Perovskite Materials: Recent Advancements and Challenges

In the past decade, hybrid organic–inorganic perovskites (HOIP) have emerged as the exotic materials for the futuristic photovoltaics. The viability of low-temperature, solution-processed manufacturing and a unique blend of electronic and optical properties that has further indicated its goal towards a potential commercialization. This article clearly articulates the emergence of HOIPs and various challenges such as toxicity, hysteresis in these devices. Additionally, this chapter also makes an effort to highlight the advancements made in the perovskite materials for solar cells in the recent years, that include the Ruddlesden-Popper (RP) phase that has enabled us reach the power conversion efficiency of 28%. This phase is reportedly a lower dimensional structure than the conventional HOIP and exhibit better stability than the latter. This chapter also focuses to elucidate a few challenges of these RP phased HOIPs such as its synthesis, stoichiometry and process-ability in integrating the organic and inorganic entities.


Background
In the early 1990s, David Mitzi at the IBM Watson Research Centre extensively explored the structural dynamics of methylammonium lead iodide perovskite (MAPBI 3 ) material engineered for niche applications such as electronics, thin film transistors, photovoltaics (PV) and light emitting diodes [1][2][3][4][5]. Today, the hybrid halide perovskites are treated as the emerging semiconductor materials, as the past decade witnessed their successful application in highly-efficient photovoltaics [6]. Compounds based on this particular hybrid arrangement of organic and inorganic molecules has emerged in an unprecedented manner by the participation of over 1000 institutes across the globe and over 8000 published articles in its decade-old research efforts [7]. This article outlines a detailed overview about these materials advancements and challenges.

Perovskites for photovoltaics
HOIPs that inherit a diversified set of properties such as stronger and broader absorption, ultra-fast charge transportation, high dielectric, and swift charge recombination makes it the best suitable candidate material for PV [39,40]. Also, its ease of fabrication, stability, cost, efficiency, and performance rivals the best thin-film PV technologies.
Perovskite materials exhibit excellent optoelectronic properties and superior device performance via two key device architectures-mesoscopic and planar-as illustrated in Figure 1. The ultimate goal of the proposed summer project is to study how the contact/electrode interfaces impact the mechanism of charge collection and investigate the role of ionic motion on electronic charge carriers. In the recent years, the MAPBI 3 has attracted a great deal of interest for applications in high-performance optoelectronic devices [41,42] due to their ability to tune optical band-gaps from the violet to near infrared [14], as well as their higher absorption coefficients [15,16] and potential for long-range electron and hole transport [17]. Moreover, the optical and electrical properties of HOIP single crystals are far superior to their thin film counterparts [43,44]. So far, researchers have been able to grow perovskite structured single crystals of methylammonium lead triiodide (CH 3 NH 3 PbI 3 ) and methylammonium lead tribromide (CH 3 NH 3 PbBr 3 ) with both size and shape controlled capabilities [45,46].
These materials potential has increased the power conversion efficiencies of solar cells from 1 to 24.2% [47,48]. Despite these materials were gaining efficiencies but were losing on the stability and durability side due to the anomalous hysteretic effects that is typically exhibited by ferroelectric materials. So, it became critical to understand the significance of hysteresis in these materials.

Hysteresis in perovskites
This unusual property of hysteresis in the J-V characteristics [49][50][51][52] of perovskites is understood to originate from various factors impacted by the various electronics parameters used to operate or test device based on these materials, such as the scan rate, sweep direction, thickness of CH 3 NH 3 PbI 3 and TiO 2 . Some researchers report that the abnormal behavior is more extreme in planar structures than the mesoporous architectures [51,[53][54][55][56]. Moreover, the presence of anomalous J-V hysteresis makes it difficult to reliably quantify the device performance, which could postpone the timely commercialization of this technology. It was found that the presence of large crystal grain sizes in the perovskite layer and the use of mp-TiO 2 layer can significantly reduce the J-V hysteresis. Recently, Yang et al. reported that hysteresis highly depends on the type of perovskite material used, and device architecture (n-i-p or p-i-n) [47]. The devices with n-i-p architecture and formamidinium lead iodide (FAPbI 3 ) as the absorber material did not show any hysteresis, whereas devices with p-i-n architecture (FTO/NiO/perovskite/PCBM/LiF/Al) showed strong hysteresis.
You et al. [57] reported that their devices with ITO/NiO x or PEDOT:PSS/ CH 3 NH 3 PbI 3 /ZnO or PCBM/Al (p-i-n) architecture were shown to exhibit negligible hysteresis (Figure 2), which is consistent with some other earlier reports [58,59]. It was speculated that n-type PCBM layer diffuses into the perovskite layer through pin-holes and grain boundaries during processing, and mobile ions in the perovskite film may interact with PCBM, forming PCBM halide radicals. This was assumed to result in stable electrostatic properties and reduced or no hysteresis [56,60]. On the other hand, if the PCBM is used as the bottom electron transport layer (n-i-p architecture), no such inter-diffusion occurs, and the unusual ion movement causing hysteresis cannot be suppressed. More recently, Xu et al. reported the fabrication of hysteresis-free PSCs with conventional architecture using a perovskite-PCBM hybrid solid thin film as the absorber [60]. The devices without PCBM, i.e., FTO/ TiO 2 /perovskite/spiro-OMeTAD/Au, exhibited hysteresis, whereas devices with a perovskite-PCBM hybrid layer showed significantly reduced or no hysteresis. Here, PCBM was shown to neutralize PbI 3 ˗ defects, traps, and perovskite grain boundaries. It also reduced non-geminate recombination, and increased carrier lifetime. This study showed that incorporating a small amount of PCBM into the perovskite layer, or using a thin PCBM layer at the interface of TiO 2 /perovskite, significantly reduces device hysteresis, while improving the device stability. However, these observations are not consistent with the hypothesis that PCBM reduces hysteresis by preventing the diffusion of ionic defects along grain boundaries. In addition to demonstrating the role of interfacial recombination in the presence of mobile ions in a semiconductor, our study targets the demonstration of the viability of controlling this ionic migration. These measurable consequences of ion migration suggests interesting possibilities of exploiting these effects for other electronic applications (e.g. sensing) where a memory of previous operating conditions could enable novel device behavior.
The majority of investigations indicate, that an electronic alignment at the interface between the perovskite absorber and transport layer is likely to become a key ingredient for designing next-generation devices, which can overcome the current performance limits [61,62]. Considering these various sources potentially contributing to hysteresis, further investigation into device architectures and materials design is required to understand the dominant sources of this unusual behavior.
Further, the architecture of PSCs is also found to affect the level of J-V hysteresis. Planar PSCs on cp-TiO 2 often show more severe hysteresis than mesoporous PSCs based on a mp-TiO 2 scaffold [50]. For mesoporous/planar hybrid PSCs with a perovskite capping layer on top of mp-TiO 2 , the grain size and thickness of the capping layer influences the J-V response. As ionic migration was identified as a possible cause of PV current-voltage hysteresis in hybrid perovskite solar cells, it was concluded that the quality of materials and crystal growth kinetics are vital in improving electronic, optoelectronic and PV applications for these classes of hybrid organic-inorganic semiconductors. Apart from hysteresis, another drawback that was hindering these devices into the commercial markets was the toxicity of lead.

Bismuth-based perovskites
The HOIP class of materials have displayed promising results for advanced and efficient photovoltaics. However, some of the urgent issues associated with these materials such as lead toxicity, poor stability, and atmospheric impacts are yet to be resolved. So, the focus of research shifted to replace toxic lead with other cations such as Sn 2+ , Ge 2+ , Mg 2+ , Mn 2+ , Ni 2+ , and Co 2+ [63][64][65]. Many proposed the  replacement of Pb by tin (Sn) in order to render perovskite light absorbers less toxic or even nontoxic [66,67]. Yet, compared to their Pb-based counterparts, Sn-based perovskites so far show inferior device performance, and they are even more sensitive to degradation because of self-oxidation [24]. In addition, Sn is also listed as a harmful chemical, raising concerns regarding its suitability as a more environment friendly alternative to lead in perovskite solar cells [68]. The most obvious route to replacing Pb in this compound is via substitution of other group-14 elements, such as Sn which tend to undergo oxidation, for example, from Sn 2+ to Sn 4+ , leading to a rapid degradation of the corresponding halide perovskites [69].
Germanium (Ge) has received relatively little attention as a replacement to lead, in part due to its strong lone pair effect, which acts to produce lower dimensionality structures with poor conductivities [70]. The series of perovskite-structured CsGeX 3 compounds, where X is chlorine (Cl), bromine (Br), and Iodine (I) have been known for some time for their nonlinear optical properties [71,72]. These compounds are stable up to 150°C, and have bandgaps correlated with the A-site cation size [73]. However, the relative stability of the +4 oxidation states decrease and the relative stability of the +2 oxidation states increase down the group IV elements. As this effect is even more prominent for the case of Ge 2+ , it is presumptive why no successful Ge-based hybrid perovskites have been developed.
These reports indicate that neither Pb nor Sn nor Ge can steer the scientific community to a roadmap for stable and non-toxic optoelectronic devices. Thus, more out-of-the-box approaches such as blending and splitting the anions and cations is required to stimulate the research in these niche areas. Fundamentally, many of the excellent properties seen in hybrid perovskites are thought to be derived from the 6 s [2] electronic configuration of lead, a configuration seen in a range of post-transition metal compounds [74]. Typically, materials containing post-transition metals with an ns [2] electronic configuration (i.e. an N-2 oxidation state) possess large dielectric constant, small effective masses, a valence band maximum composed of antibonding states, and high levels of band dispersion properties due to their soft polarizability-leading to high Born effective charges and large spin-orbit effects, which act to increase the bandwidth of the conduction band.
One promising alternative is to incorporate Bismuth (Bi) into the perovskite structure. Its size is similar to lead and the impact of steric effects on the optoelectronic properties of the material. Bismuth(III) (Bi 3+ ) compounds are attractive reagents and catalysts in organic synthesis because of their low toxicity, low cost and ease of handling. Preliminary investigations on organic-inorganic methylammonium bismuth iodide (MABiI) shows its advantages of non-toxicity, stability in ambient air and low-temperature solution-processibility, which may address both the toxicity issue of lead-based perovskites and instability concern of tin-based ones [75]. Typically for methylammonium bismuth halides, a Goldschmidt tolerance factor (t) of 0.85-0.87 (Bi 3+ = 1.03A o ) is observed for a suitable perovskite structure and to further compliment it an octahedral factor (μ) 0f 0.46 justifies a stable octahedron perovskite structure [76]. Another study reports that compounds formed with 6p block cations show a significantly larger contribution of spin-orbit coupling in the conduction band, vs. those formed from the 5p block. This implies that the Bi 3+ compounds show a much stronger spin-orbit contribution than the In, Sn, and Sb compounds. This further reiterates that Bi based compounds are the most suitable for achieving similar shallow vacancy levels as observed in MAPBI 3 [77].
Organic-inorganic bismuth iodide based hybrid materials have attracted interest because of their potential semiconducting character, rich structural diversity and interesting electronic and optical properties, for which the 6 s [2] lone pair of the Bi 3+ plays an important role in the various material properties [78,79]. In early 1990's, researchers conducted extensive studies on the phase transitions of various MBH primarily to investigate its application as scintillators in radiation detectors [80,81]. Recently, several research groups reported methylammonium bismuth iodides ((CH 3 NH 3 ) 3 Bi 2 I 9 ) as a stable and lead-free light absorber for PV applications with an efficiency of less than 1% [75,[82][83][84][85]. Our basic studies on Bi based single crystals of (CH 3 NH 3 ) 3 Bi 2 I 9 were successful and in agreement with the literature (publication pending). Figure 2a illustrates a typical schematic of MABiI structure comprising of bioctahedral (Bi 2 I 9 ) 3− clusters that are surrounded by methylammonium cations. The MABiI crystal was solution grown at ambient room temperatures with good hexagonal crystalline structural phase and X-ray diffraction as shown in Figure 2b is in agreement with the literature [75,83]. The red single crystals suitable for single crystal X-ray diffraction were grown using a layer crystallization technique by separating the two starting solutions of methyl ammonium iodide and bismuth(III)iodide with dichloromethane. In our preliminary study, all of the peaks in the XRD pattern can be indexed to a hexagonal structure, with no traces of any impurities. There are reports on XRD patterns of thin films, prepared via spin coating techniques recorded in Bragg-Brentano geometry and show good agreement when compared with the pattern calculated from single crystal data demonstrating a high degree of phase purity in the new material [79,82]. A recent study on Cs 3 Bi 2 I 9 perovskite crystal, revealed it had a hexagonal structure and its space group is P6 3 / mmc(194) which also has a monoclinic phase with space group C12/c1 [15] [83]. However, there are no reports for Bi based single crystal nanostructures.
As the research was plateauing on the lead alternatives and the observed hysteresis, the scientific community has identified a new breakthrough for these materials i.e., a lower dimensional perovskite-halide based two dimensioned organic-inorganic perovskite.
Recently, Benabdallah et al., have reported on the advantages of MABiI over lead-based perovskites [86]. The first principle calculations based on DFT have revealed that the Bi-based perovskites could be engineered to better bandgaps and have superior absorption coefficients than its lead counterparts. Separately, Sanders et al., have also reported on a novel chemical vapor deposition method to fabricate Bi-based perovskite solar cells that could potentially pave way for large scale and cost-effective commercial markets [87].

Transition from 3D to 2D crystal structures
Lately, these materials have unlocked a new stoichiometry-two-dimensional (2D), that features improved stability against atmosphere than the 3D materials. This process of lowering the dimensionality is gaining momentum and potentially serve the needs of specific applications such as solar cells, light emitting diodes (LEDs) and other optoelectronic devices. Although, there are various techniques to obtain this exotic and new 2D material, there has been significant interest for a specific kind of perovskites, namely Ruddlesden-Popper (RP) which was discovered in 1957 [88]. These perovskites have Vander Waals crystal structure carrying a general chemical formula of L 2 A n-1 B n X 3n + 1 , where L is a large molecular chained cation, A is a regular cation, B is an inorganic metal cation, X is the halide anion and n = 1, 2, etc., this arrangement of alternating organic-inorganic layers develops an ordered and ideal 2D quantum well. Additionally, these 2D structured quantum wells play a vital role in neutralizing the higher exciton binding energies formed due to contrasting dielectric constants. A simple structure is illustrated in Figure 3.
The insulating nature of the organic spacer cations creates a competitive advantage of greater atmospheric stability for the 2D HOIPs when compared to their 3D counterparts. It was rightly indicated by Mao et al. that the discovery of these 2D HOIPs could possibly be a solution to stabilize a few metastable phases that are found in the form of perovskite nanocrystals. As Spanopoulos et al., has rightly observed that the room-temperature PXRD measurements of these 2D perovskites have indicated that there are no residual low-angle peaks (<13° 2θ) which would be an indication of coprecipitation of more than one inorganic layer in each case [89]. Although there has been significant progress in the [90], (110) and (111)-oriented perovskites, there has been undivided attention for the (100)-oriented HOIPs due to their dimensional variability. Furthermore, this particular orientation is the most favored geometry to tune the layer thickness. A few researchers have expanded the family of 2D RP perovskites by increasing the organic spacer molecules (n = 1-5) and concluded that for n values higher than 5 does not exhibit sufficient thermodynamic  . Separately, other study indicated that these materials have demonstrated unique optical characteristics with high air, heat and light stability especially for n = 4. Additionally, other discoveries such as the stability increases with increasing layer thickness and the need for crystalline substrates for improved orientation and long-term air stability [89]. So, a plethora of permutations are to be considered to build an effective, stable and functional 2D HOIP. Table 1 delineates key features about individual elements of these HOIPs. As a result of its ability to dimensionally customize the n-layer, the [90] oriented 2D HOIPs are paving way for a precise tailoring of the quantum well electronic structures. A simple X-ray diffraction analysis as shown in Figure 4 would help us track the number of perovskite layers. This particular orientation exhibits a level of resistance to the thermodynamic phase. For example, this phase is more evident in the 2D perovskites at n = 2 versus a non-perovskitic phase in a 3D perovskite [6]. This further reinforces the belief that these 2D materials can further emerge with unexplored photophysics and optoelectronic properties.

2D perovskites for photovoltaics
Despite the fact that, these Vander Waal layered 2D structure of RP perovskites has complicated the growth kinetics of thin 2D perovskites, yet the mechanical exfoliation process of inserting the long organic cation into a 3D perovskite structure was investigated by various research groups [6, 91,92]. A few other groups have explored other methods such as colloidal synthesis [6, 74,93], chemical vapor deposition (CVD) [94] and solution-based methods to obtain these 2D perovskites.
Another key feature that distinguishes 2D perovskites with their 3D counterparts is its superior susceptibility towards atmospheric moisture. By far, this is believed to be the single largest factor holding its foray into commercial markets. Apart from photoinduced oxidative degradation, 3D perovskites react with water, leading to collapse of the structure and to formation of either a 0D hydrated phase or to irreversible decomposition into the precursors, for example, MAPBI3 starts to decompose at a relative humidity of 55%, which induces a color change from dark brown to yellow owing to conversion into a lead iodide [95]. Separately, other factors such as localized UV heating and light induced ion movement has also accelerated the perovskite degradation [90,[96][97][98]. Although, there are various synthesis methods for these 2D perovskite materials such as CVD, liquid and mechanical exfoliation, solution and colloidal based methods that have shown promise. But, there seem to be a critical need for controlled growth *Address all correspondence to: achilver@xula.edu monitoring especially the thickness and lateral crystal sizes is still a challenge [92]. So, new synthesis methods that warrant controlled thickness and large lateral sizes are highly preferred to institute a seamless pathway towards commercial markets.
Tsai et al., have reported a uniform and thin layered films for planar PV applications as shown in Figure 5. These hot-casted films of 2D (BA) 2 (MA) 3 Pb 4 I 13 perovskite was reproducible and highly efficient with 12.51% with an open circuit voltage of 1.01 V, short circuit current density of 16.76mAcm −2 and a fill factor of 74.13% [99]. Also, from Figure 5c it can be noticed that the J-V curves for hysteresis tests under AM1.5G illumination measured with the voltage scanned in opposite directions were observed to be no effects.

Conclusions
With the least scope for degradation and hysteresis, these 2D HOIPs have rejuvenated the scientific community at large and paved the way for a larger role in the commercial markets. Contrarily, as many consider that the dimensional transition of perovskite materials from 3D to 2D clearly outlines the scope of these materials and applications that it could create, there are equally concerning challenges such as complex growth mechanism, low thermal conductivity and high exciton binding energies. So, a reproducible and scalable fabrication mechanism is highly required to lock its potential. Also, the emergence of 2D nanostructures of HOIPs could be leading the research and evaluate the potential of these materials to its fullest. So, a methodology that can create a scalable and efficient PV devices with longer stability and improved functionalities could change the dynamics of these materials.