Functionally Graded Concrete Structure

By Ning Zhang, Aizhong Lu and Xuguang Chen

Submitted: June 5th 2018Reviewed: September 10th 2018Published: November 5th 2018

DOI: 10.5772/intechopen.81435

Downloaded: 222

Abstract

By inverse analysis, the concept, functionally gradient, is introduced into thick-walled lining to improve the supporting performance. Theoretical results show that for two linings with the same sizes, an ideal functionally graded lining (IFGL) has higher elastic ultimate bearing capacity than a traditional single-layered lining (TSL). But the IFGL model requires that the Young’s modulus should be a continuously monotonically increasing function in the radial direction, which, obviously, cannot be achieved currently for the concrete materials. In order to apply this idea to real lining, we use a simplest multilayered lining, a double-layered functionally graded lining (DFGL), as an approximate simulation of the IFGL. Then, we carried out elastoplastic analysis on IDFL and DFGL and model test on DFGL to assess the support performance. Results of elastoplastic analysis show that the elastic ultimate bearing capacities of both the IDFL and DFGL are higher than the traditional single-layered lining. Model tests also verify the conclusion.

Keywords

  • functionally graded structure
  • concrete
  • rock support
  • lining

1. Introduction

Concrete thick-walled lining is an important supporting structure widely used in many areas like mining, hydraulic power station, tunnel, underground storage project, and so on. Under the action of the outer loading, usually the in situ stresses, stress distributions are nonuniform, especially in the radial direction. For example, as a thick-walled hollow cylinder is subjected to hydraulic pressure, tangential stress concentration will occur along the inner boundary (see Figure 1). Nowadays, some underground engineering disciplines, like mining, are being excavated in depth more than 1000 m and the in situ stresses will be very large, maybe more than 27 MPa [1]. Under such a stress, if the concrete strength is not high enough, failure will probably initiate from the inner lining boundary. In order to improve the bearing capacity and ensure the lining can work safely, two means are usually used: (i) increase the thickness of lining and (ii) improve the material strength. For the first mean, using thicker lining, the stress concentration can be eased, but in a limit range. Moreover, it is not economical. Statistics show that the excavation may cost 40–60% of the total cost of a shaft construction. As deeper than 1000 m, a 10 mm decrease in lining thickness, the total cost will decrease by around 1% (reinforced concrete structure) and 0.25% (concrete structure). For the other mean, using high-strength concrete, the elastic ultimate bearing capacity will increase in a certain extent. But high strength concrete usually needs high strength cement and kinds of admixtures, and high-level construction technology, which will also lead to higher cost. Besides, as we all know, concrete materials with higher strength have more significant brittleness and very low residual strength. Thus, sudden failure will be more likely to occur in lining. Both theoretical and practical results illustrate that total cost will increase significantly and usually the failure cannot be avoided either by increasing thickness or by improving higher strength.

Figure 1.

Traditional single-layered lining under hydrostatic in situ stress.

The usually used two means are neither economic nor practical. Herein, in order to conquer these problems and increase the ultimate bearing capacity of lining, an alternative way we proposed in this work is to introduce the idea, functionally graded materials (FGMs). The concept of FGM was firstly proposed in 1984 by Japanese materials scientists as a mean of preparing thermal barrier materials. Continuous changes in the composition, microstructure, porosity, etc. of material result in gradients in such properties as mechanical strength and thermal conductivity [2]. Compositional micro/macrostructure gradient can not only dismiss undesirable effects such as stress concentration [3] but also generate unique positive function [4]. Then, its applications have been expanded to also the components of chemical plants, solar energy generators, heat exchangers, nuclear reactors, and high efficiency combustion systems [5]. Some people also carried out some works on the functionally graded performances of construction materials [6, 7]. Shen et al. [8] developed a functionally graded material system with a spatially tailored fiber distribution to produce a four-layered, functionally graded fiber-reinforced cement composite. Dias et al. [9] discussed the use of statistical mixture designs to choose formulations and presented ideas for the production of functionally graded fiber cement components. In this work, in order to improve the stress distributions, inverse analysis is carried out firstly. We let the Young’s modulus be a function of radius r, that is, E(r), not just a constant E as usual, and the Poisson’s ratio μ be a constant. Then, we induce the expressions E(r) based on the preassumed stress distributions. In this way, we can get an ideal model, the functionally graded lining. But this ideal model is not practical for concrete material used in lining. Thus, we choose the multilayered lining as an alternative. We analyze the simplest one, a double-layered lining with hydrostatic pressure acting on the outer boundary, to assess the support performance of functionally graded lining. Finally, model tests are carried out to check the theoretical results.

2. Inverse analysis of functionally graded lining

There have been many analytical results on FG thick-walled hollow cylinder subjected to temperature loads or stresses. In these works, material parameters are preassumed to be a certain function about radius. Usually, the Poisson’s ratio is set as a constant but the Young’s modulus or shear modulus is defined as different types of functions about radius like linear variation [10, 11], power law variation [12, 13, 14, 15, 16, 17, 18, 19, 20, 21], exponential variation [18, 22, 23], and other forms [24, 25]. All these abovementioned works mainly calculated the stress and displacement distributions in a FG thick-walled hollow cylinder with given Young’s modulus E(r) or shear modulus G(r). Obviously, the stresses and displacement distributions are dependent on the given E(r) or G(r). This is a forward problem. Instead, in order to obtain a stress distribution that we want it to be, we preassume the stress distribution and let the Young’s modulus E(r) be undetermined. The undetermined E(r) can be back-induced according to the preassumed stress distribution and loadings. This process is usually called inverse analysis [26]. The problem we discussed in this section is such a process. The FG lining is subjected to a hydrostatic pressure p.

2.1. Basic assumptions

If we want to give full play to the support material, the ideal state is that the whole lining enters into plastic yielding at the same time. We confine attention to the plane strain problem. Compressive stress is defined as positive in this chapter. Because of the axial symmetry of the problem, the tangential and radial stresses, σθ and σr, in the rock mass will, respectively, be the maximum and minimum principal stresses, that is, σ1 = σθ and σ3 = σr. And we assume the failure of the lining concrete is ruled by the Tresca criterion, σ1 − σ3 = c, where c is a constant reflecting the material strength. In this situation, the ideal stress state can be preassumed as σθ − σr = c. It should be noted that the values of Young’s modulus E(r) in different radius r may be different from each other, but for one point, it has the same value in any directions. It means that materials of the FG linings discussed here are isotropic. Besides, there is an implicit requirement behind “the whole lining enters into plastic yielding simultaneously”: the FG lining should have a constant strength, although the Young’s modulus may be different in the radial direction.

2.2. Basic equations and solution

The Young’s modulus E(r) only depends on the radius r. So, the problem shown in Figure 1 is a plane strain axisymmetric problem. For small strain problem, the strain-displacement relations, constitutive equations, and equilibrium equations can be given, respectively, as

εr=dudrE1
εθ=urE2
εr=1μ2Erσrμ1μσθE3
εθ=1μ2Erσθμ1μσrE4
dσrdr+σrσθr=0E5

where εθ and εr are the tangential and radial strains, respectively; u is the radial displacement; and μ is the Poisson’s ratio.

Substituting σθ − σr = c into Eq. (5) and solving the partial differential equation gives the expression of the radial stress,

σr=A+clnrE6

where A and c are constants to be determined, the values of which can be determined by the stress boundary conditions on the inner boundary r = Rin, σr = 0, and outer boundary r = Rout, σr = p. We have A=plnRin/lnRout/Rinand c=p/lnRout/Rin. And then substituting Aand cinto Eq. (6) and σθ=σr+c, we get

σr=plnr/RinlnRout/RinE7
σθ=p1+lnr/RinlnRout/RinE8

Combining Eqs. (1)(5), (7), and (8), the following ordinary differential equation can be obtained,

dErdrr+12μ1μrlnr/Rin=2ErE9

where Er=1/Er. We can get the solution of Eq. (9) as

Er=B12μ1μlnr/Rin+121μ12μE10

where B is constant of integration. To differentiate, we name the linings with Young’s modulus satisfying Eq. (10) as ideal FG lining. Figure 2 shows the dimensionless Young’s modulus as μ = 0.0, 0.25, and 0.5. Note that Eq. (10) is not available for incompressible materials, μ = 0.5. In this case, E(r) can be solved directly by Eq. (9) as

Er=Br2E11

which agrees with the result by Nie and Batra [15, 27].

Figure 2.

Dimensionless Young’s modulus with respect to radius for different Poisson’s ratios.

It can be seen from Figure 2 and Eqs. (10) and (11) that in order to achieve the preassumed stress distribution σθ − σr = c, the Young’s modulus E(r) needs to be monotonously increasing with radius r and increases faster as the Poisson’s ratio is larger.

2.3. Ultimate bearing capacity of ideal FG lining

For the ideal FG lining, the stresses in any point can satisfy the equation σθ − σr = c as we preassumed, when σθ − σr = c = σcFG (σcFG is the UCS of the ideal FG lining material), the whole FG lining will enter into plastic state at the same time. So, for the ideal FG lining, the elastic ultimate bearing capacity pFGeis actually the same with the plastic ultimate bearing capacity pFGp. In this way, the ultimate bearing capacity of the ideal FG lining can be obtained by substituting Eqs. (7) and (8) into σθ − σr = σcFG,

pFGe=pFGp=σcFGlnRout/RinE12

3. Ultimate bearing capacities of double-layered lining

3.1. Model description and basic equations

According to the inverse analysis in Section 2, we know that the ideal FG lining material should mainly satisfy two requirements: (i) constant strength and (ii) continuously increasing Young’s modulus in radial direction (see Figure 3(B)). Currently, most of the linings are constructed using concrete-based materials. But in view of the state of the art of concrete, it is scarcely possible to satisfy the second point, that is, continuously changing Young’s modulus. So, in order to apply the FG idea in practical engineering, we use multilayered lining as an alternative (see Figure 3(C)). In this way, it is required that every layer of the multilayered lining should have almost equal strength and that each layer should have larger Young’s modulus than its adjacent inner layer, that is, Ei > Ei−1. We herein, as an example, conduct the elastoplastic analysis of the simplest one, a double-layered lining subjected to hydrostatic in situ stress on the outer boundary (see Figure 4), calculating its elastic and plastic ultimate bearing capacities and comparing them with the corresponding parameters of the traditional single-layered lining and the ideal FG lining.

Figure 3.

(A) Traditional single-layered lining; (B) ideal FG lining; and (C) multilayered lining.

Figure 4.

Double-layered thick-walled hollow lining under hydrostatic in situ stress.

Similar to Section 2, the deformation pattern is restricted by the plane strain condition as well. Material behaviors of both layers are modeled by a finite strain elastoplastic flow theory based on the Tresca yield function. Perfectly elastoplastic behavior is assumed for the support material.

σθiσri=σcii=12E13

The subscript i = 1 and 2 denote the inner and outer layers, respectively (similarly hereinafter). The stresses in both layers satisfy the equilibrium Eq. (5); as we use in this section, we just need to add the subscript i for each layer, the same with the strain-displacement relations, Eqs. (1) and (2).

Ei, μi, and σci (i = 1 and 2) denote Young’s modulus, Poisson’s ratio, and uniaxial compressive strength, respectively (see Figure 4). The inner and outer radii of lining are Rin and Rout, respectively. Although the two layers are not bond with each other, the problem we discuss is axisymmetric, so the outer boundary of the inner layer and the inner boundary of the outer layer should be always together. The radius of the interboundary is R1. The calculated mechanical model is shown in Figure 4.

As we know, for a thick-walled hollow cylinder under outer and/or inner hydrostatic pressures, the most significant stress concentration will occur along the inner boundary, so the plastic yielding will initiate formation of the inner boundary. It is the same for each layer of a multilayered lining. The initiation and extension path of plastic yielding in a multilayered lining depend on the values of the Young’s modulus Ei, the strength σci, and the radius Ri of each layer. For the double-layered lining, according to the initiation and extension mode of plastic yielding, there will exist four different cases of elastic and plastic zones. Both layers stay in elastic state as the loading is small (see Figure 5(A)). As the loading is relatively large, plastic yielding may occur only in the inner layer (see Figure 5(B)) or only in the outer layer (see Figure 5(C)) or in both layers (see Figure 5(D)). rp, and rpi (i = 1 and 2) in Figure 5 denote the radii of plastic zones. As mentioned above, the main aim of the elastoplastic analysis in this section is to calculate the elastic and plastic ultimate bearing capacity. So, we just give the analyzing processes, in detail, of Case A assessing the elastic ultimate bearing capacity and Case D assessing the plastic ultimate bearing capacity.

Figure 5.

Four cases of double-layered lining under hydrostatic in situ stresses: (A) both layers in elastic state; (B) plastic yielding occurs only in inner layer, Rin < rp ≤ R1; (C) plastic yielding occurs only in outer layer, R1 < rp ≤ Rout; and (D) plastic yielding occurs in both layers, Rin < rp1 ≤ R1, R1 < rp2 ≤ Rout.

3.2. Stresses and displacement in elastic zone

For an axisymmetric plane strain problem, the radial and tangential stresses, σri and σθi, and the radial displacement, uri, can, respectively, be given by the following expressions [28],

σrie=AiBir2E14
σθie=Ai+Bir2E15
urie=1+μiEiAir212μi+BirE16

where Ai and Bi (i = 1 and 2) are constants to be determined. The superscript e represents elasticity.

3.3. Stresses and displacement in plastic zone

Substituting Eq. (13) into Eq. (5) gives the stresses in the plastic zone,

σrip=σcilnr+CiE17
σθip=σci1+lnr+CiE18

where Ci (i = 1 and 2) are constants to be determined.

In the plastic zone, total radial and tangential strains, εr and εθ, can be decomposed into elastic and plastic parts as

εri=εrie+εripE19
εθi=εθie+εθipE20

Similarly, the superscript e and p represent elastic and plastic, respectively.

In order to determine the displacement field in the plastic region, a plastic flow rule is needed. By assuming that the elastic strains are relatively small in comparison to the plastic strains and that an associated flow rule is valid, the plastic parts of radial and tangential strains may be related for the plane strain condition

εrip+εθip=0E21

From Eqs. (1), (2), (19)(21) the differential equation for the radial displacement can be expressed as

duidr+uir=firE22

where fir=εrie+εθie.

By using the generalized Hooke law with consideration of the plane strain assumption, εθi = 0, the elastic strains can be given as

εrie=1Eiσriμiσθiμi2σriμi2σθiE23
εθie=1Eiσθiμiσriμi2σθiμi2σriE24

It should be noted that σri and σθi in Eqs. (23) and (24) are stresses in the plastic zone, so, they can be expressed by Eqs. (17) and (18), respectively. So, the function fi(r) is

fir=1+μi12μiEiσci1+2lnr+2Ci=Dilnr+FiE25

where Di=21+μi12μiσciEi, Fi=1+μi12μiσci+2CiEi, Ci (i = 1 and 2) are constants to be determined. Substituting Eq. (25) into Eq. (22) and solving the differential equation, we can obtain the displacement in the plastic zone,

urip=r42DilnrDi+2Fi+GirE26

where Gi (i = 1 and 2) are constants to be determined.

3.4. Elastic ultimate bearing capacity

The elastic ultimate bearing capacity is the load p, as plastic yielding initiates along the inner boundaries of either layer. It can be calculated by elastic analysis of Case A (see Figure 5(A)). The boundary and continuity conditions include at the inner boundary of the inner layer r=Rin, σr1e=0; at the interboundary r=R1, σr1e=σr2e, and u1e=u2e; and at the outer boundary of the outer layer r=Rout, σr2e=p. These conditions can, respectively, give the following equations,

A1B1Rin2=0E27
A1B1R12=A2B2R12E28
1+μ1E1A1R1212μ1+B1R1=1+μ2E2A2R1212μ2+B2R1E29
A2B2Rout2=pE30

We have four variables Ai and Bi (i = 1 and 2) and four equations Eqs. (27)(30). When the plastic yielding initiates from the inner boundary of the inner layer, the stresses at r=Rinshould satisfy the Tresca criterion,

σθ1eσr1er=Rin=σc1E31

Similarly, if the plastic yielding initiates from the inner boundary of the outer layer, we have

σθ2eσr2er=R1=σc2E32

From Eqs. (31) and (32), we can obtain two critical loads p1eand p2e, respectively. The ratio between the two critical loads can be given as

p1ep2e=Δ2E1+Δ3E2σc1Δ1E1σc2E33

where Δ1=21μ22R12, Δ2=μ2+12μ21R1RinR1+Rin, and Δ3=μ1+12R12μ1+Rin2+R12. For simplicity sake, we take μ1 = μ2 = 0.5, considering the material as incompressible. In this situation, the ratio becomes

p1ep2e=Rin2E2σc1R12E1σc2=λ2Rin2R12E34

where λ=E2/σc2/E1/σc1. According to the value of the ratio, we have the following three cases:

  1. i. When p1e/p2e<1or R1/Rin>λ, plastic yielding will initiate from the inner boundary of the inner layer and the elastic ultimate bearing capacity pecan be given as

    pe=p1e=σc12E2Rin2E11R121Rout2+1Rin2R12E35

  • ii. When p1e/p2e=1or R1/Rin=λ, plastic yielding will initiate from both inner boundaries of the inner and outer layers simultaneously and the elastic ultimate bearing capacity pecan be given as

    pe=p1e=p2e=σc12σc2σc11E1E2+1E2E1Rin2Rout2E36

  • iii. When p1e/p2e>1or R1/Rin<λ, plastic yielding will initiate from the inner boundary of the outer layer and the elastic ultimate bearing capacity pecan be given as

    pe=p2e=σc22E1R12E21Rin21R12+1R12Rout2E37

  • 3.5. Plastic ultimate bearing capacity

    As the whole lining turns into plastic yielding state, the corresponding load is the ultimate bearing capacity, which can be calculated by analyzing Case D (see Figure 5(D)). In the same way as the elastic analysis, the elastoplastic analysis can be carried out by using the boundary and continuity conditions, which include at the inner boundary of the inner layer r=Rin, σr1p=0; at the elastic-plastic interface of the inner layer r=rp1, σr1p=σr1e, and u1p=u1e; at the interboundary r=R1, σr1e=σr2p, and u1e=u2p; at the elastic-plastic interface of the outer layer r=rp2, σr2p=σr2e, and u2p=u2e; and at the outer boundary of the outer layer r=Rout, σr2e=p. These conditions can, respectively, give the following equations,

    σc1lnRin+C1=0E38
    σc1lnrp1+C1=A1B1rp12E39
    rp142D1lnrp1D1+2F1+G1rp1=1+μ1E1A1rp1212μ1+B1rp1E40
    A1B1R12=σc2lnR1+C2E41
    1+μ1E1A1R1212μ1+B1R1=R142D2lnR1D2+2F2+G2R1E42
    A2B2rp22=σc2lnrp2+C2E43
    rp242D2lnrp2D2+2F2+G2rp2=1+μ2E2A2rp2212μ2+B2rp2E44
    A2B2Rout2=pE45

    We have 12 variables Ai, Bi, Ci, Di, Fi, and Gi (i = 1 and 2), but just eight equations (Eqs. 3845), while the four variables Di and Fi (i = 1 and 2) can be determined using the material parameters and values of other variables. So, all variables can be calculated and the stresses and displacements in both layers can be obtained. Besides, in order to determine the relationship between the load, p, and the radii of plastic zones, rp1 and rp2, we need two more equations. According to the extension path of plastic yielding, we know that the stresses along the both inner boundaries of two elastic zones should satisfy the Tresca criterion as well, which gives

    2B1rp12=σc1E46
    2B2rp22=σc2E47

    If we take the Poisson’s ratio μ1 = μ2 = 0.5, the relationship between the load and the two radii of the plastic zones can be obtained as

    p=σc121+lnrp12Rin2rp12R12+σc221+lnrp22R12rp22Rout2E48
    rp22rp12=σc1E2σc2E1E49

    By letting rp1=R1and rp2=Routof Eq. (48), we can get the plastic ultimate bearing capacity pp as

    pp=σc1lnR1Rin+σc2lnRoutR1E50

    It can be seen from Eq. (49) that for the given material parameters, the ratio between the two radii of the outer and inner plastic zones keeps equal the coefficient λwe defined in Section 3.4, that is, λ=rp2/rp1. According to the ratio, we have the following three different modes of plastic yielding:

    1. i. When Rout/R1>λ, the inner layer will first finish the plastic yielding and the corresponding critical load at this state is

      p=σc12lnR12Rin2+σc221+lnλ2λ2R12Rout2E51

  • ii. When Rout/R1=λ, the two layers will finish the plastic yielding simultaneously and the corresponding critical load is the plastic ultimate bearing capacity (see Eq. (50)).

  • iii. When Rout/R1<λ, the outer layer will first finish the plastic yielding and the corresponding critical load at this state is

    p=σc121+lnRout2λ2Rin21λ2Rout2R12+σc22lnRout2R12E52

  • 3.6. Elastic and plastic ultimate bearing capacities of traditional single-layered lining (TSL)

    In order to assess the support performance of a FG lining, we will compare the elastic ultimate bearing capacity of the FG lining with that of the traditional single-layered lining with constant Young’s modulus and Poisson’s ratio. The tangential and radial stresses σθ and σr are also the maximum and minimum principle stresses, respectively. They can be given by the classic Lame solution, which can be referred in most classic elastic mechanics books [29]. As we mentioned earlier, the plastic zone for this case will initiate from the inner boundary of the lining r = Rin. So, as the stresses along the inner boundary satisfy the Tresca criterion, that is, σθ  σr = σcc is the uniaxial compressive strength (UCS) of the traditional lining material), the loading acting on the outer boundary is just the elastic ultimate bearing capacity of the traditional lining pTSLe,

    pTSLe=σc1Rin2/Rout2/2E53

    As the outer boundary turns into plastic state, the loading is the plastic ultimate bearing capacity,

    pTSLp=σclnRout/RinE54

    3.7. Analysis and discussions

    In order to investigate the support characteristics of different kind of linings, numerical examples are illustrated in this section. Three different types of linings, that is, traditional single-layered lining (TSL), ideal FG lining (IFGL), and double-layered FG lining (DFGL), are considered. The parameters are listed in Table 1. In order to facilitate comparative analysis, the values of dimensions, Rin, R1, and Rout, the Young’s modulus, E, and the UCS, σc, are taken based on the model test shown in the following section.

    TSLIFGLDFGL
    Radii, R (m)Rin = 0.3, Rout = 0.5Rin = 0.3, Rout = 0.5Rin = 0.3, R1 = 0.4, Rout = 0.5
    Young’s modulus, E (GPa)41Eq. (11), E(Rin) = 20E1 = 25, E2 = 41
    Poisson’s ratio, μ0.50.50.5
    UCS, σc (MPa)5050σc1 = σc2 = 50

    Table 1.

    Parameters of numerical examples.

    3.7.1. Elastic and plastic ultimate bearing capacity

    Figure 6 shows the support characteristic curves (SCCs) of the three different types of linings and the ground response curves (GRCs) of a very good quality quartzite under different in situ stresses given by Hoek and Brown [1], assuming the convergence that has finished as the lining is installed, ui = 0.3 mm. The displacements of the several given coordinate values in Figure 6 are the radial displacement of the outer boundary of lining under support pressure, smaller by 0.3 mm than the tunnel deformation on the excavation boundary. It can be easily seen from Figure 6 that, as the in situ stress p0 = 27 MPa, all three lining structures can work in elastic state. As p0 = 54 MPa, the IFDL and DFGL structures can still work in elastic state, with approximate 8.4 and 2 MPa elastic bearing capacity unused, respectively. But the TSL cannot work in elastic state in such an in situ stress. Under higher in situ stress, p0 = 81 MPa, all three lining structures will turn into plastic state.

    Figure 6.

    Support characteristic curves of three different types of linings and ground response curves under different in situ stresses.

    Figure 7 shows the support pressure versus radii of plastic zones. Presenting the relationships in this way helps to visualize the extension path of plastic yielding. The points labeled by same letter in Figures 6 and 7 indicate the same moment as the support pressure increases. For the TSL, plastic yielding extends radially outward, initiating from its inner boundary (see point A in Figures 6 and 7, p = 16.00 MPa) and finishing at the outer boundary (point B, p = 25.54 MPa). For the IFGL, as we mentioned above, the elastic and the plastic ultimate bearing capacities are the same (point C, p = 25.54 MPa). But for the DFGL, the extension mode of plastic yielding becomes more complex, depending on the Young’s modulus and Poisson’s ratio of the materials of both layers. For the incompressible material, that is, μ = 0.5, the extension path can be determined by Eqs. (35)(37), (50), and (51). Taking the DFGL given in Table 1 as example, the extension of plastic yielding can be divided into four steps: (i) plastic yielding initiates from the inner boundary of the inner layer (point D, p = 19.24 MPa) and extends radially (see Figure 5(B)); (ii) along the inner boundary of the outer layer, plastic yielding begins to occur (point E, p = 20.77 MPa); in this stage, plastic and elastic zones exist alternately in both layers; (iii) the outer layer firstly turns into plastic state totally (point F, p = 25.51 MPa); and (iv) the inner layer turns into plastic state totally (point G, p = 25.54 MPa).

    Figure 7.

    Extension path of plastic yielding.

    As can be seen from the SCCs in Figures 6 and 7, the elastic ultimate bearing capacity of the DFGL is 19.24 MPa, an increase of 20.3% over that of the TSL, 16.00 MPa, and the IFGL can reach to 25.54 MPa, an increase of 59.6%, and, it should also be noted that the increase in the elastic ultimate bearing capacity is proportional to the relative thickness of lining, t/Rin. In the numerical examples, t/Rin = 0.667, which may be higher than most used in real engineering. We will discuss later the effect of t/Rin on the elastic ultimate bearing capacity. Unlike the elastic ultimate bearing capacity, the plastic ultimate bearing capacities of all three linings are the same, 25.54 MPa, which is due to the same UCS.

    One more thing that needs to be noted is that the behavior model for the lining concrete we used is perfectly elastoplastic (see Figure 8(a)), but, as known to all, the concrete material should be strain-softening (see Figure 8(b)), which means that the strength will decrease after the concrete turns into plastic yielding state. For the strain-softening TSL, the strength decrease will affect its bearing capacity significantly, may be much smaller than that of the perfectly elastoplastic TSL, because the plastic yielding initiates from the inner boundary and extends outward. But for the strain-softening DFGL, the postfailure strength of the plastic zone in the outer layer can be improved in some degree (see Figure 8(c)) because of the support action of the elastic zone in the inner layer (see Figures 5(D) and 7). In this way, the support performance of lining can be improved.

    Figure 8.

    Material behavior models.

    3.7.2. Optimized double-layered FG lining

    If we want to make the most of a multilayered lining material, the optimum case should be that plastic yielding initiates and finishes in each layer simultaneously, while, for a uniform thick multilayered FG lining like the DFGL in Table 1, the optimum case cannot happen. In order to achieve the optimum case for a double-layered lining constructed with incompressible material, according to the above elastoplastic analysis, we have

    R1Rin=RoutR1=λE55

    It can be seen from Eq. (55) that for a circular tunnel supported by a double-layered FG lining, if it requires a net space with radius Rin, the thickness δ can be chosen as δ = (λ2 − 1)Rin and the radius of the interboundary R1 should be λRin. Herein, the effect of the convergence on the required net space is ignored.

    3.7.3. Effect of thickness on elastic ultimate bearing capacity

    As we can see, from the numerical examples, the elastic ultimate bearing capacity can be improved significantly by using the FG linings, either IFGL or DFGL. And, the improvement degree, as mentioned above, is related to the relative thickness as well. So, it is necessary to discuss the effect of lining thickness on the elastic ultimate bearing capacity. The relationships between the dimensionless elastic ultimate bearing capacity and the relative thickness, t/Rin, are to be given as follows. For the TSL, the relationship can be given according to Eq. (53),

    pTSLeσc=12111+t/Rin2E56

    For the IFGL, it can be deduced according to Eq. (12),

    pIFGLeσc=pIFGLpσc=ln1+t/RinE57

    For the ODFGL, it can be deduced according to Eqs. (36) and (55),

    pODFGLeσc=t/Rin1+t/RinE58

    For an uniform thick DFGL, that is, R1 = (Rin + Rout)/2, its elastic ultimate bearing capacity is also related to the values of the Young’s modulus. If R1/Rin>λ, according to Eq. (35), we have

    pDFGLeσc=12E2E111+t/2Rin211+t/Rin2+111+t/2Rin2E59

    if R1/Rin<λ, according to Eq. (37), we have

    pDFGLeσc=12E1E21+t/2Rin21+112+121+t/Rin2E60

    It should be noted that Eqs. (56)(60) are obtained on the assumption that the UCS of each lining material is constant. Figure 9 illustrates the curves between the dimensionless elastic ultimate bearing capacity with respect to the relative thickness. The curve of the DFGL in Figure 9 is plotted based on the values of Young’s modulus list in Table 1, E1 = 25 GPa and E2 = 41 GPa. The increases on elastic ultimate bearing capacity of different types of linings with respect to relative lining thickness are listed in Table 2. As can be seen from Figure 9 and Table 2 that, if we use the IFGL and ODFGL, the increases will become more significant, especially the IFGL. But the opposite situation happens for the DFGL. The elastic ultimate bearing capacity is improved more significantly as the lining is thinner.

    Figure 9.

    Dimensionless elastic ultimate bearing capacity with respect to relative thickness.

    t/RinpTSLe/σcpIFGLe/σcIncrement (%)pODFGLe/σcIncrement (%)pDFGLe/σcIncrement (%)
    0.050.0460.0494.960.0482.440.06130.83
    0.100.0870.0959.830.0914.760.11329.72
    0.200.1530.18219.340.1679.090.19527.65
    0.300.2040.26228.520.23113.040.25725.77
    0.400.2450.33637.390.28616.670.30424.07
    0.500.2780.40545.970.33320.000.34022.53
    0.600.3050.47054.260.37523.080.36921.12
    0.700.3270.53162.280.41225.930.39219.83
    0.800.3460.58870.040.44428.570.41018.66
    0.900.3610.64277.550.47431.030.42517.58
    1.000.3750.69384.840.50033.330.43716.59

    Table 2.

    Increases on elastic ultimate bearing capacity.

    Note: All the increases are calculated comparing with the TSL.

    3.7.4. Stresses and radial displacement distributions

    In order to compare the stress distributions in different types of linings, we take the value of support pressure p = 15 and 23 MPa as examples and the other parameters are the same as in Table 1. Figures 10 and 11 illustrate the radial and tangential stress distributions in the radial direction. The main difference between the three linings is the tangential stress σθ and the radial stress distributions are almost the same. As p = 15 MPa (see Figure 10), all the three linings are in elastic state. As we know, the tangential stress concentration is the main reason of plastic yielding. Usually, the largest tangential stress concentration occurs along the inner boundary of the lining and the stress there is two dimensional, so the inner boundary of the lining is the most plastic-yielding-prone zone. In this zone, as can be seen from Figure 10 that the tangential stress concentration of the TSL σθ/p = 3.125, the largest tangential stress concentration of the TSL, while the tangential stress concentration factor σθ/p along the inner boundary of the DFGL and that of the IFGL are 2.599 and 1.958, decreases of 16.8 and 37.3% compared to the TSL, respectively. And the largest tangential stress concentration of the DFGL and that of the IFGL, σθ/p = 2.966 and 2.958, occur along the inner boundary of the outer layer and the outer boundary of the lining, respectively, where both are in three dimensional stress. So, the stress distributions in both the DFGL and IFGL are more reasonable than that in the TSL. As p = 23 MPa (see Figure 11), the given support pressure is larger than the elastic ultimate bearing capacities of the TSL and DFGL, so parts of the two linings turn into plastic state. But the IFGL is still in elastic state. The thickness of plastic zone in the TSL is about 0.092 m, 46% of the total thickness of the lining, while, for the DFGL, the thickness of plastic zone in both layers is about 0.062 m total, 31% of the total thickness of the lining. So, according to the stress distributions and the plastic area, we can come to that both the DFGL and IFGL are superior to the TSL.

    Figure 10.

    Stress distributions in the radial direction (p = 15 MPa).

    Figure 11.

    Stress distributions in the radial direction (p = 23 MPa).

    4. Model tests

    4.1. Mixture of model material

    In order to testify the superiorities of the FG linings over the TSL, we carried out a model test to compare the support characteristics. Due to the difficulties of constructing a multilayered concrete lining, the simplest multilayered lining, a double-layered lining structure, is chosen. As mentioned earlier, in order to obtain a FG concrete lining, we need a FG concrete mixture (FGC), producing concrete with same strength but different Young’s modulus.

    The main factors influencing the strength and/or the Young’s modulus contain the aggregate properties (like the quality [30], the type and maximum aggregate size [31], the grade [32],the Young’s modulus [33], etc.), the water/binder ratio [34], the chemical admixtures (like the air-void mixture [35], shrinkage-reducing mixture [36], retarders and accelerators [37], superplasticizer [38], etc). Besides, the steel or polyfibers [39], usually used in practice, also have influence on the concrete strength and Young’s modulus. In order to obtain the FGC, we conducted orthogonal test and a large number of single factor tests, investigating the influences of almost all of the abovementioned factors on the Young’s modulus and compressive strength of concrete. Experimental data were analyzed statistically. Test results of multivariate analysis of variance (MANOVA) with 95% confidence level (α = 0.05) show that the quantity and modulus of coarse aggregate are two significant factors influencing the Young’s modulus, but the compressive strength is slightly influenced by the two factors. The poly fiber also has such an influence just not that significant. So, the quantity and modulus of coarse aggregate the poly fiber are chosen as the major factors to prepare the FGC.

    4.1.1. Raw materials

    The mixture test and the model tests later in this chapter are based on Portland Cement 42.5R as the cementing material. The physical parameters of cement are listed in Table 3. The coarse aggregate is crushed limestone with the size between 5 and 20 mm. Figure 12 shows the size distribution of the coarse aggregate, including the corresponding ASTM C 33 limits. It can be seen that the coarse aggregate is within the ASTM C 33 coarse aggregate grading band [40]. The fine aggregate was river sand with a fineness modulus of 3.2 (see Figure 13). Polypropylene fibers, GRPF-12 mm (Figure 14), are added in concrete mixes at different volumetric fractions. Specifications are listed in Table 4. The superplasticizer (JM-PCA(V)) is a complex additive based on carboxylic grafted polymeric, produced by Nanjing Subote New Materials Co., Ltd., China.

    Type of cementP.O 42.5R
    Specific surface area (m2/kg)330
    Initial setting time (min)≥60
    Final setting time (h)6
    Compressive strength (3d) (MPa)≥24.0
    Compressive strength (28d) (MPa)≥48.0
    Flexural strength (3d) (MPa)≥4.5
    Flexural strength (28d) (MPa)≥7.0

    Table 3.

    Parameters of cement.

    Figure 12.

    Grading of coarse aggregates.

    Figure 13.

    Size distribution for fine aggregate with fineness modulus = 3.2.

    Figure 14.

    Polypropylene fiber.

    Material composition100% polypropylene
    Density (g/cm3)0.91
    Equivalent diameter (μm)27.69
    Fracture strength (MPa)641
    Initial modulus (GPa)8.5
    Elongation at break (%)30
    Length (mm)12
    Melting point (°C)>160
    Material shapeMonofilament
    Chemical propertiesAcid-proof, alkali-proof, nontoxic

    Table 4.

    Properties of polypropylene fiber.

    4.1.2. FGC mixture

    Based on the results of tests, six concrete mixtures and the parameters are given in Table 5.

    No.Water (kg/m3)Cement (kg/m3)Sand (kg/m3)Aggregate (kg/m3)Water reducer (kg/m3)Polypropylene fiber (kg/m3)Properties
    Compressive strength, σc (Mpa)Young’s modulus, E (Gpa)Poisson’s ratioSlum (cm)
    115639058513258.775854.640.20.2288.5
    2187467702104010.50851.341.00.23517.0
    321854681979512.285445.937.70.23512.0
    4255686102917.493450.226.90.2346.0
    5255686102917.493849.124.80.2336.0
    6255686102917.4931246.024.10.234.0

    Table 5.

    Proportions and mechanical properties of FGCs (kg/m3).

    4.2. Model test program

    4.2.1. Lining structures and dimensions

    As mentioned earlier, in the model tests, we conduct two lining structures, that is, the traditional single-layered lining (Figure 15(I)) and the double-layered FG lining (Figure 15(II)), assessing the support characteristics. Because the two layers of the DFGL need to be poured separately, the interface between them is unavoidable. In order to reduce the interface effect to the results, the TSL is also poured twice like the DFGL. The pouring process is to be given later.

    Figure 15.

    Two types of lining structures: (I) TSL and (II) DFGL.

    Considering the working space of the test platform, the dimensions are chosen as Rin = 300 mm, R1 = 400 mm, and Rout = 500 mm. It should be noted that the problem we discussed in our theoretical models is a plain strain problem; so in order to get linings that can simulate the state of a plain strain, the linings should be long enough, comparing with the dimensions of the cross section. The length in our test is 2300 mm (Figure 16).

    Figure 16.

    Pouring process of DFGL (mm).

    4.2.2. Material properties

    Combining the theoretical results and the functionally graded concrete (FGC), two types of concrete, M1 and M2, are poured using the two mixtures, No. 2 and 5 in Table 5, respectively. The mechanical parameters of the lining concretes are listed in Table 6. The parameters are obtained by testing the specimens poured using the real lining concrete mixtures, not the results in Table 5. The specimens and the linings are all cured in water (20 ± 2°C) for 28 days.

    Lining typesUCS, σc (MPa)Young’s modulus, E (GPa)Poisson’s ratio, μSlump (cm)
    Single-layered liningInner layer51.26040.6870.23519
    Outer layer50.12041.0470.23617
    Two-layered FGLInner layer49.63425.3910.23516
    Outer layer48.58341.1990.2337

    Table 6.

    Mechanical properties of lining concretes.

    4.2.3. Casting of the lining

    We firstly pour the inner layer and then the outer layer. The process in detail is as follows:

    1. Choose 400- and 300-mm-radius steel cylinders (R400 and R300) as the outer and inner moulds of the lining inner layer, respectively, and fix them on the bottom steel ring, making sure they are located with the same axis (Figure 16(I)).

    2. Wipe release agent and pour concrete of the inner layer (Figure 16(I)). In order to fix the top steel ring and ensure the contact between the concrete and the top steel ring, a certain space should be reserved and the surface should be rough (Figure 16(I)).

    3. 24 hours later, tear down the outer mold.

    4. Choose 500-mm-radius steel cylinder (R500) as the outer mold of the lining outer layer, wipe release agent, and fix it around the bottom steel ring (Figure 16(II)).

    5. Pour the concrete of the outer layer (Figure 16(III)) and fix the top steel ring.

    6. Tear down R300 and R500 (Figure 16(IV)).

    7. 48 hours later, move lining into the special curing box.

    4.2.4. Monitoring scheme

    As mentioned earlier, both ends of linings are poured in steel rings, we can say both ends are fixed in the horizontal cross section, which, of course, will lead to difference between the theoretical model and the test linings. So, three monitoring cross sections are all in the middle part of the linings. The monitoring parameters contain the radial displacements on the inner surface (all displacement sensors are fixed on a vertical steel cylinder with magnetic stands, the axial displacements at both ends, and the tangential and axial strains on the inner and outer surfaces). Due to the limited working space, displacements only in the upper two cross sections are monitored. Figure 17 shows the layout of monitoring points.

    Figure 17.

    Layout of monitoring points (mm): (A) unfolded section; (B) vertical section; and (C) horizontal section.

    4.3. Results and discussions

    As mentioned earlier, the load process is accomplished in three steps. In this section, we just analyze the third step, that is, confining pressure step. In addition, due to the complexity and the long loading time, only part of displacement sensors and strain gages work regularly, so, in our analysis, only effective data are illustrated. For the test results, the sign convention is defined positive for tension strain and outward displacement, and negative for compressive strain and inward displacement. All data, related to displacements, strains, and pressures, are collected with interval of 5 seconds.

    Figure 18 illustrates the curves of the confining pressure versus loading time. Figure 19 illustrates the convergences along inner boundaries of linings versus support pressure, containing model test and theoretical results. As can be seen from Figure 19, the confining pressures of both the TSL and DFGL drop suddenly after reaching the maximum values. For comparison, the results of theory and model test are listed in Table 7. It can be noted that the maximum confining pressure that the DFGL can bear in model test is approximately 20.44 MPa, 24.56% greater than that of the TSL, 16.41 MPa. The two maximum confining pressures are close to the theoretical elastic ultimate bearing capacities of the DFGL and TSL (19.24 and 16.00 MPa, corresponding to points D and A in Figure 19), respectively.

    Figure 18.

    Loading scheme.

    Figure 19.

    Convergences along inner boundaries of linings versus support pressure.

    Lining typesElastic ultimate bearing capacities (μ = 0.5), pe (MPa)Plastic ultimate bearing capacities, pp (MPa)Maximum confining pressure in model tests, pmax (MPa)
    TSL16.0025.5416.41
    DFGL19.24 (19.741)25.5420.44
    IFGL25.5425.54

    Table 7.

    Ultimate bearing capacities of linings.

    The value for μ = 0.24.


    4.3.1. Effect of Poisson’s ratio on ultimate bearing capacity

    It should be noted that the two theoretical elastic ultimate bearing capacities of the DFGL and TSL are obtained by assuming the lining concrete as incompressible, that is, μ = 0.5. According to the theoretical analysis, the plastic ultimate bearing capacities are just affected by the material strengths, having nothing to do with the Poisson’s ratio. The only one elastic ultimate bearing capacity related to the Poisson’s ratio is that of the DFGL (see Table 7). Let μ = 0.24 (see Table 6), we can obtain the elastic ultimate bearing capacities, peDFGL = 19.74 MPa (see point D’ in Figures 18 and 19), which is closer to the maximum confining pressure from the model tests. So, the maximum confining pressures of the TSL and DFGL should be their elastic ultimate bearing capacities, which can also be confirmed by Figure 18.

    4.3.2. Effects of the Poisson’s ratio on radial displacement

    From Figure 19, in the elastic stage, the Poisson’s ratio affects the radial displacement of all the three lining structures in a same rule, that is, for a given confining pressure, the radial displacement for μ = 0.24 is greater than that for μ = 0.5. The Poisson’s ratios of the concrete in the model tests are about 0.24. So, the p-ur curves of TSL and DFGL from model tests should be closer to those theoretical ones as μ = 0.24 than as μ = 0.5. The opposite happens, that is, the convergences by model tests are smaller than the analytical values, being closer to the analytical results as μ = 0.5. This situation may be resulted from the restrictions of steel rings at both ends of linings in our model tests (Figure 16).

    4.3.3. Effects of the Poisson’s ratio on plastic zone

    Figure 20 illustrates the extension paths of plastic yielding of all the three lining structures as μ = 0.24 and 0.5. The value of the Poisson’s ratio only affects the plastic yielding path of the DFGL, but not that of the IFGL and TSL, which is because the Poisson’s ratio is related to the displacement and the displacement continuous conditions are used in the elastoplastic analysis of the DFGL, but not in the IFGL and TSL. For μ = 0.24, the plastic yielding will (i) initiate from the inner boundary of the outer layer (point D’ in Figures 19 and 20, where p = 19.74 MPa), not from the inner layer as μ = 0.5; (ii) the inner boundary of the inner layer turns into plastic yielding at point E’, where p = 20.28 MPa; (iii) the outer layer totally turns into plastic state at point F′, where p = 24.42 MPa; and followed by (iv) the inner layer turns into plastic state at point G’, where p = 25.54 MPa.

    Figure 20.

    Extension path of plastic yielding.

    5. Conclusions

    The purpose of the work is to show a new way to improve the elastic ultimate bearing capacity of a circular single-layered concrete lining. We proposed the concept of functionally graded concrete lining, which is based on the inverse analysis of assuming the concrete failure ruled by the Tresca criterion, and the theoretical analysis can verify the effectiveness of the method. But the requirements of the theoretical ideal functionally graded lining, that is, the constant compressive strength and continuously increasing Young’s modulus in radially outward direction, can hardly be achieved for concrete material. So, we choose the multilayered lining as the alternative.

    Elastoplastic analysis is carried out, and the elastic and plastic ultimate bearing capacities are obtained. The results show that a double-layered functionally graded lining has greater elastic ultimate bearing capacity but the same plastic ultimate bearing capacity comparing with the traditional single-layered lining. The distributions of stresses in ideal functionally graded lining and double-layered functionally graded lining are more reasonable, maximum tangential stress concentration decreasing and no longer in the inner boundary of lining. Even if in the plastic stage, the areas of plastic zone in functionally graded linings are smaller than that in single-layered lining. And the opposite happens for the radial displacement, which is resulted from the lower Young’s modulus of the inner layer. Besides, the Poisson’s ratio has effect on the radial displacement, elastic ultimate bearing capacity, and extension path of plastic yielding.

    Finally, model tests are conducted in order for verifying the theoretical results. A traditional single-layered lining and a double-layered functionally graded lining are poured and loaded in axial and confining pressures. The maximum confining pressures that the linings can bear in test are only slightly greater than the corresponding theoretical elastic ultimate bearing capacity. Combined with the curves of pressure versus radial displacement, the maximum pressures can be regarded as the respective elastic bearing capacity. In this way, the theoretical results are verified by the model tests and the functionally graded lining would make a great deal of practical sense.

    Acknowledgments

    This research work was supported by the Natural Science Foundation of China (Grant No. 51704117, 11572126). Their financial support is gratefully acknowledged.

    Conflict of interest

    The authors declare that they have no conflict of interest.

    © 2018 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

    How to cite and reference

    Link to this chapter Copy to clipboard

    Cite this chapter Copy to clipboard

    Ning Zhang, Aizhong Lu and Xuguang Chen (November 5th 2018). Functionally Graded Concrete Structure, Sustainable Construction and Building Materials, Sayed Hemeda, IntechOpen, DOI: 10.5772/intechopen.81435. Available from:

    chapter statistics

    222total chapter downloads

    More statistics for editors and authors

    Login to your personal dashboard for more detailed statistics on your publications.

    Access personal reporting

    Related Content

    This Book

    Next chapter

    Cumulative Tensile Damage and Consolidation Effects on Fracture Properties of Sandstone

    By Martin Šperl and Miloš Drdácký

    Related Book

    First chapter

    ISBS 2019 - 4th International Sustainable Buildings Symposium

    By Arzuhan Burcu Gültekin

    We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

    More About Us