Ni41Co9Mn31.5Ga18.5 is a magnetic Heusler alloy, which indicates metamagnetic transition at the reverse martensite transition. In this paper, caloric measurements were performed and discussed about magnetocaloric effect. We also performed magnetization measurements around Curie temperature TC in the martensite phase and analyzed by means of the spin fluctuation theory of itinerant electron magnetism. From the differential scanning calorimetry (DSC) measurements in zero fields, the value of the latent heat λ was obtained as 2.63 kJ/kg, and in magnetic fields the value was not changed. The entropy change ΔS was − 7.0 J/(kgK) in zero fields and gradually increases with increasing magnetic fields. The relative cooling power (RCP) was 104 J/kg at 2.0 T, which was comparable with In doped Ni41Co9Mn32Ga16In2 alloy.

Part of the book: Progress in Metallic Alloys

By Takumi Kihara, Xiao Xu, Wataru Ito, Ryosuke Kainuma, Yoshiya Adachi, Takeshi Kanomata and Masashi Tokunaga

Recently, metamagnetic shape memory alloys have attracted much attention as candidates for the rare-earth free magnetic refrigerants. These materials undergo the martensitic transformation (MT) at around room temperature accompanied by a significant entropy change. The application of the magnetic field at the low-temperature martensitic phase realizes the magnetic field-induced martensitic transformation (MFIMT). Through the MFIMT, the materials show an unconventional magnetocaloric effect (MCE), which is called inverse magnetocaloric effect (IMCE). In this chapter, the direct measurement system of MCE in pulsed-high-magnetic fields is introduced. With taking the advantage of the fast field-sweep rate of pulsed field, adiabatic measurements of MCE are carried out at various temperatures. Using this technique, the IMCEs of the metamagnetic shape memory alloys NiCoMnIn and NiCoMnGa are directly measured as adiabatic temperature changes in pulsed fields. From the experimental data of MCE for NiCoMnIn, the entropy of spin system in the austenite phase is estimated through a simple mean-field model. By the combination of MCE, magnetization and specific heat measurements, the electronic, lattice and magnetic contributions to the IMCE are individually evaluated. The result for NiCoMnIn demonstrates that lattice entropy plays the dominant role for IMCE in this material.

Part of the book: Shape Memory Alloys