TiO2 Nanoparticles Prepared by Sol-Gel Method for Anode Application in Lithium-Ion Batteries

By Wafaa Nachit, S. Touhtouh, Z. Ramzi, K. Benkhouja and R. Yazami

Submitted: June 11th 2018Reviewed: September 10th 2018Published: April 30th 2019

DOI: 10.5772/intechopen.81406

Downloaded: 258


TiO 2 nanoparticles are prepared via sol-gel method using titanium tetraisopropoxide (TTIP) as a precursor under refluxing and controlled pH. It is found that pure anatase phase is obtained with pH 10. Further characterization studies are carried out on pure nanoparticle anatase phase by XRD, SEM, and transmission electron microscope (TEM). Their electrochemical performances as anode material in lithium-ion batteries are investigated by cyclic voltammetry, galvanostatic cycling, and rate capability measurements. A high discharge capacity of 321 mAh/g (vs. 335 mAh/g theoretical) is achieved at 1C rate. After the first galvanostatic charge/discharge cycle, voltage profiles show plateaus at 1.75 and 1.95 V versus Li at discharge and charge, respectively. High Coulombic efficiency (>99%) is maintained after 300 cycles, which makes anatase TiO 2 nanoparticles prepared by sol-gel method, a very promising material for anode application in lithium rechargeable batteries.


  • TiO2 nanoparticles
  • anode
  • lithium-ion batteries
  • electrochemical characteristics

1. Introduction

Nanostructured titania (NST) TiO2is a very promising alternative anode material compared with the commercialized lithium titanate Li4Ti15O12and graphite materials for lithium-ion battery application in particular when fast charging is required [1, 2, 3]. Fast charging while keeping long battery operational life is one of the most challenging tasks in lithium-ion batteries nowadays. Both mobile electronics and electro-mobility sectors need fast charging to compensate for relatively low energy density which impacts the operation time and driving range. One serious option to cope with charging time limitations resides in developing new materials able to store large amounts of lithium in a very short time. Nanomaterials, including NST, are among the most promising in this regard.

Good performances of NST result from their outstanding characteristics such as:

  1. A low volumetric change upon lithium-ion intercalation and de-intercalation providing a high crystal structure stability and long cycle life

  2. A fast diffusivity of lithium ions within the TiO2structure providing fast charging and high power discharge

  3. A practical low operating voltage

  4. An enhanced safety

Several methods have been used for the synthesis of NST, including hydrothermal [4, 5, 6, 7, 8, 9, 10], sol-gel [5, 6, 7, 8, 9, 10, 11], hydrolysis [12, 13], atomic layer deposition [14], and anode deposition [15], for the most reported in the literature. According to the synthesis method and to the post-thermal treatment conditions, NST of different morphologies are obtained such as nanorods [4, 17], nanotubes [5, 6, 8, 9, 14, 17], nanofibers/nanowires [11, 12, 13, 14, 15, 16, 17, 18, 19, 20], nanoparticles [6, 7, 10], nanocomposites [12, 21], nanofilms, and nanosheets [15, 22].

Several polymorphs of TiO2are known such as tetragonal rutile and anatase, orthorhombic brookite, and monoclinic TiO2(B) [23]. Anatase and TiO2(B) have open-channel structure and show high cycle capacity compared to rutile TiO2[24]. Anatase has edge-sharing TiO6octahedra so that planar double chains are formed with a tetragonal body-centered space group (I41/amd) [25].

Li-ion diffusion in anatase occurs along the octahedral interstitial sites up to Li0.5TiO2composition. Then the tetragonal structure reversibly transforms to the orthorhombic phase [26, 27, 28, 29, 30]. Anatase TiO2anode material reversibly uptakes 0.5 Li per TiO2formula with lithium insertion/extraction taking place at relatively low voltage and showing fast kinetics [29, 30]. However, 0.5 Li per TiO2corresponds to half of theoretical capacity of 335 mAh/g [31, 32, 33]. Enhancing practical capacity in NST should make this material more attractive for anode application in lithium-ion batteries [34].

When wet chemistry route is used to prepare NST, the medium pH is of a significant importance in the crystal structure and morphology of the final product [32]. Syntheses of TiO2 anatase were mostly performed in acidic media usually at pH greater than 4.5 [33]. To the authors’ knowledge, there has been no report on sol-gel preparation of NST in alkaline pH.

In this chapter, we show that unlike in acidic pH, which lead to mixed phases, pure anatase NST is obtained via sol-gel at pH 10. NST prepared at different pH are analyzed by XRD, transmission electron microscope (TEM), and SEM. The electrochemical properties of pure anatase phase NST are investigated by cyclic voltammetry and galvanostatic cycling, including rate capability tests in view of its application as anode material in lithium-ion batteries.

2. Experimental

2.1 Sample preparation

NST are prepared via sol-gel method using titanium tetraisopropoxide (TTIP), distilled water, and 2-propanol. Hydrochloric acid and sodium hydroxide are mixed in 24 mL of 2-propanol to fix the pH to 1, 4, 10, and 13 and to control the hydrolysis process of the solution. 24 mL of TTIP is then slowly added to the mixture, followed by refluxing at 70°C to obtain the sol. 10 mL of distilled water is added to the solution and left for 1 h under stir heating.

The obtained gel is dried at 70°C in air and then calcined at 500°C in air to produce NST powders.

2.2 Characterization

NST are characterized by X-ray diffractometry (XRD) using a PR-XPERT diffractometer (PW3064) with CuKα radiation (λ = 1.5406 Å), operating at 45 kV and 40 mA in 2θ angular range of 10–70°. The morphology and particle size were examined by transmission electron microscope (TEM, JEOL, JEM-2010) and by field-emission scanning electron microscopy (FESEM, JEOL JSM-7600F, 5 kV).

2.3 Electrochemical measurements

The anode is prepared by mixing NST prepared at pH 10 as active material, acetylene carbon black as electronic conductor, and polyvinylidene fluoride (PVDF) as a binder in the weight ratio of 80:10:10 with N-methyl-2-pyrrolidone (NMP) to form a slurry. The slurry was coated on a copper foil by doctor blade and then vacuum dried at 110°C for 6 h. The anode loading is ~0.8 mg cm−2. Lithium half-cells are assembled in a glove box under ultra-dry argon atmosphere (<1 ppm H2Oand O2). Lithium metal was used as the counter and reference electrode. The electrolyte consisted of 1.0 M LiPF6solution in ethylene carbonate (EC) and diethyl carbonate (DEC) at a volumetric ratio of 1:1. The separator is microporous polyethylene. Li/NST half-cells are investigated by cyclic voltammetry at 0.2 mV/s sweeping rate and by galvanostatic cycling at 1C–20 C rates, all between 1.0 V and 3.0 V versus Li.

3. Results and discussion

3.1 Physical characterizations

Figure 1 shows the XRD patterns of TiO2nanoparticles prepared at pH 1, 4, 10, and 13 and calcined at 500°C. X-ray patterns of anatase, rutile, and brookite are shown for reference.

Figure 1.

XRD patterns of titania nanoparticles made at different pH. Anatase, rutile, and brookite spectra are also shown for reference.

The sample prepared at pH 1 consists mostly of the rutile phase. All other samples are anatase with brookite impurities at pH 4 and 13. TiO2 nanoparticles synthesized at pH 10 consist of highly crystalline anatase phase (00-004-0477). Table 1 summarizes the XRD data of TiO2 nanoparticles synthesized at pH 10 including diffraction peak 2θ, interlayer spacing “d,” and hkl indexes. Table 2 gives the crystallographic characteristics of TiO2anatase phase prepared at pH 10 as derived from the XRD data Rietveld refinement. Average crystallite sizes of nanoparticles synthesized at different pH are reported in Table 3 using Scherrer’s equation. The particle size is in ~20–30 nm range with no obvious trends versus pH.

2θ (º)d (nm)(hkl)

Table 1.

Indexation of XRD peaks on TiO2 nanoparticles obtained at pH 10.

Phaseα β γLattice parameters
(Tetragonal I41)
α = β = γ = 90°a = b = 3.783c = 9.5190

Table 2.

Characteristics of anatase crystal structure.

pHPhaseD (nm)

Table 3.

Crystallite size of TiO2 nanoparticles synthesized at different pH.

Figure 2 shows TEM images of TiO2nanoparticles prepared at pH 10 at different magnifications. Figure 2a and b shows primary particles with relatively narrow size distribution. High-resolution TEM of Figure 2c shows the polycrystalline nature of the TiO2nanoparticles with well-resolved layers such as those assigned to the orientation corresponding to an interlayer of about 0.36 nm as indicated by an arrow.

Figure 2.

TEM images at different magnifications of TiO2 nanoparticles prepared at pH 10. (a, b) Image analysis enables size distribution to be achieved. HR-TEM image of (c) shows polycrystalline structure with some preferred layer orientation such as with interlayer spacing of about 3.6 nm.

TEM image analysis allows particle-size distribution to be determined as shown in Figure 3. The particle-size distribution is built on a discrete set of clearly identifiable grains, and, therefore, it is not necessarily representative of the overall description of the sample. This is especially true for grain sizes close to the distribution tails where the probability of finding a very large or a very small grain under the TEM objective is rather low. The average size of about 17 nm is slightly lower than the one estimated from the XRD data.

Figure 3.

Grain size distribution for the TiO2 at pH 10 from the TEM image analysis.

SEM images of NST pH 10 are displayed in Figure 4a and b. High magnification Figure 4a shows primary particles with narrow size distribution aggregate into secondary particles of about 150–600 nm in size, whereas lower magnification Figure 4b shows agglomerated particles remain basically submicron in size.

Figure 4.

SEM images of TiO2 nanoparticles synthesized at pH 10.

3.2 Electrochemical characterizations

Figure 1ashows cyclic voltammograms of the Li/NST of pH 10 half-cell at 0.2 mV/s sweeping rate for 5 cycles. In the first cycle, two reduction peaks appear at 2.15 V and at 1.75 V, respectively, whereas only one re-oxidation peak is present at 2.10 V. In the following 4 cycles, only the reduction peak at 1.75 V and re-oxidation peak at 2.10 V appeared. The first reduction peak at 2.15 V accounts for about 50% of the total discharge capacity of about 320 mAh/g, which is close to theoretical capacity of 335 mAh/g of TiO2corresponding to 1 Li/TiO2ratio. The second reduction peak at 1.75 V accounts for the second half of the total capacity and is matched by the re-oxidation peak at 2.1 V. This situation remained almost unchanged during the four following cycles, that is, the capacity of the reduction peak at 1.75 V matches the one of the re-oxidation peaks at 2.1 V of about 140 mAh/g.

The data shown above are confirmed during the two first galvanostatic cycles of the Li/NST cell displayed in Figure 5b. The first discharge profile shows two semi-plateaus at about 2.15 and 1.75 V, respectively, whereas the charge profile shows a main plateau at about 2.0 V. The first discharge semi-plateau accounts for nearly half of the total discharge capacity. The second half discharge capacity is matched by the charge capacity.

Figure 5.

Electrochemical tests performed on Li/TiO2 (pH 10) half-cells. (a) Cyclic voltammograms (CVs) at a scan rate of 0.2 mV/s for the first 5 cycles within a potential range from 1 to 3.0 V (vs. Li/Li+), (b) discharge-charge capacity of the first and second cycles at a specific current of 175 mA/g (1C), and (c) cycle capacity profile at 1C rate for 50 cycles.

Cyclic voltammetry and galvanostatic data suggest a two-step electrode reaction process:

  1. Irreversible formation of Li0.5TiO2at ~ 2.15 V average voltage.

  2. Reversible formation of Li1TiO2from Li0.5TiO2at ~ 1.75 V. During re-oxidation Li0.5TiO2is formed from Li1TiO2at about 2.1 V.

The formation of lithium-rich Li1TiO2is supported by both theoretical and experimental data [30, 31, 32, 33, 34, 35]. In the anatase phase, orthorhombic Li0.5TiO2and distorted rock-salt structure Li1TiO2 in which lithium cation occupy the octahedral sites have been stabilized due to kinetic effects. Metastability has been reported in Li-poor TiO2[30]. Accordingly, our data are consistent with reversible lithium intercalation in the stoichiometry range 0.5 < x < 1 in anatase LixTiO2, which corresponds to a theoretical capacity of 167.5 mAh/g. The cycle capacity profile in Figure 5c shows a plateau at about 120 mAh/g at 350 mA/g rate. A lower capacity may be due to limitation in lithium uptake to Li0.85TiO2and Li0.7TiO2as reported in [36, 37].

The intercalation mechanism of Li ions into anatase has been studied in a variety of experimental and theoretical works [38]. The lithium-ion intercalation can be described by the following Eq. (1):


TiO2maximum theoretical capacity is 335 mAh/g [39] which corresponds to x = 1 and to the complete reduction of Ti4+to Ti3+. This makes TiO2a highly competitive alternative to graphite anodes [40].

Practical capacity of anatase TiO2is about 200 mAh/g associated with 0.6 Li mole reversible intercalation at 1.78 V versus Li+/Li [41]. It has been demonstrated that Li1TiO2composition can be obtained from anatase TiO2at high temperature [30] or with particle size below 7 nm [42].

The discharge-charge profiles at current rates ranging from 1.0C to 20C and corresponding rate capability profiles are depicted in Figure 6a and b, respectively. It is worth noticing that after 10 cycles at 20C rate where capacity decreased to about 50 mAh/g, the capacity at 1C rate was recovered during the following 10 cycles to about 137 mAh/g. This indicates a high stability of the anatase TiO2nanoparticles based anode toward high rate cycling.

Figure 6.

Rate capability (1C–20C) tests performed on Li/TiO2 (pH 10) half-cells. (a) Discharge-charge voltage profiles, (b) discharge-charge capacity profile, and (c) cycle capacity and Coulombic efficiency profiles at 2C rate.

Figure 6c shows the cycle capacity profile at 2C rate for 300 cycles together with Coulombic efficiency. The latter stabilizes close to unity after the first 5 cycles, whereas the capacity gradually dropped to 82.4 mAh/g after 300 cycles indicating the high capacity retention and good cycling stability.

4. Conclusion

TiO2 nanoparticles are synthesized by simple sol-gel method at different pH values and found to have particle size of 10–30 nm. XRD measurements show that the sample prepared at pH 10 crystallized to pure anatase phase. The TEM and the SEM images confirm the formation of nanoparticles with diameters of 10–30 nm. The TiO2nanoparticles prepared at pH 10 exhibit initial capacity of 321 mAh/g and a remarkable high Coulombic efficiency close to unity after 300 cycles at 2C rate. However, the first cycle efficiency is relatively low perhaps due to inherent metastability of Li-poor phases at the early stage of lithium intercalation. More work has currently been performed to improve the first cycle efficiency, therefore making anatase nanoparticles based anode more practical in rechargeable lithium batteries with fast charge and high lithium storage capacity. Among possible routes considered to improve the NTO initial cycle efficiency is the incorporation of a few amounts of lithium during sol-gel process so as to achieve a pre-lithiated phase making it easier to add more lithium during the first cathodic process.

© 2019 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution-NonCommercial 4.0 License, which permits use, distribution and reproduction for non-commercial purposes, provided the original is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Wafaa Nachit, S. Touhtouh, Z. Ramzi, K. Benkhouja and R. Yazami (April 30th 2019). TiO<sub>2</sub> Nanoparticles Prepared by Sol-Gel Method for Anode Application in Lithium-Ion Batteries, Lithium-ion Batteries - Thin Film for Energy Materials and Devices, Mitsunobu Sato, Li Lu and Hiroki Nagai, IntechOpen, DOI: 10.5772/intechopen.81406. Available from:

chapter statistics

258total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

Related Content

This Book

Next chapter

Surface Chemical Analysis of Solid-Electrolyte Interphase Layer on Germanium Thin Films and the Effect of Vinylene Carbonate Electrolyte Additive

By Silpasree S. Jayasree, Shantikumar Nair and Dhamodaran Santhanagopalan

Related Book

Electromotive Force and Measurement in Several Systems

Edited by Sadik Kara

First chapter

Quantum Theory of Thermoelectric Power (Seebeck Coefficient)

By Shigeji Fujita and Akira Suzuki

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.