Effect of Fiber Waviness on Tensile Properties of Sliver- Based Natural Fiber Composites

Glass and carbon fiber-reinforced composite materials have been applied for the high demand in industrial use to date, because their advantages are light weight, high strength, and corrosion resistance. However, the disposal problem after the use of these materials has also surfaced as a serious environmental problem. As a measure to solve this problem, many researchers have tried to investigate the potential of plant-based natural fibers instead of artificial fibers. When we use natural fibers as a long fiberreinforcement, the negative point is irregular fiber waviness inherent in a sliver form. This is because such fiber waviness often decreases the mechanical properties. The purpose of this study is thus to clarify the relation between irregular fiber waviness and the composite’s tensile strength. The clarification was performed from two points of view: One is quantification of irregular fiber waviness, based on spatial analysis such as Local Moran’s I and Geary’s c. Result shows that quantified parameters were correlated well with tensile strengths of sliver-based natural fiber composites. Another is a 3-D finite element analysis in which the fiber waviness was treated as an orthotropic body. Finally, the relation of the tensile strengths with maximum stress and Tsai-Hill criterions was discussed.


Introduction
To date, fiber-reinforced composite materials have been used in many industries such as automotive and aerospace, because their advantages are high strength and low specific gravity.Especially, carbon and glass fibers are typical reinforcements of the composite materials.
On the other hand, it is known that production of these fibers needs a large quantity of electric energy [1].After the use of glass fiber composites, as is also known, serious environmental problems have been caused at the process of disposal [2,3].Although several recycle techniques have been developed for used glass fiber composites [3,4], scientists and engineers have tried to use plant-based natural fibers such as flax, kenaf, curaua, and ramie, which are environmentally friendly materials as an alternative [5][6][7][8][9].Composite materials reinforced with the natural fibers are a nonexpensive and fast-growing material, and therefore expected to replace in whole or partially artificial fibers.Materials composed of natural fibers and biodegradable or thermoplastic resin are often called "green composites," and have been applied for car interiors [10].Normally, automotive makers often apply short fiber composites to their interior or exterior parts, which are produced by injection molding, but mechanical properties of short fiber composites are less than long fiber composites.However, there is a problem in the usage of long fiber, which is fiber waviness that reduces the stiffness and strength [9].Hsiao and Daniel [11] explored the relation between fiber waviness and mechanical properties, and proposed a theoretical model of elastic constants on a unidirectional carbon/epoxy composite with fiber waviness by the assumption of sine function.The shape of waviness by sine function was also developed by numerical analysis method [12,13].The results show that the ratio of amplitudes denoted as waviness parameter has an effect on the mechanical properties.Allison and Evans [14] inserted a single waviness part in a unidirectional composite and discussed its strength by identifying its wavy shape as a notch.Karami and Garnich [12] applied a failure criterion to a laminate in which a fiber wavy layer is included, using a finite element analysis.As a key-point in these papers, the fiber wavy shape was all given as a sinusoid [15].On the other hand, the effect of irregular fiber waviness on tensile strength has also been studied.Ren et al. [16,17] used Pearson's type of one-and two-dimensional autocorrelation to analyze the randomness in fiber waviness of a curaua-and flax sliverreinforced composite, respectively.However, this method does not necessarily classify local size and intensity in irregular fiber waviness, which has the tendency to give risky areas on specimen.
Thus, the first purpose of this study is to evaluate quantitatively the randomness in fiber waviness of a flax sliver-reinforced composite, based on the spatial analysis such as Local Moran's I and Local Geary's c [18].Such analyses are known as an effective method to evaluate spatial autocorrelation of point patterns, of which the object in this study is a fiber orientation angle in a small segment on the composite specimen surface.The analyzed autocorrelation value is recognized as an intensity of fiber waviness on each segment.Finally, we discuss if total size of the high intensity segments, so-called area ratio, affects the tensile strength of a flax sliver-reinforced composite or not.
The second purpose of this study is to explore the effect of the fiber waviness on a flax sliverreinforced composite strength, using three-dimensional finite element analysis (3-D FEA).An orthotropic body was assumed for each finite element, which is corresponding to abovementioned each segment.Through major stress components, maximum stress and reduced Tsai-Hill criterions [19] were applied for the prediction of risky areas in the composite.Results show that these criterions can predict the degree of damage for each element, but are not a decisive factor inducing the composite fracture.It was estimated that, finally, the specimen was fractured by mechanical unbalance in tensile stress distribution between laminae, brought from irregular fiber waviness.

Material preparation
To prepare the composite specimen, a flax sliver (TEIKOK SEN-I Co., Ltd.) was used as a reinforcement and shown in Figure 1(a).A biodegradable resin (Randy PL-1000; Miyoshi Oil and Fat Co. Ltd., Japan) was used as a matrix resin in Figure 1(b).This resin was supplied in a water emulsion containing micro-order fine particles of approximately 5.0 μm diameter.The Randy PL-1000 is made from plant-derived resins.Some physical and mechanical properties were shown in Table 1.

Production method and the measurement of fiber orientation angle
In this research, two preparation methods were used to clarify the difference between the composites without and with fiber waviness.First method is the sheet laminate method (denoted as SLM) in which the sliver was combed to form unidirectionally oriented fibers before resin pasting.Another method is the direct method (denoted as DM), in which the sliver was used as a supply state.Thus, SLM is a composite without fiber waviness, whereas DM is a composite influenced with fiber waviness.
For the molding process, first, the emulsion type resin was painted on the sliver, and the emulsion-immersed sliver was dried for 24 hours.The semi-material obtained is called the prepreg.Next, the pre-preg was cut into the size 100 Â 100 mm, and two pre-pregs were put into the mold in a compression molding machine.The temperature was set at 150 C for 40 min, and the hydraulic pressure was set at 3 MPa.Subsequently, the temperature was reduced to room  In order to quantify the irregular fiber waviness, fiber orientation angles on the specimen surface were measured by image analysis software (Asahi Kasei Corp., Japan).On the surfaces, y-axis and x-axis were respectively placed along the longitudinal and transverse directions of the specimen.The specimen was divided into small segments of 1.0 Â 1.0 mm square size, as shown in Figure 2, which are composed of 50 segments along y-axis and 15 segments along x-axis.Thus, the total number of segments is 750 for each surface on the specimen.

Tensile test of composite specimens with and without fiber waviness
Specimens of DM and SLM composites with the size of 100 Â 100 mm square were cut to 15 mm width.Before tensile test, the fiber volume fractions of all composite specimens were calculated as: where W is the composite specimen weight, W f is the flax weight in the composite, V is the composite specimen volume, and ρ m is the density of the biodegradable resin.After that, aluminum plates were attached with epoxy adhesive to both ends, which shaved 45 for preventing the stress concentration.The shape and dimension is shown in  specimen surface to measure uniaxial strain.Tensile test was carried out using an Instron-type testing machine (Autograph IS-500; Shimadzu Corp.) at the cross-head speed of 1 mm/min.
When conducting 3-D FEA, as mentioned later, elastic constants are needed.In this study, average Young's modulus and Poisson's ratio of SLM specimens were respectively regarded as the elastic constants, E 2 , and Poisson's ratio, ν 12 .To obtain E 1 , SLM specimen with 100 Â 100 mm was cut perpendicularly to the fiber axis, and the tensile specimen with 90 direction was produced with the same shape and dimension as Figure 3. Regarding E 3 , the composite was assumed to be transversely isotropic.In addition to elastic constants, tensile strengths of SLM specimens with 0 and 90 directions were adopted as S 2 and S 1 , respectively, and were used for failure criterions in Section 2.6.

Spatial autocorrelation analysis
Spatial autocorrelation analysis is a statistical tool to interpret the degree of dependence among observations in a space, based on the feature locations and the feature values [18].From this point of view, the degree of random fiber waviness on DM composite specimen was quantified using two types of spatial autocorrelation analysis methods, Local Moran's I and Local Geary's c.

Local Moran's I
A spatial measure called Local Moran's I was created by P. A. P. Moran [18].This measure is a typical tool to analyze data point patterns of which the concept is based on a deviation from the average.Local Moran's I is given for each segment as: where θ i is the measured angle of i-th segment, and θ is the average of all measured angles.w ij d ð Þ is the weight function of the pair samples in distance class d at Eq. ( 3), given as: In Eq. ( 3), d is given as a distance between the central positions of i-th and j-th segments.Hence, x i and y i are central positions of i-th segment along the x-axis and y-axis in the ranges of 1-15 mm and 1-50 mm, respectively.From Eqs. ( 2) and (3), it is understood that I i (d) is more susceptible for segments closer to i-th segment.Local Moran's I varies between À1 and +1.If Local Moran's I approaches +1, then the angle at this location is more largely far from the average, but relatively close to the neighbor's angles in their deviation from the average.On the other hand, if Local Moran's I tends to approach À1, then the angle at this location is also higher or lower than the average.In this case, the sign is different from the neighbor angles.When Local Moran's I tends to approach 0, the angle at this location is similar to the average.
Theoretically, when Local Moran's I is either much higher or lower than 0, then the fiber orientation angle is significantly different from the average.Consequently, such Local Moran's I points, if gathered locally, could form a large disordered area in fiber orientation.
Hereinafter, Local Moran's I is denoted as LM-I.

Local Geary's c
Local Geary's c is another typical spatial measure, which avoids the effect of average data by using a deviation around i-th position.Local Geary's c is also given for each segment as: Local Geary's c varies between 0 and 1.When Local Geary's c tends to approach 0, the angle at this location is similar to the neighbor angles.In contrast, when Local Geary's c tends to approach 1, the angle at this location differs from the sign of neighbor angles or much higher than the neighbor's angles in absolute value.Consequently, such points can be disordered parts in fiber orientation.Local Geary's c is hereinafter denoted as LG-c.

Finite element analysis for composite specimen with fiber waviness
To obtain stress distributions on DM specimens, three-dimensional finite element analysis (3-D FEA) was used on Cartesian coordinate system.In this analysis, we assumed that the material was an orthotropic property, of which the stress {σ}-strain {ε} relation was given as follows [20]: where {σ} = {σ x σ y σ z τ yz τ zx τ xy } T and {ε} = {ε ).The components of the stiffness matrix [C] for an orthotropic material in terms of the engineering constants are shown as: where, E is Young's modulus, ν is Poisson's ratio, and G is shear modulus.The fibers are aligned on the 2-axis (on-axis), and 1-and 3-axes are perpendicular to the 2-axis at right angles to each other.When y-axis is placed along the longitudinal direction of the specimen, a fiber alignment has an angle θ to the y-axis on the x-y plane, and the stress components on the fiber axis are changed through [T ij ] as follows: where m = cos θ and n = sin θ.In this formulation, no inclination of fibers occurs in the z-x plane.Finite element mesh used in this analysis is shown in Figure 4, in which then isoparametric 8-node hexahedron element was used.This mesh consists of two laminae, and it is assumed that no delamination occurs during deformation.Thus, each contact point at the interface between the laminae was bonded through one-nodal point.The number of element was 1500, and the number of nodal points was 7344.Each lamina consists of 750 elements, of which the meshing was constructed in the same way as the segments at angle measurement described in Section 2.2.The angle measured in each segment was substituted for θ in Eq. ( 7).
Elastic constants used here are as follows: when we set the fiber volume faction, V f , as 0.70, E 1 and E 3 = 3210 MPa, E 2 = 39,500 MPa, ν 21 and ν 23 = 0.401, ν 12 and ν 32 = ν 21 E 1 /E 2 .These original constants were obtained experimentally, as mentioned in Section 2.3, and estimated to the constant values at V f = 0.7 through the rule of mixture and Reuss rule.G 12 and G 23 = 1610 MPa.These shear moduli was assumed as E 1 /2 through Ref. [16].G 31 was also assumed as being G 12 /2 from Ref. [21].
The boundary condition was a forced displacement, which was applied at one end of the finite element mesh along y-axis.Another end was fixed along y-axis.

Failure criterion
To evaluate risky area in the composites with fiber waviness, maximum stress and Tsai-Hill failure criterions are applied for the stresses on the specimen.

Tsai-Hill criterion
Tsai-Hill criterion is extended from the distortional energy criterion of von-Mises to anisotropic materials.According to this criterion, the general equation is written as: where F, G, H, L, M, and N are the material strength parameters.For the plane stress in 1-2 plane of a unidirectional lamina with fiber in the two direction, σ 3 = τ 13 = τ 23 = 0. Eq. ( 8) was reduced and written as: Then, we applied Tsai-Hill criterion for the definition of risky areas in failure on the specimen.The stresses at each element are influenced by the interaction between elements.Especially, as mentioned later, σ 2 and τ 12 were the dominant stress components, so in this study the reduced Tsai-Hill criterion was used as shown in the following: where, S 1 is the transverse strength of the lamina, S 2 is the tensile strength along the fiber axis, and S 12 is the shear strength.The strength values are given as S 1 = 6.44 MPa, S 2 = 232 MPa, which were obtained by normalizing the SLM experimental values to the fiber volume fraction of 0.70.S 12 was estimated as a double value of S 1 referring to the data of conventional fibrous composites [22].
The values of Tsai-Hill criterion vary between 0 and 1.When the value tends to approach 0, in general, this location is interpreted as a nonrisky area.In contrast, when it tends to approach 1, this location is recognized as a risky area.

Maximum stress criterion
Maximum stress criterion is given on the assumption that, when the ratio of stress to strength achieves to 1, the failure occurs.For this criterion, we used the longitudinal, transverse strength, and shear strength to predict the risky areas on specimens.Maximum stress criterion was hereinafter denoted as MS.When the MS trends to 1, this is the risky point on the specimen.In contract, MS trends to 0 when the value on the specimen is not the risky point.
The MS is described as the below equation.
where, S 1 , S 2 , and S 12 are transverse strength, longitudinal strength, and shear strength, respectively.

Tensile test results
Fiber orientation angles and tensile properties of SLM and DM are shown in Table 2.The results show that tensile strengths of DM specimens accompanied with the fiber waviness are lower than those of SLM.Young's moduli of DM are also lower.It should be noted that the fiber volume fraction of DM specimens are lower in whole than that of SLM.This is attributed to the fact that the fibers cannot be packed compactly, as compared to SLM specimens, because of irregular fiber waviness.However, the lower volume fraction does not necessarily cause lower tensile strength of DM specimens.Here, we estimate the tensile strength of SLM specimen at 61%, the average fiber volume fraction, using is the lower bound of the law of mixture.Where, σ c is the composite's tensile strength, V f is the fiber volume fraction, and a symbol "dash" means a predicted value, such that σ c 0 is a value at the fiber volume fraction V f 0 predicted from σ c .The calculated tensile strength was 202 MPa.
This value is clearly higher than 175 MPa, the average strength of DM specimens, despite of the value derived from the lower bound.It is considered that, therefore, the waviness is a major factor to reduce the tensile properties in strength of the sliver-based natural fiber composite, whereas several low V f specimens show relatively large strengths, as mentioned above, and therefore the effect of irregular fiber waviness is needed to be discussed with unified V f .

Angle distribution and analytical results of special autocorrelation
In order to make contour maps of the fiber orientation angle distribution, each measured angle was assigned to the center point of each segment.*The number of SLM specimens was seven, and their average values are shown.
(a) (b) Natural and Artificial Fiber-Reinforced Composites as Renewable Sources characterized by giving an even evaluation, irrespective of the difference between positive and negative angles.We consider, the intensity and scale of such disorders in fiber orientation is related with the tensile strength to some degree.

Threshold levels of LM-I and LG-c values: definition of area ratio
In this section, we tried to quantify the results of the above spatial analyses by using the concept of "area ratio" characterized by threshold levels.If the area ratios are well correlated with tensile strength data, the strength could be estimated from the fiber orientation angle distribution measured in advance.In this quantification, we used two imaging programs; first is "Graph R221," which was used for plotting a contour map, and the next is "Azo R235," which was used for calculation of area ratio.
For instance, when we choose temporarily threshold levels higher than 0.3 or less than À0.1, the corresponding LM-I areas can be obtained, as shown in black areas of Figure 8(a), (b).In these cases, the area ratios of specimens were calculated as 12.6% (positive side = 11.1% and negative side = 1.5%) and 9.1% (positive side = 6.8% and negative side = 2.3%) for the specimens 2A and 5A, respectively.In Figure 9(a), (b), the black areas of LG-c are higher than 0.2 were selected.The area ratios of specimens were calculated as 16.5 and 13.5% for specimens 2A and 5A, respectively.(b) (a) Here, we consider the change in area ratio with change in threshold level.Regarding LM-I, we take an account of the threshold levels of negative value with a relatively wide range, similarly to that of positive values.This is because the segments with negative LM-I values have a possibility of causing premature damage in shear, although these are not so major.We consider, if appropriate threshold levels are given, there is an optimal area ratio at each specimen, which is well correlated with tensile strength.In other words, the ratio of segments suffering damage during tensile loading should be related closely with the area ratio.In the next segment, thus, the relation between area ratio and tensile strength is investigated.

Relation between area ratio and tensile strength
To investigate the correlation between the area ratio and tensile strength, normalized tensile strength data were plotted as a function of area ratio, as shown in Figures 10 and  11.In these plots, each tensile strength value was normalized by dividing the measured strength by the fiber volume fraction V f and then multiplying it by 0.72, which is V f of SLM specimen.In Figure 10, it is confirmed that the normalized strength is correlated with the area ratio to some extent.The correlation coefficients of LM-I were respectively calculated as À0.44 and À0.65 when setting threshold levels at LM-I > 0.6 or LM-I < À0.1 in Figure 10(a) and LM-I > 0.8 or LM-I < À0.1 in Figure 10(b).The value of À0.65 is not so strong but presents an intermediate strong correlation.This means, if many segments in a specimen are distributed with LM-I values higher or lower than the above threshold levels, its tensile strength tends to be lowered.It also means that a rough value of tensile strength can be estimated through the least-squares regression line between area ratio and tensile strength.LG-c = 0.20).
In contrast, the LG-c area ratio plots are not so correlated with tensile strength data, as shown in Figure 11(a) and (b).The correlation coefficients between the area ratio and tensile strength were obtained as 0.18 and 0.29, when setting threshold levels at 0.2 and 0.5, respectively.The both values of 0.18 and 0.29 obviously signify weak correlation.This result implies that the values of 0.2 and 0.5 are inappropriate as a threshold level, or that LG-c is a measure not to match correlation with tensile strength. .Three positive threshold levels, 0.69, 0.75, and 0.77, were chosen for simplicity.It is confirmed that the optimal threshold levels of LM-I are 0.69 at the positive level and À0.10 at the negative level.These optimal levels brought the correlation coefficient of À0.832, from which it is concluded that LM-I area ratio yields a strong correlation LG-c > 0.5.
with tensile strength.In other words, tensile strength can be estimated to some degree through the least-squares regression line when setting the optimal threshold levels of LM-I.It is also expected that the present procedure is applied as an effective screening method extracting low quality pre-pregs at quality inspection.
Figure 13 shows the relation between correlation coefficient and threshold level of LG-c.Although the coefficient varies with change in the threshold level of LG-c, the highest coefficient is only À0.14 at threshold level of 0.36.This coefficient value is quite a weak correlation, and therefore it is concluded that LG-c area ratio is not a parameter to match correlation with tensile strength.

Normalized stress distributions and maximum stress criterion
Figure 14 shows typical computed stress distributions.Effect of Fiber Waviness on Tensile Properties of Sliver-Based Natural Fiber Composites http://dx.doi.org/10.5772/intechopen.70905maximum value of all shear stress components.The shear stress components were replaced by absolute values.It is proved that σ y distribution is much larger than σ x and σ z , because the specimen is reinforced along the loading axis (y-axis).Regarding the case of shear stress, τ xy distribution working in the plane is also much higher than the others.Shear stress τ yz slightly occurs in the specimen, while τ zx components are negligibly small.
To evaluate the degree of contribution of on-axis stress components to damage occurrence, the maximum stress criterion was used, in which the on-axis stresses, σ 1 , σ 2 , σ 3 , τ 12 , τ 23 , and τ 31 , were divided by the failure stresses, respectively.
, and τ31 ¼ τ 31 S 12 (11) The normalized stresses in Eq. ( 11 also confirmed in the other specimens.Thus, tensile strength of the specimens may be affected by local shear damage mode, according to the maximum stress criterion.But, we should also focus on the possibility of tensile fracture, because the size of the risky area is larger than the shear damage area, as seen from comparison between Figure 15(b) and (c).
3.6.Comparison between spatial autocorrelation analyses, maximum stress criterion and Tsai-Hill criterion with the fracture specimen   Effect of Fiber Waviness on Tensile Properties of Sliver-Based Natural Fiber Composites http://dx.doi.org/10.5772/intechopen.70905

Figure 1 .
Figure 1. Materials used in this study: (a) as-supplied flax sliver and (b) biodegradable resin.

Figure 3 .Figure 3 .
Figure 3. Shape and dimension of the tensile specimen.

Figure 2 .
Figure 2. Division into segments on a DM specimen surface.

Figure 4 .
Figure 4. Three-dimensional representation of finite element mesh.

Figure 5 (
a) and (b) show examples of the contour color maps.The blue (upper right portion in 5(a)) and red (center portion slightly to the right in 5(b)) color areas show the high angle on the negative and positive sides respectively on specimens 2A and 5A, of which the fiber orientation angles vary with approximately 4.0 degree standard deviation.Such contour mapping results and statistical aspect mean that the fiber waviness occurs locally and randomly.

Figure 6 (
Figure 6(a) and (b) shows typical examples of analytical results of LM-I.As shown in both the figures, positive LM-I areas higher than 0.5 are locally distributed with agglomeration of about 5-10 mm scale, whereas several negative LM-I areas are dispersed with a smaller scale.In comparison with Figure 5, it is recognized that Specimen 5A of Figure 6(b) shows quite a similar distribution.Specimen 2A of Figure 6(a) shows that, on the other hand, both positive and negative orientation angles are evaluated with similar color levels.In other words, LM-I is

Figure 7 (
Figure 7(a) and (b) shows typical examples of analytical results of LG-c.In these figures, the range from À1 to 1 is intentionally employed to compare them with LM-I distribution.As shown in the both figures, LG-c areas higher than 0.5 are locally dispersed with about 1-3 mm scale, quite smaller than LM-I, whereas major parts of the specimens are occupied by low LG-c values.Thus, LG-c is a measure accompanied with locally smaller scale.

Figure 12 (
Figure12(a) shows the change in correlation coefficient with change in positive threshold level of LM-I.In this case, the negative threshold level was fixed at À0.1.It is found that the correlation coefficient decreases gradually approximately from 0.25, and shows the lowest value around 0.70, which is approximately À0.80, the highest negative coefficient meaning a strong correlation.The correlation coefficient is also sensitive for the change in negative threshold level, as shown in Figure12(b).Three positive threshold levels, 0.69, 0.75, and 0.77, were chosen for simplicity.It is confirmed that the optimal threshold levels of LM-I are 0.69 at the positive level and À0.10 at the negative level.These optimal levels brought the correlation coefficient of À0.832, from which it is concluded that LM-I area ratio yields a strong correlation

Figure 12 .
Figure 12.Correlation coefficients between LM-I area ratio and normalized tensile strength.(a) Correlation coefficient vs. positive threshold level.(b) Correlation coefficient vs. negative threshold level.

Figure 14 (Figure 13 .Figure 14 .
Figure14shows typical computed stress distributions.Figure14(a) and (b) shows σ x and σ y contour maps, respectively, which were divided by the maximum value of all normal stress components.σ z contour map is omitted in Figure14because it is quite the same as σ x contour map.Figure14(c-e) are τ xy , τ yz , and τ zx contour maps, respectively, which are divided by the

Figure 15 .
Figure 15.Contour maps of unified normalized stress-distribution based on the maximum stress criterion (Specimen 2A).(a) Contour map of unified σ1 distribution; (b) contour map of unified σ2 distribution; (c) contour map of unified τ12 distribution; (d) contour map of unified τ23 distribution and (e) contour map of unified τ31 distribution.

Figure 16 (
Figure 16(a) and (b) shows the fractured specimen (Sample No.2) and the contour map of Tsai-Hill criterion, respectively.As is seen, the latter resembles Figure 15(c).This means, the obtained result from Tsai-Hill criterion is occupied by in-plane shear stress component.In comparison between Figure 16(a) and (b), the both shear fracture portions of the upper and lower sides (see, arrows) in Figure 16(a) may be slightly different from those of Figure 16(b), but the locations are quite close.It is considered that, on the other hand, it may be severe to cause the whole fracture from such small damage areas.It also looks in Figure16(a) that tensile fracture occurs between the two shear damage areas.Figure16(c) shows σ y stress distribution of specimen 2B.It is confirmed that the tensile fracture portion is loaded more largely, whereas σ y stress distribution of specimen 2A in Figure14(b) is reduced (see both regions surrounded by an ellipse).It is estimated that such an unbalanced σ y stress distribution between laminae 2A and 2B causes the final tensile fracture.In other specimens, the similar unbalanced σ y stress distributions were confirmed (it is omitted because of limited space).It is predicted that, thus, although the flax sliver-based composite with irregular fiber waviness may receive some small damages firstly, finally this fractures due to the unbalanced normal stress distribution between laminae.
Figure 16(a) and (b) shows the fractured specimen (Sample No.2) and the contour map of Tsai-Hill criterion, respectively.As is seen, the latter resembles Figure 15(c).This means, the obtained result from Tsai-Hill criterion is occupied by in-plane shear stress component.In comparison between Figure 16(a) and (b), the both shear fracture portions of the upper and lower sides (see, arrows) in Figure 16(a) may be slightly different from those of Figure 16(b), but the locations are quite close.It is considered that, on the other hand, it may be severe to cause the whole fracture from such small damage areas.It also looks in Figure16(a) that tensile fracture occurs between the two shear damage areas.Figure16(c) shows σ y stress distribution of specimen 2B.It is confirmed that the tensile fracture portion is loaded more largely, whereas σ y stress distribution of specimen 2A in Figure14(b) is reduced (see both regions surrounded by an ellipse).It is estimated that such an unbalanced σ y stress distribution between laminae 2A and 2B causes the final tensile fracture.In other specimens, the similar unbalanced σ y stress distributions were confirmed (it is omitted because of limited space).It is predicted that, thus, although the flax sliver-based composite with irregular fiber waviness may receive some small damages firstly, finally this fractures due to the unbalanced normal stress distribution between laminae.

Figure 16 .
Figure 16.Comparison between fractured specimen, Tsai-Hill criterion and normal stress distribution.(a) Fractured specimen; (b) contour map of Tsai-Hill criterion (specimen 2A) and (c) contour map of σ y stress distribution (specimen 2B) divided by the same maximum value as (specimen 2A).

Table 1 .
Properties of the matrix resin and fiber used in this study.MPa pressure for 24 hours.The resultant composite is a laminate consisting of two laminae.The thickness of the laminate is approximately 0.8 mm.