Vertical-Type Organic Light-Emitting Transistors with High Effective Aperture Ratios

The inherent complexity of the structures of active-matrix (AM) organic light-emitting diode (OLED) displays severely limits not only their size but also device performance. Surface-emitting organic light-emitting transistors (OLETs) may offer an attractive alternative to AM displays. We report some characteristics of vertical-type OLETs (VOLETs) composed of a source electrode of low-dimensional materials and an emissive channel layer. With a functionalized graphene source, it is shown that the full-surface electroluminescent emission of a VOLET can be effectively controlled by the gate voltage with a high luminance on/off ratio (10 4 ). The current efficiency and effective aperture ratios were observed to be more than 150% of those of a control OLED, even at high luminances exceeding 500 cd m − 2 . Moreover, high device performance of micro-VOLET pixels has been also successfully demonstrated using inkjet-patterned emissive channel layers. These significant improvements in the device performance were attributed to the effective gate-voltage-induced modulation of the hole tunneling injection at the source electrode.


Introduction
In recent years, researchers of state-of-the-art electronics utilizing organic semiconducting materials have succeeded in advancing various devices, such as organic light-emitting diodes (OLEDs), photovoltaic cells, organic thin-film transistors (OTFTs), and sensors, among others [1][2][3][4][5][6][7][8][9][10]. Among these, intensive efforts in OLEDs have led to high brightness, efficiency, and full-color electroluminescent (EL) emissions for various light-emitting optoelectronic devices [7][8][9][10]. The advantages of such OLEDs over conventional liquid crystal displays (LCDs) are well known, especially for high-quality displays in terms of their viewing angle, response time, thickness, and contrast ratio [11]. For instance, small OLED displays are constructed on an array of thin-film transistor (TFT) switches, allowing precise control of the states of the pixels [12][13][14]. In such active-matrix OLEDs (AM-OLEDs), the OLED is driven in the current mode; thus, at least two TFTs, in this case a switching TFT to select a pixel and a driving TFT to operate the OLED, are required, as shown in Figure 1(a) [12,13]. Perhaps unexpectedly, however, the complexity of such pixel circuit designs with their sophisticated procedures has led to a significantly limited light-emitting area and aperture ratio (the light-emitting area as a fraction of the total area of the device, typical aperture ratios: 25-34%) [13][14][15], introducing severe problems associated with limited device performance and limited display sizes for AM-OLEDs. Besides these issues, fundamental factors related to the architecture of the OLED itself, such as exciton quenching and photon loss, also still limit the efficiency and brightness of these devices.
In principle, the luminance from OLETs can be modulated by the gate voltage without any additional driving devices; thus, displays using OLETs have the advantage of greatly reducing both the number of TFTs and the circuit complexity (Figure 1(b)), thereby providing an effective means of increasing the aperture ratio [29]. Hence, OLETs could be a key part of the development of next-generation AM display technology [29]. Indeed, a proof-of-principle device was recently developed using carbon nanotubes (CNTs, Figure 2), delivering a CNT-based vertical-type OLET (CNT-VOLET) [31][32][33][34]. In the CNT-VOLET, a dilute network of CNTs is used as a source electrode, leading to several improvements, such as a high on/off ratio, attributed to the gate-bias-induced modulation of the lateral (or horizontal) Schottky barrier height [31,32]. Nevertheless, the improvement of the effective aperture ratio (AR eff , the percentage ratio of the current efficiency of a surface emitting OLET to that of a control ITO-base OLED at a given luminance) in the  CNT-VOLET is still limited to less than those of control OLEDs, and its parasitic power consumption (PPC, percentage of power dissipated across the driving transistor element of the device not contributing to light generation) requires further reductions [32]. Moreover, this attempt resulted in a complicated source structure, and the production of porous CNT network sources with smooth and homogeneous surfaces was problematic due to the aggregation of CNTs [35]; significant obstacles thus remain with regard to the limited reproducibility of these devices. Thus, the goal of high-performance and reliable OLETs with high AR eff and low PPC values remains a considerable challenge.
In this chapter, for the VOLET, the use of a nonporous, homogeneous, smooth, and easily processable graphene layer is described as the source contact, together with an emissive channel layer. Here, the graphene is a two-dimensional (2D) material in the form of a single atomic layer of carbon with a hexagonal lattice structure bonded in the sp 2 configuration (Figure 2) [36][37][38]. Despite the similar low dimensionality of graphene to CNTs [36,37], the optoelectric properties of a VOLET based on graphene have not yet been fully characterized. Herein, the fabrication and characterization are described for a simple VOLET with a single-layer graphene (SLG) source contact (Gr-VOLET), capable of efficiently modulating device performance levels with high luminance on/off ratios (~10 4 ) upon the application of a gate voltage. The Gr-VOLETs with doped SLG sources with FeCl 3 are demonstrated to exhibit greatly improved device performance, especially in their enhanced current efficiency and AR eff values of more than 150% of those of a control OLED, even at high EL luminance levels exceeding 500 cd m −2 . These figures are among the highest ever published for OLETs, and their low PPCs make them all the more attractive. Moreover, such high device performance has also been successfully confirmed even for micro-VOLET pixels fabricated by an inkjet-patterning technique [39].

Preparation of SLG source electrodes
Preparation of substrates: The transparent VOLET substrate used here was prepared with a pre-patterned bottom gate electrode, consisting of a transparent ITO layer (80-nm-thick, 30 ohm square −1 sheet resistance) on a glass substrate, and a sputterdeposited aluminum oxide (Al 2 O 3 ) top layer (400 nm) as a gate dielectric over the ITO gate (glass/ITO/Al 2 O 3 ). The VOLET substrate used was then cleaned with alcohol, followed by a UV treatment (5 min), prior to the fabrication of the devices.
Synthesis and transfer of SLG: The procedure used for transferring the chemicalvapor-deposition (CVD)-grown graphene onto a target substrate [40][41][42][43][44][45], in this case an FET substrate, a VOLET substrate, or a glass substrate, is described below. The first Display Technology 4 step involves the CVD growth of graphene on a copper (Cu) foil [42][43][44][45]. A clean Cu foil was placed in a quartz tube vacuum chamber and then the temperature of the chamber was increased to 1000°C under Ar (10 sccm). For the growth of graphene, a mixed gas of methane (CH 4 , 30 sccm) and hydrogen (H 2 , 10 sccm) was used at approximately 2.7 × 10 −2 Pa. The next step involved spin-coating a solution of polymethyl methacrylate (PMMA) at 3000 rpm for 60 s onto the graphene on the Cu foil [42][43][44][45]. The graphene on the back side of the Cu foil was removed by atmosphericpressure oxygen plasma. Next, a PMMA-coated Cu/Gr (Cu/Gr/PMMA) block (width: 4 mm, length: 20 mm) was floated on an aqueous FeCl 3 etching solution used to etch the Cu foil entirely, at 50°C for 20 min [40]. Next, the Gr/PMMA block was rinsed with deionized (DI) water two to five times (10 min) and transferred onto a target substrate, after which the graphene-transferred substrate was dried under reduced pressure (~1 Pa) for 1 h and left in air for 24 h. The PMMA layer was then removed by dissolving the PMMA layer in chloroform (~60 min), monochlorobenzene (~30 min), and chloroform again (~30 min), to obtain a SLG source electrode. The optical characteristics of the SLG-transferred VOLET substrate were monitored using a UV-visible spectroscopy system. The average optical transmittance (~92%) of a SLG source on a VOLET substrate in the visible range (400-800 nm) was found to be similar to that (~92%) of a conventional ITO-coated glass substrate for OLEDs.

Characterization of SLGs
In this study, a transferred SLG was investigated as a source contact, where the FeCl 3 doping is processed spontaneously during the graphene transfer process [40]. The basic properties of the three SLG sources are shown in Figures 3 and 4 and are summarized in Table 1.
In order to identify the SLG used, the surface composition of the SLG on the SiO 2 /Si substrates was analyzed by X-ray photoelectron spectroscopy (XPS). Figure 3(a) presents the wide-scan XPS spectra, showing strong photoelectron lines at binding energies of ~104, ~285, and ~531 eV, which are attributed to Si2p, C1s and O1s, respectively. Note that there is no Cu peak in the range of 932-935 eV (Cu2p and Cu 2+ ), implying the complete etching of the Cu foil. In addition, the XPS spectra also revealed small but measurable amounts of Cl and Fe. These are likely residues of the etchant (FeCl 3 ) used during the etching process. When such FeCl 3 residues adsorb onto the SLG, the transfer of electrons to the Cl from the SLG (chlorination) [46] induces unintentional p-doping of the SLG. Figure 3(b) shows the surface morphology of the SLG on the VOLET substrate as measured by a noncontact atomic force microscope (AFM). As indicated by the AFM morphology, the SLG samples exhibit a fairly smooth surface; the SLG presented an AFM morphology that was nearly identical at different positions on the investigated SLG samples with low RMS roughness levels of 1.4-2.0 nm.
The surface-contact potential difference (V CPD ) of the SLG on the VOLET substrate was also monitored using a simultaneous Kelvin prove force microscope (KPFM) by applying AC voltage (1 V) with a frequency of 18 kHz to a Pt/Ir-coated silicon KPFM cantilever. In order to calibrate the work function of the sample, V CPD of highly oriented pyrolytic graphite (HOPG) was used as a reference V CPD . The work function of the SLG (W SLG ) was obtained by a comparison of V CPD s for the SLG and the HOPG, where W HOPG is the work function of the HOPG (~4.6 eV) [47]. substrate is approximately 5.21 ± 0.07 eV, which is higher than the intrinsic work function (4.5-4.8 eV) of undoped monolayer graphenes [47,48], mainly due to the FeCl 3 doping [49].  Next, the transport characteristics of the SLG used were observed by assessing a liquid-gated lateral FET with SLG channels, a Gr-FET, as shown in Figure 3(d).
The lateral FET substrate was prepared using the VOLET substrate or a heavily doped n-type Si wafer substrate (0.05-ohm cm) with a thermally grown SiO 2 layer (300-nm-thick) as the gate dielectric for the OTFT, together with a laterally patterned metal source and drain electrodes consisting of a Cr layer (5.5-nm-thick) and a Au layer (50-nm-thick) formed on the substrate via a vacuum deposition process with a mask. The channel length (L) and width (W) of the FET were 50 μm and 1600 μm, respectively (see inset in Figure 3(d)). Regarding the transport characteristics of the SLG studied, a liquid-gated lateral Gr-FET was prepared using an FET substrate with acetonitrile (ACN) with 100 mM of tetrabutylammonium hexafluorophosphate (TBAPF 6 ). The channel of the studied SLG of the Gr-FET was gated through the ACN electrolyte with an Ag/AgCl (3.5 M KCl) reference electrode by sweeping the gate voltages from −0.8 to 0 V and then to +0.8 V with a sweep rate of 30 mV s −1 at V DS = 100 mV. In general, the liquid-gate Gr-FET has better transfer characteristics than the conventional back-gate Gr-FET because the liquid gate exhibits higher capacitance than the back gate [49,50].
For the SLG used here, the Gr-FET showed a clear asymmetrical V-shaped I DS -V G curve with a charge-neutral gate voltage (or Dirac point, V Dirac ) of ~0.54 V/V Ag/AgCl . This large positive value of V Dirac clearly indicates that the SLG used is p-type (hole) doped graphene due to the chlorination of graphene by FeCl 3 [49]. According to the V Dirac value of the SLG, the energy level of the Dirac point E D , relative to the vacuum level, can be estimated with regard to the redox potential of a probe material of ferrocene via the following relationship [51]: Here, 4.8 eV is the absolute energy level of the ferrocene and ferrocenium (Fc/Fc+) redox couple below the vacuum energy level, and E 1/2(Fc/Fc+) = 0.45 eV [51]. From Eq. (2), the V Dirac value of ~0.54 V/V Ag/AgCl for the SLG gives a Dirac point energy E D of approximately ~4.89 eV. Note that the E D value of 4.89 eV is higher than that (~4.49 eV) of epitaxial monolayer graphene [52], also confirming the p-type doping of the SLG. From the transfer characteristics, the carrier (hole) mobility μ of the SLG was also estimated using the relationship [53] of where C g is the top-gate capacitance of graphene (~1.9 μF cm −2 ) [50]. The estimated hole mobility for the SLG was approximately ~410 cm 2 For the SLG studied here, Raman spectroscopy was also carried out using a confocal Raman system with a laser source operating at 514.5 nm (~1 mW on sample surface). As shown in Figure 4(a), the Raman spectra of the SLGs studied here have two strong characteristic peaks, a G band at around ~1580-1600 cm −1 , due to the E 2g vibration of sp 2 -bonded carbon atoms, and a 2D band at around ~2644-2665 cm −1 , which is a second-order type of vibrational mode caused by the scattering of phonons at the zone boundary [54,55]. It can be observed that there are very small disorder-induced D bands around ~1340-1350 cm −1 , indicating the sparse formation of sp 3 bonds due to the relatively few defects in the SLGs studied. From the Raman peak intensities, it was found that the ratios of the integrated Raman intensities of the G band to the 2D band for the FeCl 3 -doped SLG were in the approximate range of 1.7-1.8, indicating that the SLGs studied here are high-quality monolayer graphene [55]. Moreover, from the peak positions, it was found that while the G and 2D peaks of the intrinsic undoped SLG are positioned at ~1579 cm −1 and ~2669 cm −1 , respectively, the G and 2D peak positions of the SLG used are correspondingly upshifted to ~1585 cm −1 and ~2677 cm −1 . Through a comparison of these with other examples in an earlier report of the relationship between the G and 2D peak positions of graphenes [55], it was verified that the SLG used here is p-type doped SLG.
Subsequently, the densities of the defects, the distances between the defects, and the porosities of nano-defects for the SLG were estimated from the ratio of the Raman intensities of the G bands to the D bands, I D /I G , as shown in the Raman spectra above. The density of the defects (n D ) and the distances between the defects (L D ) for the SLG, as estimated from the carbon amorphization trajectory (I D / I G ~ 0.117) [56,57], were n D ~ 3.0 × 10 10 cm −2 and L D ~ 32.8 nm, respectively, corresponding to a porosity of 9.4 × 10 −2 %. This result clearly indicates that the SLGs studied here are nonporous high-quality SLGs with a negligible number of porous defects introduced during the synthesis and transfer steps.
Next, for this SLG, polarized optical microscopy was also carried out using SLG covered with commercial nematic liquid crystals (NLCs, Merck LC ZLI-2293) in a crossed polarization state [58]. As shown in Figure 4(b), the polarized optical microscopic image of a spin-coated NLC layer on the SLG shows large graphene domains (with an average radius of the domains >100 μm) in the form of highly uniform optical retardation, in addition to small domains of several hundreds of nanometers in size [59,60], clearly indicating that the SLG studied here is highquality graphene with large-area graphene domains. Figure 5 presents a schematic illustration of the structure used and the stages of the fabrication of the SLG-based VOLETs (Gr-VOLETs) with an ITO gate separated by an Al 2 O 3 gate dielectric layer, a SLG source, organic channel layers, and an Al drain. The fabrication steps of the Gr-VOLET investigated are described below. To construct the Gr-VOLET, SLG (4 mm by 20 mm) was transferred onto a VOLET substrate, as mentioned above (Steps 1, 2). The source electrode used was FeCl 3 -doped SLG. Next, organic semiconducting materials were deposited over the SLG source electrode regions; a channel layer of poly(para-phenylene vinylene) copolymer (known as SY, 70-nm-thick) was coated as an emissive channel layer by spin coating (Step 3), after which a 2-nm-thick electron injection layer of CsF and a 80-nm-thick drain electrode of Al were deposited on the top of the SY channel layer in sequence via thermal deposition at a rate of 0.05 nm s −1 under a base pressure of less than 2.7 × 10 −4 Pa (Step 4). Finally, the fabricated device was encapsulated with an epoxy resin in a glove box. The photograph in Figure 5 shows the microscopic morphology of the device cross section as observed by field emission scanning electron microscopy (SEM).

Operating characteristics of Gr-VOLETs
The operating characteristics of the Gr-VOLET were observed using a luminance meter in conjunction with two source meters. To operate the Gr-VOLETs, sourcedrain voltage V DS (= −V SD ) on the Al drain and gate voltage, V GS (or V G ), were applied with respect to the SLG source contact, held at the ground potential. During the operation of the Gr-VOLET, an electron injection occurs from the Al drain into the SY channel layer, and the hole injection from the SLG source to the SY channel layer can be modulated by controlling the gate voltage V GS (or V G ), as discussed below. Figure 6 shows the EL light emissions of a Gr-VOLET operating under different V G values with a fixed V SD of 3.8 V. As shown in Figure 6(b), the EL light emission is uniform and bright (in the on-state) and evenly dark (off-state) over the entire surface of the active area for negative and positive V G values, respectively. Hence, V G essentially influences the radiative recombination process in the emissive channel layers.   The output current and luminance characteristics of the Gr-VOLET were investigated as described below. For comparative purposes, the diode characteristics of the Gr-VOLET were also observed with the gate electrodes isolated from the external circuits (Gr-OLED). As shown in Figure 7, the current density-voltage (J SD -V SD ) characteristics and luminance-voltage (L-V SD ) characteristics of the Gr-VOLET present the following key features: (i) the J SD -V SD characteristics are similar to the diode characteristics, as is generally observed in vertical organic FETs due to the short channel lengths [61]. (ii) Similar behaviors were observed in the L-V SD characteristics; (iii) for a given V SD , both J SD and L increase with a decrease in V G , even at low V SD values, indicating that current modulation by V G can change the EL emission brightness. Thus, the V G dependent turn-on voltage, V onset , can be reduced to well below V onset of the Gr-OLED, and (iv) both J SD and L also depend on the direction of change of V G , that is, upward or downward, implying hysteretic behavior.

Schematic illustration of the fabrication steps of a Gr-VOLET and a cross-sectional scanning electron microscopy (SEM) image of the Gr-VOLET with stacked layers of an ITO gate separated with an Al 2 O 3 gate dielectric, a SLG source, organic channel layers, and an Al drain.
Interestingly, as shown in Figure 7, at V G = −40 V, the Gr-VOLET with the doped SLG source exhibits high device performance, superior to that of the Gr-OLED, indicating an improved and balanced charge injection from the SLG source for negative V G values. Conversely, at V G = +40 V, J SD and L of the Gr-VOLET are much lower, due to the switching off effect of the hole injections from the SLG source. The highest values of the peak on/off ratios for J SD and L were ~10 2 and ~10 4 , respectively, at V G = ±40 V. Thus, the gate-bias-induced modulation effect of Gr-VOLET is shown to be quite efficient.
Next, the device performance, AR eff , and PPC, of the Gr-VOLET were estimated in the on-state in comparison with a control OLED fabricated using an identical process on an ITO anode (ITO-OLED) (Figure 8). As shown in Figure 8, the Gr-VOLET exhibits EL luminance higher than that of the control OLED (ITO/SY/CsF/Al) in the V SD < 4.0 V region. Moreover, the Gr-VOLET was shown to be more efficient than the control OLED (Figure 8(c)). For instance, at an EL luminance level of 500 cd m −2 , the Gr-VOLET emitted EL light with a current efficiency, η C , of 7.13 cd A −1 , which is approximately 154% of the η C result (4.64 cd A −1 ) for the control ITO-OLED. Thus, the AR eff value of the Gr-VOLET can be estimated to be 154% due to its full surface emission, just like the OLED. Thus, it is clear that the Gr-VOLET has a greatly enhanced AR eff compared to other reported devices ( Table 2). This result offers another substantial advantage: given the level of AR eff , the brightness of the device can be maintained under a lower J SD , providing a longer device lifetime  [62]. It is noteworthy that η C (7.13 cd A −1 ) for the Gr-VOLET was approximately 1.4 times higher than η C (5.17 cd A −1 ) of the ITO-OLED, possessing the optimized HIL of PEDOT:PSS. Thus, it is clear that the SLG source in the Gr-VOLET provides amplification of the emission and current efficiency, although further optimization of the electrodes is still possible.
Next, the PPC of the Gr-VOLET was deduced, which achieved luminance of 500 cd m −2 at V SD = 3.82 V with an AR eff rate of 154%, as discussed above. For the control ITO-OLED to emit a luminous flux through an aperture while transmitting 154% of its light, thereby matching the Gr-VOLET, it must emit 324 cd m −2 , requiring an applied voltage of 3.62 V. This indicates that 0.2 V of the V SD (3.82 V) for the Gr-VOLET was dropped through its embedded transistor element, leading to a considerably reduced PPC of only 5.2%. This is much lower than that (6.2%) of the previous CNT-VOLET and the levels (>50%) for a TFT-OLED and a MIS-OLET ( Table 2) [19,32].

Charge injection process at SLG sources
At this point, our investigation turns to the hole injection mechanism at the interface between the SY channel layer and the SLG source. To be injected across the interface (SLG/SY), the holes must overcome the barrier height at the interface either via thermionic emission or tunneling processes [63][64][65][66][67][68]. Figure 9(a) shows examples of Fowler-Nordheim (F-N) curves [63][64][65][66][67] for the Gr-VOLET at various V G s during upward changes in V G . All of the curves show two different hole injection processes with transition voltages (V T s), at which the injection mechanism changes to tunneling from Schottky thermionic emission [63][64][65][66][67][68]. In the figure, it is interesting to note that V G affects both the Schottky thermionic emission and tunneling, indicating that V T strongly depends on V G . It is also noteworthy that because EL emission of the Gr-VOLETs occurs when V SD > V onset (V onset > V T ), the main    hole injection process for EL emission is the tunneling injection in the Gr-VOLETs. According to the modified tunneling current model [70], the tunneling current density (J) of a single charge carrier through a triangular barrier at a polymer/metal junction is related to the potential barrier height (Φ) and the temperature (T), where k B is the Boltzmann constant and P i are parameters related to Φ. This relationship allows the F-N plots to be analyzed, and the potential barrier heights Φ at the SLG/SY interface between the Fermi level of SLG and the highest occupied molecular orbital (HOMO) level of the SY channel layer (~5.3 eV) [22] to be obtained (Figure 9(b)). As shown in the figure, the SLG/SY interface exhibited strong gate-bias-induced Φ modulation (ΔΦ) along the direction normal to the SLG/SY interface; that is, ΔΦ at V G = ±40 V was approximately 0.11 eV, leading to the effective modulation of the device performance of the Gr-VOLET tested here. Note that tunneling at the SLG/SY interface is the major process of hole injection, being responsible for the radiative recombinations of electron-hole pairs. Thus, the analysis of the tunneling process described above provides clear evidence that the Gr-VOLET operates based on vertical barrier height modulation along the direction normal to the SLG source surface (i.e., parallel to the direction of gate field), in contrast to the CNT-VOLET devices based on lateral modulation of Schottky barrier height along the horizontal direction on the CNT source surface (i.e., perpendicular to the direction of gate field) [31,32], and differently from conventional graphene-based barristors that operate via modulation of the Schottky thermionic injection [69,70].
The observations above show the working principle of the Gr-VOLET, as illustrated in the energy-level diagrams in Figure 10. At a given V SD , a positive gate voltage induces an upward shift of the SLG Fermi level in a direction that increases the Φ, resulting in reduced hole tunneling injections into the HOMO level of the channel layer (SY). In contrast, a negative gate voltage induces a downward shift of the SLG Fermi level, decreasing Φ significantly (enhancing tunneling) and hence allowing increased hole injections and improved EL performance. Thus, together with the band-bending effect [31], the main operating mechanism of the Gr-VOLET is energy band matching, with charge balance achieved even without a HIL through gate voltage-induced modulation of the hole carrier tunneling injection at the p-type doped SLG source with FeCl 3 .
In addition, notable instances of hysteresis were clearly observed, as shown above. Thus, bistable-like switching operations of a Gr-VOLET can allow novel applications for simple and inexpensive driving schemes together with low power consumption. However, this hysteresis effect may become an issue when attempting to realize high-quality grayscale outcomes and should be carefully, therefore, controlled when preparing the dielectric layer.

Inkjet-printing arrays of Gr-VOLET micro-pixels
Next, we turn our attention to a micro-pixel fabrication process for the Gr-VOLET using the inkjet-printing technique, as commonly used in solutionprocessable OLEDs [39,71,72]. Here, the inkjet technique used is based on the deposition of a small solvent drop onto an insulator layer, which can be easily redissolved and preferentially redeposited at the edge of the sessile drop (the contact line of the solvent drop), resulting in the formation of a via-hole with the shape of a crater, that is inkjet-etching [39].
To investigate the in situ formation of micro Gr-VOLET pixels created by means of inkjet-etching, an insulating polymer of poly(4-vinylpyridine) (P4VP) was introduced as a via-forming material, as P4VP is a hydrophilic polymer that dissolves in dimethyl formamide (DMF), toluene, chloroform, in lower alcohols, and in aqueous mineralic acids [71]. To fabricate a via-hole forming layer, a solution of P4VP with isopropanol (IPA) was spin-coated on top of the light-emitting channel layer of SY pre-coated onto a Gr-VOLET substrate (VOLET substrate/SLG/ SY/P4VP). For micro-patterning, an etching solvent of chloroform for P4VP was inkjet-printed on top of the SY/P4VP layers (Figure 11(a)). This inkjet-printed solvent drop of chloroform can dissolve the P4VP layer, and the capillary flow of the solvent pushes the dissolved P4VP from the center to the contact line of droplet due to the coffee ring effect [39,[72][73][74], resulting the formation of the via-hole through the P4VP layer. Thus, after the deposition of even a single solvent droplet (~150 pL per droplet) on a 30-nm-thick P4VP film, the P4VP polymers are removed from the printed position and completely etched, forming via-holes through the P4VP layer, of which the inner and outer diameters are ~90 μm and ~120 μm, respectively, and finally uncovering the surface of the underlying SY layer. These P4VP via-holes on the light-emitting SY layer act as micro-patterned pixel openings  for the light-emitting active areas of the Gr-VOLETs. Then, to complete the device of an array of micro Gr-VOLETs, the CsF/Al/Ag cathode is deposited following the procedure described in Section 3.1. Figure 11(a) also presents the switching behavior of EL light emissions from the array of micro Gr-VOLET pixels for two different gate voltages, V G s, at a fixed V SD of 4.0 V. The photographic images show that only the isolated micro-patterned micro-pixel areas in contact with the SY layer of the Gr-VOLET pixels can emit EL light with a width of 85 μm, similar to the dimensions of the via-hole opening (90 μm). Note that the different solubility characteristics between the P4VP and SY polymers prevents any solvent erosion of the SY layer, as expected. As also clearly shown in the figure, the EL light emission from the micro Gr-VOLET pixels with a fixed droplet spacing of ~140 μm (~180 dpi) is highly bright (on-state) and dark (off-state) over the entire active area of the pixels for negative (−40 V) and positive values of V G (+40 V), respectively. Hence, V G clearly controls the radiative recombination process in the emissive pixel areas.
Next, the output characteristics of the inkjet-printed Gr-VOLET pixels were investigated. As shown in Figure 11(b), the J SD -V SD and L-V SD characteristics of the inkjet-printed Gr-VOLET pixels present features similar to those of the spin-coated Gr-VOLET (Figure 7). For example, at V G = −40 V, the luminance reaches L ~ 1200 cd m −2 with a current efficiency of ~5.0 cd/A at V SD = 6.0 V (V onset = 3.0 V). In contrast, at V G = +40 V, J SD and L are greatly suppressed due to the switching off effect of the injection of holes from the SLG source, resulting in a peak on/off ratio of L of approximately 10 3 at V G = ±40 V. Figure 11(c) presents F-N plots of the micro Gr-VOLET pixels for various V G s. As also shown in the figure, the negative slopes of the F-N plots clearly confirm that tunneling injection process is the major charge injection process for the light emission, being responsible for radiative recombinations of electron-hole pairs in the inkjet-printed Gr-VOLET pixels.

Conclusions
In summary, herein, graphene-based VOLETs have been explored, consisting of a nonporous, homogeneous, and p-doped SLG source with FeCl 3 , an Al drain, and an emissive channel layer for efficient switching of the device performance using the gate voltage. Initially, we investigated transferred CVD SLG, which was used as the source electrode. It was found that the SLG used here was unintended p-doped SLG, exhibiting a Dirac point energy of ~4.9 eV and a work function of 5.2 eV with a shift of the Fermi level from the Dirac point and high hole mobility. It is shown that the high device performance capabilities of SLG-based VOLETs were mainly due to the p-doping effects, which were estimated quantitatively and analyzed based on the energy levels of the SLGs. It is also shown that low-drain-voltage operations and increased brightness with a high luminance on/off ratio (~10 4 ) can be achieved even at high brightness for the Gr-VOLET without any HIL. Moreover, the current efficiency and effective aperture ratio of the Gr-VOLET were at least 150% higher than those of a control OLED, with low parasitic power consumption of 5%. These significant improvements of the device performance can be attributed to the gate-bias-induced modulation of the hole tunneling injection from the FeCl 3 -doped SLG source into the emissive channel layer. Further, the feasibility of the simple fabrication process of micro Gr-VOLET pixels, that is, the inkjet-printing technique, was also proven.
The foregoing results demonstrate the notable device performance of the Gr-VOLET with graphene source, indicating considerable promise with respect to the development of high-performance VOLETs. The advances afforded by the Gr-VOLET with reliable switching performance, even at high luminance levels, clearly show its effective light-emitting transistor functionality and make it a feasible candidate for development of new voltage-driving light-emitting devices and/or highly integrated organic optoelectronics. Finally, it will be possible to apply advanced material layers to these Gr-VOLETs, which could lead to more efficient devices that operate even at low voltage levels, enabling the development of inexpensive, large-area, fast, and high-performance AM displays. Further improvements and characterizations are in progress and will be published elsewhere.