Open access peer-reviewed chapter - ONLINE FIRST

Effect of Transition Metal on Structural and Dielectric Properties of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) System

By Pallavi Saxena and Anand Yadav

Submitted: September 18th 2020Reviewed: February 19th 2021Published: April 4th 2021

DOI: 10.5772/intechopen.96729

Downloaded: 20

Abstract

This study explored the structural and dielectric features of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) that were synthesized by the Solid-state reaction (SSR) method. The X-ray powder diffraction (XRD) analysis reveals that the prepared samples are single-phase cubic structure without any impurity. Rietveld-refined X-ray diffraction results reveal the formation of cubic structure and all the peaks of Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4 are perfectly indexed in the cubic (Fd-3 m) structure. Dielectric constant and dielectric loss variation with frequency were also explored. Both decrease when the relevant alternating field is increasing and become constant at high frequencies which reflects the important role of interfacial polarization. Furthermore, the Mg0.5Cu0.5Fe2O4 having the smallest crystallite size (~ 44.73 nm) has a high dielectric constant (~ 4.41 × 104) value as compare to Mg0.5Zn0.5Fe2O4.

Keywords

  • solid-state synthesis
  • ferrite
  • crystallite size
  • X-ray diffraction
  • dielectric properties

1. Introduction

Ferrites are insulating magnetic oxides with high electrical resistance, low dielectric losses, high permeability, and high saturation magnetization. These magnetic materials are special and can be used in several device applications. Transition metal ion-doped spinel ferrites are fascinating due to high dielectric constant and low dielectric losses [1, 2]. Soft ferrite materials such as Mg-Zn ferrites have vast technological importance due to their relatively high Curie temperature, low cost, and eco-friendly stable nature. The transport properties of soft ferrites are mainly controlled by divalent impurities. Further, soft ferrites are used in advanced technologies such as magnetic resonance imaging (MRI), magnetic drug delivery, microwave absorbers, catalysis, detoxification of biological fluids, transformer cores, magnetically controlled transport of anti-cancer drugs, sensors [2].

Spinel ferrites with formula AB2O4 (A = Mg, Zn, Cu) have a cubic structure with an Fd3mspace group. However, MgFe2O4 is having an inverse spinel structure with zero magnetic moments. This inversion is usually affected by the temperature given during calcination, while ZnFe2O4 often has a normal spinel structure without magnetic moment. Due to low Neel temperature both the ferrites show antiferromagnetic characteristics. It shows paramagnetic behavior due to weak superexchange interaction at room temperature [3, 4]. The polycrystalline Mg-Zn inverse spinel ferrites are commonly represented by (ZnxMgyFe1-x-y)[Mg1-x-yFe1+x+y]O4, where Zn2+ ions are bound to the tetrahedral sites (interstitial) and Mg2+ ion occupy the B sites [octahedral]ions have an affinity towards the interstitial (tetrahedral) site and Mg2+ ions occupy octahedral sites. However, Fe3+ ions occupied at both the tetrahedral and octahedral sites [5]. The effect of Cu ion doping on Mg-Zn ferrites should be investigated as the copper ferrites possess a tetragonal structure and Mg-Zn ferrites retain the spinel structure [6].

The materials having high dielectric constant and low dielectric losses are useful in microwave devices that make transition metal and rare earth doped Mg-Zn ferrite an attractive candidate. The dielectric properties are largely influenced by the method of synthesis, chemical structure, doping concentration, grain structure, calcination temperature, and the size of the dopant [7]. The previous studies have provided important findings on the frequency-dependent dielectric properties as the value of dielectric constant for MgFe2O4 is 57.93 at 10 Hz [8], for ZnFe2O4 is 2641 at 1 kHz [9], for Mg0.75Zn0.25Fe2O4 is 740 at 100 Hz and for Mg0.5Zn0.5Fe2O4 is near to ~50 at 100 Hz [4] whereas the dielectric constant of all these materials decreases with an increase in the frequency.

We have to use the solid-state reaction method to synthesize the Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites. The key benefits of solid state reaction synthesis over other methods are that it is simple, cheaper, and convenient. It also requires less solvent, reduces contamination, and gives high yields of products. The present chapter mainly focuses on the crystal as well as the dielectric response of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrite. The techniques used for the characterization of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) are X-ray diffraction (XRD) and dielectric measurements.

Advertisement

2. Experimental details

The Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) samples were synthesized using a Solid-state reaction technique. All chemicals used here were of analytical grade without any further purification. Precursors such as zinc oxide (ZnO), magnesium oxide (MgO), ferric oxide (Fe2O3), and CuO (copper oxide) with 99.9% purity were combined in stoichiometric amounts and thoroughly mixed using a mortar pestle. The resulting powder was calcined in a muffle furnace open to the air at 1000 °C for 12 hours creating a solid sample that was again ground with mortar and pestle into a fine powder. The sample was reground and calcined again for 12 h at 1050 °C to increase the homogeneity of the prepared samples. Each heat treatment included a heating and cooling rate of 10 °C/min and with intermediate grindings. Further, an organic binder called polyvinyl acetate (PVA) is added to the powder sample to binds the particles. The obtained powder samples were compressed in the circular shape of 1 mm thick and 10 mm diameter pellets using a hydraulic press following the application of 8 tons of pressure. At last, the pellets were fully sintered at 1200 °C for 12 h, then steadily cooled to room temperature.

The X-ray diffraction patterns of the Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) were recorded at ambient conditions using a Bruker D8 advanced diffractometer with a copper anode (1.5460 Å) in Bragg–Brentano geometry. This equipment possesses a LynxEye detector based on the silicon drift detector technique. The X-ray diffraction patterns were obtained in the 2θ angle range from 20 to 80°, using a step size of 0.02°. The powder-diffraction data was processed by Rietveld refinements using the FullPROF program [10]. The dielectric properties of these samples have been tested in the impedance analyzer with the model-Novo control tech Germany alpha ATB, which is usable within the frequency range of 3 μHz-20 MHz and the acvoltage range from 100 mV to 3 V. The high temperature silver paste was used on their two major surfaces for dielectric measurements.

3. Results and discussion

3.1 Structural analysis

A powder X-ray diffraction (XRD) analysis was used to determine the crystallinity and purity of prepared samples. The room temperature XRD pattern with indexed hkl for the prepared samples of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu, and henceforth designated as Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4, respectively) samples are depicted in Figure 1. The XRD pattern of Mg0.5Zn0.5Fe2O4 indicates the presence of a single-phase, whereas the Mg0.5Cu0.5Fe2O4 sample shows minor impurity peaks which is due to the presence of minor secondary phase corresponds to unreacted monoclinic CuO phase (space group C2/c).

Figure 1.

XRD patterns of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites.

The observed diffracted peaks support the formation of a cubic spinel-type structure with the space group Fd-mand all the diffracted peaks are compared with the Joint Committee on Powder Diffraction Standards (JCPDS) data and match well with the Card No. 86–2267 [5]. The magnified view of the most pronounced peak (311) of Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4 samples are shown in the inset of Figure 1. We observe that there is a slight shift occurring for each intensity peak as compared to Mg0.5Zn0.5Fe2O4 towards the higher angle side. This shifting is taking place due to the minor difference in the ionic radii of Cu2+ (0.72 Å) and Zn2+ (0.74 Å) ions.

The observed diffracted peaks support the formation of a cubic spinel-type structure with the space group Fd-mand all the diffracted peaks are compared with the Joint Committee on Powder Diffraction Standards (JCPDS) data and match well with the Card No. 86–2267 [5]. The magnified view of the most pronounced peak (311) of Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4 samples are shown in the inset of Figure 1. We observe that there is a slight shift occurring for each intensity peak as compared to Mg0.5Zn0.5Fe2O4 towards the higher angle side. This shifting is taking place due to the minor difference in the ionic radii of Cu2+ (0.72 Å) and Zn2+ (0.74 Å) ions.

The Debye Scherrer’s (DS) and the Williamson – Hall (WH) techniques were used to calculate the crystallite size (t). In the DS method, the average crystallite size was estimated using the Scherrer’s Equation [4] t = 0.9λ/βcosθ, where βis full width at half maximum (FWHM), λis the wavelength of X-ray employed, and θis the diffraction angle. For Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4, the measured values for crystallite sizes using DS are ~30.12 and 25.59 nm respectively. In the WH method, a plot of βcosθ against 4 sinθ is plotted as shown in Figure 2. The slope thus represents strain and the y-intersect of the fitted line represents crystallite size.

Figure 2.

Williamson–Hall (WH) plot of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites.

The average crystallite size calculated by the WH method ranges from ~58.26 to 44.73 nm, which is dependent on the broadening of peaks with doping concentration [11]. The calculated value of crystallite size, dislocation densities, and microstrain for Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4 samples, are tabulated in Table 1. Furthermore, the dislocation density (δ) gives further insight into the number of crystal defects. It is seen that the value of dislocation density decreases for Mg0.5Cu0.5Fe2O4 which implies the reduction in the defects and dislocation. It should be noticed that the microstrain of Mg0.5Cu0.5Fe2O4 is significantly smaller than the microstrain of Mg0.5Zn0.5Fe2O4 and it is consistent with the larger average crystal size of Mg0.5Zn0.5Fe2O4 (as evident in Table 1).

SamplesAverage crystallite size using SM (in nm)Average crystallite size using WHM (in nm)Micro strain
ε × 10−3
(lines/m4)
Dislocation density δ × 1014 (lines/m2)
Mg0.5Zn0.5Fe2O430.1258.263.162.95
Mg0.5Cu0.5Fe2O425.5944.733.084.98

Table 1.

Average crystallite size using SM and WHM, micro strain (ε) and dislocation density (δ) derived from X-ray diffraction data.

Rietveld refinements of XRD (FullPROF software) results are shown in Figure 3, which confirm that Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4 compounds crystallize with an Fd-mspace group in a cubic form [12]. The pseudo-voigt analytical function is used to fit the experimental result of XRD. The structural cell parameters and refinement factors are listed in Table 2. The strongest reflection in both the samples comes from the (311) plane that indicates both the samples have the spinel phase. Fundamental reflections from the crystal planes (220), (311), (222), (400), (422), (511), (440), and (533), characterizing the spinel ferrites are identified.

Figure 3.

Rietveld refinement fitting results of the X-ray powder diffraction patterns of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites.

ParametersSamples
Mg0.5Zn0.5Fe2O4Mg0.5Cu0.5Fe2O4
2θ range (deg.)20° - 80°20° - 80°
Step size (deg.)0.02°0.02°
Wavelength1.5406 Å1.5406 Å
Space groupFd-mFd-m
a(Å)8.39328.3679
Rwp12.914.5
χ21.821.65

Table 2.

Details of Rietveld refined XRD parameters for Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu).

It is observed that the lattice parameters slightly decreases for Mg0.5Cu0.5Fe2O4. The refined values of lattice parameters are a = 8.3932 Å for Mg0.5Zn0.5Fe2O4 and a = 8.3679 Å for Mg0.5Cu0.5Fe2O4. These parameters are consistent with the previously reported results [13]. The slight variation in the lattice parameters may be related to the anion–cation distance for the interstitial A- and B-site in the spinel structure, which could be correlated with the fraction of Mg2+, Fe3+, and Zn3+ ions among these sites directly. The decrease in lattice constant with an increase in the copper concentration may be attributed to the smaller ionic radius of Cu2+ (0.72 Å) compared with that of Zn2+ (0.74 Å) ion [14]. Indeed, a variation of lattice parameters involves a variation in 2θ, we can say that this shift of the peaks influences the lattice parameters of the structure.

3.2 Dielectric studies

The value of the dielectric constant (ε′) is calculated using ε′ = Cp d0A, where, Cpis the measured value of the capacitance, dis the thickness of the pellet, ε0 is the permittivity of free space and Ais the area of cross-section of the pellet. Figure 4 indicates the variation in the dielectric constant as a function of the frequency at room temperature between 1 kHz and 10 MHz. It is observed that for both samples the dielectric constant decreases with an increase in frequency and becomes constant at a higher frequency. The reduction in the dielectric constant values can be caused by electron exchange interaction between Fe2+ and Fe3+ ions, which does not obey the alternating electric field. The decrease of dielectric constant with the increase of frequency is observed in the case of Mg-Zn ferrite. Similar behavior was also observed in other ferrite systems [4, 15]. The reduction in the dielectric constant with an increased frequency is a normal dielectric behavior of spinel ferrites and can be described by the dipole relaxation phenomenon. Dipole relaxation refers to the relaxation response of a dielectric medium to an external electric field. In general, relaxation is a delay in the response of a system. It is well known that in the heterogeneous structure the samples consist of well-conducting grains separated by poorly conducting grain boundaries [16]. If the resistance of the grain boundary is high enough, the electrons are pile up at the grain boundary and produce polarization. However, the electrons reverse their direction of motion more frequently, as the frequency of the applied field is changes. This reduces the probability of electrons reaching the grain boundary and thereby decreases polarization. Thus, the dielectric constant decreases with the increasing frequency of the applied field [17].

Figure 4.

Frequency dependent dielectric constant (ε') of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites.

Also from Figure 4, it is quite clear that the value of the dielectric constant is higher for Mg0.5Cu0.5Fe2O4 and is found to be ~44140, which is much higher as compared to ~281 obtained for the Mg0.5Zn0.5Fe2O4. This increase in the dielectric constant ε′ can be explained based on the mechanism of the polarization process. The origin of polarization is due to the influence of the size mismatch of the cations. The coexistence of multiple phases requires that the strain energies of the domains at the boundaries should be comparable. Since the different domains have different electronic properties, they can give rise to large dielectric constants. The whole polarization in ferrites is primarily due to the space charge polarization, the conductivity in materials, and the hopping exchange of the charges between two localized states. Thus the dielectric constant decreases with an increase in frequency for both samples. It is worth mentioning here that the dielectric constant increases with an increase in Cu concentration [18].

In Figure 5, the variation of dielectric loss (tan δ) as a function of the logarithm of frequency is depicted. It can be seen in the figure that the dielectric loss of the Mg0.5Zn0.5Fe2O4 compound is very high and is found to decrease with 50% Cu doping concentration. Besides, the decline in tan δwith the increase in frequency is following Koop’s phenomenological model [19]. The dielectric loss arises when the polarization lags behind the applied alternating field and is caused by the presence of impurities and structural inhomogeneity. The value of dielectric loss tangent is very low in the higher frequency region. The frequency-dependent acconductivity (σac) variation of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) samples are shown in the inset of Figure 5. In this study, acconductivity is found to increase as the frequency of applied acfield increases for both the samples, because the increase in the frequency of acapplied field enhances the hopping of charge carriers. It is also evident from Figure 5 that acconductivity is initially low for Mg0.5Zn0.5Fe2O4 and found to enhance with doping of Cu ion Mg0.5Cu0.5Fe2O4 at high frequency. The improvement is due to both short-range hopping motion and long-range displacement of oxygen vacancies involved in the conduction mechanism. The replacement of Zn ion with Cu ion results in the generation of more oxygen vacancies and leading to an increase in the long-range conduction path to the charged defect, which in turn increases the conductivity of Mg0.5Cu0.5Fe2O4 [20].

Figure 5.

Frequency dependent dielectric loss (tan δ) and ac conductivity (σac) of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites.

The electrical modulus analysis is very useful to detect electrode polarization, grain boundary conduction effect, electrical conductivity, and bulk properties. This technique also provides an insight into the electrical processes occurring in the materials. The modulus plots of M′ versus M″ for Mg0.5Zn0.5Fe2O4 and Mg0.5Cu0.5Fe2O4 are shown in Figure 6. The deformed semi-circles are formed in both samples. The M′–M″ plot of Mg0.5Zn0.5Fe2O4 shows two regions, the large semicircle was believed to be induced by the grain effect, due to the smaller capacitance value dominated in the electric modulus spectra. The presence of single semicircular arcs suggests the presence of only grain contributions in these types of materials. The Mg0.5Cu0.5Fe2O4 samples do not show any semi-circle type behavior, which suggests that only grain capacitance is dominant and the grain boundary modulus is beyond the measurement scale. It is based on the fact modulus plot highlights the phenomenon with small values of capacitance. It is difficult to obtain two full semicircles grain boundaries on the same scale in the impedance plot because of the huge difference in capacitive values of grain boundaries. Complex modulus analysis is useful when materials have different capacitance [21]. It is confirmed in our M″ versus frequency plot where the grain boundaries are negligible. Even if present, their contribution to the overall capacitance of the material is very small, and does not affect the relaxation process much. The modulus spectrum shows a marked change in its shape/size with Cu ion doping [22].

Figure 6.

Variation of imaginary modulus (M″) as a function of real modulus (M′) of Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrites.

4. Conclusions

The polycrystalline Mg0.5Tm0.5Fe2O4 (Tm = Zn and Cu) ferrite samples were successfully prepared using the solid state reaction method. The Rietveld refinement study of XRD reveals that the samples crystallize in cubic spinel structure with the Fd-3 mspace group. The monoclinic crystal phase of the CuO (space group C2/c) compound is seen in Mg0.5Cu0.5Fe2O4 as a minor secondary phase. It is observed that for both ferrite samples the dielectric constant (ε’) and dielectric loss (tan δ) decreases with an increase of frequency and becomes constant at a higher frequency. The value of ε′ and σac are enhanced, whereas the value of tan δ decreases for Mg0.5Cu0.5Fe2O4. The M′–M″ plot of Mg0.5Zn0.5Fe2O4 shows two regions, referring to the grain as well as the grain boundary conducting process. There is no semi-circle type behavior in the Mg0.5Cu0.5Fe2O4 sample which means that only grain capacitance is dominant and the grain boundary modulus is beyond the measurement scale.

Acknowledgments

UGC-DAE-CSR, as an institute is acknowledged for extending its facilities for sample characterization. Dr. M. Gupta, Dr. D. M. Phase of UGC-DAE-CSR, Indore, India are gratefully acknowledged for measurements and fruitful discussions.

Advertisement

Conflict of interest

The authors declare no conflict of interest.

Download for free

chapter PDF

© 2021 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Pallavi Saxena and Anand Yadav (April 4th 2021). Effect of Transition Metal on Structural and Dielectric Properties of Mg<sub>0.5</sub>Tm<sub>0.5</sub>Fe<sub>2</sub>O<sub>4</sub> (Tm = Zn and Cu) System [Online First], IntechOpen, DOI: 10.5772/intechopen.96729. Available from:

chapter statistics

20total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us