Hidden Resources of Coordinated XPS and DFT Studies Hidden Resources of Coordinated XPS and DFT Studies

Electronic configuration of chemically bound atoms, at the surface or in the bulk of a solid, contains the traps for energy absorption provided by the valence band electron transitions; the core-level excitation of any origin is coupled with traps forming the mul- tichannel route for energy dissipation. This chapter displays tracing over these channels by means of X-ray photoelectron spectroscopy (XPS) and density functional theory (DFT). Conformity between energy losses in the XPS spectra and electron transitions in relevant unit cells is verified by the examples of the pristine and half fluorinated graphite C 2 F, and the Br 2 -embedded C 2 F. Perfect XPS-DFT combination can be useful for material science providing exhaustive data on state and geometry of the atoms in a sample, regardless the field of its application. The valence band is insensitive to the energy source for its excitation. It makes the behavior of energy losses in XPS spectra of the atoms to be a descriptor of bonding between these atoms in multicomponent materials. Moreover, the state of any component can be tracked through change or invariability of satellites in the relevant XPS spectra, obtained in the course of the external influence, thus revealing a wear performance of the material.


Introduction
Fundamental studies in the field of surface science form the grounds for the sustained development of advanced technologies and new composite materials and catalysts with the desired properties [1,2]. The methods of electron spectroscopy are unique tools of the basic research enabling characterization of the structure, composition, and properties of solids and interfaces at the atomic-molecular level.
Key properties of a sample are often exposed in their responses to a core-level excitation. The specific responses have been discovered using the tunable synchrotron irradiation and became the basis of advanced techniques [3]. The X-ray absorption fine structure (XAFS) appears near the edge of photoionization threshold (XANES) and reveals the vacant state structure, while the XAFS beyond the absorption edge (EXAFS) exhibits the local geometry [4]. The resonant inelastic X-ray scattering (RIXS) is enabled by the energy and momentum transferred by a photon near the absorption edge and exhibits the intrinsic excitations [5]. Resonant photoemission (RPES) and Auger electron spectroscopy (RAES) disclose the local electronic structure and correlations in a system, respectively [6]. The use of the electron impact instead of the X-ray, as a source of the core-level excitation, has discovered the similar effects of the conjugate electron excitation (CEE) [7][8][9][10][11]. The CEE shows itself as a set of satellites in disappearance potential spectra (DAPS), which answers to valence band (VB) structures of near-surface atoms, including the adsorbed species, and plasmon excitations. Experimental evidence for the CEE phenomenon is based on DAPS spectra, obtained from various adsorbed layers and on its mechanism represented by the combination of ordinary electron transitions. For example, plasmon oscillations are often observed by means of X-ray photoelectron (XPS) and Auger electron spectroscopies (AES) [12,13]. Ionization of the VB, of the substrate and adsorbed species, is a basis of ultraviolet photoelectron spectroscopy (UPS) [14]. Similar satellite structures, above different thresholds, in DAPS spectra confirm that the core electrons are identical with regard to CEE transitions [7,8]. CEE phenomena represent, in whole, the multichannel route for energy dissipation within the DAPS probing depth of 2-3 monolayer (ML), which does not undermine the general concepts in the field of electron scattering.
Novel as well as advanced technologies strongly require the next generation materials in the fields of tribology [15][16][17], hardness [18,19], corrosion and wear performance of the material [20], and many others [21][22][23]. The progress of material science in these fields is resulted, in large measure, from the fundamental studies by means of modern techniques, including the XPS as well [16,17,[21][22][23]. The X-ray photoelectron spectroscopy is a powerful analytical tool; however, this method is limited by the content and charge state of the atoms, while it cannot disclose the chemical behavior and structural features of the atoms in a sample, which are urgently needed in case of the multicomponent substrate. These properties and many others are direct products of the DFT. In turn, the DFT runs give greatly different results depending on starting conditions and the operational parameters, which have to be found indirectly. A reliable intersection between the XPS and DFT outputs would help to employ the hidden resources of both techniques.
The CEE phenomenon is a true multi-channel route of energy dissipation through the VB. The identity of electronic nature of the surface and bulk atoms allows one to suggest the similarity of inelastic electron scattering mechanisms on the surface and in the bulk of a solid. Then, the CEE should also occur, under the X-ray core-level excitation, and manifest itself in the XPS spectra as energy losses. The plasmons in AES and XPS spectra correspond indeed to the collective CEE phenomena. Highest occupied molecular orbital-lowest unoccupied molecular orbital (HOMO-LUMO) transitions, which are often used for assignment the XPS, RPES and XANES spectra [24,25], are also clear CEE manifestations. The electron energy dissipation, accompanying the core-level excitation, is the general trend of any electronic configuration.
Auger transitions are particular cases of the event resulted from filling the core hole. CEE is another route of relaxation consisting in redistribution of the photoelectron energy through the accessible valence bands.
A close attention is paid to the graphite materials as essential parts of the advanced technical devices [26]. Fluorinated graphite serves as an intermediate of the graphene synthesis, while embedded with the alkali or halogen, exhibits high chemical stability, improves the anode activity in a fuel cell, becomes the nano-reactor or the storage nano-container of volatile compounds, and so on [27][28][29]. We have considered highly orientated pyrolytic graphite (HOPG), half-fluorinated HOPG (C 2 F), and that with the embedded Br 2 (C 2 F *0.15Br) as touchstones of the following concept [30,31]. First, inelastic electron scattering, in near-surface layer and in the bulk of a solid, follows the same regularities. Second, the X-ray core-level excitation is accompanied by the VB transitions revealing themselves as the photoelectron energy losses. Third, linking of the XPS and DFT methods via conformity between XPS spectral structures and theoretical CEE transitions justifies the other DFT products related to local geometry, chemical bonding, and states of the atoms in a sample.

Experimental
Inelastic electron scattering has been monitored by the elastic scattering, using the DAPS. Disappearance potential spectroscopy is based on the threshold core-level excitation by an electron beam of the time-based energy E p [32]. Whenever the incident potential exceeds the corelevel energy, a part of electrons disappears from the elastic current I and provides a dip in the dependence of dI(E p )/dE p on E p . The event occurs if E p is equal to difference between the core and vacant state energy. The spectrum shape is determined by the self-convolution of vacant density of states (DOS), as the destination of interacting electrons. The adsorption of test gases over the Auger-clean Pt(100)-(1 × 1) single crystal was performed at 300 K [33]; exposures are given in Langmuir (1 L = 10 −6 Torr s). The Fermi level (E F ) in DAPS spectra corresponds to E p = 314.8 eV, which is close to the reference Pt4d 5/2 core-level energy [34]. Other experimental details and the spectrum processing can be found elsewhere [7][8][9][10][11].
The XPS studies were performed on a Phoibos 150 SPECS spectrometer (Germany) using monochromatized Al K α radiation (1486.7 eV). The backgrounds of external and surface energy losses in XPS spectra have been subtracted [35]. Other experimental details, the lowtemperature synthesis technique, and characterization of HOPG, pristine and fluorinated C 2 F can be found elsewhere [36,37]. The Br 2 embedding into C 2 F was performed as in Ref. [38] and resulted in the ~C 2 FBr 0.15 stoichiometry.

Theoretical
Geometric parameters and DOS of the unit cells were calculated by the density functional theory using the Quantum ESPRESSO Software [39] and the nonlocal exchange-correlation functional in the Perdew-Burke-Ernzerhof parameterization [40]. The interactions between ionic cores and electrons were described by the projected augmented wave (PAW) method [41] with the kinetic energy cutoff E cut = 40 Ry (320 Ry for the charge-density cutoff) for a plane-wave basis set. The Gaussian spreading for the Brillouin-zone integration was 0.02 Ry; the Marzari-Vanderbilt cold smearing was used [42], and the van der Waals (vdW) corrections were included [43].
The Pt DOS was calculated using the Perdew-Burke-Ernzerhof functional [44] and the PAW with the optimized lattice constant 3.99 Å. The kinetic energy cutoff E cut = 40 Ry and a 12 × 12 × 12 grid of Monkhorst-Pack k-points were applied.
Half-fluorinated graphite, pristine and imbedded with the Br 2 molecule, was modeled with a bilayer C 24 F 12 and C 24 F 12 Br 2 unit cell, respectively, with the optimized lattice parameters a = 2.49 Å × 3, b = 2.48 Å × 2 for the hex structure and a = 2.50 Å × 3, b = 2.48 Å × 2 for the Bernal structure. The F was attached to C atoms all outside and half inside and half outside a cell (Figure 1) with 40 Bohr space between slabs to prevent the interactions. In latter case, the entry interlayer distance d layer in a C 24 F 12 Br 2 unit cell was taken larger by 2 Å than optimized d layer in a C 24 F 12 unit cell (in order to avoid unrealistic Br 2 F formation or F ↔ Br 2 replacement under relaxation of the system), in line with experimental measurements [46]. All atoms were allowed to move free under an optimization of the unit cells. The Brillouin-zone integration was performed on a 20 × 20 × 1 grid of Monkhorst-Pack k-points [47]. The accuracy was verified by testing the energy convergence. The default numbers of bands were used for free bromine particles.

Inelastic electron scattering in near-surface layer
DAPS theory directs core and primary electrons to nearest vacant states above E F [32]. The larger is the vacant DOS, the larger is the spectral dip, and the lack of free DOS gives no signal. The DAPS technique discovers all channels of the elastic electron consumption, which are specifically related to CEE phenomena and consisted of shake-up and shake-off VB transitions coupled with the threshold core-level excitation of an atom. These channels are electron transitions from the ground σ VB to vacant DOS σ Vac and the vacuum level, whose probability W(E) is in proportion to the corresponding convolution and σ VB , respectively, on the absolute energy relative to E F with a matrix element f(E, σ): The shake-off CEE moves σ VB to free DOS at the vacuum level. According to the Rutherford relation ds / d ~sin 4 (Θ / 2) , the cross-section for the nonrelativistic scattering is efficient for small angles Θ [48,49]. The probability W(E) off in Eq. (1) therefore includes one-dimensional (1D) free DOS. According to Van Hove singularities, the 1D DOS is equal to 0, infinity, and Pt at the energies below, at, and above the vacuum level, respectively [50], as shown in Figure 2(a) (where ϕ Pt = 5.6 eV is the work function of Pt(100) [51]). This provides the resonant CEE behavior and multiple tracing over the adsorbed species (including hydrogen atoms and reaction intermediates) around different thresholds [8][9][10][11]. The shake-off satellite of adsorbed particle is an intense peak of the 1-2 eV base-width and coverage-proportional intensity, which is located at its ionization potential above the Pt threshold. The DAPS spectra in Figure 2 particularly exhibit the σ state of the H ad atom and 1π, 5σ, and 4σ states of the CO ad molecule, which fit published UPS data in Table 1 [52][53][54][55]. Similar accordance between the DAPS and UPS measurements has been found for the adsorbed O, N, NO, and NH species [7].
The Pt shake-off spectrum in Figure 2(b, c) was constructed on the basis of DFT data as follows. The VB was inverted (because the larger σ VB the larger W off (E) in Eq. (1), and the larger the spectral dip); differentiated, and shifted to the higher energy by ϕ Pt . Adsorbed layer makes significant contribution into the DAPS spectrum due to superior surface sensitivity of this technique, whose probing depth 2-3 ML is determined by half the electron mean free path in a solid. The Pt shake-up spectrum in Figure 2(b) corresponds to convolution of the occupied and vacant d states by Eq. (1). The calculated Pt shake-up and shake-off spectra in Figure 2 are close to each other due to strongly localized vacant states at E F and the 1D DOS at the vacuum level, respectively, and because of domination of the equal d zx , d zy , and d xy states in total DOS [30]. An agreement between experimental and simulated spectral fragments in Figure 2 implies regular involvement of the Pt DOS into CEE events, as well as similar matrix elements f(E, σ) for different partial densities of states (pDOS) in Eq. (1) and no symmetry ban for CEE transitions.  the metal atom) [8,10]. Furthermore, the surface plasmon disappears while the bulk plasmon decreases on coverage in Figure 2(b) because of screening by the adsorbed layer, in contrast to behavior of the VB CEE satellites [9]; multiple plasmons were also detected at relevant energy points [7]. Conformity between the calculated and experimental data in Figure 2 indicates that the vacancies, at E F and at the vacuum level as well, are appropriate spots of destination of the electrons under their CEE transitions. Present consideration confirms the generality of CEE phenomena under the inelastic electron scattering in the adsorbed system. The CEE control is an additional tool of electron analyzer for fingerprinting the adsorbed layer and an alternative to the RPES, which requires a tunable synchrotron irradiation and special instrumentation [6]. Besides that, the DAPS provides the vacant state structure and geometrical parameters similar to XANES and EXAFS, respectively [56].
CEE satellites of the adsorbed species accompany the threshold core-level excitation of that neighboring atom, which is bound to the above species, while core-level energies are easily distinguishable. Therefore, the CEE control empowers localization of the adsorbed species over multicomponent surface. CEE regularities in the near-surface layer can be summarized as follows: • Shake-up transitions correspond to convolution of the occupied and unoccupied pDOS of the same atom and likely have no symmetry ban.
• Shake-off transitions are available for the substrate atom and adsorbed species as well, where the former is the energy source; the 1D DOS at the vacuum level is a common VB destination. There is no symmetry prohibition, and the satellite structure is a VB mirrorimage with respect to E F , shifted to higher energy by the work function.
• Plasmon oscillations give evidence for the collective CEE phenomenon.

Conjugate electron excitations in the bulk of a solid
The CEE phenomena occur with high probability in the near-surface layer of 2-3 ML [7][8][9][10]. Electronic affinity between surface and bulk atoms assumes similar channels of the inelastic electron scattering under the core-level excitation, no matter by primary electrons or X-ray irradiation. The photoelectron can partially lose its energy for the CEE transition and exhibits the VB peculiarities in fine XPS spectral structure. By analogy with the above findings, CEE phenomena in the bulk of a multicomponent material, under the nonresonant X-ray core-level excitation, can be characterized as follows: • Shake-off transitions are available, where pDOSs must be considered due to probable difference in their matrix elements. The same ground state (VB), the common destination (the vacuum level), and enough energy excess of any of the photoelectrons should result in analogous energy losses in the XPS spectra of different components of a sample.
• Shake-up transitions are available, in which the convolution should include pDOSs of the same atom. The VB of chemically bound atoms has no preference for a photoelectron to detach its energy for the CEE transition, and so similar energy losses are also expected in the XPS spectra of different components of a sample.
This chapter focuses on the DAPS omitting the allied threshold excitation techniques of the Auger electron and soft X-ray appearance potential spectroscopies, which follow the core hole decay and are complicated, at least, by the electron-core hole interaction [32]. In contrast, the DAPS fixes origination of the core hole, when the electron-hole interaction is not yet occurred or minimal. The same is true for energy losses in the XPS spectra because the photon absorption and the CEE energy dissipation can proceed at once or shortly, thus eliminating or minimizing the electron-core hole interaction, respectively. It is worth noting that CEE events are enabled by belonging of former core and valence band electrons to the same configuration and can be hardly detectable by electron energy loss spectroscopy, while the AES spectra are usually complicated by the background.

HOPG and half-fluorinated graphite C 2 F
DFT runs have revealed that density of states in Figure 3(a), obtained for the C 24 unit cells with the Bernal and hex structure, are similar and close to the DOS of graphite/graphene [58]. The optimized C-C bond length d C-C = 1.42 Å and the interlayer distance d layer = 3.34 Å in hex C 24 also fit to those of the graphite. The Bernal C 24 structure reveals the larger formation energy and smaller d layer by ~0.3 Å due to stronger interaction between the layers as compared to hex C 24 structure.
Conventional satellites at higher energy sides of the XPS spectra correspond indeed to the photoelectron energy consumption. The CEE approach enables complete description of the HOPG XPS C1s spectrum in Figure 3(b) by the combination of shake-up and shake-off CEE transitions.
The satellite ~5.5 eV in Figure 3(b) is assigned to a π plasmon responsible for the π → π* transition [59], although the standard plasmon is related to the collective oscillations of free electrons missing in HOPG [60].This satellite originates rather from the shake-off than from the shake-up p z transition (Figure 3(b)).
There is expected similarity between higher energy tails of the (F) C1s (C is bound to F) and F1s XPS spectrum in Figure 4, which emphasizes the indifference of the VB with respect to energy source for the CEE transition. Fine XPS spectral structures above 10 eV conform well to shake-up (Figure 4(a)) and shake-off (Figure 4 Figure 4 (a, b) evaluate f(E, σ) and the contribution of a particular CEE transition, in total theoretical energy consumption, to fit the experimental photoelectron energy losses.

(b)) CEE transitions calculated by Eq. (1). The matrix elements f(E, σ) in Eq. (1) were accepted unity for a W(E) basis set, while the Y-scale factors in
The π plasmon at ~5.4 eV in Figure 4(a, b) is assigned to the conjugated π bonds in a chain of C atoms [37]. This feature fits the shake-up Cp z transition and accompanies the C1s spectrum, since the π bond is localized exclusively at the Csp 2 atom, not bound to F. Similar feature is exhibited in the C K-and not exhibited in F K-edge XANES spectra of C 2 F [29], and the π plasmon is certainly not observed the XPS C1s spectrum under the lack of π-bonds [61]. Discovery of a similar satellite in the F1s spectrum is rather confusing because F atoms have nothing to do with the π bond between C atoms), but it is quite in line with the CEE model.
The base line shift relative to C1s = 285.1 eV in Figure 4 (C is not bound to F) saves accordance with the DFT data and enables to make a contribution to the energy loss ~5.4 eV to the other shake-off transitions ( (F) Cp y , Fp y , Fp z ). The formation energy of the Bernal unit cell C 24 F 12 is by 0.008 eV higher than that of the hex C 24 F 12 cell, while pDOSs of both structures are very similar. A sizable DOS at E F accepts plasmon oscillations that can give the energy loss at 9.1 or 12.9 eV for 1 or 2 free electrons per a C 2 F fragment, respectively [30].

Br 2 -embedded C 2 F
XPS spectra obtained after the Br 2 intercalation into C 2 F matrix reveal stoichiometry C 2 FBr 0.15 and the lack of new features compared to XPS spectra of the pristine C 2 F (Figure 4); C1s and F1s spectra are in agreement with the same CEE transitions as before the Br 2 embedding. DFT  studies were performed for the Bernal and hex C 24 F 12 Br 2 unit cells #1-9 in Table 2 at the entry angles α 0 = 0 and 90° between the Br-Br axis and C planes and different arrangements of the F atoms (Figure 1).
DFT calculations have revealed that the Br 2 embedding enlarges the interlayer distance, but insignificantly affects the pDOS of the C, (F) C and F [30]. The latter conforms to chemical inertness of the pristine C 2 F cell and to low Br content in the product C 2 FBr 0.15 [62]. Invariant pDOS of the C and F atoms and slight change in the C1s and F1s XPS spectra, after the Br 2 embedding into C 24 F 12 framework, restrain the correlation between XPS and DFT outputs. The novelties of XPS and DFT data, which are resulted from the Br 2 embedding, concern the bromine only and are considered in more detail. . XPS C1s and F1s spectrum of C 2 F (relative to E Core = 287.6 eV and 687.4 eV, respectively; the background of external and surface energy losses are subtracted [35]) and shake-up (a) and shake-off (b) transitions of (F) C and F atoms forming the C-F bond in the unit cell hex C 24 F 12 (all F are outside). (c) Shake-up and (d) shake-off CEE transitions for different arrangements of the F atoms (Figure 1). Adapted from [31].
The difference F1s spectrum in Figure 5 exhibits a distinct structure, which conforms to shakeup transitions of the pDOS responsible for C-F bonding and which is interpreted as the C-F bond strengthening [30]. It can be the case since the Br 2 embedding weakens the interactions between carbon layers, which should be accompanied with the enrichment of the occupied DOS of C and F. Arrangement of the F atoms in a cell makes no matter for the conclusion.
DFT studies have found a set of cells C 24 F 12 Br 2 with the optimized parameters and different local geometry and the state (atomic, molecular, and chain type) of the embedded Br 2 ( Table 2). Each of nine local structures is appropriate; no preference can be given to a particular cell from the conventional DFT study.Each of these unit cells is characterized by the specific Br pDOS structure [30]. DFT examinations of separate bromine species revealed a strong difference Δ s-p = 0.2-1.3 eV between the weighted average energy <E s,p > of the Br s-and p-DOS, far beyond the accuracy of DFT runs ~0.01 eV ( i for the Br atom with single, several localized, and diffused s-and p-DOS, respectively. In the same way, as the binding energy determines the oxidation rate in extensive XPS practice; the parameter Δ s-p was taken as a descriptor of the Br state [30]. For the unit cells with all F atoms outside, the minimal deviations Δ s-p of 0.02, 0, and 0.04 eV make preferable the cells #1, #2, and #3, respectively ( Table 2). Moreover, in case of the large d BrBr (the Br-Br bond is lost), the difference Δ s-p in a cell should be close to that of free Br  (Table 1). Besides, the reaction C 24 F 12 + Br 2 → C 24 F 12 Br 2 is endothermic for cell #1, in contrast to other cells [30].
The bromine p z -and s-shake-off transition conforms to the nonresolved 5-12 eV fragment and ~20 eV shoulder of the Br3d spectrum in Figure 6(a), respectively. The higher energy parts of the XPS Br3d, F1s and C1s spectra are similar [30], but they do not correlate with any of the Br CEE transitions. This indicates such a bonding between the Br 2 molecule and the C 2 F frame that provides the Br3d photoelectron energy losses via CEE transitions of pDOS of the C and F atoms.
DFT calculations for the unit cells C 24 F 12 Br 2 , with the F atoms half inside and half outside a cell, have revealed two stable Br 2 states. The first state, in cells #7 and #9, corresponds to Br 2 pairs ( Table 2), which are separated from each other in the adjacent cells and exhibit the same Br-Br distance d BrBr ~2.29 Å as in a free Br 2 molecule. The second state (cells #6 and #8) corresponds to Br arrangement as the chain, in which d BrBr ~2.44 Å within a unit cell is larger than in a free  Table 2 with different layout of the F atoms (Figure 1). Br 2 , while nearest distance between the Br atoms of the adjacent cells 2.73 Å is smaller than the nearest intermolecular distance in a solid Br ~3.37 Å [63] and still enough for the vdW interaction [45]. There is no visible difference in the Br pDOS of cell #6 and #8 (chain type Br), while there is a few difference between the Br p x and p y states for cell #7 and #9 (molecular Br 2 ). Finally, the weighted average Δ s-p values are line with the molecular Br state for cells #7 and #9; the state close to Br  Table 2).
The ~20 eV shoulder in the Br3d spectrum in Figure 6(b) conforms well to shake-off transition of the s-state in unit cells #8 and #9 with different arrangement of the Br atoms, and there is no solid reason to give preference to a particular cell. The shape and location of the 5-12 eV spectral fragment in Figure 6(b), with due regard to the baseline of this energy region, are consistent with a comparable mixture of CEE transitions calculated for the unit cells #8 and #9. According to DFT data, there is a little difference between cells #6 and #8 (chain type Br) with respect to the shake-off p y transition, while the cell #6 wins #8 by ~5% in the formation energy. On the contrary, using the cell #7 hex instead of #9 Bernal (molecular Br 2 ) results in larger discordance with the XPS data due to their specific p x structure. Finally, the unit cell C 24 F 12 Br 2 #6, with the chain type Br layout, is preferable among others, whereas the energy losses in the Br3d XPS spectrum suggest a mixture ~1:1 of unit cells #6 and #9.
Experimental data have reported the angle α ~30° between the Br-Br axis and C-planes and the molecular Br 2 state for similar to C 2 FBr 0.15 systems [38,46]. The current combination of XPS and DFT outputs suggests possibility of the chain like bromine arrangement, which can   Table 2, which have been found for the most probable unit cells #2, #6, and #9, respectively.

Outlook
Any novel approach, including the CEE model, can be truly evaluated by a benefit from its practical application. By an example of the graphite based materials, the chapter has shown how a confluence of the XPS and DFT data can provide additional information on chemical behavior, local geometry and state of the embedded Br 2 molecule and of the other atoms in a sample. A similar treatment can be useful in the field of surface engineering as well, because just a deep knowledge on chemical behavior of a sample can disclose the mechanism and dynamics of its wear performance, thus facilitating the development of advanced materials. The valence band of chemically bound atoms is insensitive to a photoelectron, whose energy it uses for the CEE transition. Then, in the case of the multicomponent materials, agreement or disagreement between energy losses in the XPS spectra of some atoms can be a descriptor of the presence or absence of chemical bonding between these atoms in a sample [17,19,22]. Moreover, the state of any component can be traced through change or invariability of the satellites in its XPS spectra, obtained in the course of external influence, thus revealing a wear performance of the material. In case of a "simple" material, the reliable structural data can be used as starting conditions for the appropriate DFT run, which gives comprehensive information on a sample at the atomic level [16,18]. Extensive use and practice of the XPS and DFT techniques make the CEE analysis easily accessible.
CEE control in a coordinated XPS and DFT study is characterized by the following obvious, verified, and hidden resources.
• Comparison of fine XPS spectra with the calculated CEE transitions can provide the local geometry and bond types in a sample from conventional DFT facilities. The occurrence and consequence of bonding between atoms can be also determined, because the core-level excitation of an atom is accompanied by CEE satellites of the next one only within the integrated valence band.
• The multiple CEE controls (around different XPS peaks) facilitate the data interpretation, while individual sets of the core-level energies improve studying of the multicomponent materials.
• Hydrogen tracing by the XPS, as a specific CEE satellite above the core-level energy of the other sample component, is possible without a contradiction with XPS principles.
• The CEE control is available for samples of any conductivity, because the photoelectron energy losses are linked up to the XPS peak regardless its apparent core-level energy.
• The valence band structure in the XPS spectra differs from that obtained by the nondestructive and theoretical methods. The CEE event is nondestructive as well, because the valence band absorbs only a part of the photoelectron energy for a CEE transition, omitting a destructive force of the incident X-ray impact.

Conclusion
Primary collecting of the extra data by a routine technique is always desirable. This chapter highlights a rational model that gives a chance to realize this desire using the conventional XPS and DFT outputs. The model is based on following statements.
• Electronic configuration of the atoms in a solid holds the traps for the energy absorption, such as valence band electron transitions; and the core-level excitation of any origin fills those traps forming the multiple channels for energy dissipation.
• These channels can be traced by the XPS, as the photoelectron energy losses, and by the DFT, as the valence band electron transitions. This pattern does not conflict with general concepts of electron-solid interaction and has been well verified in model studies of Pt and graphite-based materials.
• Intersection of the XPS and DFT outputs carries out two duties. First, it rejects those DFT results which do not conform to the fine XPS spectral structures. Second, it justifies the assignment of the refined DFT data, related to an appropriate unit cell, to a given XPS sample. As a result, the correlated XPS and DFT study discloses hidden potentialities of both techniques and provides the extra data on chemical behavior and local geometry of the atoms in a sample.
• The procedure of a coordinated XPS and DFT study being highlighted can provide a deeper insight into the mechanism of wear performance of the material, thus facilitating the development of advanced composites.