Crystallite sizes of Fe3O4 and HA in Fe3O4/HA nanocomposites.
Hydroxyapatite (Ca10(PO4)6(OH)2, HA), which is a calcium phosphate ceramic, has been widely used as a biomaterial in various applications (e.g., artificial bone and dental root, cosmetic foundation, etc.) because of its high biocompatibility and chemical stability. Moreover, many attempts are being made to give new functions to HA by incorporating effective components into a HA matrix. In particular, magnetite (Fe3O4)-incorporated HA (Fe3O4/HA) nanocomposites have attracted much attention as a promising material for hyperthermia therapy of malignant bone tumor [1–4]. Recently, Fe3O4/HA composites have also been used as adsorbents [5–7] and catalysts [8,9].
Fe3O4/HA composites can be synthesized conventionally by mixing HA powder with Fe3O4 nanoparticles which are prepared individually [1–3,5–10]. The conventional synthesis methods have disadvantages: reaction time required for completing the formation of HA and Fe3O4 is relatively long, subsequent heat treatments for long periods of time are required for aging and crystallization. Thus, the synthesis of Fe3O4/HA composites generally consist of multi-step processes. Therefore, a simple method which can provide Fe3O4/HA composites rapidly is needed to be developed.
In this chapter, a mechanochemical method for the simple synthesis of Fe3O4/HA nanocomposites is presented. In this method, superparamagnetic Fe3O4 nanoparticles are first prepared mechanochemically from ferric hydroxide , and then the mechanochemical synthesis of HA from dicalcium phosphate dihydrate (CaHPO4 2H2O) and calcium carbonate (CaCO3, calcite) is performed [12–14], followed by the aging for a short period of time. These mechanochemical treatments are sequentially performed in a single horizontal tumbling ball mill at room temperature under wet conditions. The wet mechanochemical process can also contribute to the distribution of Fe3O4 nanoparticles in the HA matrix, which can result in a good hyperthermia property. In addition, the use of horizontal tumbling ball mills is reasonable for the synthesis of Fe3O4/HA nanocomposites because the device structure is simple, the handling is easy, the energy consumption is relatively low, and the scale-up is easy . The influence of conditions on the formation of Fe3O4/HA nanocomposites was investigated and the hyperthermia property was examined. The details are described below.
2. Mechanochemical synthesis of hydroxyapatite nanoparticles
First of all, the synthesis of HA nanoparticles containing no Fe3O4 nanoparticles was investigated to optimize the synthesis process of Fe3O4/HA nanocomposites. In all the experiments presented in this chapter, the chemicals of analytical grade were used as received without further purification. Typically, 30 mmol of CaHPO4 2H2O and 20 mmol of CaCO3, corresponding to the stoichiometric molar ratio in the formation reaction of HA expressed by Equation (1) , were added to 60 ml of deionized and deoxygenated water.
The resulting suspension was subjected to a mechanochemical treatment using a horizontal tumbling ball mill, as illustrated in Figure 1. The suspension was placed in a Teflon-lined milling pot with an inner diameter of 90 mm and a capacity of 500 ml. Zirconia balls with a diameter of 3 mm were used as the milling media; the charged volume of the balls (including voids among the balls) was 40% of the pot capacity. The wet milling was performed at room temperature in air atmosphere under atmospheric pressure for a designated period of time. The rotational speed was 140 rpm, corresponding to the ideal critical rotational speed. After milling, the precipitate was isolated from the suspension by centrifugation, washed with acetone, and dried at room temperature in air. As a control experiment without milling, the starting suspension was vigorously stirred at room temperature for 24 h.
The samples obtained under various conditions were characterized according to standard methods. The powder X-ray diffraction (XRD) pattern of samples was obtained by an X-ray diffractometer (RINT-1500, Rigaku; CuKα radiation, 40 kV, 80 mA, 2θ=5°–50°, scanning rate: 1.0°/min). Figure 2 shows the XRD pattern of samples obtained in different milling times. As the milling time increased, the diffractions indicating the presence of CaHPO4 2H2O and CaCO3 decreased. Simultaneously, the diffractions indicating HA appeared. In particular, a drastic change was observed between 1 h and 3 h. On the contrary, when stirred for 24 h without milling, the XRD pattern (not shown) hardly changed from the beginning, which was almost the same as that before milling as shown in Figure 2a. These results indicate that the milling promoted the solid phase reaction expressed by Equation (1). However, after milling for 12 h, the XRD pattern was almost the same and the diffraction at 2θ=29.4°, indicating the presence of CaCO3, still remained even in 24 h.
The differential scanning calorimetry (DSC) was performed using a thermal analyzer (SDT2960, TA Instrument) with an argon flow rate of 100 ml/min. The temperature was raised from ambient temperature to 900 °C at a rate of 20°C/min. Figure 3 shows the results of DSC analysis for the raw materials and the samples. In the sample obtained in 1 h (Figure 3d), the endothermic peaks were clearly observed at around 200°C and 750°C, which resulted from the elimination of water of crystallization in CaHPO4 2H2O and the thermal decomposition of CaHPO4 2H2O and CaCO3. Although the peaks relating to CaHPO4 2H2O disappeared as the milling time, the peak resulted from the thermal decomposition of CaCO3 remained even in 12 h. Accordingly, it was found that the milling was not sufficient to complete the formation reaction of HA.
The morphology of samples was observed by field emission scanning electron microscopy (FE-SEM; JSM-6700F, JEOL). Figure 4 shows typical SEM images of samples. In a milling time of 1 h, coarse particles coated with fine particles of about 100 nm were observed. From the particle size analysis of CaHPO4 2H2O and CaCO3 by the laser diffraction/scattering method (SALD-7100, Shimadzu), the median sizes were determined to be 16.2 µm for CaHPO4 2H2O and 2.0 µm for CaCO3. In general, horizontal tumbling ball mills are difficult to produce nanoparticles for short milling times. Therefore, coarse and fine particles could be the raw materials and HA, respectively. As the milling time increased, coarse particles disappeared and the number of HA nanoparticles increased. However, even after 12 h, a little number of coarse particles was found.
In order to complete the formation reaction of HA, the heat treatment (aging) was performed after milling. For investigating the effect of heating on the formation of HA, the un-milled suspension of CaHPO4 2H2O and CaCO3 was heated under various conditions of temperature and time. Figures 5, 6, and 7 show the XRD patterns of samples obtained without milling after heating at 40, 60, and 80°C, respectively. When the suspension was heated at 40°C, the formation reaction of HA hardly took place. As increasing in the temperature, the reaction was promoted and could complete at 80°C in 8 h. Thus, when without milling, higher heating temperatures and longer heating times are needed for the formation of HA.
Next, the effect of milling of the suspension before heating on the formation of HA was investigated. Figures 8–14 show the XRD patterns of samples obtained under various conditions of milling time, heating temperature, and heating time. It was found that longer milling times, higher heating temperatures, and longer heating times promoted the formation reaction of HA. In particular, as shown in Figure 10c, when the heating was performed at 80°C, only the milling for 1 h and the following heating for 1 h provided a single phase of HA. The SEM images of samples obtained by milling for different times under constant heating conditions of 80°C and 1 h are shown in Figure 15. When heating at 80°C for 1 h, a typical morphology of HA was observed regardless of the milling time. However, the particle size intended to decrease as the milling time increased. Consequently, the combination of milling and heating of the suspension of CaHPO4 2H2O and CaCO3 can produce efficiently HA for short periods of time.
3. Synthesis and hyperthermia property of magnetite/hydroxyapatite nanocomposites
In the synthesis of Fe3O4/HA nanocomposites, first a suspension of superparamagnetic Fe3O4 nanoparticles was prepared according to a mechanochemical method reported in elsewhere . This method provides Fe3O4 from ferric hydroxide (goethite) in the absence of a reducing agent; goethite is reduced to ferrous hydroxide by mechanochemical effects and the solid phase reaction between ferrous hydroxide and goethite generates Fe3O4 . Subsequently, HA nanoparticles were synthesized in the suspension of Fe3O4 nanoparticles in the same container by the mechanochemical method mentioned above.
4.5 mmol of ferric chloride hexahydrate (FeCl3 6H2O) was dissolved in 60 ml of deionized and deoxygenated water. To precipitate amorphous ferric hydroxides (mostly, goethite), a proper amount of 1.0 M sodium hydroxide (NaOH) solution was dropped into the solution which was magnetically stirred under a continuous flow of argon at room temperature. The pH was adjusted to higher than 13. A brown suspension thus prepared was placed in a gas-tight milling pot (inner diameter 90 mm, capacity 500 ml) made of 18%Cr–8%Ni stainless steel. Stainless steel balls (diameter 3.2 mm) were used as the milling media. The charged volume including the voids among the balls was about 40% of the pot capacity. The pot was purged of air, filled with argon, and sealed. The milling was performed at room temperature for 11 h. The rotational speed was 140 rpm, corresponding to the ideal critical rotational speed.
The XRD pattern of Fe3O4 nanoparticles thus prepared is shown in Figure 16. The Fe3O4 nanoparticles had a high crystallinity and an average crystallite size of 11.7 nm which was calculated from the full width at half-maximum (FWHM) of the Fe3O4 (311) diffraction peak at 2θ=35.5° using Scherrer’s formula. The lattice constant was determined to be 8.387 Å from several diffraction angles showing high intensity peaks, which was close to the standard value of Fe3O4 (8.396 Å) as compared to that of maghemite (8.345 Å). Figure 16 also shows that no reflections indicating formation of other compounds were observed. This indicates the Fe3O4 nanoparticles were high purity.
As shown in Figure 17, the SEM image indicated that the Fe3O4 nanoparticles had a diameter of approximately 10–20 nm, which almost agreed with the average crystallite size (11.7 nm). The hydrodynamic size (number basis) was measured by dynamic light scattering (DLS; Zetasizer Nano ZS, Malvern Instruments) for a dispersion, as shown in Figure 18. The median diameter was determined to be 16.4 nm from the size distribution, which was also near the average crystallite size. These results reveal that the Fe3O4 nanoparticles have a single-crystal structure.
The magnetic property (magnetization-magnetic field hysteretic cycle) was analyzed using a superconducting quantum interference device (SQUID) magnetometer (Quantum Design model MPMS) at room temperature in the rage of magnetic field between –10 kOe and 10 kOe. Figure 19 shows the magnetization-magnetic field curve. The Fe3O4 nanoparticles had a low coercivity (4 Oe), showing superparamagnetism. The saturation magnetization (78 emu/g) was a little lower than that of the corresponding bulk (=92 emu/g) because of the smaller size .
After the suspension of Fe3O4 nanoparticles was prepared, the milling pot was opened, and then predetermined amounts of CaHPO4 2H2O and CaCO3 were added to the suspension. Their amounts were adjusted so that the mass concentration of Fe3O4 nanoparticles in the Fe3O4/HA nanocomposite was 10, 20, and 30 mass%. In order to prevent the oxidation of Fe3O4 during milling, the pot was purged of air, filled with argon, and sealed prior to milling. The suspension was milled at a rotational speed of 140 rpm for 1 h at room temperature, followed by the heating at 80°C for 1 h.
Figure 20 shows the XRD pattern of Fe3O4/HA nanocomposites with different Fe3O4 concentrations. It was confirmed that the nanocomposites consisted of Fe3O4 and HA having no by-products regardless of the Fe3O4 concentration. The average crystallite sizes of Fe3O4 and HA were calculated from the FWHM of the Fe3O4 (311) plane at 2θ=35.5° and the HA (002) plane at 2θ=25.9°, respectively, using Scherrer’s formula, and listed in Table 1. The average crystallite sizes of Fe3O4 and HA were almost constant regardless of the concentration of Fe3O4 in the Fe3O4/HA nanocomposites.
|10 mass%||11.3 nm||20.3 nm|
|20 mass%||12.8 nm||18.8 nm|
|30 mass%||9.8 nm||17.8 nm|
Figure 21 shows the SEM image of nanocomposite containing 30 mass% Fe3O4 as an example. The Fe3O4 nanoparticles with a diameter of about 20 nm were distributed homogeneously in the HA matrix without forming large aggregates. It was confirmed that nanometer-sized Fe3O4/HA composite particles were successfully synthesized.
The magnetic hyperthermia property was evaluated using an apparatus reported in elsewhere . A proper amount of Fe3O4/HA nanocomposite powder sample was placed in a polystyrene tube with a diameter of 16 mm, and packed by tapping the tube. The packing volume was constant at 0.8 cm3 regardless of the Fe3O4 concentration. The temperature increase was measured in an AC-magnetic field using an optical fiber thermometer. The frequency and amplitude of the AC-magnetic field were 600 kHz and 2.9 kA/m, respectively. Figure 22 shows the temperature increase for the nanocomposites in the AC-magnetic field. As the Fe3O4 concentration increased, the temperature increased more rapidly. When the Fe3O4 concentration was 30 mass%, the temperature increase of 40°C was achieved only after about 20 sec. This result supports that the Fe3O4/HA nanocomposites synthesized by this mechanochemical process exhibit a good hyperthermia property [1–4].
A mechanochemical method for the simple synthesis of Fe3O4/HA nanocomposites has been developed, in which superparamagnetic Fe3O4 nanoparticles and HA nanoparticles are sequentially prepared in a single horizontal tumbling ball mill at room temperature under wet conditions. First, the synthesis process of HA (containing no Fe3O4) was optimized. The obtained HA samples were characterized by XRD, DSC, and SEM. The influence of conditions on the formation of HA nanoparticles was investigated. Mechanochemical effects induced during wet milling promoted the reactions between CaHPO4 2H2O and CaCO3 forming HA even at room temperature. The combination of milling and heating (aging) of the suspension of CaHPO4 2H2O and CaCO3 can produce efficiently HA for short periods of time. The optimum operating conditions in the synthesis of HA were determined as follows: a rotational speed of 140 rpm, a milling time of 1 h, an aging temperature of 80°C, and an aging time of 1 h. Next, the synthesis of Fe3O4/HA nanocomposites was investigated. The mechanochemically synthesized Fe3O4 nanoparticles, of which the median diameter was 16 nm, had a high crystallinity and a high saturation magnetization of 78 emu/g, and showed superparamagnetism. The wet mechanochemical process also contributed to the distribution of Fe3O4 nanoparticles in the HA matrix. The Fe3O4/HA nanocomposites were confirmed to have a good hyperthermia property through the measurement of temperature increase in an AC-magnetic field. For example, the 30 mass% Fe3O4/HA nanocomposites showed the temperature increase of 40°C after about 20 sec under a frequency of 600 kHz and an amplitude of 2.9 kA/m. Consequently, the Fe3O4/HA nanocomposites thus synthesized were found to be a promising material for hyperthermia therapy.
AcknowledgmentsThe author would like to thank Professor Kenya Murase of Osaka University for his support in measuring temperature profile of nanocomposites.
Murakami S, Hosono T, Jeyadevan B, Kamitakahara M, Ioku K. Hydrothermal synthesis of magnetite/hydroxyapatite composite material for hyperthermia therapy for bone cancer. Journal of the Ceramic Society of Japan 2008;116(9) 950–954.
Andronescu E, Ficai M, Voicu G, Ficai D, Maganu M, Ficai A. Synthesis and characterization of collagen/hydroxyapatite: magnetite composite material for bone cancer treatment. Journal of Materials Science: Materials in Medicine 2010;21(7) 2237–2242.
Inukai A, Sakamoto N, Aono H, Sakurai O, Shinozaki K, Suzuki H, Wakiya N. Synthesis and hyperthermia property of hydroxyapatite-ferrite hybrid particles by ultrasonic spray pyrolysis. Journal of Magnetism and Magnetic Materials 2011;323(7) 965–969.
Tampieri A, D'Alessandro T, Sandri M, Sprio S, Landi E, Bertinetti L, Panseri S, Pepponi G, Goettlicher J, Bañobre-López M, Rivas J. Intrinsic magnetism and hyperthermia in bioactive Fe-doped hydroxyapatite. Acta Biomaterialia 2012;8(2) 843–851.
Dong L, Zhu Z, Qiu Y, Zhao J. Removal of lead from aqueous solution by hydroxyapatite/magnetite composite adsorbent. Chemical Engineering Journal 2010;165(3) 827–834.
Wang X. Preparation of magnetic hydroxyapatite and their use as recyclable adsorbent for phenol in wastewater. Clean—Soil, Air, Water 2011;39(1) 13–20.
Xie H, Li X, Cheng C, Wu D, Zhang S, Jiao Z, Lan Y. Kinetic and thermodynamic sorption study of radiocobalt by magnetic hydroxyapatite nanoparticles. Journal of Radioanalytical and Nuclear Chemistry 2012;291(2) 637–647.
Yang Z, Gong X, Zhang C. Recyclable Fe3O4/hydroxyapatite composite nanoparticles for photocatalytic applications. Chemical Engineering Journal 2010;165(1) 117–121.
Liu Y, Zhong H, Li L, Zhang C. Temperature dependence of magnetic property and photocatalytic activity of Fe3O4/hydroxyapatite nanoparticles. Materials Research Bulletin 2010;45(12) 2036–2039.
Covaliu CI, Georgescu G, Jitaru I, Neamtu J, Malaeru T, Oprea O, Patroi E. Synthesis and characterization of a hydroxyapatite coated magnetite for potential cancer treatment. Revista de Chimie 2009;60(12) 1254–1257.
Iwasaki T, Sato N, Kosaka K, Watano S, Yanagida T, Kawai T. Direct transformation from goethite to magnetite nanoparticles by mechanochemical reduction. Journal of Alloys and Compounds 2011;509(4) L34–L37.
Silva CC, Pinheiro AG, Miranda MAR, Góes JC, Sombra ASB. Structural properties of hydroxyapatite obtained by mechanosynthesis. Solid State Sciences 2003;5(4) 553–558.
Shu C, Yanwei W, Hong L, Zhengzheng P, Kangde Y. Synthesis of carbonated hydroxyapatite nanofibers by mechanochemical methods. Ceramics International 2005;31(1) 135–138.
Wu SC, Hsu HC, Wu YN, Ho WF. Hydroxyapatite synthesized from oyster shell powders by ball milling and heat treatment. Materials Characterization 2011;62(12) 1180–1187.
Iwasaki T, Yabuuchi T, Nakagawa H, Watano S. Scale-up methodology for tumbling ball mill based on impact energy of grinding balls using discrete element analysis. Advanced Powder Technology 2010;21(6) 623–629.
Iwasaki T, Sato N, Nakamura H, Watano S. Aqueous-phase synthesis of crystalline magnetite nanoparticles by a new mechanochemical method. In: proceedings of the 5th Asian Particle Technology Symposium, APT2012, 2–5 July 2012, Singapore.
Lee J, Isobe T, Senna M. Magnetic properties of ultrafine magnetite particles and their slurries prepared via in-situ precipitation. Colloids and Surfaces A: Physicochemical and Engineering Aspects 1996;109, 121–127.
Murase K, Oonoki J, Takata H, Song R, Angraini A, Ausanai P, Matsushita T. Simulation and experimental studies on magnetic hyperthermia with use of superparamagnetic iron oxide nanoparticles. Radiological Physics and Technology 2011;4(2) 194–202.