Study on the Perspective of Mechanical Properties and Corrosion Behaviour of Stainless Steel, Plain and TMT Rebars

In the present research, the effects of various alloying elements and microstructural constituents on the mechanical properties and corrosion behaviour have been studied for four different rebars. The microstructures of stainless steel and plain rebar primarily reveal equiaxed ferrite grains and ferrite-pearlite microstructures, respectively, with no evidence of transition zone, whereas tempered martensite at the outer rim, followed by a narrow bainitic transition zone with an internal core of ferrite-pearlite, has been observed for the thermomechanically treated (TMT) rebars. The hardness profiles obtained from this study display maximum hardness at the periphery, which decreases gradually towards the centre, thereby providing the classical U-shaped hardness profile for TMT rebars. The tensile test results confirm that stainless steel rebar exhibits the highest combination of strength (≈755 MPa) and ductility (≈27%). It has been witnessed that in Tafel plots, the corrosion rate increases for all the experimental rebars in 1% HCl solution, which is well expected because the acid solutions generally possess a higher corrosive environment than seawater (3.5% NaCl) due to their acidic nature and lower pH values. However, all the experimental results obtained from Tafel and Nyquist plots correlate well for both 1% HCl and 3.5% NaCl solutions.


Introduction
For the past few years, an inspection of reinforced concrete structures with steel rebars has become a subject of research because concrete provides an alkaline environment that is suitable for the spontaneous passivation of steel rebars. These steel rebars act as a reinforcement when tensile loads are applied [1]. But, still, there is a possibility of corrosion in these steel rebars when aggressive chloride ions are present in the environment [1]. Corrosion in rebars may result in surrounding concrete cracking, reduction in the bond strength of the concrete and the rebars and lowering the combination of strength and ductility [1][2][3].
Extensive research has been carried out to date on corrosion in steel rebars but a modest solution can be the usage of stainless steels rebars as a partial or complete replacement of the reinforcements in concrete. This solution is economically viable because there may be a higher initial investment cost but this can be compensated by low-repairing cost, less maintenance effort and most importantly long-range services of the designed structures [4]. As per earlier studies, it is well established that austenitic stainless steels can be considered as the common choices for rebars, whereas there is a wide range of applications of the ferritic and the duplex stainless steels that include structural components in the construction industries [1,5]. However, it cannot be domineered that the austenitic stainless steels are expensive due to the higher content of elements such as Ni and Mo. It has been reported earlier that stainless steel eliminates chances of corrosion but does not rely on concrete when it is subjected to the ingress of chlorides from marine environments. For the last few years, plenty of research has been carried out in search of more economically friendly novel stainless steels as reinforcements [6][7][8][9][10][11][12]. It is also true that, since the cost of these steels can be compared with the cost of common black steel reinforcement rather than the cost of highly alloyed stainless steels, the use of low alloyed stainless steel reinforcement has been accepted as economically more convenient [6].
Thermo-mechanical treatment (TMT) has gained researchers' attention for producing high-strength steels with lean chemistry at a reduced cost with excellent mechanical properties [13][14][15][16]. In TMT, simultaneous application of heat and deformation causes microstructural refinements [16][17][18]. These materials are highly used in the construction sectors for the construction of dams, bridges, buildings, flyovers and also in various other structural materials [16,19]. The durability of these TMT rebars is an immense problem due to corrosion in reinforced concrete structures, which is needed to be minimized as much as possible to enhance the life of that structure. Substandard quality rebars can also cause damage to the towers, buildings and other constructions in the seismic zones. However, in reinforcement concrete, the presence of alkaline solution protects the TMT rebars from corrosion due to the formation of a passive layer over the steel surface [20][21][22]. However, encountering chloride solution in this structure causes the breakdown of this passive layer. In the coastal and marine areas, excessive level of chloride causes problems of chloride-induced corrosion, thereby creating problems in corrosion resistance of the TMT rebars in the concrete [23][24][25][26][27].
It is well established that corrosion of steel reinforcement bars primarily depends on the stability of different phases that are likely to form in the cement paste and the effectiveness of the oxide layer that forms on the steel bar surface, that is, the passive layer [28]. It has been reported earlier that the concrete pore solutions preserve a strongly alkaline medium due to the significant filling of calcium hydroxide in the concrete pores depending on the hydration reactions of cement. This alkaline environment is suitable for the formation of a stable passive film on the rebar surface and thereby provides significant protection to the steel rebar against corrosive environments [28]. However, chloride-induced corrosion has been reported as a primary source for the local breakdown of this passive film on the surface of the steel bars [28][29][30]. It is also known that the volume of rebar increases when the corroded product forms on the rebar surface and results in cracks in the concrete, thereby causing failure [27]. This paper primarily emphasizes the study of mechanical and corrosion behaviours of different types of rebars in two different aqueous solutions. It is expected that this study will provide valuable information regarding the improvement in the design parameters and also the life cycle cost calculation of various structures as well as towards the selection of the best-suited rebars for industrial and marine construction purposes.

Experimental procedure
Four different steel rebars such as Fe-600, galvanized steel, stainless steel and plain rebars were chosen for this study. The approximate diameters of these samples were 12 mm, 8 mm, 16 mm, and 11 mm, respectively. Notably, Fe-600 and galvanized rebars are thermomechanically treated, whereas the other two (stainless and plain) rebars were not subjected to thermomechanical treatment. The nominal chemical compositions (wt. %) of all the rebar samples are given in Table 1. First, the samples of suitable size were cut from these steel rebars as per the requirement of optical, hardness, tensile and corrosion tests. All the samples were then tested in an optical emission spectrometer (Thermo 3460) to analyse the chemical compositions of the rebars. Standard metallographic sample preparation techniques such as grinding (belt and paper) followed by polishing (coarse, fine and diamond) and etching by using 2% nital and Snyder solutions were used to observe the microstructural constituents under an optical microscope (Leica) and scanning electron microscope (SEM).
The etched samples were further used for the Vickers Micro-Hardness Testing (Leica-VMHT) under 300 gf load and 20 seconds dwell time to analyse micro-hardness profile throughout the cross sections with a particular interval of distance. Hardness was measured on the sample surface as a function of distance from the edge to edge, keeping an interval of 50 μm, and the recorded variation in hardness values was then plotted. It is important to mention here that the hardness profile instead of surface hardness was recorded because the hardness values were expected to decrease from the periphery to the centre. A universal testing machine (UTN-10) was utilized to conduct the tensile test with a crosshead speed of 4.5 mm/min and a gauge length of 65 mm.
The electrochemical measurements were performed using a working electrode (embedded rebar specimen); a counter electrode (graphite) was placed to one side of the rebar specimen and also an independent reference electrode; that is, saturated calomel electrode (SCE) was used to observe the corrosion behaviour. Precise electrode placement was not critical, since the conductivity of the electrolytes was high. The equipment used to observe the corrosion behaviour of the rebar samples was Origalys Potentiostat, combined with the Origamaster 5 module. Electrochemical impedance spectroscopy (EIS) was utilized in the frequency range of 100 kHz-100 MHz with an AC voltage of 5 mV. The characteristic capacitance of this frequency band was maintained in between 10 À9 and 10 À6 F/cm 2 [10]. The rebar samples of standard size (area) were prepared and then immersed in two different types of solution of 3.5% NaCl and 1% HCl. These particular concentrations were chosen to simulate the saline conditions possible in marine and acidic rain in industrial areas [31,32]. In this context, it is important to mention that the area was ≈76 mm 2 for Fe 600 rebar, whereas the same for the other three samples was kept at ≈75 mm 2 for the EIS study. Table 1 shows the compositional analysis of the different types of TMT rebars (IS 1786: 2008 for Fe 600 and IS 12594:1988 for galvanized). It has been already reported that an increase in yield strength of reinforcing bars occurs by raising carbon as well as manganese content or by microalloying. It is also true that higher carbon content may cause lower weldability and ductility [13,16,23]. It is worth mentioning here that all the steel rebar samples selected in the present investigation contain a lower amount of carbon since a higher amount of carbon can cause harmful carbide formation and pearlite formation in the as-rolled steels thereby causing micro-galvanic corrosion [23,33]. Major alloying elements other than carbon are manganese and silicon in the case of all the rebar samples. However, in the case of stainless steel rebar (IS 16651:2017), apart from these two elements, chromium and nickel are also present to enhance the 'stainless' property of this steel by forming a stable and protective oxide layer to make them corrosion-resistant [34][35][36]. In this context, it is imperative to mention here that the corrosion resistance of the stainless steel rebar depends on the formation of the chromium layer (≈5 nm thickness) and the content of chromium that keeps the rebar surface electrochemically passive in corrosive environments [37]. It is well known that manganese increases the hardenability and tensile strength of the steel [23,33]. The addition of silicon is beneficial to increase the hardness and strength. It also acts as a deoxidizer during the casting of the rebar, thereby helps in reducing the casting defects and allows sound steel castings [23,38].  (Figure 1(c)) and ferrite-pearlite type for plain rebar (Figure 1(d)) have been observed throughout the samples because these two rebars were processed through the conventional cold rolling process and not subjected to thermomechanical treatments (TMT). The presence of dark peripheral ring (edge/rim) consists of tempered martensite with an intermediate narrow transition zone of bainite with a comparably grey core with ferrite-pearlite microstructure as shown in Figures 1(a) and (b) [23,33,39,40]. It is imperative to mention here that in the TMT process, quenching of hot-rolled bars  with water jet leads to the formation of martensite at the outer surface of the rebars. The residual heat flow across their bar section during cooling results in the tempering of the initially formed martensite with finer grains, which is self-tempering in nature and also produces ferrite-pearlite with coarser grains or mixed microstructure in the core region [13,33,41,42]. A clear boundary separating the outer ring from the inner core is also visible in the case of TMT rebars (Figures 1(a) and (b)). This boundary can be considered as the demarcation line between the tempered martensite and ferrite-pearlite microstructures.  Figures 2(a) and 3(a), followed by a ferritepearlite mixed microstructure in the core as shown in Figures 2(b) and 3(b). In this context, it is noteworthy to mention here that the pearlite microstructure that is shown in Figure 2(d) reveals the presence of degenerated pearlite in the case of the Fe 600 rebar sample, which can be correlated with inadequate carbon diffusion during cooling. Detailed discussion on the formation of degenerated pearlite and bainite is available in the literature [23,33,[39][40][41][42][43][44]. Figure 3(d) primarily reveals pearlite microstructure at a higher magnification with greyish ferrite and whitish cementite flake-like structures, which is completely distinguishable for galvanized rebar samples. It cannot be overruled that as the carbon percentage is very low and chromium (ferrite stabilizer) percentage is high for the investigated stainless-steel rebar, hence the microstructure is ferritic. However, mixed ferrite-pearlite microstructures with no transition zone throughout the sample have been observed for plain rebar. The lamellar configuration of pearlite with some amount of resolved pearlite has been shown at a higher magnification at the inset of Figure 5(b). Figure 6 shows the hardness profiles of different types of steel rebar samples (along the cross-sectional diameter). It has been reported earlier that the hardness value of TMT rebar samples becomes maximum at the periphery due to the presence of tempered martensite, which gradually decreases towards the  centre due to the formation of ferrite-pearlite mixed microstructure thereby exhibiting the classical U-shaped profiles [13,23,45]. It has been observed that the hardness value of Fe 600 and galvanized rebar samples in the periphery or outer rim region is around ≈285 HV, which is an indication of the presence of the tempered martensite or bainite phase [23,45]. It has been also observed that the hardness value of the transition zone is ≈220 HV for both TMT rebar samples due to the presence of lower bainite, whereas for the core region or ferrite-pearlite region, the hardness value is ≈200 HV for Fe 600 rebar and ≈180 HV for galvanized rebar, respectively. Figures 7(a) and (b) displays the comparative hardness variations for stainless steel and plain rebar samples, respectively. It is evident from Figure 7 that the stainless steel rebar shows higher values of hardness (≈195 HV to 260 HV) than the plain rebar (≈145 HV to 205 HV). Previous studies have confirmed that the hardness value in steel samples predominantly depends on the carbon equivalent value (CEV) [23]. It has been also reported that the weldability primarily depends on CEV for carbon steel; that is, higher CEV leads to a hard and brittle heat-affected zone (HAZ). The microstructure in the HAZ zone has an important role in the mechanical properties of the weldment; therefore, CEV is an important parameter for rebars [46]. Table 2 summarizes the estimated carbon equivalent values of different rebar samples that were calculated by using Eq. (1). It can be seen in Table 2 that the plain rebar sample shows the lowest CEV (≈0.2163), thereby showing the lowest value of hardness among all the samples. It is imperative to mention here that although the stainless steel rebar consists of only equiaxed ferrite microstructure (Figure 4), due to high carbon equivalent value and the presence of other alloying elements such as Mn, Si, Ni (Table 1), and it shows a higher hardness value. It cannot be domineered that Fe 600 steel rebar has a higher value of CEV (≈0.3383) than that of galvanized rebar (≈0.3227), which results in a higher core hardness value (≈196 HV) (Figure 6) when compared with that of galvanized rebar sample (≈184 HV). The aforesaid two TMT rebars with CEV < 0.42 according to IS 1786:2008 standard will exhibit superior weldability. However, the   stainless steel rebar (ferritic grade) shows higher CEV (≈2.7323) because of higher Cr content but it can be welded in accordance with IS 16651:2017.

Hardness profile analysis
(Where all the elemental values are expressed in wt.%) Table 3 summarizes the values of yield strength (YS), ultimate tensile strength (UTS), UTS/YS ratio and ductility in terms of elongation percentage (% EL) of different rebars. From Table 3, it is evident that the highest combination of strength and ductility has been achieved for stainless steel, followed by Fe 600 rebar among all the experimental rebars. It is a well-established fact that a higher CEV leads to higher UTS variations ( Table 2 vis à vis Table 3) [23]. Table 4 shows the estimated ring diameter and area of tempered martensite in TMT rebars. It is noteworthy to mention that a greater amount of tempered martensitic ring area leads to higher strength ( Table 3 vis à vis Table 4) in the case of Fe 600 rebar. The estimated ring area of tempered martensite (≈39.56%) in Fe 600 rebar results in higher strength and lower ductility compared with the galvanized rebars with ≈20.10% ring area. It has been also noticed from Table 4 that the area percentage of tempered martensite ring increases with the increasing diameter of the tempered martensitic rim. Plain rebar shows the maximum ductility due to the lower carbon content, whereas stainless steel with the lowest carbon and higher Cr contents having a completely ferritic microstructure and ferrite being a soft phase exhibits somewhat lower ductility than plain rebar. From earlier research, it has been observed that in seismic zones according to the ASTM A706:2006, UTS/YS ratio should be kept ≈1.25 [23,33]. Previous studies have confirmed that rebars with UTS/YS ratio ≈1.19-1.24 provide greater advantages to their fatigue life [23,47]. Therefore, it is clear from Table 3 that stainless steel rebar with UTS/YS value ≈1.20 can become a potential candidate for the seismic hazard zone, whereas the other experimental rebars with lower values of UTS/YS ratio are expected to show better load resistance capacity in the seismic zone [23,48].

Rebar specimen YS (MPa) UTS (MPa) (UTS/YS) Elongation (%)
Fe  Figures 8 and 9 display the Tafel plots of different rebars in acid (1% HCl) and seawater (3.5% NaCl) solutions. It can be seen from Figures 8(a) and (b) that in 1% HCl solution, stainless steel rebar undergoes passivation, while other rebars show a constant enhancement of anodic current density with increasing applied potential. Generally, the state of corrosion in rebars can be classified as passive, active or indeterminate (trans passive region), depending on the potential difference between the steel and reference electrode. Figure 8(b) shows that the polarization process is divided into the different zones for stainless steel at 1% HCl: (i) Cathodic region: From the corrosion potential of À0.969 V to À0.519 V, current density gradually decreases in the process. (ii) Activation region: Between À0.519 V and À0.275 V, the current density gradually increases in this region as rate of metal dissolution is higher than the rate of metal oxide formation and thereby accelerates the corrosion. (iii) Active passive region: From À0.275 V to À0.176 V, the current density starts decreasing here as the rate of metal oxide formation becomes greater than the rate of metal dissolution and metal slowly starts moving towards the passive region. (iv) Passive region: From À0.176 V to À0.058 V, metal undergoes complete passivation due to formation of chromium oxide layers and the corrosion current density becomes constant and corrosion resistance behaviour increases. (v) Trans-passive region: Above À0.058 V to 1.021 V, the passivation film is punctured due to various anodic processes, such as evolution of oxygen from water and/or the chromium oxide dissolution through Cr 3+ to the Cr 6+ when metal suffers high anodic polarizations; thereby, the current density increases in this region and corrosion resistance again starts decreasing. It is evident from Figure 8(b) that the value of current density is decreasing from point a to b, indicating greater ease of passivation by forming a stable passive film, which is similar to earlier observations [49][50][51]. In this connection, it is pertinent to mention here that Cr plays a major role during the transition to passive states. It has been reported earlier that increasing the Cr percentage can significantly decrease the corrosion current density values [49]. However, the analysis of the corrosion performance of different stainless steel rebars in strongly acidic environments for long-time exposure is not only limited to the effect of the elements that increase their nobility like Ni but also the effect of elements that promotes their passivation, like Cr [49]. Earlier studies have shown that the addition of both chromium and nickel to iron remarkably increases the ease of passivation [49]. It is noteworthy to mention here that when the corrosion medium changes from 1% HCl to 3.5% NaCl (Figure 8 vis à vis Figure 9), the anodic current density decreases as depicted by a shift of the curve along the X-axis (current density) from a value of À3 A/cm 2 to values of ((À4) to (À5)) A/cm 2 due to neutral nature of 3.5% NaCl solution and thereby showing enhanced corrosion resistance of the different types of rebars in 3.5% NaCl solution. It is evident from Figure 9, that the current density of Fe 600 rebar is more than the plain rebar; that is, the corrosion rate of Fe 600 rebar is greater than plain rebar. Therefore, it can be assumed from Figures 8 and 9 that although the corrosion resistance of Fe 600 rebar is higher than plain rebar in the acid medium and it is reversed in the case of seawater. It has been also observed that the corrosion resistance of plain rebar is more than galvanized rebar because the zinc coating at the surface of galvanized rebar gets damaged due to penetration of chloride ions. In this context, it cannot be overruled that the galvanized rebar undergone through thermomechanical treatments leads to the formation of a finer rim of tempered martensite, which increases the grain boundary area, thereby leading to a higher solution attack at the grain boundary and reducing the corrosion resistance of galvanized rebars.

Polarization curves
The corresponding polarization parameters determined by extrapolation methods from the polarization curves (Figures 8 and 9) are summarized in Tables 5 and 6. From Table 5, it can be seen that the corrosion potential values were more positive for Fe 600, followed by plain and stainless steel rebars in 1% HCl solution, whereas in the case of 3.5% NaCl solution, more positive corrosion potential values have been observed for stainless steel followed by plain and Fe 600 rebars as evident in Table 6. It is well established that the higher values of corrosion potentials lead to enhancement in the corrosion resistance properties [50,52]. From Tables 5 and 6, it is noticeable that the values of i corr were minimum for Fe 600 followed by plain, stainless steel and Galvanized rebars in both 1% NaCl and 3.5% HCl solutions. It is well known that higher i corr values represent the higher corrosion resistance behaviour of metal. Tables 5 and 6 also summarize the estimated values of corrosion rates that were calculated by using Eq. (2) for all the experimental rebars in both 1% HCl and 3.5% NaCl solutions. It has been observed that the corrosion rate of all the experimental rebars is almost the same and very small in 3.5% NaCl as compared with 1% HCl solution. However, when the solution is 1% HCl, mm/y values obtained from Table 5 show an increase for all the experimental rebar samples, which is well expected because the acid solutions generally possess a higher corrosive environment due to their acidic nature and pH lowering properties along with the presence of water and air, which is not seen in case of 3.5% NaCl solution due to its neutral nature [34,53]. It is well known that a lower value of corrosion rate depicts higher corrosion resistance behaviour of the samples. According to Faraday's law, the corrosion rate can be calculated by using the corrosion current density as follows [49,52].
where i corr is the corrosion current density in (A/cm 2 ), M is the molar mass of steel in (g/mol), F is the Faraday's constant (96,500 C/mol), z is the number of electrons transferred for each metal atom and ρ is the metal density (g/cm 3 ).where β a = Anodic Tafel slope (mV/dec) and β c = Cathodic Tafel slope (mV/dec).
Therefore, it is evident from these experimental results that the estimated values of corrosion rate were the lowest for Fe 600 followed by plain, stainless steel and galvanized rebars in acid solutions, but in the case of 3.5% NaCl solution, these values were significantly reduced for all the rebars, which is an indication of better corrosion resistance properties under marine environment. Figures 10 and 11 show the open-loop potential stabilities in the Nyquist plots of the experimental rebars in 1% HCl and 3.5% NaCl solutions, respectively. To compare with the results obtained from the polarization test (Figures 8 and 9) and also to get a better correlation, EIS studies were further performed. It is evident from  semi-circular loop in the electrochemical impedance spectra, thereby indicating a capacitive semicircle in the high-medium frequency range. The occurrence of two semicircles in the electrochemical impedance spectra for stainless steel in 1% HCl is due to passivation of the rebar surface, thereby indicating a capacitive semicircle and an inductive loop in the high-medium and low-frequency ranges, respectively [52]. The capacitive semicircle represents the active state of the interface between the rebar and acid solution when the carbon steel is exposed to the corrosive solutions [52,54]. It is well known that stainless steel will form a trans-passive zone after the damage of the passive layer, which is also evident in Figure 8(b). This is due to the evolution of oxygen from water and/or the chromium oxide dissolution through Cr 3+ to the Cr 6+ when metal suffers high anodic polarization [49][50][51]. For this reason, in the Nyquist plot two loops are visible (one is bigger and the other one is smaller). However, it cannot be overruled that the open-loop diameters in Figure 11 were maximum for the plain rebar sample, followed by Fe 600 rebar, stainless steel, and galvanized rebar. In this connection, it is noteworthy to mention here that the capacitive arcs overlap in the Nyquist plots (Figures 10 and 11) since concrete is a heterogeneous material and many intermixed interfacial regions influence the impedance spectra. It has been already reported that these imperfect interfaces and electrode surface roughness require a constant phase element (CPE) instead of a pure capacitor to accurately model an equivalent circuit [55].

Electrochemical impedance spectroscopy (EIS)
Tables 7 and 8 summarize the values of the resistance of the electrolyte solution (R s ), the resistance of reinforced concrete (R f ) and CPE for all the rebars. It is well established that polarization resistance (R p = R f + R ct ) is an indicator to study the corrosion resistance behaviour of carbon steel in corrosive environments [52]. It cannot be overruled that except for stainless steel all the plots in Figures 10 and 11 exhibit only single-loop curves for all the other rebars, which generally do not involve the charge transfer resistance (R ct ). Thus, the higher values of R f reveal a higher value of corrosion resistance for the sample [52,56]. Furthermore, the arc diameter in the Nyquist diagrams can be considered as R f and the reduction of the arc diameter reveals a decrease in R f values [52]. It is evident from Table 7 that the R f values were maximum for Fe 600, followed by plain, stainless steel, and then galvanized rebars in 1% HCl solution, whereas in 3.5% NaCl solution ( Table 8), it is showing maximum values for plain rebar followed by Fe 600 and stainless steel rebars with a slight variation (≈0.07) and then galvanized rebar, which is also in agreement with Figures 10 and 11. Therefore, all the experimental evidence obtained from the polarization and EIS studies under acidic and seawater solutions are in good agreement and the corrosion resistance of all the experimental rebars is higher in 3.5% NaCl than 1% HCl solutions.

Conclusions
The important conclusions drawn from this study are as follows: 1. Microstructures of all the TMT rebars consist of an outer martensitic rim with an intermediate narrow bainitic transition zone followed by a ferrite-pearlite inner core, whereas stainless steel and plain rebars show equiaxed ferrite grain and ferrite-pearlite microstructure throughout the sample with no transition zone between core and rim due to the absence of TMT.
2. Fe 600 and galvanized rebars exhibit classical U-shaped hardness profiles, whereas stainless steel and plain rebars reveal a different variation at the edges when compared with other rebars and the absence of the classical U-shaped hardness profiles.
3. Stainless steel rebar shows the highest combination of strength (≈755 MPa) and ductility (27%) among all the rebars followed by Fe 600 rebar (≈660 MPa) in terms of strength. Plain rebar although showing lower values of strength (≈470 MPa) shows the maximum amount of ductility (≈29%). Therefore, it is expected that all the experimental rebars will show improved performance in the seismic zones. 4. In the Tafel plot and Nyquist plot, stainless steel shows a different property in 1% HCl solution than the others. This is due to the formation of the transpassive zone via the evolution of oxygen from water and/or the chromium oxide dissolution through Cr 3+ to the Cr 6+ when metal suffers high anodic polarization.
5. In the Nyquist plot, a higher R p value indicates higher corrosion resistance. Also, the larger the radius of the capacitive loop, the greater will be the charge transfer resistance, that is, corrosion resistance. It is also true that greater current density (i corr ) signifies a higher corrosion rate in the Tafel plot. Therefore, it can be concluded that in both Tafel and Nyquist studies, Fe 600 rebar has revealed maximum corrosion resistance followed by plain, stainless steel and galvanized rebars in 1% HCl solution, whereas in 3.5% NaCl solution, plain rebar has shown maximum corrosion resistance and then followed by Fe 600 and stainless steel rebars with a minor variation and then galvanized rebar.