Open access peer-reviewed chapter - ONLINE FIRST

Modification of Physical and Chemical Properties of Titanium Dioxide (TiO2) by Ion Implantation for Dye Sensitized Solar Cells

By Hafsa Siddiqui

Submitted: August 7th 2018Reviewed: December 15th 2018Published: March 25th 2019

DOI: 10.5772/intechopen.83566

Downloaded: 287

Abstract

Nowadays, ion implantation is used as a leading technique for doping. Inspite of generating lattice distortions it is preferred over other techniques due to its large range of doses, extremely accurate dose control and low temperature process. This chapter deals with the modification of physical-chemical properties of titanium dioxide (TiO2) through ion implantation method. The TiO2 material is tested in many fields, e.g., nano-catalysts, light harvesting, magnetic data storage and Optics. Various synthesis routes have been reported for the preparation of TiO2 nano-micro structures (particulate solids). Further, implanting these particulate solids revealed anisotropic ferromagnetism at room temperature. On the other hand, noble ion implantation opens up the horizon for fabrication of plasmonic and optical composites. Here in this chapter, TiO2 based photoanodes have been extensively examined for dye sensitized solar cells (DSSC) with metallic and non-metallic ion implantation to realize TiO2 with specific properties.

Keywords

  • ion implantation
  • doping
  • TiO2
  • dye sensitized solar cells
  • photoanode

1. Introduction

The growing energy demand of the society has engaged scientific community over the last decade in a search to enhance the light harvesting applications by utilizing nanostructured materials [1, 2]. The situation is quite obvious that the enlargement of solar cell efficiency through nanostructured materials is very important in the future. After the year 1991, a major breakthrough has come in the area of photovoltaics as dye sensitized solar cells (DSSCs) which possess modest functioning along with their advantageous features such as flexibility in device handling, low toxicity and respectable performance in diverse light conditions [3, 4, 5, 6, 7]. So far, TiO2 is a well-known material as photoelectrode having tremendous performance in DSSC device application [6, 7, 8, 9, 10]. However, despite of the outstanding performance, TiO2 tends to suffer from high recombination center of electrons and holes coupled with wide band gap (i.e., 3.2 eV) [11]. Thus, lot of research is being carried out with the aim to enhance device performance by reducing the charge carrier recombination and improving electrical/optical performance of TiO2 photoelectrode [4, 5, 6, 7, 8, 9, 10, 11, 12, 13]. In this regard, elemental doping is the most advantageous approach to modify its properties. Much work has been reported on synthesis processes adopted for preparation of TiO2. The chemical synthesis methods involve the complexity of chemical reactions and reproducibility is often problematic [14]. Physical doping, e.g., high-energy beam modifications have an adept of post-treatment produced titania films for further precisions, were essentially ignored and less effort was conducted in this direction for doping in photoanodes of DSSC [15, 16, 17, 18, 19, 20]. The author have gone through the literature carefully and after keenly analyzing the reported results, proposed the better applicability of the ion implantation system and extensively examined the ion implanted TiO2 as photoanode in DSSC application.

The present piece of work is mainly focused on the ion implantation technique for the modification of photo-physical properties of titanium dioxide (TiO2) thin films for application as efficient photoelectrode material in dye sensitized solar cell application (Figure 1). The work focuses the finding towards the power conversion efficiency enhancement in DSSCs through ion implanted TiO2 and also discusses in detail the reported results and extensively examines the effects of ion implementation on the performance of dye sensitized solar cell. This chapter imparts knowledge in the field of ion implantation and its application in dye-sensitized solar cells. The fabrication technique adopted here is compatible with currently utilized fabrication techniques for the same and is of great interest to the readers working in the area of ion implantation for optoelectronic device application.

Figure 1.

Ion-implanted TiO2 photoanode for dye-sensitized solar cells.

2. Crystal structure of TiO2

TiO2 is an n-type wide bandgap semiconductor and has four polymorphs as tetragonal (anatase and rutile), orthorhombic (brookite) and monoclinic TiO2 (B) phases (Figure 2), apart from these polymorphs the PbO2 structure (TiO2 (II)) and hollandite structure TiO2 (H) are also synthesized from the rutile phase under high-pressure [21]. In DSSC application, both anatase and rutile phases are highly appreciated as they are stable and possesses good photoreactive properties. Brookite TiO2 has complicated phase with high unite cell volume with minimum density that makes it not suitable for device application [21]. The anatase TiO2 is most stable phase at nanoscale, however the energy difference between anatase and rutile is very small (2–10 kJ.mol−1). The crystal structure, lattice parameters, optical band gap values and related parameters of different phase TiO2 are tabulated in Table 1. TiO2 is more stable as compared to other metal oxides in DSSC, because it has suitable Fermi level to accept electrons from photoexcited dye, and its internal network structure (mesoporous structure) plays an important role in achieving high charge collection efficiency and more electron transportation.

Figure 2.

Crystal structures of TiO2 (a) anatase (tetragonal), (b) rutile (tetragonal), and (c) brookite (orthorhombic) polymorphs [21].

Crystal structureAnatase TiO2Rutile TiO2Brookite TiO2
Form. Wt.79.89079.89079.890
Crystal systemTetragonalTetragonalOrthorhombic
Point group4/mmm4/mmmmmm
Space groupI41/amdP42/mnmPbca
Unit cell
a (Å)3.78424.58459.184
b (Å)5.447
c (Å)9.51462.95335.145
Volume (Å3)136.2562.07257.38
Molar volume20.15618.69319.377
Density3.8954.27434.123
Thermal expansion (volumetric)
Alpha28.9
a00.2890
Density3.2 eV3.0 eV4.123

Table 1.

Structural properties of crystalline structures of TiO2 Ref. [21].

3. Dye-sensitized solar cells

The basic idea of dye-sensitization technique was given by Vogel and Berlin in 1873 [7] and the well understood sensitization was perfect in early 1960s and 1970s, with the pervasive photoelectrochemical examination of dye-sensitized single-crystal electrodes. However, as compared to silicon based photovoltaic devices, the performance of these early DSSCs was poor (efficiency <1%). The major obstacle was the low light harvesting efficiencies of these single-crystal cells by a dye monolayer adsorbed onto a planar TiO2 surface. Some improvements in efficiency were achieved by coating a thick layer of dye onto the planar TiO2 surface; the efficiency was still limited to <2% due to less proficiency in charge-collection from the faraway dye molecules [14]. A breakthrough in DSSC performance was achieved in early 1990s by the research group of Grätzel who creatively demonstrated that a practical DSSC which consists of ruthenium sensitizer dye-adsorbed mesoporous titanium dioxide (thin ∼10 μm) layer on fluorine doped tin oxide glass substrate serving as a photoanode (PA), a platinum-coated counter electrode (CE) and a redox couple liquid electrolyte introduced in between the two electrodes [3]. The main parts of DSSC are shown in Figure 3 [22, 23, 24, 25]. Considerable developments in DSSC efficiency have been reached since then, and the record A.M. 1.5 conversion efficiency for a DSSC presently touched at 14.3%, making it comparable to the conventional p-n junction silicon solar cells in terms of efficiency and cost-effectiveness [7]. Despite intense study of DSSCs over the past two decades, the increase in conversion efficiency has been insignificant and several aspects of the physics and chemistry of the DSSC stay uncertain or debated. If further progress is to be made in device optimization of DSSCs for use in the photovoltaic market, scientists should understand the full mechanism of electron transport in the photoanodes, dye sensitization kinetics and electron recombination at the substrate/TiO2/electrolyte interface. The ion implantation method lays emphasis on the modification of photoanode, e.g., [16, 17, 18]:

  • The ion implanted TiO2 have high surface area for dye adsorption and avoid absorbing visible light to cover high amount of light harvesting.

  • The energy level of the ion implanted TiO2 is matched with that of the excited dye molecules for smooth electron (e) injection.

  • The ion implanted TiO2 has large charge carrier mobility, for collecting the photoelectrons competently.

  • The ion implanted TiO2 is easy to synthesize, stable, cheap and environmentally friendly.

Figure 3.

(a) Semiconductor (photoanode, PA), (b) sensitizer dye, (c) redox couple/electrolyte, and (d) counter electrode [22, 23, 24, 25].

3.1 Basic principles of DSSCs

Figure 4 depicts typical structure of a DSSC and its operational principle [22, 23, 24, 25]. In DSSC the photo-excitation of electrons from lowest unoccupied molecular orbital (LUMO) of dye molecules takes place with the external light irradiance, by choosing sufficient energy, electron reaches highest occupied molecular orbital (HOMO) of dye molecule, which is further injected into the conduction band (CB) of the TiO2 and fast transferred to the external circuit through the CE, generating an electrical current. The inserted electrolyte here plays a vital role in donating an electron back to the unusual state of dye molecule and serves as a redox couple. The CE proceeds charge from the external circuit back to the cycling circuit in the cell [6, 7, 8]. Nevertheless, the device performance depends on the photoelectrode material as well. The voltage produced under irradiance shows resemblance to the potential difference between the electrolyte redox couple (I/I3−) and the quasi-Fermi level of the electron in TiO2. The net outcome is the conversion from light to electricity without any permanent chemical transformation. DSSC is thus a regenerative type photo-electrochemical cell [9, 10]. The sequence of the charge transfer processes responsible for the operation of a dye sensitized solar cell is given in the following Eqs. (1)(7) [26]: The charge transfer processes and the unwanted loss mechanisms presented below are well discussed in details in Ref. [8].

Figure 4.

(a) Schematic of a typical DSSC. (b) The basic sequence of events in a DSSC. (c) Electron transfer in dye sensitized solar cell. (d) Electrical losses in DSSCs [22, 23, 24, 25].

S+SE1

SS++eCBE2

S++32I12I3+SE3

I3+2eCE3IE4

In addition to the forward electron transfer and ionic transport processes, several electron loss pathways could be analysed as shown in Figure 4(d), which gives the electron transfer losses occurred at the dye-sensitized heterojunction. The earlier studies clearly indicate that the main losses in DSSC were due to the potential drop in the dye regeneration and recombination losses between electrons in the TiO2 and acceptor species in the electrolyte [26].

  • Fall off the electron from dye excited state to the ground state

SSE5
  • Recombination of the vaccinated electron with the dye cations

S++eCBSE6
  • Recombination of the vaccinated electron with the (3I) redox mediator

I3+2eCB3IE7
  • At CE, the electron decreases the redox mediator situated in the electrolyte of the DSSC.

  • Redox mediator diffuses to meet and regenerate oxidized dye molecules.

Hence, the challenge is to effectively regenerate the oxidized dye molecules with efficient charge transport through the ion implanted TiO2 matrix followed by the decrease in recombination which can happen at the TiO2/dye/electrolyte boundaries. The morphology and structure of the ion implanted TiO2 photoanode depends on the absorption of dye, electron injection, transportation and the recombination.

4. Ion implantation

The basic information of nucleation and growth mechanisms of TiO2 thin film is essential to understand microstructure and properties for DSSC [4, 16]. The TiO2 nanoparticle with anatase and rutile phases has been synthesized by ion implantation technique, where the degree of surface modification is significantly influenced by various implantation parameters, e.g., current density of ion beam, substrate temperature, and energy of an implant ions [17], etc. In ion implantation technique, ion dose (denoted by F0) is the key factor to determine the total implant ions. TiO2 implantation can be categorized as low-dose and high-dose under conditional surface modification. Low-dose irradiation, e.g., ∼F0 ≤ 5.0 × 1014 ion/cm2 (energy of the implant is transported to the matrix by electron shell excitation and nuclear collisions [27]), causes the radiation-induced defects, which may in turn become reversible or irreversible modification of the material structure. Several types of defects are present in TiO2 crystal such as point defects, line defects, staking faults defects, local crystallization, etc. The range of high-dose implantation can be classified into two sub-ranges, e.g., 1015 ≤ ∼F0 ≤ 1017 ion/cm2.

Figure 5 depicts the cross-section view of nucleation and growth of nanoparticles. Once the concentration of doped ions over does the solubility limit of TiO2 atoms in matrices and the system relaxes [19]. The threshold dose values which nucleate the TiO2 nanoparticles are dependent on the sort of the implant and dielectric matrix. Therefore, the ion implantation method delivers a suitable way to alter physical and chemical properties of materials. Still there is rare information or literature available on improvement of photovoltaic properties for DSSCs with ion implantation [15, 16, 17, 18].

Figure 5.

Basic physical stages of TiO2 nanoparticle synthesis by ion implantation in dependence on ion dose [27].

5. Recent progress in DSSCs

Till date, the record efficiency of DSSCs is exclusively achieved on TiO2 nanoparticles. Optimized photoelectrode films usually contain two layers: the bottom layer is a 12-μm thick transparent layer made of 10–20 nm TiO2 nanoparticles which has efficiently high surface area for dye adsorption; the top layer is a 4-μm thick film made of much larger TiO2 particles (∼400 nm in diameter) to scatter light back into the bottom layer and enhance near-IR light harvesting [3]. The highest efficiency achieved based on the different architecture of DSSCs is summarized in Table 2. Despite the excellent performance of TiO2 nanoparticle films in conventional DSSCs, they are still incapable to contribute suitable efficiency as compared to silicon based solar cells. Thus there is a need to realize a higher access rate of the photogenerated electrons from dye to the photoanode, to extend the efficiency at suitable level.

5.1 Important results

The TiO2 photoanode prepared via the ion implantation method has active paths to expand the DSSC performance [19]. Ion implantation permits the incorporation of Ti4+ ion species at accelerated high-energy into the raw surface under high applied power for short time duration. On the other hand, it can improve the properties of TiO2 like enhanced resistance to oxidization, little interfacial fault and respectable optical properties [17]. But till date the reported work on ion implanted TiO2 served as photoanode in DSSC are very limited (available reports are summarized in Table 3). The implanted ions may act as intermediaries for charge transfer and centers for electron-hole recombination, and this dual characters affect the performance of the DSSC. The true impact should be conceded by both the effects, and also depend on the doses of the implanted ions. It has been found that the annealing state also play a key to explaining the charge transfer dynamics on ion implantation, because annealing state regulates the activation and the diffusion profile of the dopant. The beginning part of the annealing is more precarious since the in-activated dopants act as recombination sites, which reduces the minority carrier lifetime and decreases the performance of DSSCs. Luo et al. and Low et al. has found that minimum temperature annealing of ion implantation TiO2 photoanode was due to shallow emitter which can enhance the quantum efficiency at short wavelengths [15, 16].

AuthorYearDyeη (%)Ref.
Kenji et al.2015ADEKA-1 and LEG414.3[28]
Simon et al.2014SM315 with cobalt (II/III) redox13.0[29]
Liyuan et.al.2012N311.4[5]
Yella et al.2011YD2-o-C812.3[11]
Kim et al.2010Black dye11.2[30]
Qingjiang et al.2010Ruthenium12.1[31]
Chen et al.2009CYC-B11 dye11.5[32]
Feifei et al.2008C101 and C10211.3[33]
Yasuo et al.2006Black dye with YD2-o-C811.1[34]

Table 2.

Photovoltaic parameters of the DSSCs under an illumination of 100 mW/cm2 (AM 1.5G).

Dopant/ModifierStrategiesη (%)Ref.
Ag-ionTri-layer titania films has been doped with Ag ions using metal vapor vacuum arc ion-implantation.5.85[15]
TiTi ion implantation has been used to modify the reduced graphene oxide nanosheet by incorporating the Ti4+ ion at various applied powers ranging from 50 to 250 W8.51[16]
Ruthenium-ironThe anatase TiO2 electrode has been prepared via a sol-gel process and deposited onto ITO. The deposited TiO2 films have been subjected to MPII at 20 keV in order to incorporate ruthenium Ru and Fe atoms into the TiO2 surface layer.8.0[17]
CarbonThe optimal concentration of ions implantation for C-implanted cells is 1 × 1015 atom*cm25.32[18]
NitrogenTiO2 layer has been uniformly implanted with 100 keV nitrogen (N) ions of fluence 1 × 1016 ions cm2.1.64[19]
IronFe-doped TiO2 electrodes with the illumination of 6 × 1015 atom∕cm24.86[20]

Table 3.

Doped/surface modified through ion implanted TiO2 based DSSCs.

6. Conclusions

In the future, dye-sensitized solar cells will be used in many fields, such as mobile commerce, building-integrated photovoltaics (BIPVs), and vehicles. Moreover, DSSCs are essential in the Smart Grid, which are utilized in our daily lives. To apply solar energy in the Smart Grid, DSSCs are required to have transparency, flexibility, lightweight, low cost, and high power conversion efficiency. In terms of low cost and lightweight, organics, inorganics, and hybrid materials have brighter prospects than the semiconductors. In hybrid materials, photovoltaic cells have been prepared with the advantages of organics or inorganics selectively. However, it is not easy to increase the power conversion efficiency. One potential solution presented in this study is to use ion implanted TiO2 nanostructures in DSSCs. The slow progress of ion-implanted TiO2-based DSSCs in the past 7 years has demanded to realize the reliable and practical commercialization of DSSCs. It is expected that ion-implanted TiO2 can efficiently separate photoexcited charge carriers and generate higher photocurrent in DSSCs. In comparison to untreated cell, the implant ion can act as mediators for electron transport that reduces charge transfer resistance and enhance the dye loading resulting in boost of PCE [15]. One way of achieving the better light-harvesting ability is to grow the various low dimensional nanoparticles on the ion-implanted TiO2 thin film, which is presently the active field of study [17]. Thus, the future prospects of material and ideas revealed in the present chapter can be better applied to efficient visible light-activated material to boost the performance of DSSCs.

Acknowledgments

I would like to express my sincere gratitude to Mrs. Shaju Summi (Vice President) and Syed Maqbool Husain Sha-Shib Group of Institutions for their continuous support and encouragement throughout this work. The help rendered by Dr. Oroosa Subohi (Assistant Professor, Department of Physics, Visvesvaraya National Institute of Technology (VNIT), Nagpur, 440010, Maharashtra) is highly appreciated.

Download

chapter PDF

© 2019 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Hafsa Siddiqui (March 25th 2019). Modification of Physical and Chemical Properties of Titanium Dioxide (TiO<sub>2</sub>) by Ion Implantation for Dye Sensitized Solar Cells [Online First], IntechOpen, DOI: 10.5772/intechopen.83566. Available from:

chapter statistics

287total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us