Nanolevel Surface Processing of Fine Particles by Waterjet Cavitation and Multifunction Cavitation to Improve the Photocatalytic Properties of Titanium Oxide Nanolevel Surface Processing of Fine Particles by Waterjet Cavitation and Multifunction Cavitation to Improve the Photocatalytic Properties of Titanium Oxide

Titanium oxide particles were treated by water jet cavitation (WJC) generated and multif- unction cavitation (MFC) using an ejector nozzle. Generation, growth, and collapse of cavitation are repeated with the particles of titanium oxide and platinum. Because the cavitation has an extremely high collapse pressure, the surface of the titanium oxide particles is processed by the microjets of cavitation in a reactor comprising the ejector nozzle. In the multifunction cavitation, ultrasonic irradiation of a waterjet during floating cavitation was used to generate microjets with hot spots. Hot working can be performed at the nanoscale on a material surface using this MFC process, resulting in morphological changes and variations in the surface electrochemical characteristics. The fundamental characteristics of multifunction cavitation were investigated theoretically and experimentally. Furthermore, the additional nozzle was put on the ejector nozzle in order to increase the temperature and pressure of bubble and the mechanism was clarified. The quantities of hydrogen and oxygen generated from titanium dioxide particles treated by multifunction cavitation in response to UV and visible light irradiation were remarkably increased compared to the amounts produced by particles treated by WJC processing. In this chapter, the methods and their results of processing particles by cavitation are introduced.


Introduction
In recent years, a variety of industrial applications have been identified for cavitation processing, including peening, surface and molecular structure modifications, fatigue strength improvement, and surface cleaning. Waterjet cavitation involves imparting mechanical action to the surface of a material as the result of the extremely high pressures generated during the collapse of a microjet close to the surface [1]. In contrast, ultrasonic cavitation is known to generate hot spots that can promote chemical reaction by producing temperatures of several thousand K [2]. The authors have developed the multifunction cavitation, which is caused by ultrasonic irradiation of a waterjet during floating cavitation to generate microjets with hot spots. This technique combines the properties of both waterjet and ultrasonic cavitation. Furthermore, the additional nozzle was put on the waterjet nozzle (ejector nozzle) in order to increase the temperature and pressure of bubble. The generation mechanism of ultra-high temperature and pressure cavitation was clarified theoretically. The multifunction cavitation was applied to the enhancement of the photocatalytic properties of titanium oxide under visible light.
At present, there are many technical challenges associated with the development of new energy sources as alternatives to thermal and nuclear power generation. Since the use of hydrogen as a fuel generates only water, hydrogen is seen as a potential clean energy source that does not produce hazardous exhaust gases such as carbon monoxide (CO), hydrocarbons (HCs), or nitrogen oxides (NOx). Hydrogen generation via the decomposition of water using a photocatalyst has been studied extensively, and photocatalytic hydrogen generation under UV irradiation has been developed, typically using titanium oxide as a substrate. Ideally, this technology would exhibit high efficiency in the visible light portion of the electromagnetic spectrum. The study reported herein represents an attempt to move closer to this goal by developing highly efficient, visible light-responsive photocatalyst materials [3].
Titanium oxide (TiO 2 ) is widely used as a white pigment in paints, UV absorbing materials, and cosmetics. It is both inexpensive and safe, and can even be used as a food additive. In addition, the application of titanium oxide to photoelectrodes and photocatalyst materials with applications in solar energy conversion is also anticipated [4]. The TiO 2 photocatalyst reaction proceeds most efficiently under irradiation by UV light (350 nm). However, only a portion of the sun's emission spectrum is at this wavelength, so it is important for effective energy conversion to be able to use visible light, which comprises one half of the solar energy output. There have been many studies attempting to append other compounds to titanium oxide-based catalysts to obtain visible light responsiveness, but none have successfully produced hydrogen using these catalysts. Previously, we developed a new method for the nanoscale processing of TiO 2 particles as well as a new technique for adding a Pt co-catalyst to TiO 2 particles [5]. Furthermore, TiO 2 particles were processed by multifunction cavitation [6][7][8][9][10][11] in order to modify the surface morphology and electrochemical surface condition. It was determined that multifunction cavitation is effective at improving the photocatalytic properties of TiO 2 under visible light irradiation.
2. Theory of multifunction cavitation and ultra-high temperature and pressure cavitation 2.1. Multifunction cavitation mechanism Figure 1 shows the mechanism of our multifunction cavitation process, in which ultrasonic radiation is imparted to the cavitation cloud generated by a high pressure waterjet. In this method, the microjets generate mechanical action, but so-called "hot spots [12]" at which chemical reactions can occur are also formed. As the ultrasonic cavitation proceeds, isothermal expansion takes place once the pressure is above the Blake threshold value. Following this expansion, Rayleigh shrinkage occurs. Repeated expansion and shrinkage leads to cavitation, which in turns results in high pressure collapse and the generation of high temperature hot spots. In the conventional heat treatment of metals, the application of heat treatment after cold working is quite different from cold working after heat treatment. In contrast, multifunction cavitation has the capacity to allow so-called microlevel or nanolevel forging, in which the material is simultaneously worked and heat treated.

Blake threshold
The liquid pressure in the vicinity of the bubble wall, p B , may be expressed as follows: Here, the surface tension, σ, is defined as the surface energy per unit area. In the case of pure water, this value is 7.275 Â 10 À2 (N/m) (J/m 2 ) at 20 C. The other terms in this equation are the bubble radius R, the equilibrium bubble radius Ro, the static pressure p 0 (normally, 1 atm), and the vapor pressure p v .
When the heat exchange between the bubble and the surrounding liquid is negligible, thermally insulated conditions can be assumed and Here, γ is the heat capacity ratio, equal to the ratio of the molar heat capacity at constant pressure to the molar heat capacity at constant volume (in the case of air, γ = 1.4). When the expansion and the shrinkage of the bubbles is minimal, the process becomes isothermal and k = 1. According to Eq. (1), in the case of an air bubble with Ro = 10 μm in water at 20 C, the minimum value of À0.014 bar occurs at a bubble radius of 30 μm. If the liquid pressure falls below À0.004 bar during the ultrasonic irradiation, the bubble is able to expand greatly.
The minimum value of p B (p B,min ) required to expand the bubble can be obtained from Eq. (2): When ultrasonication is applied to the liquid, the liquid pressure at a distance from the bubble wall can be expressed by p 0 þ p s t ð Þ. Here, p 0 is the atmospheric pressure and p s(t) is the pressure induced by ultrasonication at time t. The time-dependent term can be expressed as p s t ð Þ ¼ A sin ωt, where A is the sound pressure amplitude and ω is the angular frequency. Therefore, the minimum value of p s(t) is ÀA and the bubble is able to expand at the point at which the value derived from Eq. (2) is equal to p 0 À A. This condition can be summarized by the following equation: Thus, the bubble will overcome the effect of surface tension (that is, the Laplace stress) and expand significantly when A ≥ A Blake , where A Blake is the Blake threshold value [13].
In the case that the bubble radius is less than the equilibrium radius, a high sound pressure is necessary to expand the bubble. However, when the bubble radius is greater than the equilibrium radius, the Blake threshold value is approximately equal to atmospheric pressure. Therefore, because the diameters of bubbles being circulated in the waterjet are typically more than 100 μm, cavitation can readily proceed without the application of especially high sound pressure.
As noted above, the application of ultrasonication during conventional waterjet cavitation (or floating cavitation), generates both high pressure and high temperature cavitation through repeated isothermal expansion and compression under thermally insulated conditions.

Multifunction cavitation induced by low pressure liquid flow
During the flow of an ideal liquid, the external pressure p 0 in any infinite direction (that is, atmospheric pressure), the pressure p, and the velocity v, are related according to Bernoulli's theorem: Here, g is the acceleration due to gravity and γ is the specific gravity of the liquid. From this relationship, the following equation is derived: Here, p (or p v ) is the pressure at an arbitrary point and the density of the liquid is expressed by r ¼ γ=g.
As p 0 decreases or v is increased, p is reduced. When the p v term of Eq. (3) is substituted for the p term in Eq. (5), the following formula is obtained, which expresses the conditions required for cavitation expansion: The flow rate at a far distance v 0 is zero and the relationship between v and the Blake threshold value is shown in Figure 2(a). The flow rate v is calculated to have a value of 4.52 m/s when the Blake threshold value becomes 1 bar. This result indicates that elevated sound pressure is necessary in order to expand the cavitation at high flow rates.

Multifunction cavitation induced by liquid flow circulation
Normal waterjet cavitation (or flow cavitation) is typically generated by the application of high pressure waterjets using underwater nozzles. In such cases, the low pressures induced by the whirlpool motion of the fluid result in cavitation.
In the case of a potential flow, the circulation Γ can be defined as follows: This value is not uniform but rather varies with the radius rc from the internal nucleus. The pressure p at a given radius position r c will be less than the pressure p 1 at a position associated with a wider radius r 1 , and may be expressed as follows: Because r c = 0 at the nuclear center, the pressure at the center p m represents the minimum pressure, and may be calculated as in Eq. (9): When the pressure at the nuclear center, p m (p v ), equals the saturated steam pressure at the temperature in the region around the flowing water, cavitation will occur. In the case of high pressure waterjets from a nozzle, a circulation whirlpool is formed in the vicinity of the nozzle exit, resulting in flow cavitation. In the case that the equilibrium radius of the air bubble is R 0 , and substituting p m for p v (the steam pressure) in Eq. (3), the conditions necessary for whirlpool cavitation are achieved, as expressed in the following equation: At high values of the flow velocity u from the waterjet nozzle, circulation is increased, and when R 0 equals the circulatory nuclear radius r 1 , the following equation holds true: Assuming circulation of the nuclear radius, the following expression can be written: Because the first term on the right hand side of this equation has the greatest effect and the Break threshold increases, significant sound pressure is required to inflate the circulation bubble when the circulation becomes overly large. Figure 2(b) presents the relationship between u and A Blake . At an A Blake value of 1 bar, the value of u is 3.2 m/s. Under these conditions, high sound pressure is needed to inflate the circulation bubble because the cavitation flow rate in the area of the nozzle exit is more than 100 m/s. These results demonstrate that multifunction cavitation should take place far from the nozzle exit.
As noted, the introduction of ultrasonic irradiation to floating cavitation can result in isothermal expansion. In this technique, the supersonic wave is a primary wave and the pressure pitch repeats with a period of wavelength λ. As an example, in the case of an underwater sound velocity of 500,000 mm/s, λ is 1,500,000 mm/s / 28,000 Hz = 53.6 mm when employing a 28 kHz supersonic wave.

The Rayleigh-Plesset equation
The expansion and shrinkage of bubbles may be expressed using the Rayleigh-Plesset equation [14,15] shown below: Here, R is the bubble radius, σ is the surface tension, p g is the gas pressure, p 0 is the static pressure, p v is the vapor pressure, and p s t ð Þ is the sound pressure at time t. The acceleration rate shown below in Eq. (14) can be obtained from Eq. (13).
When a bubble shrinks severely, such that R Á 2 increases, the first term on the right-hand side will be important while the second term can be ignored, and Eq. (15) is obtained: The acceleration R ÁÁ of the air bubble wall will always be negative, indicating that the velocity decreases. When an air bubble shrinks, R Á < 0 and this decrease in the shrinkage rate tends to increase the value of R Á . That is, the right side of Eq. (15) increases to generate a larger negative value. Therefore, the acceleration rises and there is a more pronounced drop in the velocity. The air bubble shrinkage accelerates automatically and become increasingly large; this is termed Rayleigh shrinkage or Rayleigh collapse.
The air bubble shrinkage continues to accelerate, with gas molecules and steam within the bubble. As such, the pressure in the bubble rises and a portion of the gas dissolves in the liquid around the bubble. In addition, a part of the steam condenses on the bubble interior wall and returns to a liquid. However, many gas molecules and a quantity of steam remain because of the constrictive speed of the bubble. Therefore, the pressure in the bubble continues to rise. The high rate of shrinkage of the bubble also causes heat generated by the shrinkage, and transmitted to neighboring liquids by outward flow from the air bubble interior, increasing the thermal energy of the bubble. This represents the adiabatic process that occurs in conjunction with so-called insulated compression. The temperature in the bubble increases and the pressure p g also rises.
The value of p g increases especially rapidly, from 10 to 100 MPa, as the bubble is compressed and the internal density eventually matches that of the surrounding liquid. As a result, term 2 on the right side of Eq. (14) increases and the acceleration of the air bubble wall takes on a large positive value such that the air bubble shrinkage ceases. At this point, the temperature in the bubble can exceed several thousand K.
The cavitation resulting from low flow pressure has a size of more than 100 μm, a value that is larger than that associated with ultrasonic cavitation, since the size of the inner part of the bubble is limited by the vapor pressure of the water. It is a characteristic of this cavitation collapse pressure that it is larger than that associated with ultrasonic cavitation. The cavitation generated by low flow pressure and circulation is associated with expansion and shrinkage, leading to multifunction cavitation. Multifunction cavitation involves larger bubbles with higher temperatures and pressures than those generated during conventional cavitation processes, increasing the work ratio of the microjets.
The mechanism described above transitions floating cavitation to the multifunction cavitation process in which hot spots are generated. This multifunction cavitation is applied to the solid surface as soon as the cavitation starts to collapse, and the associated decrease in the cavitation volume in conjunction with the high velocity waterjet generates a so-called microjet, just as in conventional cavitation. Because the microjet in this new process is capable of both mechanical and electrochemical action, it can generate changes in both surface morphology and chemical characteristics of the material being treated. Thus, multifunction cavitation is anticipated to have applications in various industrial fields, including photocatalysis, clean energy, medical care, chemistry, and engineering.

Ultra-high temperature and pressure cavitation
In order to generate the high-temperature and high-pressure cavitation, the effect of placing an additional nozzle on a waterjet nozzle is evaluated experimentally and theoretically. Instead of a waterjet nozzle, the ejector nozzle is attached to the additional nozzle to measure the static pressure around the exit point of the waterjet nozzle, as shown in Figure 3     no additional nozzle is combined to is À8.5 kPa. On the other hand, the static pressure at the exit of ejector nozzle in the swirl flow straight nozzle shown in Figure 1 is a high negative pressure of À36.5 kPa. The negative pressure of the swirl taper nozzle further decreases to be À47.5 kPa. The static pressure at the exit point of the waterjet nozzle decreases with the increase of dynamic pressure caused by a high flow rate. The static pressure when there is only the waterjet nozzle with no additional nozzle combined with it is À8.5 kPa. On the other hand, the static pressure at the exit point of the ejector nozzle in the swirl flow straight nozzle shown in Figure 1 has a high negative pressure of À36.5 kPa. The negative pressure of the swirl taper nozzle further decreases to À47.5 kPa.
In a swirl flow straight nozzle and a swirl flow taper nozzle, the surrounding water enters through the inflow pipe and the swirl flow occurs due to the static pressure decreasing at the exit point of the waterjet nozzle. When the inflow hole is closed, the static pressure at the nozzle outlet portion is À3 kPa, and the negative pressure becomes smaller than À6 kPa when the swirl nozzle is not attached. This is probably because the supply of ambient water is restricted as compared to when there is no additional nozzle, so the fluid pressure in the swirling nozzle increases, the inflow of high pressure water decreases, and the dynamic pressure at the outlet decreases.
The discharge pressure of the high-pressure pump used in this experiment was 35 MPa and the flow rate was 15 L/min, but when a waterjet nozzle with a nozzle diameter of ϕ 0.8 mm was used, the measured value of the flow rate was 6.9 L/min. The flow velocity of nozzle discharge obtained from the nozzle sectional area is 229 m/s.
An increase in the number of occurrences of cavitation due to a swirling flow in the nozzle and a pressure required for bubble expansion are obtained. When the internal pressure p n of the swirling nozzle becomes negative, the flow velocity v i in the inflow hole can be obtained by Eq. (16). Here, the pressure p i at the entrance of the inflow hole is set to atmospheric pressure. In practice, however, it is necessary to consider the tube inlet loss and tube friction pressure loss. The pressure loss is expressed by Eq. (17), the actual pipe flow rate u is expressed by Eq. (18), and the flow rate Q is expressed by Eq. (19), with the pipe inlet loss coefficient ζ being 0.5 and the tube friction coefficient λ being 0.03.
Here, the inlet loss coefficient ζ in: 0.5, the pipe friction coefficient λ: 0.03, d: pipe inner diameter (20 mm) The relationship between the pressure p n at the outlet of the waterjet nozzle and the flow velocity u within the pipe and the relationship between the pressure p n at the outlet of the waterjet nozzle and the flow rate Q within the pipe are shown in Figures 5 and 6, respectively. As shown in Figures 5 and 6, the flow rate was 6.83 Â 10 À4 m 3 /s and the flow rate was 2.17 m/s at the swirling straight nozzle (one inflow hole) having a pressure of À36.5 kPa at the outlet of the waterjet nozzle, and the waterjet had a flow rate of 7.79 Â 10 À4 m 3 /s and flow velocity of 2.48 m/s in the swirling taper nozzle (2 inflow holes) with the nozzle outlet pressure of À47.5 kPa.
After entering at 7 , a swirling flow is formed, but it was assumed that the inner wall of 64 mm of the SFN nozzle was the earliest swirling flow. Thus, the maximum radius of the swirling flow was 32 mm, which was half of the 64 mm inner diameter of the SFN. The vortex flow that has flowed into the swirl nozzle can be treated as a circulation Γ defined by the expression (20).
Here, the circulation of the bubble nucleus is Γ, r c = 0, the pressure at the center is p m, the pressure in the swirl nozzle is p n , and the circulation radius is r. An arbitrary pressure p in the vortex is given by Eq. (21).
However, with the actual vortex, this state cannot be continued to the center, and it forms the core part corresponding to the strength of the vortex. Inside the nucleus, the value of the circulation is not constant and varies according to Eq. (22) by the radial position r c .
Considering the flow in this swirl nozzle, the radius r 1 of the nucleus is determined as the turning radius obtained from the position of the inflow hole. The circulation Γ increases as the inflow velocity increases and the pressure p m of the swirl center (nucleus center) is further reduced as compared with the nozzle exit pressure p n as shown in the Eq. (23).
It is considered that the negative pressure increases from the one-hole swirling straight nozzle to the two-hole taper nozzle, as shown in Figure 7.
Cavitation number is a dimensionless number used for analysis of cavitation in hydrodynamics. It is mainly used for analyzing fluid machinery using a liquid such as a pump, water piping, and hydraulic equipment. The cavitation number Ca is defined as a dimensionless version of the difference between the pressure of the liquid and the vapor pressure, and is expressed by Eq. (24), where p m is the absolute pressure, p v is the vapor pressure (20 C), (1/2)rv n 2 is the representative pressure (dynamic pressure), r is the fluid density, and v n is the representative velocity of the flow (swirl center flow velocity).
Ca = 1 at the cavitation generation point, and when Ca < 1, cavitation occurs in this piping system. The smaller the cavitation number, the more easily cavitation occurs. The faster the representative speed of flow, the easier the cavitation occurs. Generally, when the temperature is high, the vapor pressure rises, so cavitation tends to occur.
In this study, the flow velocity from the nozzle exit is estimated from the spreading of the free jet from the waterjet nozzle, and Figure 8 is obtained when the cavitation number is obtained.
Compared with the case when there are no additional nozzles, it can be seen that the number of cavitation increases for a one-turn swirl straight nozzle, and furthermore that the two-hole swirling taper nozzle tends to generate more cavitation bubbles. As a result, the number of waterjet bubbles flowing out of the additional nozzle and being irradiated with ultrasonic waves increases, and more high-temperature and high-pressure cavitation is generated.
The liquid pressure p B in the vicinity of the bubble wall is expressed by Eq. (25). As shown in Figure 9, in the case of the initial bubble radius R 0 = 10 μm, when the pressure (liquid pressure) around the bubble reaches a minimum value of 0.003 bar (absolute pressure) or less, the bubble can expand greatly.
Here, p v is the water vapor pressure, p 0 is the ambient pressure, σ is the surface tension, R 0 is the equilibrium radius, R is the bubble radius, and κ is the specific heat ratio (1-1.4).   shows the pressure and bubble radius of the process of bubble growth when the bubble radius is 10, 100, 150, and 200 μm at 1 atm. When the swirl flow nozzle (SFN) is used, the pressure is reduced to an absolute pressure of about 0.6 atm (dashed line), so that the bubbles increase by about 20% at each size. In addition, in the multi-bubble state, a local low-pressure region is formed due to bubble collapse. Therefore, as shown in Figure 9, large bubbles tend to expand with lower pressures, and when the pressure is lower than the critical pressure, the bubbles expand greatly. The addition of a negative sound pressure, such as by irradiation with ultrasonic waves, is required to reduce the pressure below the critical pressure. As described above, the swirl flow nozzle rapidly expands the numerous bubbles produced by the WJC. As a result, bubbles flowing out of the swirl flow nozzle produce ultra-high-pressure cavitation.
Further, when the swirl flow nozzle is tapered, the circulation radius gradually increases and the pressure at the circulation center decreases, so that it is possible to further increase the size of the bubble and achieve high temperature and high pressure (see Figures 7 and 8). Figure 9 shows the dependence of initial bubble radius on temperature and pressure of hightemperature and high-pressure cavitation bubbles. The initial bubble radius of the conventional ultrasonic cavitation and that of the multifunction cavitation is assumed to be 4 and 100 μm, respectively. On the other hand, the initial bubble radius of the ultra-high-temperature and pressure cavitation is supposed to be 300 μm, owing to the expansion by the SFN. The isothermal expansion and adiabatic compression provides the increase in temperature and pressure. In conventional ultrasonic cavitation, the bubble pressure can be increased only to 10 MPa, but it is 1 Â 10 5 MPa in the conventional functional cavitation and over 5 Â 10 6 MPa in the ultra-high-temperature and high-pressure cavitation using the swirl flow nozzle. In the conventional ultrasonic cavitation, the temperature can be raised only to 3900 K, whereas the temperature increases remarkably to 1 Â 10 8 K in the multifunction cavitation. On the other hand, in the conventional ultrasonic cavitation, the temperature can be raised only to 3900 K, whereas the temperature increases remarkably to 1 Â 10 8 K in the multifunction cavitation. The bubble temperature of 1 Â 10 10 K is obtained in the super-high-temperature and highpressure cavitation using the SFN. However, in fact, at the final stage of contraction, although the increase in the bubble temperature is suppressed by chemical reaction heat and heat conduction accompanying the thermal decomposition of steam, it is handled as a qualitative comparison in the calculation formula. In conventional measurement data of sonoluminescence, it is considered that the maximum bubble temperature is 100,000 K, and it is considered that this temperature has been reached in this calculation ( Figure 10).

Experimental
Previously, we developed an ejector nozzle that can produce mechanochemical cavitation. As shown in Figure 11, sub-stream suction occurs in small-sized high-pressure ejector nozzles because the dynamic pressure of the high-pressure water in the nozzle can increase. Moreover, the sub-stream contains water, TiO 2 particles, and Pt particles mixed with the high-pressure water. In the ejector nozzle, the generation, growth, and collapse of cavitation are repeatedly applied to the surfaces of the titanium oxide and platinum particles. Because the cavitation has an extremely high collapse pressure, the surfaces of the titanium oxide and platinum particles are processed by the cavitation microjets in the ejector nozzle reactor. The surface area of the titanium oxide and platinum particles should increase, which would lead to the increment of reaction activation point and improved photocatalysis. For comparison with the cavitation processed powder, titanium oxide particles and mixed titanium oxide and platinum particles were immersed in water and stirred with a magnetic stirrer. This represents a more conventional approach, in which TiO 2 and Pt particles undergo simple mixing in solution via a magnetic stirring mechanism [16]. Generally, the Pt or other co-catalyst is added to TiO 2 in a concentration range of 0.1-1.0 wt% when investigating photocatalytic properties [17], and it has been reported that a Pt content of 0.75 wt% in Pt-TiO 2 produces the best photocatalytic performance [18]. However, since it was anticipated that some of the Pt in the sub-stream would be lost during the Ejector Cavitation (EC) processing, a TiO 2 to Pt ratio of 10:1, which corresponds to 9.1 wt% Pt, was also employed for comparison. In order to compare the results of EC processing with the results obtained by processing with simple ultrasonic cavitation, a TiO 2 -9.1 wt% Pt (1 μm) particle mixture was suspended in water and subjected to ultrasonic irradiation for 30 min. In these trials, the frequency of the ultrasonic waves was 38 kHz and the power output was 100 W. The particles processed via EC, ultrasonic cavitation and simple stirring were all collected by heating the solutions to evaporate the water.
Titanium oxide may adopt three different crystal structures, each with the chemical formula TiO 2 . The first is rutile-type, the second is anatase-type and the third is brookite-type. The anatase-type and the rutile-type are typically used in photocatalysis studies. The anatase-type has better photocatalytic properties than the rutile-type, although the rutile-type tends to absorb light with longer wavelengths (closer to visible light) than the anatase-type. The rutiletype TiO 2 used for experimental trials was obtained by the chlorine method (also known as the gas phase method). The TiO 2 content of the resulting material was 99.997%, the average particle size ranged from 200 to 300 nm, the rutilation coefficient was 100% as measured by X-ray diffraction, and the specific surface area was 6.57 as assessed by the BET method. The anatase-type TiO 2 employed in this work was TIPAQUE ® A-100, synthesized by the sulfuric Figure 11. Cavitation processing of a photocatalyst powder by the ejector reactor.
acid method (the liquid phase method). A-100 is small-particle, sulfate-processed anatase that exhibits greater brightness and a more bluish color tone than rutile. The non-surface treated product is less durable, but has good self-cleaning properties and is sufficiently versatile that it can be used in cosmetics as well as industrial-type applications such as plastics, rubber and traffic paints. The average particle size of the material was 160 nm, the TiO 2 content was 98%, its oil absorption was 22/100 g and its pH ranged from 6.5 to 8.0. The platinum particles were greater than 99.0% pure and had a bulk density of 3.80 g/cm 3, a specific surface area of 20.99 (as measured by the BET method), and a loss on drying of 0.29% on heating to 80 C. Figure 12 shows the equipment used to measure the photocatalytic properties of titanium powders. The cavitation processed particles and the stirred particles were placed on a quartz glass sample stand, and the chamber was exhausted by a turbomolecular pump to a vacuum level of 5 Â 10 À4 Pa. The total pressure was measured by an ionization gauge. The position of the specimen was controlled by the feedthrough motion of magnet coupling. Monochromatic UV light from a xenon lamp source with a wavelength of 365 nm and a power density of 4000 mW/cm 2 was irradiated onto the specimen through a quartz glass viewport. The total amount of UV energy ranged from approximately 200-400 mW, and the focal distance of the lens was 120 mm. The gas generated from the TiO 2 surface under ultraviolet irradiation was measured by quadrupole mass spectrometry (QMS). In the initial 20 seconds of these measurements, the quadrupole mass spectrometry was performed without the ultraviolet irradiation. Then, ultraviolet irradiation and the mass spectrometry were both applied to the specimen for the next 20 seconds. Finally, the irradiation was stopped while the quadrupole mass spectrometry continued for another 20 seconds. Furthermore, LED device emitting light ranging from 400 to 800 nm and having a power density of 100 mW/cm 2 was used to generate simulated sunlight and this light was applied to the test specimen through a quartz glass viewport. The gases generated from the TiO 2 surface under visible light irradiation were quantified by quadrupole mass spectrometry. In the initial 20 seconds of each trial, the quadrupole mass spectrometer was operated without applying visible light irradiation, after which visible light irradiation was applied to the specimen until hydrogen and oxygen generation was detected based on their respective peaks.
The specimen produced by ejector cavitation processing (as shown in Figure 11) did not generate hydrogen through water splitting in response to visible light irradiation, whereas hydrogen generation did occur upon UV irradiation. This can be explained by noting that the energy of UV light is greater than that of visible light. Because the band gap associated with water splitting by the photocatalyst is in the range 3.0-3.2 eV, the generation of holes in the valence band and the movement of electrons to the conduction band are both difficult when the increased reaction points are generated only by nanolevel ejector processing. As noted, multifunction cavitation results in both mechanical and electrochemical processing by the microjet as a consequence of the presence of hotspots and their chemical reaction field. Therefore, reductions in the band gap and the promotion of water splitting would be expected. In present study, the surface potential images of titanium oxide particles was measured by KFM (Kelvin Probe Force Microscope).
A Kelvin force microscope (KFM) was used to measure surface potential. A KFM observes specimen morphology and potential by variations in the work function and the contact potential. "Work function" is the energy required in order to extract a single electron from the surface of the substance, or, in other words, how easy it is to extract hydrogen. This is diagrammed in Figure 13.

Results and discussion
Chemical reactions of the ITO film on the soda-lime glass can also be induced by multifunction cavitation, as shown in Figure 14. The ITO film is composed of In 2 O 3 and SnO 2 and its melting point is in the range of 1800-2200 K, while the soda-lime glass on which the ITO film is deposited has a melting point of 1270 K and is made from a mixture of SO 2 , Na 2 CO 3 , and CaCO 3 . The microjet hot spots were found to peel the ITO film from the glass to generate particles consisting of a combination of the ITO film and the soda-lime glass. Figure 15 presents a surface FE-SEM image of TiO 2 particles supporting minute Pt particles after EC processing. Nanoscale roughness was formed on the surface of the TiO 2 particles after the cavitation processing. The pressure of cavitation collapse was estimated to be approximately 1000 MPa. It is considered that the titanium surface was processed by the micro-jet of cavitation, when the cavitation approaches to the surface of the titanium particles in the ejector reactor.
Because the exit of the ejector nozzle is narrow and has a small gap, the particles are very likely to encounter the cavitation and suffer the micro-jet fabrication in the ejector nozzle. Because the specific surface area of the titanium oxide particles increases, the reaction activation point changes, and the amount of gases generated should increase under ultraviolet irradiation. The Pt nanoparticles were detached from the surfaces of the original Pt particles and attached to the surfaces of the TiO 2 particles, as shown in Figure 15. Such nanoparticles are thought to act as a co-catalyst to promote the photocatalytic reaction. Conventionally, Pt addition is performed using an electrodeposition method [16], in which Pt becomes attached to the titanium oxide surface by stirring Pt and TiO 2 particles in a methanol/water solution under UV irradiation for about 40 hours [16]. In contrast, it takes only a few seconds to add Pt nanoparticles to the titanium oxide surface in case of EC processing. Thus, EC processing is an effective method not only for nanoscale surface processing but also for supporting one substance on another.
After treating the mixture of TiO 2 and Pt particles with multifunction cavitation, nanoscale TiO 2 particles were obtained and were found to agglomerate to produce porous structures, as shown in Figure 16. The microjets resulting from floating cavitation of the waterjet were not able to fabricate nanoscale TiO 2 particles such as these. In addition, the hot work performed by the microjet hot spots tended to melt the TiO 2 particles. It should be noted that Pt co-catalyst particles were also generated during the multifunction cavitation process and were intermingled with the molten, porous TiO 2 .
It may be premature to expect that surface treatment by micro-jet can enhance the photocatalytic properties in emulsified water under visible light. However, the bandgap of rutile-type TiO 2 Figure 15. FE-SEM images of TiO 2 particles supported by Pt particles as a co-catalyst after cavitation processing (Â100,000). (a) Pt particle mixed with TiO 2 and (b) minute Pt particles supporting TiO 2 particles. Figure 16. FE-SEM images of titanium oxide particles (a) as-received, (b) after WJ processing, (c) after MFC processing (Â100,000). is 3.0 eV at a wavelength of 413 nm, whereas the bandgap of anatase-type TiO 2 is 3.2 eV at a wavelength of 388 nm. In this study, a mechanical cavitation jet was used for surface processing in an ejector reactor. If the sub-stream contains not only TiO 2 but also Pt but also a chemical, mechanochemical cavitation is generated. This mechanochemical cavitation has a synergy of mechanical processing and chemical processing in the study of ballast water treatment [19,20] and in the study of improvement of corrosion resistance. The bandgap water splitting should be decreased by the processing of mechanochemical cavitation.
When water is irradiated with ultrasound, acoustic cavitation occurs with the concurrent generation of active oxygen species and shock waves [21][22][23]. Previously, the use of ultrasound was investigated for disaggregation of agglomerated particles and surface modification of diamond nanoparticles [24]. Coating of host particles with guest nanoparticles by ultrasonic irradiation in liquid CO 2 has also been studied [25,26], as well as mixing and conjugation of nanoparticles using ultrasonic cavitation in high-pressure liquid CO 2 [27,28]. Sonodynamic therapy was applied to cancer cells based on the delivery of titanium oxide (TiO 2 ) nanoparticles modified with avidin protein, which preferentially discriminated cancerous cells from healthy cells [29]. Figure 18 compares the amount of hydrogen, oxygen and water generated from EC-processed, ultrasonic cavitation (UC)-processed and stir-processed TiO 2 particles supporting Pt (TiO 2 + 9.1 wt% Pt). It can be seen that gas generation for the UC-processed particles is less than that for the EC-processed material. In this study, the EC processing technique was investigated with the aim of obtaining a new photocatalytic material, and it was shown to represent a potentially useful approach to nanoscale surface processing and synthesis of hybrids of different particles, with applications not only in the field of photocatalysis but also other industrial processes ( Figure 17).
It was found that the work ratio generated by multifunction cavitation could be varied by tuning the pressure and processing duration as well as the power and frequency of the ultrasonic wave. The balance between hot treatment by hot spots in the microjet and high pressure physical working by the microjet is thus determined by both the waterjet and Figure 17. Comparison of EC processing, UC processing and stir processing with regard to amount of gas generation from TiO 2 particles supporting Pt (TiO 2 + 9.1 wt% Pt) under UV irradiation. ultrasonication parameters. In the case of TiO 2 , the highest work ratio was obtained when applying a waterjet pressure of 35 MPa together with a duration of 2 min, an ultrasonication power in the range of 150-300 W (ideally 225 W) and frequencies of 28, 40, and 100 kHz (with 28 kHz being optimal). Figure 18 shows FE-SEM image and elemental maps for TiO 2 particles supporting Pt particles and other compounds produced by processing with multifunction cavitation. As noted, the TiO 2 powder was 99.997% pure and the Pt powder was more than 99.0% pure. Therefore, both materials contained low levels of impurities such as Al, Fe, Si, Na, Mg, and S. In the high potential reaction field of multifunction cavitation, these impurities will gather locally in the porous structure of the TiO 2 . In fact, NaCl crystals can be observed in Figure 16. Figure 19 demonstrates the enhanced visible light photocatalytic properties obtained by processing with multifunction cavitation. The levels of hydrogen and oxygen that were generated following multifunction cavitation were greatly increased compared to the quantities obtained from material treated with standard waterjet processing. Interestingly, even the waterjet processing was more effective than the conventional approach, in which TiO 2 and Pt particles undergo simple mixing in solution via a magnetic stirring mechanism. It should be noted that the quantities of hydrogen and oxygen produced by water splitting under visible light irradiation were in accordance with the expected stoichiometric ratio, indicating efficient photocatalysis.
As experiments showing the effectiveness of MFC, experimental results of WJC processing, UC processing, UC processing after WJC processing, and WJC processing after UC processing were compared (Figures 20 and 21) [30].
A significant increase in the amount of hydrogen generation by MFC processing compared to the other processing indicates that high-temperature and high-pressure microjet is generated, suggesting an increase in the water splitting reaction point due to the increase in surface area. It can also be realized from Figure 17(b) and (c). In addition, there is a high possibility that the band gap of water splitting by MFC treatment was reduced. Compared with other treatment methods, the amount of hydrogen generation dramatically increased in MFC treatment, and it became clear that microjet with hot spot is effective for water splitting. Also from the result of oxygen generation shown in Figure 19, it was confirmed that the amount of oxygen generation dramatically increased by MFC treatment as well.   Figure 22 shows the results for rutile, and Figure 23, for anatase. The images on the left show the results before MFC processing, and those on the right, after processing. Table 1 also provides the measured values of the surface potential.  The results for surface potential in Figure 23 indicate that both rutile-and anatase-type TiO 2 during processing by MFC decreases the surface potential. Also, as Table 1 shows, for an evaluation of the surface potential of a single particle of TiO 2 powder, the mean surface  Nanolevel Surface Processing of Fine Particles by Waterjet Cavitation and Multifunction Cavitation to Improve… http://dx.doi.org/10.5772/intechopen.79530 potential of a rutile-type TiO 2 before MFC processing was 0.554 V, while it fell to 0.272 V after processing, a difference of À0.282 V in the contact potential. In anatase-type TiO 2 , the mean surface potential before MFC processing was 9.928 V, but it fell to 0.166 V after processing, a difference of À9.762 V in the contact potential. The anatase-type TiO 2 showed a far higher reduction than the rutile-type TiO 2 . This advantage of the anatase-type TiO 2 is consistent with its superior results in dissociation of water and with the already-known lower band gap of rutile-type TiO 2 under visible light. Table 2 shows how the measured volume of evolved H as measured with a QMS compared with the surface potential results. In rutile-type specimens, the surface potential fell after processing, while the volume of evolved H increased. This is consistent with the promotion of H generation by the low band gap. There was also a correlation between the difference between evolved H volume and surface potential in both rutile-and anatase-type specimens.
In rutile-type specimens, the surface potential fell after processing, while the volume of evolved H increased. This is consistent with the promotion of H generation by the low band gap. The particles processed by swirling taper nozzle (inflow hole: 2 pieces) of Figure 4 further Table 1. Measured surface potential values. Table 2. Relationship between surface potential and H + H 2 pressure.