Nano-Plasmonic Filters Based on Tooth-Shaped Waveguide Structures

Along with development of human society and technology, it becomes more dependable on the miniaturization and integration of semiconductor components, circuits and devices. The performance of integrated circuits, such as micro-processor, is in accordance with the famous Moore’s law that the number of transistors placed inexpensively on an integrated circuit doubles approximately every two years. However, the integration of modern electronic components and devices for information communication and processing have been approaching its fundamental speed and bandwidth limitation, because the ultra-intensive electrical interconnects have an increased effective resistor-capacitor (RC) time constant that increases the time of charging and discharging [1, 2]. This has caused an increasing serious problem that hinders further development in many fields of modern science and technology. Using light signals instead of electronic is one of the most promising solutions. The speed of optical signal is on the order of 108 m/s, which is about 3 orders of the saturation velocity of electrons in a semiconductor such as silicon [3]. However, a major problem with using light as information carrier in conventional optical devices is the poor performance of integration and miniaturization. Dielectric waveguides are basic components and cannot allow the localization of electromagnetic waves into subwavelength-scale regions because of diffraction limit λ0/2n, here λ0 is the wavelength of the light in the free space and n is the refractive index of the dielectric. Photonic crystal (PC) structures and devices have been studied by many researchers since E. Yablonovitch and S. John ’ s two milestone published papers in 1987 [4, 5], which confirmed that the light can be confined in the nanoscale. However, the dimensions of the PC system are on the order of the wavelength or even larger, making them less appropriate for nano-scale optical elements integration.


Introduction
Along with development of human society and technology, it becomes more dependable on the miniaturization and integration of semiconductor components, circuits and devices.The performance of integrated circuits, such as micro-processor, is in accordance with the famous Moore's law that the number of transistors placed inexpensively on an integrated circuit doubles approximately every two years.However, the integration of modern electronic components and devices for information communication and processing have been approaching its fundamental speed and bandwidth limitation, because the ultra-intensive electrical interconnects have an increased effective resistor-capacitor (RC) time constant that increases the time of charging and discharging [1,2].This has caused an increasing serious problem that hinders further development in many fields of modern science and technology.Using light signals instead of electronic is one of the most promising solutions.The speed of optical signal is on the order of 10 8 m/s, which is about 3 orders of the saturation velocity of electrons in a semiconductor such as silicon [3].However, a major problem with using light as information carrier in conventional optical devices is the poor performance of integration and miniaturization.Dielectric waveguides are basic components and cannot allow the localization of electromagnetic waves into subwavelength-scale regions because of diffraction limit λ0/2n, here λ0 is the wavelength of the light in the free space and n is the refractive index of the dielectric.Photonic crystal (PC) structures and devices have been studied by many researchers since E. Yablonovitch and S. John ' s two milestone published papers in 1987 [4,5], which confirmed that the light can be confined in the nanoscale.However, the dimensions of the PC system are on the order of the wavelength or even larger, making them less appropriate for nano-scale optical elements integration.Surface Plasmon polaritons (SPPs) are electromagnetic waves that propagate along the interface of metal and dielectric.In recent years, plasmonics is called the area of nanophotonics under the light diffraction limit that studies the transmission characteristics, localization, guiding of the SPP mode using metallic nanosturctures.The plasmonic waveguides are the most basic components and have been given much attention.Various kinds of metallic nanostructures have been proposed for SPP guiding.Generally these structures could be classified into three big categories: 1) chains of metal nanoparticles [6] and cylindrical metallic nanorods with various geometries [7].2) Metaldielectirc-metal (MDM) or Metal-insulator-metal (MIM) plasmonic waveguides, including groove channel structures in metallic substrates [8], slot waveguide [9].3) Dielectricmetal-dielectric (DMD)/ Insulator-metal-Insulator (IMI) waveguide [10].It should be noted that not all these plasmonic structures can be used for guiding SPP mode to achieve subwavelength localization.Among them, MDM/MIM plasmonic waveguide can propagate SPP mode in the subwavelength scale with relatively low dissipation and large propagation distance.Our following proposed structures are mainly based on the MDM/MIM structures.
Wavelength selection is one of key technologies in fields of optical communication and computing.To achieve wavelength filtering characteristics, plasmonic Bragg reflectors and nanocavities have been proposed.They include the metal hetero-structures constructed with several periodic slots vertically along a metal-dielectric-metal (MDM) waveguide [11], the Bragg grating fabricated by periodic modulating the thickness of thin metal stripes embedded in an insulator [12] and the periodic structure formed by changing alternately two kinds of the insulators [13,14].Lately, a high-order plasmonic Bragg reflector with a periodic modulation of the core index of the insulators [15], and a structure with periodic variation of the width of the dielectric in MDM waveguide [16] have been proposed.Most of the periodic structures mentioned above, however, have total length of micrometers and relatively high propagation loss of several decibels.
In this chapter, we present our recent work on compact nano-plasmonic waveguide filters based on T-series and nano-capillary structures.In section 2, we introduce the novel nanometeric plasmonic filter in a tooth-shaped MIM waveguide and give an analytic model based on the scattering matrix method.In section 3, we investigate the characteristics of double-side teeth-shaped nano-plasmonic waveguide.In section 4 and section 5, we introduce the multiple multiple-teeth-shaped plasmonic filters and asymmetrical multiple teeth-shaped narrow pass band subwavelength filter.In section 6, we introduce a wavelength demultiplexing structure based on metal-dielectric-metal plasmonic nanocapillary resonators.Finally, we make a conclusion.

Single-tooth shaped plasmonic waveguide filter [17]
To begin with the dispersion relation of the fundamental TM mode in a MIM waveguide (shown in the inset of Fig. 1) is given by [18]: with kz1 and kz2 defined by momentum conservations: Where in  and m  are respectively dielectric constants of the insulator and the metal, k0=2π/λ0 is the free-space wave vector.The propagation constant β is represented as the effective index neff =β/k0 of the waveguide for SPPs.The real part of neff of the slit waveguide as a function of the slit width at different wavelengths is shown in Fig. 1.It should be noted that the dependence of neff on waveguide width is also suitable to the region of the tooth waveguide with the tooth width of wt shown in Fig. 2. The imaginary part of neff is referred to the propagation length which is defined as the length over which the power carried by the wave decays to 1/e of its initial value: Lspps=λ0/[4π•Im(neff)].In the calculation above and the following simulations, the insulator in all of the structures is assumed to be air ( 1 and the frequency-dependent complex relative permittivity of silver is characterized by Drude model:   The tooth-shaped waveguide filter is shown in Fig. 2. In the following FDTD simulations, the grid sizes in the x and z directions are chosen to be 5nm×5nm.Since the width of the waveguide is much smaller than the operating wavelength in the structure, only fundamental waveguide mode is supported.Two power monitors are respectively set at the positions of P and Q to detect the incident and transmission fields for calculating the incident power of Pin and the transmitted power of Pout.The transmittance is defined to be T=Pout/Pin.The length of L is fixed to be 300nm, while the tooth width and depth are respectively wt=50nm and d=100nm.The tabulation of the optical constants of silver [19] is used in the simulation.As shown in Fig. 3(a), the tooth-shaped waveguide is of a filtering function: A transmission dip occurs at the free space wavelength nearly 784nm with the transmittance of ~0%.The maximum transmittance at the wavelengths longer than 1700nm is over 90%.The contour profiles of the field distributions around the tooth-shaped area at different wavelengths are shown in Figs.The phenomenon above can be physically explained in the scattering matrix theory [20] as follows: where , ri, ti and si (i=1,2,3) are respectively the reflection, transmission and splitting coefficients of a incident beam from Port i (i=1,2,3), caused by the structure.in i E and out i E stand for the fields of incident and output beams at Port i, respectively.Using the fact that 1 S  , one can obtain: For the case of in in which in 3 E is given as follows: where the phase delay 4 ( ) ( )  is the phase-shift caused by the reflection on the air-silver surface.Combined Eq. ( 5) and Eq. ( 6), the output field at Port 2 is derived as: Therefore, the transmittance T from Port 1 to Port 2 is given by: It can be seen from Eq. ( 8) that, if the phase satisfies ( ) (2 1) m ), the two terms inside the absolute value sign on the right of the equation will cancel each other (as it can be seen in Fig. 3(c)), so that the transmittance T will become minimum.Therefore, the wavelength λm of the transmission dip is determined as follows: It can be seen that the wavelength λm is linear to the tooth depth d, and depends on tooth width wt, through the somewhat inverse-proportion-like relationship between neff and wt shown in Fig. 1.
Figure 4(a) shows the transmission spectra of the waveguide filters with various tooth widths of wt.The maximum transmittance can reach 97%. Figure 4(b) shows the wavelength of the trough vs. the tooth width of wt.The primary dip of the transmission moves very significantly to short wavelength (blue-shift) with the increase of wt for wt<20nm.The shift rate rapidly becomes small after wt>20nm, and tends to be saturated when wt>200nm.As revealed in the Eq. ( 9), the above relationship between the dip position and wt mainly results from the contribution of the inverse-proportion-like dependence of neff on wt.The change rate of Δneff /Δwt within the tooth width of 20nm is much higher than that of Δneff /Δwt after wt>20nm, as shown in Fig. 1, and becomes finally saturated after wt>200nm.Obviously, tooth width wt should be chosen within the range of 20-200nm to avoid the critical behavior and the difficulty in fabrication process.9).Therefore, one can realize the filter function in various required wavelength with high performance by changing the width or/and the depth of the tooth.For example, to obtain a filter with a transmission dip at the wavelength of 1550nm, the structural parameters of wt=w=50nm and d=237.5nmcan be chosen.It can be seen that the wavelength λm is linear to the tooth depth d and depends on tooth width w through the somewhat inverse-proportionlike relationship between neff and w shown in Fig. 1.The dip width of the double-side structure is wider compared with that of the single-side tooth-shaped structure.For better understanding the characteristics of double-side teeth structure, we next discuss the dependence of its filtering spectrum on the symmetry of teeth depth.
Figure 7 shows the transmission spectra of the double-side teeth-shaped waveguide filters with different teeth depths of d1 and d2.From Fig. 7(a), one can see that there are two transmission dips at the free-space wavelengths of nearly 790nm and 1230nm with d1=100nm and d2=180nm.It is found that the wavelength of the second dip shifts to a long wavelength with the increasing of d2 while the first trough keeps unchanged due to a fixed value of d1=100nm.From Fig. 7(b), we can see that the first dip shifts to a long wavelength with the increasing of d1 while the position of the second dip is fixed due to a given d2=180nm.To better understand the origin of the two dips, the transmission spectra of an asymmetrical double-side teeth-shaped waveguide filter with d1=100nm and d2=180nm and two single tooth shaped structures with the tooth depths of 100nm and 180nm are all shown in Fig. 8. From it, one can see that the trough positions of the two single tooth waveguide filters with the tooth depths d1=100nm and d2=0 as well as d1=0 and d2=180nm overlap with the positions of the dips of the asymmetrical double-side teeth-shaped structure, which means the positions of the two dips of the double-side teeth-shaped structure are almost respectively determined by its two different single-tooth parts.Therefore, one can realize the filter function in various required wavelengths by respectively changing the depths of d1 and d2 of the two single teeth.

A multiple-teeth-shaped waveguide bandgap filter [22]
It is straight forward and basic interest to expand a single tooth structure to multipleteeth structure (shown in Fig. 12(a)), and check the difference between them.For the sake of comparison, the waveguide width w and the distance L are fixed to be 50nm and 300nm.Λ and N are the period and the number of rectangular teeth, respectively.wgap stands for the width of the gap that between any two adjacent teeth, and one has    Figure 14(a) and (b) show the transmission spectra of a multiple-teeth-shaped waveguide filter at different periods Λ and period numbers N. As one can see from Fig. 14(a), when Λ=100nm is chosen, the coupling of the SPPs waves between two adjacent teeth is strong which causes the central bandgap wavelength to shift left and the bandgap to be wider.When the period equals to Λ=200nm, the coupling between any two adjacent teeth becomes very weak.One can see in Fig. 14(b) that, the forbidden bandwidth increases little with the changing of the period number from N=3 to 7, while the transmittance of the passband decreases from 93% to 86%.The reason for the decreasing in transmittance can be attributed to the increasing of the propagation loss of the lengthened structure with a large period number.From the simulation results, a tradeoff period number N=4 is the optimized number with the transverse filter length of 4×150nm, which is ~5 times shorter than the previous grating-like filter structures.

A narrow band subwavelength plasmonic waveguide filter with asymmetrical multiple teeth-shaped structure [23]
The asymmetrical multiple-teeth-shaped structure is shown in Fig. 15(a), which is composed of two sets of multiple-teeth with two different teeth depths.The short set has three teeth, and the long set has four teeth.Λ, N1 and N2, are the period, the numbers of short rectangular teeth and long teeth, respectively.wgap stands for the width of the gap between any two adjacent teeth in multiple-teeth structure, and one has t  One can see the maximum transmittance at the wavelength of 1287nm is nearly 90%, and the full-width at half-maximum (FWHM) is nearly 70nm which is much smaller than the bandgap width of 1300nm.The FWHM of the asymmetrical multiple-teeth-shaped structure is also smaller than our previous coupler-type MIM optical filter [24].
In order to understand the origin of the narrow passband of the structure, the spectra of the transmission of a single-set of short three-teeth structure and a single-set of long four-teeth structure are calculated, and shown in Fig. 16.The parameters of the two structures are respectively equal to the parameters of the short teeth part and the long teeth part of the asymmetrical multiple-teeth-shaped structure (shown in Fig. 15(a)).One can see that the passband (or the bandgap) of the long teeth structure and the bandgap (or the passband) of the short teeth are overlapped from 800nm to 1200nm (or from 1450 to 1800nm), and then the transmission of the cascade of the two structure is very low within the two regions.Only the overlapping between the right edge of the passband of the long teeth structure and the left passband of the short teeth is non-zero.This is the reason why the wavelengths around 1300nm have a transmission peak in Fig. 15 (b). Figure 17 shows the central wavelength of the narrow-band as a function of the variation of △d=△d1=△d2.△d is the increment of d1 and d2.The initial values of d1 and d2 are respectively, 128nm 320nm.From the Fig. 17 can see that the central wavelength of the narrow-band linearly increases with the simultaneous increasing of d1 and d2. Figure 18 shows the dependence of transmission characteristic on separation ws.It is found that the transmission at the wavelength of 1287nm reaches the peak value when the separation of ws equals the gap of wt.Therefore, one can realize the narrow-bandwidth filter function at different required wavelengths by means of properly choosing the parameters of the device, such as the teeth-depth, the period or the separation of ws.

A wavelength demultiplexing structure based on metal-dielectricmetal plasmonic nano-capillary resonators [25].
The inset of Fig. 19 shows the nano-capillary resonators composed of two parallel metal plates with a dielectric core.Obviously, the structure can be treated as two MDM waveguides with different widths.Because the width of the lower MDM waveguide is much smaller than that of the upper part, here we call the lower (narrower) part as a nanocapillary.When the gap width w of the MDM waveguide is reduced below the diffraction limit, only a single propagation mode TM0 can exist.The dielectric in the core of the structure is assumed to be air with a permittivity εd =1.
To fully understand how the width of the nano-capillary structure influences the SPPs propagation, the dependences of the effective index of SPPs on the width w at various wavelengths of the incident light are calculated and shown in Fig. 19.From the figure 19, one can see that the effective index of the waveguide decreases with increasing of w at the same wavelength.The effective index at short wavelength is larger than that at long wavelength, for a given width w.The effective index neff2 of the nano-capillary can be larger than neff3 of upper MDM part and n1 of air.As shown in inset of Fig. 19, the waves will flow into the nano-capillary due to its higher effective index, when SPP waves propagate along the interface between metal and air.The wave transmitted into the capillary will be partly reflected at two ends of nano-capillary, because of index differences between neff2 and neff3 as well as n1. are respectively the phase shifts of a beam reflected on the entrance of the capillary and the junction connecting the nano-capillary and the upper MDM waveguide, and d is the length of the capillary.The waves propagating through the structure will be trapped within the nano-capillary when the following resonant condition is satisfied: Here, positive integer m is the number of antinodes of the standing SPP wave.The resonant wavelengths can be obtained as follows:
It can be seen that the wavelength λm is linear to the length and the effective index of the nano-capillary, respectively.Obviously, only the waves with the wavelength λm can stably exist in the nano-capillary, and thus partly transmit or drop into the output end of the nano-capillary.When wideband SPP waves incident into the structure, only the resonance waves with the wavelength λm can be selected and dropped by the nanocapillary.In other words, a transmission peak with the wavelength λm will be formed in the output section.Fig. 20(a) shows a typical schematic of a 1×3 wavelength demultiplexing structure based on MDM nano-capillary resonators.The wavelength demultiplexing structure consists of three nano-capillary resonators perpendicularly connected to a bus waveguide.w1 and d1 stand for the width and the length of the first nano-capillary, respectively.Since the width of the bus waveguide is much smaller than the operating wavelength in the structure, only the excitation of the fundamental waveguide mode is considered.The incident light used to excite SPP wave is a TM-polarized (the magnetic field is parallel to y axis) fundamental mode.In the following FDTD simulation, the grid sizes in the x and the z directions are chosen to be Δx = 5 nm, Δz = 1.5 nm.Power monitors are respectively set at the positions of P and Q to detect the incident power of Pin and the transmitted power of Pout.The transmittance is defined to be / .
out in T P P  The width w΄ of the bus waveguide is set to be 250 nm while the length of L1 and L2 are fixed to be 50 nm and 500 nm.As an example, three nano-capillaries have been designed to split the first, the second and third optical transmission windows, although more nano-capillaries can be added.The parameters of the structure are set to be w = 15 nm, w1 = 250 nm, d1 = 202 nm, d2 = 290 nm, and d3 = 347 nm in calculation.Fig. 20(b) shows the transmission spectra at the outputs of the three channels, and inset of fig.20(b) shows transmittance and reflectance of the bus waveguide.From it, one can see channels l-3 can select 980 nm, 1310 nm, 1550 nm bands, respectively, and the maximum transmittance in three bands can exceed 30% (-5.2 dB).And there is also another high transmission in channel 3 around 820 nm wavelength for m = 2. Given the total phase shift φr, one can estimate the resonance wavelength from Eq. (10).Submitting λm = 1310 nm into Eq.( 10) gives φr = 0.35 for d = 290 nm and neff = 2.01.Other resonance wavelengths can be approximately calculated with the formula.For the lengths of the nano-capillaries of 347 nm and 202 nm, resonance wavelengths are simply estimated to be 1559 nm and 926 nm.The deviation between FDTD simulation and the result from Eq. ( 10) could be partly attributed to the neglecting of wavelength dependence of φr.And it is partly due to the fact that Eq. ( 10) is derived based on the effective index approximation that SPP waves with the phase factor of exp(i2 / ) eff n x   travel back and forth within a capillary, similar to a 3-dimentional plane wave with exp( 2 / ) i nx


 traveling in a bulk medium with refractive index n.
The FWHM of channel 1-3 are 75 nm, 130 nm, 160 nm, respectively.Obviously, the FWHM of the channel 2 and channel 3 are larger than that of channel 1.The reason is that, from the calculation in Fig. 19, the effective index at short wavelength with a fixed width of nanocapillary is higher compared with the one at long wavelength, thus the waves at short wavelength have a higher reflectivity at two ends of nano-capillary and its Q factor is higher.Cross-talk is defined as the ratio between the power of the undesired and desired bands at the outputs.The cross-talk between channel 1 and channel 2 is around -19.7 dB for the 980 nm branch, and the cross-talk between them is -13.1 dB for the 1310 nm branch.The cross-talk between channel 1 and the whole channel 3 is around -19.2 dB for the 980 nm branch, and is -16.6 dB for the 1550 nm branch, although there is also another high transmission in channel 3 around 820nm wavelength for m=2.Therefore, this structure is suitable for wideband wavelengths demultiplexing.
Equation (10) indicates that the transmission behavior of each nano-capillary (channel of the demultiplexing structure) mainly depends on two parameters: the length of the nanocapillary, and the effective index of SPPs in the nano-capillary, which is determined by its width.Figure 21 shows the central wavelength of the nano-capillary resonator as a function of nano-capillary length d.One can see that the central wavelength of nano-capillary shifts toward longer wavelengths with the increasing of nano-capillary length d, as expected from equation (10).Therefore, one can realize the demultiplexing function at arbitrary wavelengths through the nano-capillary resonator by means of properly choosing the parameters of the structure, such as nano-capillary length and width.

Conclusion
In this chapter, we present our work on nano-plasmonic waveguide filters based on tooth/teeth-shaped and nano-capillary structures.We firstly investigated a novel plasmonic waveguide filter constructed with a MDM structure engraved single rectangular tooth.The filter is of an ultra-compact size with a few hundreds of nanometers in length, with reducing fabrication difficulties, compared with previous grating-like heterostructures with a few micrometers in length.We then extended it to symmetric/asymmetric multiple-teeth, capillary structures.The asymmetrical multiple-teeth structure and the capillary structure can achieve selective narrow-band filtering and wavelength demultiplexing functions, respectively.The plasmonic filters might become a choice for the design of all-optical high-integrated architectures for optical computing and communication in nanoscale.In the future, it will be very interesting and usefully to find some solutions to improve the performance of the MIM/MDM plasmonic components.Such as to combine surface plasmons with electrically and optically pumped gain media such as semiconductor quantum dots, semiconductor quantum well, and organic dyes embedded to the dielectric part.Electrically and optically pumped semiconductor gain media and the emerging technology of graphene are also expected to provide loss compensation from visible to terahertz spectra range [26].
plasma frequency, which represents the natural frequency of the oscillations of free conduction electrons.
frequency of the oscillations,  is the angular frequency of the incident electromagnetic radiation,   stands for the dielectric constant at infinite angular frequency with the value of 3.7[16]

Figure 1 .
Figure 1.Real part of the effective of refraction index versus the width of a MIM slit waveguide structure.
3(b)-3(d).The filtering structure is distinguished from the Bragg reflectors based on periodical heterostructure.

Figure 2 .
Figure 2. The structure schematic of a single tooth-shaped waveguide filter, with the slit width of w, the tooth width of wt, and the tooth depth of d.

Figure 3 .
Figure 3. (a) Transmission of the single tooth-shaped MIM waveguide compared with a straight MIM slit waveguide.The width of the waveguide is w=50nm, and the tooth width and depth are respectively wt=50nm and d=100nm.The contour profiles of field Hy of the tooth-shaped waveguide at different wavelengths of (b) λ=510nm, (c) λ=783nm, and (d) λ=1550nm.

Figure 4 .
Figure 4. (a) Transmission spectra of the waveguide filters with various tooth widths of wt, at a fixed tooth depth of d=100nm and the slit width of w=50nm.(b) The wavelength of the trough versus the tooth width of wt.

Figure 5 (
Figure 5(a) shows the transmission spectra of the filters with different tooth depths of d.It is found that the wavelength of the transmission dip shifts to long wavelength with the increasing of d.Figure 5(b) reveals that the wavelength of the transmission dip has a linear relationship with the tooth depth, as our expectation in Eq. (9).Therefore, one can realize the filter function in various required wavelength with high performance by changing the width or/and the depth of the tooth.For example, to obtain a filter with a transmission dip at the wavelength of 1550nm, the structural parameters of wt=w=50nm and d=237.5nmcan be chosen.

Figure 5 (
Figure 5(a) shows the transmission spectra of the filters with different tooth depths of d.It is found that the wavelength of the transmission dip shifts to long wavelength with the increasing of d.Figure 5(b) reveals that the wavelength of the transmission dip has a linear relationship with the tooth depth, as our expectation in Eq. (9).Therefore, one can realize the filter function in various required wavelength with high performance by changing the width or/and the depth of the tooth.For example, to obtain a filter with a transmission dip at the wavelength of 1550nm, the structural parameters of wt=w=50nm and d=237.5nmcan be chosen.

Figure 5 .
Figure 5. (a) Transmission spectra of the waveguide filters with different tooth depths of d, and with a given tooth width of wt=50nm and the slit width of w=50nm.(b) The wavelength of the transmission dip vs. the tooth depth of d with wt=15nm, wt=30nm and wt=50nm.

Figure 7 .
Figure 7. (a)Transmission spectra of the asymmetrical double-side teeth-shaped waveguide filters for different tooth depths of d2 with a fixed d1=100nm and wt=50nm.(b) Transmission spectra of the asymmetrical double-side teeth-shaped waveguide filters for different tooth depths of d1 with a fixed d2=180nm and wt=50nm.

Figure 8 .
Figure 8. Transmission spectra of the two single-tooth waveguide filters and an asymmetrical doubleside teeth-shaped structure with a given tooth width of wt=50nm and a slit width of w=50nm.It is also interest to address a staggered double-side teeth-shaped MIM waveguide structure (shown in Fig.9(a)).Ls stands for the shift length between two single teeth.A typical transmittance of the staggered double-side teeth-shaped waveguide filter with wt=50nm, d1=d2=260.5nm,and Ls =250nm is shown in Fig.9(b).A wide bandgap occursaround =1700nm with the bandgap width (defined as the difference between the two wavelengths at of which the transmittance is equal to 1%) is 660nm, and the transmittance of passband is over 85%.The filter's feature can be attributed to the interference superposition of the reflected and transmitted fields from each tooth of the double-side structure.

Figure 10
Figure 10 shows the central wavelength of the bandgap as a function of the double-side teeth depth of d.During the simulation, we set d=d1=d2.The FDTD simulation results reveal

Figure 10 .
Figure 10.The central wavelength of the bandgap as a function of the double-side teeth depth of d at teeth width of 50nm.

Figure 11
Figure11shows how the shift length of the teeth influences or modifies the filtering spectrum of the structure.One can see that central bandgap shifts left and becomes wider with increasing the shift length of Ls.It reveals the filtering characteristics of the structure depend on the phase difference between the plasmon waves passing through the tooth.The optimized filtering response with a sharp left band-edge and high passband-transmittances over 85% can be achieved when the shift length is around 200nm.
typical transmittance of the multiple-teeth-shaped waveguide filter with wt=50nm, Λ=150nm, d=260.5nmand N=5 is shown in the Fig.12(b), which is obtained with FDTD method.A wide bandgap occurs around  =1.55μm with the bandgap width 590nm, and the transmittance of passband is over 90%.The filter's feature can be attributed to the superposition of the reflected and transmitted fields from each of the five single tooth-shaped components.Figure13(a)shows the central wavelength of the transmittance bandgap, while the right y-axis displays the bandgap width of the waveguide filter as a function of teeth depth d at various wt with the same Λ=150nm and N=5.The FDTD simulation results reveal that the relationship between the central wavelength of the bandgap and the teeth depth d is a linear function for any wt, which is indeed the one of expectations in Eq. (9).
Figure 13(b) shows the central wavelength of the bandgap and the bandgap width as a function of teeth width of wt at various teeth depths.As revealed in the Eq.(9), the relationship between the bandgap position and wt mainly results from the contribution of the inverse-proportion-like dependence of neff on wt as shown in Fig. 1(a).Obviously, teeth width wt should be chosen within the range of 50-100nm with a slope of / Fig. 13(b), and to reduce the sensitivity of the central wavelength of bandgap in fabrication process.Therefore, one can realize the filter function at various required wavelengths with high performance, by choosing the width or/and the depth of the teeth.

Figure 13 .
Figure 13.(a) The central wavelength of the bandgap and the bandgap width as a function of the teeth depth of d at various teeth widths.(b) The central wavelength of the bandgap and the bandgap width as a function of teeth widths of wt at various teeth depths.For the multiple-teeth-shaped structure with the parameters of ,

Figure 14 .
Figure 14.(a) Transmittance spectra of multi-teeth filters with different periods and a fixed N=5, (b) Transmittance spectra of multi-teeth filters consisting of 3-7 periods with a fixed Λ=150nm.
separation between the 3rd short tooth and 1st long tooth is ws.The length of L and the waveguide width w are, respectively, fixed to be 150nm and 50nm.In Fig.15(a) we set d1=148nm, d2=340nm, wt=50nm, wgap= ws =84nm.Figure15(b) shows a typical transmission spectrum of the asymmetrical multiple-teeth-shaped structure using FDTD method.

Figure 17 .
Figure 17.Central wavelength of the narrow-band as a function of the variation of △d=△d1=△d2, △d1and △d2 are respectively the increment of d1 and d2.

Figure 19 .
Figure 19.Dependence of real part of the effective index of SPPs in a plasmonic MDM waveguide on wavelength of the incident light and width w.Inset: schematic picture of a MDM nano-capillary resonator.

Figure 21 .
Figure 21.The central wavelength of nano-capillary resonator as a function of nano-capillary length d.Finally, Figure22shows the propagation of field Hy for two monochromatic waves with different wavelengths of 980 nm and 1550 nm launched into nano-capillary resonator demultiplexing structure.The demultiplexing effect is clearly observed.From the figure, one can see the wave with wavelength of 980 nm passing through the first nano-capillary and the wavelength of 1550 nm wave transmitting from the third nano-capillary.This is in good agreement with the transmission spectra shown in Fig.20(b).

Figure 22 .
Figure 22.The contour profiles of field Hy of the 1×3 wavelength demultiplexing structure at different wavelengths, (a) λ = 980 nm, (b) λ = 1310 nm.All parameters of the structure are same as in Fig. 2(b).
One can expect the nano-capillary operates as a resonator.Resonance waves can be formed only in some appropriate conditions within nano-capillary segment.Defining 