Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts by Electrochemical Anodization: Influence of Hydrodynamic Conditions Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts by Electrochemical Anodization: Influence of Hydrodynamic Conditions

Nanostructured semiconductor metal oxides, such as TiO 2 , WO 3 , Fe 2 O 3 or ZnO, are being widely investigated for their use as photoanodes, due to their higher surface areas in contact with the electrolyte, which increases the efficiency of photoelectrochemical processes. Metal oxide nanostructures have been synthesized by a number of different techniques. Anodization is one of the simpler methods used to synthesize nanostructured photoanodes, and the morphology and size of nanostructures can be designed by adequately controlling anodization parameters. Besides, these nanostructures are directly bound to the metallic back contact, improving significantly the efficiency of electron collection. It has been observed that hydrodynamic conditions during anodization (using a rotating disk electrode, RDE) greatly influenced the morphology of nanostructures and, therefore, their photoelectrochemical per -formance. The objective of this chapter is to review the innovative nanostructures with high- aspect ratios that can be fabricated by anodization under different hydrodynamic conditions.


Introduction
Photoelectrochemistry (PEC) is a multidisciplinary area, which involves electrochemistry, materials science, solid-state physics and optics [1], and studies, in general, processes taking place at the interface between an electrode and an electrolyte, under the influence of an illumination source. The most interesting part of PEC is related to the absorption of incident light in a semiconductor valence band. If the incident light energy is high enough (higher than the band-gap of the semiconductor, hυ ≥ E g ), this process results in electron excitation from the valence band to the conduction band, hence generating photogenerated electron/hole pairs (e − /h + ). PEC has numerous attractive applications, such as the split of a water molecule in its fundamental constituents (gaseous hydrogen and oxygen), or the removal of persistent organic pollutants in water treatment processes. The schematic representation of PEC is depicted in Figure 1.
In that scheme, a common PEC cell with an n-type semiconductor photoanode and a metallic cathode (typically Pt) is presented. Upon illumination, electrons are promoted from the valence band to the conduction band and are subsequently driven toward the metallic back contact through the semiconductor bulk and, from there, to the cathode through the external circuit. Once in the cathode, these electrons can be used to reduce the oxidized redox species present in the electrolyte, such as water to form gaseous hydrogen. Photogenerated holes, which remain in the semiconductor valence band, are transported toward the semiconductor/ electrolyte interface, where they can oxidize the reduced redox species present in the electrolyte, such as water to form gaseous oxygen or oxygen compounds, for example, hydroxyl radical, which could, in turn, directly oxidize recalcitrant organic pollutants (R in Figure 1) present in the aqueous solution. The movement of photogenerated charge carriers (e − /h + pairs) described above takes place due to the development of a depleted space-charge region inside the semiconductor, where the electric field acts on these charge carriers. To increase the thickness of this space-charge region and to sustain the electric field built up within it, a small external polarization is used in PEC. This polarization significantly improves the transport of electrons from the semiconductor conduction band to the cathode, hence increasing the lifetime of photogenerated charge carriers, minimizing the recombination of these carriers and, therefore, enhancing the PEC process overall efficiency [2][3][4].
The semiconducting photoanode is the central part of a PEC cell. Consequently, it is essential to develop strategies to fabricate efficient photoanodes, which is a materials science issue. Hence, the development of PEC is closely related to the advances achieved in the design and synthesis of materials used as photoanodes, in which the understanding of their properties and characteristics is fundamental. Among the most important characteristics, an efficient photoanode must satisfy the following [1,5,6]: • Appropriate bandgap energy (E g ). The bandgap is the smallest energy difference between the lowest edge of the conduction band and the highest edge of the valence band. A photoanode material should have bandgap energy high enough as to assure that the desired electrochemical reactions can take place (e.g., ~2 eV for water splitting, taking into account electrochemical losses and kinetic aspects [5], but not so high as to severely reduce the amount of usable solar radiation. • Appropriate band edge positions. For hydrogen evolution, the conduction band edge must be positioned above hydrogen evolution, that is, at a more negative potential than that of the normal hydrogen electrode (NHE). For oxygen evolution, the valence band edge must be positioned below the oxygen evolution, that s, at a potential more positive than 1.23 V versus NHE. For generation of hydroxyl radicals, the position of the valence band edge must be located at potentials as high as 2.02 V versus NHE [7].
• Suitable flat-band potential (E FB ). The flat-band potential is the potential that needs to be applied to the semiconductor to reduce the band bending to zero, that is, at this potential, there is no depleted space charge layer and, therefore, no electric field inside the photoanode. The flat-band potential affects the recombination probability of photogenerated charge carriers: in general, the more negative the value of E FB , the higher the potential drop at the depletion space charge layer and, consequently, the stronger the electrical field within the depleted space charge layer, which is the driving force to separate the photogenerated electron-hole pairs [5,6,8].
• Good electrical conductivity. Once electrons have been promoted from the valence band to the conduction band of the semiconductor photoanode due to light irradiation, a fast charge separation is crucial for efficient photoelectrochemical processes. For this, the transport of electrons and holes in the material must be good. The electrical conductivity of the photoanode material can be modified by modifying its defect disorder. The density of defects inside the semiconductor (i.e. vacancies, interstitial elements, etc.) must be high enough to enhance electrical conductivity but not so high to negatively affect the efficiency by favoring the recombination of charge carriers.
• Good chemical, electrochemical and photoelectrochemical stability. Photoanodes must be stable under prolonged exposure to the electrolyte under the operation conditions (applied potential and illumination).
In recent years, increasing attention is being paid to the design and synthesis of nanostructured metal oxides due to their exceptional properties. Photocurrent density obtained in PEC systems has two main contributions, one coming from the electrocatalytic process and other arising from the photon absorption process. The electrocatalytic process consumes the photogenerated charge carriers and it can become the rate-determining step of the PEC process (the charge transfer at the semiconductor/electrolyte interface) [4]. Current densities in electrochemistry are directly influenced by the real surface active area, since increasing surface area enhances the number of electroactive sites; therefore, nanostructuring the photoelectrode can improve its electrocatalytic performance. Moreover, in nanostructured photoelectrodes, the diffusion path of photogenerated holes toward the semiconductor/ electrolyte interface is significantly shorter, which reduces electron-hole recombination. On the other hand, by roughening the semiconductor surface, direct light reflection is reduced due to the scattering of reflected photons, enhancing thus the chance of light absorption by the semiconductor and the possibility of further photoexcitation. Consequently, creating nanostructured photoanodes has immediate benefits on both their electrocatalytic activity and photoactivity [4].
During the last decades, several n-type semiconductor metal oxides, such as TiO 2 , WO 3 , Fe 2 O 3 and ZnO, have been investigated as potential candidates for photoanode materials in PEC cells due to their different characteristics.
Titanium oxide (TiO 2 ) is a wide bandgap semiconductor (E g ≈ 3.2 eV in the anatase crystalline form [3,4,9], equivalent to a maximum wavelength of ~390 nm) with an exclusive set of properties, such as high chemical stability, resistance to photocorrosion and favorable band-edge position relative to the redox potentials for the decomposition of water, allowing the use of light for effective direct water splitting [5,10,11]. However, due to its high E g , TiO 2 absorb photons only in the UV range, which represents a very small part of the solar spectrum.
Tungsten oxide (WO 3 ) is another attractive photoanode material owing to its high electron mobility and moderate hole diffusion length (≈150 nm). Besides, WO 3 can also absorb a part of the visible rays of the solar spectrum (its E g ≈ 2.6 eV, which corresponds approximately to a wavelength of λ = 480 nm) [3,12,13]. Moreover, in contrast with almost the rest of semiconductor oxides used as photoelectrocatalysts, WO 3 can safely operate in acidic environments, which is very useful in the treatment of low-pH wastewater [11].
Hematite (α-Fe 2 O 3 ) is the most thermodynamically and stable iron oxide form under ambient conditions and it is a non-toxic, chemically stable and low cost material. Furthermore, it has a bandgap of E g ≈ 2.1 eV which indicates its suitability for visible light absorption up to ~590 nm, that is, hematite can collect up to ~40% of solar spectrum energy [4,11]. Apart from its properties, hematite has some drawbacks such as low carrier mobility and short holes diffusion lengths, which can be overcome by nanostructuring the material.
Zinc oxide (ZnO) is also a wide bandgap semiconductor (E g = 3.37 eV; λ = 369 nm) with similar characteristics as TiO 2 but with the advantage that ZnO possesses a higher electron mobility (from 10 to 100 times higher in comparison with TiO 2 ), that is, a large conductivity which makes ZnO a very suitable and promising substitute of TiO 2 [14,15]. In spite of this, photogenerated electron-hole pairs tend to recombine fast in ZnO, so the use of hybrid semiconductors systems between ZnO and ZnS has been proposed to overcome this inconvenience [16,17].
In order to prepare nanostructures of the oxides described above, various methodologies have been reported, such as sol-gel processes, hydrothermal and solvothermal methods, deposition processes or anodization. Of these, anodization is a fast and simple method to synthesize metal oxide nanostructures [12,[18][19][20][21][22]. With anodization, surface morphology can be designed by adequately controlling several parameters, such as the anodization potential, duration, electrolyte composition, temperature, and so on. Hence, the morphology and dimensions of nanostructures fabricated by anodization, as well as their PEC behavior, can be controlled by adjusting the aforementioned parameters. Moreover, nanostructures formed by anodization can be grown directly on the substrate (the back metal collector), thus avoiding compaction or sintering of nanostructures. This fact significantly reduces the contact resistance between the nanostructure and the metallic substrate, providing the basis for efficient charge collection. Therefore, anodization offers a robust and economical way to fabricate nanostructured metallic oxides.
Among the parameters that can be controlled to design and fabricate high-performance oxide nanostructures by anodization, hydrodynamic conditions during the synthesis process can be of great importance. Indeed, depending on the used material and the operation conditions, the mechanisms of nanostructures formation by anodization may involve one or more stages where mass transfer becomes the rate-determining step [8,23]. Therefore, hydrodynamic  conditions can play a central role in the synthesis of nanostructures by anodization. This chapter presents a review of the innovative high-performance nanostructures that have been fabricated by anodization under different hydrodynamic conditions. Although various fabrication conditions have been used, depending on the material, in all cases, hydrodynamic conditions have been controlled by connecting rods of the different metals to a rotating disk electrode (RDE) to assure reproducible mechanical convection of the electrolyte near the electrode surface. Figure 2 shows an illustration of the electrode configuration used during all the anodization processes. The specific synthesis conditions for the different materials are detailed in the following sections.

TiO 2
Influence of hydrodynamic conditions for nanostructures formed from titanium (Ti) anodization is presented for samples synthesized in two different electrolytes and anodization conditions: ethylene glycol +1 M H 2 O containing 0.05 M NH 4 F and glycerol/water (60:40 vol.%) containing 0.27 M NH 4 F. When anodization was performed in ethylene glycol based electrolytes 55 V for 30 min were directly applied to anodize the Ti. Nevertheless, in glycerol based electrolytes the potential was increased from 0 to 30 V at a rate of 200 mV s −1 , applying subsequently the potential of 30 V for 3 h. The active anode area exposed to the electrolyte was 0.5 cm 2 .

Morphological characterization
Since the morphology of the nanostructures is highly dependent on the electrolyte used for anodization, the discussion of the influence of Reynolds number on the morphological properties of the TiO 2 nanostructures will be discussed for each particular anodization media. A field emission scanning electron microscope (FESEM) was used to characterize the morphology of the nanostructures.
Nanostructures anodized in ethylene glycol based electrolytes present an initiation layer which blocks the mouth of the nanotubes, preventing part of the solar radiation from being absorbed at the photoelectrode (Figure 3a). It was observed that rotating the electrode during anodization, part of the initiation layer was removed, and this elimination was more important as Reynolds number (Re) was increased (Figure 3b).
On the other hand, the hydrodynamic conditions completely changed the morphology of the formed nanostructures when anodization was carried out in glycerol based electrolytes, that is from nanotubes (at Re = 0, Figure 4a) to nanosponges (at Re > 0, Figure 4b). Nanosponge morphology is characterized by a connected and highly porous TiO 2 structure.

Anodization profile: current densities vs. time
The formation and growth of the TiO 2 nanostructures was monitored by recording the current density-time behavior (Figure 3c and 4c). The current density profile follows a similar trend regardless the electrolyte used for anodization.
In the first stage (I), current density decreases with time due to a compact TiO 2 oxide layer formation [9,24]. Then, in the second stage (stage II), an increase in current density indicates the onset of TiO 2 dissolution due to the presence of fluoride ions in the electrolyte (stage II), according to the reaction shown in Eq. 1 [25][26][27]. Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts… http://dx.doi.org/10.5772/intechopen.78303 After that, in the third stage (stage III), current density remains almost constant due to the formation and growth of regular nanotubes or nanosponges [9,28].
In general, Figures 3c and 4c show that current densities increase with increasing Re in all the stages, which indicates that hydrodynamic conditions enhance the electrochemical processes taking place during anodization.

Crystalline structure characterization
In order to obtain a crystalline structure, samples were annealed in air at 450°C for 1 h. After the annealing treatment, all the samples possessed the Raman peaks of the  [28][29][30]).

Electrochemical and photoelectrochemical characterization
Electrochemical impedance spectroscopy (EIS) measurements at open circuit potential (OCP) and Mott-Schottky plots were performed in 0.1 M Na 2 SO 4 in order to evaluate the electrochemical properties of the samples. Figure 5 shows the Nyquist (Figure 5a), Bode-phase (Figure 5b) and Bode-modulus (Figure 5c) plots for the nanostructures anodized in ethylene glycol-based electrolytes. Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts… http://dx.doi.org/10.5772/intechopen.78303 Figure 6 shows the electrical equivalent circuit used to fit EIS data, where R s is the electrolyte resistance, and the two groups of resistances and constant phase elements (R-CPE) correspond to the nanotubular layer (R 1 -CPE 1 ) and the compact TiO 2 underlayer (R 2 -CPE 2 ) [8,31,32].
The different parameters obtained from the fitting of the EIS data in the electrical equivalent circuit are shown in Table 1. From Table 1, it is important to highlight that the resistance of the compact layer is always higher than the one obtained for the nanotubes (R 2 > R 1 ), due to the higher conductivity of the nanostructures. On the other hand, R 1 decreases as Reynolds number increases, that is, the conductivity of the nanotubes increases at higher hydrodynamic conditions.
In order to observe the electrochemical behavior of nanostructures formed in glycerol-based electrolytes, Figure 7 shows the Mott-Schottky (MS) plots at a frequency of 10 kHz (to eliminate the capacitance dependence on frequency) for nanotubes (Re = 0) and nanosponges (Re > 0).
In Figure 7, positive slopes of the MS plots are characteristic of n-type semiconductors. The dominant TiO 2 defects are oxygen vacancies due to their lower formation energy compared with Ti 3+ interstitials [32][33][34][35][36][37][38]. Table 2 shows the donor densities (N D ) and the flat band potential (E FB ) values at different Re.
The donor density can be determined from the positive slopes of the straight lines in the MS plots using the Mott-Schottky equation for an n-type semiconductor: (2) Figure 6. Electrical equivalent circuit used to simulate the experimental data obtained from EIS experiments shown in Figure 5. where ε is the dielectric constant of the TiO 2 layers (100 for TiO 2 nanostructures [39]), ε 0 is the vacuum permittivity (8.85·10 −14 F/cm), e is the electron charge (1.60·10 −19 C) and σ is the positive slope of each straight line in the MS plots. Table 2 shows that N D decreases with increasing Re, that is, N D is lower for the nanosponges than for the nanotubes. In this case, the increase in N D leads to a decrease in the depletion layer thickness, resulting in an increase of recombination losses [6,40,41]. In fact, oxygen vacancies in TiO 2 act as recombination centers for electron and holes, playing a critical role in the trapping process [42][43][44]. Table 2 also shows the flat band potentials for the different nanostructures obtained in glycerol-based electrolytes. These values were determined from the intercept of the straight line in MS plots with the potential axis. To reduce the recombination probability, flat band potentials  should be high and negative [6,42]. It can be observed in Table 2 that flat band potentials are more negative with increasing Re, that is, nanosponges formed under hydrodynamic conditions possess more negative flat band potentials than nanotubes formed under static conditions. Thus, the charge recombination probability is lower in the case of the nanosponges. It can be observed in terms of the photocurrent transient vs. potential curves that the nanostructures obtained under hydrodynamic conditions present a higher performance in comparison with the nanostructures anodized at the same potential, time and electrolyte but at Therefore, on the one hand, hydrodynamic conditions are beneficial in ethylene glycol-based electrolytes because of the removal of the initiation layer which offers a high surface area for photoelectrochemical water splitting. On the other hand, nanosponges formed in glycerol based electrolytes under dynamic conditions enhance the rate of the photoelectrochemical reaction over the photoelectrode due to their surface-active sites.
These nanostructures were produced by anodization of tungsten rods in sulfuric acid media in the presence of small amounts of complexing agents (NaF and H 2 O 2 ). For example, tree-like globular clusters of WO 3 nanoplatelets were obtained in a 1.5 M H 2 SO 4 + 0.1 M NaF electrolyte and at different rotation velocities of the RDE. Figure 9 shows the FE-SEM images of the samples anodized in that electrolyte at different rotation velocities (0 and 375 rpm) [23,58]. It can be observed that in both cases, the nanostructures formed on the tungsten surface presented nanoplatelet morphology, as other authors reported when anodizing in similar acid electrolytes [53-55, 57, 58]. Nevertheless, the morphology and dimensions of these nanoplatelets varied noticeably with rotation speed. At 0 rpm (Figure 9a), nanoplatelets grew quite orthogonal to the electrode surface, in a more or less ordered way. At 375 rpm (Figure 9b), nanoplatelets formed globular clusters that grew in a tree-like manner, forming a multilevel WO 3 layer resembling a forest seen from above. It is perceptible that the new nanostructure obtained under controlled hydrodynamic conditions exposed more surface area to the electrolyte than the one synthesized at 0 rpm.
In the presence of other well-known complexing agent of tungsten-hydrogen peroxideand under controlled hydrodynamic conditions, a different nanostructure was obtained [59]. In this case, anodization of tungsten in a 1.5 M H 2 SO 4 + 0.05 M H 2 O 2 and at 375 rpm (the same rotation speed as in the example shown above for the NaF electrolyte), resulted in very small nanoplatelets or nanosheets forming a kind of spongy layer (Figure 10).
The three nanostructures shown in Figures 9 and 10 shared a common formation mechanism, that is, a dissolution/precipitation mechanism, although it was greatly influenced by hydrodynamic conditions. In order to study the influence of rotation speed of the electrode on the formation and growth of WO 3 nanoplatelets, current density transients were recorded during the anodization processes. Figure 11 shows, by way of illustration, current density transients recorded for the WO 3 nanostructures anodized in the 1.5 M H 2 SO 4 + 0.1 M NaF electrolyte, under static (0 rpm) and hydrodynamic conditions (375 rpm).
During the first seconds of anodization, a notable decrease in current density can be observed for both cases. This decrease has been associated with the formation of a compact WO 3 layer on the electrode surface [19,23,58,60]. Subsequently, current density started increasing, indicating the dissolution of the WO 3 layer due to the effect of H + and F − [23,58,61]. This dissolution process resulted in the release of soluble cationic species, such as WO 2 2+ (or [W(OH) 4 (H 2 O) 4 ] 2+ in its hydrated form) or [WF n ] (6−n) , from the electrode surface. Afterward, current density gradually decreased again, eventually reaching a steady-state value. This decrease and the later stabilization of current density can be explained by the precipitation of soluble species upon reaching supersaturation conditions near the electrode surface. In fact, as the dissolution of the WO 3 layer proceeded, increasing amounts of tungsten cationic species were formed and they reacted to produce polycondensed tungstates [62]. These species finally precipitated on the electrode surface in the form of insoluble and highly polymeric tungstic acids (WO 3 •H 2 O and WO 3 •2H 2 O) due to strongly acidic pH of the electrolyte  [ 59,62]. The particular morphologies of nanoplatelets were a consequence of the interaction between soluble tungsten species and fluoride anions during the precipitation process [59], being hydrodynamic conditions especially important [23].
Under static conditions (0 rpm), current densities recorded during the whole anodization process were notably lower than under hydrodynamic conditions. Moreover, steady-state values were attained much earlier than with rotation, indicating that the WO 3 nanoplatelet layer completely covered the electrode surface after ~2000 s from the beginning of the anodization process. These facts imply that the electrode rotation permitted the ions in the electrolyte (F − and H + ) to transport to the electrode more rapidly, resulting in higher current densities being measured at the working electrode due to the enhancement of the WO 3 compact layer dissolution. Consequently, an increase in the rotation speed increased the release of soluble species from the electrode surface, which would result in a higher precipitation rate of hydrated WO 3 in the form of nanoplatelets.
Photoelectrochemical characterization of the nanostructures was performed under simulated sunlight illumination AM 1.5 (100 mW cm −2 ) imposing an external polarization of 1 V (vs Ag/ AgCl). Photocurrent density-potential curves for the three different WO 3 nanostructures presented in Figures 9 and 10 are shown in Figure 12. It can be observed that nanoplatelets anodized under static conditions (0 rpm) provided the lowest photocurrent density (~0.41 mA cm −2 at 1 V). Nanostructures anodized under hydrodynamic conditions (in the different electrolytes) showed a large enhancement of their photoelectrocatalytic activity (~1.51 mA cm −2 at 1 V and ~1.86 mA cm −2 at 1 V for nanostructures anodized in the presence of NaF and H 2 O 2 , respectively). This clear improvement is directly related to the increase of the electrochemically active surface area in nanostructures synthesized under hydrodynamic conditions. As explained earlier, nanoplatelets formed in the presence of NaF and with rotation grew in a tree-like manner forming globular clusters, which made this new nanoplatelet configuration Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts… http://dx.doi.org/10.5772/intechopen.78303 expose much more active area than normal nanoplatelets fabricated at 0 rpm. In the presence of 0.05 M H 2 O 2 , the obtained nanoplatelets were very small and they aggregated forming very thin layers, also resulting in an increase in the surface area with respect to other WO 3 nanoplatelets and in higher photoelectrochemical efficiencies.

Fe 2 O 3
Iron oxide nanostructures were made by electrochemical anodization in order to evaluate the effect of hydrodynamic conditions on the formed nanostructures. Prior to anodization, iron rods were abraded with SiC papers of 220, 500 and 4000, sonicated in ethanol, rinsed with distilled water and dried in nitrogen stream. Electrochemical anodization was carried out at room temperature with an ethylene glycol-based solution with 0.1 M NH 4 F and 3% vol. H 2 O for 15 min at 50 V with iron rod as working electrode and a platinum foil as counter electrode [63]. Different rotation speeds: 0, 1000, 2000 and 3000 rpm, corresponding to Reynolds numbers of 0, 165, 325 and 490, respectively, were applied. Once synthesized, samples were annealed in argon atmosphere for 1 h at 500°C at a heating rate of 15°C · min −1 , and cooled within the furnace by natural convection [21]. Figure 13 shows the different obtained curves during anodization where three stages can be seen for all the cases (scheme in Figure 13). In the first stage, an abrupt drop in the current density from 80 mA · cm −2 to less than 15 mA·cm −2 (in the case of 0 rpm) and less than 25 mA · cm −2 (in the case of hydrodynamic conditions), indicated a formation of an insulating compact oxide layer (Fe 2 O 3 ) on the iron substrate according to Eq. (3). In the second stage, a slight increase in current density indicated that tiny pits occur in the surface of the compact layer, followed by the formation of the nanostructures resulting in a decrease in resistance. This process occurs because of the fluoride ions (F − ) and the applied potential which lead to partial dissolution of the compact layer forming the nanoporous structure as Eq. (4) indicates.

Electrochemical anodization
2Fe Finally, in the third stage, further dissolution and cation-cation repulsion occurs and the nanoporous structure leads to a nanotubular one. This occurs until equilibrium between the formation of the oxide layer and its chemical dissolution by F − is reached. In this way, current density remains almost constant and the formation of nanotubular structure stops [64,65].
According to Figure 13, the formation of the nanostructure under stagnant conditions (0 rpm) leads to lower values of the current density in comparison to the ones synthesized under hydrodynamic conditions. In fact, the higher the rotation speed the higher the current density, achieving the maximum value for the samples anodized at 3000 rpm. This is because steady-state current density is controlled by diffusion processes, hence stirring the iron rods during anodization increases the diffusion and then, current density increases [66,67].

Structural characterization
A field emission scanning electron microscope was used in order to evaluate the morphology of the synthesized nanostructures. Moreover, crystalline structure of the samples was evaluated by a confocal Raman microscope with the aim to determine crystalline phases present in the nanostructures. Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts… http://dx.doi.org/10.5772/intechopen.78303 Figure 14a shows the morphology obtained for the samples under stagnant conditions. In this case, a cracked porous initiation layer appears over the nanotubes, partially covering the entrances of the tubes. This initiation layer results in a decrease in the efficiency of the nanostructures since they might be less accessible to light. On the contrary, Figure 14b shows that the initiation layer is etched and the nanotubes are accessible to light irradiation, which leads to higher photoactivity. Nanotubular morphology is advantageous for photoelectrochemical water splitting since it improves electron transport behavior with the tubular orientation. Furthermore, nanotubes avoid short hole diffusion lengths problem since tubes walls make shorter the route from the places where the holes are generated to the surfaces where oxidation reactions are occurring [68]. and the top morphology seems to be chaotic. This morphology results in less photoactivity since light irradiation cannot go deep into the nanotubes. On the other hand, when rotation speed is 3000 rpm (see Figure 14d), the morphology is a mixture between what occurs at 0 and 2000 rpm, that is, the nanotubes are collapsed and stacked and an initiation layer appears in some parts of the nanostructure covering the tubes [69]. Hence, illumination is not effective in this case, and the photoactivity is affected. This could be due to the fact that at 3000 rpm, some vortex could be formed and then the conditions are non-homogeneous during anodization.
On the other hand, thickness of the nanostructures were measured, and they were comprised between 810 and 870 nm in all cases, which indicated that rotation speed does not affect the thickness of the synthesized nanostructures [69].
Raman spectroscopy was measured with a neon laser 632 nm with ~700 μW. Raman spectra of all the samples were the same, suggesting that rotation speed does not change the crystalline structure of the formed nanostructures. Figure 14e shows a Raman spectrum as an example. The Raman shift at which appear the peaks indicates that the nanostructures are mainly composed of hematite with peaks at roughly 229 cm −1 (A 1g ), 249 cm −1 (E g ), 295 cm −1 (E g ), 414 cm −1 (E g ), 500 cm −1 (A 1g ), 615 cm −1 (E g ) and 1317 cm −1 (2nd order). However, some peaks appearing at approximately 554 cm −1 , 672 cm −1 and 820 cm −1 also indicated the presence of some amount of magnetite [70,71].

Photoelectrochemical water splitting tests
For the photocurrent density versus potential measurements the potential was varied from −0.4 to +0.6 V Ag/AgCl at a scan rate of 2 mVs −1 .

Figure 15
shows that the highest photocurrent density values were achieved for the nanostructure synthesized at 1000 rpm (reaching 0.130 mA · cm −2 at 0.54 V Ag/AgCl ), which indicated its suitability as photocatalyst for water splitting [69]. This is in agreement with FE-SEM images Fabrication of Ordered and High-Performance Nanostructured Photoelectrocatalysts… http://dx.doi.org/10.5772/intechopen.78303 since they revealed that the morphology of the nanostructures synthesized at 1000 rpm was the most adequate for being illuminated in photoelectrochemical measurements.
Furthermore, inset of Figure 15 indicates that all synthesized nanostructures were stable against photocorrosion at the indicated conditions.

Mott-Schottky analysis
For the Mott-Schottky analysis, the potential was swept from the OCP value (~ −0.3 V) in the negative direction at 28 mV s −1 with an amplitude signal of 0.01 V at a frequency value of 5 kHz.  2)), with an assumed ɛ r of 80 for the nanostructures [72,73]. Table 3 shows the results for the different nanostructures and all the values are in the order of 10 19 cm −3 , regardless the rotation speed during anodization. However, the samples anodized at 0 and 3000 rpm achieved donor density values too high which is detrimental for the photoelectrochemical water splitting since the defects could act as carrier traps (trapping the electrons or holes) [42]. Hence, the efficiency of the water splitting is lower as shown in Figure 16. On the contrast, lower donor density values, as in the case of the nanostructure synthesized at 1000 rpm, achieved better photoelectrochemical results (see Figure 16) since it avoids recombination processes. This indicates that donor density is a parameter that considerably affects the efficiency of the water splitting.
On the other hand, flat band potential (E FB ) is related to the potential drop at the depletion space charge layer (Δφ SC ) and to the applied external potential (E) according to Eq. (5). Then, the higher and more negative flat band potential, the lower recombination rate [6]. Table 3 shows that the flat band potential does not vary for the different nanostructures, which in fact demonstrates that electrode rotation speed during anodization does not affect flat band potential of the synthesized nanostructures.

ZnO/ZnS heterostructures
The influence of hydrodynamic conditions was studied for ZnO/ZnS heterostructures obtained from anodization of zinc (0.5 cm 2 area exposed to the electrolyte) in glycerol/water (60:40 vol%) media with 0.025 M NH 4 F and 0.2 M Na 2 S. Nanostructures were synthesized at different voltages: 20, 30 and 40 V. The advantage of this type of heterostructure is the good photocatalytic behavior of ZnS, which in combination with ZnO could reduce the recombination rate of the charge carriers due to their separated band gaps.

Morphological characterization
As an example of the nanostructures of ZnO/ZnS obtained from anodization of zinc, Figure 17 shows the FESEM images of top and cross-sectional views of the samples anodized at different voltages and hydrodynamic conditions. It has been demonstrated [22,74] that anodization  to a porous tubular morphology (Figure 17c). Therefore, as rotation speed is increased during anodization, the nanotubular morphology is predominant. This change in morphology continues as anodization potential is increased. In fact, as it can be appreciated in Figure 17d, a porous tubular morphology is obtained when anodization is carried out for higher anodization potentials (40 V) even under stagnant conditions. This might be explained taking into consideration that at higher anodization potentials, nanostructures grow faster [75,76], which involves a lower oxide dissolution, and consequently, a tubular morphology. Besides, the length of the nanostructures was measured obtaining the following values: ~360-600 nm at 20 V, ~800-1100 nm at 30 V and ~1100-1400 nm at 40 V. Thus, longer nanostructures are formed at higher anodization voltages, regardless the hydrodynamic conditions. In this case, longer nanostructures possess a high surface/volume relation, increasing the interaction with light and the electrolyte, and consequently, improving their photocatalytic activity.

Figure 17e
shows, as an example, the current density profiles during the anodization process at 30 V and at the different studied hydrodynamic conditions (0, 1000, 2000 and 3000 rpm). For all cases, the tendency of the current densities is to sharply decrease at the beginning of the anodization, owing to the ZnS precursor layer formation. After that decrease, the current densities continue decreasing until, finally, they stabilize. This tendency is typical of an oxide layer formation in glycerol-based electrolytes [22]. Additionally, it is important to highlight that the higher current density values obtained for the samples anodized stirring the zinc rod are in agreement with the enhancement of the diffusion of the fluoride ions due to the flowing conditions [77]. Besides, the background noise obtained in the current density register of the heterostructure synthesized under static conditions is related to the formation of oxygen bubbles in the zinc surface of the rod during anodization, which generates an irregular anodization of the surface.
It is important to point out that the profiles of current densities versus time for the rest of the heterostructures anodized at 20 and 40 V follow the same trend with hydrodynamic conditions. However, the current densities possess higher values when samples are anodized at higher potentials. Figure 18a shows, as an example, the Raman spectra of the annealed ZnO/ZnS heterostructures anodized at 30 V at the different hydrodynamic conditions (0, 1000, 2000 and 3000 rpm). Zinc is characterized by a strong broad background signal, which hinders the Raman peaks (Figure 18a). This response is associated with the photoluminescence (PL) due to a broad defect band emission in the nanostructures, such as oxygen vacancies [22,78]. This high concentration of defects was produced due to the absence of oxygen in the atmosphere during the thermal treatment (samples were annealed for 3 h at 375°C in an argon atmosphere), so the evaporated oxygen present in the material cannot be replaced [79] and therefore, the density of oxygen vacancies increases. Then, X-Ray Diffraction (XRD) tests were carried out in order to check the crystalline structure of the annealed samples. Figure 18b shows, as an example, the XRD spectrum for the ZnO/ZnS heterostructure anodized at 30 V and at 2000 rpm.

Crystalline structure characterization
In the XRD spectra shown in Figure 18b, the presence of both ZnO and ZnS can be clearly demonstrated due to the presence of their characteristic peaks [74]. The peak at 25° is related to the ZnS phase with the orientation of (002) [74]. The peaks situated at 36° and 70° are associated with the refraction produced by the polycrystalline Zn substrate [74]. The high intensity of the peak centered at 36° is characteristic of the wurtzite ZnO phase, with an orientation of (101) [80], which is the most abundant phase of the heterostructures. Another ZnO characteristic peak is the one roughly centered at 34°, which corresponds to the orientation (002) [81]. The peaks at 32°, 56° and 67° are associated with the wurtzite ZnS phase with the orientations (101), (112) and (104), respectively [81]. Besides, the peaks centered at 48° and 63° are related, the former, with the ZnS phase with an orientation of (110) and the ZnO phase with an orientation of (102), and the latter, with the ZnO phase with an orientation of (103) [74,80,81].

Photoelectrochemical characterization
The ZnO/ZnS nanostructures were characterized as photoanodes in a previously degasified solution of 0.24 M Na 2 S and 0.35 M Na 2 SO 3 [22]. Figure 19 shows the photocurrent densities applying different potentials obtained under simulated sunlight AM 1.5 conditions for the different anodization potentials (20, 30 and 40 V) at the studied hydrodynamic conditions (0, 1000, 2000 and 3000 rpm).
In Figure 19a, it can be observed that the dark current density values for the ZnO/ZnS heterostructures anodized at 20 V are, in general, high. This fact might be related to a low  photocorrosion resistance and could be occasioned by the heterogeneous ZnS precursor layer formed when anodization is performed at 20 V (this was confirmed in FESEM characterization, see Figure 17a). On the other hand, when anodization was performed at higher voltages, photocorrosion resistance is increased (Figure 19b and c), regardless the applied hydrodynamic conditions. In particular, for applied potentials of −0.4 and 0.2 V, the ZnO/ZnS heterostructures show a good stability, since the dark current densities are close to zero and the photocurrent densities are high. Besides, the photocurrent densities for the nanostructures anodized at 30 and 40 V increase for the heterostructures anodized under hydrodynamic conditions. This could be related to the morphology obtained for the nanostructures anodized under hydrodynamic conditions, which showed more nanotubular aspects (Figure 17) as the rotation speed was increased, which enhances the charge separation [16,[82][83][84][85]. Hence, the photocatalytic response is improved. Figure 19c shows that the ZnO/ZnS heterostructures anodized at 40 V and under hydrodynamic conditions present the best photocatalytic behavior in terms of higher photocurrent densities and good photocorrosion resistance. In particular, the best conditions were obtained for the ZnO/ZnS heterostructures anodized at 40 V and at 1000 rpm, where the photocurrent density for photoelectrochemical water splitting increased in 100% with respect to the one anodized at 20 V and at 0 rpm, and in a 71% in relation to the photocurrent density obtained for the heterostructure anodized at 20 V and 1000 rpm.

Conclusions
In this chapter, the effect of rotating the electrode during electrochemical anodization (hydrodynamic conditions) has been evaluated for different metal oxides. In all cases, hydrodynamic conditions enhanced the photoelectrochemical response of the nanostructures in photoelectrochemical water splitting process.
For nanostructures of TiO 2 , hydrodynamic conditions in ethylene glycol media removed the initiation layer over the nanotubes, whereas in glycerol-based electrolytes, rotating the electrode changed the morphology from nanotubes to nanosponges, increasing then the porosity of the structure. For the nanostructures formed in both electrolytes, the surface area increased, resistance values decreased (as EIS showed) and flat band potential became more negative (as MS plots indicated).
In the case of WO 3 nanostructures, the ones synthesized under hydrodynamic conditions presented high active surface area. Furthermore, in the presence of NaF and rotating the electrode, the nanoplatelets grew in a tree-like manner forming globular clusters with more exposed area than in the case of nanostructures synthesized under stagnant conditions. When H 2 O 2 is present in the electrolyte, the nanoplatelets were very small, and they aggregated forming very thin layers with high surface areas, which in turn resulted in higher photoelectrochemical efficiencies.
For nanostructures of iron oxide (mainly α-Fe 2 O 3 ), stagnant conditions resulted in nanostructures with an initiation layer that partially covered the top of the nanotubular structure. This layer was removed under hydrodynamic conditions, in particular at 1000 rpm. At higher rotation velocities, collapsed and stacked nanostructures were formed, which caused lower photoelectrochemical efficiencies. Rotating the electrode during anodization at 1000 rpm led to nanotubular structures with suitable donor densities values and flat band potentials (as MS results indicated), which enhanced photoelectrochemical results.
In the case of ZnO/ZnS heterostructures, high applied potentials and hydrodynamic conditions during anodization led to nanotubular morphology which resulted in higher photoelectrochemical performance. In particular, heterostructures anodized at 40 V and under hydrodynamic conditions presented the best photocatalytic behavior and good photocorrosion resistance.