Evaluation of Ultrasound-assisted Modified Fly Ash for Treatment of Acid Mine Drainage Evaluation of Ultrasound-assisted Modified Fly Ash for Treatment of Acid Mine Drainage

The aim of this chapter is to assess the suitability of utilizing fly ash (FA) and modified fly ash (MFA) in the treatment of acid mine drainage (AMD). The effects of various experi mental conditions such as mixing speed, fly ash dosage, contact time, and pH on the efficiency of metal removal from AMD was studied in batch experiments. For modifica tion of FA, ultrasound (US) process was conducted at low frequency (20 kHz) to activate surface area and decrease particle size of FA at 90 W for 30 minutes. Chemical, physical and mineralogical compositions of FA, MFA and solid residues (SR) were determined using arrays of X-ray fluorescence (XRF), Brunauer-Emmett-Teller (BET), scanning elec tron microscopy coupled with energy dispersive X-ray spectrometry (SEM-EDX), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) techniques and par ticle size analysis. The removal efficiency of Al, Fe, Mn, Ni, Zn and SO 4 2− from AMD was compared using FA and MFA. According to the obtained results, ultrasound-assisted MFA provided successful results for metal removal in a shorter reaction time and with smaller dosage than FA. As the pH of the solution (ash:AMD) increased, the metal and SO 4 2− concentrations in SR increased mainly due to precipitation; this data was verified with XRD and XRF analysis. Preliminary treatment of AMD from Etili coal mine (NW Turkey) indicates that MFA could be an effective and low-cost adsorbent for the treat - ment of AMD.


Introduction
The Can coal basin (Canakkale province, NW Turkey) is rich in lignite (100 Mt); though these reserves, known as Can coals, cannot be described as quality coals due to low calorific value and high sulphur content (max: 14.36 wt%) [1]. In the Can coal basin, the Etili mine has operated as open pit since the 1980s [2]. When mining activities ceased without any accompanying remediation methods, these depressions filled with surface and ground waters. During the time, artificial lakes formed and showed typical characteristics of acid mine lakes (AML) with low pH (min: 2.59) and high electrical conductivity values (max: 6430 μS/cm), in addition to high SO 4 2− (max: 5370 mg/L) and metal (Al, Fe, Mn, etc.) concentrations [3]. Acid mine lakes are located upstream of the Kocabas stream, which passes through the Can coal basin before flowing into the Sea of Marmara. Along this stream, drinking water for several residential areas is supplied from boreholes [4]. The pH value of creeks around the mine lakes varies between 2.85 and 5.75 [5], with these creeks passing close to settlement areas. Soil and groundwater quality has been affected along these creeks. These conditions prohibit discharge of untreated acid mine drainage (AMD) into public streams, as they have a detrimental effect on environment. So, for removal of metals from AMD, suitable physical or chemical treatment processes such as chemical precipitation, adsorption, oxidation-reduction, ion exchange, etc. must be performed [6][7][8][9][10][11][12]. Adsorption refers to a mass transfer process by which a substance is transferred from the liquid phase to the surface of a solid and becomes bound by physical and/or chemical interactions [13]. Activated alumina, activated carbon, silica gel, fly ash, saw dust and zeolite are different adsorbent materials reported in the literature [10][11][12][13][14][15][16] for removal of pollutants from water with the adsorption process.
Fly ash (FA), which is a low cost and abundant industrial by-product, has been known for its effectiveness in the remediation of different kinds of industrial wastes in Europe and USA since 1960s [14]. In Turkey, 13 million tons of FA is produced annually and this amount is expected to reach 50 million tons per year by 2020 [17,18]. But only a small amount of FA in Turkey (approximately 1%) is reused in the construction industry (particularly cement industry) [19,20] and the rest is disposed of in ash dumps or landfill which is an inconvenient solution both from environmental and economical points of view [21]. Recent studies have demonstrated that treatment of AMD with FA is an effective adsorption process for metal uptake from water [16,[22][23][24][25][26][27][28]. Ultrasound (US) has been used recently as one of the most successful means of activating adsorbate surfaces [29,30]. The US technology works according to the principle of cavitation and the adsorbent surface modification is achieved by means of pyrolysis and •OH radicals which burst in the water under high temperature and pressure and this results in continuity of use of the adsorbent for purification purposes [30][31][32][33]. High power US produces a permanent chemical or physical change in a material and •H, •OH and •OH 2 radicals when water is liquid irradiated with US [34][35][36]. High intensity shear forces and radicals formed during the US mechanical effect create pits and cracks on adsorbate surfaces resulting in larger specific surface area, higher pore volume and lower particle diameter [37]. The use of US cavitation with adsorption for water treatment has been reported in the literature [38][39][40]. This chapter is a site-specific research carried out to assess the suitability of utilizing FA and modified fly ash (MFA) in the treatment of AMD from Etili coal mine. Within this chapter, an AML that is one of the largest mine lakes in Etili coal mine 1 km Southwest of Keciagili village with 29.41 decar area in July 2016 not drained since the 1990s was chosen (Figure 1a and b). Fly ash was collected directly from the fluidized bed combustion thermal power plant precipitator, which is a coal-fired 135 MW generating facility, located in Northwestern Turkey. In this chapter, FA, a coal combustion by-product, was US-assisted modified with the aim of activating the surface area and decreasing particle size. Removal of metal and SO 4 2− using FA and MFA was determined under various conditions such as mixing speed, ash dosage, contact time and pH in batch experiments. The possibility of utilizing FA and MFA to remove selected metals and SO 4 2− from AMD is evaluated.

Acid mine lake characterization
Four different sampling points were selected and water samples were taken from 0.5 to 1 m depths in the lake using a bailer sampler (Eijkelkamp). Physicochemical parameters of AML  were measured in the field, including pH, oxidation-reduction potential (ORP, mV), temperature (T, °C), electrical conductivity (EC, μS/cm), dissolved oxygen (DO, mg/L), total dissolved solids (TDS, mg/L) and salinity (Sal, %), using a multi-parameter measurement device (WTW 3410). All water samples were stored in 500-mL polyethylene bottles and refrigerated at 4°C until further analysis. Water samples were analysed for major and trace elements using an inductively coupled plasma-mass spectrometer (ICP-MS) at AcmeLabs (Canada). Acidity was measured as methyl orange acidity with digital titrator (APHA 2310 titration method), and Fe(II) was determined by ferrozine spectrophotometric method using a Hach Lange DR 2800 spectrophotometer. Fe(III) was calculated as the difference between Fe(t) and Fe(II). Sulphate was measured by Hach Lange DR 2800 using SulfaVer 4 method.

Fly ash modification
The FA modification was achieved using US technology. The US system was equipped with a titanium probe having diameter of 19 mm, connected to a horn-transducer of 20 kHz supported with a booster and eventually plugged to a power supply of 500 W with a cable (VibraCell 505, Sonics&Materials) ( Figure 2). The batch reactor had a cooling jacket through which tap water was circulated to absorb the heat generated by US treatment. Each 200 mL pure water sample initially containing 10 g of FA was placed in the cooling-jacket reactor, and then modified with US (20 kHz) at 90 W for 10, 30 and 60 minutes. Modified FA was dried in the oven at 80°C for 12 hours. The variations in particle size of MFA at 10, 30 and 60 minutes were determined to identify optimum modification time according to particle size analysis Coal Fly Ash Beneficiation -Treatment of Acid Mine Drainage with Coal Fly Ash (Figure 3). The particle size diameter of FA was decreased and surface area was increased by US mechanical effects. The obtained particle size distribution resulted for 30 minutes had similar Dx (10, 50 and 90) values compared to 60 minutes. Therefore, 30 minutes was chosen as optimum time for modification of FA due to reduce US energy, cost and time.

Batch experiments
Batch experiments were conducted to determine various parameters such as (1) mixing speed (rpm), (2) ash dosage (g), (3) contact time (hour) and (4) pH that affect the removal of metal and sulphate (SO 4 2− ) from AMD using FA and MFA at ambient temperature. (1) Twenty grams of FA and MFA was mixed with 100 mL AMD samples and was agitated under different mixing speeds (60, 120 and 180 rpm) using an orbital shaker (GFL®3005) to determine optimum mixing speed for 0-6 hours contact time. It was found that removal of metal increased with increasing mixing speed. Thus, 180 rpm was selected for optimum mixing speed. (2) FA and MFA were weighed at 5, 10 and 20 g dosage and subsequently added to AMD of 100 mL volume in a conical flask. The mixed sample was agitated using an orbital shaker at 180 rpm for 0-6 hours to determine optimum adsorbent dosage for Fe removal. (3) The effect of contact time on the adsorption of metal (Al, Fe, Mn, Ni and Zn) and SO 4 2− from AMD using 10 and 20 g FA and MFA dosage was evaluated with various contact times (0.2, 0.5, 1, 2, 3, 4, 5 and 6 hours) at 180 rpm. (4) The pH of the AMD was adjusted to 3, 5, 7 and 9 using 1 N NaOH before the tests. All experiments were conducted according to optimum mixing speed (180 rpm), 20 g adsorbent dosage, 6 hour contact time and various pH values to determine Al, Fe, Mn, Ni, Zn and SO 4 2− removal from the solution. At the end of mixing, FA and MFA were separated from  suspension by filtration through a 0.45 μm membrane filter. pH and EC values of the suspension were measured with a multi-parameter device. The residual concentrations of the metal ions in the supernatant were determined using ICP-MS technique. The amount of metal ions adsorbed by FA and MFA was taken as the difference between the initial and residual concentration of the metal ions. Each test was repeated at least three times. In each case, the percentage error for the experiment was lower than ±5%. The solid residues (SR) including FA:AMD and MFA:AMD determined for optimum Fe removal results could settle for 5 minutes and separated from water. Then, SR was dried in the oven at 80°C for 12 hours to determine SR characterization.

Fly ash and modified fly ash characterization
The physical, mineralogical and chemical composition of FA, MFA and SR were identified with particle size, Brunauer-Emmett-Teller (BET), scanning electron microscopy (SEM) coupled with energy-dispersive X-ray spectrometry (EDX), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and X-ray fluorescence (XRF) analyses. The particle size distribution of FA, MFA and SR were measured using a laser-based particle size analyser ( The chemical compounds of FA, MFA and SR were identified using a single-beam FTIR-PerkinElmer spectrum 100 spectrometer, equipped with a diamond crystal in the Chemistry Laboratory in Canakkale Onsekiz Mart University. IR spectra were recorded as changes in absorption as a function of wave number ranging from 600 to 4000 cm −1 .

Hydrochemical characteristics of acid mine lake
The pH value of the mine lake was strongly acidic (2.66). Low pH value of the lake increases the dissolution of numerous elements. Electrical conductivity value of the mine lake was measured as 5.2 mS/cm ( Table 1). Electrical conductivity is related to the concentration of TDS and major ions. Total dissolved solids may be obtained by multiplying the conductance by a factor, which is commonly between 0.55 and 0.75, and generally multiplication factor is approximately 0.67 [41]. Total dissolved solids were measured and calculated as 2720 and 3484 mg/L, respectively. Temperature of the lake (26.3°C) was related to climatic fluctuations (e.g. season and different times of day and depth of water body). Oxidation-reduction potential and DO values were measured as 355 mV and 5.7 mg/L, respectively. Oxidation-reduction potential influences the mobility of most metals, which can exist in several oxidation states. Typically, high ORP values correspond to the presence of oxidizing agents. Thus, ORP values are typically found to be high when DO levels are high [42]. Acidity values based on titrations performed in the laboratory were quite high, 2000 mgCaCO 3 /L. The titrated values are slightly lower than acidity values (2128 mgCaCO 3 /L) calculated using the formula of [43]. Major cation order is Ca 2+ (496 mg/L) > Mg 2+ (267 (mg/L) > Na + (156 mg/L) > K + (3 mg/L), and major anion order is SO 4 2− (3600 mg/L) > Cl − (65 mg/L). Therefore, lake water is best classified as Ca-SO 4 water. The concentrations of Fe and Al in the mine lake are in most cases greater than those of the common ions Na + and K + . The dominant dissolved metals in the lake water, , Al, Fe, Mn, Zn, Co, Ni and Cu values in class IV, and were classified as highly polluted waters.

Mineralogical, physical and chemical characterization of original and modified fly ash
The mineralogical, physical and chemical properties of fly ash depend on the nature of the parent coal, conditions of combustion, type of emission control devices, storage and handling methods [45,46]. Fly ash (pH = 10.95) and MFA (pH = 11.58) have alkaline character when added to deionized water 1:2 (solid:solution ratio) at the end of 24 hours ( , mica (1%) and K-feldspar (1%). Modified FA contains quartz (37%), amorphous phase (31%), mullite (10%), plagioclase (10%), mica (5%), K-feldspar (4%), hematite (2%) and magnetite (1%). Ultrasound-assisted modification decreased particle size diameter of FA and so the percentages of mineral composition changed. Particle size characterization of FA is important for metal adsorption. Adsorption capacity of the smallest particles is better as they are more reactive, and in addition trace elements tend to concentrate in the finest particles. The mean particle size distribution of the FA and MFA is presented in Figure 3.
The results show that the particle size distribution of the FA and MFA ranges between 1 and 144 μm and 0.9 and 116 μm, respectively. From the cumulative distributions, the following values for Dx (

Effect of agitation
At higher agitation speeds, the mass transfer resistance related to ion diffusion through the liquid film surrounding the FA is reduced as the film thickness reduces due to agitation, resulting in greater metal uptake [52].

Effect of adsorbent dosage
Neutralization is generally the first step in AMD treatment [11]. The kinetics of the neutralization reactions was investigated by monitoring the pH and EC values of FA:AMD and  (Figure 7c). Low pH value with a minimum of 2.66 was measured in initial, and the highest pH value was measured ash dosage of 20 g at 6 hours, which compared well with the adsorbent dosage and contact time. Alkaline pH value of solution indicates that modification of FA affects the alkalinity. Acid mine drainage reacted with MFA in 6 hours using 1:5 and 1:10 MFA:AMD ratios by weight produces neutral and alkaline process waters. Electrical conductivity values ranged between 5.2 and 4.85 mS/cm, 5.2 and 4.8 mS/cm, 5.2 and 4.2 mS/cm were measured for MFA dosage of 5, 10 and 20 g at 0-6 hours, respectively (Figure 7d). A sudden increase in EC was observed during the first 10 minutes for all MFA dosages, indicating that soluble material dissolved into the solution resulting in a rapid and irregular increase in EC value. Adsorbent dosage is effective parameter for metal removal [53]. In order to determine the effect of adsorbent dosage on the removal of Fe, AMD (100 mL) was homogeneously mixed with FA and MFA (5, 10 and 20 g) at 180 rpm for 0-6 hours. According to FA, various adsorbent dosages (5, 10 and 20 g), Fe concentration were determined 1.43 mg/L at pH = 4.28, 1.03 mg/L at pH = 4.43, 0.1 mg/L at pH = 5.18 at the end of 6 hours, respectively (Figure 8a). According to Turkish inland water quality regulations [44], Fe concentration must be lower than 0.3 mg/L for unpolluted water classification (Class I). Considering this regulation, optimum FA dosage for Fe removal from AMD was determined as 20 g in this chapter. Fe concentration shows approximately 99.9% removal at pH = 5.18 attained by the FA:AMD ratio of 1:5. According to various adsorbent dosages (5, 10 and 20 g) for MFA,  Fe concentration was determined 0.5 mg/L at pH = 5.51, 0.1 mg/L at pH = 7.3 and 0.05 mg/L at pH = 7.9 at the end of 6 hours, respectively (Figure 8b). It was observed that the adsorbent dosage is an effective parameter for Fe removal using FA and MFA into AMD. Previous studies reported that higher adsorption capacity and larger surface area of FA is related to the efficiency of pollutant removal [54][55][56][57][58]. In this chapter, attempt was made to improve the efficiency of metal removal from AMD with modified FA using US mechanical effect. Modification of FA was provided to increase surface area and decrease diameter range of adsorbent and so, adsorbent dosage reduced by half using MFA. Iron concentration shows approximately 99.9% removal at pH = 7.3 attained by the MFA:AMD ratio of 1:10.

Effect of contact time
In order to determine the effect of contact time on the removal of Al, Fe and SO 4 2− , AMD (100 mL) was homogeneously mixed with FA (20 g) and MFA (10 g) at 180 rpm for 0-6 hours. Figure 9a and b shows the effect of contact time on Al, Fe and SO 4 2− removal from AMD. The pH of the solution (FA:AMD) ranged between 2.66 and 5.18. It is shown from Figure 9a that the removal percentage of Iron from solution increased rapidly for 20 g FA dosage and reached up to 99% at the end of 2 hours. A further increase in the contact time has a negligible effect on the rate of adsorption of Fe. Therefore, the optimum contact time of 2 hour for 20 g FA dosage could be considered for the adsorption of Fe on FA for entire batch studies. The pH of the solution (MFA:AMD) ranged between 2.66 and 7.3. The adsorb Fe on MFA increased with an increase of contact time in particular of the first 1 hour with 99% removal percentage. Iron concentration was successfully reduced below 0.3 mg/L at the end of 1 hour. Therefore, the optimum contact time of 1 hour for dosage of 10 g MFA could be considered for the adsorption of Fe on MFA for entire batch studies. Aluminium precipitates from AMD when they are diluted or neutralized to a pH of ≥ 4.5-5 [59] because pK1 = 5 for Al 3+ hydrolysis, a necessary condition for onset of precipitation [60]. Removal percentage of Al from solution was calculated 85% (pH = 5.18) for dosage of 20 g FA at the end of 6 hours. Aluminium removal from solution was obtained as 86% (pH = 7.3) using 10 g MFA dosage at the end of 6 hours. Modification of FA was provided to reduce adsorbent dosage to half. Initial SO 4 2− concentration of AMD was measured 3600 mg/L. The maximum removal efficiency of SO 4 2− was obtained 18 and 25% for FA and MFA, respectively. According to the obtained results, the effectiveness of SO 4 2− removal from solution using FA and MFA by US enhanced with increasing ash dosage and contact time.

Effect of pH
pH is a major control on the solubility of most metal compounds [61]. The dependence of metal adsorption on pH is different for each metal [62]. Effect of various pH initial (3, 5, 7 and 9) on removal of selected metals (Al, Fe, Mn, Ni and Zn) and SO 4 2− from AMD were determined using 20 g dosage of FA and MFA for 6 hours contact time. The removal efficiency of Al, Fe, Mn, Ni and Zn was obtained 85.5, 99.9, 23.4, 67.5 and 51.2% for FA and 90.7, 99.9, 71.6, 93.8 and 99.4% for MFA at pH = 3, respectively (Figure 10a and b). The removal efficiency of Al, Fe, Mn, Ni and Zn was obtained 98.3, 99.9, 49.3, 83.7 and 99.3% for FA and 99.9, 99.9, 88.4, 97.8 and 99.7% for MFA at pH = 5, respectively. Ultrasound process can also accelerate chemical reactions [38]. The removal efficiency of metals increased in pH (7 and 9) reached over 97% removal. The obtained results showed that metal removal from AMD using FA and MFA depends on the final pH of solution. Sulphate removal as a function of different solutions and pH is shown in Figure 10. Approximately 39% of SO 4 2− can be removed from the solution (MFA:AMD) when the pH increased from 2.66 to 8.03.

Discussion
The AMD in Etili coal mine is highly acidic (pH of 2.66) because of intensive sulphide oxidation and ineffective neutralization processes. The abundance of pyrite in the volcanic rocks, , indicates that this mineral is the main sulphide mineral undergoing oxidation [3]. Sulphate is the predominant anion and Fe and Al are the most predominant metal species in AMD. Two anthropogenic pollutants (i.e. AMD and FA), usually formed in close proximity to each other, were reacted together in this chapter. Fly ash collected from the thermal power plant was modified with US process with the aim of activating surface area and decreasing particle size. The pH value of the ash-water system depends mainly on the Ca/S molar ratio in FA, although other minor alkalis or alkaline earth cations may also contribute to the balance [51,63,64]. Based on the Ca/S ratio and pH value, FA can be classified into three main groups: strongly alkaline ash (pH 11-13), mildly alkaline ash (pH 8-9) and acidic ash [51]. Fly ash is strongly alkaline, and its surface is negatively charged at high pH (see Table 2). Hence, it can be expected to remove metal ions from solutions by precipitation or electrostatic adsorption [62]. Besides, it contains a certain volume of unburnt carbon, which has a high adsorption capacity. The major inorganic species Al, Fe, Mn and SO 4 2− seem to be mainly removed through precipitation of amorphous oxides, (oxy)hydroxides and basic hydroxyl sulphates [16]. The AMD was characterized by high concentrations of Fe 3+ as compared to Fe 2+ ( Table 1). The initial decrease in concentration for both ratios at pH 4-4.5 indicates removal of Fe 3+ in the form of hydroxides or (oxy)hydroxysulphates [16]. Aluminium and Fe mobility at mining sites is related to pH and SO 4 2− concentration [65]. Saturation of iron-hydroxysulphate minerals generally occurs around pH = 4 and so, at pH > 4, Fe precipitates as a solid and is no longer mobile [61,65]. Dissolution of FA and MFA components is confirmed through the decrease of Fe in the Fe-oxide fraction at pH 4.5-4.7. It is often suggested that the tendency of metal cations to adsorb on the oxide surfaces is highly related to their pH of hydrolysis [62,66]. At pH greater than 7, 90.7% of the Al was removed from solution at 20 g MFA dosage and significant proportion of Al from AMD was hydrolysed to form amorphous (oxy)hydroxides. It was observed that the maximum removal   Table 3). The removal of SO 4 2− depends on CaO containing FA. Soluble CaO (1.74-1.81%) in FA and MFA increased the pH value of AMD. According to particle size analysis, the particle size distribution of SR (FA:AMD) increased 31, 18 and 12% for Dx (10,50 and 90), respectively. The particle size distribution of SR (MFA:AMD) increased 5, 6 and 12% for Dx (10, 50 and 90), respectively (Figure 11). Fly ash and MFA reacted with AMD were explained based on the particle morphology, shape and mineralogical components. These interpretations from the particle surface analysis were supported with SEM images. Figure 12a and b shows the SEM images of SR (MFA:AMD). Modified fly ash particles viewed in a predominantly irregular-shaped and have pores and creeks. These results confirm that the surfaces of FA particles were disrupted with US shear forces. According to EDX analysis results, Al, Fe, Mn and Zn concentrations in SR accumulated and precipitated on adsorbent surface. The XRD analysis of the sonicated and unsonicated FA showed no mineral phase change ( Table 4). Gypsum was the only new mineral phase after treatment of AMD with FA and MFA was identified by XRD analysis in the SR. Gypsum was also detected by SEM-EDX analysis (Figure 12c). Gypsum crystals are containing 83.1% O, 8% S and 6.7% Ca, as quantified by EDX analysis (Figure 12d). As the final pH of solution increased, more CaO is available and more Ca 2+ ions are resulting in enhanced removal of SO 4 2− as gypsum. The FTIR spectra of the FA, MFA and SR are illustrated in Figure 13. The FTIR data validate the observations made through XRD. The main band, due    to Si-O and Al-O vibrations, which is located at 1046 cm −1 in FA, moves towards lower frequencies when those are activated [69]. Ultrasound energy strengthens the bond at the solid particle phase interface [38]. Band at about 1000 cm −1 , corresponding either to the stretching vibrations of Si-O bonds in SiO 4 or to the skeleton of bonded SiO 4 tetrahedra, shows the greatest change during crystallization [38,70,71]. The FTIR spectrum of the FA and MFA of crystallization contains a number of characteristic vibration bands in the regions 1100-900 and 850-650 cm −1 .

Conclusion
Due to unique properties of the all mines, AMD may display variable hydrogeochemical characteristics; special studies are required for each mine site, though the general approach remains the same. In this chapter, treatment of AMD using FA and MFA under various conditions was investigated. The effect of US on the surface of FA was ensured adsorbent surface activation by ultrasonic cavitation. The physical changes on the surface of the FA caused by the US-assisted modification were identified using arrays of XRF, BET, SEM-EDX, XRD, FTIR techniques and particle size analysis. It was observed that due to the ultrasoundassisted modification, beside the physical properties of FA, the morphological and mineralogical characteristics are varied as well. The MFA has a lower Si and Al concentrations and higher surface area and pH than the FA. The chemical results imply that it is possible to use FA and MFA in order to neutralize AMD followed by precipitation and adsorption of metals. The 99.9% Fe removal was determined using FA with optimum 2 hours contact time and 1:5 (FA:AMD) ratio and using MFA with optimum 1 hour contact time and 1:10 (MFA:AMD) ratio under the same experimental conditions. Modified fly ash provides more successful results in a shorter reaction time and with smaller FA dosage for metal and SO 4 2− removal from AMD when compared to FA. Acid mine drainage reacted with MFA resulted in neutral pH after a longer reaction time was accompanied by 39% SO 4 2− removal. The five factors that dictate the nature of the final solution in neutralization reactions and metal removal are modification, mixing speed, pH, adsorbent dosage and contact time. Preliminary treatment of AMD revealed that the MFA has the potential to be used as an effective adsorbent to treat AMD. Additionally, this chapter provides an example for other areas with AMD environmental problems.