Abstract

From the past few decades, photodetectors (PDs) are being regarded as crucial components of many photonic devices which are being used in various important applications. However, the PDs based on the traditional bulk semiconductors still face a lot of challenges as far as the device performance is concerned. To overcome these limitations, a novel class of two-dimensional materials known as transition metal dichalcogenides (TMDCs) has shown great promise. The TMDCs-based PDs have been reported to exhibit competitive figures of merit to the state-of-the-art PDs, however, their production is still limited to laboratory scale due to limitations in the conventional fabrication methods. Compared to these traditional synthesis approaches, the technique of pulsed laser deposition (PLD) offers several merits. PLD is a physical vapor deposition approach, which is performed in an ultrahigh-vacuum environment. Therefore, the products are expected to be clean and free from contaminants. Most importantly, PLD enables actualization of large-area thin films, which can have a significant potential in the modern semiconductor industry. In the current chapter, the growth of TMDCs by PLD for applications in photodetection has been discussed, with a detailed analysis on the recent advancements in this area. The chapter will be concluded by providing an outlook and perspective on the strategies to overcome the shortcomings associated with the current devices.

Keywords

  • two-dimensional semiconductors
  • transition metal dichalcogenides
  • pulsed laser deposition
  • photodetectors

1. Introduction

Photodetectors (PDs) are the optoelectronic devices which convert incident optical signals into electrical outputs through the phenomenon of light-matter interaction, which can be processed by the conventional read-out electronics. PDs form the basis of many vital components present in numerous electronic and optoelectronic devices as they find applications in a broad range of fields such as in photovoltaics [1, 2], military and defense technology [3], optical communication [4], remote sensing [3], biomedical imaging [5], environmental and ozone layer monitoring [4], and so on. Therefore, highly efficient photodetection has become very crucial for the industrial and scientific communities. With advancements in the matured technology of three-dimensional (3D) semiconductors [6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17] such as gallium nitride (GaN), zinc oxide (ZnO), indium gallium nitride (InGaN), indium nitride (InN), gallium oxide (Ga2O3), gallium arsenide (GaAs), silicon (Si), aluminum gallium nitride (AlGaN), germanium (Ge), mercury cadmium telluride (HgCdTe), gallium antimonide (GaSb), and so forth, high-performance PDs sensitive to wavelengths in the entire ultraviolet (UV)-far infrared (FIR) have been successfully fabricated. However, further advances in these PDs are hindered by the certain drawbacks encountered due to the intrinsic limitations in 3D semiconductors such as lower charge carrier mobilities, low light absorption properties, presence of dangling bonds at the interface, high fabrication costs involved, and so forth [18]. Thus, it is crucial to explore alternate materials, which can overcome the above-mentioned drawbacks for the development of multifunctional PDs.

The successful delamination of graphene in the revolutionary work by Geim and Novoselov in 2004 [19] ignited a plethora of research, in the field of two-dimensional (2D) layered materials and their heterostructures [20, 21, 22]. In the recent years, the amount of research focused on these layered materials has increased multifold. A layered material is nothing but an ultrathin phase of a material, scaled down to the level of atomic thickness, and is characterized by weak inter-layer van der Waals (vdW) forces and a strong intra-layer covalent interaction [23]. This makes these ultrathin materials possess electronic and optoelectronic properties such as band gap, mobility, etc., that are thickness-dependent [24], and thus, their novel chemical and physical characteristics pave a way towards the unexplored areas, both in the fields of fundamental research as well as engineering applications. In spite of possessing unparalleled electronic and optoelectronic properties such as high carrier mobility, dangling bonds-free surface, large current carrying capacities, excellent mechanical properties, the zero band gap or the gapless electronic structure of graphene [25] limits its use in realization of practical applications-based PDs, which demand switching behavior or in other words, a definite on/off state. This has led to the exploration of graphene alternatives with a substantial band gap, and researchers and scientists across the world have resurrected a class of conventional 2D materials known as the transition metal dichalcogenides (TMDCs), characterized by low-fabrication cost, chemical stability, earth-abundance and environment-friendly properties. Some of the well-studied TMDCs are molybdenum disulfide (MoS2), tungsten disulfide (WS2), molybdenum diselenide (MoSe2), molybdenum ditelluride (MoTe2), tungsten diselenide (WSe2), and so on [26, 27, 28]. As of now, semiconductors of the TMDC family have enabled tremendous accomplishments in the field of photodetection, such as from monofunctional to multifunctional PDs, from homogeneous to hybrid 2D semiconductors-based PDs, and from rigid to flexible electronic devices [29, 30, 31].

Regardless of the efforts of the researchers and scientists, some common challenges are still being faced related to fabrication and the performance of these TMDCs-based devices [18]. The challenges include growth of high-quality crystals, controlling the morphology and the thickness, scaling up the growth for industrial scale production, optimizing the device architectures, and so forth. To address these challenges, pulsed laser deposition (PLD) has emerged as a perfect tool for the synthesis of TMDCs. With the use of PLD, the actualization of high quality and wafer scale synthesis of TMDCs has become possible [32]. Eminently, PDs based on the PLD-synthesized TMDCs have exhibited competitive device performance parameters when compared with the commercial PDs, and thus, offer great opportunities towards the next generation photonics. In the subsequent section, we will give an introduction about TMDCs and their properties. Afterwards, the fundamentals of PLD will be discussed in detail, followed by the recent advancements in the PLD-grown TMDCs for photodetection application. Finally, we will conclude by highlighting the unresolved problems and suggest future perspectives in this evolving field of optoelectronics.

2. Transition metal dichalcogenides (TMDCs)

TMDCs are denoted by the general formula of MX2 where M and X represent a transition metal (Mo, Nb, W, Hf, Ti, and so on), and a chalcogen (S, Te, and Se), respectively. In the periodic table, groups IV-X belong to the transition metals and they contain different number of d-electrons. Thus, the difference in the valance d-electrons of different transition metals gives rise to the different electronic properties such as metallic, semiconducting, and superconducting [33]. TMDCs exist in a layered form at the atomic level, containing one or few monolayers. Figure 1(a) shows a schematic depicting the layered structure of MoS2.

Figure 1.

(a) Schematic showing a monolayer of a TMDC, where the atoms of transition metal are bonded through covalent bonds with the chalcogen atoms. These individual monolayers are stacked and held together by vdW forces to form the bulk structures. (b) Crystal structures of layered MoS2 with different stacking sequences as shown to form the two most common phases: trigonal prismatic (2H) and octahedral (1T). Figure is adapted from Ref. [23]. (c) Transformation of the band structure of 2H phase of MoS2 calculated by first principles from bulk to a single layer. Figure is adapted and reproduced with permission from Ref. [36].

A TMDC can exist in various structural phases which are a result of the different co-ordinations of the transition metal atom. The most common structural phases in which the TMDCs crystallize are the trigonal prismatic (2H) and the octahedral (1T) phase. These crystal phases can also be seen in the terms of different stacking sequences of the atoms (as a representative result, Figure 1(b) shows crystal structure of MoS2). The three atomic planes i.e. chalcogen– metal–chalcogen form the individual layers of TMDCs. The 2H phase corresponds to an ABA stacking, whereas, the 1T phase is characterized by an ABC stacking order. For most of the bulk TMDCs (MoS2, MoSe2, MoTe2, WS2, WSe2, etc.), the 2H phase is thermodynamically more stable than the metastable 1T phase. Tungsten ditelluride (WTe2) shows an exception where the most stable phase is the orthorhombic (1Td phase) at room temperature [33].

The assortment of chemical compositions as well as the different crystal structures of TMDCs results in varying band structure characters, which in turn lead to a wide range of electronic properties. In the thermodynamically most stable 2H phase, MoS2, WS2, MoSe2, and WSe2 show semiconducting behavior [33]. These semiconducting properties accentuated these TMDCs as potential 2D materials for next generation electronic devices. As a representative result, the basic characteristics of the band structure of MoS2 has been shown in Figure 1(c). The transformation of the band structure as calculated from density functional theory (DFT) for 2H-MoS2 upon increasing its thickness from monolayer form to the bulk has been shown in Figure 1(c). The positions of the conduction and valence band edges change with increasing the number of layers of MoS2, and the direct band gap in the monolayer form changes into an indirect band gap in the bulk material [33]. The calculated value of the band gap of the monolayer 2H-MoS2 is ~1.89 eV [34]. The experimentally observed value for the electronic band gap of 2H-MoS2 in its monolayer form is 2.15 eV [35]. Notably, the conduction band minimum and the valence band maximum are situated at the two inequivalent high-symmetry points, which represent the corners of the hexagonal Brillouin zone [33]. This attribute is common between monolayer 2H phase MoS2 (and the other group VI single-layer 2H phase TMDCs) and graphene and allows the observation of potential valleytronics applications.

Through the persistent efforts over the last decade, researchers have developed several techniques to produce ultrathin TMDCs. In principle, these techniques can be broadly classified into two categories. The first one is to produce TMDCs by thinning bulk crystals, which is called as a top-down technique. Different types of exfoliations (mechanical, chemical, etc.) fall under this category. Since different layers of 2D materials are held together by vdW interactions, therefore, the interlayer bonding is weak. Thus, under any external perturbations, bulk 2D materials are readily processed into their few-layered forms. The second category is to produce TMDCs through a bottom-up approach, where constituent atoms and molecules are assembled together to form continuous layers. These mainly include chemical vapor deposition (CVD), atomic layer deposition (ALD), magnetron sputtering, molecular beam epitaxy (MBE) and PLD.

As mentioned above, researchers have developed several methods to fabricate TMDCs. In spite of the substantial progress, none of the above techniques can meet the comprehensive demands for industrial-scale production, as in the terms of process simplicity, good scalability, excellent homogeneity and continuity, high quality of the products, high compositional and thickness control, low cost for mass production and higher safety. The techniques such as exfoliation, CVD and ALD suffer from a huge drawback that the growth process occurs in absence of high vacuum, which generally leads to unclean interfaces, and therefore, one has to compromise with the device performance. Moreover, exfoliation and CVD are further associated with low product yield as the films formed are non-continuous and in the range of several microns. Sputtering and MBE are much more sophisticated in terms of the interface quality due to the involvement of ultrahigh vacuum, however, sputtering is characterized by poor surface quality of the films whereas MBE poses drawbacks such as bulky and expensive setups, time-consuming growths, and limitations in terms of substrates. Such limitations further hinder the utilization of these growth methods for industrial scale fabrication of devices. Thus, research and development towards a potentially competent approach which can address the above issues is greatly required.

PLD is a synthesis technique where a high-power pulsed laser beam is focused on a target, which results in the vaporization of the material in the form of a plasma plume and this material gets deposited on a substrate in the form of a thin film. A typical illustration of a PLD process is shown in Figure 2. Compared with the conventional methods discussed above, PLD exhibits the following advantages:

  • PLD is the most versatile growth method where a focused and high-energy pulsed laser ionizes almost all types of materials, because of the generation of instantaneous and localized high temperatures up to tens of thousands of OC on the target’s surface. Therefore, majority of the materials can be ablated to form a plasma, which carries out the deposition. In addition, PLD exhibits an excellent compatibility with different substrates which provides numerous routes for the construction of heterojunctions-based devices.

  • PLD is highly scalable, because the plasma plume can be readily positioned and directed just by adjusting the external optical path of the laser beam. Consequently, PLD is very much suitable for the growth of wafer-scale and uniform TMDCs for practical industrial production. Serna et al. [37] have successfully fabricated continuous bilayers of MoS2 on sapphire with a diameter up to ~50.8 mm using PLD. Singh et al. [38] have also synthesized centimeter-scale MoS2 thin films on various substrates.

  • The substrate temperature required for the PLD growth of TMDCs is relatively low when compared with techniques like CVD and sputtering because the species (atoms, molecules, ions, etc.) ablated by the focused pulsed laser possess a very high energy, and therefore, can freely migrate on the substrate’s surface. Therefore, direct growth of TMDCs on substrates that are intolerable towards high temperature can be achieved with PLD. For instance, Singh et al. [38] have successfully fabricated MoS2 on InN at a low substrate temperature of 450°C. It may be noted that low temperature deposition is required for InN as it dissociates above 500°C.

  • PLD is a clean, highly efficient, safe, and highly controlled deposition technique where the product is highly continuous and uniform. Due to the ultrahigh vacuum growth conditions, the products of PLD are clean and contamination-free. Furthermore, Siegel et al. [32] fabricated MoS2 on centimeter-scale sapphire substrates using PLD, varying the thickness from 60 monolayers down to a single monolayer, just by tuning the number of laser pulses.

Figure 2.

Schematic view of a typical PLD process. Adapted from Ref. [51].

In the past few years, TMDCs have elicited tremendous research interest, owing to their novel properties in the 2D form, which has triggered a spark in the growth of TMDCs using PLD [18]. In this part of the chapter, a few reports describing the chronological developments in the area of PLD grown TMDCs have been briefly discussed. One of the earliest works on PLD deposited MoS2 was reported by Zabinski et al. [39], where they have prepared PbO-MoS2 thin films for tribological applications. Other early reports on MoS2 thin films by PLD include growth of amorphous MoS2 by McDevitt et al. [40] and MoS2 coatings for friction-related studies by Mosleh et al. [41]. The major advancements in this area have been achieved in the past few years. In 2010, Fominski et al. [42] have experimentally studied the fabrication of MoSex thin films with varying compositions obtained by PLD in vacuum condition and in presence of different rarefied gases. They also developed a process-based mathematical model which played a dominant role on the chemical composition of these thin films. Loh et al. [43] in 2014 fabricated MoS2 on different metals such as Ag, Ni, Al, and Cu by PLD. In 2015, a significant step towards the fabrication of transfer-free TMDC-based PDs was demonstrated by Serrao et al. [44] in which MoS2 was directly deposited on substrates like sapphire, SiC-6H and GaN. The first significant work towards the wafer-scale growth of TMDCs by PLD was done by Siegel et al. [32] who reported growth of centimeter-scale MoS2 thin films of varying thickness (from monolayer to 60 monolayers). Growth of other members of the TMDC family such as WS2 was also investigated simultaneously. In 2015, Loh et al. [45] synthesized WS2 thin films on Ag substrates by PLD and reported the thickness dependent Raman and PL spectra. However, the obtained WS2 was having a mixed phase (1T and 2H). In subsequent works, Yao et al. [46] obtained the pure 2H phase WS2 directly by PLD on insulating SiO2/Si substrates. The growth of selenides via PLD usually suffers from a large number of Se vacancies. Therefore, a two-step growth method was adopted for production of MoSe2 [47]. This included deposition of MoO3 film via PLD, followed by its selenization. Later on, Mohammed et al. [48] achieved 1–8 monolayers of WSe2 via single-step deposition. This was achieved through a hybrid PLD cluster, where a tungsten target was ablated by the laser beam and selenium vapors were synchronously provided from an effusion cell by thermal evaporation. In 2018, a single-step PLD approach was used by Seo et al. [49] to deposit WSe2 on Al2O3 and SiO2/Si substrates by using a Se-rich target. Lately, Gao et al. [50] demonstrated a two-step synthesis route to fabricate 2D WTe2, which included PLD of amorphous WTe2 target followed by annealing treatment of the thin films in a Te atmosphere. These reports suggest that the technique of PLD can be suitably applied for the successful production of various TMDCs. In the next section, we will discuss in detail about the fundamentals associated with PLD.

3. Basics of pulsed laser deposition

PLD falls under the category of physical vapor deposition and is a method used to synthesize materials (generally thin films) in an ultrahigh vacuum environment. The development in the field of laser-assisted film growth can be traced back to 1960, after the successful technical realization of the first laser by Maiman [52]. Following on from there, from just being a growth method for fundamental laboratory research, PLD has moved on to become a technique employed in industries. A typical PLD system mainly consists of a laser (usually an excimer laser), an optical path system consisting of apertures, lenses and reflectors, and a stainless-steel growth chamber equipped with gas paths, vacuum pumps, vacuum gauges, and a heating source [51]. The basic principle behind a PLD process is that a high-intensity pulsed laser interacts with the target or the source material (called ablation) and produces a plasma plume of the target material [51]. The formation of plasma involves a sequence of complex phenomena such as collision, localized heating and subsequent ionization of atoms and molecules. Afterwards, the plasma plume expands, travels downstream, condenses on the substrates and finally crystallizes into the desired materials [51]. Figure 3 shows the PLD setup located in Materials Research Centre, Indian Institute of Science, Bangalore, India.

Figure 3.

PLD setup in Materials Research Centre, Indian Institute of Science, Bangalore, India.

The major advantage of a PLD system is that the laser can be operated from outside the vacuum chamber. Thus, just by changing the optical paths of the laser beam, a single laser source can be used for multiple deposition systems. All the other components such as the target carousel, substrate holder, heater, vacuum gauges, and so on are mounted in the vacuum chamber. A set of optical components such as apertures and mirrors are used to focus the pulsed laser beam over the target surface. Therefore, a variety of materials (semiconductors, metals and insulators) can be grown by PLD just by optimizing the growth parameters and by incorporation of different gases during the process in a controlled manner. With this, the exact stoichiometry of the target material can be copied down onto the substrates, which is one of the major benefits of PLD over other deposition techniques. Some of the important parameters associated with PLD have been described below.

Laser source: A krypton fluoride (KrF) laser is a type of excimer laser, and with a wavelength of 248 nm, it is a deep UV laser which is commonly used for the growth of various thin films as the absorption spectrum of most of the inorganic materials lies in the range of 200–400 nm. Typically, excimer lasers contain a mixture of two gases: a noble gas such as argon, xenon or krypton; and a halogen such as chlorine or fluorine. Under suitable conditions of stimulation and pressure, an excimer molecule is created, which decays via a stimulated emission and a coherent beam of stimulated radiation is emitted in the UV range. The continuous emission is then converted into a pulse by various discharge mechanisms and a pulse width of ~10–20 nanoseconds (ns) can be achieved.

Laser fluence: The laser fluence or laser energy density is defined as the laser output energy per unit area and is a very important parameter which decides the proper ablation of the target where the laser beam interacts with the target. A minimum threshold laser fluence is required to carry out the proper ablation process, otherwise, only evaporation takes place. The plume formation depends upon the target conditions such as its density, porosity, morphology, and compositional impurities as well as the laser conditions such as laser pulse duration and laser pulse width. If the laser fluence is much above the threshold value, crystallographic defects and damage can occur in the deposited thin film because of the bombardment by the ablation particles possessing high kinetic energy. Also, it can lead to macroscopic particles ejection during the process of ablation, particulate formation on thin films as well as back-sputtering of species from the deposited thin film. Various mechanisms have been proposed for the formation of particulates and several methods have been devised to minimize these effects [53, 54].

Laser-target interactions: The three main processes taking place during the laser-target interaction are: (i) the laser beam interacts with the surface of the target and gets absorbed into surface layer; (ii) the removal of atomic species from the material is done by vaporization of the surface region in a non-equilibrium state; (iii) afterwards, rapid vaporization further produces a recoil pressure, which leads to the expulsion of the molten pool and produces the plasma plume, and the formed plasma is a collection of electrons, neutral atoms, ions, etc. Therefore, the absorption process is highly dependent on the target properties as well as the laser characteristics. Also, this absorption process is different for metals, insulators and semiconductors [55, 56]. When the laser beam interacts with the target, the photoenergy gets converted into electronic excitations immediately, and the energy relaxation through lattice takes place in ~1 picosecond (ps). Next, the photoenergy is transformed into heat diffusion (over a few microseconds (μs)), which results in the melting of the solid surface (in tens of ns). During the laser-target interactions, the localized temperature of the target reaches up to 10,000 OC or even higher, leading to the evaporation of the target material. At this point of time, the plume formation takes place (in the range of few μs). The plasma plume consists of atoms, electrons, ions and particulates of varying sizes, ranging from nanometer (nm) to micrometer (μm). This plasma reaches the substrate and undergoes re-solidification and condenses in the form of a thin film [53, 57].

In most of the cases, melting of a material depends on the rate of thermal conduction via lattice, which can be well described by the Fick’s laws of diffusion. If the heated volume of the material is smaller than or equivalent to the thickness of ablated layer per laser pulse, then congruent melting will take place. Hence, PLD offers the advantage of congruent melting and vaporization. The amount of heated volume depends on the time of the laser-target interaction, i.e. the pulse duration. For a pulse duration of ~10 ps, heat diffusion will not play a role in the melting and vaporization of the material, whereas, above ~20 ps, conventional heat diffusion dependent ablation occurs [57]. Therefore, the use of a pulsed laser with a pulse duration of a few ns is more likely to provide congruent ablation. This allows the PLD process to preserve the anion-cation stoichiometry of the target material during the mass transfer of the material from the target onto the substrate.

Ambient growth pressure: The background pressure during deposition is a very important and critical parameter that plays a significant role in the plume collisions and plasma dynamics. Keeping the right background pressure is of utmost importance in order to obtain controlled stoichiometric products during the PLD growth. A specific phase and composition of a material can be achieved under controlled and optimized conditions of background pressure at specific temperature. Plasma species with kinetic energies greater than 50 eV can re-sputter the material already deposited on the substrate and this usually leads to a lower deposition rate, modifications in the stoichiometry of the film, and increase the surface roughness. Controlling the background pressure can reduce re-sputtering of the deposited thin films. Increasing the background gas pressure to an optimum value slows down the highly energetic species in the dilating plasma plume [58].

Target-substrate distance: The target to substrate distance is a useful parameter for reducing the particulate formation since majority of the PLD depositions are carried out in high pressure conditions. If the thin film is deposited in vacuum environment, the target to substrate distance mainly affects the angular spread of the ejected flux. Thus, the effect of target to substrate distance and the background gas pressures is inter-related. The plume length decreases as the ambient gas pressure increases, because of the increased collisions between the plume species and background gas molecules. Therefore, a smaller target to substrate distance should be kept in the case of depositions carried out at high pressures.

Deposition rate: This mainly depends on the repetition rate or the frequency of laser shots which controls the volume or amount of the plume species reaching the substrate and, thus, controls the thickness of the deposited thin film. Deposition rate also depends on the background gas pressure as described previously and mainly modulates the super-saturation process during deposition, which has an influence on the critical nucleation point and the density of nucleation sites. Also, ultra-smooth thin films can be obtained at optimized deposition rates.

Substrate temperature: Substrate temperature plays a critical role in terms of the diffusion barrier during the growth process and strongly affects the growth modes. It influences the nucleation process as well as the mobility of the condensed species across the substrate, and therefore, is crucial in deciding the phase boundary in the crystalline thin films during PLD growth. At lower substrate temperatures, the thin film produced may be amorphous or polycrystalline due to the lower nucleation rate, as the thermal energy provided is too small for overcoming the nucleation barrier. When the substrate temperature is too high, the nucleation rate gets limited due to the high rate of atomic exchange between the solid and gaseous species. Thus, an optimum temperature is required for the easy crystallization of thin films as it becomes easier to overcome the nucleation barrier and form nuclei on the substrate [57].

4. Recent advancements in the PLD growth of TMDCs-based PDs

In general, the PLD-grown TMDCs-based PDs exhibit device performance that is comparable with the PDs based on traditional bulk semiconductors. Additionally, PLD is also beneficial for scalable production up to the wafer-scale. Therefore, growth of these TMDCs through PLD for applications in photodetection shows a tremendous potential to translate the fundamental laboratory research to realization of industrial and practical applications.

MoS2 is probably the most studied material among various TMDCs and was probably the first member to be fabricated by PLD. One of the earliest investigations on the photodetection studies of MoS2-based PDs was done by Alkis et al. [59], in which the authors have fabricated MoS2 nanocrystallites through PLD in deionized water and have demonstrated ultraviolet photodetection using the thin films of the obtained MoS2 nanocrystallites. Mostly, the PLD fabricated PDs based on the TMDCs are in the form of thin films. The earliest MoS2 thin film-based PD grown by PLD can be traced back to 2014, when Late et al. [60] synthesized wafer-scale MoS2 thin films on flexible kapton substrates. The devices showed a good photoresponse towards UV light, with stable response and recovery in self-powered mode (Figure 4a and b). The origination of this self-powered behavior might be from the unintentional inhomogeneities in the contact electrodes [61, 62]. However, the observed response was very weak in the zero-biased mode. This work demonstrated that layered TMDCs can be promising candidates to be used as flexible devices in future photonic applications. In the meantime, researchers across the world started to explore the synthesis of other TMDCs by PLD. In 2015, Yao et al. [46] deposited multilayered WS2 by PLD and performed detailed and systematic investigations on its photodetection properties (Figure 4cf). The synthesized device exhibited a broadband and reproducible photoresponse with good stability. The photoresponse in ambient conditions reached 0.51 AW−1, which was several orders higher than the CVD-grown WS2 thin films. In vacuum conditions, the responsivity was found to be enhanced to a value of 0.7 AW−1. The lower responsivity in ambient conditions has been explained on the basis of oxygen molecules adsorbed on the surface of WS2 which trap conduction electrons, and form O2. These species act as recombination centres for the photogenerated carriers. Thus, a greater number of adsorbed O2 molecules are present in ambient air environment, which hampers the responsivity of the device. Furthermore, the device maintained a stable and reproducible photoswitching even after one-month of storage in air, indicating the robustness of the device.

Figure 4.

(a) MoS2 thin film deposited on flexible kapton substrate and (b) temporal response of the device in zero-bias mode. Figures have been reproduced with permission from Ref. [60]. (c) Cross-sectional schematic view of the WS2-based photoresistor, (d) temporal response of the device in air, (e) I-V curves of the WS2-based device in vacuum and in air, and (f) schematic of the photodetection mechanism based on adsorption and desorption of O2 molecules. Figures have been reproduced with permission from Ref. [46].

The progress in the PLD growth of TMDCs has been quite significant, however, the crystal quality normally remains inferior when compared to the bulk natural crystals. This opens a window to further improve the device quality as well as the performance of PLD-fabricated PDs. One such work has been reported recently, where Wang et al. [63] have attained a dramatic improvement in the quality of the PLD-synthesized WS2 photoresistors by using a post-synthesis annealing procedure. With increase in the post-deposition annealing temperature from 310 to 610°C, the device performance parameters of the WS2-based PD (annealed at 610°C) enhanced by 2–3 orders of magnitude when compared to the devices annealed at lower temperatures. Annealing treatment usually provides a sufficient amount of energy and time to the atoms and molecules, for the structural reconstruction to annihilate crystal defects, and thus, has been adopted as a universal post-fabrication technique for improving the quality of the products. In another work, Yao et al. [64] have synthesized a hybrid WS2/Bi2Te3/SiO2/Si-based PD. The purpose of the insertion of the Bi2Te3 layer in between WS2 and SiO2 was to passivate the interface. The device demonstrated a stable, reproducible and broadband photoresponse (370 to 1550 nm). Moreover, the device showed a high photoresponsivity of 30.7 AW−1 and a pronounced specific detectivity of 2.3 ×1011 Jones with a rise time of 20 ms. The performance of the detector has been attributed to the surface passivation of SiO2 by the Bi2Te3 interfacial layer. SiO2 surface possess a lot of unscreened dangling bonds. When WS2 is directly deposited on SiO2, these bonds can introduce a large density of defects at the bottom of the WS2 layer, which will act as recombination and scattering centers for the photogenerated charge carriers. With the introduction of Bi2Te3 layer, these dangling bonds are greatly suppressed, and this results in the growth of WS2 film with high crystalline quality, which eventually enhances the PD’s performance.

Spectral range of a PD is equally important when compared with the other figures of merit and altering the effective wavelength range of TMDC-based PDs is extremely important for specific applications. It has been shown that by introducing defect states in the forbidden gap of a semiconductor, the detection range can be dramatically extended, and sub-band gap detection can be accomplished. Xie et al. [65] have demonstrated ultra-broadband MoS2-based PDs through PLD by forming sulfur vacancies in MoS2. The S/Mo atomic ratio was modified from 1.89 to 1.94 by controlling the number of laser pulses from 1200 to 300, resulting in a dramatic increase in the band gap of the semiconductor. Consequently, the S-deficient MoS2-based PD exhibited an unprecedented ultra-broadband detection range from 445 to 2717 nm. However, theoretical calculations have been done which indicated that the Mo vacancies in MoS2 possess a higher capability for narrowing the band gap. Therefore, in a subsequent work, Xie et al. [66] have synthesized a series of Mo-deficient MoS2-based PDs by moderating the target to substrate distance during the PLD growth. As a result of these modulations, the effective spectral range of a MoS2.17 PD spanned all over from 445 nm to 9536 nm. Although the detection range can be extended up to mid infrared (MIR) with the introduction of the defect states, however, it is accompanied by certain challenges that hinders the usability of this method in practical devices. These include the control over the creation of these defects, which is still an unresolved problem. Furthermore, the electronic properties of the charge carriers are severely hampered owing to the increased scattering effects from these defect states. Thus, such devices often suffer from meager responsivities and slower response speeds.

Recently, Jiao et al. [67] have synthesized high-quality and wafer-scale 2D layered MoS2 thin films by PLD. The device exhibited competitive device performance to the commercial Si and Ge-based PDs. The value of the responsivity was recorded to be 1.96 AW−1 for single layer MoS2-based device, under 300 nm light illumination (Figure 5). The PD shows a broadband photoresponse ranging from UV to NIR, with a fast response of 96 ms. This enhancement in the performance was attributed to the variation in the Schottky barrier at the Au/MoS2 interface.

Figure 5.

(a) Schematic of the interdigital patterned gold electrodes to form a metal-semiconductor-metal type contact, and (b) the wavelength dependence of responsivity (300 to 900 nm) for the device. Figures have been reproduced with permission from Ref. [67].

The above discussed PLD-grown TMDC-based PDs are based on the metal-semiconductor-metal type device configuration, and suffer from relatively lower photoresponsivity, low on/off ratios, narrowband detection and slower detection speed. Hence, strategies are being developed to overcome these limitations. PDs having transparent electrodes such as indium tin oxide (ITO) and graphene, instead of the conventional metal contacts and PDs based on heterojunctions of two or more materials have many advantages such as low value of dark current, higher on/off current ratios, broadband detection range, and higher responsivities due to favorable band alignments.

One such work was carried out in 2016, when Zheng et al. [68] successfully prepared centimeter-scale and highly-crystalline WSe2 thin films on polyimide substrates by the technique of PLD and have fabricated high-performance PDs based on these WSe2 thin films. They obtained a broadband spectral response, ranging from 370 to 1064 nm. Moreover, a reproducible photoresponsivity approaching up to 0.92 AW−1, an EQE of 180% and a fast response speed of 0.9 s have also been achieved. The PD also exhibited excellent air durability and mechanical flexibility. The enhanced performance has been attributed to the good Ohmic contacts WSe2 forms with ITO, because of a low mismatch between the work functions of the two materials. Due to the Ohmic contacts, the carriers can be efficiently injected through the ITO electrodes under an applied bias, which will result in generation of a high photocurrent. Ohmic contacts lead to photodetection mechanisms based on the intrinsic properties of the photosensitive material under light irradiation.

Using a similar approach of integration of ITO electrodes on the device, Kumar et al. [69] have reported a UV PD which utilizes few layered MoS2 deposited by PLD. The device shows a high responsivity of 3 ×104 AW−1 and detectivity of 1.81 ×1014 Jones, at a nominal voltage of 2 V with fast response time of 32 ms. This performance is better than most of the reported devices based on 2D layered materials. The PD exhibited a very low value of dark current (~10−10 A) which is the reason behind such an excellent device performance. This may be because of suitable band alignment with the ITO electrodes as well as the deposition of high-quality films as the deposition was carried out in the presence of nitrogen gas, leading to lower number of sulfur vacancies.

Till now, all the above reported devices require some external bias for obtaining significant photodetection. Over the years, PDs which consume no external power have attracted a lot of attention because in the current scenario of energy crisis, a lot of research has been focused on energy producing and energy storage devices [70, 71, 72, 73, 74]. Such self-powered PDs depend on the interfacial built-in potential which enhances the effective separation of photogenerated carriers. This built-in electric potential also suppresses the dark current, which is another benefit for such PDs. Therefore, these self-powered devices have a great prospect for the next-generation PDs.

In 2015, Yao et al. [75] designed a Bi/WS2/Si heterojunction-based PD by depositing polycrystalline WS2 and Bi thin films on a p-type Si substrate by PLD (Figure 6). The PD exhibited a decent responsivity of 0.42 AW−1 and a high detectivity of 1.36 ×1013 Jones with ultrahigh sensitivity. It was observed that the performance of the Bi/Si heterointerface was enhanced by the insertion of the WS2 film. The enhanced device performance has been attributed to the effective passivation of the junction, and enhanced light absorption. Moreover, due to the favorable band alignment, WS2 acts as a selective carrier blocker, which further enhances the device performance.

Figure 6.

(a) Transient behavior of the Bi/Si and Bi/WS2/Si PDs under zero bias. (b) Corresponding single on-off cycle. Schematic of the energy band diagrams of the (c) Bi/Si and (d) Bi/WS2/Si heterointerfaces. Figures have been reproduced with permission from Ref. [75].

Recently, Singh et al. [4] demonstrated an MoS2/AlN/Si-based PD grown by PLD, thus combining the excellent and unique properties of MoS2 with the matured technologies of Si and III-nitride semiconductors. Moreover, due to a large difference in the work functions of these materials, the band bending of the heterojunction at the interfaces resulted in self-powered behavior. The vertical transport of the PD exhibited an exceptional broadband photoresponse (300–1100 nm) in the self-powered mode. The device shows a responsivity of 9.93 AW−1 under zero-bias condition with ultrafast response speeds (response/recovery times - 12.5/14.9 μs). The photoresponse of MoS2/Si has also been given, to show the importance of inserting the AlN layer. The MoS2/Si PD exhibits a responsivity of 1.88 AW−1 (~5 times less) in self-powered mode. The authors have shown that the native oxygen defects are present throughout the AlN layer, and this has been confirmed with the help of X-ray photoelectron spectroscopy and transmission electron microscopy. These oxygen impurities form deep donor states in AlN and modulate the transport of the charge carriers, and this leads to the enhanced performance of the MoS2/AlN/Si-based device (Figure 7).

Figure 7.

(a) Spectral response of the MoS2/AlN/Si-based PD. (b) Schematic of the deep defect states-modulated carrier transport in MoS2/AlN/Si-based device. Figures have been reproduced with permission from Ref. [4].

5. Summary

The past few years have undoubtedly witnessed tremendous advances in the PLD growth of TMDCs and their applications in the field of photodetection. In this chapter, the basic properties of TMDCs and the common growth techniques employed for their fabrication have been reviewed briefly, followed by a detailed and elaborated discussion about PLD and the important parameters associated with it. Finally, a progressive investigation about the PDs based on TMDCs fabricated through PLD has been discussed. These extensive achievements in the field of photodetection have unquestionably established PLD as one of the most competitive and reliable methods for fabricating industrial-scale and high-quality TMDCs. PLD, therefore, certainly has a lot of potential to contribute in the development of the next-generation TMDCs-based PDs in the future.

6. Looking into the future

Based on the analysis of the previous reports in this area, an outlook regarding the future of PLD-synthesized TMDCs and the related follow-up research work has been summarized below.

  • The research on the PLD-fabricated TMDCs-based PDs is still in its nascent stage and therefore, there is still a room for improvement in the crystal-quality of the PLD-grown thin films, by selecting appropriate substrates and by further tuning and optimizing the various unexplored growth parameters, such as annealing temperature and time, cooling ramp rate, geometry of the laser spot, surface morphology of the source targets, laser frequency, and so on [18].

  • Apart from a few reports, most of the research regarding PLD growth of TMDCs for photodetection application is based on the use of a single photosensitive material. Therefore, promising results are expected on the exploration of the heterojunctions of these layered materials with established bulk semiconductors like III-nitrides, which have shown great results in this field. Moreover, TMDCs can serve as excellent substrates for high quality and epitaxial growth of III-nitrides, which would lead to better device performance.

  • The use of transparent 2D semiconductors such as graphene or graphene derivatives and semi-metallic phase of TMDCs, can be used in place of the conventional metal electrodes, as they maximize the area of light absorption along with having outstanding electronic properties.

  • Till date, researchers and scientists across the world have mostly exploited heterojunctions of TMDCs in their thin film forms. Heterointerfaces based on one dimensional (1D) nanostructures may provide new routes for the development of high-performance devices. The nanowire-based heterostructures of the TMDCs with growth along these nanowires or a core-shell structure will enable a much higher surface to volume ratio and therefore, a larger active interface. This will lead to enhancement in the photoresponse and superior optoelectronic performance.

As a concluding statement, PLD has been proven to be a promising synthesis technique for TMDCs for applications in photodetection, and these PDs have shown outstanding performance that can compete with those of the commercially available PDs. The fabrication through PLD is cost-effective and scalable, and hence, PLD is a perfect tool for fabrication of practical devices for optoelectronic applications at an industrial scale production.

Acknowledgments

D.K.S. is thankful to Council of Scientific and Industrial Research, Government of India, New Delhi for providing senior research fellowship. S.B.K. acknowledges INSA senior scientist fellowship.

Download for free

chapter PDF

© 2020 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Deependra Kumar Singh, Karuna Kar Nanda and Saluru Baba Krupanidhi (December 18th 2020). Pulsed Laser Deposition of Transition Metal Dichalcogenides-Based Heterostructures for Efficient Photodetection [Online First], IntechOpen, DOI: 10.5772/intechopen.94236. Available from:

chapter statistics

30total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us