Measured geometrical and mechanical properties of pristine MWCNTs. Shown are the nanotube inner diameter (ID), outer diameter (OD), length (
1. Introduction
Novel materials and processing routes provide opportunities for the production of advanced high performance structures for different applications. Ceramic matrix composites are one of these promising materials. Engineering ceramics such as Al2O3, Si3N4, SiC and ZrO2 produced by conventional manufacturing technology have high stiffness, excellent thermostability and relatively low density, but extreme brittle nature restricted them from many structural applications (Mukerji, 1993). Considerable attention has been adopted to improve the fracture toughness. An approach has been paid to the development of nanocrystalline ceramics with improved fracture properties. Decreasing the grain size of ceramics to the sub- and nano-meter scale leads to a marked increase in fracture strength (Miyahara et al., 1994). However, fracture toughness of nanocrystalline ceramics generally displays modest improvement or even deterioration (Miyahara et al., 1994; Rice, 1996; Yao et al., 2011). As one possible approach, incorporation of particulates, flakes and short/long fibers into ceramics matrix, as a second phase, to produce tougher ceramic materials is an eminent practice for decades (Evans, 1990). Recently, researchers have focused on the carbon nanomaterials, in particular carbon nanotubes (CNTs), which are nanometer-sized tubes of single- (SWCNTs) or multi- layer graphene (MWCNTs) with outstanding mechanical, chemical and electrical properties (Dai et al., 1996; Ebbesen et al., 1996; Treacy et al., 1996; Huang et al., 2006; Peng et al., 2008), motivating their use in ceramic composite materials as a fibrous reinforcing agent.
It is well recognized that some difficulties appear to be the major cause for the limited improvement in CNT/ceramic composites prepared to date. The first is the inhomogeneous dispersion of CNTs in the ceramic matrix. Pristine CNTs are well known for poor solubilization, which leads to phase segregation in the composite owing to the van der Waals attractive force (Chen et al., 1998). Such clustering produces a negative effect on the physical and mechanical properties of the resultant composites (Yamamoto et al., 2008). The second is the difficulty in controlling connectivity between CNTs and the ceramics matrix, which leads to a limited stress transfer capability from the matrix to the CNTs (Peigney, 2003; Sheldon & Curtin, 2004; Chen et al., 2011). The strengthening and toughening mechanisms of composites by fibers are now well established (Evans, 1990; Hull & Clyne, 1996); central to an understanding is the concept of interaction between the matrix and reinforcing phase during the fracture of the composite. The fracture properties of such composites are dominated by the fiber bridging force resulting from debonding and sliding resistance, which dictates the major contribution to the strength and toughness. Thus, the adequate connectivity with the matrix, and uniform distribution within the matrix are essential structural requirements for the stronger and tougher CNT/ceramic composites. To overcome these obstacles, various efforts, such as surface modification (De Andrade et al., 2008; Yamamoto et al., 2008; Kita et al., 2010; Gonzalez-Julian et al., 2011), heterocoagulation (Fan et al., 2006a, 2006b), extrusion (Peigney et al., 2002), and their combination, have been made to effectively achieve good dispersion of CNTs in ceramic matrix. Until now, however, most results for strengthening and toughening have been disappointing, and only little or no improvement have been reported in CNT/ceramic composite materials, presumably owing to the difficulties in homogeneous dispersion of CNTs in the matrix and in formation of adequate interfacial connectivity between two phases.
This chapter presents that novel processing approach based on the precursor method. The MWCNTs used in this study are modified with an acid treatment. Combined with a mechanical interlock induced by the chemically modified MWCNTs, this approach leads to improved mechanical properties. Mechanical measurements on the composites revealed that only 0.9 vol.% acid-treated MWCNT addition results in 37% and 36% simultaneous increases in bending strength (689.6 ± 29.1 MPa) and fracture toughness (5.90 ± 0.27 MPa m1/2), respectively, compared with a MWCNT-free alumina sample prepared under similar processing conditions. Structure-property relationship of present composites will be explained on the basis of the detailed nano/microstructure and fractographic analysis. We also explain why previous reports indicated only modest improvements in the fracture properties of MWCNT based ceramic composites. Here, the failure mechanism of the MWCNTs during crack opening in a MWCNT/alumina composite is investigated through transmission electron microscope (TEM) observations and single nanotube pullout tests. Achieving tougher ceramic composites with MWCNTs is discussed based on these results.
2. A novel approach for preparation of MWCNT/alumina composites
To disperse the MWCNTs homogeneously in the matrix and improve the connectivity between MWCNTs and matrix, we developed a novel approach with combination of a precursor method for synthesis of an alumina matrix, an acid treatment of MWCNTs and a spark plasma sintering method. The improvement on the bending strength and fracture toughness was confirmed by the fracture tests.
2.1. Materials and specimen preparation
2.1.1. Starting materials
The MWCNT material (Nano Carbon Technologies) used in this research was synthesized by a catalytic chemical vapor deposition method followed by high temperature annealing at 2600˚C. The purity was claimed to be 99.5% by the producer. Fig. 1 shows scanning electron microscope (SEM, Hitachi S-4300) and TEM (Hitachi HF-2000) images of the pristine MWCNTs. It can be seen from Fig. 1b that the pristine MWCNTs have a highly crystalline multi-walled structure with a narrow central channel. The corresponding geometrical and mechanical properties of the pristine MWCNT are listed in Table 1. The estimated diameter and length of the pristine MWCNTs from SEM and TEM measurements ranged from 33 to 124 nm (average: 70 nm) and 1.1 to 22.5 μm (average: 8.7 μm), respectively. Tensile-loading experiments with individual MWCNTs using a nanomanipulator tool operated inside SEM revealed that the tensile strengths of 10 pristine MWCNTs ranged from ∼2 to ∼48 GPa (average: 20 GPa) and the Young's modulus ranged from ∼50 to ∼1360 GPa (average: 790 GPa) (Yamamoto et al., 2010). It seems that the average tensile strength of the pristine MWCNT used in this research were somewhat lower than that of the arc-discharge grown MWCNTs (Yu et al., 2000).
ID (nm) | OD (nm) | l (μm) | ρ (Mg/m3) | (GPa) | E (GPa) | I (nm4) | EI (N·nm2) |
7 (3~12) | 70 (33~124) | 8.7 (1.1~22.5) | 2.1 | 20 (2~48) | 790 (50~1360) | 1.2×106 | 9310×10-4 |
2.1.2. Acid treatment of MWCNTs
The rationale behind the acid treatment is to introduce nanoscale defects and adsorb negatively charged functional groups at the MWCNT ends and along their lengths. The pristine MWCNTs were refluxed in 3:1 (volume ratio) concentrated H2SO4:HNO3 mixture at a temperature of 70˚C for 1 hour, 2 hours and 4 hours, washed thoroughly with distilled water to be acid-free, and then finally dried in an air oven at 60˚C. Fig. 2 shows the typical TEM images of a series of the acid-treated MWCNTs and the corresponding distribution of nanodefect depths treated with the various conditions. It is demonstrated that with the acid treatment of the pristine MWCNTs, we have deliberately introduced nanoscale defects on the surface of the MWCNTs. The depth of the nanodefects is on the nanoscale and the average size is in the range of 4.4~7.0 nm for the acid treatment used in this study. We can see that the nanodefects density, i.e., the number of nanodefects per unit of a MWCNT surface area increases with the increasing treatment time. Hereafter, the number of the nanodefects per unit of the MWCNT surface area is referred to as the nanodefect density.
In addition to the nanodefects density, the average size of the nanodefect depths appears to vary with respect to the treatment time. When the treatment time increases from 1 hour to 2 hours, the average size of nanodefect depths increases from 4.4 nm to 6.5 nm. Furthermore, when the treatment time further increases to 4 hours, it increases to 7.0 nm. The aspect ratio (
The zeta potential values of the pristine MWCNTs and the acid-treated MWCNTs at different pH values are shown in Fig. 3a. Here, the changes in zeta potentials were measured in 1.0 mM KCl aqueous solution of varying pH using a zeta potential analyzer (ZEECOM ZC2000, Microtec). The pH value of the aqueous solution was adjusted with HCl and NaOH. Zeta potential values were calculated using the Smoluchowski equation. The isoelectric point (pHiep) for the pristine MWCNTs is located at about 3.0, whereas the acid treatment process makes the surface more negatively charged at tested pH values. The change in the zeta potential may be mainly due to the introduction of more functional groups after the acid treatment (Esumi et al., 1996; Liu et al., 1998). These functional groups make them easily dispersed in polar solvents, such as water and ethanol. Fig. 3b shows a photograph of the pristine MWCNTs and acid-treated MWCNTs suspensions at pH 6, respectively. It is clear that the pristine MWCNTs are not dispersed at pH 6. In contrast, the dispersion of the acid-treated MWCNTs is seen to improve dramatically. Furthermore, it can be expected that the larger electrical repulsive force between the acid-treated MWCNTs will facilitate their dispersion and prevent them from tangling and agglomeration. The zeta potential of the aluminum hydroxide, which is used as the starting material for synthesis of the alumina matrix, exhibited positive values over a wide pH range (pH = 3~9), while that of the acid-treated MWCNTs was negative in this pH range. On these two colloidal suspensions are mixed, particles of the aluminum hydroxide will bind onto the acid-treated MWCNTs because of the strong electrostatic attractive force between them, and this results in a homogeneous MWCNTs and aluminum hydroxide solution.
2.2. Preparation of MWCNT/alumina composites
A typical synthesis procedure for the composite preparation is as follows. The 50 mg MWCNTs acid-treated for 2 hours or pristine MWCNTs were dispersed in 400 ml ethanol with aid of ultrasonic agitation. 15.2 g aluminum hydroxide (Wako Pure Chemical Industries) was added to this solution and ultrasonically agitated. 73 mg magnesium hydroxide (Wako Pure Chemical Industries) was added to prevent excessive crystal growth. Here, the weight loss of the hydroxides caused by the dehydration process was accounted for in the calculation of the composite composition. The weight loss of the aluminum hydroxide and the magnesium hydroxide was 34.7% and 31.9%, respectively. The resultant suspension was filtered and dried in an air oven at 60˚C. Finally, the product obtained in the previous step was put into a half-quartz tube and was dehydrated at 600˚C for 15 min in argon atmosphere. The composites were prepared by spark plasma sintering (SPS, SPS-1050 Sumitomo Coal Mining) (Omori, 2000) in a graphite die with an inner diameter of 30 mm at a temperature of 1500˚C under a pressure of 20 MPa in vacuum for 10 min. For comparison, similar preparation processes were applied while using the pristine MWCNTs as the starting material. Fig. 4 shows X-ray diffraction patterns (M21Mac Science) of the (a) aluminum hydroxide–MWCNT mixture, (b) dehydrated product and (c) sintered body, respectively. It is difficult to distinguish the MWCNT peaks from all XRD patterns, probably due to the small quantity of MWCNTs. The diffraction peaks corresponding to the aluminum hydroxide and the intermediate were observed in the aluminum hydroxide–MWCNT mixture. However, the diffraction peaks corresponding to the aluminum hydroxide and the intermediate disappeared completely in the sintered body, suggesting the phase transformation of the aluminum hydroxide to form
2.3. Micro- and nanostructures of MWCNT/alumina composites
We now discuss the micro- and nanostructures of the acid-treated MWCNT/alumina composites using SEM and TEM analysis. An interesting geometric structure was observed between the individual MWCNT and the alumina matrix, as shown in Fig. 5. It is revealed that a nanodefect on the acid-treated MWCNT is filled up with alumina crystal, which may be intruding into the nanodefect during grain growth. This nanostructure is novel in that its structure resembles a nanoscale anchor with an alumina crystal spiking the surface of the MWCNT.
From the SEM observations on the fracture surface, the following features can be noted. First, numerous individual MWCNTs protrude from the fracture surface, and the pullout of the MWCNTs can be clearly observed (Fig. 6a), which had not been obtained until now for conventional CNT/ceramic composites. Most of MWCNTs are located in the intergranular phase and their lengths are in the range 0~10 μm. The alumina grains have sizes in the micron range, around 1.5 μm (The grain size of the composite was obtained using SEM images, and the observation was made for 224 grains.). No clear difference in the grain size is observed between the acid-treated MWCNT/alumina composites and the pristine MWCNT/alumina composites, even though the incorporation of MWCNTs seems to suppress the grain growth of the alumina. Second, in the case of the smaller amount of the acid-treated MWCNTs, no severe phase segregation was observed, whereas the composites made with the pristine MWCNTs revealed an inhomogeneous structure even for MWCNT addition as low as 0.9 vol.%. In addition to the above features, some MWCNTs on the fracture surface showed a ″clean break″ near the crack plane, and that the diameter of MWCNT drastically slenderized toward their tip, as illustrated in Figs. 6 b and 6c, respectively. As SEM cannot clearly resolve the thickness of a single MWCNT, TEM was used to determine if the fracture phenomenon of MWCNTs was indeed occurring during crack opening.
TEM observations on the fracture surface demonstrated that a diameter change in the MWCNT structure was evidently observed for a certain percentage of the MWCNTs (Fig. 7a). At least, 25% MWCNT appear to have an apparent diameter change (The observation was made for 281 MWCNTs.). As shown in Fig. 7b, the high magnification TEM image clearly showed a change in diameter, and this morphology is quite similar to a ″sword-in-sheath″-type failure (Yu et al., 2000; Peng et al., 2008; Yamamoto et al., 2010). Key features are illustrated in enlarged TEM image, taken from the square area in Fig. 7b. The inset showed that outer-walls having approximately 10 shells were observed to break up at the location where the MWCNT undergo failure, and that the edges of the broken outer shells were observed to be perpendicular to the cylinder axis. Since no apparent variation in the diameter of the MWCNTs has been observed along the axis in the as-received MWCNTs, these results imply that some MWCNTs underwent failure in the sword-in-sheath manner prior to pullout from the matrix. Note that MWCNT failure was also observed in fracture surfaces of alumina composites made with arc-discharge-grown and chemical vapor deposition-grown MWCNTs prepared under the same processing conditions (Yamamoto et al., 2011).
2.4. Physical and mechanical properties of MWCNT/alumina composites
The bending strength of the composites was measured by the three-point bending method under ambient conditions, in which the size of the test specimens was 2.0 mm (width) × 3.0 mm (thickness) × 24.0 mm (length). The span length and crosshead speed for the strength tests were 20.0 mm and 0.83 μm/s, respectively. The fracture toughness was measured by the single-edge notched beam (SENB) method (Japanese Industrial Standards, 1995) under ambient conditions, in which the size of test specimens was 2.0 mm (width) × 3.0 mm (thickness) × 15.0 mm (length). A notch with depth and width of 0.3 mm and 0.1 mm was cut in the center part of the test specimens. A span length of 12.0 mm and crosshead speed of 0.83 μm/s were applied for the toughness test. The bending strength (
where
where
It was found that surface modification of the MWCNTs is effective in improvement of bending strength and fracture toughness of the MWCNT/alumina composites. Figs. 8 a and 8bshow the dependence of the bending strength and the fracture toughness on MWCNT content in the composites. There are few papers which report significant improvement in the mechanical properties such as toughness (Zhan et al., 2003), and the improvement by MWCNT addition has been limited so far in previous studies (Ma et al., 1998; Sun et al., 2002; Wang et al., 2004; Sun et al., 2005; Cho et al., 2009). In our composites, however, the bending strength and the fracture toughness simultaneously increased with the addition of a small amount of the acid-treated MWCNTs. The bending strength and the fracture toughness of the 0.9 vol.% acid-treated MWCNT/alumina composite reached 689.6 ± 29.1 MPa and 5.90 ± 0.27 MPa m1/2,respectively. At the same time, the bending strength and the fracture toughness of the acid-treated MWCNT/alumina composites were always higher than those of the pristine MWCNT/alumina composites with identical MWCNT content, indicating enhanced stress transfer capability from the alumina to the acid-treated MWCNTs. The Vickers indentation toughness calculated by using the Eq. (4) was 6.64 MPa m1/2, which is a slightly larger value than that measured by using SENB method (5.90 MPa m1/2). These observations revealed that the high structural homogeneity and enhanced frictional resistance of the structural components led to a simultaneous increase in the strength and the toughness of the acid-treated MWCNT/alumina composites. In contrast, for the larger amount of the MWCNTs, the degradation of mechanical properties of both the composites may be primarily attributed to the severe phase segregation. Because a bundle of segregated CNTs has poor load-carrying ability, the effect of this kind of CNT aggregate in the matrix may be similar to that of pores (Yamamoto et al., 2008a, 2008b).
3. Evaluation of crack bridging characteristics
Ceramic-CNT interfacial behavior is another key factor in controlling the mechanical and physical properties of fiber reinforced composite materials (Evans, 1990; Hull & Clyne, 1996; Chen et al., 2011). In general, strong interfacial connectivity facilitates effective load transfer effect, but it prevents CNT pull-out toughening from occurring. Weak interfacial connectivity favors CNTs pull-out but fails to toughen the ceramic matrix. Thus, a balance must be maintained between CNT pull-out and toughening mechanics. It is well recognized that improved toughness of fiber-reinforced ceramic composites is obtained under moderate fiber-ceramic interfacial connectivity. In this regard, suitable (neither too strong nor too weak) ceramic-CNT interfacial connectivity is needed to ensure effective load transfer, and to enhance the toughness and strength of ceramic-CNT composites. Here, the failure mechanism of the MWCNTs during crack opening in a MWCNT/alumina composite is investigated through TEM observations and single nanotube pullout tests. Achieving tougher ceramic composites with MWCNTs is discussed based on these results.
3.1. Pullout experiment sample preparation
The MWCNT failure during crack opening motivated our research of the crack bridging characteristics through the single nanotube pullout tests. The single nanotube pullout experiments were carried out using an
where
where
A crosshead speed – i.e., movement rate of the cantilever – of about 100 nm/s was applied for the pullout tests.
We fractured a composite specimen by conducting the fracture tests, which caused single MWCNT to project from the crack plane, as exemplified in Fig. 6a. This allows single MWCNT ″pickup″ with cantilever tip for subsequent tensile loading using the nanomanipulator. As mentioned above, however, the MWCNTs crossing the crack planes were strained during crack opening and possibly underwent failure, as shown in Figs. 6b, 6c and 7. Therefore, by observing the fracture surface on the composites, MWCNTs with no apparent damages were selected for the pullout tests. The physical and mechanical properties, and electrical conductivity of the composite used for the pullout testes are shown in Table 2.
Relativedensity(%) | Grainsize(μm) | Bendingstrength(MPa) | Fracturetoughness(MPa·m1/2) | Hardness(GPa) | Young’smodulus(GPa) | Poisson’sratio |
98.9 | 1.43±0.31 | 543.8±60.9 | 4.74±0.12 | 17.0 ± 0.4 | 358.0 | 0.20 |
3.2. Nanotube fracture during the failure of MWCNT/alumina composites
Results obtained from the pullout experiments revealed that strong load transfer was demonstrated, and no pullout behavior was observed for all 15 MWCNTs tested in this present research. Eight of these MWCNTs fractured at the composite surface and the remaining 7 MWCNTs underwent failure in the region between the fixed point on the cantilever and the crack plane, as illustrated in Fig. 10.
Two series of SEM and TEM images for each of two individual MWCNTs, captured before and after their breaking, are shown in Figs. 11 and 12. In the first series (Fig. 11; sample number 14), a MWCNT projecting 5.72 ± 0.01 μm from the fracture surface (Fig. 11a) was ″welded″ to a cantilever tip by local EBID, and then loaded in increments until failure. The resulting fragment attached on the cantilever tip was at least 10.9 μm long (Fig. 11b), whereas the other fragment remained lodged in a grain boundary of the alumina matrix (Fig. 11c), suggesting that MWCNT underwent failure in a sword-in-sheath manner. TEM images show a change in diameter at the location where the MWCNT underwent failure, and that the inner core protruding from the outer shells has a multi-walled closed-end structure, as shown in Figs. 11d and 11e, respectively. Given that uniformity of the interwall spacing of 0.34-nm-thick cylinder structure, approximately 11 shells underwent failure. There results strongly suggest that the MWCNTs broke in the outer shells and the inner core was then completely pulled away, leaving the companion fragment of the outer shells in the matrix. The sword-in-sheath failure did not always occur. Instead a few MWCNT failed leaving either a very short sword-in-sheath failure or a clean break. As for one example (Fig. 12; sample number 10), a MWCNT projecting 5.34 ± 0.01 μm from the crack plane (Fig. 12a) underwent failure on the composite fracture surface. The resulting fragment attached on the cantilever tip was at least 5.7 μm long (Fig. 12b), and no fragment was observed at the original position on the crack plane, suggesting that in this case the MWCNT failed by breaking inside the matrix, and did not pull out. Fig. 12c shows the TEM image of the tip of the same MWCNT which underwent very short sword-in-sheath failure or clean break during crack opening.
Next, we schematically describe possible processes and mechanics, explaining the MWCNT failure during crack opening (Fig. 13). As for one example, considering the sample number 14 (Fig. 11), the initial state of the MWCNT in an ideal case is a completely impregnated and isolated embedded in the matrix (Fig. 13a). Tensile stresses parallel to the axis of MWCNT length lead to matrix crack formation. Subsequently, interfacial debonding between two phases may occur (Fig. 13b), perhaps over a limited distance (but this is unlikely to make a major contribution to the fracture energy.). Since there is variability in the MWCNT strength in the debonded region on either side of the crack plane, and it is possible for the MWCNT to break at a certain position, when the stress in the MWCNT reaches a critical value. As displacement increases, the MWCNTs, rather than pulling out from the alumina matrix, undergo failure in the outer shells and the inner core is pulled away, leaving the fragments of the outer shells in the matrix (Figs. 13c and 13d).
4. Conclusion
Creating tough, fracture-resistant ceramics has been a central focus of MWCNT/ceramic composites research. In this research, the MWCNT/alumina composite with enhanced mechanical properties of 689.6 ± 29.1 MPa for bending strength and 5.90 ± 0.27 MPa m1/2 for fracture toughness have been successfully prepared by a novel processing method. A combination of the precursor method for synthesis of the alumina matrix, the acid treatment of the pristine MWCNTs and the spark plasma sintering method can diminish the phase segregation of MWCNTs, and render MWCNT/alumina composites highly homogeneous. The universality of the method developed here will be applicable to a wide range of functional materials such as tribomaterials, electromagnetic wave absorption materials, electrostrictive materials, and so on. Our present work may give a promising future for the application of MWCNTs in reinforcing structural ceramic components and other materials systems such as polymer- and metal-based composites.
We have also shown from TEM observations and single nanotube pullout experiments on the MWCNT/alumina composites that strong load transfer was revealed, and no MWCNT pullout behavior was observed. It is well recognized the fracture properties of fiber-reinforced composites are dominated by the fiber bridging force resulting from debonding and sliding resistance, which dictates the major contribution to the strength and toughness (Evans, 1990; Hull & Clyne, 1996). The results reported here suggest that modest improvements in toughness reported previously may be due to the way MWCNT’s fail during crack opening in the MWCNT/ceramic composites. Our finding suggests important implications for the design of tougher ceramic composites with MWCNTs. The important factor for such tougher ceramic composites will thus be the use of MWCNT having a much higher load carrying capacity (as well as a good dispersion in the matrix).
Acknowledgement
The authors thank our colleague, Dr. M. Omori, Mr. K. Shirasu, Mr. Y. Nozaka, Mr. Y. Aizawa and Ms. N. Suzuki of Fracture and Reliability Research Institute (FRRI), Tohoku University, for their helpful discussions, and Mr. T. Miyazaki of Technical Division, School of Engineering, Tohoku University, for technical assistance in the TEM analysis. The authors acknowledge Prof. R.S. Ruoff of The University of Texas at Austin for his useful guidance. This work is partially supported by Grand-in-Aids for Scientific Research (Nos. 23860004 and 21226004) from the Japanese Ministry of Education, Culture, Sports, Science and Technology. This work is performed under the inter-university cooperative research program of the Advanced Research Center of Metallic Glasses, Institute for materials Research, Tohoku University.
References
- 1.
Chen J. Hamon M. A. Hu H. Chen Y. Rao A. M. Eklund P. C. Haddon R. C. 1998 Solution properties of single-walled carbon nanotubes. Science,282 95 98 - 2.
Chen Y. L. Liu B. Huang Y. Hwang K. C. 2011 Fracture toughness of carbon nanotube-reinforced metal- and ceramic-matrix composites. Journal of Nanomaterials,2011 Article ID 746029. - 3.
Cho J. Boccaccini A. R. Shaffer M. S. P. 2009 Ceramic matrix composites containing carbon nanotubes. Journal of Materials Science,44 1934 1951 - 4.
Dai H. J. Wong E. W. Lieber C. M. 1996 Probing electrical transport in nanomaterials: conductivity of individual carbon nanotubes. Science,272 523 526 - 5.
De Andrade M. J. Lima M. D. Bergmann C. P. Ramminger G. D. O. Balzaretti N. M. Costa T. M. H. Gallas M. R. 2008 Carbon nanotube/silica composites obtained by sol-gel and high-pressure techniques. Nanotechnology,19 article265607 - 6.
Ding W. Dikin D. A. Chen X. Piner R. D. Ruoff R. S. Zussman E. Wang X. Li X. 2005 Mechanics of hydrogenated amorphous carbon deposits from electron-beam-induced deposition of a paraffin precursor. Journal of Applied Physics,98 article014905 - 7.
Ding W. Q. Calabri L. Chen X. Q. Kohhaas K. M. Ruoff R. S. 2006 Mechanics of crystalline boron nanowires. Composites Science and Technology,66 1112 1124 - 8.
Ebbesen T. W. Lezec H. J. Hiura H. Bennett J. W. Ghaemi H. F. Thio T. 1996 Electrical conductivity of individual carbon nanotubes. Nature,382 54 56 - 9.
Esumi K. Ishigami M. Nakajima A. Sawada K. Honda H. 1996 Chemical treatment of carbon nanotubes. Carbon,34 279 281 - 10.
Evans A. G. 1990 Perspective on the development of high-toughness ceramics. Journal of the American Ceramic Society,73 187 206 - 11.
Fan J. P. Zhao D. Q. Wu M. S. Xu Z. Song J. 2006 Preparation and microstructure of multiwalled carbon nanotubes-toughened composite. Journal of the American Ceramic Society,89 750 753 - 12.
Fan J. P. Zhuang D. M. Zhao D. Q. Zhang G. Wu M. S. Wei F. Fan Z. J. 2006 Toughening and reinforcing alumina matrix composite with single-wall carbon nanotubes. Applied Physics Letters,89 121910 1219103 - 13.
Gonzalez-Julian J. Miranzo P. Osendi M. I. Belmonte M. 2011 Carbon nanotubes functionalization process for developing ceramic matrix nanocomposites. Journal of Materials Chemistry,21 6063 6071 - 14.
Huang J. Y. Chen S. Wang Z. Q. Kempa K. Wang Y. M. Jo S. H. Chen G. Dresselhaus M. S. Ren Z. F. 2006 Superplastic carbon nanotubes- conditions have been discovered that allow extensive deformation of rigid singlewalled nanotubes. Nature,439 281 - 15.
Hull D. Clyne T. W. 1996 An Introduction to Composite Materials (Second edition). Cambridge University Press, 0521388554, The Edinburgh Building, Cambridge CB2 2RU, UK. - 16.
Japanese Industrial Standards (JIS). 1995 R 1607. - 17.
Kita J. Suemasu H. Davies I. J. Koda S. Itatani K. 2010 Fabrication of silicon carbide composites with carbon nanofiber addition and their fracture toughness. Journal of Materials Science,45 6052 6058 - 18.
Liu J. Rinzler A. G. Dai H. Hafner J. H. Bradley R. K. Boul P. J. Lu A. Iverson T. Shelimov K. Huffman C. B. Rodriguez-Macias F. Shon Y. S. Lee T. R. Colbert D. T. Smalley R. E. 1998 Fullerene pipes. Science,280 1253 1256 - 19.
Ma R. Z. Wu J. Wei B. Q. Liang J. Wu D. H. 1998 Processing and properties of carbon nanotubes-nano-SiC ceramic. Journal of Materials Science,33 5243 5246 - 20.
Miyahara N. Yamaishi K. Mutoh Y. Uematsu K. Inoue M. 1994 Effects of grain size on strength and fracture toughness in alumina, JSME International journal37 231 237 - 21.
Mukerji J. 1993 Ceramic matrix composites. Defence Science Journal,43 385 395 - 22.
Omori M. 2000 Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS). Materials Science and Engineering A,287 183 188 - 23.
Peigney A. 2003 Composite materials: tougher ceramics with nanotubes. Nature Materials,2 15 16 - 24.
Peigney A. Flahaut E. Laurent Ch. Chastel F. Rousset A. 2002 Aligned carbon nanotubes in ceramics-matrix nanocomposites prepared by high-temperature extrusion. Chemical Physics Letters,352 20 25 - 25.
Peng B. Locascio M. Zapol P. Li S. Y. Mielke S. L. Schatz G. C. Espinosa H. D. 2008 Measurements of near-ultimate strength for multiwalled carbon nanotubes and irradiation-induced crosslinking improvements. Nature Nanotechnology,3 626 631 - 26.
Rice R. W. 1996 Grain size and porosity dependence of ceramic fracture energy and toughness at 22°C, Journal of Materials Science,31 1969 1983 - 27.
Sader J. E. Chon J. W. M. Mulvaney P. 1999 Calibration of rectangular atomic force microscope cantilevers. Review of Scientific Instruments,70 3967 3969 - 28.
Sader J. E. Larson I. Mulvaney P. White L. R. 1995 Method for the calibration of atomic force microscope cantilevers. Review of Scientific Instruments,66 3789 3798 - 29.
Sheldon B. W. Curtin W. A. 2004 Nanoceramic composites: tough to test. Nature Materials,3 505 506 - 30.
Sun L. Gao L. Li X. 2002 Colloidal processing of carbon nanotube/alumina composites. Chemistry of Materials,14 5169 5172 - 31.
Sun J. Gao L. Xihai Jin. X. (2005 2005 Reinforcement of alumina matrix with multi-walled carbon nanotubes. Ceramics International,31 893 896 - 32.
Treacy M. M. J. Ebbesen T. W. Gibson J. M. 1996 Exceptionally high Young’s modulus observed for individual carbon nanotubes. Nature,381 678 680 - 33.
Wang X. Padture N. P. Tanaka H. 2004 Contact-damage-resistant ceramic/single-wall carbon nanotubes and ceramic/graphite composites. Nature Materials,3 539 544 - 34.
Yamamoto G. Omori M. Yokomizo K. Hashida T. Adachi K. 2008 Structural characterization and frictional properties of carbon nanotube/alumina composites prepared by precursor method. Materials Science and Engineering B,148 265 269 - 35.
Yamamoto G. Omori M. Hashida T. Kimura H. 2008 A novel structure for carbon nanotube reinforced alumina composites with improved mechanical properties. Nanotechnology,19 article315708 - 36.
Yamamoto G. Omori M. Yokomizo K. Hashida T. 2008 Mechanical properties and structural characterization of carbon nanotube/alumina composites prepared by precursor method. Diamond and Related Materials,17 1554 1557 - 37.
Yamamoto G. Suk J. W. An J. Piner R. D. Hashida T. Takagi T. Ruoff R. S. 2010 The influence of nanoscale defects on the fracture of multi-walled carbon nanotubes under tensile loading. Diamond and Related Materials,19 748 751 - 38.
Yamamoto G. Shirasu K. Hashida T. Takagi T. Suk J. W. An J. Piner R. D. Ruoff R. S. 2011 Nanotube fracture during the failure of carbon nanotube/alumina composites. Carbon,49 3709 3716 - 39.
Yao W. Liu J. Holland T. B. Huang L. Xiong Y. Schoenung J. M. Mukherjee A. K. 2011 Grain size dependence of fracture toughness for fine grained alumina, Scripta Materialia,65 143 146 - 40.
Yu M. F. Lourie O. Dyer M. J. Moloni K. Kelly T. F. Ruoff R. S. 2000 Strength and breaking mechanism of multiwalled carbon nanotubes under tensile load. Science,287 637 640 - 41.
Zhan G. D. Kuntz J. D. Wan J. Mukherjee A. K. 2003 Single-wall carbon nanotubes as attractive toughening agents in alumina-based nanocomposites. Nature Materials,2 38 42