In this chapter, the detailed characterization of processes of grain fragmentation and refinement resulting from gradual imposition of strain by individual equal‐channel angular pressing (ECAP) passes is reported. A great emphasis is placed on the processing of materials with different crystal structure, particularly the face‐centred cubic (FCC), the body‐centred cubic (BCC) and the hexagonal close‐packed (HCP). Advanced techniques of electron microscopy, electron and X‐ray diffraction and positron annihilation spectroscopy have been employed to characterize microstructure, texture and defect evolution in the material as a function of strain imposed by ECAP. Microstructure development was correlated with mechanical properties obtained by both mechanical tests and microhardness measurements. Processes controlling the microstructure refinement and texture development were identified and discussed in detail.
Part of the book: Severe Plastic Deformation Techniques
This chapter reviews the thermal stability of ultra-fine grained (UFG) microstructure in selected magnesium and titanium-based materials prepared by severe plastic deformation (SPD). The focus is on the wide palette of experimental methods applicable for investigation of microstructural stability. These methods include scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), microhardness measurement, positron annihilation spectroscopy (PAS), and electrical resistance measurement. Microstructural stability of UFG commercially pure (CP) Ti and Ti-6Al-7Nb alloy produced by equal-channel angular pressing (ECAP) is studied ex situ after annealing by SEM, by microhardness measurements, and in situ during heating, by high precision electrical resistance measurements. Both materials show stable UFG structure up to 440°C. Further annealing causes recovery and recrystallization of the microstructure. At 650°C, the microstructure is completely recrystallized. Magnesium alloy AZ31 is prepared by hot extrusion followed by ECAP. UFG microstructure recovers and continuously recrystallizes during annealing. The microstructure of UFG AZ31 alloy is stable up to 170°C and subsequent grain growth is analyzed. Special attention is paid to interpret the activation energy of the grain growth. The superplastic properties of UFG AZ31 alloy are investigated in the temperature range of 170–250°C.
Part of the book: Severe Plastic Deformation Techniques