High-Entropy Ceramics

High-entropy ceramics is an emerging class of high-entropy materials with properties superior to conventional ceramics. Recent research has been focused on the development of new high-entropy ceramic compositions. High-entropy oxides, carbides, borides, silicides, and boron carbides had been reported with superior mechanical, oxidation, corrosion, and wear properties. The research work on the processing and characterization of bulk high-entropy ceramics and coating systems has been summarized in this chapter. The composition design, structure, chemistry, composite processing of bulk high-entropy ceramics, and evolution of microstructure and properties are reported. The literature on the deposition of high-entropy ceramic coating and the influence of coating parameters have been discussed to produce high-entropy ceramic coatings with superior mechanical, oxidation, and wear properties.


Introduction
The concept of high-entropy alloy (HEA), an alloy with five or more constituents with a concentration between 5 and 35%, has triggered extensive research to develop new metallic and ceramic high-entropy materials. Like HEAs, high-entropy ceramics (HECs) consist of multicomponent ceramic oxides, borides, and nitrides. The HECs exhibit homogeneous crystalline single-phase despite the complex structure of ceramic compounds and offer superior properties over the constituents and conventional ceramics. The development of high-entropy ceramic coatings is an important route to design new and novel high-entropy ceramic materials with superior properties for practical applications. In this chapter, the recent work on HECs is summarized in the following two sections: bulk HECs and HEC coatings. Bulk HEC section is focused on the processing and the evolution of significantly enhanced mechanical properties of borides, oxides, and carbide ceramics and composites. Moreover, the potential of HECs in thermal-electrical, tribological, and high temperature applications are discussed. In the section on high-entropy coatings, recently reported researches on different HEC coating techniques and the properties of the HEC coatings have been summarized.

Fabrication routes
The fabrication of HEAs can be achieved through solid and liquid state routes. The processing of bulk HECs is preferred in solid state due to the high melting points of ceramics. The solid-state processing includes high energy ball milling, conventional solid state sintering, self-propagating high temperature synthesis (SHS), and spark plasma sintering (SPS) under the combined effect of heating using electric current and pressure. The SPS is a rapid and facile method to produce nearly dense components and suitable for sintering of high-entropy ceramics. Typically, the precursor ceramic powders are mixed and filled into a graphite die and rapidly sintered under high vacuum, pulsed direct electrical current, and uniaxial pressure.
Different types of the ceramic precursors have been used to fabricate HECs. The most commonly used precursors are commercial ceramic powders. The ceramic powders are mixed in desired stoichiometric ratio and homogenized using ball milling followed by spark plasma sintering to a target temperature and uniaxial pressure. The synthesis of high-entropy ceramic powders has been investigated as well. The precursor ceramic powders can be pre-synthesized via thermal reduction (TR) where metal oxide powders are used as reactants (Figure 1). The advantages of using oxide powders as raw materials include reducing the cost of the starting materials and possibilities of producing high purity ceramic powders with controlled grain size. Feng et al. [1] used metallic oxides and carbon black powder as starting material to produce high-entropy (Hf, Zr, Ti, Ta, Nb)C powder. The carbothermal reduction of oxide ceramics was completed at 1873 K under vacuum in 1 hour. Subsequent solid solution formation was achieved at a higher temperature of 2273 K, demonstrating a single-phase rocksalt structure of the solid solution. Ye et al. [2] reported the synthesis of high-entropy (Zr 0.25 Ta 0. 25 Nb 0.25 Ti 0.25 )C powders of a single-phase rocksalt crystal structure by carbothermal reduction of metal oxides and graphite.
Liu et al. [3] demonstrated the synthesis of high-entropy (Hf 0.2 Zr 0.2 Ta 0.2 Nb 0.2 Ti 0.2 )B 2 powders with single-phase hexagonal structure through borothermal reduction from metal oxides and amorphous boron powders at 1973 K under argon atmosphere. The synthesized high-entropy metal diboride powders showed a fine particle size of 310 nm. Instead of boron, Zhang et al. [4] used the combination of B 4 C, graphite, and metal oxides to synthesize (Hf 0. 2  )C by employing different methods using commercial carbide powders and thermally reduced carbide powders and in-situ fabrication process from elemental powders [5]. All three compositions revealed single-phase face-centered cubic (FCC) structure according to X-ray diffraction (XRD) patterns. The comparison of the High-Entropy Ceramics DOI: http://dx.doi.org /10.5772/intechopen.89527 three methods suggested the microstructure inhomogeneity in case of elemental powders and TR approach.

High-entropy oxides (HEOs)
The first high-entropy ceramic was reported by Rost et al. [6], on the production of entropy stabilized metal oxides with rocksalt crystal structure, synthesized from equimolar CoO, CuO, MgO, NiO, and ZnO in a tube furnace at temperatures above 850°C. Homogenous distribution of the cations in the crystal structure was observed. The system showed a reversible transformation between the highentropy solid solution and multicomponent oxide mixture. Later on, detailed investigation using extended X-ray absorption fine structure (EXAFS) was performed to investigate the localize structure of the aforementioned high-entropy oxide [7], demonstrating that the anion lattice (O sublattice) has the most distortion to accommodate the size mismatch in the cation lattice (metal sublattice). The phase stability, as a result of configurational entropy, of the same HEO system was studied by Anand et al. [8].
The entropy stabilized oxide ((Mg, Ni, Co, Cu, Zn)O with colossal dielectric constant was discovered by Bérardan et al. [9]. With a Li + ionic conductivity of >10 −3 S/cm, which is much higher compared to lithium phosphorous oxynitride (LiPON) solid electrolyte (2 × 10 −6 S/cm) [10], the produced high-entropy oxide was suggested to be an excellent substituent as superionic conductors for Li + and Na + . The potential of high-entropy oxide in the lithium battery has been reported by Sarkar et al. [11] with improved storage capacity retention and cycling stability.
Jiang et al. [12] synthesized high-entropy perovskite oxides from multiple ABO 3 perovskite oxides. Djenadic et al. [13] utilized nebulized spray pyrolysis (NSP) to synthesize single-phase rare earth oxide powders from seven equiatomic rare earth oxides. In the REO system, the importance of selecting the starting component in the reported multicomponent oxide system was highlighted, with cerium (Ce 4+ ) addition being confirmed to improve the formation of single-phase solid solution. Gild et al. [14] fabricated high-entropy fluorite oxides from five fluorite oxides via high-energy ball milling and SPS, followed by various annealing treatments. Most of the fabricated HEOs revealed as nearly fully dense pellets with single-phase Fm-3 m crystal structure. Phonon scattering effect in the HEO system resulted in low thermal conductivity, making the synthesized HEOs desirable for thermal insulation applications.

High-entropy borides (HEBs)
The high-entropy borides are designed and fabricated from transition metal diborides, HfB 2 , ZrB 2 , TaB 2 , etc., aiming at developing a new class of ultrahigh temperature metal diboride materials with superior mechanical properties over conventional diborides.
Gild et al. [15] (Figure 2) as the parent metal diborides, with alternating hexagonal metal cations net and rigid boron net in the high-entropy structure. The authors reported that in case of using W 2 B 5 in the starting precursors, single-phase solid solution was not successfully formed. Notably, W 2 B 5 has a different crystal structure with other utilized metal borides, as well as limited solubility in other borides, which could  [16]. In the unique layered hexagonal lattice structure shown in Figure 2, the metal layer and 2D boron layer contain metallic bonds and covalent bonds, respectively, while both ionic and covalent bond were found between the two hexagonal layers. The high stability of the studied HEBs is contributed by strong boron-boron bond and metal-boron bond. Density-functional theory (DFT) calculations suggested negligible solid solution strengthening effect in elastic modulus, showing similar value with elastic modulus calculated by the mixing rule.
Tallarita et al. [17] synthesized bulk HEB (Hf 0.2 Mo 0.2 Ta 0.2 Nb 0.2 Ti 0.2 )B 2 by selfpropagating high-temperature synthesis (SHS) from elemental metal and boron powders, followed by SPS at 2223 K. High fraction of high-entropy phase with hexagonal (space group P6/mmm) was obtained after the SHS process, along with minor amount of binary diborides and metal oxides. The SHS powders showed good sinterability with a relative density of 92.5% in the SPS product. The sintered HEB exhibits a single-phase hexagonal crystal structure which is similar to the hexagonal AlB 2 structure reported by Gild et al. [15], with improved hardness (22.5 ± 1.7 GPa) and oxidation resistance. The authors mentioned that the single-phase structure could not be obtained when performing one-step reactive SPS process with the same reactants.
Based on the developed HEB system, Zhang et al. [18] adopted borothermal reduction process to synthesize high-entropy borides from metal oxides and amorphous boron powder, aiming at producing ultra-fine HEB powder with improved sinterability. The obtained HEB powders (Hf 0.2 Zr 0.2 Ta 0.2 Cr 0.2 Ti 0.2 )B 2 , (Hf 0.2 Mo 0.2 Zr 0.2 Nb 0.2 Ti 0.2 )B 2 , and (Hf 0.2 Mo 0.2 Ta 0.2 Nb 0.2 Ti 0.2 )B 2 showed an average particle size smaller than 1 μm and led to final relative densities greater than 95% in the SPS products. The sintered HEBs showed ultrahigh hardness values of 28.3, 26.3, and 25.9 GPa, respectively. Compared to the HEBs with same compositions sintered from −325 mesh diboride powders by Gild et al. [15] (about 22 GPa), these HEBs have improved hardness properties as a result of utilization of ultrafine starting particles in SPS.

High-entropy carbides
The first reported high-entropy carbides were synthesized from transition metal carbides HfC, TaC, ZrC, NbC, and TiC by Castle et al. [19]. Four-component metal carbides were mixed in equiatomic ratio using high-energy ball milling and sintered in SPS with a maximum sintering temperature of 2573 K to form high-entropy (Hf-Ta-Zr-Ti)C and (Hf-Ta-Zr-Nb)C ultra-high temperature carbides. A singlephase solid solution with a rocksalt crystal structure was formed. More complete inter-diffusion in the formation of single-phase solid solution was found in the (Hf-Ta-Zr-Nb)C than (Hf-Ta-Zr-Ti)C system. As the atomic radius of Ti, as well as the lattice parameter of TiC is the smallest among the five starting components, the effect of lattice mismatch among the starting metal carbides on formability of high-entropy solid solution was highlighted. By considering the metal atomic radii, melting points and vacancy formation energy of the carbides, it is believed that TaC, which has the lowest metal vacancy formation energy, acted as the host lattice during the diffusion, while other metal atoms migrate into TaC lattice and occupy the cation positions. The nanoindentation of the fabricated high-entropy (Hf-Ta-Zr-Nb) C shows a hardness of 36.1 ± 1.6 GPa, which is 30% higher than the theoretical value calculated from the rule of mixture. Low thermal conductivity was observed in the reported SPS high-entropy carbides. Further investigation on the microstructure, atomic structure, and localized chemical disorder of the fabricated four-component high-entropy (Hf-Ta-Zr-Nb)C was reported by Dusza et al. [20]. Homogeneity of the chemical composition in both micro-and nanoscale was proved by various experimental approaches including scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron backscattered diffraction (EBSD).
The low thermal conductivity and diffusivity behavior were observed by Yan et al. [21] in the five-component high-entropy (Hf 0.2 Zr 0.2 Ta 0.2 Nb 0.2 Ti 0.2 )C ceramic. The high-entropy carbide was synthesized in SPS at 2273 K and displayed rocksalt crystal structure with the metal atoms occupying the cation positions, while carbon occupied the anion positions in the lattice. The measured thermal diffusivity is reported to be lower than monocarbides and even some of the binary carbides. The increased number of principal elements in the structure led to lattice distortion, mainly through the carbon sublattice, which consequently caused severe phonon scattering. The same high-entropy carbide (Hf 0.2 Zr 0.2 Ta 0.2 Nb 0.2 Ti 0.2 )C in powder form was synthesized by Zhou et al. [22] via pressureless sintering in SPS.
Entropy-forming-ability (EFA), the first systematic criterion to determine relative propensity of a multicomponent (metal carbide) system to form a high-entropy single-phase crystal structure was introduced by Sarker et al. [23], published on Nature Communication in November 2018. A total of 56 five-component systems from 12 metal carbides (Hf, Nb, Mo, Ta, Ti, V, W, and Zr) were investigated in the work by evaluating the energy distribution spectra of the structures that were generated by the AFLOW-POCC (automatic FLOW partial occupation) [24] algorithm. A narrow spectrum suggests low energy barrier to introduce more configurational disorder, thereby displays high EFA value. The calculation results were verified by synthesizing nine from the 56 compositions in SPS at 2473 K and comparing the experimental and calculation results. The phase identification in Figure 3 suggested that six compositions MoNbTaVWC 5 , HfNbTaTiZrC 5 , HfNbTaTiVC 5 , NbTaTiVWC 5 , HfNbTaTiWC 5 , and HfTaTiWZrC 5 that have higher EFA values than the rest three compositions reveals single-phase rocksalt crystal structure after SPS, while secondary phases were observed in compositions HfMoTaWZrC 5 , HfMoTiWZrC 5 , and HfMoVWZrC 5 with low EFA values.
The ab initio entropy descriptor invented by Sarker et al. [23] provides a new understanding of the formation of single-phase high-entropy materials and offers a systematic guide for researchers to design high-entropy carbides. Group IV and V carbides are known to have nearly complete mutual solubility; therefore, the formation of single-phase solid solution is relatively probable, attributed to enthalpy stabilization. Meanwhile, the incorporation of carbides with different crystal structures was commonly understood to impede the formation of the highentropy phase because of the mismatch of lattice structure. It was observed that the addition of group VI elements (Cr, Mo, and W) is likely to reduce the chance of forming a single phase, as group VI metal monocarbides are generally demonstrated as non-cubic structure at room temperature. However, the MoNbTaVWC 5 composition that simultaneously contains tungsten carbide (W 2 C) and molybdenum carbide (Mo 2 C), which exhibit orthorhombic and hexagonal structure, respectively, shows the highest EFA value among the 56 analyzed compositions and demonstrates single-phase FCC structure after SPS. The mechanical properties measured by experiments showed that the Vickers hardness and elastic modulus have significant enhancement compared to the predicted value from the rule of mixture, contributed by mass disorder in the structure and solid solution hardening. Following the work of the pioneers, a systematic study focused on the phase stability and mechanical properties of high-entropy carbides synthesized from group IV, V, and VI metal carbides [25] was carried out. It was verified that carbide system that was stated to have EFA value lower than 45 cannot form single-phase solid solution via SPS.

Other high-entropy ceramics-silicide, borocarbide, sulfide, etc.
To date, the work of bulk high-entropy ceramics is mostly focused on oxide, boride, and carbide, and several other classes of high-entropy materials like silicide, sulfide, and borocarbide have been reported. DOI: http://dx.doi.org /10.5772/intechopen.89527 The synthesis of high-entropy silicide was reported by Gild et al. [26] and Qin et al. [27]. Gild utilized SPS and sintered high-entropy silicide (Mo 0.2 Nb 0.2 Ta 0.2 Ti 0.2 W 0.2 )Si 2 at 1923 K, resulting in a single hexagonal C40 crystal structure (space group P6 2 22). Hardness enhancement over the constituent silicide and low thermal conductivity similar to high-entropy carbide was reported. On the other hand, Qin produced (Ti 0.2 Zr 0.2 Nb 0.2 Mo 0.2 W 0.2 ) Si 2 from compositional elemental powders, leading to the formation of a hexagonal structure highentropy silicide, with the same space group P6 2 22. Zhang et al. [28] developed a data-driven model to design high-entropy sulfides for thermoelectric applications. Compositions Cu 5 SnMgGeZnS 9 and Cu 3 SnMgInZnS 7 were picked to be synthesized via high energy ball milling and SPS. Single-phase high-entropy sulfide with homogeneous distribution of the elements is reported. By increasing the Sn content in the Cu 5 SnMgGeZnS 9 system, a figure of merit zT value of 0.58 at 773 K was obtained.
By adding B 4 C into the four-component HEC (HfMoTaTi)C, Zhang et al. [29] studied the capability of a high-entropy carbide system on accommodating one more nonmetal element, boron. The quaternary (HfMoTaTi)C contains FCC structures, while the addition of B 4 C induced the formation of a small fraction of hexagonal phase. Similar with the diffusion process reported by Castle et al. [19], TaC is suggested to act as the host lattice in the borocarbide system. The effect of employing different particle sizes for host carbide TaC and other constituent carbides on the phase formation and mechanical properties of the HEC composites was discussed. A high-entropy B 4 (HfMo 2 TaTi)C ceramic exhibiting hexagonal structure, with alternating metal and nonmetal layers in the lattice, was found when SiC whiskers are introduced to the borocarbide system [30]. The hexagonal HEC solid solution shows great improvement of the mechanical property with an ultrahigh hardness of 35 GPa.

Sputtering
Sputtering is a physical vapor deposition (PVD) technique where a solid surface (target) is bombarded with accelerated charged ions (Ar + ) resulting into backward scattering of surface atoms of solid. Sputtering technique is used to deposit thin coatings. There are several sputtering systems employed for deposition of thin coatings, such as direct current (DC) magnetron sputtering and radio frequency (rf) sputtering being the widely used techniques. DC-magnetron sputtering is a low pressure sputtering system for metal deposition and electrically conductive target coating materials. The magnetic field from magnetron lowers the sputtering gas pressure and increases the deposition rate of sputtered coatings. On the other hand, when metallic target is replaced by an insulator target, the plasma discharge cannot be maintained due to buildup of surface charge of positive ions on the target. Thus, an rf power supply is used instead of dc voltage power supply to sustain the glow discharge on an insulator target [31]. Another advantage of using sputtering for thin coating deposition is the use of reactive gases, substrate bias, and substrate temperature to vary the composition and properties of deposited coatings. In reactive sputtering, different reactive gases, such as oxygen, nitrogen, and CH 4 can be used to deposit ceramic coatings of oxides, nitrides, and carbides, respectively [32][33][34]. Furthermore, deposition of carbonitride and oxynitride coatings can be Engineering Steels and High Entropy-Alloys achieved by using a mixture of CH 4 + N 2 and O 2 + N 2 , respectively [35,36]. In reactive sputtering, a mixture of Ar and reactive gas (5-70%) is used for sputtering. The increasing bias between the target and substrate can affect the chemical composite, microstructure, and mechanical properties of the coating by giving compact coating structures. Lastly, substrate temperature can be varied in reactive sputtering to enhance the ion mobility and the interaction between the deposited ions, which can affect the microstructure, composition, and the properties of the coating. The following section will be used to highlight the use of reactive sputtering to deposit high-entropy nitride, carbide, and oxide ceramic coatings.

High-entropy nitride coatings
High-entropy alloys based on multi-principle elements make it possible to design various nitride coatings. The use of nitride forming multi-principle elements can enhance the physical and mechanical properties that are not achievable in the conventional binary-and ternary-nitride coatings [37]. The high-entropy nitride coatings form amorphous and/or solid solution with face-centered cubic (FCC) structure. The severe lattice distortion and solid solution hardening help in developing high strength nitride coatings for various applications that require wear resistance, corrosion resistance, diffusion barrier, electrical resistivity, biocompatibility or light reflectivity [38]. The versatile sputtering deposition can be used to vary the N 2 flow, substrate temperature, and substrate bias to obtain nitride coatings with good physical, chemical, and mechanical properties, respectively.

Effect of N 2 flow rate
The high-entropy nitride (HEN) coatings developed by DC-magnetron sputtering were reported by research group of Yeh et al. using targets of FeCoNiCrCuAlMn, FeCoNiCrCuAl, AlxCoCrCuFeNi (x: 0.5 and 2), and AlCrNiSiTi [39]. In all the cases, the resulting HEN coatings showed formation of FCC solid solution at low N 2 flow rate (R N ) and became amorphous at higher N 2 flow rate (R N ) due to severe lattice distortion and presence of weak nitride forming elements, such as Al and Si, where R N = (N 2 /(Ar + N 2 )). Following this work, Lai et al. developed (AlCrTaTiZr)N HEN coating, where the coating structure changed from amorphous phase metallic coating to FCC solid solution HEN with increasing N 2 flow rate [32]. The sputtering rate decreased from 35 nm/min (R N = 0%) to 15 nm/min (R N = 60%) with increasing N 2 flow ratio (R N ). The decreasing sputtering rate was attributed to a lower sputtering yield due to nitrogen absorption, nitridation of the target, and/or decreasing sputtering efficiency of reactive gases with increasing R N as compared to argon ions. The increasing R N ratio resulted in increasing the hardness from 9 GPa (0% R N ) to 32 GPa (15% R N ). In another study, Tsai et al. developed octonary principal element (AlMoNbSiTaTiVZr)N HEN coatings using magnetron sputtering with nitrogen flow ratio from 0 to 70% R N [40]. The deposition rate decreased from 31 nm/min (R N = 0%) to 8.3 nm/ min (R N = 67%) with increasing nitrogen flow ratio. In contrast, the hardness values increased from 13.5 GPa (0% R N ) to 37 GPa (50% R N ). Such high increase in hardness has been attributed to the stronger bonding between N and target elements. The coating morphology of (AlMoNbSiTaTiVZr)N HEN changed from coarser grain-like morphology (R N = 0%; grain size: 30-100 nm) to reduced grain morphology (R N = 11%; grain size: 10 nm) and then to rougher morphology (R N = 33%). Similarly, the cross-section of the coating changed from a glass-like featureless morphology to fine columnar structure with increasing nitrogen flow ratio from R N = 0-11% to R N = 33%, respectively. Similarly, Xing et al. developed (NbTiAlSiZr)N HEN coating using RF sputtering with increasing nitrogen flow rate from 10 to 50% [41]. The coating thickness and deposition rate were found to decrease with increasing nitrogen flow rate, as shown in Figure 4.
The cross-section of (NbTiAlSiZr)N HEN coatings is shown in Figure 5. The coating thickness was found to decrease from 298.8 to 200 nm with increasing nitrogen flow rate. Furthermore, the hardness was found to increase from 9.5 to 12 GPa with the increasing nitrogen flow rate of R N = 10% to R N = 50%, respectively.
In another work, Chang developed a duodenary (TiVCrZrNbMoHfTaWAlSi)N HEN coatings with R N from 0 to 50% using DC magnetron sputtering and similar structural evolution from amorphous to FCC solid solution was observed with increasing R N [42]. The hardness after reactive sputtering increased from 13 GPa (0% R N ) to 34.8 GPa (50% R N ).

Effect of substrate bias
The changing substrate bias during coating deposition effects the chemical composition, microstructure, and mechanical properties of coatings. Chang et al. studied the effect of substrate bias from 0 to −200 V on (AlCrMoSiTi)N HEN coatings developed by DC magnetron sputtering at 50% R N [43]. The coating showed FCC solid solution structure even though it contained immiscible nitrides, such as AlN, TiN, and Si 3 N 4 . However, the lattice parameter increased from 4.15 to 4.25 Å, and the grain size decreased from 16.8 to 3.3 nm with increasing substrate bias. This change in the lattice parameter was attributed to increase in adatom mobility, and the decreasing grain was due to increase in nucleation rate at ion-induced surface defects with changing substrate bias. The increasing substrate bias had a small effect on the hardness properties from 25 GPa with no bias to highest hardness of 32 GPa observed at −100 V bias. Following these findings, Huang et al. studied the effect of increasing substrate bias from 0 to −160 V on (AlCrNbSiTiV)N HEN coating using RF magnetron sputtering with R N and substrate temperature kept constant at 28% and 300°C, respectively [44]. The XRD analysis of HEN coatings

Effect of substrate temperature
The growth of film during the deposition in sputtering system is dependent on the mobility of ions to the substrate. The substrate temperature can play a key role toward ion mobility and diffusion between deposited ions that affect the microstructure, composition, and properties of the coatings. Liang et al. investigated the effect of substrate temperature on the deposition of (TiVCrZrHf)N HEN coating using RF magnetron sputtering from room temperature (RT; 25°C) to 450°C with a fixed 4% R N and −100 V substrate bias [49]. The XRD analysis showed formation of FCC solid solution without any significant phase separation at all substrate temperatures. However, grain size decreased from 10.7 nm at RT to 8 nm at 250°C and then increased to 9.7 nm at 450°C. The surface morphology of (TiVCrZrHf)N HEN coating became more smooth and dense with increasing substrate temperature. The cross-section morphology changed from an amorphous phase at coatingsubstrate interface to FCC phase toward coating surface. This phenomenon was reported to be due to higher stresses generated in the initial coating deposition and the greater lattice mismatch of 19% between the HEN coating and silicon substrate. The hardness of the coating increased from 30 to 48 GPa with increasing substrate

Surface and cross-section SEM micrographs of (NbTiAlSiZr)N HEN coatings at various R N : (a) R N = 10%, (b) R N = 20%, (c) R N = 30%, (d) R N = 40%, and (e) R N = 50% [41].
High-Entropy Ceramics DOI: http://dx.doi.org /10.5772/intechopen.89527 temperature from RT to 450°C. The high hardness with increasing substrate temperature was attributed to the higher mobility of deposited atoms and reduction of growth void leading to denser coatings. Similar studies on the effect of substrate temperature on structure and enhancement of mechanical properties were studied on the deposition of (AlCrNbSiTiV)N [50][51][52] and (TiVCrAlZr)N [53] HEN coating.

High-entropy carbide coatings
Similar to high-entropy nitride coatings, high-entropy carbide coatings have been developed to obtain coatings for tribological and biomedical applications.

Effect of CH 4 flow rate ratio
Braic et al. performed the initial studies on development of high-entropy carbide coatings for tribological and biomedical applications. Their research group deposited (TiAlCrNbY)C high-entropy carbide coatings from co-sputtering of elemental targets using DC-magnetron sputtering with different CH 4 flow ratios (R C ), and at constant substrate temperature and substrate bias of 400°C and −100 V, respectively [54], where CH 4 flow ratio is given by: R C = CH 4 /(CH 4 + Ar). The XRD data showed a change of structure from nanostructured broad FCC phase (0% R C ) to a single FCC carbide phase (10 and 17% R C ) and then to amorphous phase at higher carbon concentration (26 and 33% R C ). The coating morphology changed from slightly higher surface roughness of 7 nm (0% R C ) to fine grained surface roughness of 2 nm (33% R C ) with increasing CH 4 flow ratio. The hardness values increased from 8.2 GPa (0% R C ) to 22.6 GPa (26% R C ). Similarly, Braic et al. studied the effect of CH 4 flow ratio on (TiZrNbHfTa)C high-entropy carbide coating with elemental target co-sputtering using DC-magnetron sputtering on Ti6Al4V alloy substrate [55]. However, in this work, formation of only FCC solid solution was observed at R C of 13 and 35% with hardness values of 22.4 and 32.1 GPa, respectively. Similar to earlier work, the surface roughness and crystallite size decreased, while the hardness increased with increasing CH 4 flow ratio. In another work, Braic et al. deposited (CuSiTiYZr)C high-entropy carbide coating using elements with large atomic radii differences and reported the effect of different CH 4 flow ratios on the structural and mechanical properties. In all the deposited high-entropy carbide coatings, the XRD showed the formation of amorphous phase irrespective of the amount of carbon. The higher lattice distortion in the high-entropy carbide coatings resulted in hardness values of 20.7 GPa (25% R C ), 27.2 GPa (35% R C ), and 29.5 GPa (50% R C ). Thus, proving the work of Zhang et al. [56] and Guo et al. [57] in the case of high-entropy alloys, a solid solution is formed when the constituent elements have a close atomic radius. Similarly, Jhong et al. developed (CrNbSiTiZr)C highentropy carbide coatings and studied the effect of increasing CH 4 flow ratio on the structural evolution and mechanical properties [58]. In this system, the structure of high-entropy carbide coating changed from FCC solid solution phase at lower R C of 3-10% to amorphous phase at higher R C of 15-20%. Such structural change from FCC to amorphous phase resulted in reducing the hardness from 32.8 to 22.3 GPa.

Effect of substrate temperature
Braic et al. studied the effect of substrate temperature on the deposition of (CrCuNbTiY)C high-entropy carbide coating with DC co-sputtering of elemental targets with a constant substrate bias and two different CH 4 flow ratios. The substrate temperature was increased from 80 to 650°C, and its effect on the structural Engineering Steels and High Entropy-Alloys evolution and mechanical properties were reported. The high-entropy carbide coating with lower carbon concentration showed formation of FCC structures at all the deposition temperatures, while the coating with higher carbon concentration showed poor crystallinity and approaching toward an amorphous phase. The grain size and surface roughness increased with increasing substrate temperature in both coatings. In contrast, the hardness values increased with increasing substrate temperature from 13 GPa (80°C substrate temperature) to 30 GPa (650°C).

High-entropy oxide coatings
Most of the research on high-entropy ceramic coatings has been focused on high-entropy nitrides and carbide coatings. Few research works have been reported on high-entropy oxide (HEO) coatings. Initial work on HEO coatings was reported by Chen and Wong, where (Al x CoCrCuFeNi)O (x: 0.5, 1 or 2) HEO coating by RF magnetron sputtering using different oxygen flow ratios (O 2 /Ar) was developed, and the resulting structural evolution was characterized [59]. The structural evolution was observed to change from FCC, FCC + BCC or BCC (depending on the amount of Al content) to cubic spinal oxides with increasing oxygen flow ratio. The hardness increased from 5-8 GPa to 13-22.6 GPa with increasing O 2 flow ratio. In a subsequent work, Lin et al. used strong oxide forming elements to develop (AlCrTaTiZr)O HEO coating using DC magnetron sputtering with increasing O 2 flow ratio (R O = O 2 /(O 2 + Ar)) from 0 to 50%. The XRD analysis revealed a metastable amorphous structure irrespective of the O 2 flow ratio [33]. The tendency of forming amorphous phases at different O 2 flow ratios has been attributed to the large difference in the lattice parameters of oxides from each constituent element of Al, Cr, Ta, Ti, and Zr. The hardness values were reported to be in the range of 8-13 GPa. However, the hardness values increased in the range of 20-22 GPa after annealing at 900°C. The reported hardness values of HEO coatings were relatively higher than most of the reported oxide films, such as Al 2 O 3 (10 GPa) [60], TiO 2 (18 GPa) [61], V 2 O 5 (3-7 GPa) [62], and ZrO 2 (15 GPa) [63].

Mechanical properties
Based on the reported high-entropy nitride (HEN) coatings in literature, it can be seen that the hardness of HEN coating is dependent on the selection of element that are strong nitride formers in multicomponent alloy. In the earlier work on (FeCoNiCrCuAlMn)N and (FeCoNiCrCuAl 0.5 )N HEN coatings, a maximum hardness of 10.4-11.8 GPa was observed at higher N 2 flow ratio [39]. Consequently, HEN coatings containing strong nitride forming elements, such as (AlCrNbSiTiV) N [44], (TiVCrZrHf)N [49], and (TiZrNbAlYCr)N [64], were developed resulting in hardness increase of 40-48 GPa with increasing N 2 flow ratio. Furthermore, the mechanical properties have been found to increase with increasing substrate-bias and temperature. Some of the HEN coatings reported in literature with superior mechanical properties have been summarized in Table 1.

Tribological properties
The superior mechanical properties and high temperature stability of highentropy nitride (HEN) and high-entropy carbide coating make them suitable toward tribological applications. Few research works have been reported on tribological studies of HEN and high-entropy carbide coating as a function of N 2 / DOI: http://dx.doi.org/10.5772/intechopen.89527 CH 4 gas flow ratio and substrate bias. Lai et al. studied the effect of substrate bias on tribological properties of (AlCrTaTiZr)N HEN coatings against steel counter ball [46]. The resulting wear test showed a high COF of 0.7, while the wear rate decreased from 6.4 × 10 −6 to 3.6 × 10 −6 mm 3 /Nm with increasing substrate bias. The (AlCrTaTiZr)N HEN coating was found to be stable after the wear test of 70 m sliding distance. In another work, Cheng et al. studied the effect of N 2 flow rate on tribological properties of (AlCrMoTaTiZr)N HEN coatings against steel counter ball for a sliding distance of 90 m [72]. The resulting tribological test showed a low wear rate of 2.8 × 10 −6 mm 3 /Nm; however, the COF was found to be still high around 0.7. Similarly, Braic et al. studied the tribological behavior of (TiZrNbHfTa)N HEN coating and (TiZrNBHfTa)C high-entropy carbide coating on M2 steel substrate against sapphire counter ball for a sliding distance of 400 m at ambient conditions [68]. The wear test showed an average COF of 0.9 and an average wear rate of 2.9 × 10 −6 mm 3 /Nm for (TiZrNbHfTa)N HEN coating, and an average COF of 0.15 and an average wear rate of 8 × 10 −7 mm 3 /Nm for (TiZrNbHfTa)C high-entropy carbide coating. Following this work, wear test of (TiZrNbHfTa)N HEN coating and (TiZrNBHfTa)C high-entropy carbide coating was carried out in simulated body fluid (SBF) against sapphire counter ball for a sliding distance of 400 m [55]. The resulting wear test showed an average COF and wear rate of 0.17 and 2.9 × 10 −7 mm 3 /Nm for (TiZrNbHfTa)N HEN coating and an average COF and wear rate of 0.12-0.32 and 2-9 × 10 −7 mm 3 /Nm for (TiZrNbHfTa)C high-entropy carbide coating, respectively. Furthermore, Braic et al. and Jhong et al. studied the tribological performance of (TiAlCrNbY)C [54], (CuSiTiYZr)C [34], (CrCuNbTiY)C [73], and (CrNbSiTiZr)C [58] high-entropy carbide coatings and showed high-entropy carbide coating possessing superior tribological properties with wear rate and COF values in the range of 0.12-12 × 10 −6 mm 3 /Nm and 0.07-0.4, respectively.
Following the initial works on ball-on-disc sliding wear tests on HEN coatings, simulated tests have been performed for cutting tools application. Shen  against SKD11 steel for a sliding distance of 900 m and compared its performance to commercial TiN and TiAlN coatings [74]. The resulting milling tests showed a lower flank wear of 200 μm/min for (AlCrNbSiTi)N HEN coating as compared to 255 μm/ min in TiN and 270 μm/min in TiAlN, as shown in Figure 6. Similarly, machining performance of (TiZrHfVNbTa)N [75], (AlCrNbSiTiV)N [51], and nanolaminate (TiAlCrSiY)N/(TiAlCr)N [76] HEN coatings showed better tribological properties than commercial nitride coatings.

Corrosion properties
The increase in lattice distortion with high number of principle elements results in formation of amorphous phase in high-entropy alloys, which in return gives better mechanical and electrochemical properties. The corrosion resistance of conventional alloys can be enhanced with amorphous HEA coatings by choosing the appropriate chemical compositions. Lin deposited (TiAlCrSiV)N HEN coatings on a mild steel substrate at different R N flow ratios and studied its electrochemical properties in 3.5 wt.% NaCl solution at room temperature (RT; 22°C). The coating structure changed from amorphous phase at lower R N flow ratio to FCC solid solution at higher R N flow ratio. The highest polarization resistance of 11.36 kΩ/cm 2 was observed in the metallic TiAlCrSiV HEA coating, while the polarization resistance slightly decreased to 8.03-8.55 kΩ/cm 2 in its nitride coatings. Furthermore, the polarization resistance of HEN coatings was enhanced by developing an interlayer of metallic TiAlCrSiV HEA coating. In another work, Hsueh et al. deposited (AlCrSiTiZr)N HEN coating on 6061 aluminum alloy and mild steel substrates using DC magnetron sputtering at various R N flow ratios, and studied the effect of R N flow ratio and substrate bias during deposition on corrosion properties in 0.1 M H 2 SO 4 aqueous solution at RT [77]. The (AlCrSiTiZr)N HEN coating changed from an amorphous structure to partially crystalline structure at higher R N flow ratios. The resulting corrosion current density (i corr ) for 6061 aluminum alloy substrate decreased from 29

Future possibility and commercialization
As compared to high-entropy alloys, fewer reports have been published on crystalline high-entropy ceramics (HECs). Due to the high melting point, high hardness, and good thermal and chemical stability, as well as excellent wear and oxidation resistance of ceramic materials, most of the bulk HECs such as highentropy borides and carbides are designed to be the new type of ultra-high-temperature ceramics (UHTC) with increased high-temperature stability and superior mechanical properties over conventional ceramics. The current understanding of processing and evolution of properties of bulk HECs was built on and developed from the knowledge of HEAs. For bulk HECs, the preferred ceramic components are group IV, V, and VI metal ceramics (metal boride, carbide, silicide, etc.) due to their closely matched structure and properties. Compared to metallic HEAs system where only elemental materials are used, the combination of HEC composition is greatly limited. More experimental efforts on screening and investigation of HECs with different compositions are required to explore the potential of HECs. Furthermore, most of the reported bulk HECs is based on experimental observations, while a few are systematically discussed in combination with the modeling results. In order to give future researchers a clear guideline of designing HECs, further development on computational methods including corresponded thermodynamic ceramic database is needed to more effectively and accurately predict the structure and properties of HECs.
The research on the processing of HECs is progressing, and there have been considerable work performed in the industry on the coatings of HECs toward the next generation of nitride and carbide coatings. High-entropy carbide and nitride coatings have potential applications in biomedical industry, cutting tools, and hard facing die coatings due to their superior mechanical, corrosion, and oxidation resistant properties [55,74]. HEC coatings of nitride with high thermal stability can be applied as diffusion barrier coatings in integrated circuits to inhibit the diffusion of adjacent materials (e.g., Cu and Si) [79]. Furthermore, high-entropy oxide coatings can be considered as a potential future material for cuprate superconductors, visible-light photocatalysts, and transparent field-effect transistors (TFETs) [59].

Summary
Researches of bulk high-entropy ceramic have been reported on metal oxides, refractory carbides, borides, and silicides. HECs with homogenous single-phase structure reveal superior mechanical performance and additional properties like thermal-electrical property of high-entropy oxides. Most scientific effort has been put in exploring various fabrication methods, characterizing the high-entropy structure and the remarkable physical and chemical properties. However, to fully understand HECs that involves a complex multicomponent ceramic system, the problem remains: what are the most significant phase formation rules in a HECs material? How can the potential applications of HECs be realized? A more systematic investigation of the material selection rules that already exists in a metallic high-entropy system is highly demanded in the ceramic system in order to optimize the material design and processing work.
The reported research in the past 10 years on high-entropy ceramic coatings has shown development of coatings with exceptional mechanical, high temperature, electrical, corrosion, and wear-resistant properties. High-entropy ceramic coatings have great potential in different applications, such as wear and corrosion resistant coatings, thermal barrier coatings, and electrical and biomedical applications. The control on variation of deposition parameters can be advantageous in achieving coating with extremely high strength values and highly densified structures, which can be corrosion resistant and biocompatible. Future work on development of nanocomposite and multilayer high-entropy ceramic coatings can possess super