Open access peer-reviewed chapter

Applications of Strontium Aluminate Cements

By Petr Ptáček

Reviewed: April 18th 2014Published: July 2nd 2014

DOI: 10.5772/58616

Downloaded: 2625

The applications such as dense or thermal insulating refractory materials, the preparation of seawater resistance concretes and as the protection against X-ray and gamma ration are supposed for strontium aluminate cements [12,14]. The option to use strontium aluminate cement for the preparation of MDF composites as was described in Chapter 6.4 is also mentioned.

1. Refractory materials

Refractory products(refractories) possess the ability to resist high temperatures without physical or chemical destruction, the corresponding properties are termed as refractoriness. These materials can be classified according to their temperature resistance, chemical composition, porosity, etc. According to the most general viewpoint the ceramic and non-ceramic refractory materials and products can be recognized [423].

Based on the chemical composition, the following types of refractory materials can be specified:

  • Oxide ceramics:are an extensive group of materials based on one or few oxides (SiO2, Al2O3, Cr2O3, ZrO2, MgO and CaO) and their stable compounds (ZrO∙SiO2, MgO∙Cr2O3, MgO∙Al2O3, 3Al2O3∙2SiO2...). The silica refractory products, alumina-silica refractory products with different content of alumina, basic refractory products, alumina-zirconia-silica refractory products, alumina-chromic oxide-zirconia-silica refractory products, etc., are the most common examples of these materials. The alumina silicate refractories are extensively used in metallurgical, ceramic and glass industries. These materials are made primarily of refractory and kaolinitic clays, which are used both in crude and grog forms [424,425]. Spinel (MgO⋅Al2O3) is very attractive as refractory material in heavy industries because of its high melting point, low thermal expansion, considerable hardness, high resistance to chemical attack, favorable chemical stability, and good thermal spalling [426].

  • Non-oxide ceramics:carbides (SiC

    The formation of SiC was firstly described by Berzelius in 1810 and 1821, but silicon carbide was latterly rediscovered by Despretz, Schützenberger and Moissan. The preparation of SiC on a large scale was managed by Acheson is 1891 who named the new substance as carborundum [429].

    [427-429], B4C [429-431], Al4C3 [432],...), nitrides (Si3N4 [433-435], BN [436], TiN [437], AlN [438], SiAlONs [439],...) silicides (MoSi2 [440,441]) can be considered as the most common types. Among the physico-chemical properties of material the kind of applied bound is an important factor for these materials.

  • Other:this type includes carbon or carbon containing refractory products such as Al2O3 – C [442,443], MgO-C [444], Al2O3-MgO-C [445,446], etc.

Another point of view for the classification of refractory products is the true porosity of refractory products:

  • Dense refractory products:brick and castables of low porosity [447].

  • Insulating refractory products:brick and castables of high porosity [447,448,498]. Insulating refractory castables are made of refractory light-weight aggregates, additives and HAC.

  • Ultra-light refractory products:are refractory materials with true porosity higher than 75 %.

The morphology of refractory materials enables to recognize:

  • Shaped refractory products:such as dense shaped refractory products, shaped insulating refractory products or fused cast refractory products.

  • Unshaped refractory products:refractory castables for linings and reparations.

1.1. Regular refractory castable

The design of structures made of hydraulic–bound ceramics and subjected to high thermal stresses is of great importance today [449]. The development of refractory castables is important due to their increasing applications in metallurgical, cement and chemical industries. In last decades an increasing trend among refractories has arrived towards the replacement of bricks by castable refractories. Refractory castables can be classified on the basis of different aspects including the CaO content, the binder source, the chemical composition, the fluidity, the bulk density, etc. Their binding system plays a relevant role in different processing steps, including the workability, the dry-out and the service performance. Therefore, all efforts are made to improve the bonding agents [450-452,462].

The first reference on calcium aluminate bound refractory castables is provided by Deville [453], who prepared a refractory crucible using alumina aggregate and aluminate cement in 1856. Calcium aluminate cement and its industrial production was patented by Lafarge in 1908 [12,454] and the first industrial production was by Lafarge in 1913 and became known as “Ciment Fondu” [7,12,455]. Calcium aluminate cements are normally made by complete fusion of limestone or lime and bauxite or other aluminous materials with low content of SiO2 at 1450 – 1600 °C. The molten clinker is tapped off continuously from the furnace, solidifies and its ground to the fines of about 3000 cm2∙g-1. Their properties include rapid strength development, good resistance to sulfates and many other forms of chemical attack [7,12].

During the hydration of calcium aluminate as the main constituent of calcium aluminate cement, different hydrate phases can be formed. Up to 10 °C the hexagonal prisms of CAH10 (mono-calcium aluminate hydrate) are formed as the major product of hydration. The primary formed CAH10 converts to hydrogarnet (C3AH6), the only thermodynamically stable hydrate phase in the C-A-H system (Eq.1).

3CAH10C3AH6+2AH3+18HE1
3C2AH82C3AH6+H3+9HE2

At temperatures above 10 °C, increasing amount of C2AH8 (di-calcium aluminate hydrate, strätlingite) is formed together with AH3, while the content of formed CAH10 decreases. The conversion reactions (Eqs.1 and 2) are accelerated at high temperatures and moisture. The process is also associated with the strength loss and the formation of microcracks in the concrete structure. Above 27 °C the CAH10 hydrate is not formed at all and above 50 °C the C3AH6 is the only product of hydration. The hydration reactions of calcium aluminate can be summarized by the scheme in Fig.1. The hydration of ferrite phase is much slower than that of CA and C3(A,F)H6 is formed as the final product of hydration, with C2(A,F)Hx and C4(A,F)Hx as intermediates [7,12,415,456-460].

Figure 1.

Hydration scheme of calcium aluminate cement [458].

Adding CaCO3 to calcium aluminate cement induced the C3A⋅CaCO3⋅11H hydrate formation (37 °C, samples immersed in water for 1 up to 30 days), inhibiting the formation/ conversion of CAH10 and C2AH8 metastable phases. Thus leading to better mechanical performance and dimensional stability. Moreover, although the mono-carbonate phase provides high mechanical strength to cement samples on the first day of curing, its decomposition combined with the C3AH6 and Al(OH)3 generation due to continuous hydration of CA and CA2 phases, seems to be one of the factors which lead to further improvement in compressive strength up to the 7th day [458].

CACs harden rapidly immediately after the massive precipitation of hydrates begins. Relatively high proportions of water are taken up in the hydration reactions, the theoretical w/c ratios needed for complete hydration of CA are 1.14, 0.63 and 0.46 for the formation of CAH10, C2AH8+AH3 and C3AH6+2AH3, respectively [7,12]. The properties of the main hydrates are listed in Table 1. If the slurry of calcium aluminate cement is mixed with anhydrite (or gypsum), lime, bentonite or lithium carbonate (accelerator), the reaction is brisk and ettringite is the major product of hydration [599].

HydrateChemical composition [%]TemperatureCrystalline structureDensityDecomposition[°C]
CaOAl2O3H2O[°C][g·cm-3]
CAH1016.630.153.5< 20Hexagonal1.72120
C2AH831.328.440.320 - 301.95170 – 195
C3AH644.427.028.6> 30Cubic2.52240 – 370
AH3---65.434.6> 30Hexagonal2.42100

Table 1.

Properties of hydrates formed in the strontium aluminate cement [460,461].

In monolithic refractories, calcium aluminate cement (CAC), one of the most widely used binders, promotes initial hardening and mechanical strength before firing. In the last few decades, the service life of alumina based refractory castables has been improved significantly by reducing the cement content. Carbon is not wetted by molten metal and does not melt, which is an excellent advantage for the refractory use. The reason for the cement content to be reduced is to prevent the formation of low melting temperature compounds in the presence of lime (CaO) [462-464].

Bond type1920s1930s1940s1950s1960s1970s1980s1990s2000s2010s →
Hydraulic bond
Based on hydraulic setting and hardening
Conventional cement bonded castables
(Silicate cement, low purity CA cement)
Pure CA cement bonded castables (CA cement with improved purity)
High purity CA cement bonded castables
(High purity CAC + uf.-Al2O3)
ρ-Al2O3 bonded castables
Hydratable Al2O3 bonded castables.
ChemicalPhosphate bonded castables (H3PO4 or Al(H2PO4)3 + MgO or CA)
Water glass bonded castables (Na2O∙nSiO2 + Na2SiF6)
Sulfate, chloride bonded castables (Al2(SO4)3 + CA, MgCl2 or MgSO4)
PolymerizationPolyphosphate bonded castables (Na5P3O10 or (NaPO3)6 + MgO, CaO or CA)
Resin bonded castables
(Phenol resin, Novalac resin + cross linker)
Hydraulic + coagulatingLow cement castables
(CAC + Clays, CAC + uf.-SiO2)
CoagulatingClay bonded castables (CA + Ca-, Na-clay)
Ultralow cement castables (uf.-SiO2, uf.-Al2O3 + CA)
Non-cement castables (uf.-SiO2, uf.-Al2O3 + electrolyte, uf.-SiO2 + MgO)
Sol bonded castables (silica sol, alumina sol + electrolytes)
Carbon bondedMgO – Carbon Castables
Nano-engineeredIn progress

Table 2.

Progress in binding system for refractory castables [451].

Different types of binding systems have been developed (Table 2) throughout the years starting with hydraulic bonding, in which higher amounts of calcium aluminate cement (CAC) were used, towards coagulating binders such as colloidal silica or alumina [450,451]. In general, the refractory castables can be considered as composites, where the bonding phase (matrix) is reinforced by particles of aggregate (reinforcement) [465,480].

Nevertheless, there are some drawbacks related to the use of CAC in the systems containing microsilica and/ or magnesia, as the presence of CaO coupled with these other oxides results in the formation of low melting point phase at high temperatures. Other important concerns for cement-based castables arise during the curing and dewatering steps, which must be performed carefully in order to reduce the explosive spalling probability. In order to minimize these drawbacks, the properties of the refractory castables were improved by decreasing the cement content [111,450,466,470].

Based on the content of cement, the following types of refractory castables are defined by ASTM C401-91 (Standard Classification of Alumina and Alumina Silicate Castable Refractories):

  • Normal Cement Refractory Castable (NCCs) or Conventional Cement Castables (CCs) where the content of CaO > 2.5 %.

  • Low Cement Refractory Castable (LCCs) where 2.5 > CaO > 1.0 %.

  • Ultra-low Cement Refractory Castable (ULCCs) where 1 > CaO > 0.2 %.

  • No-Cement Refractory Castable (NLCCs) also Zero Cement Refractory Castables (ZCCs) or Cement Free Castables (ZFCCs).

Another way often applied for the classification of refractory castables is based on the density and the bonding system (see Fig.2) [455].

Figure 2.

Types of Refractory Castables [455].

Calcium aluminate cement acts as a suspension lubricant and binder in fresh mix and after hardening in room temperature it provides the strength. Cement castables (CCs) are usually porous and open textured, due to relatively large amounts of water required for the hydration of AC. They also exhibit a characteristic drop in strength at intermediate temperatures as sluggish sintering does not allow the development of ceramic bond after breaking down the hydraulic bond. Furthermore, high content of lime in these castables favors the formation of low melting phases such as anorthite and gehlenite at elevated temperatures. These phases are known to degrade the refractoriness and corrosion resistance of conventional CCs [111,466].

Especially low-(LCC) and ultralow-cement castables (ULCC) are widely used in steel industry due to their superior rheological and physical properties. Initially, castable refractories were composed of only cement and aggregates. Then, the addition of deflocculants and fine fillers has followed with the aim to optimize and control the properties such as workability as a function of time [463]. Such castables have valuable properties, including low thermal expansion coefficient, good thermal conductivity, good thermal shock resistance, high resistance to slag and liquid metal corrosion and high strength at low and high temperatures. ULCC refractories have strong slag penetration resistance [462].

Different calcium-free binding systems such as hydratable alumina (HA), colloidal silica (CS) and colloidal alumina (CA) were developed for the refractory castables. Hydratable aluminas (HA) are amorphous mesophase transition aluminas (TA)

Transition aluminas are described in Chapter 4.1.

which are produced by flash calcination of gibbsite in the temperature interval from 400 to 800 °C

The process is commonly used for the production of catalysts, carriers and absorbents.

, which leads to high specific surface area transition phase of ρ-alumina (rho-alumina) [486,450,467-470].

The binding ability of ρ-alumina derives from its particular characteristic while undergoing the rehydration when in contact with water (or water vapor). During the hydration, a thick layer of gel is formed, a part of the gel subsequently crystallizes into traces of boehmite and major quantities of bayerite. The remaining gel phases were identified as boehmite gel or pseudo-boehmite (a poorly crystallized boehmite), together with totally amorphous gel, and may represent up to 60% of final hydrated phases, depending on the hydration temperature and pH. Interlocking bayerite crystals and gel confer the mechanical strength to green body of the refractory structure by filling pores and interfacial defects and by forming the honeycomb structures on the surface of aggregates attaching adjacent grains to each other and to the surrounding matrix [450,470,471].

The process of TA (transition aluminas) rehydration in Hydratable Alumina-bonded Refractory Castables (HAB)

Usually prepared by flash calcination of gibbsite.

can be expressed by the following reaction scheme [471,472]:

TA+H2OamorphousgelpseudoboehmiteboehmitebayeriteE3

The hydration process can be divided into four stages [458]:

  1. The intensive period of preliminary hydration.

  2. The induction period.

  3. The acceleratory period, in which the maximum speed of evolving heat is attained. The crystallization of amorphous gel phase and the formation of bayerite as well as the changes in the morphology of grains proceed in this period.

  4. The final period, where the amount of released heat decreases asymptotically.

Although hydratable aluminas outweigh the low-melting point phase generation associated with microsilica-containing CAC-bonded castables, there are still some drawbacks attributed to this binder. Compared to equivalent CAC formulations, HA-bonded castables require longer mixing time and high water contents due to high specific surface area of the binder. Moreover, after hardening, HA-containing castables form much less permeable structure in comparison with CAC bonded castables, which leads to higher explosive spalling probability during the water dry-out [450].

A great concern has been employed during recent years to refractory castables bound by nano-powders and colloidal suspensions in order to improve the refractory’s bonding and densification and the behaviour during sintering. Therefore the addition of nano-particles could improve the castable properties, as long as the nano-agglomeration problem is kept under control. High price of commercially available nano-powder products can also be a hindrance. Thus, nano-particles containing aqueous suspensions (colloidal binders) are preferred to nano-powders [450].

Among colloidal suspensions, the silica sol is of greatest interest for refractory castable applications. One of the reasons for its use is the possibility of mullite formation at low temperatures for alumina-rich systems. Actually, the reaction activity of nanoSiO2 particles in silica sol is extremely high. Colloidal particles can be absorbed on the surface of active α-Al2O3 ones and fill in their packing gaps, which can reduce the temperature of mullite formation, with suitable densification at about 1100 °C. Another reason for applying colloidal silica to refractory castables is related to its high solid contents, ranging from 15 to 50 wt. % of silica [450].

The fact of increasing the utilization of colloidal silica as a binder has initiated a discussion concerning the possibility of adding colloidal alumina for the same purpose. Despite the colloidal silica advantages, its addition always implies that SiO2 will be present in the final product, which would inhibit its use in various steel plant applications. This drawback was the driving force towards using colloidal alumina. At first, the addition of colloidal alumina was restricted to the contents lower than 1wt %, most likely due to processing difficulties such as high water demand and low flowability and workability. However, after overcoming these limitations, recently higher colloidal alumina solid contents (up to 4 wt. %) could be added to the refractory castables. For lower solid contents in the composition, the role of colloidal alumina as a binder may be insufficient whereas if it exceeds 4 wt. %, higher water amounts are required for mixing and the mechanical properties may be spoiled [450].

In addition to colloidal silica and alumina, there is also a report related to the utilization of mullite and spinel sols (Fig.3(a)) as bonding agents in high alumina ULCC castables [450,473,474]. These sols with low solid content (about 5 wt. %) in water suspension were prepared by the addition of silica fume and MgCl2 6H2O into vigorously stirred boehmite sol (Fig.3(b) and (c)) and used as an additive for CAC containing castables in order to evaluate their effect on physical and mechanical properties, as well as on slag corrosion and thermal shock resistance. The microsilica content in a spinel bound high alumina castable must be reduced to a very low level to eliminate the detrimental glassy phases or the formation of SiO2-Al2O3 melt at the temperatures close to 1250 °C [475,478].

Figure 3.

Preparation of co-precipitated spinel (a), sol-gel derived spinel (b) and mullite (c) [473,474].

The spinel additive from the sol–gel route contained more fine particles and showed better performance in castables than co-precipitated spinel additive, although both of them are energetically favorable to produce desired spinel phases at lower temperature but with significant volume expansion. The magnesium aluminate spinel (MA, MgAl2O4) is a very desirable phase in castables which improves the hot strength, the creep resistance, the thermal stability and restricts slag penetration of spinel containing castables [474,476,477,480].

Alumina-magnesia castables are widely known for their expansive behaviour, due to in situ formation of MgAl2O4 at temperatures higher than 1000 °C. CAC-containing alumina-magnesia castables performed better regarding the mechanical strength and thermal shock resistance. Nevertheless, they attained higher in situ expansion, due to the CA6 formation during the thermal treatment. An efficient way to control the volumetric stability can be achieved by the addition of hydratable alumina, as its shrinkage behaviour counterbalances the in situ spinel expansion. Furthermore, this binder leads to higher creep resistance and also low apparent porosity levels, which can be useful to reduce the slag infiltration [445,478,479].

Self-flow refractory castables (SRFC) are characterized by their consistency after mixing, which allows them to flow and de-air without the application of external energy, i.e. vibration. Added water promotes the flowability of the particulate system but it has to be kept at minimum dosage (typically between 3 and 8 wt.% in conventional castables), to avoid coarse particles segregation and the increase in final porosity. In order to compose the Self-Flow Refractory Castable, the deflocculants and the particle size distribution of aggregates have to be selected carefully since the particle size distribution is one of the most important factors that affect the refractory’s rheological properties [480-482].

The reliability of linings and pieces of refractories used in vessels (ovens, converters and ladles) must also be ensured because these structures are subjected to high temperatures under normal conditions. Previous studies were undertaken to model the thermo-mechanical behaviour of concrete and refractories. For these materials the temperature range of 20-800°C is of particular interest because, due to the dehydration, the cement undergoes significant microstructural transformations during the first thermal load [111,449].

These transformations considerably modify the thermo-mechanical behaviour of the material and must be taken into account for a realistic structural analysis. The chemical reactions may be described by the following equations [449]:

AH3AH+2HE4
AHA+HE5
C3AH6C3AH1.5+4.5HE6
C3AH1.5(C12A7,CA,CA2,CA7,A)+1.5HE7

The hydrogarnet phase C3AH6 is decomposed into two phases C12A7H and CH, the chemical condensed formula of which is C3AH1.5. Therefore it should be written [457,483]:

7C3AH6C12A7H+9CH+32HE8

Growing demand for refractory castables with designed properties has brought about continuous technological development involving the simultaneous understanding of particle size distribution, the use of additives improving workability as well as sintering additives and the binder performance [484].

1.2. Particle packing density

Particle packing density (PSD) was evaluated by the Andreasen model [463,480,485,486]:

CPFT=100×(DDL)n[%]E9

where CPFTdenotes the cumulative percent of grains finer than D, DL is the size of maximum used grain, Dmeans the grain size and nis the particle size distribution parameter.

Another packing model is proposed by Dinger and Funk [485,487]:

CPFT=100×(DqDSqDLqDSq)[%]E10

where DS and DL are the smallest and largest particle sizes, respectively. The parameter qis the coefficient, which depends on the particle size distribution.

Despite the fact that water is used in rather small amount (usually 3 – 8 % in convectional refractory castables), it still remains the key ingredient that enables to keep the desired rheological characteristics of fresh castable (Fig.4). Since water fills the voids between solid particles first, improving the packing density is an obvious way to reduce the water requirement. The workability can be improved by external vibration but when it is not possible or advisable, self-flow refractory castables (SFRC) are used. SFRC “works” as a suspension of powders in which the fine matrix is the flow medium that envelops the aggregate particles, fills in the voids between them and suspends them, promoting higher flowability [486-489].

Figure 4.

Factors influencing the rheology of castables [489].

1.3. Opening material

Opening material (aggregate) and filler usually improve the drying and firing shrinkage, the material mechanical properties, the thermal stability, the corrosion resistance and the thermal conductivity of refractory materials. Dense refractory castables from alumina-silica system often use corundum or calcined bauxite [110,131,463], mullite [484], refractory clays [423,490] or sand [491]. Moreover, the aggregates such as SiC [464,492,493] or zircon [494,495] are used.

1.4. Sintering additive

The use of boron-based sintering additive to speed up the refractory densification at lower temperatures can be a suitable alternative to develop novel compositions for fluid catalytic convertors (FCC) of petrochemical units [484]. Cr2O3 nanoparitcles are effective sintering additive for MgO based refractories due to the formation of MgCr2O4 spinel. The layer of spinel precipitates at the grain boundaries of MgO grains [496]. The addition of SiO2, CaCO3, TiO2 and Y2O3 also improves the densification of refractories based on MgCr2O4 spinel [497].

1.5. SrAC bound refractory castable

Refractory castables based on strontium aluminate cement can be prepared by mixing strontium aluminate cement, grog (Chapter 6.1.3) and additives (Chapter 5.4). The increase of Al2O3 content in the castable by the addition of corundum or calcined bauxite (Fig.3 in Chapter 2) shifts the equilibrium composition towards the high alumina phases (Fig.1 in Chapter 1.2) such as calcium dialuminate and calcium hexaaluminate. Build line or casted panel is less sensitive to humidity, because newly formed strontium aluminate phases are much less reactive after mixing with water (Fig.12 in Chapter 5) than original strontium aluminate cement.

Optical and electron microscopy of prepared refractory castable based on strontium aluminate cement is shown in Fig.5 and Fig.6, respectively.

Figure 5.

Optical microscopy of texture of SrAC bound refractory castable with bauxite aggregate.

Figure 6.

Electron microscopy of refractory castable before the thermal treatment.

The sample fired to the temperature of 1300 °C shows zero total shrinkage

Total shrinkage consists of the change of specimen dimensions during setting, drying and thermal treatment.

, therefore the castable has sufficient temperature stability that is necessary in order to avoid cracks formed during drying and further thermal treatment.

The texture of fired sample is shown in Fig.7. The texture of the material shows hexagonal plates, which are the pseudomorphosis of original hydrates. These hydrates are already decomposed at temperatures lower than 600 °C (please see Fig.5 in Chapter 5). Moreover, the excess of Al2O3 from applied aggregate (calcined bauxite) changes the equilibrium composition as was discussed above. Some sites show the initial stage of sintering process, i.e. the formation of necks between neighboring particles, and newly formed phases nucleating from the melted zone.

Figure 7.

Electron microscopy image of refractory castable treated to the temperature of 1300°C.

The recrystallization or better sinter-crystallization takes place in the material treated to the temperature of 1400 °C (Fig.8). The process is connected with increasing dimension

This expansion should be avoided by the addition of silica bearing component into the refractory castable as was discussed in Chapter 6.2.3.

of specimen, which is also visible in Fig.28 in Chapter 4. The first marks of crystallization of hexagonal plates from melted phase can be found in the SEM picture of the sample heated to the temperature of 1300 °C (Fig.7), but at the temperature of 1400 °C the sample crystals do not show glassy phase. Therefore, the crystallization from non-equilibrium melt takes place.

XRD analysis of sintered sample (Fig.8) confirms the formation of non-hydraulic compound (SrO⋅6Al2O3) due to the reaction with bauxite. The traces of quartz in bauxite cause the formation of feldspar strontian (SrO⋅Al2O3⋅2SiO2, described in Chapter 10.4).

Figure 8.

Electron microscopy image of refractory castable treated to the temperature of 1400°C.

Specimen heated to the temperature of 1500 °C (Fig.9) shows the volume density of 2.28 g⋅cm-3 and the cold crushing strength of 21.6 MPa. Measured expansion related to the thermal treatment to the temperature of 1500 °C is about 2.2 %. As the temperature increases, the small crystals are consumed during the large crystals growth and are dissolved in the melt phase.

Figure 9.

Electron microscopy image of refractory castable treated to the temperature of 1500°C.

Figure 10.

Electron microscopy image of refractory castable treated to the temperature of 1600°C.

After the treatment to the temperature of 1600 °C, the ceramic body of prepared refractory material consists of corundum (59 %), strontium hexaaluminate (29 %) and strontianite (12 %). Electron microscopy (Fig.10) shows that the specimen consists of large tabular pseudo-hexagonal crystals of SrA6 surrounded by solidified glass. The sintering process reduces the dimension and porosity of the sample.

Advertisement

2. Insulating refractoriness

Insulating firebricks (IFBs) represent one of the refractory groups which are most commonly used for the heat insulation in industrial applications today. They are highly porous and lightweight refractories having much lower thermal conductivity and heat capacity than other refractories. Different types of insulating firebricks are manufactured mainly by using the raw materials such as diatomite, perlite, expanded vermiculite, calcium silicate, fireclay, kaolin, quartz, alumina and lightweight refractory aggregates by conventional methods. The porosity is usually created by the addition of combustible material to the raw material mixture. During firing, the combustible material burns out, and leaves large fraction of pores within the fired body [498].

Different types of pore-formers such as sawdust, foam polystyrene, fine coke, binders and organic foams, or granular materials such as hollow microspheres and bubble alumina are commonly used to obtain decreased density or to produce porous bodies in the insulating material. A considerable research is carried out recently on the reuse of pulp and paper industry wastes as a new source of raw material or pore-former in the ceramic materials due to their organic and inorganic contents [498-501].

Insulating firebricks which have highly porous structure (between 45% and 90% porosity) exhibit low thermal conductivity values. The thermal conductivity not only depends on their total porosity, but also on their pore size and shape, chemical and mineralogical composition [498]. Insulating firebricks are classified by ASTM according to the bulk density and maximum service temperature [502]. The methods for measuring the weight, dimensional measurements and bulk density of the produced bricks are defined by ASTM C134-95 [503]. Apparent porosity measurements of samples were performed by immersion into boiling water for 2 h and soaking in water for 24 h [504]. The techniques for the assessment of cold crushing strength and thermal shock resistance are specified by ASTM C133-97 [505] and ASTM C1171-96 [506], respectively.

2.1. Fillers for thermal insulating refractory castables

Lightweight fillers make the structure of refractory castables lighter and provide required thermal insulating properties via the formation of pores in structure. Some examples of these materials are shown in Fig.11.

Figure 11.

Examples of lightweight filler: cenospheres, bubble alumina and fireclay.

2.2. Properties of refractory materials

Currently, we observe a noticeable change of climate, worldwide, probably associated with the global warming. In order to reduce the emission of greenhouse gases, especially of carbon dioxide, the generated energy should be reasonably managed. A very large amount of total energy produced in the world is heat. It is used in various industrial processes and buildings. The solution in saving the heat is a suitable construction of walls to ensure thermal insulation [507,508].

Most applications of ceramic materials are advantageously used as thermal-insulating or thermal-conducting materials. From the viewpoint of industrial applications, low thermal conductivity is needed for the thermal insulation, while high thermal conductivity is important for achieving the high heat release, high thermal shock resistance and temperature homogeneity throughout the material [509].

The quality control of thermal insulating materials typically focuses on the determination of thermal conductivity value (λ). For this purpose, special plate apparatuses are used, which are based on [510,511]:

  1. Stationary heat transfer conditions;

  2. Dynamic heat transfer conditions.

The heat flux vector (q¯) is given by the Fourier´s law [509,512]:

q¯=λgradTorq¯=λTE11
=(xi¯+yj¯+xk¯)E12

where λis the coefficient of thermal conductivity, Tis the temperature. The vectors of the basis are denoted as i, jand k.

Effective thermal conductivity(ETC) is one of the key thermophysical properties used to quantify the thermal behaviour of heterogeneous materials like granular metals, ceramics, ceramic raw materials, composites, inorganic or polymeric foams, catalysts, etc. Much of the effective thermal conductivity literature is concerned with porous materials; however, the term porous itself may be the cause of a confusion. In some situations it refers to granular or particulate materials, in which the void volume may be occupied by either liquid or gaseous components; alternatively, it may refer to the material having continuous solid matrix that contains pores/bubbles, which may be isolated or interconnected. The problems may arise when a model that has been shown to work well for one type of porous material is assumed to be applicable to another type, simply because both materials are described as porous [512-514].

The Francl´s model [512,515] calculates the effective thermal conductivity of porous material (λe) from the thermal conductivity of solid material (λs) and its porosity as follows:

λe=λs(1ε)E13

The law was shown to be effective for a certain porous material. However, if it were applied to a granular material such as sand, the thermal conductivity would be predicted with error of several orders of magnitude.

The influence of porosity (ε) and pore size (d) on the effective thermal conductivity is described as follows [516]:

λe=λs(1ε)+ελa+4dσT3E14

where the thermal conductivity of gas phase (λa) and the radiation transport of heat at the temperature Tare taken into account. σdenotes the Boltzmann constant.

The effective thermal conductivity of heterogeneous material is strongly affected by its composition and structure. Foams and porous materials can be considered as a two-phase (or two-component) systems consisting of solid skeleton and air, and the thermal conductivity can be described as the heat transfer through such complex system according to some of suggested analytical models [508,517-519].

Five structural models (Figs.12 and 13) are taken into account which can be expressed for two component system as follows [508,513,514,520-522,527]:

  1. Series model:

λe=1(1ν2)λ1+ν2λ2E15
  1. Parallel model:

λe=λ1(1ν2)+λ2ν2E16
  1. ME-1 (Maxwell-Eucken model with one continuous component) model:

λe=λ12λ1+λ22(λ1λ2)ν22λ1+λ2+(λ1λ2)ν2E17
  1. ME-2 (Maxwell-Eucken model with two continuous components) model:

λe=λ22λ2+λ12(λ2λ1)(1ν2)2λ2+λ1+(λ2λ1)(1ν2)E18
  1. EMT (Effective Medium Theory) model, which represents isotropic materials with two phases dispersed in continuous medium:

(1ν2)λ1λeλ1+2λe+ν2λ2λeλ2+2λe=0E19

The parameters λand νare the thermal conductivity and the volume fraction. The subscripts e, 1 and 2 represent two component material and its first and second constituents, respectively. The plot of relative thermal conductivity (λe/λ1) for two-component material with λ1/λ2=20 calculated according to the five structural models mentioned above is shown in Fig.12.

Figure 12.

Relative effective thermal conductivity according to different structural models [512].

If the system consists of icomponents and is considered for nsmall spheres with the radius Ri and the thermal conductivity λi, which are dispersed in uniform medium of thermal conductivity λm (Fig.13),the distribution of temperature for the single small sphere under steady-state conditions is given by the Laplace´s equation [508,512]:

1r2r(r2Tr)+1r2sinΘΘ(sinΘTΘ)+1r2sin2Θ2Tφ2=0E20

with following boundary conditions applied:

  • When r=0 then Ti ≠ ∞.

  • When r=Ri then λiTir=λiTmrandTiΘ=TmΘ.

  • When r>> Ri thenTm=brcosΘ.

where rand Θare the polar radius and the polar angle, respectively, Tis the temperature and bdenotes the temperature gradient in the continuous medium. Assuming the symmetry of the z-axis so that Tis independent of ϕ, Eq.20 has a general solution:

T=A+Br+CrcosΘ+Dr2cosΘE21

Figure 13.

Structural models applied for the derivation theory for thermal conductivity of multiphase material [508] and schematic representation of tw-component material as the uniform mixture of two fundamental structural models [522]: ME-1+ME-2 (a), Parallel+ME2(b), ME-1+EMT (c) and ME-2+EMT (d).

The solution using the boundary conditions to substitute for A, B, C and D in Eq.21 and further transformation yield to the equation [508]:

νi(λiλeλi+2λm)=0E22

For two-phase system (e.g. porous solid material – air) Eq.22 can be then written as:

(1ε)λsλeλs+2λm+ελaλeλa+2λm=0E23

where λand εare the thermal conductivity and the porosity and subscripts e, aand sdenote two-phase material, air and solid, respectively. Eq.23 represents individual structural models:

  • Series model when λm=0;

  • Parallel model when λm=∞;

  • Maxwell-Eucken model with one continuous component when λm=λs;

  • Maxwell-Eucken model with two continuous components when λm=λa;

  • EMT model when λm=λe.

To avoid potential misapplication of the effective thermal conductivity models, the materials which may be described as porous should be divided into two classes:

  1. Internal porosity materials which have bubbles/pores suspended within a continuous condensed phase (e.g. sponges, foams, honeycombs), where the optimal heat transfer pathway is through the continuous phase.

  2. External porosity materials which include granular particulate materials where the optimal heat conduction pathway is through the dispersed phase.

A model that accurately predicts the effective thermal conductivity of internal porosity materials will not necessarily be applicable to external porosity materials or vice versa.

Carson at al. [512] proposed that the effective thermal conductivity of internal porosity materials was bounded above by the Maxwell–Eucken equation for the lower-conductivity material as the dispersed phase, and below by the EMT equation; and that the effective thermal conductivity of external porosity materials is bounded above by the EMT equation, and below by the Maxwell–Eucken equation for the lower conductivity material as the continuous phase.

The equation which unifies five structural models mentioned above for heterogeneous material was developed by Wang [522]:

λe=i=1mλiνidiλ¯(di1)λ¯+λii=1mνidiλ¯(di1)λ¯+λiE24

Each structural model can be derived by suitable choice of parameters di and λ¯:

  • Series model when di=1orλ¯0;

  • Parallel model when di=orλ¯λi;

  • Maxwell-Eucken model when di=3orλ¯λm;

  • EMT model whendi=3orλ¯λe.

Parameter di can have a physical interpretation. Kirkpatrick [523] related similar parameter to the number of Euclidean dimensions of the system involved, while Fricke [524] and Hamilton and Crosser [525] related it to the sphericity of dispersed phase. However, it may be possible to define a parameter that combines both aspects; the component shape and the number of Euclidean dimensions. This is the topic of ongoing investigations by the authors, but it falls outside the scope of this publication. The most common approach is to use di=3 (spherical dispersed phase) [508,522].

The model suggested by Levy [526] is based on the Maxwell–Eucken model and is based solely on algebraic operations and has no stated physical basis:

λe=λ12λ1+λ22(λ1λ2)F2λ1+λ2+(λ1λ2)FE25

where

F=2G1+2ν2(2G1+2ν2)28ν2G2E26
G=(λ1λ2)2(λ1+λ2)2+λ1λ22E27

In order to make the basic structural models more general for different structures, the additional parameter is sometimes introduced. The Krischer’s approach assumed that the complex structure could be approximated by a mixture of simpler structures, where the relative amounts of each of the simpler structures was determined empirically. We define the ‘‘structure volume fractions (εj)’’ to be distinct from the component volume fractions (νi) for the j-th type of structure by the relation [522]:

εj=iνiϕijE28
jεj=1E29

The ‘‘structure composition factors’’ ϕij, are the measures of the fractions of material component ithat is a part of structure j. Therefore the total amount of component i must be distributed between the structures:

jϕij=1E30

The effective thermal conductivity of structureΛj, which consists of ncomponents, is the function:

Λj=Λj(ν1,ν2νn,ϕ1j,ϕ2jϕnj,λ1,λ2λm)E31

Since this structure can be described by one of five structural models listed above, it can be written as

Please consult with Eq.24.

:

Λj=i=1mλiνiϕijdiλ¯(di1)λ¯+λii=1mνiϕijdiλ¯(di1)λ¯+λiE32

The effective thermal conductivity of the material which is formed from zstructures can be considered for the function:

λe=λe(Λ1,Λ2Λz)E33

In order to solve Eq.32, based only on λi and νi without any empirical parameters, it is necessary to determine the expressions for ϕij as functions of λi and νi. Therefore, the assumption of relative amounts of each structure εj, in total volume and of relative contributions of different Λj to λe is necessary. The infinite number of relationships between ε´j and Λj could be found. It is possible to relate ε´j to structural characteristics. However, such detailed information is often unavailable. Therefore the simplest possible relationships were adopted. They are to assume that each structure comprises an equal fraction of total volume:

εj=1zE34

and that the thermal conductivity of each structure is equal to the effective thermal conductivity:

λe=Λ1=Λ2==ΛzE35

The solution for selected binary structure models (Fig.13) with suitable choice of di and λ¯according to Eq.24 can be expressed as follows [522]:

  1. ME-1+ME-2 model:

λe=λ1ν1ϕ11+λ2ν2(12ν1ϕ112λ2)(3λ12λ1+λ2)ν1ϕ11+ν2(12ν1ϕ112λ2)(3λ12λ1+λ2)E36
  1. Parallel+ME-2 model:

λe=λ1ν1ϕ11+λ2ν2ϕ21ν1ϕ11+ν2ϕ21=λ2ν2ϕ22+λ1ν1ϕ123λ22λ2+λ1ν2ϕ22+ν1ϕ123λ22λ2+λ1E37
  1. ME-1+EMT model:

λe=C+C2+2λ1λ22E38

where

C=(2λ1λ2)ν1(2ν1+2ν2ϕ2112ν1)+(2λ2λ1)ν2(1ϕ21)E39
  1. ME-2+EMT model:

λe=D+D2+2λ1λ22E40

where

D=(2λ1λ2)ν1(1ϕ11)+(2λ2λ1)ν2(2ν2+2ν1ϕ1112ν2)E41

For ternary-structure models composed of EMT+ME-2+Series the following can be derived [522]:

λe=λ1ν1ϕ123K2K+λ1+λ2ν2ϕ223K2K+λ2ν1ϕ123K2K+λ1+ν2ϕ223K2K+λ2E42

Where:

ν1ϕ11+ν2ϕ21=1/3ν1ϕ12+ν2ϕ22=1/3ν1ϕ13+ν2ϕ23=1/3ϕ11+ϕ12+ϕ13=1ϕ21+ϕ22+ϕ23=1

Krischer uses the empirical approach fwhich is sometimes referred as the distribution factor. This parameter ranges from 0 to 1 and serves as the weighting factor that makes the basic structural model more universal for different structures. The value of this parameter must be determined by the experiment. This parameter is used in [508,522,527]:

  • Krischer model, i.e. weighted harmonic mean between the series model and the parallel model:

λe=11fλ1(1ν2)+λ2ν2+f(1ν2λ1+ν2λ2)E43
  • Hamilton model:

λe=λ1(f1)λ1+λ2(f1)(λ1λ2)ν2(f1)λ1+λ2+(λ1λ2)ν2E44
  • Chaudhary-Bhandari model:

λe=[λ1(1ν2)+λ2ν2]f(1ν2λ1+ν2λ2)(1f)E45
  • Kirkpatrick model:

i=1νiλiλeλi+(f21)λe=0E46

2.3. Thermal insulating castables

The refractory castables filled by cenospheres (Fig.14), alumina bubbles (Fig.15) and fireclay (Fig.16) were prepared as an example of thermal insulating castables based on strontium aluminate cement. The specimens were prepared using strontium aluminate cement, bauxite and filler in the mass ratio of 1:3:1 and w/c=1. The applied opening material was described in Chapter 6.1.3.

Figure 14.

Thermal insulating castable based on cenospheres.

The microphotographs and some properties and information on applied filler can be found in Chapter 6.2.1.

Some properties of prepared samples of thermal insulating castables before and after (Fig.17) thermal treatment are listed in Table 3.

Used opening materialVolume density [g.cm-3]Shrinkage [%]Cold crushing strength [MPa]
After settingAfter thermal treatmentAutogenousThermal treatmentTotal
Cenosphere1.281.650.325.025.3---
Bubble alumina2.051.760.3+6.3*+6.6*16.2
Fireclay1.962.25+4.0*11.415.424.7

Table 3.

Properties of thermal insulating castable before and after thermal treatment to 1500°C.

* Expansion with regard to the initial volume of specimen.


While the dimensions of thermal insulating castables prepared with cenospheres and fireclay were reduced, the expansion was observed for the sample prepared with bubble alumina filler (Table 3).

Figure 15.

Thermal insulating castable filled with alumina bubbles.

The reason for the expansion behaviour of this sample is probably the same as for dense refractory castables filled by bauxite (Chapter 6.1.5). Observed behaviour provides some really interesting possibilities to control the volume changes during the thermal treatment. Since the addition of alumina led to the expansion (recrystallization) and the addition of fireclay to the shrinkage (formation of SrO Al2O3 2SiO2 and sintration), the proper mutual ratio of these constituents enables to prepare the dimension stable refractory.

Furthermore, the addition of fireclay enables to avoid undesirable growth of large crystals during the thermal treatment (please compare Figs.7-10). The introduction of cenospheres led to the formation of eutectic melt with iron, therefore they are not optimal for high temperatures and reductive conditions.

X-ray diffraction analysis of samples prepared with fireclay and cenospheres confirms the formation of strontianite and strontium hexaaluminate (SrA6) in the ceramic body (Fig.17(b)). Due to missing source of SiO2, strontianite isn’t formed in the sample prepared with bubble alumina. Corundum is the main phase in all prepared samples.

Figure 16.

Thermal insulating refractory castable prepared with fireclay.

Figure 17.

Specimens prepared with bubble alumina, fireclay and cenospheres treated to the temperature of 1500 °C (a) and x-ray diffraction analysis of prepared samples (b).

Figure 18.

Thermal insulating refractory castables with bubble alumina treated to the temperature of 1500 °C.

The microphotographs of fracture area of thermal insulating refractory castable filled with alumina bubbles after the thermal treatment is shown in Fig.18. The bubbles are surrounded by hexagonal crystals of recrystallized strontium aluminate matrix of binding phase. The inner side of alumina balls shows well-developed crystals of alumina.

Thermal insulating castable prepared with fireclay and fired to the temperature of 1500 °C is shown in Fig.19. The specimen texture shows large bauxite grains covered by matrix of recrystallized strontium aluminate phase where the artefacts of layered aggregate of fireclay filler can be seen.

Large amount of melt phase formed during the thermal treatment of specimen prepared with cenospheres led to extensive sintering, firing shrinkage and deformation of the shape. Cenospheres were completely dissolved in formed eutectic melt and there is no artefact in the body of specimen after the thermal treatment. The SEM analysis (Fig.20) shows the strontium aluminate crystals surrounded by glassy phase.

Figure 19.

Thermal insulating refractory castables with fireclay treated to the temperature of 1500 °C.

Figure 20.

Thermal insulating refractory castables with cenospheres treated to the temperature of 1500 °C.

3. Ceramic Foams

3.1. Properties and processing of ceramic foams

Foams can be defined as dispersion systems based on the bubble gas phase, usually air, in continuous matrix of liquids-“aqueous and non-aqueous liquid foams”, or solids “solid foams” (e.g. pumice as well as steel, glass and concrete foams). The diameter of bubbles is usually of several millimeters, but the spherical shape is not common as the weight of foam leads to mutual deformation and to the formation of irregular polyhedral cells. The structure of foams is often compared to honeycombs. The walls of bubbles make always the same angle of 120° hence maximum four bubbles can be in contact at one point. This structure provides foams with certain mechanical strength and elasticity [528-531].

Liquid foams are usually prepared via mechanical dispersion of gas in liquid in the presence of surfactants. These compounds reduce the surface tension via the formation of films on the interface as they contain both the hydrophobic and the hydrophilic groups. Foams are then always formed under dynamic conditions so the adsorption equilibrium of surfactant is usually not achieved. Applied kind and concentration of surfactant determine the time-stability and the structure of foams. Higher viscosity of surface layer, its flexibility and hydration of polar groups of surfactant decelerate the water flow-out from bubble walls and thus are the factors contributing to the time-stability of foams. This fact may have a significant effect on the magnitude of forces stabilizing the foam and foam films [530,532-536].

The research on the structure, behaviour and properties of foams is motivated by both, the preparation of foams and the prevention from undesirable formation of foam. For technical applications (usually filters, carriers of catalysts, biomaterials, thermal insulating materials, refractories [531,537,538]) the factors such as the stability, specific surface and porosity of foams are important. Foams were also used in wide range of industrial processes e.g. flotation [539].

As for the time-stability of foams, the control of bubble size and the preparation of monodispersed foams are intensively studied [540]. The structure and the processes of coarsening and drainage of foams [541] and their dynamics are also affected by fine particles [542-546].

Open cell (reticulated) ceramic foams, which are defined as dispersion systems based on the interconnected bubbles of gas phase in continuous ceramic matrix, can be prepared via different manufacturing techniques [531,547] including the transformation of ceramic powder slurry into the solid foam [536,548,549], the reticulated sponge method (replica technique) [550-553], the gel casting [554-557], the bubble generation methods [558] or direct foaming [559]. The replica technique is based on the pyrolysis of a polymeric sponge coated by ceramic slurry. Following high-temperature treatment leads to the ceramic bond via sintering. The gel casting method uses the mechanical work and foaming agents in order to foam the ceramic suspension.

Cellular cement is a lightweight material consisting of Portland cement (PC) [560,561], alumina cement (AC) [562,563] or blended cements [564,565] paste or mortar with homogeneous void or cell structure created by introducing air or gas in the form of small bubbles. Cement and concrete foams can be made by adding aluminium powder to the mix before adding gauging water or by injecting aqueous foaming agent to the cement slurry to give foams with the porosity of 50-90 %. Microsilica and a plasticizer were added to the cement-water slurry and polyester fibers were incorporated to improve the foam stability and strength [566-569]. Foamed concrete was patented in 1923 [570,571].

Using mixed cationic/anionic surfactants in aqueous foam systems has been of an interest for several years because they could provide good foam stability [572].Therefore the mixed surfactants used in pure aqueous foams are intensively studied [535,536,573].

In order to evaluate the maximum capillary pressure (PC,max [MPa]) and the effective bubble pressure for a stable bubble (ΔPeff [MPa]), the following relationships can be used [543,574,575]:

PC,max=4fγRP(cosΘ+Z)E47

and

ΔPeff=(Patm+2γRB+ρgH)[1f(1cos2Θ)]E48

where fis the fraction area of the bubble’s surface that is coated by particles, Θis the wetting angle of particles [°], RP is the particle’s radius [m], γis the surface tension [N m-1] on the gas-liquid interface and Zis a parameter related to the sort of particle configuration within the film, Patm is the atmospheric pressure [0.101 MPa], ρis the foam density [kg m-3], gis the gravity acceleration [m s-2], His the height of foam column [m] and 2RB is the bubble diameter. The term ρgHis also known as the hydraulic pressure. The Laplace pressure due to the radius of curvature of the bubble is considered in the term of 2γ/RB. The value of ΔPC,max is not the function of bubble size and Eq.48 is not a function of the particles size at the bubble’s film.

The approach for the calculation of foam “stability index” (SI) proposed by Vivaldini et al. [575] in order to combine the PC,maxΔPeff difference with ΔGads/kBTratio is given by the following equation:

SI=(PC,maxΔPeff)ΔGadskBTE49

where ΔGads is the adsorption free energy [J] of the particles at the bubble interface regarding their thermal energy expressed by term kBT[J]. The symbols kB and Tdenote the Boltzmann constant and the temperature, respectively. The dimension-less ratio ΔGads/kBT(adsorption energy/ thermal energy) then describes the stability of the gas-liquid interface.

When a particle is attached to a gas-liquid interface, the overall Gibbs free energy of the system is reduced, which makes this process thermodynamically favorable. The energy decrease due to this adsorption process at a flat interface can be for 0 ≤ Θ≤ 90° mathematically described by the equation:

ΔGads=πRP2γ(1cosΘ)2E50

Nevertheless, the ΔGads value cannot be used to state whether the interface is stable or not. That argument can only be sustained when the energy released due to the adsorption of particles is compared to their own thermal energy, which is the origin of the Brownian motion of colloidal particles in suspension [575,576].

3.2. Ceramic foams stabilized by HAC

Since water is consumed by hydration, calcium aluminate cement can be used for the stabilization of raw ceramic foams. Moreover, setting of cement confers the mechanical properties to foam, which enable the manipulation prior to drying and thermal treatment. Some examples of foamed materials prepared using the techniques described in works [577,578] are shown in Fig.21. The ceramic bond formed during the thermal treatment enables to cut tapes or desks by cutting and shaping the original foamed large cast profile.

Large aggregates of kaolinite particles are delaminated and redistributed closer to the surface of liquid phase to form the solid framework of foam. The thickness of the bubble walls is approximately ten times smaller than the median of particle size of applied kaolinite. Foam with the thickness of walls of 100 nm can be prepared. Hence forced delamination of kaolinite aggregates occurs and the lamellar particles of kaolinite form the framework or solid replica of original liquid bubble wall. The thermal treatment of foam provides the ceramic foam of high service temperature and chemical stability, with high specific surface area, extremely low volume density and excellent thermal insulating properties [577,579].

Figure 21.

Examples of refractory foam prepared with calcium aluminate cement (a). Raw and fired block of ceramic foam (b).

3.3. Ceramic foams stabilized by SrAC

Since the ceramic foam can be stabilized by calcium aluminate cement, it is possible to use also strontium aluminate cement for the same purpose. On the other hand, there are some differences in hydration and setting of both cements as was discussed in Chapter 5. The application of additives or certain modification of foam processing is necessary in order to improve the cement behaviour (Chapter 5.4).

Figure 22.

Raw foam before the thermal treatment.

The microphotograph of raw foam prepared via foaming the slurry prepared from strontium aluminate cement, meta-kaolinite and water in the mass ratio of 1:4:5 is shown in Fig.22. Applied method is analogical to the techniques used for the preparation of foam with calcium aluminate cement [577,578], but formed structure is quite different from the foam prepared with kaolinite. The reorganization of particles from original aggregates of kaolinite does not occur in metakaolinite. That results in the formation of thick-walled cells with more spherical shape.

Figure 23.

Foam after the thermal treatment to 1500 °C.

The morphology of foam cells before and after the thermal treatment shows that the walls of cells in foam form an angle of ~120°. The microphotograph of foam treated to the temperature of 1500 °C is shown in Fig.23. The SEM picture shows sintered foam, where the side walls of bubbles contain large amount of needle-like crystals of mullite.

The results of thermal analysis (Fig.24(a)) show that drying, the thermal decomposition of hydrates and the pyrolysis of surfactant takes place up to the temperature of 300 °C. Large surface of foamed structure supports the carbonation. Therefore the content of carbonates in foamed samples is usually higher than that in dense materials. The thermal decomposition of SrCO3 and removing of residual water from metakaolinite leads to the decrease of the sample mas by 3.4 % within the temperature range from 550 to 900 °C. SrO formed during the thermal decomposition of strontium carbonate is a reactive species which reacts with both, metakaolinite and other strontium aluminates, to strontium aluminate and Sr-gehlenite (strontio-gehlenite, SrAl2SiO7 [580,581]).

Figure 24.

TG-DTA (a) and heating microscopy (b) of raw foam.

The abundance of metakaolinite leads to the formation of usual and well described products such as Al-Si spinel phase and mullite [582,583]. Strontium bearing aluminosilicates are further transformed to Sr-celsian with increasing temperature [584-586,893]. The temperature, which is required for the preparation of sintered sample was determined by heating microscopy (Fig.24(b) and Fig.25). The sintering begins at the temperature of 1350 °C.

Figure 25.

The behaviour of specimen of foam during heating to the temperature of 1550 °C at the rate of 5 °C min-1.

Infrared spectrum of foam before the thermal treatment (Fig.26(a)) shows the features of meta-kaolinite [587], strontium carbonate, hydrogarnet, gibbsite, surfactant (C-H stretching in -CH3 and -CH2 groups in the region from 2975 to 2825 cm-1) as well as the stretching (3440 cm-1) and bending bands (1460 cm-1) of absorbed water. The spectral features of SrCO3, gibbsite and Sr3AH6 were already described in Chapter 5.1. Excessive carbonation results from high surface of foam.

Figure 26.

Infrared spectrum of raw foam (a), foam after the thermal treatment (b) and XRD of foam after the thermal treatment to 1500 °C (c).

After the thermal treatment (Fig.26(b)), the characteristic absorption bands of mullite (3Al2O3 2SiO2) [583,588,589] and Sr-celsian, the Si-O stretching (1095 cm-1) and bending (455 cm-1) can be recognized in the spectra. The results of x-ray diffraction analysis (Fig.26(c)) confirm mullite and Sr-celsian as the main components in the sample.

4. MDF composites

Macro-defect-free (MDF) cements were developed by the research group led by Birchall at ICI during late 1970s and early 1980s [590]. MDF cements have unusual and superior properties compared to traditional cement pastes and concretes, and are often referred to as chemically bound ceramics or MDF composites. The suggestions of applications of MDF cements are extremely wide ranging. These include roofing tiles, fire resistant doors, sewage pipes, airport bridges, window shutters, plastic moulds, printing rollers, thermal insulators, tube exhaust, oil tanks, corrosion resistant tanks, cable duct covers, electric generator propellers, electrical parts, boat decking, brake lining, body armor, pallets, toys, cryogenic vessels, signboards, cooler boxes, sound insulators and electromagnetic interference screenings [591,592].

However, after 25 years since they were first patented, the incorporation of MDF materials into commercial processes has been very limited. Despite the identification of many potential applications, MDF cements have certain limitations, in particular the loss of strength on exposure to moisture or humidity. The modifications of the MDF manufacturing process and the selection of polymer used have overcome many of these problems. The major obstacles restraining MDF cements from many applications are the economics of manufacturing on a large scale and their overall commercial viability compared to existing materials [591-593].

The manufacture of MDF cement involves high shear mixing of selected polymers and hydraulic cements at low w/cratios typically between 0.08 and 0.20. The key stages of the typical MDF preparation process are shown in Fig. 27. Calcium aluminate cement (CAC), polyvinyl alcohol (PVA) and glycerol are the most applied input materials [12,592].

Figure 27.

Typical stages of MDF manufacturing process [592].

MDF microstructure was described as close packed unhydrated cement grains within a three dimensional PVA network, with the coatings of hydrated cement on the surface, which interacts with the bulk polymer via chemical cross-linking. MDF cements comprise three distinct regions [592,594]:

  1. Unhydrated cement grainsdue to the low w/cratio there is a stoichiometric deficit of water that restrains all cement from full hydration;

  2. Bulk polymer phase;

  3. Complexinter-phase region which includes hydrated cement particles and polymer chains

A new alternative to MDF composites is the CAPR composites (Calcium Aluminate Phenol Resin), which are produced using the processing similar to that required for MDF cement manufacture (Fig.27). In CAPR composites high alumina cement (or other hydraulic cement) is mixed with a phenol resin precursor. A modifier is used to control the cross linking density and glycerol is added as a plasticizer. The process does not involve the addition of water and the cement is hydrated only by water given off by the phenol precursor during the condensation polymerization reaction that occurs in situ. This can lead to CAPR composites with an effective w/c ratio as low as 0.01 [592,595-597].

The formation of pastes in both systems is shown in Fig.28. Calcium-rich calcium aluminates, CaO, and Ca(OH)2 showed high reactivity with phenol resin during roll milling while calcined alumina showed poor combining during roll milling. This indicates that Ca2+ion is the reactive component whereas Al3+ions control the excessive stiffness of the high alumina cement/phenol resin system.

Figure 28.

Flow chart of the preparation process of CAPR [595].

The formation of pastes in both systems is shown in Fig.29. Calcium-rich calcium aluminates, CaO, and Ca(OH)2 showed high reactivity with phenol resin during roll milling while calcined alumina showed poor combining during roll milling. This indicates that Ca2+ion is the reactive component whereas Al3+ions control the excessive stiffness of the high alumina cement/phenol resin system.

Higher strength was achieved by Al3+ion-rich calcium aluminate cements, and lower strength of calcium silicate based OPC indicates that the presence of Al3+ions is essential for active thermal curing. On the basis of these observations, we suppose that the phenol resin precursor cross-links with Ca2+ions of cement through an ionic cross-linking reaction during the roll milling and then with Al3+ions through a chemical cross-linking reaction during thermal curing [598].

Figure 29.

Mechanism of the paste formation of MDF system CA – PVA (a) and of CAPR composite (b) [597].

4.1. MDF composites based on strontium aluminate cement

MDF cement based on strontium aluminate is a promising material for the preparation of refractory products with thin wall and complicated shape. MDF composites based on strontium aluminate cement can be prepared by similar way as MDF cements based on calcium aluminate cement (Fig.27). A certain drawback is fast hydration of strontium aluminate cement, therefore the utilization of additives improving the workability of cement mixture with polymer and plasticizer is necessary.

Figure 30.

Preparation of strontium aluminate based MDF using twin roll mixer.

The MDF material in Fig.30 is the first prepared sample of macro defect free composite based on strontium aluminate cement. It was prepared from the mixture of SrA cement, glycerol and PVA. After premixing of MDF components the mixing on twin roll mixer was performed. The sample compacted between two steel plates was then cured at the temperature of 60 °C.

Figure 31.

SEM analysis of MDF from strontium aluminate cement.

The SEM picture in the BSE-COMPO mode in Fig.31 shows the structure of prepared material where unhydrated grains of strontium aluminate cement were covered by the layer of hydration products. On the other hand the structure is not optimal due to fast hydration of strontium aluminate cement. Therefore, the additives improving cement workability are necessary in order to prepare MDF of higher quality. The other interesting options for the preparation of MDF should be the utilization of SrAC and CAC blend (Chapter 7.1.1) or the structural modification of the main clinker phase, e.g. by B2O3 (Chapter 7.3.2).

The preparation of shell of refractory product requires the thermal treatment to the temperatures, at which the ceramics bond is form. The behaviour of hydrated cement upon the thermal treatment is described in Chapter 6.5 and some properties of the product after the thermal treatment in Chapter 6.4.2.

4.2. Using MDF for refractory purposes

The options to use MDF composites prepared from strontium aluminate cement for refractory purposes require the information on the behaviour at high temperatures. High temperature heating microscopy performed up to the temperature of 1600 °C shows the thermal stability of MDF based on strontium aluminate cement (Fig.32).

Figure 32.

Heating microscopy of SrAC MDF specimen.

The initial shrinkage of specimen of about 3 % which takes place below the temperature of 600 °C is caused by the thermal decomposition of hydrates. The synthesis of strontium and tri-strontium aluminate from the product of dehydration and the thermal decomposition of strontium carbonate leads to the small expansion of 1 % within the temperature range from 650 to 900 °C. Up to the temperature of 1290 °C, the single thermal expansion of the sample takes place with the average thermal expansion coefficient of 1.073⋅10-5 K-1. The length contraction of sample occurs at temperatures higher than 1290 °C. The start of sintering was observed at the temperature of 1400 °C, but the change of height was still very small (about 2 %) at the temperature of 1600 °C.

The SEM image of MDF heated to the temperature of the start of sintering for 1 hour, where newly formed ceramic bond substitutes the hydraulic bond, which was lost during the thermal decomposition of hydrates (Chapter 6.5) is shown in Fig.33. The fracture area morphology shows the formation of necks (first stage sintering) between grains. In this stage, the material reaches the flexural strength of 14.6 MPa and the Young´s module of 5.2 GPa.

Figure 33.

SEM image of fracture area of strontium aluminate MDF treated to the temperature of 1400 °C

5. Behaviour of hydrated cement stone during thermal treatment

The processes which take place during the thermal treatment of materials based on hardened strontium aluminate cement include the thermal decomposition of hydrates, repeated synthesis of strontium aluminate phases and sintering (formation of ceramic bond) in the case that material was treated to sufficient temperature. In the materials prepared with opening materials (aggregate) the newly formed phases appear. Their composition depends on the kind of applied aggregate.

Figure 34.

Kissinger plot [379].

The Kissinger plot related to the thermal decomposition of hydrates is shown in Fig.34. Table 4 summarizes the kinetic results of the behaviour of hardened strontium aluminate cement stone during the thermal treatment.

PhaseEaAαmw1/2nThe description of the mechanism of process
[kJ∙mol-1][s-1][%][°C]
SrAH7467.79·10549.5050.00.92Growth of particles of appreciable initial volume, needles and plates of finite long dimensions.
AH3 gel2003.46·102252.1324.320.79Growth of particles of appreciable initial volume, thickening of very large plates.
γ-AH31081.45·102250.489.144.18Interface-controlled growth of a new phase, constant or increasing nucleation rate.
Sr3AH61173.94·101049.7017.752.54Diffusion-controlled growth of a new phase, constant or increasing nucleation rate.
SrC¯5922.28·102446,1119.312.31Diffusion-controlled growth of a new phase, decreasing nucleation rate.
SrA6424.30·102654.2517.952.48Diffusion-controlled growth of a new phase, constant or decreasing nucleation rate.

Table 4.

Mechanism and kinetics of thermal decomposition of hydration products.

The final product of the thermal treatment of hydrated cement stone is also strontium aluminate, i.e. the same compound as in the original clinker phase. Nevertheless it is formed through different reaction pathway compared to the original mixture of raw materials.

The thermal treatment of hydraulically bound refractory castables based on strontium aluminate cements leads to the thermal decomposition of hydrates. Disappearing of hydraulic bond naturally leads to decreasing strength, but bonding function is gradually adopted by ceramic bond formed with increasing temperature. The sintering of cement stone takes place at temperatures higher than 1400 °C (Fig.32) and the material becomes almost dehydrated at temperatures higher than 600 °C (Fig.35 and Fig.5 in Chapter 5). Therefore, there is a temperature range with significantly reduced strength.

The influence of temperature on to the equilibrium composition of hydrated cement stone with the composition corresponding to the 28th day of hydration process (Fig.2 in Chapter 5) is shown in Fig.35(a). The thermal treatment leads to the same compounds as the processing of strontium aluminate clinker from the mixture of raw materials (Fig.30 in Chapter 4). On the other hand, there is one significant difference, which is that the hydration process leads to better homogeneity than can be reached by the processing of raw material. That facilitates the solid state synthesis of clinker minerals.

Figure 35.

Effect of temperature on the equilibrium composition of hydrated cement stone (a) and hypothetical NCC (b).

The utilization of pure strontium aluminate cement without opening material (corundum, bauxite, mullite, fireclay, etc.) is not supposed, therefore Fig.35b shows the temperature evolution of equilibrium of refractory material in which the content of Al2O3 is increased to 90 % by the addition of alumina. These systems do not prefer the formation of tri-strontium aluminate.

The tri-strontium aluminate hexahydrate (Sr3AH6) is the main product of hydration of strontium aluminate cement. The thermal decomposition of analogical C3AH6 phase (Eqs.6 and 7), the calculation of the dependence of equilibrium composition on the temperature (Fig.35) as well as the thermal analysis of hydrated samples (Figs.5 and 15(a) in Chapter 5) indicate the formation of strontium hydroxide during thermal decomposition of Sr3AH6. Assuming analogical thermals decomposition sequence as for C3AH6, it can be written as:

Sr3AH6Sr3AH1.5+4.5HE51
Sr3AH1.5anhydrousphases+1.5HE52

The theoretical mass loss on ignition for Sr3AH6 phase is 15.56+5.19=20.75 %. The mass loss of 15.36+4.98=20.34 % can be read from the first and second step of TG curve in Fig.15 in Chapter 5. That indicates that the thermal decomposition of tri-strontium aluminate hexahydrate can be described by Eqs.51 and 52. Therefore it should be written as:

7Sr3AH6Sr12A7H+9SrH+32H.E53

Notes

  • The formation of SiC was firstly described by Berzelius in 1810 and 1821, but silicon carbide was latterly rediscovered by Despretz, Schützenberger and Moissan. The preparation of SiC on a large scale was managed by Acheson is 1891 who named the new substance as carborundum [429].
  • Transition aluminas are described in Chapter 4.1.
  • The process is commonly used for the production of catalysts, carriers and absorbents.
  • Usually prepared by flash calcination of gibbsite.
  • Total shrinkage consists of the change of specimen dimensions during setting, drying and thermal treatment.
  • This expansion should be avoided by the addition of silica bearing component into the refractory castable as was discussed in Chapter 6.2.3.
  • Please consult with Eq.24.

© 2014 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Petr Ptáček (July 2nd 2014). Applications of Strontium Aluminate Cements, Strontium Aluminate - Cement Fundamentals, Manufacturing, Hydration, Setting Behaviour and Applications, Petr Ptacek, IntechOpen, DOI: 10.5772/58616. Available from:

chapter statistics

2625total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

Related Content

This Book

Next chapter

Blended and Multicomponent Cements Based on Strontium Aluminate

By Petr Ptáček

Related Book

First chapter

Introduction to Apatites

By Petr Ptáček

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us