Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium from Water Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium from Water

Adsorption of Cr(VI) from aqueous solution onto the nanomaterials prepared by modified chitosan was investigated in a batch system to evaluate the efficiency of biomass as an adsorbent. The crosslinking materials of chitosan & silicon dioxide and carboxymethyl chitosan & silicon dioxide were synthesized, respectively, as new adsorbent materials for the removal of Cr(VI) from aqueous solutions. The adsorption potential of Cr(VI) by the nanomaterials for desalination was investigated by varying experimental conditions such as pH, contact time and the dosage of the nanomaterials. Adsorption isotherms of Cr(VI) onto the membrane were studied with varying initial concentrations under optimum experiment conditions. The surface property of the membrane was characterized by SEM (scanning electron microscope) and Fourier transform infrared spectrometer (FT-IR). The concentrations of Cr(VI) in solution are determined by ICP-AES (inductively coupled plasma atomic emission spectrometry). The membrane of carboxymethyl chitosan & silicon dioxide exhibited higher adsorption capacity than the membrane of chitosan & silicon dioxide for Cr(VI). The adsorption sites and specific surface area may be increased by changing from chitosan to carboxymethyl chitosan. The maximum adsorption capacity was estimated as 80.7 mg (cid:1) g (cid:3) 1 for Cr(VI) under the optimum conditions.


Introduction
With the rapid growth of mankind, society, science and technology, the environmental disorder with a big pollution problem has become one of the most important issues in the past half Heavy metals include lead (Pb), cadmium (Cd), zinc (Zn), mercury (Hg), arsenic (As), silver (Ag) chromium (Cr), copper (Cu) iron (Fe), and the platinum group elements [12]. Heavy metals are not biodegradable and tend to accumulate in living organisms, causing various diseases and disorders [13]. They enter the body system through food, air, and water and bioaccumulate over a period of time. Although adverse health effects of heavy metals have been known for a long time, exposure to heavy metals continues and is even increasing in some areas [14], such as metal plating facilities, mining operations, and tanneries. Among these heavy metals, Cr is one of the top priority list of toxic pollutants defined by the U.S. Environmental Protection Agency.
Cr mainly consists of two stable oxidation states such as trivalent state Cr(III) and hexavalent state Cr(VI) in natural aqueous environment [15]. Cr(VI) is more toxic, carcinogenic and mutagenic. The typical mobile forms of Cr(VI) in natural environment are CrO 4 2À , HCrO 4 À ; and the relative distribution of each species depends on the solution pH, on the concentration of Cr(VI) and redox potential [16]. Cr(III) tends to form [Cr(H 2 O) 6 ] 3+ , Cr(H 2 O) 5 (OH) 2+ , Cr (H 2 O) 4 (OH) 2 + , or Cr(III) organic complexes. The use of Cr and its compounds in several industrial processes (automobile manufacturing, production of steel and alloys, mining of chrome ore, plating, and electroplating, etc.) leads to contamination of natural waters mainly due to improper disposal methods [17]. They can be taken up by plants and easily be leached out into the deeper soil layers, leading to ground and surface water pollution. It is well known that Cr(III) is essential materials for living organisms, whereas Cr(VI) is the most toxic form. Cr (VI) can diffuse as CrO 4 2À or HCrO 4 À through cell membranes [18] leading to carcinogenic, mutagenic, liver damage, pulmonary congestion, and causes skin irritation resulting in ulcer formation to living organisms [19][20][21][22].
From the above-mentioned, Cr(VI) must be substantially removed from the waste water before being discharged into the aquatic system. Therefore the separation and reduction of Cr in waste water is very important for environmental protection and human health.
Different technologies for the removal of heavy metal ions are available such as chemical precipitation, coagulation, ion exchange, membrane technologies, and adsorption. Adsorption has been proved as one of the most efficient methods for the removal of heavy metals from aqueous media [23]. The major advantages of biosorption are its high effectiveness, easy operation, no two pollution, and the use of inexpensive biomaterials.
Chitosan has proven to be very efficient biosorbent for the removal of several toxic metals such as mercury (Hg), uranium (U), molybdenum (Mo), vanadium (V) and platinum (Pt) [24][25][26]. Chitosan, which full chemical name is known as (1,4)-2-amino-2-deoxy-β-D-glucose, can be environmentally friendly adsorbent due to the low price and no second pollution. Chitosan is produced by the alkaline deacetylation of chitin, and the preparation process of chitosan is shown in Figure 1. Chitosan is the most abundant biopolymer in nature originated from cellulose that can be obtained from the shells of seafood such as prawns, crabs, and lobsters [27]. The biopolymer is characterized by its high content of nitrogen, and is existed in the form of amine groups, free amino groups and hydroxyl groups, which are responsible for metal ion binding through chelation mechanisms [28].
However, chitosan had some defects such as notable swelling in aqueous media and nonporous structure resulting in a very low surface area [29]. Therefore, many types of chemical modification can be undertaken to produce some chitosan derivatives for improving the removal efficiency of heavy metal [30]. For example, silicon dioxide can be one of the materials for offsetting the defects of chitosan because it has many characteristics such as rigid structure, porosity and high surface area.
Silica gels are low-density solids, consisting of silicon oxide. The study of silica gels has attained considerable attention due to open mesoporic structure, high surface area, large pore volume and good performance as effective adsorbents [31]. Silicon dioxide is a synthetic amorphous polymer with silanol groups on the surface allowing metal adsorption [32,33]. In case of silicon dioxide, the modified silicon dioxide through the graft between silanol groups and ligands has been developed [34][35][36]. At present, an interest has grown in the field of organic and inorganic hybrid materials. The silica gels doped with some organic or inorganic material possess a number of novel properties [37].
Due to above-mentioned reason, novel adsorption materials were designed to combine the beneficial properties of silica gel and chitosan. The membrane of cross-linked chitosan with  silicon dioxide was synthesized in this work to enhance the adsorption potential of heavy metal ions. Furthermore, carboxymethyl chitosan has been prepared by using chloroacetic acid (and chitosan) under alkaline conditions to improve the removal efficiency. Using the carboxymethyl chitosan, the membrane of carboxymethyl chitosan & silicon dioxide was also synthesized, and was employed to remove heavy metal ions from aqueous solution. In present study, the adsorption capacity of the membrane was investigated for the removal of toxic chromium ions from aqueous solution under varying experimental conditions. Moreover, the surface morphology of the cross-linked membrane was determined to characterize these nanomaterials for desalination, and regeneration experiments were also conducted using the membrane.

Materials, reagent and apparatus
3-Aminopropyltriethoxysilane was purchased from Nacalal Tesque., Inc. (Tokyo, Japan), and chitosan was from Tokyo Chemical Industry Co. (Tokyo, Japan). Cr(VI) standard solutions were prepared by diluting a standard solution (1.005 mgÁdm À3 K 2 Cr 2 O 7 solution) purchased from Kanto Chemical Co., Inc. All other chemical reagents were also bought from Kanto Chemical Co., Inc. All reagents used were of analytical grade, and water (>18.2 MΩ in electrical resistance) which was treated by an ultrapure water system (Advantec aquarius: RFU 424TA, Advantec Toyo, Japan), was employed throughout the work.
The pH of Cr(VI) aqueous solution were measured by the pH meter (HORIBA UJXT 06 T8, Japan). The surface property of the membrane of carboxymethyl chitosan & silicon dioxide was characterized by SEM (JEOL, JSM-5800, Japan) and Fourier transform infrared spectroscopy in pressed KBr pellets (FTIR-4200, Jasco, Japan). The concentrations of Cr(VI) in solution were determined by ICP-AES (inductively coupled plasma atomic emission spectrometry).

Prepared the membrane of chitosan & silicon dioxide
The solution of chitosan (3%, w/v) was prepared by dissolving 3 g of chitosan in 100 ml of 0.2 molÁdm À3 acetic acid solution. Silica sols (which was prepared by dissolving 2 ml of 3-aminopropyltriethoxysilane in 100 ml ethanol) was added into the solution of chitosan (3%, w/v) at 25 C, and was stirred for 24 h. The membrane of cross-linked chitosan with silicon dioxide was dried at 25 C.

Prepared the membrane of carboxymethyl chitosan & silicon dioxide
Under alkaline conditions, chitosan can react with chloroacetic acid to obtain the carboxymethyl chitosan. Chitosan (5 g) was accurately weighed into a round-bottomed flask containing 75 ml isopropanol and 25 ml ultrapure water, and then 6.75 g of sodium hydroxide was added for alkalization. The mixed solution was stirred in a water bath at 50 C for 2 h, and was cooled to room temperature after continued stirring for 4 h. In addition, chloroacetic acid solution was prepared by dissolving 6 g of chloroacetic acid in 25 ml isopropanol solution, and slowly dropped into the round-bottomed flask under stirring for 4 h. The solution was adjusted to neutral using hydrochloric acid, and washed three times with 70% isopropanol, and then filtered. After washing completely with 90% isopropanol again, the solution was filtered. Then, carboxymethyl chitosan was dried at 50 C and used for preparation of membrane.
The reaction process of membrane synthesized from carboxymethyl chitosan & silicon dioxide is shown in Figure 2. The solution of carboxymethyl chitosan (3%, w/v) was prepared by dissolving 3 g of carboxymethyl chitosan in 100 ml ultrapure water. Silica sols (prepared by dissolving 5 ml of 3-Aminopropyltriethoxysilane in 100 ml ethanol) was added into the solution of carboxymethyl chitosan (3%, w/v) at 25 C, and the solution was stirred for 24 h. The membrane of carboxymethyl chitosan & silicon dioxide was dried at 25 C.

Adsorption experiment of Cr(VI) using the membrane
The adsorption capacities of Cr(VI) from aqueous solution using the membrane were investigated by a batch method. The membrane was thoroughly mixed with 50 ml of containing known concentrations of Cr(VI) in a 200 ml conical flask. According to the above-mentioned procedure, Cr(VI) were adsorbed at different pH values (1-7), contact time (20-120 min) and sorbent dosage (0.05-0.3 g dm À3 ). The pH of each solution was adjusted by using 0.1 mol dm À3 NaOH and 0.1 molÁdm À3 HCl. Adsorption isotherms of Cr(VI) onto the membrane of chitosan & silicon dioxide were measured at varying initial Cr(VI) concentrations (10-50 ppm) under optimized conditions.
The adsorption capacity of adsorbents for heavy metal ion was calculated using the mass balance equation: Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium… http://dx.doi.org/10.5772/intechopen.76035 where q e is the adsorption capacity (mgÁg À1 ) of heavy metal ion by the adsorbents at equilibrium, C i and C e are the concentrations of heavy metal ion at initial and equilibrium in a batch system respectively (mgÁdm À3 ), V (dm À3 ) is the volume of the heavy metal solution, and m (g) is the mass of the adsorbents.

Langmuir and Freundlich isotherm models
Langmuir and Freundlich isotherms were modeled in order to evaluate the performance of adsorbents in adsorption processes by the relationship between the metal uptake (q e ) and the concentration of heavy metal ion (C e ) at equilibrium.
The Langmuir isotherm equation is defined as follows: where C e is the concentration of heavy metal ion at equilibrium (mgÁdm À3 ), q e and q max are the amount of adsorption of heavy metal ion at equilibrium (mgÁg À1 ) and the maximum adsorption capacity by the adsorbents (mgÁg À1 ) respectively, K L (dm À3 Ámg À1 ) is the adsorption constant of Langmuir isotherm.
The linearized Freundlich isotherm equation is defined as follows: In this equation, K F is the adsorption capacity [(mgÁg À1 )Á(dm À3 Ámg À1 ) 1/n ], 1/n is the adsorption intensity. The values of 1/n and K F were determined on the basis of the plots of q e versus C e in log scale.

Kinetic models
Kinetic models have been proposed to determine the rate of adsorption of the adsorbent. In addition, the process of kinetic study is very important for understanding the reaction process and the rate of adsorption reactions.
The pseudo first-order model is given by the following equation: where q e and q t are the adsorption capacity of heavy metal ion using the adsorbents at equilibrium and time t, respectively (mgÁg À1 ), and k 1 is the rate constant of the pseudo-firstorder adsorption (h À1 ).
The pseudo-second order rate equation is expressed as follows: where k (gÁmg À1 Áh À1 ) is the rate constant of the second-order model, and q e and q t are the adsorption capacities of heavy metal ion using the adsorbents at equilibrium and time t, respectively (mgÁg À1 ).

Characteristics of the cross-linked membrane
The SEM pictures of the membrane of cross-linked chitosan with silicon dioxide are shown in Figure 3. It can be observed that the nanomaterial exists in the form of particles. The theory of chitosan and silica network where chitosan moieties were combined through silica groups via both ionic and covalent bonds was proposed [38]. The adsorbents synthesized in this work also may contain free amino groups that are responsible for metal ion binding through chelation mechanisms.
The surface property of the membrane of carboxymethyl chitosan & silicon dioxide was also investigated by SEM, and SEM images are shown in Figure 4. The surface morphology of the membrane showed the form of grain coalescence, which may be due to the crosslinking among adjacent carboxymethyl chitosan groups. Moreover, there was the porous structure in the surface of the membrane. It indicates that silicon dioxide was incorporated into the carboxymethyl chitosan definitely, and thereby the porous structure increased. Carboxymethyl has a high chelating ability for metal ions to form stable metal chelates. The lone pair electrons on the nitrogen atom can also constitute coordination bonds with the metal ions to form the Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium… http://dx.doi.org/10.5772/intechopen.76035 complex precipitation. The molecule also may contain free amino groups and hydroxyl groups, which can remove the heavy metal ions by chelation mechanisms.
The FT-IR spectroscopy is an important technique of characterization used to explain the changes in chemical structures (i.e., the functional group on the surface of the samples).
FTIR spectra of the membrane of carboxymethyl chitosan & silicon dioxide are presented in Figure 5. The strong broad band at the wave number region of 3300-3500 cm À1 is the characteristic of -NH 2 stretching vibration, and the band at 3400 cm À1 are related to symmetrical valent vibration of free NH 2 and -OH groups. The -CH stretching vibration in -CH and -CH 2 were observed at 2916 and 1376 cm À1 . The -NH 2 bending vibration was observed at 1652 cm À1 shifted to lower frequencies (The lower frequencies observed in the membrane may be explained by the presence of primary amine salt ÀNH 3 + [39]). A strong C=O stretching band at 1655 cm À1 may be related to the carboxymethyl group. Others bands at 1090 cm À1 are    In case of cross-linking membrane of chitosan & silicon dioxide, the removal of Cr(VI) more than 76% was observed at pH 3 ( Figure 6). It is well known that pH influences significantly in the adsorption processes by affecting both the protonation of the surface groups and the degree of the ionization of the adsorbates [40]. The surface of the adsorbent will be positively charged at lower pH, and it will not favor the adsorption of positively charged ions. Then it will favor the adsorption of Cr(VI) in the anionic form as HCrO 4 À [41]. As shown in Figure 8 taken from Irgolic et al. [42], the dominant form of Cr(VI) exists as hydrogen chromate anions (HCrO 4 À ) between pH 2 and 6. With the increase of pH, the dominant species will change from HCrO 4 À to other form CrO 4 2À [43].
Then, pH 3 was selected as the optimal pH in case of the membrane of chitosan & silicon dioxide for further work. It is well known that pH influences significantly the adsorption processes by affecting both the protonation of the surface groups and the chemical form of Cr (VI  [45,46]. The process of shifts is given Eqs. (6)- (8): It is found that the adsorption capacity was relatively low at pH 1. It may attributable to the strong competition between H 2 CrO 4 and protons for adsorption sites. In case of carboxymethyl chitosan & silicon dioxide, the adsorption efficiency of Cr(VI) increased with the increase of pH, and reached maximum at pH 5 (80%). It is considered that the (ÀNH 2 ) in the adsorbent may be protonated to form (ÀNH 3 + ) at pH 2-6. The surface of the membrane become positively-charged due to strong protonation at these pH range, which leads to a . Then protonation will enhance the Cr(VI) adsorption at pH 5-6. However, at higher pH, Cr may precipitate from the solution as its hydroxides. Hence, pH 5 was considered as optimum pH for further work.

Effect of contact time
Adsorption experiments were performed in order to determine the optimum contact time at optimal pH under the condition of the concentration of Cr(VI) for 50 mgÁdm À3 , and the dosage of the adsorbent for 0.2 gÁdm À3 .
The effect of contact time on the removal of Cr(VI) using the membrane of chitosan & silicon dioxide in Figure 9, the adsorption capacity of the membrane for Cr(VI) reached adsorption equilibrium at 80 min, and after that there are a slight decrease due to the swelling properties of the membrane absorbent. Therefore, the optimized contact time was selected for 80 min.
The effect of contact time on the removal of Cr(VI) using the membrane of carboxymethyl chitosan & silicon dioxide is shown in Figure 10. It can be observed that the adsorption capacity of Cr(VI) increases with increasing time within 60 min. The removal rate for Cr(VI) reached approximately 80% at 60 min, and after that there is no appreciable increase Then, 60 min was selected as the optimized contact time.

Effect of the membrane dosage
In order to estimate the optimal dosage of the membrane, the adsorption experiments were carried out with the range of 0.05-0.3 gÁdm À3 for the adsorbent under the optimum conditions of pH, contact time, and the concentration of Cr(VI) for 50 mgÁdm À3 .
The effect of dosage on the removal of Cr(VI) using the membrane of the membrane of chitosan & silicon dioxide are shown in Figure 11. The adsorption capacity of membrane for Cr(VI) reached adsorption equilibrium at 0.2 g dm À3 , and the removal rate reached 78.6%. However, remarkable decrease is observed at a dosage more than 0.2 gÁdm À3 . Thus, 0.2 g dm À3 was considered as optimized dose.
The effect of dosage on the removal of Cr(VI) using the membrane of carboxymethyl chitosan & silicon dioxide is shown in Figure 12. The results indicate that the adsorption capacity of the membrane for Cr(VI) reached adsorption equilibrium at the dosage of 0.25 gÁdm À3 , and that no significant change is observed at a dosage from 0.2 to 0.3 gÁdm À3 . The removal rate reached about 80% at 0.25 gÁdm À3 , and 0.25 gÁdm À3 was selected as the optimal dosage.

Effect of initial concentration
The experiments were performed by varying concentrations from 10 to 50 mgÁdm À3 under optimized condition of pH, contact time and adsorbent dosage.  The effect of initial concentration on the removal of Cr(VI) using the membrane of chitosan & silicon dioxide is shown in Figure 13. There was a continuous increase in the uptake of Cr(VI) per gram of adsorbent up to the concentration of 40 mgÁdm À3 , but the uptake is almost constant at further higher concentrations. The removal rate reached 78.7%. Then, 40 mgÁdm À3 was considered as optimum initial concentration for Cr(VI).
The effect of initial concentration on the removal of Cr(VI) using the membrane of carboxymethyl chitosan & silicon dioxide is shown in Figure 14. There was a slight increase from 20 to 50 mgÁdm À3 except at the concentrations of 30 mgÁdm À3 . The initial concentration was taken as 40 mgÁdm À3 .
Data from these studies were fitted to the Langmuir and Freundlich isotherm equations.

Adsorption isotherms
Adsorption isotherms are commonly used to reflect the performance of adsorbents in adsorption processes [47]. To understand the adsorption process of Cr(VI) using the membrane, adsorption isotherms of Langmuir and Freundlich were investigated under the optimal conditions. The adsorption data obtained for Cr(VI) using the membrane of chitosan & silicon dioxide were analyzed by Langmuir ( Figure 15) and Freundlich equations ( Figure 16). The correlation coefficient (R 2 ) of these isotherms for Cr(VI) on the membrane is shown in Table 1 along with other relevant parameters. From Table 1, it is found that R 2 value for Cr(VI) is comparatively large, and favorable adsorption of Cr(VI) on the membrane was presented. Particularly, R 2 values in Langmuir isotherm are larger than that in Freundlich isotherm. The maximum adsorption capacity (q max ) calculated from Langmuir model was 21.2 mgÁg À1 . This result  suggests that the adsorption of Cr(VI) on the membrane of chitosan & silicon dioxide mainly occurred by monolayer reaction.
The adsorption data obtained for Cr(VI) using the membrane of carboxymethyl chitosan & silicon dioxide were analyzed by Langmuir ( Figure 17) and Freundlich equations ( Figure 18). The correlation coefficient (R 2 ) of Langmuir and Freundlich isotherms for Cr(VI) using the membrane is shown in Table 2 along with other relevant parameters.
The maximum adsorption capacity (q max ) calculated from Langmuir model was 80.7 mgÁg À1 . Based on Table 2, it is found that R 2 value of Langmuir isotherm is larger than that of Freundlich isotherm. This result suggests that the adsorption of Cr(VI) on the membrane of carboxymethyl chitosan & silicon dioxide mainly occurred by monolayer reaction.
Moreover, the adsorption isotherm of Cr(VI) by the membrane was more suitably described by Langmuir model, indicating that monolayer adsorption of Cr(VI) on the membrane is more dominant.

Kinetic studies
Kinetic models were tested in this study for the adsorption of Cr(VI) onto the membrane under the optimized experimental conditions. Adsorption time is one of the important factors which Langmuir isotherm Freundlich isotherm Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium… http://dx.doi.org/10.5772/intechopen.76035  Langmuir isotherm Freundlich isotherm help us to predict kinetics as well as the mechanism of the uptake of heavy metals on material surface [47].
The adsorption data obtained for Cr(VI) using the membrane of chitosan & silicon dioxide were analyzed by kinetic studies are shown in Figure 19. Based on the data in Figure 18, the pseudo second-order kinetic coefficients for Cr(VI) by the membrane are estimated ( Table 3).
The rate constant of second-order equation (k) diffusion are 1.17 Â 10 À2 gÁmol À1 Áh À1 for Cr(VI). The correlation coefficients (R 2 ) were 0.996 for Cr(VI) adsorption on the membrane.
The results for rate constant (k) and the amount of adsorbed Cr(VI) (q e ) are shown in Table 4 along with the regression coefficients (R 2 ). From Table 4, it is found that R 2 value of the pseudo second-order is larger than that of pseudo first-order, therefore, the pseudo second-order kinetic model provided more comparable.
Then, the pseudo first-order and pseudo second-order kinetic model of Cr(VI) adsorption using the membrane of carboxymethyl chitosan & silicon dioxide are shown in Figures 20 and 21.
It implies that the adsorption kinetics based on the experimental values is in good agreement with the pseudo second-order kinetic model, and that the rate constant of second-order equation (k) are 3.4 Â 10 À2 gÁmg À1 Áh À1 in this work.
From the kinetic studies, it is found that the pseudo second-order model provided more comparable, the pseudo second-order model implies that the adsorption process for Cr(VI) Figure 19. The pseudo second-order kinetic model on the membrane of chitosan & silicon dioxide.
Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium… http://dx.doi.org/10.5772/intechopen.76035 was mainly chemical, and that the adsorption process involves the valency forces through sharing electrons between the metal ions and adsorbent.
It is obvious that the adsorption capacity of Cr(VI) by the membrane of carboxymethyl chitosan & silicon dioxide is higher than that by the membrane of chitosan & silicon dioxide from the comparison of each maximum adsorption capacity.
Pseudo-first-order Pseudo-second-order q e (mgÁg À1 )   The comparison of maximum adsorption capacity of Cr(VI) by these membranes in present study with that of another adsorbents in literatures are presented in Table 5. As seen in Table 5, the adsorption capacity of the membrane for Cr(VI) in this work is on a level with that of another adsorbents in previous works.

Effect of competitive ions on the adsorption of Cr(VI)
Competitive experiment for Cr(VI) was performed at optimized pH (pH 5), contact time

Adsorption mechanism
Novel adsorbent for Cr(VI) was synthesized by chitosan & silicon dioxide. Adsorption mechanism chromium onto the membrane is shown in Figure 24.
The membrane has carboxymethyl, free amino group and hydroxyl groups on its surface as the adsorption site. It can remove Cr(VI) by forming stable metal chelates, and the porous structure of the membrane enhance the adsorption capacity of Cr(VI). Silanol groups (Si-OH) on the silica surface cross-linked with amino groups and carboxyl groups on the carboxymethyl chitosan were reacted to prepare the membrane. The main role of silicon dioxide is as follows: (1) the specific surface area of the membrane is increased by the porous structure of silicon dioxide, (2) the hydroxyl groups in silicon dioxide may enhance the adsorption capacity of the membrane for the removal of Cr(VI). Carboxymethyl chitosan as well as chitosan was used to enhance the adsorption capacity in this work, and the adsorption sites and specific surface area will increase by changing from chitosan to carboxymethyl chitosan.

Regeneration studies
From industrial and technological point of view, it is desirable to recover and reuse the adsorbed material. Then, regeneration experiments were conducted using the membrane of carboxymethyl chitosan & silicon dioxide after adsorption of Cr(VI) at pH 13.5. In each desorption experiment, 75 mg of the spent adsorbent after adsorption was treated with 200 ml of 0.5 molÁdm À3 NaOH and 2 molÁdm À3 NaCl solution as desorption agent, and then filtered. Cr(VI) content in the filtrate was determined by ICP-AES. Adsorption and desorption studies have been continued during five cycles at room temperature for 4 h as eluent. The adsorption capacity after desorption using the above leaching agent is shown in Figure 25. From this Figure 25, it is found that the membrane still present the high adsorption capacity (74.6%) towards Cr(VI) within three cycles.  Carboxymethyl-Chitosan Cross-Linked 3-Aminopropyltriethoxysilane Membrane for Speciation of Toxic Chromium… http://dx.doi.org/10.5772/intechopen.76035

Conclusions
The efficiency of the membrane synthesized as an adsorbent for Cr(VI) was investigated by batch techniques. The following conclusions can be drawn considering the results of this work: 1. The optimal conditions of adsorption Cr(VI) using the membrane of chitosan & silicon dioxide are determined. The optimal pH is pH 3; the optimal contact time is 80 min; the optimal dosage is 2.0 g dm À3 and 40 mgÁdm À3 was considered as optimum initial concentration. The removal of Cr(VI) by the membrane was more than 80% under the optimal experimental conditions (at pH 5, contact time of 60 min, dosage of 0.25 g dm À3 and initial Cr(VI) concentration of 40 mgÁdm À3 ). The adsorption of Cr(VI) using the membrane conforms to the Langmuir isotherm adsorption equation, and the correlation coefficients was 0.985. The maximum adsorption capacity of Cr(VI) calculated by Langmuir model was 21.2 mgÁg À1 .

2.
The adsorption isotherm of Cr(VI) by the membrane of carboxymethyl chitosan & silicon dioxide was also more suitably described by Langmuir model, and the correlation coefficients was 0.998. It suggests that monolayer chemical adsorption of Cr(VI) on the membrane is more dominant. The maximum adsorption capacity was estimated as 80.7 mgÁg À1 for Cr(VI) under the optimum conditions. The adsorption capacity of the membrane for Cr (VI) in this work is on a level with that of another adsorbents in previous works. The best fit was obtained with a pseudo-second order kinetic model while investigating the adsorption kinetics of Cr(VI) adsorption on the membrane, and the correlation coefficients was 0.990. The rate constant (k) are 3.4 Â 10 À2 gÁmg À1 Áh À1 .

3.
From regeneration experiments (repetition of adsorption and desorption experiment), it is found that the membrane of chitosan & silicon dioxide still presents the high adsorption capacity (74.6%) towards Cr(VI) within three cycles.
From this work, it was quantitatively found that nanomaterials for desalination synthesized in this study can be an efficient adsorbent for Cr(VI). It is very significant information from the viewpoint of environmental protection, and can be used for treating industrial wastewaters including pollutants.