Effect of Combination of Natural Dyes and the Blocking Layer on the Performance of DSSC

Over the years, researchers have been working on replacing sensitized dye for dye sensitized solar cells (DSSC), because of its low production cost, biodegradability, and non-toxicity. However, the overall performance of natural dye-based DSSCs is low compared to the DSSCs sensitized with Ruthenium based dyes. The combination of natural dyes with an optimized choice of the extracting solvents and the proper volume ratio of mixture of the dyes, enhances inherent properties, such as absorption and adsorption of the dyes. It also allows the device to utilize photon energy more efficiently over the entire visible wavelength. As a result, DSSC sensitized with the dye mixture shows higher absorbance, and cumulative absorption properties over the whole visible region than the DSSC fabricated with individual dyes and showed higher photocurrent. Another effective way to improve cell efficiency is by using a blocking layer. The blocking layer increases the photocurrent, is mainly due to the improvement of the electron recombination at the transparent conducting oxide/electrolyte interfaces. Also, the blocking layer’s compact structure creates an effective pathway for electron transportation; thus, the device’s photocurrent increases. Additionally, a slight improvement in the open-circuit voltage and fill factor was observed, thus cell efficiency enhances significantly. By both the proper ratio of dye mixture and the blocking layer improves cell performance of DSSC and opens a new pathway for future studies.


Introduction
The global energy demand has been continuously increasing due to the continuous growth of the world population, economic development, standard of living, and drive of modern technologies. In the current situation, about 87% of the primary energy needs are mostly supplied through fossil fuels (coal, oil, and gas) [1,2].
However, the sources of these fossil fuel reserves are depleting very fast. The existing sources of energy are inadequate, and if the fuel consumption continued at current usage rates, it would last only about 50 years [3]. On the other hand, burning fossil fuels releases carbon dioxide and other greenhouse gases (e.g., water vapor, methane, nitrous oxide, sulfur dioxide, and other ozone-depleting substance) in the atmosphere, making them the primary contributors to global warming and climate change. Because of the depletion of fossil fuels and global warming, in recent years, researchers are endeavoring severe attempts to find out various ways to meet energy demand around the world. Renewable energy could be an eco-friendly, alternative, sustainable energy resource because they are inexhaustible and will not pollute the environment for us or those of future generations by emitting harmful gases. Many alternative renewable energy sources have already been available, such as solar, hydro, wind, biogas, biomass, geothermal, wave, and tidal energy. Among all renewable resources, solar energy can be the solution to the problem of dwindling fossil-fuel reserves [4].
Solar energy is the cleanest and most abundant renewable energy source available. The solar cell or photovoltaic (PV) device is used for converting the energy of sunlight into useable electrical energy. The generated energy from solar does not produce any harmful emissions, consumes no fossil fuels, has no moving parts, and requires little maintenance. The development of PV technology is growing, and intensive research works are undertaken worldwide to improve cell performance and reduce the cost of the cell. With a history dating back over 60 years, since the very first silicon bipolar solar cell, the last three decades silicon solar cell has seen immeasurable advancement in both the performance of experimental and commercial cells. First-generation silicon solar cells showed their value in the market with the advantages, including high efficiency (26.6%), high reliability, low cost, ease of fabrication, and environmentally friendly traits [5][6][7][8]. Second generation thin-film (e.g., amorphous silicon (a-Si), cadmium telluride (CdTe), and copper indium gallium selenide (CIGS)) solar cells are cheaper than the mature Si solar cells; additionally, thin-films are easier to handle and more flexible. However, the shortage of Tellurium and Indium makes it hard to manufacture solar cells commercially. Also, Cadmium is extremely poisonous and medical problems with environmental impact [9]. This significant concern opened the method of exploration of finding other elective materials and further innovation for solar cells. Several new thinnerfilms have surfaced through concentrated research with higher potential, including dye-sensitized solar cell (DSSC), perovskite solar cell (PSC), copper zinc tin sulfide (CZTS) solar cell, organic solar cell (OSC), and quantum dot solar cell (QDSC) [10].
The DSSC belongs to the group of thin-films, functions on a semiconductor generated into an electrolyte and a light-sensitive anode [11]. In 1988, Brian O'Regan and Michael Grätzel at UC Berkeley, USA initially co-invented the modern version of DSSC and later they further developed this work at the ÉcolePolytechni-queFédérale de Lausanne, Switzerland [12]. Brian O'Regan and Michael Grätzel reported the first modern version of DSSC in 1991 with an efficiency of 7.1-7.9% [13,14]. DSSC can convert the solar energy to electrical energy by using photosensitive dye. DSSC is fabricated by using conventional roll-printing systems. The semi-transparency and semi-flexibility of DSSC offer a diversity of usages not appropriate for glass-based construction and most of the materials used are lowcost. However, practical elimination of several expensive elements has proven to be difficult, notably Pt and ruthenium (Ru). The energy conversion efficiency of the most recent laboratory-developed module is approximately 14.7% [15]. This chapter is focused on the improvement of efficiency of DSSC by the combination of natural dyes and the blocking layer. In this work, structure and operation principle of the third generation dye-sensitized solar cell (DSSC) has been discussed in the second section. Section 3 explains the combination of natural dyes with an optimized choice of the extracting solvents and the dye mixture's at proper volume ratio, enhancing the dye sensitizer's inherent properties, such as absorption and adsorption, thus improving the cell efficiency. Section 4 explains the comprehensive study of the blocking layer and its effect on the cell efficiency, and finally in section five, overall conclusions and accomplishments of this study have been mentioned.

Basics of DSSC
As shown in Figure 1, a typical DSSC consists of five different parts, such as, (1) transparent conducting oxide (TCO), glass substrate, (2) anode (wide band-gap semiconductor material layer on TCO), (3) photosensitizer, (4) electrolyte and (5) cathode (platinum/carbon layer on TCO). The components of a DSSC are: two transparent conductive oxide [indium tin oxide (ITO), fluorine-doped tin oxide (FTO), Indium Zinc Oxide (IZO) and Aluminum Zinc Oxide (AZO)] glass electrodes. One of the electrodes is the anode, the working anode, which is printed with semiconductor material [TiO 2 , ZnO, SnO 2 , SrTiO 3 , Zn 2 SnO 4 , Nb 2 O 5 , etc.] nanoparticles (particle size around 20-50 nm). The semiconductor oxides are sensitized with a photosensitizer (metal complex sensitizer, metal-free organic sensitizer or natural dye sensitizer), which absorbs the photons. The other electrode is the counter electrode [platinum or carbon coated TCO] and in between the two working electrodes is the electrolyte containing the redox couple [I À /I 3 À , Br À /Br 3 À , SCN À / (SCN) 3 À and SeCN À / (SeCN) 3 À , etc.]. Figure 2 illustrates the schematic diagram of the basic working principle of a typical TiO 2 based DSSC. All other semiconductor-based DSSC such as ZnO, SnO 2, etc. works under the same principle. Under illumination, a photo-excited electron is injected from the excited state of the dye (D*) from the highest occupied molecule orbital (HOMO) to lowest un-occupied molecular orbital (LUMO) (Eq. (1)). The excited electron is injected to the conduction band of the semiconductor material. The injected electron percolates through the semiconductor material by a driving chemical diffusion gradient and is collected at the TCO glass substrate (Eq. (2)). After passing through an external circuit, and reaches the counter electrode, thus, dye regeneration takes place due to the acceptance of electrons from I À ion redox mediator, and I À gets oxidized to I 3 À (Eq. (3)). To complete the circle, by electron donation, I À ions regenerated by the reduction of I 3 À ions at the cathode (Eq. (4)). However, some undesirable reactions are simultaneously taking place, such as nonradiation relaxation (Eqs. (5) and (6) no. red arrow in Figure 2), recombination of injected electrons with the oxidized dye (Eqs. (6) and (7 no. red arrow in Figure 2) and recombination of injected electrons with I 3 À (Eqs. (7) and (8) no. red arrow in Figure 2). In brief, the sequence of events in a DSSC is as follows [16]: TiO 2 |D * ! TiO 2 |D þ þ e À Oxidation of dye due to injection of electrons in TiO 2 photoanode (2) I À Restoration of electrolyte at the counter electrode (4) TiO 2 |D þ þ e À ! TiO 2 |D Dye recover to ground state (6) D: Dye sensitizer; D * : Excited dye upon illumination; D + : Oxidized dye. Nemours researchers are working on to improve cell performance by different means, such as modifying the TCO/semiconductor material interface by blocking layer; modifying semiconductor material by doping, annealing time, radiation, carbon nanotubes, etc.; modifying the absorption properties of the dyes by Ru dye, organic dye, dye mixture, etc. to enhance cell efficiency [17][18][19][20][21][22].

Effect of combination of natural dyes
The dye in DSSCs has a vital role in harnessing solar energy from the sun and converts it into useable electrical energy. The primary charges in the dyes separate through photo-excitation, and photo-excited dyes inject electrons into the conduction band of semiconductor material. A dye should fulfill some prerequisites to be considered efficient dye: (1) binding firmly with the semiconductor material; (2) higher molar absorption capabilities for maximum absorption from visible to IR-region; (3) fast electron transfer; (4) LUMO of the dye should be higher than the conduction band of semiconductor for efficient electron injection into the semiconductor material; (5) HOMO of the dye should be lower than the redox couple for efficient regeneration of oxidized dye; and (6) slow degradation (or do not degrade at all) [16,[23][24][25]. The dyes used in DSSC are divided into three types: metal complexes dye sensitizer, metal-free organic dye sensitizer, and natural dye sensitizer. Metal complexes dye sensitizers, such as polypyridyl complexes of Ruthenium (Ru), Osmium (Os), metal porphyrin, phthalocyanine are the most efficient and durable dye for DSSC application. However, these dyes have a complex synthesis process, release chemicals as a by-product, and require rearearth material for the synthesis process. As a result, the overall fabrication process highly depended on the rear earth material that is neither sustainable nor economical. On the other hand, metal-free organic dye sensitizer has advantages over metal complex dye sensitizer, reducing the use of rear-earth material, higher molar absorption co-efficient, and preprocessing color. However, these advantages are offset by their instability, tedious manufacturing process, tendency to undergo degradation, and toxicity. These significant limitations influenced scientists to work on possible replacements for metal complexes or metal-free organic dye sensitizers [16].
Over the years, significant research has been done to determine the possibility of replacing sensitized dye. Natural dye has several advantages over sensitized dyes. These include low production cost, high availability, easy access, simple fabrication technique, biodegradable, environment friendly, purity grade, non-toxic, and reducing the use of rear-earth material. Natural dye-based DSSCs have attracted considerable attraction as an alternative way to produce low-cost dyes to a large extent by extracting dyes from natural resources. In nature, some vegetables, fruits, flowers, leaves, seeds, roots, stems, bacteria, and algae exhibit various colors due to plant pigmentation [16]. The natural dyes are four major families which are chlorophyll, anthocyanin, carotenoids, and flavonoids [26,27].
Chlorophyll, which is the most widespread pigment occurring naturally in plants, fungi, bryophytes and algae. The molecular structure of a chlorophyll consists of a Magnesium-containing tetrapyrrolic ring, encircled by other side chains. The chlorophylls are classed mainly as chlorophyll-a, chlorophyll-b, chlorophyll-c1, chlorophyll-c2, chlorophyll-d, and chlorophyll-f. They absorb light from red, blue, and violet in the visible wavelengths with an absorptionmaximumof $670 nm while reflecting green wavelengths. Chlorophyll dye molecule create an electronic coupling with the conduction band of semiconductor material through the carboxylic groups, which helps to anchor the dye molecules and transfer injected electron efficiently from the dye sensitizer to the conduction band of semiconductor material [16,28]. Figure 3 shows the basic molecular structure of chlorophyll and the binding chlorophyll and semiconductor material (e.g., TiO 2 ).
Anthocyanins are also an abundant and widespread group of water-soluble pigments in plants. They absorb light at the longest wavelengths. Depending on the pH value, anthocyanins are responsible for the existence of attractive colors, such as red, orange, magenta, pink, blue, blue-black and purple floral [16,30]. Generally, the carbonyl and hydroxyl functional groups in the anthocyanin dye sensitizers create an electronic coupling with the semiconductor material's conduction band, which helps transfer the excited electron efficiently to the conduction band of Chlorophyll-semiconductor material (i.e., TiO 2 ) interaction [29]. semiconductor material [16]. Figure 4 shows the basic interaction between anthocyanin and semiconductor material (e.g., TiO 2 ).
Carotenoids occur in many plants and algae, as well as several bacteria, and fungi. It contributes to yellow, orange, and red colors and allows them to absorb short-wave visible light [32]. Carotenoids can be divided into two major types: xanthophylls (with oxygen) and carotenes (purely hydrocarbons and without oxygen) [16,33]. Figure 5 illustrates the interaction between carotenoids-semiconductor material (i.e., TiO 2 ).
Flavonoids are essential floral pigments. The development of a specific color depends on the accumulation of flavonoid chromophores and other intrinsic and extrinsic factors. Chemically, the flavonoids have a C6-C3-C6 carbon framework with two connected two phenyl rings (A and B) and a heterocyclic ring (C). Depending on the oxidation potential of the C-ring, the particular flavonoids absorb light in the visible wavelength. Till now, over 5000 flavonoids have been identified from different plants.
Most of the flavonoid pigment has loosely or unbound electrons. Thus less energy is required for excitation of such electrons is lower compared to the others. As a result, those pigment molecules can be energized by the light within the visible range [16].
The overall cell efficiency of natural dye-based DSSCs is comparably low compared to DSSCs sensitized with sensitized dyes. Due to the inadequate interaction between dyes and semiconductor surface, a significant reduction of the cell's shortcircuit current. The pigment's long structure obstructs the dye molecules to form a bond with the oxide surface of the semiconductor materials effectively. Those are the field of works that are yet to be developed in natural dye DSSCs to achieve highefficiency devices and device stability. To further raise the efficiency of the DSSC combination of dyes has been explored and reported DSSC or to broaden the absorption spectrum [35][36][37][38][39]. A combination of natural dyes with an optimized choice of the extracting solvent enhances the absorption of solar light and allowed utilization of the photon energy more efficiently. As a result, DSSC sensitized with the dye mixture shows higher absorbance, and cumulative absorption properties over the entire visible region than the DSSC fabricated with single individual dyes [35,36].
Kabir et al. studied the effect of chlorophyll and anthocyanin dye mixture on the cell performance of natural dye-based DSSC. They also mixed the dyes at five different volume ratios to find the optimized dye mixture. The cell conversion efficiency of DSSC fabricated with individual chlorophyll, and anthocyanin dyes were 0.466% and 0.531%, respectively. DSSC co-sensitized with the optimized dye mixture (20% chlorophyll +80% anthocyanin) showed cell conversion efficiency of 0.847%, which is almost 1.82 and 1.6 times higher than the cell efficiency of the individual chlorophyll and anthocyanin dye-sensitized DSSC's (shown in Figure 6). The chemical characteristics study of the dye showed that no new bond except has formed; however, few shifts in the adsorption peak was observed (Shown in Figure 7 and Table 1). Similar characteristics were seen when dyes were adsorbed the TiO 2 semiconductor material (shown in Figure 8. and Table 2, [36]. Figure 9 illustrates the UV-visible absorption spectra of natural chlorophyll (green), anthocyanin (red), and the optimum combination of dyes (green + red) diluted in ethanol. The dye mixture has demonstrated the cumulative absorption properties of both individual green and red dye.
Kabir et al. also studied the effect of betalain and curcumin dye combination on the cell performance of natural dye-based DSSC. They also mixed the dyes at three different volume ratios to find the optimized dye combination. The optimized dye mixture demonstrated the cumulative absorption properties of both individual betalain and curcumin dye (shown in Figure 10). The DSSC fabricate with the combination of betalain and curcumin dye also showed superior cell performance than DSSC manufactured with individual betalain and curcumin dye (shown in Figure 11 and Table 3) [35].  FT-IR adsorption spectra of natural chlorophyll (green), anthocyanin (red), and combination (20% green +80% red) of dyes (without TiO2) [36].
Nonetheless, to the best of our knowledge, combination of dyes have a positive impact on the cell performance of natural based DSSC.

FT-IR adsorption spectra of natural chlorophyll (green), anthocyanin (red), and combination (20% green +80% red) of dyes (with TiO 2 ) [36].
DSSC influences the photo generated current. Highly porous structures and large surface areas of the nanostructured semiconductor materials increase the dye absorption and move the photo-induced electron towards the load [56]. Intensive research has been undertaken by the DSSC research community to increase photoinduced current and understand the mechanisms responsible for losses in the cell. Radiation less relaxation of energized dye, electron recombination with the oxidized dye; and electron recombination with the tri-iodide in the electrolyte are the main reasons for limiting the photocurrent in the cell. Generally, the first two have a negligible impact, while the last one shows a significant impact [56,57]. Electron recombination occurs when electron transfer to I 3 À in the electrolytes via semiconductor material and the TCO. Electron recombination through both routes needs to be reduced to prevent loss. In I À /I 3 À redox couple, the electron transfer via the TCO is negligible due to small exchange current density between I 3 À -I À . Generally, the losses via the FTO under short-circuit condition is insignificant, because the Fermi level of the TCO (i.e., FTO) is close to the redox Fermi level. However, under illumination, the quasi-Fermi level of the semiconductor material (i.e., TiO 2 ) rises rapidly with distance from the TCO (as shown in Figure 12a). As a result, a higher driving force is observed when electron transfer from the semiconductor material to I 3 À , which is much higher than in the bulk of the sensitized layer that is close to the TCO glass substrate. Thus, I 3 À electrons are anticipated to recombine with the semiconductor material at short-circuit conditions [57].
However, under illumination, the open-circuit condition is entirely different (shown in Figure 12b). Due to the rise ($0.7 eV) of the Fermi level of TCO glass substrate, a much higher driving force is observed when electron transfer from the TCO glass substrate to I 3 À . Thus, the electron recombination with I 3 À via the TCO glass substrate and the back reaction by these two routes causes a photo stationary state in the cell [57].   [36].
The blocking layer works as a barrier layer at the TCO/semiconductor material interface to improve cell performance. Studies had shown that a significant improvement in photo induced current observed when the blocking layer was introduced in the cell. Park and colleagues found that due to the blocking layer's  presence, total transfer resistance at the blocking layer/electrolyte interface increased that increased cell performances by preventing electron recombination near the TCO glass substrate [58,59]. Fabregat and co-workers found that BL Figure 11. I-V characteristics of DSSC fabricated with betalain, curcumin, and combination of dyes [35].  Table 3.
improved physical contact between the TCO and semiconductor material that produce higher photo conversion efficiency. However, the advantage obtained by utilizing blocking layer is lost if the layer is too thick, and, generally, generates a series of resistance and an electron barrier that reduces the charge collection efficiency [59,60]. A significant amount of photo-induced electron recombined and results in lower photocurrent. Recombination of the electron at the interfaces reduces the photocurrent and affects the fill factor; thus, cell performance decreases [60]. The complete photo anode is constructed layer-by-layer stack of suitably designed structures to maximize different cell functionalities. The recombination losses in DSSCs occurred primarily at the interface between the glass substrate of TCO and the electrolyte. The compact blocking layer acts as a physical barrier and physically separates and reduces the contact surface area between the TCO glass substrate from the electrolyte [59]. By employing the blocking layer with suitable thickness, the recombination can be reduced; and photo induced current and fill factor increase, leading to the DSSC efficiency improvement. Studies also showed that the blocking layer also improved the open-circuit-photo voltage of the cell [61]. The schematic on the effect of blocking layer is shown in Figure 13.
There are many kinds of preparation methods for blocking layers in DSSCs, including spin coating, deep coating, spray coating, sol-gel, sputtering, hydrothermal technique, etc. Spin-coating is a simple method for preparing uniform thin films onto flat substrates. Generally, the spin coating method includes deposition, spinup, spinoff, and evaporation [62]. Usually, a small amount of coating material is applied to the center of the substrate then rotated at speed up to 10,000 rpm to spread the coating material by centrifugal force. Rotation is continued while the fluid spins off the substrate's edges until the desired thickness of the film is achieved. The film's thickness also depends on the solvent and solvents concentration [63].
Yeol et al. prepared a ZnO precursor on FTO substrates for the blocking layer. For ZnO precursor, a homogeneous mixture of 2.195 g zinc acetate dehydrate, 20 mL isopropanol, and 0.605 mL monoethanolamine (MEA) was prepared. The concentration was 0.5 M, with MEA: zinc acetate molar ratio of 1: 1. The prepared solution was stirred for 2 hrs at 200 rpm at 60°C, then stirred at the same rpm at ambient temperature for 22 hrs. For the spin-coated film, rotation speed and duration were held at 3000 rpm and 20 s, respectively. They annealed the spin-coated films at 500°C for 1 h to form a blocking layer of ZnO (55 nm to 310 nm). The ZnO blocking layer thickness is a function of the number of deposition cycles in the spincoating process. ZnO blocking layer thickness increased linearly with the number of deposition cycles, a typical feature of the spin-coating technique [64]. Figure 14a illustrates the morphology of FTO. Figure 14b and c show that ZnO nanoparticles are distributed uniformly across the FTO substrate's surface to form a compact layer. Comparing both Figure 14a and c, when the thickness of the ZnO blocking layer increased, the size of the ZnO nanoparticles also slightly increased.
Yeol et al. showed that the effect of ZnO blocking layer and increasing its thickness on the cell performance of TiO 2 based DSSC. Table 4 lists photovoltaic performance and Figure 15    Lee et al. prepared several TiO 2 gel films with the spin coating method with different thicknesses. The thickness and roughness of the TiO 2 layers are among the most critical factors in the cell performance of DSSC [66]. Table 5 lists the thickness and root-mean-square roughness of TiO 2 thin films. SEM images of 10 μm thin films (surface and cross-sections) are shown in Figure 16. Table 6 lists photovoltaic performance and Figure 17 illustrates the J-V characteristics of the cell, including ZnO blocking layers of different thicknesses.
TiO 2 layers also enhance the contact property between the FTO and TiO 2 electrode. Figure 16c and d illustrate the photovoltaic performance and the J-V characteristics curve of DSSC with different blocking layer thicknesses. The thickness of the TiO 2 blocking layer affects the efficiency of DSSC. As thin films' rpm increased, the thickness and roughness of the TiO 2 blocking layer also decreased, and the film becomes smooth and uniform. This increase in the smoothness and uniformity of  Table 5.
the TiO 2 blocking layer results in improved cell performance. The increased number of efficiently transferred photo generated electrons to the TiO 2 electrode results in an improvement in short-circuit current [67]. By suppressing the recombination of electrons injected from excited photosensitizers in the TiO 2 and electrolyte interface, a higher value of open-circuit voltage was obtained [57]. Their study also showed that when the resistance at the FTO/TiO 2 layer interface was decreased, the electron lifetime in DSSCs was increased [66].  [66].  Figure 18 illustrates the SEM of bare FTO and blocking layer-deposited FTO glasses (surface and cross-sections). Table 7 lists the photovoltaic property of DSSC with a blocking layer, where short-circuit current density increases with increasing the precursor concentration (and increased blocking layer thickness).
Zou et al. studied the effect of the TiCl 4 blocking layer (or pre-treatment) in ZnO based DSSC. Figure 19 shows the fabricated ZnO films, with and without TiCl 4 pre-treatment on the FTO glass substrate. From Figure 19a-d, it can be seen that fabricated ZnO films have porous flakes, both with and without blocking    layers. However, TiCl 4 treated ZnO anode has a larger flake, which can offer a large surface area to absorb much more dyes. Table 8 lists the photovoltaic property of DSSC with TiCl 4 blocking layer [68]. Kabir et al. studied the effect of post-treatment of TiCl 4 in TiO 2 based DSSC. Post TiCl 4 treatment not only increases the overall cell conversion efficiency of DSSC but also enhances cell stability. TiCl 4 treated TiO 2 anode based DSSC's degradation rate is much lower than the TiCl 4 untreated TiO 2 anode based DSSC. Studies showed that TiCl 4 treated TiO 2 anode based DSSC's cell stability of the increase around 38-44.5%. Figure 20 shows the effect of post TiCl 4 treatment in the cell conversion efficiency of TiO 2 based DSSC [69].

Surface (A-H) and cross-section (a-h) SEM
Cameron et al. [57], Heo et al. [70], Yu et al. [71] used spray coating method to prepare TiO 2 blocking layer. Introducing the blocking layer into the device decreases charge carrier trapping and recombination. Subsequently, short-circuit current increases significantly. Additionally, a slight improvement in the opencircuit voltage and fill factor is observed, thus cell efficiency enhances significantly.

Summary
In conclusion, natural dye is a promising alternative to replace the metal complexes or organic dyes in the DSSC application. They are low-cost, abundant, ecofriendly, simple extraction procedures, and non-toxic. The combination of natural dyes with an optimized choice of the mixture of the volume ratio of the extracting dye extracting solvent accounts for many possible interactions that promise to provide more charge injection upon sensitization and allowed utilization of the photon energy more efficiently. DSSC co-sensitized with the dye mixture shows higher absorbance, and cumulative absorption properties over the entire visible region than the DSSC fabricated with individual dyes.

Figure 20.
Effect of post TiCl4 treatment in the cell performance of TiO2 based DSSC [69].
A blocking layer in DSSC provides good adhesion between the transparent conducting oxide (e.g., ITO, FTO, etc.) and an active semiconductor layer, TCO (e.g., TiO 2 , ZnO, etc.). It also represses the electron back transport between electrolyte and TCO by blocking direct contact. Also, it offers a more uniform layer than bare TCO glass substrate. The conventional blocking suppresses electron leakage, recombination, and trapping; thus, the photovoltaic performance of the DSSC improves. Introducing a blocking layer in the DSSCs show lower dark current and operates efficiently under high-intensity sunlight and ambient light conditions.