A Case Study: Particulate-Filled Polyester Hybrid Laminated Composites
The aim of this work was to develop the novel glass fiber–reinforced polyester hybrid composites (PHCs) filled with micro-sized titania (TiO2) particles and investigate their functional, mechanical and thermal behaviors. To equip PHCs of unsaturated polyester resin (UPR) with multifunctional characteristics, TiO2 particles (1–5 wt.%) were dispersed with high disperser homogenizer using hand lay-up process (HLUP), combined with compression molding technique (CMT). The interactions (cross linking and hydrogen bonding) between polymeric chains, styrene, silica contents of glass fiber and TiO2 particles in PHCs were confirmed by Fourier transform infrared spectroscopy (FTIR). The mechanical and thermal properties increased brilliantly by potential utilization of TiO2 particles. The 3 wt.% of TiO2-imbedded PHCs showed remarkable progress in tensile strength (46 MPa) as well as tensile modules (2.9 GPa) relative to unloaded PHCs. The 5 wt.% of TiO2-imbedded PHCs showed 61 and 64% increase in impact energy and hardness, respectively. Thermo-gravimetric analysis (TGA) showed that controlled PHC-0 had the mass loss up to 50%, which was restricted to 17% by using TiO2 particles for PHC-5. Hence, it was inferred that micro-sized TiO2 was encouraging filler for incremental valuation in functional, mechanical and thermal characteristics of PHCs. After finding the marvelous mechanical and thermal properties of PHCs, it is endorsed that these polyester composites can be tested for high strength and high temperature applications.
Part of the book: Polyester