Tafel parameters for corrosion of mild steel in 1.0 M HCl with different loading level of PANI & PSC in epoxy resin.
Intrinsically conducting polymers (ICPs) have been considered for use in various applications. One of the most important applications of these materials which are attracting considerable attention in the most recent times is in corrosion protection of oxidizable metals . The effective use of conducting polymers for corrosion protection of metals can be carried out by different methods; like formulation of polymers with paints, by electro-deposition of conducting polymers onto metal surface and by direct addition of polymers in the corrosive solution as corrosion inhibitors. Coatings on the surface of metals by polymeric materials have been widely used in industries for the protection of these materials against corrosion [2-13]. Some specific conducting polymers like polyaniline and its derivatives, have been found to display interesting corrosion protection properties. In the past decade, the use of polyaniline as anticorrosion coatings had been explored as the potential candidates to replace the chromium-containing materials, which have adverse health and environmental concerns [14-17]. A polymer behaves as a barrier when it exists in the electronically and ionically insulating state. An important feature of the polymer coating in its conductive state is the ability to store large quantity of charge at the interface formed with a passive layer on a metal. This charge can be effectively used to oxidize base metal to form a passive layer. Thus, the conducting polymer film was also capable of maintaining a stationary potential of the protected metal in the passive range . Application of conducting polymers like polyaniline to corrosion protection of metals is, however, subject to some limitations. First, charge stored in the polymer layer (used to oxidize base metal and to produce passive layer) can be irreversibly consumed during the system’s redox reactions. Consequently, protective properties of the polymer coating may be lost with time. Also, porosity and anion exchange properties of conducting polymers could be disadvantageous, particularly when it comes to pitting corrosion caused by small aggressive anions (
Present chapter is based on the preparation of conducting polymer nanocomposites coating onto the mild steel surface by using powder coating techniques. Powder coatings are often used as an alternation to liquids paints finishing or traditional liquid finishing. The key benefits of powder coating techniques are cost effective, environmentally friendly, excellence of finish and performance. This shows single coat finishes with no primer or any other solvent required and high film thickness can be achieved with single coat. Preparation of PANI/SiO2 nanocomposites was carried out using in-situ polymerization and evaluation of corrosion protection effect for the polyaniline/SiO2 nanocomposite materials on the mild steel surface. Corrosion protection performance of these composites was compared with that of the polyaniline by performing a series of electrochemical measurements of corrosion potential, polarization resistance, and corrosion current in 1.0 M HCl solution.
In order to improve anticorrosion performance of mid steel in 3.5 % NaCl aqueous medium, preparation of highly hydrophobic polyaniline-SiO2 nano-composite coating have also been developed. There are several ways to develop hydrophobic surfaces i.e. by electrodeposition method [39-41], solvent casting of polymers , layer-by-layer deposition [43-45], chemical vapor deposition [46, 47], dip-coating and/or self-assembly [48-51] and chemical grafting [52-55]. Most of those methods cannot be easily developed and they need very strict conditions of preparation, and low adhesion coatings are often obtained. However, development of highly hydrophobic conducting polymer nanocomposite coatings via powder coating method was found to be highly adhesive, long lasting and more convenient [56, 57].
2. Corrosion study
The corrosion inhibition performance study was carried out at room temperature in aqueous solution of 1.0 M HCl/ 3.5 % NaCl by using Tafel extrapolation and chrono-amperometry methods. Experiments were carried in a conventional three electrode cell assembly using Autolab Potentiostat/ Galvanostat, PGSTAT100 (Nova Software). In three electrode cell assembly, pure iron of dimension 1 cm x 1 cm is taken as working electrode embedded in araldite epoxy, Pt as counter electrode and saturated calomel electrode (SCE) as reference electrode. The cleaning of the working iron electrode was carried out by 1/0, 2/0, 3/0 and 4/0 grade emery papers. The electrodes were then thoroughly cleaned with acetone and trichloroethylene to remove any impurities on the surface.
2.1. Tafel extrapolation method
Tafel extrapolation method involves the measurement of over potentials for various current densities. Figure 1 shows a potential vs. log absolute current plot for an applied potential scan. The linear Tafel segments to the anodic and cathodic curves (-0.2 to + 0.2 V versus corrosion potential) were extrapolated to corrosion potential to obtain the corrosion current densities. The slope gives the Tafel slopes (ba and bc) and the intercept corresponds to icorr. The corrosion current density [ icorr (A/cm2)] was calculated with the Stern-Geary equation  (Eq.1);
where MW is the molecular weight of the specimen (g/mole), ρ is density of the specimen (g/m3) and z is the number of electrons transferred in corrosion reactions.
The corrosion protection efficiency (% P.E.) was determined from the measured icorr (corrosion current densities with blank mild steel electrode (i0corr) without coatings and corrosion current densities with a mild steel electrode coated with polymer coated (iccorr) values by using the following relationship;
2.2. Weight loss method
The weight loss methods have also been performed for corrosion study. Polymer coated mild steel specimens of dimension 4 x 3.5 cm2 have been tested for same span of time by immersing the samples in 1.0 M HCl or aqueous 3.5 % NaCl solution for 60 days. The uncoated and polymers coated mild steel specimens were weighed in an electronic balance with an accuracy of 0.1 mg. before immersion in saline medium. After the 60 days of immersion the mild steel specimens were withdrawn from the tested solution, washed thoroughly with distilled water followed by acetone and dried with air, then weighed again. The performance of the coating was examined visually and through calculation of the weight loss. Weight loss (W.L) is expressed as the loss in the weight per unit area or per unit area per unit time (g cm-2 h-1) as follows:
where, w0 = initial weight of the sample before immersion (g); w1 = weight of the sample after immersion (mg); a= surface area (cm2) of specimen; t = end time (h) of each experiment. If we introduce the density of metal; d (g/cm3), the loss in the thickness of metal per unit time can be calculated. Corrosion rate (C.R) in mm/year can also be calculated by weight loss method as follows:
2.3. Surface study
Surface studies comprise the analysis of surface of metals before and after corrosion in order to estimate the rate as well as mechanism of corrosion. Techniques like scanning electron microscopy and electron probe micro analysis are used to study the structure, chemical composition of corrosion product formed onto metal surface. Other techniques like atomic force microscopy and ellipsometry are used to study the surface of metals with and without corrosion.
3. Synthesis of the SiO2 nanoparticles
The syntheses of mono disperse uniform- sized SiO2 nanoparticles were carried out by using ammonia as catalyst and ethanol as solvent. Hydrolysis method of tetra-ethylorthosilicates (TEOS) was used for synthesizing SiO2 nanoparticles. Aqueous ammonia (0.1M) was added to a solution containing ethanol (1.0 M) and 20 ml of deionized water which was stirred for 1 h then 0.05M TEOS was added and again stirred for 1 h at room temperature. Appearance of white turbid suspension indicating the formation of silicon dioxide, this suspension was retrieved by centrifugation and further calcination at 823 K for 6 hours.
4. Preparation of PANI/SiO2 composites:
4.1. Chemical oxidative polymerization
PANI/SiO2 composites were prepared by
4.2. Electro-chemical polymerization
The electrochemical polymerization of 0.1 M aniline and aniline in the presence of SiO2 in 0.2 M H3PO4 /0.2 M PFOA was carried out between −0.20 to 1.5 V on platinum electrode vs. Ag/AgCl reference electrode. The polymer film growth was studied by sweeping the potential between −0.20 to 1.5V on Pt electrode at a scan rate of 20 mV/s. Prior to polymerization, the solution was deoxygenated by passing argon gas through the reaction solution for 30 min. Peak potential values of the corresponding polymer and PANI-SiO2 composites were recorded in 0.2 M H3PO4 /0.2 M PFOA medium.
5. Preparation of PANI/SiO2 composites coated mild steel
Mild steel coated with PANI/SiO2 nanocomposites electrode of dimension 1 cm x 1 cm were employed to carry out the corrosion studies. Surface treatments were applied on the samples including the cleaning of the electrode was carried out by 1/0, 2/0, 3/0 and 4/0 grade emery papers. The electrodes were then thoroughly cleaned with acetone and trichloroethylene to remove any impurities on the surface. The powder polymer was mixed with epoxy formulation in various proportions ranging from 1.0 % to 6.0 wt. %. The polymer-epoxy powder coating was applied to a thickness of 45 ± 3 μm using an electrostatic spray gun. After obtaining uniform coverage of the powder the powder-coated panels were placed in air drying oven for curing at 140oC for 20 min. The adhesion of the coating was tested by tape test as per ASTM D3359-02 and found to pass the test.
6. Characterization of PANI-SiO2 nanocomposites
6.1. Electrochemical behaviour
Figure 2 shows the electrochemical growth behaviour of aniline and aniline-SiO2 in 0.2 M H3PO4. The polymer film growth was studied by sweeping the potential between -0.20 and 1.5 V on Pt electrode at a scan rate of 20 mV/s. Peak potential values of the corresponding PANI and PSC were recorded in H3PO4 medium. First anodic peak (oxidation peak) corresponds to the oxidation of monomer. During the first reverse sweep, a reduction peak appears which shows that the formation of oligomers and polymer on electrode surface as shown in Figure 2.
After the first scan, well defined oxidation and reduction peaks of polymers between 0.2 and 0.6 V vs. Ag/AgCl appeared. The current values of each oxidation and reduction peaks are greater than that of a previous cycle which indicate the built up of an electro active polymeric material on the electrode surface.
Figure 3 shows the cyclic voltammogram of PANI-SiO2 composite and the inset figure shows the cyclic voltammogram of PANI in H3PO4 medium. We have observed quite interesting observation when we recorded the cyclic voltammogram of aniline in phosphoric acid medium and when SiO2 nanoparticles were incorporated in the monomer matrix. On recording the cyclic voltammogram of aniline in H3PO4 medium, it was observed that anodic peak potential is observed at 0.456 V.
However, in the presence of SiO2 matrix, these peaks appeared at 0.247 V. The reason for getting these deviations in H3PO4 medium is that phosphoric acid is a weak protonic acid whose pKa1 value is 2.21 which results in shifting of peak potential value to 0.456 V. Conventionally, in strong acidic medium like 1.0 M HCl medium, these values of peak potential for PANI are observed at 0.1 V. However, when the CV was recorded for aniline in the presence of SiO2 and H3PO4 medium, there is a possibility that protons from phosphoric acid medium might have protonated SiO2 resulting in generation of well-defined peaks as observed in the growth behavior of CV resulting in observing peak potential values at 0.247 V (EaI). These experiments were repeated by us number of times and each time this type of cyclic voltammogram was observed which has led us to draw the above conclusion. Protons from phosphoric acid might have led to the formation of protonated silica thereby shifting of peak potential values which might have enhanced the electropolymerization of aniline.
6.2. FTIR spectra
Figure 4 shows the FTIR spectra of SiO2, PANI and PANI-SiO2. PANI showed the main characteristics bands at 1565 and 1475 cm−1 attributed to the stretching mode of C=N and C=C, the bands at 1292 and 1245 cm−1 indicating the C–N stretching mode of benzenoid ring and the band at 1117 - 1109 cm−1 is assigned to a plane bending vibration of C–H mode which is found during protonation . The FTIR spectra of SiO2 indicated that the characteristic peak at 1081 cm-1 and 807 cm-1 are assigned to the stretching and bending vibration of Si–O–Si respectively. By comparing the peaks of PANI and PSC, it was observed that some peaks of PSC were shifted due to the presence of SiO2 particles in polymer matrix. For example, the peaks at 1565 cm-1, 1475 cm-1, 1292 cm-1, and 1245 cm-1 shifted to higher wavenumbers, and the bending vibration of Si–O–Si peak at 1056 cm-1 shifted to the lower wavenumbers. These changes also indicate that an interaction exists between PANI molecule and SiO2 particles. These peaks were also observed in PSC indicating the interaction of SiO2 particles in polyaniline chain.
6.3. Thermogravimetric analysis
Figure 5 shows the thermo-gravimetric curves (TG) of pure SiO2, PANI and their composites. The materials were heated from 25 to 800ºC under a constant heating rate of 10ºC/min and in the inert atmosphere of nitrogen gas (60 ml/min). The SiO2 particle has excellent thermal stability up to 800ºC and weight loss was only 0.15 %. The TGA curve of PSC indicated, first weight loss at 110ºC may be attributed to the loss of water and other volatiles species. The weight loss in the second step at about 280ºC involves the loss of phosphate ions as well as onset of degradation of polyaniline backbone. The increasing SiO2 content slightly affects the decomposition temperature (DT) which increases from 280ºC (PANI) to 295ºC (PSC). The third weight loss step between 300 to 550ºC can be ascribed to the complete degradation of dopant as well as polymeric backbone. The composites show little weight loss between the 500-800ºC and the residue remaining in this region gives an approximate estimate of filler content. Therefore, the final weight of SiO2 incorporated in polymer was found to 21 %. The results indicate that actually incorporated SiO2 fraction is less than the ratio of aniline: SiO2 taken in the initial reaction mass.
The TGA data clarify that these composites are thermally stability up to 295ºC, which envisages them as a good candidate for melt blending with conventional thermoplastics like polyethylene, polypropylene, polystyrene etc.
6.4. UV-Visible spectra
Figure 6 shows the UV absorption spectra of polyaniline and its composite with SiO2. We have measured the UV absorption spectra of polymer using dimethyl sulfoxide (DMSO) as a solvent from 250 to1100 nm.
The UV-visible absorption data indicates that λmax values in case of polyaniline doped with o-phosphoric acid medium in DMSO solvent lies at 326nm, 431nm and 619 nm whereas in PSC composite these values lies at 336 nm, 447 nm and 654 nm. In case of polyaniline, π-π* transition [61, 62] occurs at 326 nm whereas in case of PSC composite, this transition value lies at 336 nm.This indicates that the addition of SiO2 particles absorbed in aniline matrix and on polymerization in o-phosphoric acid medium may have caused some interactions with polymer matrix resulting in shifting of bands from 326 nm to 336 nm. This is the reason of shifting of polaronic bands which also shows a shift from 431 nm to 447 nm and 619 nm to 654 nm.
7. Anticorrosive properties of PANI and PSC coated mild steel in 1.0 M HCl medium.
7.1. Chronoamperometry method
Figure 7 shows the chronoamperometric response of uncoated, epoxy coated, PANI and PSC coated mild steel sample in 1.0 M HCl. After the samples reached a stable OCP (open circuit potential), a potential in the range of 1.2 V vs SCE was applied and current was recorded as a function of time. It was observed that the current of PANI and PSC coated mild steel sample remained at a very small value as compared with the uncoated mild steel electrode indicating the good protective properties by these polymers coating. Moreover, it has been observed that the current density value of PSC coated mild steel was lower than that of PANI-coated mild steel sample. The decrease in current density with increasing amount of PSC material in epoxy resin. Hence, chronoamperometric test results showed that mild steel coated with PANI/SiO2 composites shows the higher corrosion protection performance as compared to PANI coated mild steel samples. This statement was further confirmed by other corrosion test methods like Tafel extrapolation and weight loss methods.
7.2. Tafel extrapolation method
The corrosion kinetic parameters derived from these curves are given in the Table 1. As shown in Table 1, PSC coated mild steel sample showed a remarkable current shift from 132 µA to 0.09 µA versus Ag/AgCl in the corrosion current (icorr), relative to the value of the uncoated mild steel.
The significant reduction in the corrosion current density (icorr) in polymer coated mild steel indicated the effective corrosion protection performance of these polymers. The corrosion current values (icorr) were found to be decreased from 132 μA/cm2 for uncoated mild steel sample to 107.6 μA/cm2 for epoxy coated mild steel sample to 0.09 µA /cm2 for PSC coated mild steel samples.
The corrosion current values (icorr) decreased with increasing the concentration of PSC in epoxy resin. icorr value decreased from 15.4 µA/cm2 at 1.5 wt. % to 0.09 µA/cm2 at 6.0 wt. % loading of conducting material in epoxy resin as shown in Figure 9. While PANI coated mild steel showed the icorr in the range of 10.9 μA/cm2 at 6.0 % loading as shown in Figure 8.
|Blank mild steel||-||132.0||1.54||--|
|Epoxy coated mild steel||--||107.6||1.26||18.48|
The corrosion protection efficiency calculated from Tafel parameter revealed that PANI coated mild steel showed 25% protection efficiency at 1.5 wt.% loading while PSC coated mild steel showed 88 % P.E at the same loading level. Up to 99.93 % protection efficiency have been achieved by using 6.0 wt.% loading of PSC in epoxy resin.
7.3. SEM studies of uncoated and coated mild steel observed by weight loss method
The scanning electron micrographs of SiO2 particles, PANI and PSC are shown in Figure 10. SiO2 particles showed spherical shaped morphology and PANI showed globular morphology. Figure 10 b shows the TEM image of of SiO2 particles, which indicates the dimension of SiO2 particles, was found to be 90-100 nm. Morphology of PSC indicates the incorporation of SiO2 particles in PANI matrix. SEM image of PSC revealed that the entrapment of SiO2 particles in the globular space of PANI matrix during in situ polymerisation of polyaniline.
SEM images of uncoated, epoxy coated and polymer coated samples before and after the immersion test of 60 days have been shown in Figure 11 & Figure 12. These images clearly show the formation of large pits on the surface of mild steel after immersion. These pits and cracks were developed during the corrosion of mild steel in acidic medium. In the case PANI coated sample, few pits still appeared on mild steel surface. While, PSC coated mild steel samples did not show any cracks and pits on the metal surface. No detachment of coating from mild steel substrate was also observed after the immersion of these samples in 1.0 M HCl medium for 60 days of immersion indicating strong adherence of PSC composite to the mild steel substrate and it is resistant to corrosion in aqueous 1.0 M HCl solution as shown in Figure 13.
When epoxy coated mild steel sample was immersed in the acidic medium for 60 days, detachment of coating from mild steel substrate have been observed. The pits were also appeared on the metal surface as shown in Figure 12 b.
It was found that the PSC content has a great influence on the anticorrosive performance of the coating. The corrosion protection effect of PSC coated mild steel sample improved slowly when PSC content in epoxy formulation increases from 1.5 to 3.0 wt. % Afterward, an excellent corrosion protection effect appears at 6.0 wt. % loading of PSC content in epoxy resin.
Corrosion rates (C.R) in mm/year have also been calculated by weight loss method and the values have been given in Table 2. It was observed that the corrosion rate was highest for uncoated mild steel in HCl medium. After 60 days of immersion, the C.R value of uncoated mild steel was found to 7.25 mm/year. Epoxy and PANI coated samples showed C.R. value of 6.37 mm/year and 1.90 mm/year respectively. While in the case of PSC coated sample in 6.0 % loading, C.R. value reduced to 0.73 mm/year.
|Blank mild steel||-||30354.6||17256.30||13098.30||43.15||7.25||-|
8. Characterization of hydrophobic PANI - SiO2 Nanocomposites (HPSC)
8.1. Electrochemical behaviour
Figure 14 shows the electrochemical growth behavior of aniline and aniline-SiO2 in 0.2 M PFOA solution. Electrochemical polymeriztion was carried out at 0.9 V on platinum electrode vs Ag/AgCl reference electrode. The polymer film growth was studied by sweeping the potential between -0.20 and 0.9 V on Pt electrode at a scan rate of 20 mV/s.
Peak potential values of the corresponding PANI and HPSC were recorded in PFOA medium. First anodic peak (oxidation peak) corresponds to the oxidation of monomer. The intensity of this peak gradually decreases with subsequent scans. During the first reverse sweep, a reduction peak appears which shows that the formation of oligomers and polymer on electrode surface as shown in Figure 14. Figure 15 shows the Schematic representation of formation of HPSC coating onto mild steel surface. After the first scan, well defined oxidation and reduction peaks of polymers between 0.2 and 0.6 V vs. Ag/AgCl appeared. The current values of each oxidation and reduction peaks are greater than that of a previous cycle which indicate the built up of an electroactive polymeric material on the electrode surface. Moreover, it was observed that current value of PANI film was found to be higher than that of HPSC film which revealed higher conductivity of PANI as compare to HPSC coating on electrode surface.
Cyclic voltammogram of HPSC and PANI in PFOA medium indicates that the first peak potential value of PANI in PFOA medium lies at 0.15 V. Incorporation of SiO2 particle in PANI, the first peak potential value shifted from 0.15 V to 0.041 V vs Ag/AgCl as shown in Figure 16.
This implies that the polymerization of aniline leads to larger peak potential shift as compared to the aniline in presence of SiO2 which indicates the presence of SiO2 particles in the polymer chain induce some change in configurations along the polymer backbone which is responsible for the negative shift in the oxidation potential.
8.2. FTIR spectra
The Figure 17 shows the FTIR spectra of SiO2, PANI and HPSC. PANI showed the main characteristics bands at 1554 and 1438 -1440 cm−1 attributed to the stretching mode of C=N and C=C, the bands at 1250 cm−1 indicating the C–N stretching mode of benzenoid ring.
The FTIR spectra of SiO2 indicated that the characteristic peak at 1081 cm-1 and 807 cm-1 are assigned to the stretching and bending vibration of Si–O–Si respectively. These peaks were also observed in HPSC indicating the interaction of SiO2 particles in polyaniline chain. HPSC and PANI showed a characteristic strong peak at 1738 cm-1 due to C=O stretching mode and peak at 1365 cm-1due to C-F stretching mode , which indicates the interaction of PFOA dopant in the polymer chain.
8.3. Wettability of HPSC coating
The surface wettability was measured by static contact angle measurements with water (γ=72.8 mN/m) to determine surface hydrophobicity. The drop volume used for the measurements was 2.0 μL. The PANI-SiO2 nanocomposite (HPSC) coated electrodes exhibited hydrophobic properties with static water contact angle of about 115o as shown in Figure 14.
9. Anticorrosive properties of HPSC coated mild steel in 3.5 % NaCl solutionAdvertisement
9.1. Tafel Extrapoaltion method
Tafel polarization behaviour of mild steel in 3.5 % NaCl solution with uncoated, epoxy coated, PANI and HPSC coated mild steel are shown in the Figure 18& Figure 19. The corrosion kinetic parameters derived from these curves are given in the Table 3. As shown in Table 3. HPSC coated mild steel sample showed a remarkable current density shift from 106.5 µA/cm2 to 4.36 µA /cm2 versus Ag/AgCl in the corrosion current (Icorr), relative to the value of the uncoated mild steel.
The significant reduction in the corrosion current density (icorr) in polymer coated mild steel indicated the effective corrosion protection performance of these polymers. The corrosion current values (icorr) found to be decreased from 106.5 μA/cm2 for uncoated mild steel sample to 98 μA/cm2 for epoxy coated mild steel sample to 4.36 µA /cm2 for HPSC coated mild steel samples. The corrosion current values (icorr) decreased with increasing the concentration of HPSC in epoxy resin. icorr value decreased from 32.6 µA/cm2 at 1.5 wt. % to 4.36 µA/cm2 at 6.0 wt. % loading of conducting material in epoxy resin.
|Blank mild steel||-||106.5||1.51||0|
|Epoxy coated mild steel||0||98.0||1.39||7.9|
While PANI coated mild steel showed the icorr in the range of 20.4 μA/cm2 at 6.0 % loading. The corrosion protection efficiency calculated from Tafel parameter revealed that PANI coated mild steel showed the protection efficiency 39.4 % at 1.5 wt.% loading while HPSC coated mild steel showed 69.4 % P.E at the same loading level.
Up to 96 % protection efficiency have been achieved by using 6.0 wt. % HPSC in epoxy resin. While in case of PANI, only 80.84% protection has been achieved at 6.0 wt. % loading, as shown in Figure 20.
9.2. Weight loss method
Table 4 shows the values of the weight loss from mild steel samples during the immersion test. The results revealed that HPSC coated samples were more protectable to mild steel than that of only PANI coated samples in same immersion time. After the immersion of coated and uncoated samples in 3.5% NaCl solution for 60 days, it was observed that uncoated and epoxy coated samples showed the maximum weight loss of 34.18 % and 29.11 % respectively
|Blank mild steel||-||32632.1||21478.45||11153.7||34.18||4.18||0|
PANI coated mild steel showed the weight loss up to 10.13 % at 6.0 wt. % loading while HPSC coated samples at the same loading level showed negligible weight loss (i.e < 3 % ) after 60 days of immersion in 3.5 % NaCl medium. Corrosion rate (C.R) in mm/year have also been calculated by weight loss method. It was observed that the corrosion rate was highest for uncoated mild steel in 3.5 % NaCl medium. After 60 days of immersion, the C.R value of uncoated mild steel was found to 4.18 mm/year. Epoxy and PANI coated samples showed C.R. value of 3.56 mm/year and 1.24 mm/year respectively. While in the case of HPSC coated sample in 6 % loading, C.R. value reduced to 0.28 mm/year.
The appearance of the uncoated and HPSC coated mild steel samples after exposure to salt spray fog for 35 days is shown in Figure 21.
It was observed that epoxy coated and PANI coated (at 6.0 wt. % loading) mild steel have more corrosion extended area from the scribes as shown in Figure 21 (a) and 21(b) while HPSC coated mid steel (at 1.0 wt. % loading) showed less corrosion extended area as compared to epoxy and PANI coated mid steel as shown in Figure 21(c). However, HPSC containing coating sample (at 6.0 wt.% loading) were found to be free from rust and blister as shown in Figure 21 (d). Moreover, there was no spreading of rust along the scribed areas.
9.3. SEM studies of uncoated and coated mild steel before and after immersion test
It was observed that SiO2 particles showed spherical shaped morphology as shown in Figure 10 a. The scanning electron micrographs of PANI and HPSC are shown in Figure 22. PANI doped with PFOA showed uniform net like morphology as shown in Figure 22(a). Morphology of HPSC was entirely different with incorporation of SiO2 particles in PANI matrix during polymerisation. SEM image of HPSC revealed that the entrapment of SiO2 particles in the globular space of PANI matrix during in-situ polymerisation of polyaniline as shown in Figure 22 (b).
SEM images of uncoated, epoxy coated and polymer coated samples before and after the immersion test of 60 days have been shown in Figure 23 and 24 respectively. These images clearly show the formation of large pits on the surface of mild steel after immersion. These pits and cracks were developed during the corrosion of mild steel in NaCl medium.
When epoxy coated mild steel sample was immersed in the acidic medium for 60 days, detachment of coating from mild steel substrate have been observed. The pits were also appeared on the metal surface as shown in Figure 24. In the case PANI coated sample, few pits still appeared on mild steel surface. While, HPSC coated mild steel samples did not show any cracks and pits on the metal surface. No detachment of coating from mild steel substrate was also observed after the immersion of these samples in 3.5 % NaCl medium for 60 days of immersion indicating strong adherence of HPSC composite to the mild steel substrate and it is resistant to corrosion in aqueous 3.5 % NaCl medium.
It was found that the HPSC content has a great influence on the anticorrosive performance of the coating. The corrosion protection effect of HPSC coated mild steel sample improved slowly when HPSC content in epoxy formulation increases from 1.5 to 3.0 wt. % Afterward, an excellent corrosion protection effect appears at 6.0 wt. % loading of HPSC content in epoxy resin.
9.4. Mechanism of corrosion protection of PANI-SiO2 nanocomposites
The corrosion studies show that the PANI-SiO2 nanocomposites containing coating showed better corrosion protection as compared to PANI coating which may be due to the redox property and uniform distribution of PANI in the coating containing PANI-SiO2 nano-composites. Earlier studies [63-64] have shown that the redox property of PANI coating on metal surface plays an important role to protect the metal by passivating the pin holes. Corrosion protection of metals occurs via reduction of PANI–Emeraldine salt (PANI–ES) to PANI–Leucosalt (PANI–LS) with the concomitant release of phosphate dopant . Phosphate ions help to form passive film on mild steel at the defect. PANI–LS is assumed to undergo a subsequent re-oxidation by dissolved oxygen to PANI–ES. Due to this cyclic reaction, the coating containing PANI is able to offer higher corrosion protection. However, in case of PANI-SiO2 nano composites containing coating, these composites have a dual protection mechanism; forming a passive layer and simultaneously acting as a physical barrier to avoid chloride ion penetration. Moreover, it acts as a barrier between metal surface and corrosive environment. Entrance of water and corrosive ions on the metal surface causes the defects in the paint coating and therefore the protective property of the coating is decreased. Due to uniform distribution of PANI, the possibility of forming uniform passive layer on the mild steel surface is more since PANI has been shown to protect the mild steel surface by passive film formation. Furthermore, powder coating technique also plays an important role for achieving high quality, durable and good anticorrosive coatings.
Corrosion protection property of these coating may also be attributed to the PSC/HPSC content in epoxy resin which can react with epoxy to form highly adherent, dense and non porous polymer film on the mild steel surface. On the other hand, presence of SiO2 nanoparticles entrapped in PANI chain provide the reinforcement to PANI chain which reduce the degradation of polymer chain in corrosive condition.
10. Antistatic performance of the conducting polymers nanocomposites based on nanotubes of poly (aniline-co-1-amino-2-naphthol-4-sulphonic acid)/LDPE composites
Electrostatic charge dissipation has become an important issue within the electronic components such as data storage devices, chips carriers and computer internals. Antistatic protection is also required for parts where relative motion between dissimilar materials occurs  like weaving machine arms, airplane tyres etc. Conventional polymers commonly being used for packaging of various electronic equipments but due to their inherent electrical insulating nature, these polymers failed to dissipate the static or electrostatic charge. The generation of static electricity on the materials leads to a variety of problems in manufacturing and consumer use. Moreover, electronic components are susceptible to damage from electrostatic discharge. Thus the challenge is to convert inherently insulating thermoplastic to a product that would provide an effective antistatic material. Various attempts have been made to achieve the antistatic polymers with retained mechanical properties such as addition of antistatic agents , conducting additives  and fillers like carbon powder  and carbon nanotubes  etc. The electrical conductivity of the polymeric material depends on the amount, type and shape of the conducting filler . According to electronic industries association (EIA) standards, in ESD protected environments, the optimal surface conductivity should be in the range of 10-6 to 10-10 S/cm. However the functioning of antistatic agents is critically dependent on the relative humidity  whereas the metal and carbon filled materials suffer from the problems like bleeding and poor dispersion . Moreover, it has been observed that carbon black loaded static controlling materials usually contain 15-20 % carbon black. The addition of carbon black at higher concentrations showed a negative effect on the proccessability of the compound and mechanical properties such as increase in melt viscosity and decrease in impact resistance. Use of conducting blends and composites with conventional polymers as an electrostatic charge dissipative material is one of the promising application of conducting polymers which combines the mechanical properties of conventional polymers and electrical properties of conducting polymers. Polyaniline is one of the most promising intrinsically conducting polymer (ICPs) because of its good environmental stability and high electrical conductivity, which can be reversibly controlled by a change in the oxidation state and protonation of the imine nitrogen groups. Blending of polyaniline with conventional polymers like polypropylene, ABS, LDPE etc. can also be used to improve the proccessability of polyaniline creating new materials with specific properties for the desired application at low cost that can also be used for different applications like electromagnetic shielding and corrosion prevention where conductivity, proccessability and mechanical properties of the materials are of the primary importance. Hence desired properties of conducting polymers can be enhanced by mixing it with a polymer that has good mechanical properties and the unique combination of electrical and mechanical properties of conducting copolymers blends with insulating polymers seems to have great potential for their use in many applications [73-75].
11. Antistatic measurements
Antistatic or electrostatic charge dissipative performances of blends of conducting polymers were measured by Static decay meter, John Chubb Instrument and Static Charge Meter. The detailed method is given below.
11.1. Static decay meter
Static decay meter is very useful device for measurement of static decay time of the conducting polymer blends in the form of injection moulded sheets and blown film. The samples of conducting copolymer blends (LDPE/conducting copolymer) were cut in to the 15 x 15 cm2 blown film and was used for measurement of static decay time on Static Decay Meter by measuring the time on applying a positive voltage of 5000 V and recording the decay time on going down to 500 V. Similarly the static decay time was measured by applying a negative voltage of 5000 V. Here, these measurements were carried out on Static Decay Meter; model 406D, Electro-tech System, Inc., USA. The model 406D Static Decay Meter is designed to test the static dissipative characteristics of material by measuring the time required for charge test sample to discharge to a known, predetermined cut-off level. Three manually selected cut-off threshold at 50%, 10% and 1% of full charge are provided and samples are charged by an adjustable 0 to ±5kV high voltage power supply.
11.2. John Chubb Instrument
John Chubb Instrument (JCI 155 v5) charge decay test unit is a compact instrument for easy and direct measurement of the ability of materials to dissipate static electricity and to assess whether significant voltage will arise from practical amount of charge transferred to surface . The JCI 176 Charge Measuring Sample Support (connected with JCI 155 v5) provides a convenient unit to support film and layer materials (and also powder and liquids). The samples of conducting copolymer blends (LDPE/conducting copolymers) i.e. 45 x 54 mm2 blown film were used for measurement of static decay time on John Chubb Instrument (Model JCI 155 v5) by measuring the time on applying the positive as well as negative high corona voltage of 5000 V on the surface of material to be tested and recorded the decay time at 10 % cut-off. A fast response electrostatic field meter observes the voltage received on the surface of sample and measurements were to observe how quickly the voltage falls as the charge is dissipated from the film. The basic arrangement for measuring the corona charge transferred to the test sample during corona charge decay measurements is shown in Figure 24. Charge is measured as a combination of two components-‘conduction charge’ and ‘induction charge’. The ‘conduction’ component is that which couples directly to the sample mounting plates within the time of application of corona charging and the time for the plate carrying the corona discharge points to move away.
The ‘inducting’ relates to the charge that has been deposited but has not coupled out directly to the mounting plates and the total charge transferred to the sample can be measured as:
where the factor ‘f’ is actually close to 2.2. This factor can be determined experimentally. The film and layer polymeric samples are easily mounted in the JCI 176 between the two hinged flat metal plates. The aperture in the sample mounted plates, to which the conduction charge is measured, are 5 mm larger all round than the 45 x 54 mm2 test aperture of the JCI 155. The JCI 155 Charge Decay Test unit sits on top of the JCI 176 Charge Measuring Sample Support into the recess between the boundary edges. The measurements are recorded in the form of graphs (ESD/ JCI-graphs) which show the decay of surface voltage with respect to decay time.
12. Synthesis of poly(aniline-co-1-amino-2-naphthol-4-sulphonic acid)
Copolymers of 1-amino-2-naphthol-4-sulphonic acid (ANSA) and aniline of varying composition (i.e. by varying the co-monomer feed compositions in the initial feed) were synthesised by chemical oxidative polymerization in the presence of PTSA. Polymerization was initiated by the drop wise addition of ammonium persulphate solution (0.1 M APS in distilled water). The polymerization was carried out at a temperature of 0 C for a period of 4-6 h. Their copolymers were synthesised by varying the molar ratio of co-monomers in the initial feed. The synthesized copolymers were isolated from reaction mixture by filtration and washed with distilled water to remove oxidant and oligomers.
PTSA doped copolymers of aniline and ANSA (poly(AN-co-ANSA) in 80:20 molar ratio and 50:50 molar ratio is abbreviated as PANSA2-PTS and PANSA5-PTS respectively whereas PTSA doped polyaniline is abbreviated as PANI-PTS.
13. Preparation of LDPE-Conducting Copolymer Film
Composites of copolymers with LDPE were prepared by melt blending method. Required amount of LDPE and copolymers were loaded in internal mixer for 20-30 minutes at around 60 rpm. Blending of copolymers with LDPE was carried out in twin-screw extruder at the temperature range from 140-150oC by melt mixing method. The blown film of the copolymer/LDPE composite was made by Haake Blown Film instrument at the temperature range of 160oC where speed of screw was maintained at 40 rpm. PTSA doped copolymers of aniline and ANSA (poly(AN-co-ANSA) in 80:20 and 50:50 molar ratio blended with LDPE is abbreviated as PANSA2-PTS/LDPE and PANSA5-PTS/LDPE respectively.
14.1. Characterization of PTSA doped PANI and copolymers of AN and ANSA
ANSA is a tri-functional monomer having three functional groups (i.e. -NH2, -OH and –SO3H) along with two fused benzene rings.
This monomer can be copolymerized with aniline to give different materials and it has been observed that the participation of functional groups (-NH2 and –OH) in the polymerization depends upon the reaction conditions. It is proposed that polymerization of ANSA in the presence of PTSA occurred selectively through –NH2 group (figure 26) as confirmed by structural characterization (FTIR and NMR spectroscopy) .
14.1.1. Morphological Characterization
Figure 27 shows SEM micrographs of PTSA copolymers of ANSA and AN. PANI-PTS show a globular sponge like structure (Figure 27a) and morphology changed with varying copolymer composition. PTSA doped copolymers of aniline and ANSA exhibit hollow tube like morphology. The use of 1-amino-2-naphthol-4-sulphonic acid as a co-monomer as well as nature of external dopant played an important role for achieving the tubular morphology. In case of PTSA doped copolymers of aniline and ANSA in ratio of 80:20 (PANSA2-PTS), the globular morphology of the resultant copolymer tend to change to the tube forms (Figure 27b).
However, well defined tubes were formed when molar ratio of aniline/ANSA was 50:50 in the presence of PTSA (Figure 27c). The difference in the morphology between polyaniline and its copolymers with ANSA may be related to the different reactivities of the two monomers, nature of reaction media and reaction route.
TEM image of PTSA doped copolymer of aniline and ANSA in 50:50 molar ratios (Figure 26d) shows that these tubes are hollow with outer diameter of 80-90 nm.
Room temperature conductivity values of PTSA doped samples are summarised in Table 5, which reveals that the room temperature conductivity of PANI-PTS was found to be better than PTSA doped copolymers.
|PANSA2-PTS||4.48 x 10-1||195|
|PANSA5-PTS||1.98 x 10-2||188|
On increasing the molar ratio of ANSA in copolymer, conductivity tends to decrease accordingly due to the presence of three functional groups in ANSA unit which exerted a strong steric effect on the doping process hence induces additional deformation along the polymer backbone.
14.2. Characterization of LDPE/Conducting Polymer composite film
14.2.1. Thermal Properties
These copolymers (PANSA2-PTS/PANSA5-PTS) can be melt blended with conventional polymers like LDPE. Figure 28 shows the TG traces of blown films of PTSA doped copolymer/LDPE composites. The degradation temperature of pure LDPE blown film was around 400oC. Thermal stability of the blown film of copolymer/LDPE blends (0.5-1.0 wt % loading) was also found to be same as LDPE.
14.2.2. Mechanical properties
The mechanical properties of PTSA doped poly (AN-co-ANSA)/LDPE film was measured and the results are summarised in the Table 6. In case of pure LDPE film, the tensile modulus and yield stress were 141 MPa and 16.3 MPa respectively. However, the inclusion of poly (AN-co-ANSA) in LDPE led to decrease in both tensile modulus and yield stress depending upon the molar ratio of ANSA in the copolymer chain as well as type of dopant.
|LDPE/PANSA2-PTS||1.0||129||12.1||176||1.28 x 10-6|
|0.5||134||13.1||180||2.22 x 10-9|
|LDPE/PANSA5-PTS nanocomposites||1.0||120||10.3||166||8.18 x 10-7|
|0.5||131||12.3||171||4.13 x 10-9|
In the case of film prepared by composites of LDPE/conducting copolymer (99/1 w/w or 99.5/0.5 w/w), tensile modulus, yield stress and % elongation decreased (Table 6). Tensile modulus decreased from 141 MPa (LDPE) to 120 MPa (LDPE/PANSA5-PTS) at a concentration of 1.0 % w/w. Yield stress also decreased for 16.3 MPa (LDPE) 10.3 MPa (LDPE/PANSA5-PTS). Similarly, the ultimate elongation also decreased in the same manner.
At a loading of 0.5 % (w/w) of PTSA doped copolymers in LDPE, tensile modulus also decreased from 134 MPa (for PANSA2-PTS/LDPE) to 120 MPa (for PANSA5/LDPE). Similarly, 0.5 wt. % loading of PTSA doped copolymers with LDPE, yield stress reduced from 13.1 MPa in case of PANSA2-PTS/LDPE to 12.3 MPa for PANSA5-PTS/LDPE film and the ultimate elongation was also found to be 180 % and 171 % for PANSA2-PTS/LDPE and PANSA5-PTS/LDPE composite films respectively. Hence, the mechanical strength of PTSA doped poly(AN-co-ANSA)/LDPE blended films was found to be better in case 0.5 wt.% loading of copolymers than that of 1.0 wt. % loading. Moreover, it has also been observed that mechanical properties of PTSA doped copolymers-LDPE film were different from that of self doped copolymers-LDPE films. Mechanical strength of the poly(AN-co-ANSA)/LDPE composites decreased with increasing the molar ratio of ANSA in the copolymer (Table 6).
14.2.3. Electrical Properties
Room temperature conductivity values of PTSA doped copolymers/LDPE composite film are summarised in Table 6. The room temperature conductivity of copolymers of aniline with ANSA decreased from 4.48 x 10-1 to 1.98 x 10-2 S/cm depending on the molar ratio of ANSA in the copolymer feed and type of dopant. The conductivity values copolymers were found to be 4.48 x 10-1 S/cm and 1.98 x10-2 S/cm for PANSA2-PTS and PANSA5-PTS respectively (Table 5). On blending with LDPE at 1.0 wt %, conductivity value decreased from 1.28 x 10-6 S/cm to 8.18 x 10-7 S/cm respectively. When the loading level of copolymers with LDPE reduced from 1.0 wt % to 0.5 wt %, the conductivity of the resultant composites decreased. 0.5 % (w/w) loading of LDPE films based on PANSA2-PTS and PANSA5-PTS had conductivity value in the order of 2.22 x 10-9 S/cm and 4.13 x 10-9 S/cm respectively.
14.2.4. Morphological Characterization
Figure 29 show the SEM images of LDPE films in the presence of PTSA doped copolymers at 0.5 wt. % loading. When these copolymers were blended with LDPE, the copolymer domains were found to disperse in the LDPE matrix as evident by the appearance of tubes and needle like granules in the LDPE matrix (Figure 29). In addition, the formation of the conducting path is evident and agrees with the results relating to electrical conductivity of the composites. In copolymer composites (matrix and dispersed phase), the level of interaction between the two components and mode of dispersion in the matrix, influence the electrical and mechanical properties of the composites . The SEM micrographs of the LDPE/copolymer film showed two different phases i.e. conducting copolymer and non conducting matrix (LPDE). Interconnection of conducting phase in the non-conducting matrix creates a conducting path along the LDPE matrix.
Moreover, it has also been observed that the conduction mechanism and transportation of charge carrier in the blends depend on the loading level and mode of dispersion of the conducting materials. PANSA5-PTS nanotubes at 0.5 wt. % loading with LDPE, the surface conductivity was found to be in the order of 10-9 S/cm, which is suitable for their use in ESD protection applications.
Hence, it may be presumed that when the sufficient amount of conducting material is loaded in the polymer matrix, the conducting particles get closer and form linkage which makes an easy path for conduction of charge carrier throughout the blend which shows sufficient loading and good dispersion of conducting material in the polymer matrix (i.e. LDPE). While in the case of very low loading of conducting material in the polymer matrix, the gap between conducting particles in the polymer matrix is large with the result that no conduction path in the blend.
Hence, the conductivity of films based on blends depends on the morphology of conducting material. The nanotubular or fibre like morphology of conducting materials which form a network in the whole blend facilitate the conduction of charge carrier through the continuous structure of the chain of conducting material in the insulating matrix at very low loading of conducting material in the insulating matrix.
15. Antistatic Behaviour of LDPE/Copolymer Film
The results of static decay time on application of positive/negative voltage of 5000 V and recording the decay time on going down to 500 V are summarised in Table 7. It was observed that blank LDPE film shows a static decay time of 120.1 sec. It decreased upon addition of copolymer and was found to be dependent on the amount of copolymer. LDPE film having 1.0 % (w/w) and 0.5 % (w/w) of PANSA2-PTS showed a decay time of 0.1 sec. and 1.4 sec. respectively at 10 % cut-off. However, the PANSA5-PTS/LDPE film showed a static decay time of 0.8 sec. at a loading of 0.5 wt. % and 0.2 sec. at 1.0 wt.% loading . Any material which showed a static decay time less than 2.0 sec passes the criteria for its use as antistatic material. Based on the above observations, we can say that LDPE film prepared by blending of conducting copolymer based on AN and ANSA at 1.0 % w/w loading, can be used as an effective antistatic film. Similar measurements were recorded with copolymer composite film with a cut-off value of 50 % and the results are summarised in Table 7.
Static decay measurements were also performed on John Chubb Instrument (JCI 155 v5) charge decay test unit by measuring the time on applying the positive as well as negative high corona voltage of 5000 V on the surface of material to be tested and recorded the decay time at 10 % cut off. A fast response electrostatic field meter observes the voltage received on the surface of sample and measurements were to observe how quickly the voltage falls as the charge is dissipated from the film. Graphs obtained from these experiments have been shown in the Figure 30, which show the decay of surface voltage and decay time.
The surface voltage and surface charge received by the materials depend on nature of materials. When positive or negative high corona voltage (i.e. 5000 V) was applied to the surface of the material, only a limited amount of voltage was received by the blend depending on the nature of materials. When high corona voltage was applied on the surface of insulating material, only some voltage was drained away and greater amount of voltage were retained on its surface. This surface voltage decays at particular time. Moreover, the surface charge received by the blends was also calculated during the experiment.
Hence the charge retention capability of conducting materials was found to be very low thus they quickly dissipate this surface charge. The static decay time of blank LDPE film was found to be very high on applying the positive and negative corona voltage of 5000 V. The peak at 2146 V indicate that the LDPE film has received 2146 V at the surface corresponding to 55.79 nC of static charge, which get dissipated very slowly and was not found to be able to dissipate it up to 10 % cut off as shown in the Figure 30A. Due to insulating nature of the material, lot of charges were found to be retained on the surface of LDPE film. Blending of 1.0 wt. % of conducting copolymer with LDPE, decreases the charge retention capability by reducing the decay time. In case of PANSA5-PTS/LDPE film at 1.0 wt. % loading of PANSA 5-PTS in LDPE, the peak started at 475 V on applying the voltage of +5000 V, which indicates that the voltage received at the surface is only 475 V corresponding to 9.51 nC of charges which dissipated quickly, around 0.5 sec., at 10% cut off as shown in the Figure 30B (curve a).
Similar trend has been found for negative polarity charging at the same corona voltage. In the case of film samples prepared by blending of 0.5 wt. % PANSA5-PTS with LDPE, 475 V of voltage and 10.45 nC of charges were received by its surface which was dissipated up to 10 % cut off in 1.1 sec (Figure 30C). on the other hand, LDPE + 0.5 wt. % PANSA2-PTS showed + 800 V of surface voltage received by the composite on applying the voltage of +5000 V which showed the large decay time (2.0 sec at 10 % cut off). Similar behaviour was observed at negative polarity charging. Hence the ESD protection performance of the conducting blends not only depends on the loading level of conducting materials but also depend on the morphology and dispersion of conducting materials in the polymer matrix. Nanocomposites based on LDPE/PANSA5-PTS film showed better ESD performance as compared to LDPE/PANSA2-PTS film.
PANI/SiO2 nanocomposites were prepared by chemical oxidation polymerization of aniline and SiO2 by using ammonium persulfate (APS) as an oxidant in the presence of phosphoric acid/PFOA medium. FTIR, UV-Visible, cyclic voltammetry and SEM techniques confirmed the interaction of PANI with SiO2 particles. The excellent corrosion protection performance by PSC coated mild steel could be due to the strong adherence of polymer film which uniformly covers the entire electrode surface as has shown by the surface morphology. The corrosion current densities were lowered several orders of magnitude with these coatings. The coating had good protective efficiency which increased with increasing the loading of PSC to the maximum of 99 % at 6.0 wt.% loading and reduced to about 89.93 % after 60 days of immersion in highly corrosive environment confirming the improved coating performance. Weight loss method also revealed that PSC coated samples showed very low weight loss as well as negligible corrosion rate as compared to PANI coated samples at same immersion time, which indicates the better protection and adhesion of PSC onto the mild steel surface as compared to PANI in strong acidic condition.
In order to improve anticorrosion performance of iron in 3.5 % NaCl aqueous medium, preparation of highly hydrophobic polyaniline-SiO2 nano-composites (HPSC) have also been carried out by chemical oxidation polymerization. Water repellent property of the PSC has been developed by using fluorinated dopant i.e. perfluoro-octanoic acid (PFOA). HPSC coating were evaluated for protection of mild steel from corrosion in 3.5 % NaCl aqueous solution. Suitable coating with HPSC was formed on mild steel using epoxy resin by powder coating technique which showed the contact angle in the range of 115o. Corrosion protection efficiency of mild steel coated HPSC in 3.5 % NaCl aqueous solution has been evaluated using Tafel Extrapolation method, surface morphology, salt spray test and weight loss methods. The results reveals that the HPSC coating showed the significant reduction in the corrosion current density reflects the better protection of mild steel in marine environment. The coating had good protective efficiency which increased with increasing the loading of HPSC to the maximum of 96 % at 6.0 wt.% loading and reduced to about 93.3 % after 60 days of immersion in 3.5 % NaCl solution confirming the improved coating performance.
Presence of SiO2 nanoparticles entrapped in PANI chain which was evident my surface morphology of composite coating, provide the reinforcement to PANI chain which reduce the degradation of polymer chain in corrosive environment. PSC/HPSC coating protect metal by dual mechanism by forming passivating layer as well as act as a physical barrier. Furthermore the role of powder coating technique for achieving high quality, durable and good anticorrosive coatings have also been explained. These studies revealed that the polyaniline-SiO2 nanocomposites has excellent corrosion protection properties and it can be considered as a potential material for corrosion protection of mild steel in corrosive medium like.1.0 M HCl as well as 3.5 % NaCl solution.
In order to carry out the effective use of conducting polymer for antistatic application, nanocomposites based on poly(aniline -co- 1-amino-2-naphthol-4-sulphonic acid) (PANSA5-PTS) with low density polyethylene (LDPE) have been developed. The copolymer nanotubes of aniline and ANSA were synthesised in tosyl medium in 50: 50 molar ratio. Formation of nanotubes of copolymers was confirmed by morphological characterization using SEM and TEM. Dimension of nanotubes of PANSA5-PTS was found to be 80-90 nm. Blending of copolymers with LDPE was carried out in twin screw extruder by melt blending method by loading 0.5 wt. % and 1.0 wt. % of the conducting copolymer in LDPE matrix. The conductivity of the blown film of poly (AN-co-ANSA) /LDPE composites was found to be in the range of 1.28 x10-6 to 4.13x 10-9 S/cm. Thermo gravimetric traces of copolymers reveals that these copolymers were thermally stable from 180oC to 195oC. Such copolymers were successfully melt blended with LDPE and conducting film was prepared using film blending technique. Antistatic performance of PANSA5-PTS/LDPE nanocomposite have compared with PANSA2-PTS/LDPE composites to show the influence of nanotubes in composites. Static charge measurements carried out on the films shows that no charge is present on the surface. Copolymer/LDPE composites films (1.0 % w/w) showed static decay time in the order of 0.1 to 0.2 sec. at 10 % cut-off on recording the decay time from 5000 V to 500 V. When the loading level of copolymers in LDPE was reduced to 0.5 wt. %, only the nanocomposites based on PANSA5-PTS showed better good performance to ESD protection. Better antistatic behavior shown by these copolymers at very low loading in LDPE was investigated by their nanotubular morphology. Blending of 0.5 and 1.0 wt. % of PTSA doped copolymers with selective composition of ANSA and aniline with LDPE has a great potential to be used as effective antistatic films. The loading level, morphology of the conducting material, and its proper dispersion with insulating matrix affect the properties like surface conductivity, mechanical properties, and its performance to application for electrostatic charge dissipation.
Zhua H. Zhonga L. Xiaoa S. Gan F. 2004 49 5161
Jones D. A. 1992 New York
Lacroix J. C. Camalet J. L. Aeiyach S. Chane-Ching K. I. Petitjean J. Chauveau E. Lacaze P. C. 2000 481 76
Kinlen P. J. Menon V. Ding Y. 1999 146 3690
Kinlen P. J. Ding Y. Silverman D. C. 2002 58 490
de Souza S. da Silva J. E. P. de Torrosi S. I. C. Temperani M. L. A. Torresi R. M. 2001 4 B27
Samui A. B. Patankar A. S. Rangarajan J. Deb P. C. 2003 47
Dominis A. J. Spinks G. M. Wallace G. G. 2003 48 43
Sathiyanarayanan S. Muthukrishnan S. Venkatachari G. 2006 55 5
Plesu N. Ilia G. Pascariu A. Vlase G. 2006 156 230
Su S. J. Kuramuto N. 2001 114 147
Gurunathan K. Amalnerker D. P. Trivedi D. C. 2003 57 1642
Sathiyanarayanan S. Muthukrishnan S. Venkatachari G. Trivedi D. C. 2005 53 297
Deberry D. W. 1985 132 1027
Wessling B. 1991 41 907
Elsenbaumer R. L. Lu W. K. Wessling B. 1994 Seoul, Korea Abstract No. APL(POL)1
Wrobleski D. A. Benicewicz B. C. Thompson K. G. Byran C. 1994 35 265
Spinks G. M. Dominis A. J. Wallace G. G. Tallman D. E. 2002 6 85
Sathiyanarayanan S. Azim S. S. Venkatachari G. 2007 52 2068
Majumdar G. Goswami M. Sarma T. K. Paul A. Chattopadhyay A. 2005 21 1663
Chowdhury D. Paul A. Chattopadhyay A. 2005 21 4123
Feng X. M. Yang G. Xu Q. Hou W. H. Zhu J. J. 2006 27 31
Hasan M. Zhou Y. Mahfuz S. Jeelani S. 2006 429 181
Li X. Dai N. Wang G. Song X. 2008 107 403
Xia H. S. Wang Q. 2003 87 1811
Zengina H. Erkan B. 2010 21 216
Stejskal J. Kratochvı’l P. Armes S. P. Lascelles S. F. Riede A. Helmstedt M. Prokes J. Krivka I. 1996 29 6814
Al-Dulaimi A. A. Hashim S. Khan M. I. 2011 40 757
Beck F. Michaelis R. Scholoten F. Zinger B. 1994 39 229
Camalet J. L. Lacroix J. C. Aeiyach S. Chane-Ching K. Lacaze P. C. 1998 93 133
Kilmartin P. A. Trier L. Wright G. A. 2002 131 99
Meneguzzi A. A. P. Ferreira C. A. Pham M. C. Delamar M. Lacaze P. C. 1999 44 2149
Bhandari H. Choudhary V. Dhawan S. K. 2010 519 1031
Kinlen P. J. Menon V. Ding Y. J. 1999 146 3690
Talo A. Passiniemi P. Forse´n O. Yla¨saari S. 1997 85 1333
Wessling B. Posdorfer J. 1999 44 2139
Iribarren J. I. Armelin E. Liesa F. Casanovas J. Aleman C. 2006 57 683
Mc Andrew T. P. Miller S. A. Gilleinski A. G. Robeson L. M. 1996 74 204
Mc Hale G. Shirtcliffe N. J. Aqil S. Perry C. C. Newton M. I. 2004 93 36102
Shirtcliffe N. J. Mc Hale G. Newton M. L. Chabrol G. Perry C. C. 2004 16 1929
Wu X. F. Shi G. Q. 2006 110 11247
Jiang L. Zhao Y. Zhai J. 2004 43 4338
Jiang W. H. Wang G. J. He Y. N. An Y. L. Wang X. G. Song Y. L. Jiang L. 2005 Chin. Univ. (Chinese) 26, 1360
Han J. T. Zheng Y. Cho J. H. Xu X. Cho K. J. 2005 109 20773
Soeno T. Inokuchi K. Shiratori S. 2004 237 543
Li H. Wang X. Song Y. Liu Y. Li Q. L. Zhu D. 2001 113 1793
Wu Y. Sugimura H. Inoue Y. Takai O. 2002 8 47
Wang S. T. Feng L. Jiang L. 2006 18 767
Qu M. N. Zhang B. W. Song S. Y. Chen L. Zhang J. Y. Cao X. P. 2007 17 593
Pan Q. M. Jin H. Z. Wang H. B. 2007 18 355605
Yabu H. Takebayashi M. Tanake M. Shimomura M. 2005 21 3235
Li X. Reindhout D. Crego-Calama M. 2007 36 1350
Callies M. Quere D. 2005 1 55
Ma M. L. Hille R. M. 2006 11 193
Blossey R. 2003 2 301
Anoop Kumar. S. Bhandari H. Sharma C. Khatoon F. Dhawan S. K. 2012
Anoop Kumar. S. Bhandari H. Sharma C. Khatoon F. Dhawan S. K. 2012
Stern M. Geary A. 1957 104 56
Spinks G. M. Dominis A. J. Wallace G. G. Tallman D. E. 2002 6 85
Silverstein R. M. Webster F. X. 2002 sixth edition John Wiley and Son, Wiley India 165
Kim H. Foster C. Chiang J. Heegar A. J. 1989 29 285
Pron A. Rannou P. 2002; 27 135
Huerta-Vilca D. Moraes S. R. Motheo A. J. 2003 14 52
Mc Andrew T. P. Miller S. A. Gilleinski A. G. Robeson L. M. 1996 74 204
Kusy R. P. 1986( Dekker New York 1
Rosner R. B. 2001 1
Edenbaum J. Reinhold V. N. New York 615
Narkis M. Lidor G. Vaxman A. Zuri L. 1999 47 201
Li C. Liang T. Lu W. Tang C. Hu X. Cao M. Liang J. 2004 64 2089
Narkis M. Ram A. Stein A. Z. 1980 25 1515
Kobayashi T. Wood A. Takemura A. Ono A. 2006 64 377
Yukishige H. Koshima Y. Tanisho H. Kohara T. 1996
Angelopoulos M. 2001 Conducting polymers in microelectronics 45 1 57 76
Laska J. Żak K. Prón A. 1997 Conducting blends of polyaniline with conventional polymers 84 1 117 118
Mitzakoff S. De Paoli M. A. 1999 35 10 1791 1798.
Chubb J. N. 2002 54 233
Bhandari H. Bansal V. Choudhary V. Dhawan S. K. 2009 58 489
Chen S. A. Hwang G. W. 1996 29 3950
Bhandari H. 2011 Synthesis, Characterization and Evaluation of Conducting Copolymers for Corrosion Inhibition and Antistatic Applications Indian Institute of Technology Delhi, India
Bhandari H. Singh S. Choudhary V. Dhawan S. K. 2011 22 9 1319 1328
Strumpler R. Glatz-Reichenbach J. 1999 Conducting polymer composites 3 4 329 346.