Ferroelectric crystals are important materials in many kinds of applications. Since the invention of so called quasi-phase matching technique, periodically domain-inverted ferroelectrics crystals with modulated second order nonlinear susceptibility has received much attention owing to its outstanding nonlinear optical properties (Magel et al.,1990; Xu et al.,1993; Zheng et al.,1998). In periodically domain-inverted ferroelectrics crystals, besides the nonlinear optical coefficients, other third-rank tensors, such as the electro-optic (EO) coefficient, are also modulated periodically because of the periodically reversed ferroelectric domains. Since the theoretical research on EO effect in PPLN was proposed by Y.Q Lu et al (Lu et al.,2000), this periodically modulation of the EO coefficient has given birth to some novel essential applications, especially when the voltage is applied along the transverse direction of the crystal. In this chapter, current research of transverse EO-based PPLN applications, such as tunable wavelength filter, polarization controller, electro-optical switch and laser Q-switch in periodically poled lithium niobate are summarized.
2. Solc-type wavelength filter
Tunable optical filters play an important role in optical signal processing and optical communication. In particular, a narrow flat-top bandpass filter, which not only enables a particular wavelength channel to pass through but also significant to keep signal stable, as well as a multiple-wavelength filter, which enables several wavelengths to pass through together at the same time, are widely needed in wavelength-division multiplexing systems. In this section, we present our research on tunable filter with single-wavelength, multiple-wavelength and flat-top passband based on PPLN crystal. Photovoltaic effect in PPLN is also investigated and based on which a tunable filter by use of UV light is demonstrated. Moreover, the latest researches on solc-type filter based on Ti:PPLN channel waveguide are also presented in the end of this section.
When an electric field is applied along the Y axis of a crystal with 3m symmetry, the new index ellipsoid deforms to make its principal axes rotated at an angle θ about the x axis with respect to the unperturbed principal axes. Since θ is proportional to the product of the electric field and the electro-optic coefficient, when an uniformed electric field applying along the Y axis of the crystal, the rotation angle of the original domain is opposite to that of the inverted domain because of the reversal of the spontaneous polarization(Lu et al.,2000). Thus, in a periodically domain inverted crystal with a uniformed electric field applied along the Y axis, a structure with alternating left and right rotation angle θ will be formed due to the periodic EO coefficient. This structure is similar to the well known folded Solc filter structure with alternating azimuth angles of the crystal axes. So we call it Solc layered structure.
To have an insight into the filter process, polarization coupled-mode theory is established to track the polarization state of light propagation along PPLN. In PPLN the coupled-wave equations of the ordinary and extraordinary waves are:
So the solution of coupled-mode equation (1) is:
where s is given by
2.2. Device of tunable Solc-type wavelength filter
2.2.1. Tunable single-wavelength filter
The first observation of a Solc filter based on PPLN operating in the optical communication wavelength range was proposed by our group in 2003 ( Chen et al., 2003 ). Similar to the traditional folded type Solc filter, a PPLN crystal is placed between two crossed polarizer. This sample is with dimensions of 28 mm×5 mm×0.5 mm consists of four gratings with periods from 20.2 to 20.8μm and a width of 1 mm. A measured transmission power versus wavelength for 20.6μm and 20.8μm period is shown in Fig. 3, from which a typical transmission spectrum of traditional Solc-type filter can be seen. The amplitude modulation of the transmission power by applying an electric voltage along the Y axis of the PPLN is also observed and the result is shown in Fig.4. In above discussion, we have known that the fundamental wavelength is determined by equation
The experiment result on wavelength modulation is showed in Fig.5, where -0.415nm/0C tuning rate is achieved. Wavelength tuning by temperature is interesting in dense wavelength division multiplexer optical fiber communication systems, where it can be employed as a wavelength-tunable filter for all-optical wavelength routing.
2.2.2. Tunable multiple-wavelength filter
In previous section, we have discussed that the central wavelength of a PPLN Solc-type filter is determined by the period of the domain inversion and the ordinary and extraordinary refractive indices. Since the indices are temperature dependent, the central wavelength of such filter can be shifted by changing the working temperature of the whole PPLN. If we apply a temperature distribution along the PPLN through a local-temperature-control technique to control and reshape the second harmonic (SH) curve, then the PPLN will be divided into several temperature sections and each section will give a central wavelength determined by its local temperature. By combining the contributions from all the temperature sections in the PPLN, a multi-wavelength filter can be realized. By properly controlling the temperature of each section, we can construct a tunable multi-wavelength filter for any wavelength according to the practical needs of different applications(Wang et al.,2007).
The multiple-wavelength filter can also been designed by optimizing the sequences of the opposite domains in aperiodic poled lithium niobate (APLN) using simulated annealing (SA) algorithm(Gu et al.,2004). Here, Jones matrix, a 22-matrix method, is employed to track the polarization state of light propagation along APLN (Yariv & Yeh,1984). The sequence of the positive and negative domains is optimized with the target that the transmission of the prescribed wavelengths are equal with maximum values at the same time. Here, we chose the objective function in the SA method as
where the symbol max[…] (min[…]) manifests to take their maximum (minimum) value along all the quantities including into […].
The first experimental observation of narrowband multi-wavelength filters based on aperiodically poled lithium niobate crystals was reported by C. H. Lin et.al(C.H.Lin et.al.,2007 ). In the experiment, they simultaneously transmitted 8 ITU-standard wavelengths through a 5-cm long EO APLN filter with a transmittance of >90% and a bandwidth of ~0.45 nm for each wavelength channel. Moreover，the transmission spectrum of the EO APLN filter can be conveniently tuned by temperature at a rate of ~0.65 nm/0C in the telecom C band.
2.2.3. Flat-top wavelength filter
Generally, the passband of this kind filter is extremely narrow. Tiny shift of the fundamental wavelength because of unstable temperature or any other factors will contribute to great loss. Thereby, a flat-top filter which can avoid the interference of the outside and maintain signal quality is necessary.
To begin with this section, we would like to introduce the spectrum waveform similarity (SWS) rule discovered in PPLN firstly(Liu et al.,2009a). The SWS rule can be described as follows: if the product of the domain N and the rocking angle θ is fixed, the shape of the spectrum waveform remains similar, as N varies. To get a clear picture of this rule, Fig.9 will be helpful. In figure 9, “A” represents the product of the domain N and the rocking angle θ. With “A” fixed at pi/2, the shape of the spectrum waveform remains similar when N is changing, despite the FWHM correspondingly increases. Based on the spectrum waveform similarity (SWS) rule, we come to a conclusion that the shape of the spectrum waveform is determined by the product A. By observing the spectrums at different value of A, our study reveals a critical point (A=2.24) at which the spectrum surprisingly evolved into flat-top type (Fig.10). The 1 dB width of the flat-top waveform can be fitted as follows:
where λ0 is the fundamental wavelength of the filter.
In order to confirm this theoretical discovery about flat-top spectrum in PPLN, further investigation has been performed experimentally(Liu et.al,2009b). The PPLN sample, employed in the experiment, with a dimension of 30(L)×10(W)×0.5(T)mm3 consists of 2857 domains with the period of 21 (μm). In above discussion, we have known the flat-top spectrum requires Nθ=2.24 which is greater than the single wavelength Solc-type filter (2Nθ=л/2). Thereby, as to a given PPLN (N fixed), higher electric field is requested than usual. During the experiment, the transmission of the fundamental wavelength attends to maximum at 3 (kV/cm) (A) and gradually declines when the electric field keeps on arising subsequently. Consistent with the theoretical result, the spectrum evolves into flat-top type with higher electric field at the critical point 4.2 (kV/cm) (B). The corresponding transmission spectrums at A and B are, respectively, shown in Fig.11. A flat-top waveform with 1 (nm) flat-top width is obtained in the experiment.
Interestingly, as to a given PPLN, by extending the external electric field to a higher value, the theoretical results reveal that new critical points of flat-top will be found every 2.4 (kV/cm) electric field. Besides, the width of each flat-top transmission spectrum is proportionally increased with the increment of external electric field. Thereby, tunable passband can be achieved by switching the external electric field between different critical points which is shown in Fig.12.
In this section, both the theory and the experiment show that there is a critical voltage at which a flat-top transmission spectrum can be achieved. To have an insight into the flat-top process, more studies should proceed in future. We believe this phenomenon may be also found in other materials and structures similar to PPLN. As the flat-top spectrum is able to keep signal stable, this finding may improve the possibility of the practical application of Solc-type PPLN filter in optical networks and optical signal processing in future.
2.2.4. Photovoltaic effect in PPLN crystal
In the experiments of above sections, we also found that, without field applied, the device also has the function of Solc filter, which shows disagreement with the theory. Our study reveals that the photovoltaic effect (PVE) plays an essential role in the performance of non-field applied PPLN Solc filter(Chen et al.,2006). The PVE effect sometimes can not be neglected, especially in electric-optic devices.
Our theoretical analysis shows that only the electric field E in the Y direction can enable the Solc filter. If the input polarizer is put in the Y direction, there will be a field formed in the Y direction that will make the device work as a Solc filter; Whereas, if the input polarizer is set in the Z direction, no field will cause the half-wave plate rocking and the PPLN will have no filter function. By observing the spectrums with two types of setups shown in Fig.13, the theoretical analysis is experimentally confirmed in Fig.14.
On the other hand, this PVE effect inspires us a new thought to build the light controlled optical devices or to measure the PVE coefficients (Shi et al., 2006).
Fig. 15 shows measured output power against wavelength for the PPLN of period 20.8μm with and without the illumination of the UV light, respectively. The UV light intensity is about 143mw/cm2. The passband of the filter moves from 1531.9nm to 1529.1nm.4). It costs several seconds until spectrum of the filter becomes stable. However, the peak value and the shape of the pass band are unchanged. It means the Y field of the PVE is not changed. This suggests that no Y direction field is induced when a non-polarized light propagates in Z direction.
2.2.5. Solc-type filter in Ti:PPLN channel waveguide
In this section, we will present the latest research on solc-type filter based on Ti:PPLN channel waveguide which has a significant advantage of low driven voltage. The filtering mechanism of this kind filter is same to the filter based on PPLN crystal introduced above.
In this kind filter, the gap between the electrodes can be as short as (m) level, therefore, only several voltages are enough for filtering or switching a light(Lee et al.,2007). The experimental setup to perform the wavelength filtering based on the Ti:PPLN channel waveguide is shown in Fig.16. An optical signal from a wavelength-swept fiber laser based on a semiconductor optical amplifier and a Fabry–Perot tunable filter was collimated and end-fire coupled into the Ti:PPLN waveguide, which is placed between two crossed polarizer by a 10х objective lens. The polarization direction of input beam was adjusted parallel to the Y axis of the Ti:PPLN device, and the output signal was observed by an optical spectrum analyzer. The filtering results of one-mode guiding condition and two-mode guiding condition are shown in Fig. 17. In one-mode condition, the measured FWHM of the filter was about 0.21 nm, and in two-mode condition, the origin of one peak is the TEM00-like mode, and the other is the TEM01-like mode. The wavelength difference of the two peaks is about 0.8 nm.
Similar to the light controlled optical solc-type filter by use of PVE effect in PPLN crystal, Y.L. Lee et.al demonstrate a tunable all-optical solc-type wavelength filter based on Ti:PPLN channel waveguide(Lee et al.,2008). Fig.18 shows the centre wavelength of the filter as a function of the UV illumination intensity. As the intensity increases, the centre wavelength of the filter shifts to a shorter wavelength.
The measured wavelength tuning rate of the filter was about -26.42 nm/W cm-2 which shows more slant than that of a bulk PPLN Solc-type filter (-19.23 nm/W cm-2) (Shi et al.,2006). The right axis of Fig.18 indicates the amount of change in the refractive index difference between no and ne as a function of UV intensity. These results indicate that a Ti:PPLN solc-type filter gives a wider wavelength tuning range than that of a bulk PPLN solc-type filter.
3. Polarization controller
In this section, we will introduce our study on precise linear polarization-state controller based on PPLN (Liu et al., 2009c), which was also inspired by Y.Q. Lu et.al.’s study (Lu et al.,2000), where they theoretically proposed the electro-optical effect in PPLN. The working mechanism is the same with the Solc-type filter. It is known that with respect to the fundamental wavelength of solc-type filter, each domain serves as a half-wave plate. Therefore, after passing through the stack of half-wave plates, the optical plane of polarization of the fundamental wavelength rotates continually and emerges finally at an angle of 2Nθ. As θ is controlled with external electric field, the final rotation angle is as well dominated by the electric field. Consequently, an EO linear polarization-state controller for the fundamental wavelength can be realized. In the following discussion, we use another name of “operating wavelength” to represent the fundamental wavelength which is more appropriate than the latter.
As for the PPLN sample employed in the experiment, the operating wavelength is found out to be λ=1543.47nm. Then, experimental measurement of the state of polarization of the output light (λ=1543.47nm) is shown on a Poincare sphere in Fig.19 when varying the applied electric field. The experiment shows the state of polarization remains on the equatorial plane when changing the electric field which indicates the output light remains linear state of polarization. The corresponding rotation angle at each electric field is shown in Fig.20, where the electric field intensity is tuned from 0 to 3 (kV/cm), with the step of 0.1 (kV/cm) each time and the rotation angle linearly varies between 0-100 degrees.
To obtain higher precision, we reduce the electric field step to 0.01 (kV/cm) and 0.001 (kV/cm), respectively. Higher precision of 0.4 degree and 0.04 degree is finally achieved, limited by the accuracy of the measurement system, which are shown in Fig.21. Moreover, the operating wavelength can be tuned to a series of different wavelengths by changing the temperature.
The device operating as a precise linear polarization-state controller may find many applications where high precision control of linear polarization-state light is requested ranging from polarization analysis to monitoring of network performance, material birefringence, and measurement of polarization mode dispersion, swept-wavelength measurement, medical imaging and fiber sensor systems.
4. Electro-optical switch
High speed optical switch is one of the key components in optical communication. In this section, with the same experimental setup of solc-type filter, we change to with focus on the application of a precise EO switch. The first observation of an EO switch in PPLN is shown in Fig.22, where high extinction ratio with 43 dB is gained in the experiment.
However, an obstacle to the application of such switch is the narrowband and wavelength limit. Inspired by the discovery of flat-top spectrum in PPLN in 2.2.3 section, we further find out a critical electric field at which the spectrum evolves into broadband. Fig.23 shows the flat-top width and the critical electric field as a function of the domain number. Considering a given PPLN with 60 domains, the transmission spectrum at the critical electric field is shown in Fig.24, which has a broadband with 50 nm flat-top width. The broadband here can efficiently extend the switch’s operating wavelengths. However, although sharp increase of the flat-top width can be learned from Fig.23 (a), higher width than 50 nm is impossible in practice, because the corresponding critical electric field will synchronously rapidly rise in Fig.23 (b), which will damage the PPLN.
5. Laser Q-switch
A class of Q-switched lasers employs a fast intra-cavity polarization rotator for switching the laser polarization between high- and low-loss laser modes. The two loss modes can be established by using a polarization-dependent loss element such as EO PPLN crystal. In this section, we present another significant application on laser Q switch laser based on EO PPLN crystal, which were proposed by Y. H. Chen et.al ( Chen & Huang,2003 ) and Y. Y. Lin et.al ( Lin et al.,2007 ).
In the year of 2003, Y. H. Chen et.al successfully employed a PPLN Pockels cell as a laser Q-switch with a switching voltage as low as ~100 V( Chen & Huang, 2003 ). The PPLN Pockels cell consists of a quarter-wave plate and an EO PPLN crystal having the same crystal orientation as a typical PPLN wavelength converter.
Fig. 25 shows the continuous-wave (CW) performance of the Nd:YVO4 laser with and without a 100-V voltage applied to the EO PPLN crystal. Without the applied voltage, the Nd:YVO4 laser had a CW threshold of 400-mW pump power, attributable to the high output coupling loss (13%). With a 100-V voltage applied to the EO PPLN crystal, the laser’s CW threshold was increased to ~1.4-W pump power as expected from the polarization rotation effect.
To show laser Q-switching operation, the EO PPLN is drove by using a 7-kHz, 100-V voltage pulser with a 300-ns pulse width. At 1.2-W pump power, 60-mW average power or 0.74-kW peak power with 8.6-mJ pulse energy in an 11.6-ns laser pulse width is measured in the experiment (Fig.26).
Despite the low switching voltage and excellent integrated QPM performance, the PPLN Pockels cell was sensitive to temperature and generated appreciable green-laser power at 532 nm in the Nd:YVO4 laser, both due to the QPM structure in the PPLN. It is desirable to have a “green-free” and temperature-insensitive laser Q-switch that still retains the advantages of low switching voltage and excellent integrated QPM performance.
In the year of 2007, Y. Y. Lin et.al reported such a laser Q-switch which had overcome the previous disadvantages using a novel EO PPLN Bragg modulator, producing 7.8 ns, 201 μJ pulses at a 10 kHz repetition rate when pumped by a 19.35 W diode laser at 808 nm(Y.Y. Lin et al.,2007 ). The schematic setups of two different kind laser Q-switches are shown in Fig.27.
Figure 28 shows the measured Q-switched pulse energy versus the diode pump power of the second kind laser Q-switch. At 19.35 W pump power, the Q-switched output pulse at 1064 nm has 201μJ energy and 7.8 ns width, corresponding to a peak power of 26 kW. The error bar in the plot shows that the pulse-to-pulse energy jitter was less than 5% over the range of our measurement. The inset shows the temporal profile of the Q-switched output pulse.
In the experiment, no noticeable change was observed on the laser performance when the EO PPLN grating was heated from room temperature to 180 C; In addition, no green-laser power produced from the non-phase-matched second-harmonic generation in the EO PPLN grating was observed in the experiment as well. The experiment successfully confirmed the advantages of this kind Q-switch.
In this chapter, we have reviewed essential applications by use of polarization coupling in periodically poled lithium niobate during the past five years. Because of the outstanding properties of PPLN, we believe that PPLN will remain to be an important contemporary realm of research.
Chen X. F. Shi J. H. Chen Y. P. Zhu Y. M. Xia Y. X. Chen Y. L. 2003Electro-optic Solc-type wavelength filter in periodically poled lithium niobate, Opt. Lett. 28.
Chen Y. H. Huang Y. C. 2003Actively Q-switched Nd:YVO4 laser using an electro-optic periodically poled lithium niobate crystal as a laser Q-switch, Opt. Lett. 28 1460 1462.
Chen L. J. Shi J. H. Chen X. F. Xia Y. X. 2006Photovoltaic effect in a periodically poled lithium niobate Solc-type wavelength filter, Appl. Phys. Lett. 88, 121118.
Gu X. Chen X. F. Chen Y. P. Zeng X. L. Xia Y. X. Chen Y. L. 2004Narrowband multiple wavelengths filter in aperiodic optical superlattice, Opt. Commun. 237 53 58.
Jundt D. H. 1997Temperature-dependent Sellmeier equation for the index of refraction, no, in congruente lithium niobate,” Opt. Lett. 22 1553 1555.
Lu Y. Q. Wan Z. L. Wang Q. Xi Y. X. Ming N. B. 2000Electro-optic effect of periodically poled optical superlattice LiNbO3 and its applications, Appl. Phys. Lett. 77, 3719.
Lin C. H. Chen Y. H. Lin S. W. Chang C. L. Huang Y. C. Chang J. Y. 2007Electro-optic narrowband multi-wavelength filter in aperiodically poled lithium niobate, Opt. Exp. 15 9859 986.
Lee Y. L. Yu N. E. Kee C. Ko D. Lee J. Yu B. Shin W. Eom T. J. Noh Y. 2007Wavelength filtering characteristics of Solc filter based on Ti:PPLN channel waveguide, Opt. Lett. 32 2813 2815.
Lee Y. L. Yu N. E. Kee C.-S. Ko D.-K. Noh Y.-C. Yu B.-A. Shin W. Eom T.-J. Oh K. Lee J. 2008All-optical wavelength tuning in Solc filter based on Ti:PPLN waveguide, Electron. Lett. 44 30 32.
Lin Y. Y. Lin S. T. Chang G. W. Chiang A. C. Huang Y. C. Chen Y. H. 2007Electro-optic periodically poled lithium niobate Bragg modulator as a laser Q-switch, Opt. Lett. 32 545 547.
Liu K. Shi J. H. Zhou Z. E. Chen X. F. 2009aElectro-optic Solc-type flat-top bandpass filter based on periodically poled lithium niobate, Opt. Commun. 282 1207 1211.
Liu K. Shi J. H. Chen X. F. 2009bElectro-optical flat-top bandpass Solc-type filter in periodically poled lithium niobate. Opt. Lett. 34, 7.
Liu K. Shi J. H. Chen X. F. 2009cLinear polarization-state generator with high precision in periodically poled lithium niobate, Appl. Phys. Lett., 94, 101106.
Magel G. A. Fejer M. M. Byer R. L. 1990Quasi-phase-matched second-harmonic generation of blue light in periodically poled LiNbO3, Appl. Phys. Lett. 56 108 110.
Shi J. H. Wang J. H. Chen L. J. Chen X. F. Xia Y. X. 2006Tunable Šolc-type filter in periodically poled LiNbO3 by UV-light illumination, Opt. Exp. 14, 6279.
Wang J. H. Shi J. H. Zhou Z. E. Chen X. F. 2007Tunable multi-wavelength filter in periodically poled LiNbO3 by a local-temperature-control technique, Opt. Exp. 15,1561.
Xu C. Q. Okayama H. Kawahara M. 19931. 5μm band efficient broadband wavelength conversion by difference frequency generation in a periodically domain-inverted LiNbO3 channel waveguide, Appl. Phys. Lett. 63 3559 3561.
Yariv A. Yeh P. 1984 Optical Waves in Crystal: Propagation and Control of Laser Radiation(Wiley, NewYork).
Zheng J. J. Lu Y. Q. Luo G. P. Ma J. Lu Y. L. Ming N. B. He J. L. Xu Z. Y. 1998Visible dual-wavelength light generation in optical superlattice through Er:LiNbO3 unconversion and quasi-phase-matched frequency doubling, Appl. Phys. Lett. 72 1808 1810.
Zhu Y. M. Chen X. F. Shi J. H. Chen Y. P. Xia Y. X. Chen Y. L. 2003 Wide-range tunable wavelength filter in periodically poled lithium niobate, Opt. Comm., 228 139 143.