Magnesium in Synthesis of Porous and Biofunctionalized Metallic Materials
Magnesium particles are used in metallurgic routes, where it can be total or partially evaporated creating pores for ingrowth bone tissue. This book chapter contains the latest findings on the microstructural physical and mechanical properties of β-Ti alloys with Mg additions designed and obtained by the authors. As well as the main new techniques used to fabricate Ti-Mg alloys. An especial emphasis on the microstructure-properties relationship was made to assist on the guide for future efforts of the scientific community towards developing more efficient biomaterials. The β % were related to the low elastic modulus which were in the range of 31–49 GPa close to cortical bone and hardness close to commercial Ti grade 2. The compressive strength was greater than the value of cortical bone. Pore size were in the range of 5–100 μm depending on the sintering temperature, with higher wettability the samples with more porosity. These findings were promising to application of β titanium alloys containing Mg for orthopedic application.
Part of the book: Current Trends in Magnesium (Mg) Research