Open access peer-reviewed chapter - ONLINE FIRST

Mechanism of Photoluminescence in Erbium-Doped Chalcogenide

By Volodymyr V. Halyan and Inna A. Ivashchenko

Submitted: May 13th 2018Reviewed: September 11th 2018Published: December 8th 2018

DOI: 10.5772/intechopen.81445

Downloaded: 207

Abstract

The monograph describes the technique of the synthesis of glasses and the method of the growth of erbium-doped single crystals. The photoluminescence spectra of Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses and glasses from the Ga2S3-La2S3-Er2S3 system have been investigated in the visible and near-infrared ranges. According to the energy transitions in the erbium ions, a radiation mechanism for conversion and up-conversion luminescence has been established. The role of structural ordering and the influence of defects on the radiation efficiency of Er3+ ions have been investigated. The spectra of photoluminescence of (Ga54.59In44.66Er0.75)2S300 and (Ga69.75La29.75Er0.5)2S300 single crystals have been studied. The efficiency of the radiation of the amorphous and crystalline materials has been compared. Also, the temperature dependence of the integral intensity of the radiation of glasses and single crystals has been studied. It is established that in a limited temperature range, these materials can be used for the manufacture of non-contact optical thermosensors.

Keywords

  • glass
  • single crystal
  • photoluminescence
  • energy transition
  • radiation mechanism
  • visible
  • and near-infrared ranges

1. Introduction

Modern scientific and technological progress requires the constant search for and introduction of new multifunctional materials. One of the directions in the search for new semiconductor materials is the study of multicomponent systems of binary and ternary phases, which are promising for practical use. This is due to increasing requirements for semiconductor materials in connection with the development of new or modernization of known technical devices. To expand the list of materials, a study of chalcogenide quasi-ternary systems was undertaken.

Chalcogenide semiconductor materials were the object of research for many decades. The best studied glassy and crystalline chalcogenides are based on the Ge-X, Ga-X, As-X systems (X = S, Se, Te) modified by the admixture of Hg, Sb, Pb, Ag, etc. [1, 2, 3]. An important feature of chalcogenide glass is that the introduced admixtures are electrically and optically inactive. As a rule, they do not create localized states in the band gap. When introduced into a glass-forming matrix, admixture atoms rebuild their local environment resulting in the saturation of their valence bonds. Exceptions are the admixtures of bismuth, platinum, and gold into arsenic sulfide [4, 5, 6].

Special attention is devoted to the research of the luminescence properties of chalcogenide crystals and glasses due to practical application in optoelectronic technology. Their unique properties create advantages over other light-emitting materials and cause considerable interest both from the fundamental and the applied point of view. The chalcogenide materials combine high transparency in the visible, near-infrared, and medium-infrared spectral regions. By selecting the optimal component composition, it is possible to obtain wide areas of glass formation and to introduce relatively high concentration of rare earth metals (RE). Additionally, chalcogenides are characterized by high refractive index, good nonlinear optical properties, resistance to aggressive media, and easy manufacture technology. The addition of RE (Er, La, Eu, Pr, Tb, Ho, etc.) to the crystalline or amorphous chalcogenide medium creates potential opportunities for their use as high-quantum output luminophores, optical filters, active media in laser technology, in telecommunication devices, as well as non-contact optical temperature, and γ-irradiation sensors. The chalcogenide media that are activated by RE ions can also exhibit both conversion and up-conversion photoluminescence (PL) which creates the prerequisites for the design of effective converters from the infrared range to visible light.

Therefore, the preparation of chalcogenide glasses and crystals doped with rare earths and the study of their emission properties under different temperature and irradiation regimes are an extremely important area of modern solid-state physics and chemistry.

2. Synthesis of glasses and single crystal growth

Elementary high-purity substances were used for the synthesis of samples: Ag (99.99 wt.% of the principal), Ga, In, Ge (99.999 wt.% purity), La, Er (99.9 wt.%), and S, Se (99.997 wt.%). The elements for single crystal growth were further purified by double vacuum distillation. The weight of the starting components for the glasses was 3 g; the batches for the synthesis of single crystals were 10 g.

The samples were synthesized in cylindrical quartz containers with 9–15 mm diameter. The loaded ampoules were evacuated to a residual pressure of 1.33 × 10−2 Pa. The synthesis of glasses was performed in a shaft-type furnace with a temperature control system of ±5 K accuracy.

The alloys for the glasses of the La2S3-Er2S3-Ga2S3 system with sample weight 2 g were pre-synthesized at 870 K and 24 h exposure. Obtained samples were ground in an agate mortar and loaded into quartz containers with a spherical bottom of 1 cm diameter. The heating was stepwise, first to 1070 K at a rate of 50 K/h and then to 1420 K at a rate of 40 K/h. After 3 h exposure at the maximum temperature, the samples were quenched into saturated NaCl solution with crushed ice.

Synthesis of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glass alloys was performed in two stages. Initially, the ampoules were heated in the flame of an oxygen-gas burner to complete bonding of elemental sulfur. Then the ampoules were placed in a shaft-type furnace and heated at a rate of 20 K/h to 1273 K. The samples were kept at the maximum temperature for 10 h with periodic vibration. The alloys were cooled at a rate of 10–20 K/h to annealing temperature. The homogenizing annealing was held for 500 h at 720 K. The annealed alloys were quenched into 25% aqueous NaCl solution at room temperature.

To prevent the spatter of melt during quenching as well as to reduce losses due to the vapor phase condensing on the walls of the container, the special form of the container was used (Figure 1), and the upper part was thermostated by asbestos cord after the binding of sulfur in the oxygen-gas burner flame was used.

Figure 1.

Container for the synthesis of glassy alloys: (1) cylindrical part of the container; (2) neck; (3) thin-walled pear-shaped chamber.

The method and conditions for the single crystal growth of the phases (Ga55In45)2S300 and (Ga55In45)2S300:0.3 at.% Er [7] were selected from the Ga2S3-In2S3 phase diagram; the supercooling temperature was determined from the cooling curves of the sample thermograms. The solution-melt method was used; supercooling of the solution melt was 70 K. The synthesis of the initial alloys at the maximum temperature of 1200 K and the growth of crystals were combined in evacuated graphitized quartz container with a conical bottom and a 2 mm diameter neck. The growth process was performed in a vertical two-zone furnace. The maximum temperature was 1200 K; the temperature gradient at the solid-melt interface was 20 K/cm. After melting the batch, the ampoule was lowered at the maximum rate. After crystallization of 10 mm of melt along the length of the ampoule, the growth was stopped, followed by re-melting of 6.0–8.0 mm of the crystallized portion and by annealing the seed during 100 h. Further growth of the single crystal was performed at a rate of 5 mm/day. After completion of the process, both furnaces were cooled to 820 K at a rate of 50–70 K/day, and the resulting single crystal was annealed for 100 h. After that, the furnace was switched off. The single crystals of orange color, 14 mm in diameter and 20 mm in length, were obtained.

The single crystal growth was performed in a setup installation shown in Figure 2a along with the temperature distribution along the heaters. The temperature in the growth zone was maintained by precision temperature controllers with an accuracy of ±0.5 K.

Figure 2.

Growth unit setup and the container for the single crystal growth: (a) 1—metal flange, 2—asbestos-cement casing, 3—Pt/Pt-Rh-thermocouple, 4—growth container, 5—melt, 6—metal disk, 7—heater, 8—thermal insulator, and 9—pulley for moving ampoules; (b) 1—cylindrical part of the container, 2—necks for seed formation, and 3—pear-shaped chambers.

A version of a container with two pear-shaped chambers connected by a neck was used for the growth of single crystals (Figure 2b). This increases the probability of obtaining a single crystal with its subsequent growth to a larger size in the cylindrical portion of the container.

Independent temperature control in different areas of the heater allows us to vary the gradient at the solid-melt interface within 3–5 K/mm. The growth rate was within 2 mm/day. The vertical movement of the plane of the crystallization zone was ensured by moving the container while the heater was at a fixed position.

3. Photoluminescence in chalcogenide glasses

An analysis of literature sources shows that chalcogenide glasses, unless doped with REs, do not usually exhibit luminescent properties at room temperature. For a long time, this limited their use in optoelectronic technology. Investigations of RE-free glasses with the substitution of selenium for sulfur revealed the existence of a broad unstructured PL band at 80 K (Figure 3).

Figure 3.

(a) Luminescence spectra of the glassy alloys of the AgGaSe2 + GeS2 ⇔ AgGaS2 + GeSe2 system (at.% Se is indicated). (b) Dependence of the emission intensity at the maximum (λm ≈ 1180 nm) on the content of Se (excitation wavelength 532 nm, temperature 80 K).

The glasses of the AgGaSe2 + GeS2 ⇔ AgGaS2 + GeSe2 system excited by a laser with 532-nm wavelength exhibit at low-temperature luminescence with a single maximum in the near-infrared range (λm ≈ 1150–1180 nm) with an emission band half-width ΔE ≈ 0.26–0.30 eV (Figure 3a), which is typical of the recombination luminescence in disordered systems. The intensity of the luminescence maximum depends on the content of Se (when sulfur is substituted with selenium, Figure 3b). The dependence is complex and to a large extent is due to the change in the level of luminescence excitation (caused by the shift of the absorption edge with increasing concentration of selenium in the alloy [8]). An important feature of the luminescence spectrum is that the position of the luminescence maximum is close to the center of the band gap (as determined by the position of optical absorption edge [8]). This is well illustrated by the model of Mott and Davis [9] stating that a band of localized states (several tenths of eV wide) is located in the center of the band gap of chalcogenide glass semiconductors. Optical transitions of electrons into this band can cause luminescence with the energy of light quanta close to the half-width of the band gap.

The glassy alloy Ag0.05Ga0.05Ge0.95S2 is characterized by the largest transparency window [8] among other glasses of the AgGaSe2 + GeS2 ⇔ AgGaS2 + GeSe2 system. This alloy was doped with an Er2S3 admixture. PL spectra investigation (Figure 4) was performed on the glasses (100 − X)Ag0.05Ga0.05Ge0.95S2-(X) Er2S3, where X = 0.42, 0.25, and 0.18 mol.% (0.27, 0.16, and 0.12 at.% Er, respectively).

Figure 4.

Conversion FL spectra of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses.

The excitation was performed by a laser with 980-nm wavelength which corresponds to the 4I15/2 → 4I11/2 transition, whereas the PL emission band is due to the 4I13/2 → 4I15/2 transition in Er3+ ion, respectively. The PL intensity increases with Er content. The position of the luminescence maximum at 1540 nm does not depend on the content of Er or other components of the glass-forming matrix. The effective width Δλeff of the spectra PL was calculated for these glasses according to the formula

E1

where І(λ) is the emission intensity at wavelength λ and Іmax is the maximum emission intensity.

The maximum Δλeff value was found for the sample with 0.27 at.% Er (61 nm); this decreases the alloys with 0.16 at.% (52 nm) and 0.112 at.% Er (52 nm). The widening of the PL band in erbium-doped glasses was associated by the authors of [10] with the formation of clusters in the samples where Ga/Er < 10 is performed. Among the glassy alloys investigated here, the PL band widens in the sample with 0.27 at.% Er, and the above inequality is fulfilled. The microstructure study of alloys [11] showed the existence of inhomogeneities of 6–7 μm size the concentration of which increases with the amount of erbium. The generated inhomogeneities are good drains of defects which serve as the basis for cluster formation. Higher amounts of erbium favor the formation of clusters which include it. Thus, the PL intensity in the glasses is due to the emission of erbium ions which are uniformly distributed in the glass-forming matrix, as well as those which are located near the inhomogeneities and are involved in the formation of clusters. The study of static magnetization in the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses [12] confirmed the formation of clusters. The calculated number of erbium ions in the cluster was estimated there as 1–1.5 × 103.

The excitation at 980 nm yielded, in addition to the conversion PL (maximum at 1540 nm, Figure 4), the up-conversion PL bands in the visible and near-infrared spectral range at room temperature (Figures 5 and 6).

Figure 5.

Up-conversion FL spectra of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses.

Figure 6.

Up-conversion FL spectra of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses for various excitation power.

For all glasses, the luminescence is represented by three maxima at 520, 657, and 855 nm, which correspond to the radiative transitions 2H11/2 → 4І15/2, 4F9/2 → 4І15/2, and 4S3/2 → 4І13/2 in Er3+ ions, respectively. In addition, a wide PL band in the range of 695–810 nm with an emission maximum at 765 nm was detected for the sample containing 0.27 at.% Er that cannot be interpreted by any radiative transition in erbium ion.

The intensity of the up-conversion PL bands depends on the laser excitation power (IIR) which is expressed by the formula IPL ∝ InIR, where n is the number of infrared photons per one PL photon. The number (n) can be found by the slope of the dependence of log (IPL) on log (IIR). PL spectral dependences for the sample with 0.27 at.% Er at different laser excitation powers are shown in Figure 6; these are also typical of the main maxima (520, 657, and 855 nm) in samples with less erbium content. The logarithmic dependence of the PL intensity on the excitation power [13], log (IPL) from log (PIR), is plotted in Figure 7.

Figure 7.

Dependence of the luminescence intensity on the laser excitation power for the glass with 0.27 at.% Er.

Studies show that two photons with a wavelength of 980 nm are needed for the emission of one IPL photon. An energy level diagram in erbium ions when excited by hν980 quanta is shown in Figure 8. The absorption by the ground-state erbium ion of one hν980 photon excites it to 4I11/2 state. Such a transition can also take place via energy transfer (ET) from the neighboring excited erbium ion.

Figure 8.

Energy level diagram of erbium ions (for the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses, excitation by 980 nm).

The excited state 4F7/2 may be attained by the successive absorption of two hν980 photons as well as by energy transfer to Er3+ ion in the 4I11/2 state from another neighboring excited Er3+ ion [14]:

4I15/2+9804I11/2+9804F7/2E2
4I11/2+4I11/24I15/2+4F7/2E3

The states 2H11/2 and 4S3/2 arise from non-radiative relaxation of the state 4F7/2 due to the small energy distance between them. The non-radiative relaxation of Er3+ from the state 4S3/2 to 4F9/2 is unlikely due to large energy gap between them (about 3000 cm−1) and low energy of phonons. According to Raman spectroscopy study, the energy of phonons for these glasses is close to 300–400 cm−1 [13]. Consequently, the state 4F9/2 may arise by the absorption of the hν980 photon (transition 4I13/2 → 4F9/2) or through the ET from the neighboring excited erbium ion. Additionally, the state 4F9/2 state may appear due to cross-relaxation (CR):

4F7/2+4I11/224F9/2E4

Such a mechanism of occurrence of the excited state 4F9/2 would explain the decrease in the intensity of the green (520 nm) and the amplification of the red PL band with an increase in the content of Er3+ ions when the distance between them decreases and the conditions favor ET.

The increase of PL intensity in the chalcogenide glasses may be due to the increase in erbium content and the change in the composition of the glass-forming matrix. It should be noted that an increase in erbium content in glasses can lead to the concentration quenching of PL [15] as well as to the crystallization of the host. Therefore, increasing the PL efficiency requires the selection of optimal composition of the glass-forming matrix and adding into its composition the maximum concentration of erbium that will not cause PL quenching and the crystallization of glass. The choice of the components of the glass-forming matrix should take into account their glass-forming ability and the ability of sustaining large amount of REs and also maintaining a wide transparency window in the visible and infrared range when adding admixtures. With the above considerations, the Ga2S3-La2S3-Er2S3 system is of interest, in our opinion. Using the technique in paragrap. 2, we successfully introduced up to 40 mol.% La2S3 and 3 mol.% Er2S3 into the glass. The shift of the optical absorption edge does not exceed 0.13 eV with Er2S3 doping and 0.10 eV with the addition of 30–40 mol.% La2S3 [16]. Thus, the luminescence properties of the Ga2S3-La2S3-Er2S3 system glasses at room temperature and 80 K were investigated with a considerable variation in the host composition. The component composition of the glasses is listed in Table 1.

Sample no.Ga2S3La2S3Er2S3
(mol. %)
164351
262353
359401
457403

Table 1.

Component composition of the Ga2S3-La2S3-Er2S3 glasses.

Photoluminescence spectra in the 480–1700 nm range upon laser excitation at 488 nm wavelength at 80 K are shown in Figures 9 and 10. The intense maxima at 550, 855, 985, 1100, and 1540 nm correspond to 4f intra-shell transitions 4S3/2 → 4І15/2, 4S3/2 → 4І13/2, 4І11/2 → 4І15/2, 2H11/2 → 4І11/2, 4I13/2 → 4І15/2 in Er3+ ions. The lower-intensity maxima at 492, 660, 810, and 1245 nm correspond to the transitions 4F7/2 → 4І15/2, 4F9/2 → 4І15/2, 4І9/2 → 4І15/2, 4F7/2 → 4І9/2 in erbium ions, respectively.

Figure 9.

PL spectra of the Ga2S3-La2S3-r2S3 glasses at 80 K (visible range).

Figure 10.

PL spectra of the Ga2S3-La2S3-Er2S3 glasses at 80 K (infrared range).

PL intensity increases in the visible and infrared ranges with Er2S3 concentration at constant content of La2S3. The best medium for PL (the most intense PL) is the glass-forming matrix with 35 mol.% La2S3 and 3 mol.% Er2S3. PL intensity decreases when La2S3 content increased to 40 mol.%. A similar effect was observed by Ivanova in [17] in the glasses of the GeS2-Ga2S3 system, explaining this by an increase in the number of homopolar metallic bonds. It is likely that the number of La-La-type bonds increases in the Ga2S3-La2S3-Er2S3 glasses with increasing La2S3 content.

Changing the component composition of glass leads to redistribution of the intensity of PL bands. The maximum at 550 nm is dominating in the visible range, and its intensity decreases with increasing La2S3 content. The greatest increase in the intensity of PL bands occurs for the infrared spectral range with an increase in erbium concentration. The changes in the PL spectra are clearly related to the mechanism of the realization of excited states in Er3+ ions.

The redistribution of the PL intensity is due to the competing ways of achieving excited states in erbium ions. Figure 11 shows an energy level diagram of erbium ions [18] which reveals the mechanism of PL emission in the glasses of the Ga2S3-La2S3-Er2S3 system. Accordingly, erbium ions jump from the ground to the excited state of 4F7/2 upon excitation by 488 nm wavelength. Intense emission of green and infrared light (550, 1100, and 855 nm) results when the majority of erbium ions non-radiatively relax to the states 2H11/2 and 4S3/2. Only a small fraction of erbium undergoes transitions 4F7/2 → 4I15/2 and 4F7/2 → 4I9/2 as PL bands at 492 and 1245 nm are characterized by low intensity. Additionally, PL with a maximum at 660 nm occurs due to the cross-relaxation process CR resulting in the excited state 4F9/2.

Figure 11.

Energy level diagram of erbium ions (for the Ga2S3-La2S3-Er2S3 glasses).

PL spectra of the Ga2S3-La2S3-Er2S3 glasses at room temperature are shown in Figures 12 and 13. Compared to the spectra at 80 K, the PL intensity at 530 nm increased slightly (transition 2H11/2 → 4I15/2), and the band intensity at 660 nm increased (transition 4F9/2 → 4I15/2). Additionally, the intensity of the maxima of 1100 and 855 nm significantly decreased, and a weak PL band at 1050 nm was observed in the infrared spectral range. Such intensity redistribution of the PL maxima is associated with a change in the concentration of erbium ions in different excited states. This is related to the fact that when the temperature rises, the phonon subsystem of the glass-forming matrix is transformed, so the probability of the energy exchange of the neighboring erbium ions increases. As a result, the role of cross-relaxation processes increases and the number of erbium ions in the state 4F9/2 increases. Thus the intensity of the PL band with a maximum at 660 nm increases. Additionally, CR affects the decrease of the number of erbium ions in the states 2H11/2 and 4S3/2 leading to the decrease of the intensity of the maxima at 1100 and 855 nm at room temperature. The band with a maximum at 1050 nm (transition 4F3/2 → 4I9/2) is completely overlapped by the intense PL maximum at 1100 nm at 80 K.

Figure 12.

PL spectra of the Ga2S3-La2S3-Er2S3 glasses at room temperature (visible range).

Figure 13.

PL spectra of the Ga2S3-La2S3-Er2S3 glasses at room temperature (infrared range).

4. Photoluminescence in erbium-doped single crystals

The occurrence of recombination PL that is characterized by wide emission bands in the visible, rarely in the infrared range, is quite often found in single-crystalline chalcogenide semiconductors at room temperature or low temperatures [19, 20]. From the application viewpoint of laser technology and telecommunications, the introduction of erbium to such materials has significant advantages since the emission bands of erbium-doped glasses and single crystals are usually intense and narrow. The addition of erbium is also accompanied by the extinction of PL radiation [21] which is due to the crystalline or amorphous chalcogenide host. The influence of external factors on the PL efficiency in erbium-doped chalcogenides is limited due to the shielding of radiative transitions in the 4f-shell of Er by outer shells. At the same time, the local environment of erbium ion, both in glasses and single crystals, affects the efficiency of PL emission which is why it is extremely important for the design of fluorescent materials. It should be noted that the single crystals, unlike glasses, do not permit a wide variation of the component composition since it is limited by the solid solubility of impurities and the homogeneity of the crystalline compound. It is more difficult to select the composition of the host to obtain effective emission in erbium-doped single crystals; therefore, PL is less common in these than in the corresponding amorphous media.

The investigation of the optical properties of the single crystals (Ga55In45)2S300 and (Ga54.59In44.66Er0.75)2S300 [7] determined that the introduction of erbium does not result in a change in the bandgap energy or significant changes in the electronic structure [22]. The absorption maxima at 530, 660, 810, 980, and 1530 nm [7] recorded for (Ga54.59In44.66Er0.75)2S300 single crystal correspond to 4f intra-shell transitions from the ground state to the excited states 2H11/2, 4F9/2, 4I9/2, 4I11/2, and 4I13/2 in Er3+ ions, respectively. PL spectra at room temperature in the visible and close infrared range (600–1650 nm) were studied when excited by a laser with 532 nm wavelength (Figure 14). Two intense PL bands with maxima at 810 and 1540 nm were recorded, which correspond to the transitions of 4I9/2 → 4I15/2 and 4І13/2 → 4I15/2 in Er3+ ions, respectively.

Figure 14.

Visible (a) and NIR (b) PL spectra of the (Ga54.59In44.66Er0.75)2S300 single crystal (excitation by 532 nm).

Er3+ ions excited by a 532 nm laser are promoted from the ground 4I15/2 to the excited state 2H11/2. The emission mechanism in this case is quite simple as demonstrated at an energy transition diagram in erbium ions (Figure 15). Erbium ions cannot relax non-radiatively from the state 4S3/2 to 4F9/2 or 4І9/2 due to the large energy distance and the low phonons energy (200–300 cm−1 for the single crystals (Ga55In45)2S300 and (Ga54.59In44.66Er0.75)2S300 [23]). Therefore, the appearance of excited states 4I9/2 involves the cross-relaxation process CR. Energy transfer between adjacent erbium ions in the states 2H11/2 and 4І15/2 promotes one ion into the excited state 4І9/2 and the other into 4І13/2:

2H11/2+4I15/24I9/2+4I13/2E5

Figure 15.

Energy level diagram in erbium ions (for a (Ga54.59In44.66Er0.75)2S300 single crystal, excitation by 532 nm).

Such a mechanism yields substantial numbers of erbium ions in excited states 4I9/2 and 4I13/2, which results in PL with maxima at 810 and 1540 nm.

Similar to glasses, we also investigated single crystals in which two rare earth metals were introduced. (Ga55In45)2S300 and (Ga54.59In44.66Er0.75)2S300 single crystals were obtained by a solution-melt method [24] selected in accordance with the phase diagram of the Ga2S3-La2S3 system. The bandgap energy of the single crystals little changes upon erbium doping at 2.01 and 1.99 eV for (Ga55In45)2S300 and (Ga54.59In44.66Er0.75)2S300, respectively [24]. PL of (Ga54.59In44.66Er0.75)2S300 single crystal in the 500–1700 nm range was investigated at room temperature (Figure 16). Four intense PL bands with maxima at 525, 545, 980, and 1540 nm and one low-intensity band at 660 nm were recorded. They correspond to the transitions in Er3+ ions from excited states 2H11/2, 4S3/2, 4I11/2, 4I13/2, and 4F9/2 to the ground state.

Figure 16.

PL of the (Ga69.75La29.75Er0.5)2S300 single crystal (excitation by 810 nm).

Energy transition diagram (Figure 17) shows that the wavelength of 810 nm can excite erbium ions from the ground state 4I15/2 to the state 4I9/2. Er3+ ions, either by directly absorbing light quanta or through ET, can be promoted from the state 4I13/2 to 2H11/2 resulting in PL at 525 nm. Additionally, after non-radiative relaxation of erbium ions to the state 4S3/2, there is a PL band with a maximum at 545 nm [25]. The appearance of excited states 4F9/2 and 4I11/2 occurs by cross-relaxation CR 2:

2H11/2+4I13/24F9/2+4I11/2E6

Figure 17.

Energy level diagram in erbium ions (for a (Ga69.75La29.75Er0.5)2S300 single crystal, excitation by 810 nm).

The transition from these states to the ground state produces PL at 660 and 980 nm. An intense PL band at 1540 nm wavelength occurs due to the formation of a significant number of Er3+ ions in the state 4I13/2 by cross-relaxation CR 1:

2H11/2+4I15/24I9/2+4I13/2E7

The excitation of the single crystal yields also an intense up-converted green PL (Figure 16). Therefore, (Ga54.59In44.66Er0.75)2S300 single crystal can be recommended as a material for the manufacture of light converters.

5. The influence of temperature on the photoluminescent properties of glasses and crystals

Doping the binary and ternary chalcogenides, particularly by rare earth metals, creates materials for the design of active and passive media for laser technology, photonic devices, light converters, and telecommunications. Special attention is given to the crystalline and amorphous environments that can exhibit high-intensity PL under the influence of external factors.

Additionally, modern optoelectronic industry actively researches and implements high-precision temperature sensors based on the sensitivity of PL emission to temperature changes. The design of such devices requires the investigation of the effect of temperature on the mechanism of the achievement of excited states and the processes of the relaxation of erbium ions when the PL intensity changes in various temperature ranges. This will allow optimizing the component composition of crystals and glasses to produce effective luminescent materials for the development of non-contact optical sensors.

PL of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses in 600–1050 nm range was investigated in a temperature range of 80–300 K upon laser excitation at 532 nm [26]. Recorded PL bands with maxima at 660, 860, and 980 nm correspond to the radiative transitions 4F9/2 → 4I15/2, 4S3/2 → 4I13/2, 4I11/2 → 4I15/2 in erbium ions, respectively. The dependences of PL intensity on wavelength at different temperatures for the sample with 0.27 at.% Er are plotted in Figure 18 (also typical of the glasses with 0.12, 0.16 at.% Er). The temperature increase leads to changes in the ratio of PL intensities, with the intensity of all bands decreasing at temperatures above 180 K. The PL band with a maximum at 860 nm is the most sensitive to temperature changes. The PL emission mechanism is well explained by the energy level diagram of Er3+ ions (Figure 19).

Figure 18.

PL spectra of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glass (0.27 аt.% Er) at various temperatures.

Figure 19.

Energy level diagram in erbium ions (for the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses, excitation by 532 nm).

Illumination by 532 nm wavelength promotes erbium ions to the excited state 2H11/2. The states 4F9/2, 4I9/2, and 4I11/2 result in the cross-relaxation processes CR1, CR2, and CR3. Er3+ ions in the 2H11/2 state can also nonradiatively relax to the 4S3/2 state due to small energy gap between them. The integral intensity of the emission bands was calculated from the results of the investigation of PL spectra. The dependence of integral PL intensity on temperature is shown in Figure 20 for the glass with 0.27 at.% Er.

Figure 20.

Temperature dependence of integral PL intensity of the Ag0.05Ga0.05Ge0.95S2-Er2S3 glass (0.27 аt.% Er).

The dependence of PL intensity on temperature can be described using the probability of radiative and non-radiative processes by the formula [27]:

E8

where Іо is a constant, k is Boltzmann’s constant, ωnr, ωr is the probability of non-radiative and radiative processes, respectively, and Et is the thermal activation energy of luminescence.

The I(T) dependence (Figure 20, solid line) was calculated from Eq. (8) for the band with the 860 nm maximum, and the corresponding activation energy Et was calculated as 90 ± 6 meV [26]. According to the diagram in Figure 19, this energy determines the activation of erbium ions from the state 4S3/2 в 2H11/2 (i.e., the energy gap between these states). It should be noted that changes in PL intensity is complex. Therefore we calculated the logarithm of the ratio of integral PL intensities ln (І980660) and plotted its dependence on temperature (Figure 21). This dependence is linear in the range of 125–300 K. The sensitivity of the sample as the temperature sensor was calculated according to the results of these studies as 0.43 K−1.

Figure 21.

Ratio of integral PL intensity of the glasses of the Ag0.05Ga0.05Ge0.95S2-Er2S3 system (0.27 аt.% Er).

Erbium-doped single crystals may also exhibit changes of PL intensity with temperature. PL spectra of the single crystal (Ga54.59In44.66Er0.75)2S300 were investigated at 150, 200, 250, and 300 K upon laser excitation at 980 nm wavelength (Figures 22 and 23). The position and shape of the maxima do not change but the intensity of PL increases with temperature. For the majority of semiconductor materials where the recombination luminescence was recorded [28], the PL intensity decreases with increasing temperature. At the same time, the emission intensity may increase with temperature in crystals and glasses where PL is associated with transitions in the 4f-shell of erbium ions. This is due to the fact that the neighboring erbium ions are in different excited states. As the temperature increases, the phonon subsystem of the crystal changes which contributes to the cross-relaxation processes of Еr3+ ions. If a crystal is excited by 980 nm wavelength, the absorption of two photons promotes erbium ion into the state 4F7/2 (Figure 22). Due to small energy gap, Еr3+ ions can non-radiatively relax to the state 2H11/2. Excited states 4I13/2 and 4I9/2 result from the CR process:

4I15/2+2H11/24I13/2+4I9/2E9

Figure 22.

Conversion PL spectra of the (Ga54.59In44.66Er0.75)2S300 single crystal at various temperatures.

Figure 23.

Up-conversion PL spectra of the (Ga54.59In44.66Er0.75)2S300 single crystal at various temperatures.

Therefore, CR processes play greater role with increasing temperature, which will contribute to a higher concentration of erbium ions in the 4I9/2 and 4I13/2 states and the increase in PL intensity.

The integral PL intensity for both maxima was calculated from the spectra of up-conversion and conversion PL of (Ga54.59In44.66Er0.75)2S300 single crystal (Figure 24). The plots of integral PL intensity linearly depend on temperature. From the results of the temperature dependence of the integral PL intensity, the sensitivity was calculated as 1.187 × 10−3 K−1 for PL at 805 nm and 1.818 × 10−3 K−1 for the maximum at 1540 nm. It should be noted that the sensitivity defined as the ratio of the integral intensities of the two PL bands is higher in the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses. The sensitivity in (Ga54.59In44.66Er0.75)2S300 single crystal was calculated separately for each PL band (maxima at 805 and 1540 nm), the latter being in the operating range of fiber-optic networks and telecommunication devices.

Figure 24.

Temperature dependence of integral PL intensity of the (Ga54.59In44.66Er0.75)2S300 single crystal.

Therefore, in a limited temperature range, the Ag0.05Ga0.05Ge0.95S2-Er2S3 glasses (with 0.27 at.% Er) and the single crystals (Ga54.59In44.66Er0.75)2S300 can be used to design non-contact optical temperature sensors.

6. Conclusions

The principal mechanisms of the occurrence of PL due to the transitions in the 4f-shell of erbium ions are presented on the basis of sulfide glasses and single crystals. The appearance of many emission bands in chalcogenide glasses (unlike single crystals) is due to the fact that in an amorphous medium, erbium ions may occupy several different positions in the glass-forming matrix. The change of the excitation wavelength leads to a change in the mechanism for the excited states in Er3+ ions and the emergence of some radiation bands and the extinction of others. Energy exchange processes (energy transfer, cross-relaxation) between the neighboring Er3+ ions strongly influence the intensity of the conversion and up-conversion PL. The investigation of the temperature dependence of PL indicates that erbium-doped chalcogenide semiconductors can be recommended as materials for the design of non-contact optical thermometers.

Download

chapter PDF

© 2018 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Volodymyr V. Halyan and Inna A. Ivashchenko (December 8th 2018). Mechanism of Photoluminescence in Erbium-Doped Chalcogenide [Online First], IntechOpen, DOI: 10.5772/intechopen.81445. Available from:

chapter statistics

207total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More about us