Magnetoresistance and Structural Characterization of Electrospun La 1− x Sr x MnO 3 Nanowire Networks Magnetoresistance and Structural Characterization of Electrospun La x Sr x MnO 3 Nanowire Networks

Nanowire network fabrics of La 1 (cid:1) x Sr x MnO 3 (LSMO) with different doping levels x = 0.2, 0.3, and 0.4 were fabricated by means of electrospinning. The resulting nanowires are up to 100 μ m long with a mean diameter of about 230 nm. The nanowires form a nonwoven fabric-like arrangement, allowing to attach electric contacts for magnetoresistance (MR) measurements. The resistance in applied magnetic fields and the MR effect were measured in the temperature range 2 K < T < 300 K in magnetic fields up to 10 T applied perpendicular to the sample surface. An MR ratio of about 70% is obtained for x = 0.2 at 10 T applied field and T = 20 Kr. The highest low-field MR of 5.2% (0.1 T) is obtained for the sample with x = 0.2. Magnetization measurements reveal the soft magnetic character of the samples. A thorough analysis of the microstructure of these nanowire networks is performed including scanning electron microscopy (SEM) and transmission electron microscopy (TEM).


Introduction
Colossal magnetoresistance (CMR) is a property of some materials, mostly manganese-based perovskite oxides that enables them to dramatically change their electrical resistance in the presence of a magnetic field, i.e., magnetoresistance (MR) [1][2][3]. To bring the CMR materials toward applications, it is still necessary to further optimize the sample processing to find the optimal microstructure, especially concerning grains in the nanometer range. The low-field magnetoresistance response (LFMR) of such manganese perovskite oxides like La 1Àx Sr x MnO 3 (LSMO) with different doping levels x is closely connected to the existence of interfaces and grain boundaries (GBs) within the samples [4][5][6][7], and the high-field magnetoresistance (HFMR) was found to increase progressively on decreasing the grain size [8]. Therefore, the measurements of nanostructured or nano-sized samples are an important issue to provide a deeper understanding and further improvement of the MR effect, especially for the improvement of the behavior of devices based on the MR effect in reduced dimensions.
Commonly, the manganese perovskite samples studied in the literature are prepared as bulks or as thin films, mainly on SrTiO 3 substrates. Nanometer-sized bridges are then prepared using lithography techniques or the focused ion-beam technique [9,10]. The use of a substrate in the case of thin-film samples is always causing strain effects within the functional layer due to the lattice mismatch, which may play an important influence on the resulting magnetic properties [11]. The situation may be considerably different in nanostructures without substrate, being recently investigated in several types of nanoscale composites [12][13][14]. These nanostructures include nanorods, nanowires, nanotubes, and nanobelts; all of them having specific physical properties depending on the chosen preparation route.
In the present contribution, we have fabricated nanowire network fabrics of La 1Àx Sr x MnO 3 (LSMO) with different doping levels x by means of the electrospinning technique [15][16][17]. This technique is common for the fabrication of organic polymer nanostructures but can be modified by employing different precursors to deliver inorganic compounds. Up to now, only a small number of reports are dealing with magnetic nanostructures prepared in this way [17][18][19]. In the case of LSMO, exhibiting the CMR effect, the resulting nanowires are of polycrystalline nature with a high-aspect ratio (length up to 100 μm and diameters of about 230 nm) and show a large number of grain boundaries (GBs) within each individual nanowire. In Ref. [19], individual nanowires were separated from the as-spun networks and placed on a prepatterned substrate. Electric contacts were prepared using Ti/Cu electrodes, and the nanowires could be measured individually, allowing to observe a dependence of the MR on the nanowire diameter. Single nanowires of CMR materials may be employed as sensitive gas sensor elements or electrodes [20][21][22].
However, the as-spun nanowires form a nonwoven fabric-like network, where numerous interconnects between the individual nanowires are formed in the final heat treatment step. As a result, the current flow through such a nanowire network fabric shows percolative character, and several sub-loops can be formed. The interconnects between the individual nanowires add additional crossover points for the currents and can enhance the tunneling transport across the interfaces, together with the GBs. This additional scattering of the electrons at the interfaces provided by the interconnects is lost when measuring only extracted parts of the nanowires as done in Ref. [19]. Furthermore, no information on the LSMO grain size of their nanowires was presented. An analysis of the grain sizes within our nanowires showed values ranging between 10 and 32 nm. Therefore, it is obvious that the LSMO grains within the present nanowires are smaller as compared to, e.g., Ref. [8].
Therefore, we may expect interesting new properties of this new class of magnetic material. Furthermore, the nanowire network fabrics are an extremely lightweight material with a density of about 0.084 g/cm 3 , which is considerably less than the theoretical density of 6.5 g/ cm 3 [23]. Furthermore, there is no sample size limitation imposed by the fabrication technique, as electrospinning may produce very large sample sizes [24]. This makes such fabrics interesting for applications in bulk form, whenever the weight of the sample counts.
In order to achieve a better understanding of the transport properties through these nanowire network fabrics, we also performed a thorough microstructure analysis including scanning electron microscopy (SEM) and transmission electron microscopy (TEM).

Experimental procedures
The electrospinning precursor is prepared by dissolving La, Sr, and Mn acetates in PVA (highmolecular-weight polyvinyl alcohol). The PVA is slowly added to the acetate solution with a mass ratio of 2.5:1.5. This solution is stirred at 80 C for 2 h and then spun into cohering nanofibers by electrospinning. To remove the organic compounds and to form the desired LSMO phase, the sample is subsequently heat treated in a lab furnace. An additional oxygenation process is required to obtain the correct phase composition. The constituent phase was checked by means of X-ray diffraction (XRD) and EDX analysis. Further details about the electrospinning process of ferromagnetic and superconducting nanowires are given elsewhere [25][26][27][28].  The as-grown fabric has a white color, and the entire fabric sample is fully flexible. Figure 1(c, d) finally presents the fully reacted sample after having received the full thermal treatment. The reacted sample shows a fully black color, indicating the completed chemical reaction. As a result, the final nanowire network fabric is extremely thin and brittle. Here, it is important to note that the sample size shrunk to about one sixth of its original size. This shrinkage has to be considered for the application of such fabric-like materials. In the thermal treatment, numerous interconnects between the individual nanowires are formed, which are essential for the resulting current flow through the sample.
The entire nanowire network was electrically connected by means of silver paint and Cu wires (50 μm diameter) to the sample holder. Due to the high fragility of the ceramic sheet, a pseudo four-point configuration is realized where the current and voltage links connect immediately on the sample contacts. This arrangement is presented in Figure 2. The magnetoresistance is measured in a 10/12 T bath cryostat (Oxford Instruments Teslatron) with a Keithley source meter (model 2400) as a current source, and the voltage is recorded using a Keithley 2001 voltmeter. The constituent phases of the samples were determined by means of a high-resolution automated RINT2200 X-ray powder diffractometer using Cu-K α radiation (40 kV, 40 mA) Figure 3. SEM imaging was performed using a Hitachi S800 scanning electron microscope operating at a voltage of 10 kV, and the TEM analysis was performed by a JEOL JSM-7000F transmission electron microscope (200 kV, LaB 6 cathode). For TEM imaging, pieces of the nanowire network fabrics were deposited on carbon-coated TEM grids. High-resolution TEM and EBSD were performed on selected nanowire sections being thin enough for electron transmission ( Figure 6).
The magnetization of the nanowire networks was measured using a SQUID magnetometer (Quantum Design MPMS3) with AE7 T magnetic field applied perpendicular to the sample surface, using a piece of the nanowire network fabric with a size of 14.86 mm 2 .

Microstructure
Scanning electron microscopy revealed an average diameter of the resulting nanowires of around 220 nm and a length of more than 100 μm. Fabric-like nanowire networks with numerous interconnects are formed after the heat treatment. The individual nanowires are polycrystalline with a grain size of about 10-30 nm, which corresponds to the dimensions obtained via transmission electron microscopy and electron backscatter diffraction (EBSD) analysis. This is presented in Figure 4 giving SEM images of the nanowire network fabrics at 5000Â magnification (first column) and at higher magnification (10,000Â, second column) for all LSMO samples studied here. Figure 4   nanowire. Furthermore, it is obvious from these images that the LSMO grains do not show a texture but are randomly oriented with high-angle grain boundaries between them.    some grain clusters connected with low-angle grain boundaries are also visible, which explains the differences between the grain sizes determined from X-ray data and from TEM images and EBSD [29]. The nanowires are built up from stacks of several individual LSMO grains. Figure 7 presents the magnetization data obtained for all three compositions. The soft magnetic character of the LSMO fabric samples is clearly revealed. From the Sr-doping level x = 0.2 to x = 0.4, the saturation magnetization M s ð Þ is at 10 K 52.12, 58.13, 55.03 emu/g, and at 300 K, and the results are 18.10, 33.09, and 24.62 emu/g, respectively. These values are lower than the ones from the corresponding bulk materials (56 emu/g [30], 33.09 emu/g [31], 24.62 emu/g [32]). The x = 0.3 sample shows the highest M s among the three compositions, while the x = 0.2 sample shows the lowest ones at both 10 and 300 K. This matches the conclusion drawn from bulk materials that the optimized doping level around x = 0.33 supplies the strongest magnetism. The M s value of all our samples being lower than the bulk values can be attributed to the smaller LSMO grain size of our nanowire network fabric samples.

MR data
With respect to the literature, the MR data can be divided into two different regimes. According to Ref. [8], the high-field magnetoresistance (HFMR) behavior sheds light on the influence of the sample microstructure via the interface response. Therefore, analyses of the electronic transportation properties and of the magnetoresistive effects of the nanowire networks were carried out by four-probe measurements in external magnetic fields up to 10 T. Firstly, we have a look at the high-field regime. Figure 8 presents the resistance measurements for the samples x = 0.2, 0.3, and 0.4 with the temperature swept from 5 to 300 K. The magnetic field is applied perpendicular to the surface of the nanowire network, i.e., the current flow is mainly perpendicular to the applied field. Magnetoresistance plots are calculated from the data obtained by these sweep measurements at different field strengths using the relation As result, we find a maximum MR for the sample x = 0.2 at low temperatures and 10 T applied magnetic field of 70%.   Table 1 summarizes our findings at three selected magnetic fields for the three doping levels studied here, and the last row of Table 1 gives the maximum MR obtained, together with the respective temperature.
At 100 K, sample x = 0.4 shows the highest MR of 23.58% (close to the overall maximum of 26%) at 1 T applied field. In higher applied fields, the maximum value of the MR shifts to sample x = 0.2. A maximum MR ratio of 26.01 at an applied field of 1 T (63 K) is obtained for the sample x = 0.4. At 2.5 T applied field, the maximum MR of 17.97 (57 K) is found in sample x = 0.4.
At 10 T applied magnetic field, the maximum MR rate of 69.28% (25 K) is found in sample x = 0.2. Note also that the highest MR of sample x = 0.3 is obtained at a relatively high temperature, ranging from 203 K (1 T) to 92 K (10 T). Secondly, Figure 9 shows the MR ratio of sample x = 0.2 as a function of applied field for various temperatures. The MR is found to increase on lowering the temperature down to 50 K, whereas the MR at low temperature (3 K) is found to be smaller as compared to the 50 K data. The inset of Figure 9 presents the LFMR at an applied magnetic field of 0.1 T for the sample x = 0.2, showing a maximum LFMR of 5.2% at T = 50 K.

Discussion
From the graphs and the tables presented here, three main features can be deduced: Firstly, there is a suppression of the metal-insulator transition. This provides another evidence of the size effect. Nanoscale grains are always accompanied by a large number of grain boundaries, which enhance electron scattering. The metallic behavior is negatively influenced by the Coulomb blockade [13], and as a result, an upturn of the resistivity appears at low temperatures. On the The last row gives the maximum MR obtained, together with the respective temperature. other hand, the influence from certain size effects varies with the doping level. So, a step-shape resistance behavior can be observed for the x = 0.2 sample, which indicates that the metalinsulator transition is not completely suppressed. However, in the x = 0.4 sample, the resistance decreases almost linearly from 5 K to 200 K. Secondly, the x = 0.3 sample with the highest saturation magnetization shows the weakest MR effect, and inversely, the x = 0.2 sample exhibits the strongest MR effect at low temperatures. At 2.5 T, the maximum of the MR is already over 40%, which points to an obvious LFMR effect. The increase of the MR with reducing magnetization has been reported by Balcells et al. [8]. In their work, the variation of the grain size is the main reason of the behavior observed. In contrast to this, there is no obvious grain size difference between our samples. The dependence of the MR on the magnetization requires further investigation. Thirdly, at around 200 K with the doping level x = 0.2 and 0.3, the MR curves at 2.5 T have a crossover with the curves at other fields, which means that above 200 K, the absolute value of the magnetoresistance does not monotonously increase with the external field.
To enable a comparison with data on other LSMO sample types but with the same chemical composition (x = 0.2) published in the literature, we summarize some data at 1 T applied magnetic field in Table 2 and compare them with our results.
From Table 2, we see that the nanowire sample x = 0.2 exhibits a larger MR of 20.66% as compared to the nanoparticles and the powder samples of the same chemical composition studied in the literature, however, at some lower temperature. This points clearly to the important contribution of the much smaller LSMO grains in our nanowire network fabric samples, and the additional scattering at the numerous interconnects provides extra MR.
Jugdersuren et al. [19] reported a large LFMR at room temperature in their LSMO nanowires extracted from the networks produced by electrospinning and showed a dependence of the LFMR on the nanowire diameter, but no information on the LSMO grain size was presented. However, the LFMR at 300 K for our sample is comparable to their data, even though the chemical composition is somewhat different. Nevertheless, this demonstrates that the LFMR as well as the HFMR can be considerably enhanced by reducing the nanowire diameter as well as the LSMO grain size.

Conclusion
Nonwoven nanowire networks of LSMO with three doping levels x = 0.2, 0.3, and 0.4 were fabricated by means of electrospinning. The magnetoresistance effect of these nanowire fabrics was measured up to 10 T applied field between 5 K and 300 K. The reduced dimensions of the nanowires and the large number of interconnects between them were found to increase the MR effect as compared to bulk samples. An MR ratio of 70% was observed for the sample x = 0.2 at low temperatures and 10 T applied magnetic field.