Investigation of Zn/Ni-Based Electrocatalysts for Electrochemical Conversion of CO2 to SYNGAS

By Mohammadali Beheshti, Saeid Kakooei, Mokhtar Che Ismail and Shohreh Shahrestani

Submitted: September 8th 2020Reviewed: December 23rd 2020Published: January 11th 2021

DOI: 10.5772/intechopen.95626

Downloaded: 41

Abstract

In the last decade, there is some research on the conversion of CO2 to energy form. CO2 can be converted to value-added chemicals including HCOOH, CO, CH4, C2H4, and liquid hydrocarbons that can be used in various industries. Among the methods, electrochemical methods are of concern regarding their capability to operate with an acceptable reaction rate and great efficiency at room temperature and can be easily coupled with renewable energy sources. Besides, electrochemical cell devices have been manufactured in a variety of sizes, from portable to large-scale applications. Catalysts that optionally reduce CO2 at low potential are required. Therefore, choosing a suitable electrocatalyst is very important. This chapter focused on the electrochemical reduction of CO2 by Zn-Ni bimetallic electrocatalyst. The Zn-Ni coatings were deposited on the low-carbon steel substrate. Electrochemical deposition parameters such as temperature in terms of LPR corrosion rate, microstructure, microcracks, and its composition have been investigated. Then, the electrocatalyst stability and activity, as well as gas intensity and selectivity, were inspected by SEM/EDX analysis, GC, and electrochemical tests. Among the electrocatalysts for CO2 reduction reaction, the Zn65%-Ni35% electrode with cluster-like microstructure had the best performance for CO2 reduction reaction according to minimum coke formation (<10%) and optimum CO and H2 faradaic efficiencies (CO FE% = 55% and H2 FE% = 45%).

Keywords

  • electrocatalyst
  • electrochemical method
  • CO2 reduction reaction
  • Zn-Ni
  • energy conversion
  • pollution
  • catalyst activity and stability

1. Introduction

Carbon dioxide is a chemical compound made up of one carbon atom and two oxygen atoms. It is existing in minimal concentrations in the atmosphere and behaves as a greenhouse gas that promotes environmental warming and pollution. However, carbon dioxide can be used as a source of high-value chemicals, as a source of sustainable energy. So far, many activities have been done to convert CO2 into chemical materials, which can be applied as fuel for the industries.

With the increasing demand for energy and population growth, CO2 emissions have grown as a by-product of power and industrial plants. In the last decade, CO2 conversion has increased to other beneficial products. This process is useful for reducing pollution and warming of the earth. Developing a variety of electrocatalysts with high efficiency and good stability is a crucial issue [1].

The electrochemical CO2 reaction reduction in recent decades has become crucial because it is a good reaction to artificial fuels and energy storage. When this process is linked to renewable energy sources such as solar cells, it can be a good alternative to fossil fuels. It also reduces CO2 emissions in the atmosphere. But there are major problems for the reaction of CO2 reduction, which includes low efficiency and low catalytic activity with cost-effective catalysts. Therefore, there is an important challenge in the present research, so that catalyst with better selectivity and higher activity and stability can be developed [2].

In recent years, several studies were done on various electrocatalysts, but yet, there are problems in Faradaic Efficiency (FE), Current Density (CD), Energy Efficiency, electrocatalyst deactivate, the internal resistance of electrocatalysts, and the potential for scalability to the large sizes without the loss of efficiency, because CO2 is a thermodynamically stable molecule, it is fully oxidized [3, 4, 5, 6, 7, 8, 9, 10, 11, 12]. A suitable electrocatalyst to reduce CO2 is necessary to reach a low-cost process with acceptable selectivity and efficiency. In recent decades, the electrochemical reduction of CO2 has interested a lot of consideration as low-cost electricity can come from renewable sources of energy such as solar and wind [13, 14, 15, 16, 17, 18].

1.1 Zn-Ni coating

Zinc as another choice of cadmium has been studied for its ability to resist corrosion regarding its sacrificial properties and has demonstrated its ability to provide adequate corrosion behavior results through the study conducted on mechanical properties and corrosion protection of Zn electrodeposition [19]. Though Zn is considered a possible option, its corrosion behavior does not look acceptable in an aggressive condition with greater temperatures. Electrodeposited Zn coatings study tests indicated that pure Zn has weak corrosion resistance properties compared to cadmium [20]. Therefore, the need for metal coatings with corrosion properties outstanding to those of pure Zn and comparable or improved to cadmium has driven the industrial production of electrodeposits involving Zn alloys with VIIIB-group metals (e.g. Zn-Fe, Zn-Ni, Zn-Co) [21]. The electrodeposition of Zn and its eight-group metals including Co, Fe, and Ni have been extensively investigated and analyzed for their ability to be an excellent corrosion resistant alloy.

1.1.1 Zinc-nickel alloy corrosion behavior

In recent years, a lot of research has been performed to investigate the possibility that the Zn-Ni alloy could be a substitute with a corrosion property corresponding to the toxic coatings of cadmium. Much research has also been done to distinguish and determine the corrosion resistance of the Zn-Ni coatings [22, 23, 24, 25]. The corrosion resistance of deposited Zn-Ni coatings on steel substrate indicated as having the acceptable corrosion property (corrosion rate: ~ 11 mm/year) was reached for Zn-Ni alloys in the range from 12 to 15 wt.% of Ni content in the coating so that the coating with Ni content from 12 to 15 wt.% maintains the anodic behavior of the steel, retaining the sacrificial behavior with a decrease corrosion rate after the addition of Ni, which increases the potential nearer to the substrate providing protection for a too time [21]. This has been endorsed by reports conducted by other authors [22, 23, 24, 25] who have stated that Zn-Ni coating with a Ni amount of 12 to 15 wt.% supplies adequate corrosion protection. While the coating retains its sacrificial behavior regarding the steel substrate, whenever the alloy with more than 30 wt.% of Ni turns nobler than the substrate, missing its sacrificial behavior. Hence, it led to preferential corrosion of the steel, and Ni amount of less than 10 wt.% in the coating produced smaller barrier performance. Byk et al. [25] performed tests showing the greatest corrosion resistance properties utilizing a poor acid chloride solution with the Zn-(15 wt.%) Ni coating having the least corrosion CD, demonstrating the best corrosion protection, and this is qualified to the existence of the γ phase (Ni5Zn21) which is gained with Zn-Ni coatings with Ni amount from 12 to 15 wt.% [25]. The coatings of Zn-Ni coating with 10–15 wt.% of Ni have more suitable corrosion resistance, better weldability, and superior formability. The presence of Ni in the Zn-Ni alloy in the optimal range from 12 to 15 wt.% reduces the rate of Zn dissolution, supplying greater and longer corrosion resistance than pure Zn [24].

1.2 CO2 reduction reaction

Environments change due to greenhouse gases (CO2) is a significant hazard to the protection of human society. The capture and conversion of carbon to the value-added chemical are attended to be the most agreeable method to prevent the rise of CO2 in the environment as seen in Figure 1. But the cost of high technology accessible to capture, store, and convert CO2 stops its functional operation [26]. Recycling CO2 and transforming it into value-added chemicals create challenges for researchers in the area of catalysts. Among the various methods, the electrochemical method has unique advantages [27, 28, 29]. Most of the electrochemical reactions can be seen in small to industrial conditions. Besides, if the electricity is required from renewable sources, these sources of energy generate the required electricity, CO2 will not be produced and, therefore, will have a good effect on the worldwide CO2 level [30].

Figure 1.

Graphical schematic of the influence of CO2 on the globe and conversion of CO2 to the useable energy.

Studies showed that CO was an intermediator and also methane (CH4) or ethylene (C2H4) was generated from HCO* or COH* intermediates. Norskov et al. presented details of reaction pathways to produce C2H4 and CH4 from the CO2 reduction reaction at copper catalysts using the Density Functional Theory (DFT) [31, 32, 33, 34]. The outcomes demonstrated that the formation of HCO* was a key step for the reaction. They also compared the carbon dioxide reduction reaction in several transition-metal electrodes and determined that copper is the most efficient electrode for this case [35]. In the electrolysis of CO2, the anode and cathode were located on separate sides, which were interconnected with a membrane in the middle of them. In the anode, the water oxidized to ion hydrogen (H+) and molecular oxygen (O2), while in the cathode, CO2 was reduced to carbon compounds, and hydrogen was reduced [36]. The electrocatalysts for the reduction reaction of CO2 totally divided into a few different classes as seen in Figure 2. Metals such as Ni, Pt, Al, Fe, Ti, and Ga were used as the catalysts for H2 production, and CO was not created as the main product [37, 38, 39, 40]. The H2 evolution reaction rates by these group metals are commonly greater than that of the CO2RR rate.

Figure 2.

A set of three main categories of electrocatalysts for CO2 reduction reaction [36, 62, 63, 64, 65, 66, 67, 68, 69, 70, 71, 72, 73, 74].

Another class of metals of Ag, Au, and Zn convert CO2 to CO with an acceptable efficiency [41]. Catalysts consist of In, Pb, Hg, and Sn convert CO2 to formate as the main product. On these metals, the mechanism of CO2RR to formate is different in which there is no breaking of the C-O bond. Electrodes including W, Cr, and Mo have been reported as inadequate catalysts because of weak selectivity and reduction rate. Copper as a metal catalyst can react to a reduction in CO2 to alcohol and hydrocarbons (C2H4, CH4, CH3OH). However, recent research had shown that the CO2RR to these fuels was made at lower efficiency, which was influenced by the binding-energy of the intermediate species of CO. For example, Ag and Au catalysts can produce CO more rather due to less energy for intermediate carbon monoxide molecules. Since it can be evolved from the surface without more reaction. Therefore, producing higher carbon species at these levels is extremely minimal. However, Cu is a unique catalyst that allows it to produce various carbonaceous products (such as, alcohol and hydrocarbons) with higher activity [41].

Electrodes play a key role in all reactions according to heterogeneous electrochemical reactions, such as CO2RR [42]. The durability and performance of the electrochemical cells are essentially defined by the processes happening at the electrolyte-electrode interface. Overall, electrodes include an electrocatalyst layer as well as a backing layer or substrate that attend multiple acts: firstly, to transport reactant gases, CO2, from the electrolyte to the catalyst layer; secondly, to derive products from the catalyst layer into the membrane/electrolyte; and lastly, electrons connectivity with little resistance [42, 43, 44, 45]. Most electrode efficiency, and accordingly electrochemical cell efficiency, requires enhancing all these three processes that greatly relate to the complicated microstructure of the electrodes. Till now, the nanoparticles of Ag [46, 47], Sn [48], Au [49], MoO2 [50, 51], Bi [52], MoS2 [49], etc., coated on low carbon steel substrate and Cu2O/TiO2/FTO [53] have been utilized to convert CO2 to CO applying room-temperature ionic liquids (RTILs) as electrocatalysts. Nevertheless, none of these materials enabled the development of CO with a CD of >100 mA/cm2 in CO2RR during controlled potential electrolysis (CPE) tests in combination with any of the utilized RTIL assistant catalysts, which is required to commercially use any of these procedures. In the last decade, the electrochemical CO2RR had been widely considered [54, 55, 56]. The reduction reaction products of electrochemical CO2RR on the Cu-based electrodes are hydrocarbons for example C2H4 and CH4 [57, 58, 59]. Practical investigations on the electrochemical CO2RR in the base electrodes of copper showed that the exhaust gas contains CO, CH4, C2H4, and primary alcohol that depended on their electrolyte [60, 61]. There were numerous studies of electrochemically CO2 reduction reaction on Cu-based electrodes [62, 63, 64].

Table 1 shows the summarized characterization of electrocatalysts for the CO2RR to various. As shown in Table 1 and Figure 3 for SYNGAS (CO + H2) production, there is not enough research in this field. Also, for the production of SYNGAS, the Au0.76 –Pd0.24 electrocatalyst has the highest Faraday efficiency (~90%) and CD (~10 mA/cm2), which is a high-cost and unsuitable alloy electrode for large-scale use [67]. Other electrocatalysts for SYNGAS production have low FE and/or low CD, as can be seen in Table 1. The Ag/Au nanostructure catalysts for electrochemical CO2RR to CO with a FE of further than 90% and a CD greater than 30 mAcm−2 have been stated by researchers [65, 66, 67, 68]. Zinc performs as an electrocatalyst for CO2RR to CO, while it is a cost-effective, non-noble, and abundant choice to gold and silver [69]. There are also statements of nano-structured Zn catalysts including hexagonal, dendritic, and nanoscale [70, 71, 72]. Quan et al. have reported Zn nanoscale and Zn foil as a catalyst for the CO2RR at the NaCl and NaHCO3 electrolytes. They demonstrated that the nano-scale catalyst at NaCl cathodic solution has the greatest proficiency in terms of CD and FE about 6 mA.cm−2 and > 90%, respectively, at a potential of −1.6 V by linear sweep voltammetry (LSV) method [70]. Rosen et al. have studied Zn balks and Zn dendrite catalysts for the electrochemical CO2RR in 0.5 M NaHCO3 cathodic solution. They stated Zn dendrite electrocatalyst has a CD of 4 mA.cm−2 at the potential value of −1.14 V (vs. RHE) and FE of 80% [71]. By modifying the surface microstructure, morphology, or orientation of the Zn catalyst, the more FE and product selectivity can be attained for converting CO2 to CO.

ElectrocatalystsFaradaic EfficiencyCurrent Density (mA/cm2)Main productRef.
Fe-Porphyrin< 5Hydrocarbon[75]
Sn-based91%15[48]
nano-SnO280%9[76]
Sn foil<20%< 5[76]
Sn/SnOx nanoclusters<40%[76]
Ni-Ga<70%<1[77]
Molybdenum disulphide~90%65[49]
Cl-induced bi-phasic Cu2O–Cu~70%<0.2[76]
Conductive Polymer microporous polymer doped with Pt np>95%[78]
Strontium-doped lanthanum<15%<20[79]
Iridium/Ruthenium Oxide~90%[80]
Zn-Cu60%4[74]
Pb - Sn2.5[35]
Zn-Co based70%-8[3]
Cu-Pt<38%[81]
Cu-Ni<40%[82]
Ni-based80%5[3]
CNT/GC<10%~2[76]
NCNT/GC60%~4[76]
PEI-NCNT/GC<85%~10[76]
Nitrogendoped nanodiamond90%~1[76]
Pd –based<50%<5(CO + H2)
Syngas
[83]
Au0.76 –Pd0.24~90%<10[84]
Cu-Co33%8[85]
Au0.78 –Pt0.22~90%0.6[86]
Cu-Ag~64%10[87]
Bismuth- based<90%<4Carbon monoxide (CO)[52]
[EMIM]BF4-Bi93%4[76]
Graphene oxide/carbon nanotube85%2.3[88]
carbon paper68%0.9[89]
Sn/SnOx nanoclusters<60%[76]
Zn electrode64%2.8[76]
Zn porous77.9%8[76]
Zn dendrite80%12[74]
Zn hexagonal~83%4.4[75]
Cu polycrystalline30%[76]
Au np>90%81[68]
Au bulk80%2.2[70]
Oxide Derived-Au10[65]
Ag bulk82%2.0[46]
Ag np~80%29[69]
Ag np92%10[71]

Table 1.

Product distribution for electrochemical CO2 reduction reaction on various electrocatalysts.

Figure 3.

Total published documents for the electrochemical CO2 reduction reaction and specifically convert CO2 to SYNGAS in terms of over time [Scopus data based].

Nguyen et al. showed that microstructural or morphological changes in catalysts play a significant role in developing CO2RR [73]. The surface of the Zn catalyst is simply oxidized although immersed in aqueous solutions or exposed to air. Thus, situations should be restricted to avoid zinc oxidation [73]. Nguyen et al. have also reported a porous nanostructure of the Zn catalysts which were prepared of zinc-oxide for the CO2RR. By applying this porous metal, they obtained a faradaic efficiency of 78.5% for CO2RR at a potential value of −0.95 V (vs RHE) in the KHCO3 electrolyte [73]. Keerthiga and Chetty have reported a modified zinc-copper catalyst for the CO2RR to hydrogen, C2H6, and CH4 products. They coated zinc on the copper with different concentrations of electrolytes, and the outcomes were evaluated with pure Cu and Zn catalysts. They showed that zinc-copper with a high-level concentration of electrolyte had superior performance, also, the FE of CH4 was the order Zn (7%) < Cu (23%) < Cu-Zn (52%). Moreover, the H2 FE for Cu and Cu-Zn were 68% and 8%, respectively [74].

In this way, it has been selected inexpensive materials as electrocatalysts for commercial and industrial applications. Electrocatalysts must be appropriate that could have acceptable efficiency and cheap price for the reforming process. By referring to Figure 2, zinc and nickel are affordable materials for carbon monoxide and hydrogen production, respectively. Hence, to produce SYNGAS (CO + H2) in this study, the Zn-Ni bimetallic material is chosen from these two groups of catalysts for CO and H2 products. Other electrocatalysts are either inefficient or expensive. This work aims to investigate the Znx-Ni1-x coatings for the electrochemical CO2 reduction reaction.

2. Experimental methods

2.1 Preparation and investigation of Zn-Ni Electrocatalyst for CO2 reduction reaction

Zinc-nickel Alloys were coated on the low-carbon steel substrate by chronopotentiometry method at different electrochemical parameters. Then, Zn-Ni coatings were investigated in terms of microstructure, microcrack formation, and coating composition using SEM / EDX analysis and corrosion resistance by Autolab potentiostat (Model: PGSTAT128N) to obtain the coating with the best performance and quality. Besides, the coatings were analyzed using SEM/EDX analysis after CO2 reduction reaction for microstructure and coke formation, as well as gas efficiency by gas chromatography analyzer. Nickel chloride hexahydrate (NiCl2.6H2O), ammonium chloride (NH4Cl), and zinc chloride (ZnCl2) of raw materials were utilized for bath electrolyte preparation and ammonia solution (25%) for pH modification. All electrolytes were made using distilled water. The zinc and nickel alloy solutions were prepared in the laboratory to allow the study of the deposition at different bath solution temperatures. The pH of the solution was measured using a pH meter. Ammonia solution (25%) was used to raise the pH of the electrolyte to the needed level of pH 5. The solution was stirred using a glass rod and the pH measuring was taken applying a pH meter, continuously. Chronopotentiometry electrodeposition was applied at different bath solution temperatures of 25°C, 40°C, 60°C, and 70°C. There were three types of electrodes, low carbon steel (working electrode), Ag/AgCl (reference electrode), and Pt mesh (counter electrode). The electrodeposition process was performed galvanostatically for each deposition temperature. The experimental setup for electrodeposition was performed as seen in Figure 4.

Figure 4.

Electrodeposition setup for Zn-Ni coatings, (1) counter electrode, (2) reference electrode (3) working electrode, (4) thermometer.

The deposited Zn-Ni coatings were analyzed on their compositional and microstructural properties applying SEM. The morphologies were observed and investigated for the electrodeposited zinc-nickel alloy samples at different temperatures of the bath solution. The material composition is determined by the SEM equipped with EDX which shows the composition information of the alloy coating. Linear polarization resistance (LPR) analysis was performed regarding the ASTM standard of G 96.– 90 (Reapproved 2001)e1.

2.2 Electrochemical CO2 reduction reaction

For CO2RR an H-shaped electrochemical cell was used which has 2-chambers (cathodic and anodic sections) that were connected with membrane Nafion 117 as seen in Figure 5. CO2 gas was inserted into the cathodic section for the reduction process. In this method, electrocatalyst, reference electrodes (Ag/AgCl), and CO2 saturated cathodic electrolyte were in the cathodic part, where CO2RR happened, in the other part, the counter electrode (graphite) and anodic electrolyte (0.1 M H2SO4) were placed where the oxidation occurred. It was, therefore, predicted that SYNGAS (H2 + CO) and coke would form in the cathodic portion, and O2 would be produced in the anodic portion. Working, reference, and counter electrodes (WE, RE, and CE), were linked to the Autolab potentiostat device (Model: PGSTAT128N) to inspect potential and current records. A gas bag was attached to the exhaust to collect products for gas chromatography to characterize gases. Images of the catalyst morphologies were examined utilizing SEM. The catalysts were analyzed by EDX for coke formation and electrocatalyst surface compositions.

Figure 5.

Cell setup for electrochemical CO2RR by Zn-Ni electrocatalyst, graphite CE, 0.1 M KCl (cathodic solution), H2SO4 (anodic solution) and Ag/AgCl RE.

3. Results and discussions

3.1 Zn-Ni electrodeposition

The cathodic protection (CP) graph at various temperatures for the Zn-Ni deposition is displayed in Figure 6. The graph of the potential in terms of time for Zn-Ni coating depositions at 25°C, 40°C, 60°C, and 70°C were seen throughout the electrodeposition process. A decrease (more positive) in CP was detected over time with increasing temperature. The CP in chronopotentiometry was related to the ion’s concentration becoming reduced at the substrate surface in response to the utilized current.

Figure 6.

Deposition potential of Zn-Ni coatings in terms of time by chronopotentiometry method at various bath solution temperatures.

The standard potential Eo (V) for Ni and Zn is −0.25V and 0.76 V (vs. SHE), respectively [90]. The CPs seen in the deposition were nearest to Eo (V) of the reactants that were converted to its metal. Therefore, the outcomes on the decrease in CP towards a further positive amount over time for electrodepositions at high temperature (60°C and 70°C) demonstrated the CP’s deposition was shifting nearer to Eo (V) of Ni reduction, favoring the reaction of Ni-ion reduction to Ni-solid on the substrate. This opinion was more confirmed by EDX outcomes (Figure 7). The rise in Ni amount was assigned to a decrease in CP (more positive) over time through the electrodeposition reaction. This supposition is reported by Velichenko et al. [91], who stated the decrease in CP with rising Ni-ion concentration in the bath solution resulting in an improvement in Ni deposition. Qiao et al. [92] detected similar findings of reducing CP with increasing deposited Ni amount in the surface deposition with rising temperature.

Figure 7.

EDX analysis results in terms of Zn and Ni contents (wt%) vs. bath solution temperature (°C).

3.2 Linear polarization resistance testing for Zn-Ni deposits

Zn and Ni amounts in the coatings have a considerable effect on the corrosion properties of Zn-Ni deposits. As revealed by Baldwin et al. [93] and Conde et al. [21], the lowest corrosion rate is obtained when the Ni amount is between 12 wt.% to 15 wt.% in the coating. Zn being a lower noble metal plays as an anode that sacrifices in relative to the substrate under a standard situation. Zn is extra favored compared with a nobler metal for instance Ni to be developed into coatings regarding its further sacrificial behavior. But adding more noble elements to Zn improves the corrosion resistance of Zn. By adding Ni to Zn, the rate of sacrificing of coating for the substrate is lower compared to bare Zn. Ni act to hinder or reduce the dissolution rate of Zn. But, when the Ni amount in the coating enhancements to more than 30%, the sacrificial performance decreases, and the coating turn nobler compared to the substrate (Steel). At this stage, the corrosion rate is entirely according to the coating characteristics. As seen in Figure 8, with rising temperatures, the corrosion rate increases. This shows that adding Ni to Zn no more enhances corrosion resistance. The coating turns nobler than the substrate and the existence of cracks that are detected causing a rise in the corrosion rate. As the bath solution temperature increases, hydrogen reduction occurs around the working electrode, which creates bubbles form on the surface that prevents the deposition. On the other hand, hydrogen penetrates the coating and makes internal stress. The cracks and disruptions (as shown in Figure 9) in the coatings increase speed the corrosion rate of the substrate. These clarify the important variation in the corrosion rate for coatings deposited at 25°C and 40°C, 60°C, and 70°C.

Figure 8.

LPR corrosion rate measurements taken for Zn-Ni alloy coatings vs. uncoated carbon steel for hourly for 24 h.

Figure 9.

SEM images for electrodeposition of Zn-Ni alloy coatings at temperature of (a) 25°C, (b) 40°C, (c) 60°C, and (d) 70°C of bath solution.

The ratio of Zn and Ni for deposits formed at 25° C is in the optimal range of Ni amount from 12 to 15 wt.%. Therefore, the sacrificial performance of Zn is retained relative to the adding of the Ni, and this makes the steel substrate with decreasing corrosion rate as Zn acts as an anode. By adding 12–15 wt.% of Ni, the dissolution rate of Zn slows down, and the corrosion rate reduces. The cracks and defects in the deposits do not substantially influence the corrosion properties of the metal layers, as further anodic Zn causes preferential corrosion.

3.3 SEM and EDX analysis for Zn-Ni deposits

As the bath electrolyte temperature raises, the ion mobility in the electrolyte rises. Hence, the coatings can be smoother. However, the SEM results displayed in Figure 9 indicate that microcracks are detected in all deposited coatings at various temperatures. The micro-cracks intensity with rising the bath solution temperature is considered to be 25°C < 40°C < 60°C < 70°C. The microcracks formation can depend on the internal stress created and the evolution of hydrogen during the deposition. As the temperature increased, the evolution of hydrogen happened.

Enhancement of inner stress through deposition can be attributed to a lot of reasons. Alfantazi et al. [94] revealed the existence of microcracks in Zn-Ni coatings when the Ni amount in the coating increased. Qiao et al. [92] and Rehim et al. [95] reported the micro-cracks in the Zn-Ni coatings deposited in the acidic bath solution were attributed to H2 embrittlement via the H2 evolution. A rise in the hydrogen release was observed with the outputs of a rise in the hydrogen CD with the temperature rises. This H2 reduction reaction causes H2 atoms to penetrate the coated layer, straining the crystal lattice, and causing high-stress internal cracks.

3.4 Investigation of Zn-Ni bimetallic electrocatalysts for CO2RR

To realize the impacts of the catalysts for the CO2RR, the composition, morphology, and structure of the catalysts were investigated. Figure 10 and Figure 11 display EDX results and SEM images of the Zn-Ni with various compositions after the 48 h for the CO2RR by cyclic voltammetry with scan rate 0.05 V. s−1, graphite counter electrode, 0.1 M KCl cathodic, and 0.1 M H2SO4 anodic solutions. According to EDX analysis, as shown in Figure 10, carbon with ~28–30 wt.% was deposited on the Zn85%-Ni15% electrocatalyst after 48 h of testing. The microstructure of Zn0.85 - Ni0.15 is a block-like morphology in which carbon is almost uniformly distributed in the substrate due to CO2 reduction. As can be seen in Figure 11(a), some electrocatalytic regions are carbon-covered, preventing CO2 reduction over time. Therefore, for further consideration of this electrocatalyst, gas chromatography of produced gases (the produced gases were collected with the gas bag) has been investigated.

Figure 10.

EDX results of C content (wt.%) in terms of Zn-Ni compositions after 48 h of electrochemical CO2RR.

Figure 11.

SEM images of Zn-Ni electrocatalysts after 48 h of CO2RR on (a) Zn85%- Ni15%, (b) Zn65%-Ni35%, (c) Zn35%-Ni65%, and (d) Zn20%-Ni80% electrocatalysts.

According to EDX analysis, as shown in Figure 10, carbon with ~10 wt.% was deposited on the Zn65%-Ni35% electrocatalysts after 48 h of testing. As shown in Figure 11(b), the microstructure of the Zn65%-Ni35% electrocatalyst is a cluster-like morphology where coke formation is minimized by the reaction of CO2 with this microstructure after 48 h. With comparing Znx-Ni1-x electrocatalysts, with decreasing Zn amount in Znx-Ni1-x coatings from 85 wt.% to 65 wt.% of Zn, coke formation upon Zn-Ni electrocatalysts decreases. Furthermore, the electrocatalyst microstructures have changed from block-like to cluster-like with decreasing Zn content from 85 wt.% to 65 wt.%. Therefore, the activity and efficiency of electrocatalysts increase with decreasing Zn content from 85 wt.% to 65 wt.% in Zn-Ni electrocatalysts. By further reducing the amount of Zn until ~33 wt.%, coke formation upon Zn-Ni electrocatalyst increases.

Furthermore, as seen in Figure 11c, the microstructure of the Zn35%-Ni65% electrocatalyst is semi-spherical, where carbon was deposited between the semi-spherical grains with needle-like microstructure. This high coke formation is due to changes in the microstructure and electrocatalytic activity due to the interaction between Zn and Ni with the ions present in the solution. By further reducing the amount of Zn up to 20 wt.% in the Zn-Ni coating, the coke formation (after 48 h of CO2RR) on the electrocatalyst decreased. The microstructure of 20%Zn-80%Ni is a glossy spherical morphology where carbon is grown with a dark semi-spherical morphology about 22 wt.%.

Due to the results of gas chromatography, as shown in Figure 12, the Zn85%- Ni15%, Zn65%-Ni35%, Zn35%-Ni65%, and Zn20%-Ni80% electrocatalysts have 63%, 55%, 25%, and 30% selectivity for CO and 37%, 45%, 75%, and 70% selectivity for H2 products, respectively. Also, according to Table 2, the total efficiency for CO2RR after 48 h of testing is 53%, 66%, 31%, and 57%, respectively. The Zn65%-Ni35% electrocatalyst is appropriate in terms of morphology, stability, coke formation, product selectivity, and intensity of the electrochemical CO2RR. The coke formation on the catalysts can influence the activity spots of the catalyst and have a negative impact on the efficiency and life cycle of the catalyst. Consequently, the chemical compositions, microstructure, and morphology of catalysts have a crucial role for the CO2RR to produce gases with satisfactory ratio, desired product, least-coke formation, and suitable efficiency, activity, and stability.

Figure 12.

Gas chromatography results for CO2RR by various electrocatalysts in terms of CO and H2 gas selectivity by cyclic voltammetry method.

Coating compositionCoating performance
Zn content (%)Ni content (%)CR (mm/yr)MorphologyCO (%)H2 (%)C (%)Efficiency after 48 h (%)
Coatingcarbon
Znx-Ni1-x85150.11Block-whiteBlock-black63373053.33
65350.15Cluster-likeLow amount55451066.00
35650.17Semi-sphericalNeedle- like25756531.88
20800.25White Sphericalblack Spherical30702257.27

Table 2.

Zn-Ni Electrocatalysts performance with different compositions and electrodeposition parameters for CO2RR.

4. Conclusions

The lower corrosion rate of coatings deposited at 25°C is mainly related to the role of nickel in zinc-nickel alloy and a higher corrosion rate at higher temperatures of 40°C, 60°C, and 70°C are related to the lower barrier properties such as uniformity, compactness and cracks in the alloy. Zinc-nickel alloy coatings with the highest corrosion resistance, within required composition of 12–15%, dense and compact morphology, better uniformity with less crack is achieved with coatings deposited at 25°C. CO2RR on Znx-Ni1-x electrocatalysts in 0.1 M KCl as the cathodic solution and 0.1 M H2SO4 as the anodic solution using cyclic voltammetry method demonstrated that the Zn65%-Ni35% electrode had the best performance for the CO2RR with regarding the minimum coke formation (<10%) and optimal faradaic efficiencies of CO and H2 (FECO = 55% and FEH2 = 45%). The coke formation on the catalysts can influence the activity spots of the catalyst and have a negative impact on the efficiency and life cycle of the catalyst. Consequently, the chemical compositions, microstructure, and morphology of catalysts have a crucial role for the CO2RR to produce gases with satisfactory ratio, desired product, least-coke formation, and suitable efficiency, activity, and stability. Therefore, the Zn65%-Ni35% electrocatalyst with cluster microstructure had the best performance for CO2RR among other electrocatalysts in this study.

Download for free

chapter PDF

© 2021 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Mohammadali Beheshti, Saeid Kakooei, Mokhtar Che Ismail and Shohreh Shahrestani (January 11th 2021). Investigation of Zn/Ni-Based Electrocatalysts for Electrochemical Conversion of CO<sub>2</sub> to SYNGAS [Online First], IntechOpen, DOI: 10.5772/intechopen.95626. Available from:

chapter statistics

41total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us