 1963) with principal g-values (Weil et al., 1994, Pacchioni et al., 2000): g1=2.0003, g2=2.0006, g3=2.0018.

Another relevant absorption band, diffusely observed in the UV range in various forms of irradiated silica, is the one peaked at about 258 nm (4.8 eV) (Pacchioni et al., 2000, Skuja, 1998). This band can be described by a gaussian profile with FWHM of 1.05 eV and oscillator strength f=0.03 (Cannas et al., 2006). Excitation within this absorption originates a well known red luminescence band at about 650 nm (1.9 eV) that has an additional excitation channel at 620 nm (2.0 eV). This overall optical activity has been attributed to the Nonbridging Oxygen Hole Centers (NBOHC) (Pacchioni et al., 2000). The microscopic model associated to this defect consists in a non-bridging oxygen atom: OSi-O, having an unpaired electron in a non-bonding oxygen orbital (Pacchioni et al., 2000). The electronic transitions responsible for the absorption and emission of this defect are still debated but, usually, they are related to electron promotion from bonding states of the OSi-O moiety to the non bonding states of the dangling O and, in particular, to that of the unpaired electron (Bakos et al., 2004). Due to the presence of an unpaired electron in the oxygen orbital, this defect is responsible also for an EPR signal (Pacchioni et al., 2000, Skuja, 1998). By studying the dependence of this signal as a function of temperature the following main g values have been determined: g1=1.9999, g2=2.0095, g3=2.078 (Pacchioni et al., 2000). However, the identification of NBOHC by the EPR technique is complex due to the overlap with other signals and to the resonance line being spread over a wide magnetic field (about 80 G at 9.8 GHz microwave frequency, X-band) that prevents its detection at low defect concentrations (typically below 1016 centers/cm3).

Other defects responsible for the absorption increase around 258 nm (4.8 eV) are interstitial ozone molecule (O3) and the peroxy radical: OSi-O-O (Skuja et al.; 2005). Both these defects should be observed as product of irradiation in oxygen rich materials or as a consequence of oxygen displacements processes induced by irradiation. Their detection is however difficult due to the overlap with the NBOHC band and, in particular, the attribution of an absorption band to the peroxy radical in this spectral range is still a matter of debate (Skuja et al.; 2005).

A defect of particular relevance for the UV optical absorption in SiO2 is also the oxygen deficient center: ODC(II) (Pacchioni et al., 2000, Skuja et al.; 2005, Skuja 1998). This defect is usually associated to an absorption band peaked at 248 nm (5.0 eV) and gives rise to two emission bands at 460 nm (2.7 eV) and 280 nm (4.4 eV) (Skuja, 1998). The ODC(II) can be induced during fiber fabrication but it is also relevant in relation to the photosensitivity of silica and in connection to fiber photon writing processes (Pacchioni et al. 2000, Karlitschek et al., 1998). In this respect, the connection of the ODC(II) with another defect usually named H(I) center is of particular importance due to the use of hydrogen for radiation hardening of fibers. This latter defect is paramagnetic and is characterized by a doublet of EPR lines split by 74 G (Skuja, 1998). The structural model for the H(I), confirmed by many experimental investigations, consists in a silicon atom bonded with two oxygen and one hydrogen and having an unpaired electron on silicon: O=Si-H (Pacchioni et al., 2000, Skuja, 1998).

The existence of a conversion between ODC(II) and H(I) has been evidenced by studies on surface defects on silica and has been used to support the model of the ODC(II) as consisting in a two-fold coordinated silicon: O=Si (Radzig, 1998, Skuja, 1998).

Despite the almost clear identification of many absorption features in the UV spectral range, the processes of defect formation and defect stability are still matter of investigation, both experimentally and theoretically (Griscom, 2001, Mashkov et al. 1996, Kajihara et al., 2008). In particular, it has been shown that the defect formation processes feature a complex dynamics related to the presence of precursor of the defects and also affected by the inhomogeneity intrinsic to the amorphous nature of the material. Furthermore, the stability of irradiation induced defects is affected by the presence of species present in the material and, in particular, it has been evidenced that H related species (H, H2, H2O) usually affects the formation and thermal removal of many defects as NBOHC, E’ and ODC(II) (Griscom et al., 1998, Devine et al., 2000, Pacchioni et al. 2000, Nuccio et al. 2009, Messina et al. 2009).


3. Experiment

The goals of the here reported investigations were: to further improve the optical absorption measurements in the UV-visible spectral range in fibers; to evaluate the possibility to use alternative methods for identifying colour centres in fibers (i.e. EPR, luminescence); to check through an inter-laboratory comparison the capabilities of two laboratories located in Italy and Romania in performing EPR tests on irradiated optical fibers.

The investigated optical fibers were commercially available products. The characteristics of some of the investigated optical fibers are summarised in Table I.

Characteristics Core diameter (μm) Cladding diameter (μm) Maximum operating temperature ( °C) Jacket type
Optical fiber sample nickname
S42-1 1000 1035 (TECS) - Tefzel
S43-1 400 440 (doped silica) 150 Tefzel
S44-1 600 660 (doped silica) 300 Polyimide
S45-1 600 660 (doped silica) 300 Polyimide
S46-1 600 660 (doped silica) 300 Polyimide
S47-1 400 500 - Tefzel

Table 1.

The irradiated optical fibers.

The optical fibers are either solarization resistant optical fibers, optical fibers with enhanced UV transmission or radiation hardened optical fibers developed for UV applications.

The length of the samples for the optical absorption measurements was 120 mm. For the case of EPR and luminescence tests five pieces from the same optical fibers samples, without jacket and having a length of 10 mm each, were measured in the same time.

3.1. Set-ups

The general set-up for the off-line optical absorbance measurements is similar to that previously used (Sporea, 2005, Sporea, 2007), but, for the purpose of this investigation, it has a better S/N ratio (1,000:1 full signal), 16 bits A/D conversion resolution, a dynamic range of 25,000:1, a greater quantum efficiency in the UV range (65 % at 250 nm), spectral resolution 1.2 nm, a sensitivity of 0.065 counts/e-, and a minimum OD detection level of 0.4 for the optical set-up used (this value is determined by two factors: first, the core of the connecting optical fibers and the core of the samples are different, and second, the sample optical fibers have no fixed connectors, hence, a biasing level which limits the set-up lowest detectable OD). Such a detecting scheme makes possible a better tracking of the colour centre development in the UV spectral range and enables a higher range of absorption levels to be detected (O.D. of 4.4). For the reported optical absorption curves the signal was averaged over three detected acquisitions with a value of 2 for the box car parameter. Irradiation and off-line measurements were carried out at room temperature.

Depending on the case, various set-ups were used for on-line measurements. During the gamma, beta and neutron irradiations tests were carried out both at room temperature and with the optical fiber heating. For these purposes specially designed set-ups were built (Figure 1), to make possible the simultaneous irradiation at room temperature (upper plate) and with the heating of the optical fibers (lower plate). In the case of neutron and beta irradiation a small oven was constructed which made possible the irradiation of the optical fibers in a linear geometry. For on-line measurements during gamma irradiation a circular geometry was used, the optical fiber samples (items 4 and 7 in Fig. 1 b) were coiled with a diameter of about 130 mm, and the gamma source was placed at the coil centre (item 6 in Fig. 1 b).

Figure 1.

The set-up for on-line measurements of gamma-irradiated optical fibers at room temperature and under heating conditions: a – the sketch of the irradiation hot-cell (1 – hot -cell window; 2 – remote manipulators; 3 – set-up for the optical fibers positioning; 4 – shielding; 5 – connecting optical fibers; 6 – hot-cell room; 7- hot cell access door; 8 – optical fiber mini spectrometer; 9 – broad band stabilized light source; 10 – laptop); b – detail of the set-up for the optical fiber positioning and heating.

The design of the special set-up made possible the irradiation at room temperature of one sample while a second sample was heated up to 240 C. The possibility to have the sample heated during the irradiation enables the study of the colour centres dynamics under temperature stress.


3.2 Irradiations and measurements

The 60Co gamma-ray off-line irradiations have been performed at room temperature by using the SVST-Co-60/B, tote-box type, multipurpose irradiation facility of the National Institute for Physics and Nuclear Engineering – Horia Hulubei (IFIN-HH). The SVST-Co-60/B irradiator has today an activity of 267000 Ci, and the irradiations were performed in the irradiation chamber, at a dose rate ~ 700 Gy/h.

For the absorbed dose measurements two dosimetric systems are used: ALANINE / EPR dosimetry system, calibrated for 20 Gy – 10 kGy range, and ECB dosimetric system, calibrated for 1 kGy – 100 kGy ranges. The measured absorbed doses for both the systems are traceable to RISO High Dose Reference Laboratory – Denmark, and their performances were tested by international dosimetric intercomparisons. The uncertainty of absorbed dose measurement is around 3%.

The on-line irradiations were performed in a hot-cell at the 60Co gamma-ray irradiation facility of the “Horia Hulubei” National Institute of R&D for Physics and Nuclear Engineering–IFIN-HH. The dose rate can be modified by changing the distance of the optical fiber sample from the gamma source (i.e. a dose rate of 5.3 kGy/ h at 6 cm distance form the source).

The beta irradiation conditions were the following: the mean electron energy: 6 MeV, the electron beam current: 1 μA, the pulse repetition rate: 100 Hz, the pulse duration: 3.5 μs, the beam diameter: 10 cm, the spot uniformity: +/- 5 %. In order to have Bremsstrahlung, the electron beam collided on a tungsten target, and gamma-rays were generated. To separate the electron flux from the gamma-rays two Al foils, one having a thickness of 3 mm, and one of 4 mm were placed at the distances of 10 mm and respectively at 120 mm away from the target.

The neutron irradiation was performed at the Cyclotron accelerator facility of the National Institute of R&D for Physics and Nuclear Engineering “Horia Hulubei”, Magurele, based on the reaction 9Be + d n + X, using a deuteron beam (13 MeV) and a thick beryllium target of 165 To obtain the desired neutrons fluencies the samples are located downstream at the distances from 10 to 40 cm from the Be target. The neutrons flux above 1 MeV is estimated with a relative error of about 20 %. The maximum neutron flux achievable in our setup, at a distance of 10 cm from the target, is 2.109μA-1, corresponding to a deuteron beam intensity of 10 μA. In practice, a neutron fluence of 1013 can be obtained in about 1-6 days of irradiation, depending on the position of the samples in respect to the Be target. It is estimated that the neutron flux was uniform over 10 mm length of the optical fiber sample, with a spatial uniformity of 3%.

The EPR measurements were performed in Romania at the IRASM irradiation facility (National Institute for Physics and Nuclear Engineering – “Horia Hulubei”) using an X band Magnettech MiniScope MS 200 spectrometer provided with a rectangular TE102 resonant cavity and 100 kHz modulation frequency.

Both non-irradiated and irradiated samples have been introduced into fused quartz tubes (1 cm sample length, 5 mm outer tube diameter) and fixed into the resonant cavity always in the same position. The mass of measured samples varied between 20 and 130 mg. The EPR spectra have been registered under the experimental conditions, detailed in the following figures, and with the magnetic field sweep rate of 18 G/min. The g-factors of the observed EPR signals have been determined by using a ZnS: Mn2+ standard. Similar measurements were done at the University of Palermo on a Bruker EMX-micro working in X-band (about 9.8 GHz) with a rectangular TE102 resonant cavity and at 100 kHz magnetic field modulation using an EPR tube, 10 mm outer diameter, for sample mount. For specific colour centres detection, a preliminary calibration of the two instruments (the Magnettech MiniScope MS 200 spectrometer in Romania and the Bruker EMX-micro in Italy) was run using a gamma ray irradiated sample of high purity silica to compare the sensitivity of the two instruments. Based on this calibration, additional parallel measurements were performed in the two laboratories and with the equipment of Palermo a concentration estimate has been carried out.

The luminescence effects were investigated at this stage only in Palermo with a Jasco FP6500 spectrofluorometer using a 150 W Xenon lamp. Excitation light impinged on the fiber samples perpendicularly to their axis using an artwork mount at 45 back-scattering configuration, and emission light was collected at 90 with respect to the excitation direction.


4. Results

Figures 2-4 illustrate the optical absorbance of the irradiated optical fibers as they were subjected to various total gamma irradiation doses. These spectra evidence that irradiations mainly induce the formation of bands below 300 nm that could be associated to E’-Si centres and Non-Bridging oxygen hole centres (Skuja, 1998), whose amplitude increase on increasing the irradiation dose. At higher wavelength negligible absorption is found. It can be observed that the fibers S44, S45 and S46 are more radiation resistant than the others.

Figure 2.

Optical absorption spectra in optical density units (OD) for: a - sample S42-1; b - sample S43-1.

Optical fibers S44-1, S45-1 and S46-1 are hydrogen loaded type optical fibers, so they exhibit a higher radiation hardening than the other samples. Optical fibers S42-1 and S43-1 are optical fibers with an enhanced UV response and have a high OH content. The optical fiber S47-1 was designed for UV laser beam delivery applications with high fluorine content.

Figure 3.

Optical absorption spectra in optical density units (OD) for: a - sample S44-1; b - sample S45-1.

Figure 4.

Optical absorption spectra in optical density units (OD) for: a -sample S46-1; b - sample S47-1.

Decomposition of the spectra as a function of energy obtained from the data of fibers S43, S44 and S45 (Figs. 2, 3) has been carried out using Gaussian bands. This decomposition enabled to further explore the presence of specific point defects in the irradiated fibers.

In Fig. 5 an example of the decomposition result is reported for the fiber S45 at the various irradiation doses. The found bands are characterized by peak position (4.8 0.1) eV and FWHM (1.0 0.1) eV, and by (5.7 0.1) eV and FWHM (0.8 0.1) eV, in reasonable agreement with the bands attributed to the NBOHC and to the E’ center (Pacchioni et al., 2000, Skuja, 1998), respectively.

It is found also that more than 70% of the absorption spectra is attributed to the absorption bands of the E’ center and of the NBOHC. A further band peaked at 198 nm (6.25 eV), whose origin is unknown, is necessary to describe the absorption below 210 nm (at energy larger than 5.9 eV). Usually this band contributes less than 25% to the overall decomposition. It was also found that these Gaussian amplitudes increase for all investigated dose evidencing that the induced absorption is related to the processes of these defects generation.

Similar results are found for the other investigated fibers. As can be observed the spectra of the S43 sample (Fig. 2) feature a low contribution at about 258 nm (4.8 eV) with respect to the component at 213 nm (5.8 eV), at variance to the samples S44, S45 and S46 (Fig. 3, 4). These aspects are confirmed by the spectra decomposition. Since the ratio between the composing bands, and in particular those related to the E’ center and to the NBOHC, is not constant and depends on the fiber, it can be guessed that the microscopic process of defects generation depends on the specific preparation method and could be affected by hydrogen loading (Devine et al., 2000, Karlitschek et al., 1998 ).

In Fig. 6 the change of the optical attenuation for an optical fiber with enhanced UV transmission, 400 μm core diameter, and Tefzel jacketing (sample similar to S43-1) under neutron irradiation at a total fluence of 1.18 x 1013 n/cm2 is given as an example.

It is observed that also in this case the absorption increases non-linearly with the fluence for wavelengths below 400 nm. Due to the instrumental reduced sensitivity below 235 nm no specific feature can be associated to point defects in this case.

A solarization resistant 600 μm core diameter, Polyimide jacketed optical fiber (sample similar to S46-1) was subjected to beta irradiation and separately to Bremsstrahlung (Fig. 7a), at room temperature. During an additional experiment the same type of optical fiber

Figure 5.

Spectral decomposition using Gaussian bands of the spectra of sample S45-1 irradiated at various doses; the circles represent experimental points, the dashed lines the component Gaussian bands (peaked at about 4.8 eV, 5.8 eV and 6.25 eV) and the full line the sum of dashed lines.

Figure 6.

The optical absorption spectra in the UV-visible range for an optical fiber with enhanced UV transmission, subjected to neutron irradiation: a - the UV-visible spectrum; b – detail of the attenuation spectrum in the 210 nm - 280 nm spectral range.

was also heated during the irradiation (Fig. 7b). The tested optical fibers were of hydrogen loaded type and exhibit a lower radiation hardening under heating conditions, as the temperature contributes to hydrogen diffusion.

Figure 7.

The change of the optical attenuation of an optical fiber subjected to beta irradiation (total dose of 139.15 kGy_e) and to Bremsstrahlung (total dose of 5.8 kGy_g): a - at room temperature; b – heated at 240 OC during the irradiation.

Investigation of the effects of irradiation on these fibers has been also carried out by EPR measurements. As shown in Fig. 8, these measurements evidenced the presence of resonance signals in some non-irradiated samples. A detailed investigation carried out in Palermo has shown that these signals do not arise from intrinsic defects of silica.

Figure 8.

The EPR signals for the non-irradiated samples corrected for sample mass (Power = 3.2 mW; modulation amplitude = 4 G; scanning time = 655 s; receiver gain = 9 x 102 ). Spectra are arbitrarily vertically shifted.

The EPR measurements carried out on the irradiated fibers are reported in Figs. 9 and 10. It is worth to note that in these figures the spectra recorded for the irradiated samples subtracted by spectra recorded for the respective pristine materials are reported, and show that the defects contents increase by irradiation. Furthermore, the higher radiation resistance of the samples S44, S45, S46 with respect to the other investigated fibers, already evidenced by optical measurements, is confirmed also by the EPR measurements.

Figure 9.

The EPR spectra for 618 Gy irradiated samples corrected for sample mass, after non-irradiated signal subtraction (Power = 3.2 mW; modulation amplitude = 4 G; scanning time = 655 s; receiver gain: 1 x 102 for S 42 and 9 x 102 for the others). Spectra are arbitrarily vertically shifted.

Figure 10.

The EPR spectra for 1800 Gy irradiated samples corrected for sample mass, after non-irradiated signal subtraction. (Power = 3.2 mW; modulation amplitude = 4 G; scanning time = 655 s; receiver gain: 1 x 102 for S 42 and 9 x 102 for the others). Spectra are arbitrarily vertically shifted.

In addition to the optical fiber specified in Table I, several irradiated samples (S7.7; S7.9; S1-440B and S3-440B) were investigated through EPR for comparative studies both in Bucharest and Palermo. The results of EPR measurements performed in Bucharest are given in Figs. 11-13 (spectra are arbitrarily vertically shifted and are not normalized for the samples weight).

These measurements evidence the presence of E’-Si centres (Pacchioni et al., 2000, Karlitschek, 1995) and of the H(I) defects in some of the irradiated samples (Skuja, 1998). The presence of H(I) defects, identified by the doublet of lines split by about 74G, is evidenced by the magnified spectrum.

The same measurements have been done in Palermo showing qualitatively the same results, and supporting the calibration procedure to individuate specific point defects induced by irradiation. Furthermore, the quantitative analysis carried out in Palermo, enabled to estimate the concentrations of E’-Si and H(I) point defects as reported in Table II.

Optical fiber sample nickname Sample mass (g) E’-Si defects (centers/cm 3 ) H(I) defects (centers/cm 3 )
S7.7 0.124 8.2 x 10 16 1.2 x 10 15
S7.9 0.132 5.7 x 10 16 1.0 x 10 15
S1_440B 0.023 3.3 x 10 16 Not detected
S3_440B 0.020 3.1 x 10 16 Not detected
SSU1.1 0.052 Not detected Not detected

Table 2.

The concentration of E’-Si and H(I) point defects.

For some non-irradiated and irradiated samples luminescence measurements were performed (Fig. 14). These measurements have shown that in the non-irradiated samples no PL associated to intrinsic point defects of silica could be detected.

As shown in Fig. 14, in the irradiated fibers S7.9, S1_440B and S3_440B, the luminescence centred at about 4.4 eV excited at 5.0 eV associated to the oxygen deficient ODC(II) defects is detected (Skuja, 1998).

Figure 11.

The EPR signals for some irradiated samples at 113 kGy (samples S7.7 and S7.9) and at 40 kGy (samples S1-440B and S3-440B). Power = 0.1 mW; modulation amplitude = 0.1 G; scanning time = 655s; receiver gain = 1 x 102 for S7.7 and S7.9 and 9 x 102 for S1_440B and S3_440B.

Figure 12.

The EPR signals recorded in Bucharest for the S7.7 sample irradiated at the dose of 113 kGy.

Figure 13.

The EPR signals recorded in Bucharest for the S7.9 sample irradiated at 113 kGy.

Sample S.7.7 was a common, 1000 μm core diameter optical fiber, gamma irradiated up to 113 kGy, in 4 steps, with sample heating at 100 OC for 4 h between each irradiation step. The optical fiber S.7.9 was a solarization resistant optical fiber of 1000 μm core diameter, gamma irradiated to 113 kGy. Samples S1-400B and S3-440B were of the same type (enhanced UV transmission), irradiated by gamma-rays up to a total dose of 40 kGy, the first one was also subjected to temperature stress (140 OC for 4 h, between the irradiation steps). In Fig. 14, the SSU1.1 fiber, not showing emission, is reported for comparison. Photoluminescence excitation spectra confirmed these attributions by evidencing an excitation band centred at 5.0 eV, as reported in literature for ODC(II) (Skuja, 1998). The presence in the sample S7.9 of the ODC(II) emission band agrees with the observation of the H(I) defects that, as reported in the paragraph 2, can be considered a product of the reaction between ODC(II) and H species dissolved in the sample (Skuja, 1998). As regards the samples S3_440B and S1_440B, the absence of H(I) centers signal is also compatible with the much lower amplitude of the emission band of ODC(II), proving a lower content of these latter defects.

Figure 14.

Photoluminescence spectra excited at 5.0 eV of fibers irradiated at 113 kGy (sample S7.9), at 40 kGy (samples S1-440B and S3-440B) and at 500 kGy (sample SSU1.1).


5. Future work

Further investigations on the generation/recovery of colour centres in the UV-visible spectral range are of interest as new radiation hardened optical fibers are developed and more accurate measuring means are available. We shall focus in the near future on the evaluation of the irradiation effects on commercially optical fibers from different vendors in order to assess the role played in such cases by the dopants, core/cladding ratio, temperature stress. On-line measurements have to be extended to have a better understanding of the colour centre dynamics. Tests at higher irradiation dose and dose rates will be run for gamma and beta rays irradiation. To complement the inter-laboratory comparison on EPR measurements a supplementary inter-comparison dedicated to photoluminescence investigations will be organized between laboratories in Romanian and Italy.


6. Conclusions

Eleven types of commercially available optical fibers operating in the UV spectral range were investigated as they were subjected to gamma, beta, and neutron irradiation. The evaluation of the irradiation induced colour centres was done by off-line optical absorption measurements, EPR, and luminescence. E’-Si and H(I) defects were revealed by EPR, the ODC(II) diamagnetic centres were identified by photoluminescence. From the optical absorption measurements it is observed that the induced absorption increases for all the investigated doses suggesting a growth of the concentration of induced colour centres, with a prominent role of the E’ centers and of the NBOHC. A dependence of irradiation effects on the materials is found.



The work was done in the frame of the bilateral collaboration existing between the National Institute for Laser, Plasma and Radiation Physics in Bucharest, and the Department of Physical and Astronomical Sciences of the University of Palermo. The Romanian authors acknowledge the financial support of the Romanian Ministry for Education, Research and Innovation in the frame of the research grant 12084/2008. The Italian authors acknowledge the financial support by the University of Palermo grant CoRI 2006. The authors thank to the following colleagues, for their competent technical assistance and advice: Dr. Adelina Sporea for taking care of the optical absorption measurements and samples preparations, Ms. Rodica Gerogescu for gamma irradiations and some of the EPR measurements, Mr. I. Vata for neutron irradiation, Dr. C. Oproiu for beta irradiations, Mr. A. Alessi and Dr. L. Nuccio for part of EPR and photoluminescence measurements.


  1. 1. Agnello S. Buscarino G. Gelardi F. M. Boscaino R. 2008 Optical absorption band at 5.8 eV associated with the E’ centers in amorphous silicon dioxide: Optical absorption and EPR measurements, Physical Review B, 77 19 May 2008), (195206 1-7), 1098-0121
  2. 2. Ahrens R. G. Jaques J. J. Luvalle M. J. Digivanni D. Windeler R. S. 2001 Radiation effects on optical fibers and amplifiers, Proceedings of Testing, Reliability, and Applications of Optoelectronic Devices, 217 225 , SPIE 4285 978-0-81943-963-5 May 2001, SPIE
  3. 3. Alam M. Abramczyk J. Manyam U. Farroni J. Guertin D. 2006a Performance of optical fibers in space radiation environment, Proceedings of ESA/CNES,ICSO, 6th Intl. Confernce on Space Optics, 9-29092-932-4 June 2006, ESA Publications Division, Noordwijk
  4. 4. Alam M. Abramczyk J. Farroni J. Manyam U. Guertin D. 2006b Passive and active optical fibers for space and terrestrial applications, Proceedings of Photonics for Space Environment XI, 1 14 , SPIE 6308 978-0-81946-387-6 San Diego, August 2006
  5. 5. Alfeeli B. Pickrell G. Garland M. A. Wang A. 2007 Behavior of random hole optical fibers under gamma ray irradiation and its potential use in radiation sensing applications”, Sensors, 7 7 (2007), (676-688) E1424-8220
  6. 6. Bakos T. Rashkeev S. N. Pantelides S. T. 2004 Optically active defects in SiO2: The nonbridging oxygen center and the interstitial OH molecule. Physical Review B, 70 7 August 2004), (075203 1-9), 1098-0121
  7. 7. Berghmans F. Brichard B. Fernandez Fernandez. A. Gusarov A. Van Uffelen M. Girard S. 2008 An introduction to radiation effects on optical components and fiber optic sensors, In: Optical Waveguide Sensing and Imaging, NATO Science for Peace and Security Series B: Physics and Biophysics, Bock, W.J.; Gannot, I. & Tanev, S. (Eds.), (127-165), Springer Netherlands, 978140206950
  8. 8. Brichard B. Fernandez Fernandez. A. 2005 Radiation effects in silica glass optical fibers, Short Course Notebook, New Challenges for Radiation Tolerance Assessment, RADECS 2005, 95 138 , Cap d’Agde, Septembert 2005, RADECS Association
  9. 9. Campbell D. J. Ingesson L. C. Cecconello M. Ciattaglia E. 2005 ITER Diagnostics, Presented at ITER- Opportunities for European industry Workshop, Barcelona, December 2005
  10. 10. Cannas M. Vaccaro L. Boizot B. 2006 Spectroscopic parameters related to non-bridging oxygen hole centers in amorphous-SiO2, Journal of Non-Crystalline Solids, 352 (January 2006), (203-208), 0022-3093
  11. 11. Devine R. A. B. Duraud J. P. Dooryhée E. 2000 Structure and Imperfections in Amorphous and Crystalline Silicon Dioxide, John Wiley & Sons, 978-0-47197-536-6 Chicester
  12. 12. Fernando W. Gan K. K. Jackson P. D. Johnson M. Kagan H. Kass R. Rahimi A. Rush C. Smith S. Ter-Antonian R. 2005 Radiation-Hard Optical Link for the ATLAS Pixel Detector, Presented at IEEE05, Puerto Rico
  13. 13. Fielder R. S. Duncan R. Palmer M. 2005 Recent advancements in harsh environment fiber optic sensors: An enabling technology for emerging nuclear power applications, Luna Innovations, Inc., 2005
  14. 14. Florous N. J. Saitoh K. Murao T. Koshiba M. 2007 Radiation dose enhancement in photonic crystal fiber bragg gratings: towards photo-ionization monitoring of irradiation sources in harsh nuclear power reactors, Proceedings of Conference on Lasers and Electro-Optics, CLEO 2007, 1 2 , 978-1-55752-834-6 Baltimore, May 2007, Institute of Electrical and Electronics Engineers, Inc.
  15. 15. Friebele E. Sigel G. Griscom D. 1976 Drawing-induced defect centers in a fused silica core fiber, Applied Physics Letters. 28 9 (1976), (516-518), ISSN DOI:10.1063/1.88839
  16. 16. Gan K. K. Abi B. Fernando W. Kagan H. P. Kass R. D. Law A. Lebbai M. R. M. Rau A. Rizardinova F. Skubic P. L. Smith D. S. 2008 Radiation-hard optical link for SLHC, J. of Physics: Conference Series, 110 (2008), doi:10.1088/1742-6596/110/9/092011
  17. 17. Griscom D. L. 1998a Radiation hardened fiber optics for fusion reactor diagnostics, Final Technical Report, Naval Research Laboratory, Department of the Navy
  18. 18. Griscom D. L. Mizuguchi M. 1998b Determination of the visible range optical absorption spectrum of peroxy radicals in gamma-irradiated fused silica, Journal of Non-Crystalline Solids, 239 1-3 , (1998), (66-77), 0022-3093
  19. 19. Griscom D. L. 2001 Fractal kinetics of radiation-induced point-defect formation and decay in amorphous insulators: Application to color centers in silica-based optical fibers Physical Review B, 64 17 October 2001), (174201 1-14), 1098-0121
  20. 20. Henschel H. Körfer M. Wulf F. 2001 Fibre optical radiation sensing system for TESLA, Proceedings DIPAC 2001- ESRF, 73 75 , Grenoble, May 2001,
  21. 21. Hodgson E. R. Decreton M. Cecconello M. Ingesson C. Campbell D. J. 2006 Radiation-hard ceramic materials for diagnostic and heating and current drive systems for ITER, Proceedings of the 33rd EPS Conference on Plasma Phys., Rome, June 2006, 119.pdf
  22. 22. ITER Physics Expert Group on Diagnostics 1999 ITER Physics basis, Nucl. Fusion, 39 (1999), (2541-2575)
  23. 23. Kaiser P. 1974 Drawing-induced coloration in vitreous silica fibers, JOSA, 64 4 (1974), (475-481), ISSN doi:10.1364/JOSA.64.000475
  24. 24. Kajihara K. Hirano M. Skuja L. Hosono H. 2008 Intrinsic defect formation in amorphous SiO2 by electronic excitation: Bond dissociation versus Frenkel mechanisms, Physical Review B, 78 9 September 2008), (094201 1-8), 1098-0121
  25. 25. Karlitschek P. Hillrichs G. Klein K. F. 1995 Photodegradation and nonlinear effects in optical fibers induced by pulsed uv-laser radiation, Optics Communications, 116 1-3 , (1995), (219-230), 0030-4018
  26. 26. Karlitschek P. Hillrichs G. Klein K.F. 1998 Influence of hydrogen on the colour center formation in optical fibers induced by pulsed UV-laser radiation: Part 2: All-silica fibers with low-OH undoped core, Optics Communications, 155 (October 1998) (386-397), 0030-4018
  27. 27. Kimurai E. Takada Y. Hosono M. Nakazawa Takahashi. H. Hayami H. 2002 New Techniques to Apply Optical Fiber Image Guide to Nuclear Facilities, J. of Nuclear Sci. and Techn., 39 6 (603-607), 0022-3131
  28. 28. Li J. Lehman R. L. Sigel G. H. Jr 1996 Electron paramagnetic resonance characterization of nonuniform distribution of hydrogen in silica optical fibers, Applied Physics Letters, 69 14 (September 1996), (2131-2133), 0003-6951
  29. 29. Mashkov V. A. Austin Wm. R. . Zhang Lin. Leisure R. G. 1996 Fundamental role of creation and activation in radiation-induced defect production in high-purity amorphous SiO2, Physical Review Letters, 76 16 October 1995), (2926-2929), 0031-9007
  30. 30. Messina F. Agnello S. Cannas M. Parlato A. 2009 Room temperature instability of E′γ centers induced by γ irradiation in Amorphous SiO2, The Journal of Physical Chemistry A, 113 6 (December 2008), (1026-1032), 1520-5215
  31. 31. Nuccio L. Agnello S. Boscaino R. 2009 Role of H2O in the thermal annealing of the E’ center in amorphous silicon dioxide, Physical Review B, 79 N. 12, (March 2009), (125205 1-8) 1098-0121
  32. 32. O’Keeffe S. Fitzpatrick C. Lewis E. Al-Shamma’a A. I. 2008 A review of optical fibre radiation dosimeters, Sensor Review, 28 2 (136- 142), 0260-2288
  33. 33. Ott M. N. 2002 Radiation effects data on commercially available optical fiber: database summary, Proceedings of2002 IEEE Radiation Effects Data Workshop, 24 31 , 0-78037-544-0 July 2002, Institute of Electrical and Electronics Engineers, Inc.
  34. 34. Pacchioni G. Skuja L. Griscom D. L. 2000 Defects in SiO2 and related dielectrics: science and technology, Kluver Academic Publishers, 0-79236-686-7
  35. 35. Radiation effects, 2007 10 th Europhysical Conference on Defects in Insulation Materials, Phys. Status Solidi, 4 3 (2007), (1060-1175)
  36. 36. Radzig V. A. 1998 Point defects in disordered solids: Differences in structure and reactivity of the (OSi-O)2Si: groups on silica surface, Journal of Non-Crystalline Solids, 239 (1998), (49-56), 0022-3093
  37. 37. Reichle R. Brichard B. Escourbiac F. Gardarein J. L. Hernandez D. Le Niliot C. Rigollet F. Serra J. J. Badie J. M. van Ierschot S. Jouve M. Martinez S. Ooms H. Pocheau C. Rauber X. Sans J. L. Scheer E. Berghmans F. Decréton M. 2007 Experimental developments towards an ITER thermography diagnostic, J. of Nuclear Materials, 363-365 , (June 2007), (1466-1471), doi:10.1016/j.jnucmat.2007.01.207
  38. 38. Shikama T. Nishitani T. Kakuta T. Yamamoto S. Kasai S. Narui M. Hodgson E. Reichle R. Brichard B. Krassilinikov A. Snider R. Vayakis G. Costley A. 2003 Irradiation test of diagnostic components for ITER application in a fission reactor, Japan materials testing reactor, Nuclear fusion, 43 7 (2003), (517-521), 0029-5515
  39. 39. Skuja L. 1998 Optically active oxygen-deficiency-related centers in amorphous silicon dioxide, Journal of Non-Crystalline Solids, 239 1-3 , (1998), (16-48), 0022-3093
  40. 40. Skuja L. Hirano M. Hosono H. Kajihara K. 2005 Defects in oxide glasses, Physica Status Solidi (c), 2 1 (2005), (15-24), DOI:10.1002/pssc.200460102
  41. 41. Sporea D. Sporea R. 2005 Setup for the in situ monitoring of the irradiation-induced effects in optical fibers in the ultraviolet-visible optical range, Review of Scientific Instruments, 76 11 (2005), DOI:10.1063/1.2130932
  42. 42. Sporea D. Sporea A. Agnello S. Nuccio L. Gelardi F. M. Brichard B. 2007 Evaluation of the UV optical transmission degradation of gamma-ray irradiated optical fibers, CLEO/ The 7th Pacific Rim Conference on Lasers and Electro-Optics, Seoul, August 2007
  43. 43. Troska J. Cervelli G. Faccio F. Gill K. Grabit R. Jareno R. M. Sandvik A. M. Vasey F. 2003 Optical readout and control systems for the CMS tracker, IEEE Trans. Nuclear Sci., 50 4 Part 1, (2003) (1067 EOF 1072 EOF ), 0018-9499
  44. 44. Weeks R. A. 1956 Paramagnetic resonance of lattice defects in irradiated quartz, J. Appl. Phys., 27 11 (1956), (1376-1381), DOI:10.1063/1.1722267
  45. 45. Weeks R. A. Sonder E. 1963 The relation between the magnetic susceptibility, electron spin resonance, and the optical absorption of the E1’center in fused silica, In: Paramagnetic Resonance II, W. Low (Ed.), 869 879 , Academic Press, LCCN 63-21409, New York
  46. 46. Weil J. A. Bolton J. R. Wertz J. E. 1994 Electron Paramagnetic Resonance, John Wiley & Sons, 0-471-57234-9, New York
  47. 47. Zabezhailov M. O. Tomashuk A. L. Nikolin I. V. Plotnichenko V. G. 2005 Radiation-induced absorption in high-purity silica fiber preforms, Inorganic Materials, 41 3 (2005), (315 321 ), 0020-1685

Written By

Sporea Dan, Agnello Simonpietro and Gelardi Franco Mario

Published: 01 February 2010