Terahertz Emitters, Detectors and Sensors: Current Status and Future Prospects

The region of the electromagnetic spectrum from 0.3 to 20 THz (10 – 600 cm-1, 1 mm – 15 μm wavelength) is an area for research that encompasses physics, chemistry, biology, materials science and medicine. The lack of sources of high quality radiation has limited developments in this area. However, there has been an upsurge of activity in the last five years due to the emergence of a wide range of new technologies. Terahertz radiation is now available in both continuous wave (cw) and pulsed form, down to single-cycles or less, with peak powers up to 10 MW [Ginzburg et al., 2011; Sizov& Rogalski, 2010; Williams, 2004; Tochitsky et al., 2005]. There is a wealth of information that can be extracted from a study of matter (solid, liquid or gaseous) at these frequencies. It is becoming evident that such directed basic research would also lead to a phenomenally large number of applications covering Physics, Chemistry, Life Sciences and Engineering [Jacobsen et al., 1996; Mueller, 2003; Chamberlain, 2004; Bolivar et al., 2004; Lewis, 2007; Tonouchi, 2007] .


Introduction
The region of the electromagnetic spectrum from 0.3 to 20 THz (10 -600 cm -1 , 1 mm -15 μm wavelength) is an area for research that encompasses physics, chemistry, biology, materials science and medicine.The lack of sources of high quality radiation has limited developments in this area.However, there has been an upsurge of activity in the last five years due to the emergence of a wide range of new technologies.Terahertz radiation is now available in both continuous wave (cw) and pulsed form, down to single-cycles or less, with peak powers up to 10 MW [Ginzburg et al., 2011;Sizov& Rogalski, 2010;Williams, 2004;Tochitsky et al., 2005].There is a wealth of information that can be extracted from a study of matter (solid, liquid or gaseous) at these frequencies.It is becoming evident that such directed basic research would also lead to a phenomenally large number of applications covering Physics, Chemistry, Life Sciences and Engineering [Jacobsen et al., 1996;Mueller, 2003;Chamberlain, 2004;Bolivar et al., 2004;Lewis, 2007;Tonouchi, 2007] .
As stated earlier, to achieve further understanding of physical phenomena in the THz region of the electromagnetic spectrum it is essential that there are reliable sources (including materials, devices and integrated systems) that emit THz radiation.Furthermore, there is need for materials, devices and systems that detect this radiation.Another aspect, which is central to all developments in THz science and technology is the development of reliable standards.Thus, THz metrology is another area that has to develop simultaneously with development of emitters and detectors.One of the applications, which is still in its infancy but has remarkable potential, is THz sensors for a variety of contexts in security, life sciences and medicine.
a phenomenon that was central to explaining conventional superconductivity.A Josephson plasma resonance is produced by coherent propagation of Cooper pairs between superconducting "sheets" in layered superconductors.In a variety of layered superconductors this mode falls in THz frequency range [ Tonouchi, 2007;Ferguson & Zhang, 2002;Sizov & Rogalski, 2010] Other similar strongly correlated electron systems have very complex phase diagrams with several transitions among them.Understanding the nature of these phases, as well as the transitions among them, requires detailed characterization of their excited states, or elementary excitations.The most important excitations are those with an energy of order k B T above the ground state and therefore in the THz region of the electromagnetic spectrum.Fundamental interactions between quasiparticles, phonons, spin-excitations and other constituents of correlated materials occur on ultrafast time scales [ Kida et al., 2005].It is worth noting that the phonon modes of inorganic and organic crystals fall in the THz region of the spectrum [Zheng et al., 2007].
The classical rotation period for a nitrogen molecule with one ħ of angular momentum is about a pico second.Similarly, the time of a molecular collision at room temperature is 0.1 to 1 ps.At very low temperatures the collisional energy of molecular collisions is comparable to the rotational energy level spacing.As a consequence, the collisions are quantum mechanical in nature and resonances in their cross sections occur in the THz region.The time scale of gas phase collisions is of the order 10 -12 seconds which is ideally suited for THz studies.Rydberg atoms in the n = 20 to n = 60 range span the spectrum of sensitive response to THz fields.These are model systems for studying many aspects of few body quantum mechanics, including quantum chaos, quantum-classical correspondence, and quantum systems in the presence of strong external fields [Rangan & Bucksbaum, 2001] .
Interaction of high-intensity femtosecond lasers with solid matter generates plasmas that can be employed as sources of short x-ray pulses, coherent harmonic radiation, energetic electron and ion beams, plasma-based accelerators, ultra high magnetic fields.These plasmas can also serve as a source of intense THz emission [Li et al, 2011].
There are several processes in liquids that occur in the THz region and lend themselves to be probed using THz radiation.THz spectroscopy can also reveal information about protein structure and dynamics.It is possible to distinguish many amino acids based on their THz spectrum, particularly in the crystalline form.The THz spectra of individual DNA base pairs can be used to understand dynamics and conductivity.It could lead to label-free measurement of protein-protein interactions as cellular activity is occurring in live cells.THz radiation holds promise in new medical imaging techniques based on pulsed and cw THz sources.Differences in tissue water, architecture and chemical content can easily be detected using THz techniques since this radiation is strongly absorbed by water.This can lead to early detection of diseases by revealing features that are not apparent with other imaging techniques.[Nagel etal., 2003] .
It is evident that THz region is a region of the electromagnetic spectrum that is rich with information on all forms of matter.It is further obvious that significant developments in this area are technology limited rather than being limited by science.
The research and development in THz science and technology can be broadly divided in to the following categories based on the fundamental phenomena that occur at the THz region www.intechopen.comPhotodetectors 118 of the em spectrum.In all these cases there are issues relating to materials, processing technologies, devices, and system integration issues need to be addressed.

Sources 2. Emitters 3. Detectors and sensors
It is pertinent at this point to distinguish between detectors and sensors.For purposes of this review, detectors are used to signify components that provide only frequency information of the THz radiation.Sensors, in contrast, provide information on both the frequency and time domain as well as the source that causes variation in frequency of radiation incident on the detector.Detectors, thus, form a sub-set of the sensor.Sensors can, therefore be used for imaging, spectroscopy and sensing the nature of environment around the THz emitter or detector.

THz emitters
Terahertz radiation has potential in various short-wavelength communication devices and security applications.In order to attain the potential offered by terahertz technology, design of solid state terahertz emitters is indispensible.Terahertz sources based on femto second lasers pulses is one of the most promising techniques to generate THz radiation.Lasers are strong sources of electromagnetic energy where energy is stored both in the intensity and frequency.THz generation by ultrafast laser pulses can be classified as linear and non linear optical processes.The linear process involves injection of photocarriers by a laser pulse into the semiconductor connected to the antenna.The photocarriers are accelerated by dc bias applied to the antenna.The antenna radiates THz signal of a frequency that is determined by the pulse duration of laser pulses.In contrast, in the nonlinear optical process THz radiation is generated by optical rectification or difference frequency mixing techniques.The nonlinear optics methods are attractive for terahertz devices because of several properties, including (i) possibility of room-temperature operation (ii) easy operation.However, one of the major hurdles in operating terahertz emitters lies in poor power conversion efficiency, which is of the order of 10 -6 to 10 -5 .Terahertz sources can be divided according to their bandwidth, output power, and operating principle [Sakai & Tani, 2005].In following sections we focus on the several kinds of terahertz emitters.Brief theories of the operating principle have been put forth with the explanation of their merits and demerits.

Photoconductive broadband THz antenna
An ultrashort laser pulse incident on the surface of a photoconductor at an angle of incidence θ, generates photocarriers, which then move under the influence of an electrical bias field.The bias field may be either externally applied (parallel or perpendicular to the surface) or internally generated by band bending from trapped surface charges (perpendicular to the surface).The resulting transient photocurrent gives rise to the emission of THz electromagnetic pulses in the reflected and transmitted directions.When a femto second (fs) laser pulse, with an arbitrary intensity profile, excites a biased semiconductor with photon energy greater than its bandgap, electrons and holes are produced at the illumination point in conduction and valence bands, respectively.The rapid changes of the density of photocarriers and their acceleration due to the applied DC bias www.intechopen.comproduce an electromagnetic field radiation into free-space with the help of an antenna.The production of ultrashort currents with a FWHM lifetime of 1 ps or less strongly depends on the carrier's lifetime in the semiconductor.The space-charge screening and radiation-field screening are two factors preventing photoconductor from generating higher power THz radiation, which could affect all kinds of the photoconductive antenna.Based on the shape of antenna, their effects are different.Generally speaking, the space-charge screening can be important to small dipole antennas, but, for large area antennas, radiation-field screening is the major cause of saturation.Photoconducting switches are commonly used in timedomain terahertz spectroscopy, where, a generation and detection THz wave is carried out by use of biased photoconducting GaAs aperture antenna.The advantage of semiconductor photoconductive switches is that they can be used to efficiently generate signals and to generate and detect electrical transients in guided media or free space.However, the problem with photoconductive switches is that electrical pulse width is limited by a number of factors such as the laser pulse width, circuit parameters of the generation and detection site, and the carrier lifetime in the semiconductor.Furthermore, the carriers can be captured by traps at the grain boundaries, resulting in a rapid decay in number of carriers [Sizov & Rogalski, 2010].
Usually materials with reduced carrier lifetimes and high carrier mobility such as LT-GaAs or ion implanted semiconducting layers are utilized.Ga doped InAs based photo conductive switches are expected to yield higher terahertz output because of their higher electron mobility [Lloyd-Hughes et al., 2005].Liu et al. report improvement in photoconductive response in shorter terahertz emission pulses from spiral antennas fabricated on multienergy-implanted GaAs:As [Liu et al., 2005].This is due to the uniformity of arsenic antisite defects (traps) distributed in multi-energy-implanted GaAs:As which contributes to the unchanged carrier trapping time as compared to single-energy-implanted GaAs:As.Miyadera et al. [Miyadera et al., 2004] used amorphous Ge thin films fabricated on (1 0 0) MgO substrates as a terahertz emitter by coupling with Au/Cr transmission lines.Amorphous Ge will be beneficial for optical to electrical signal converter, due to the potential advantages of fabrication without heating process and smaller bandgap of about 0.66 eV.
Light absorption process in the photoconductive switches which generates free carriers near the surface must also be considered.The absorption of terahertz pulses by free carrier can degrade overall efficiency of photoconductors.GaAs constituents of photoconductive switches have a phonon resonance around 8 THz that generates a broad absorption band between 7 and 10 THz.In order to reduce absorption caused by phonon resonance, Kasai et al. have fabricated LT-GaAs epitaxial layer which is transferred onto high resistivity Si substrates [Kasai et al., 2009].These detectors showed higher sensitivity than conventional photoconducting switches at high frequencies.The typical schematic of a photoconductive switch is shown in fig 1.

Photo-Dember effect emitter
If surface energy bands of a semiconductor lie within its bulk band gap, then Fermi level pinning occurs, leading to band bending and the formation of a depletion/accumulation region at the surface.The resulting electric field will separate photo generated electrons and holes, forming a dipole perpendicular to the surface which emits THz radiation, this is the surface-field emission.By changing doping from n type to p type, the sign of the electricfield direction is reversed.This leads to a change in the polarity of the dipole, which is observed as a change in sign of the generated THz transient.A photo-Dember field can occur at the surface of a semiconductor after photo excitation.Two factors lead to this field: a difference in diffusion coefficients for electrons and holes, and a structural asymmetry.In a typical semiconductor, electrons have a larger diffusion coefficient than holes.Therefore, after photo excitation, the electron population diffuses more rapidly than the hole population.In the absence of a surface boundary, there would be no net dipole field, since the center of charge does not change.However, in the vicinity of the surface, reflection or capture of charges results in the center of charge for electrons and holes moving away from the surface.A dipole is thus formed perpendicular to the surface, leading to THz emission.In this case changing the semiconductor doping from n to p type has no effect on the sign of the emitted THz pulse.One of the main applications of photo-Dember effect is the generation of terahertz (THz) radiation pulses for terahertz time-domain spectroscopy.This effect is present in most semiconductors but it is particularly strong in narrow-gap semiconductors (mainly arsenides and antimonides) such as InAs and InSb owing to their high electron mobility.[ Yi et al, 2010;Reklaitis, 2011;Klatt et al., 2010;Krotkus, 2010]

Current transient effect emitter
The current transient emitter or Auston switch is simply a gap in a uniform transmission line defined by thin-film metal fabrication on the top surface of an ultrafast photoconductor The transmission line is, generally, a coupled-strip line terminated in a planar antenna, within a planar strip dipole.The entire transmission line structure is biased with a voltage through an inductor.The principle of operation is that the gap in the transmission line initially creates an open-circuit condition.When a short pulse from a mode-locked laser arrives in the gap, a shower of electron-hole pairs are generated in the first few microns below the surface.The instantaneous concentration of these pairs is high enough to "shortout" the gap.When the laser pulse is terminated, the electron-hole pairs quickly recombine, creating an electrical impulse (or surge current) on the same time scale as the laser pulse.Due to the wide bandwidth of the planar transmission line, the electrical impulse propagates down the line to the antenna with minimal dispersion or droop.So upon reaching the antenna, the electrical pulse generates a significant amount of THz radiation that propagates primarily into the substrate.[Reimann, 2007;Suen et al., 2010;]

Optical rectification based emitters
One of the more popular means of generating THz frequency radiation is through the bulk second-order nonlinear effect of optical rectification.Optical rectification occurs if highintensity light is directed onto an electro-optic material.If the excitation beam contains components of two or more frequencies then difference-frequency mixing, also known as optical rectification, may take place.Depending on the spectrum of the excitation beam, the resulting frequency may be in the THz range.The optical rectification process has been widely developed for THz generation, typically in materials with a completely nonresonant response.The advantage of such an approach is the inherent speed of the response, which may be viewed as essentially instantaneous.The disadvantage is the relative weakness of the nonlinear response.Thus, in order to obtain significant THz emission via the optical rectification mechanism it is desirable to use a medium of appreciable thickness which leads to the necessity of considering phase-matching constraints.The problem of broadband phase matching is a challenge.One possibility is exploiting the non-resonant second-order nonlinear response expected in any non-centrosymmetric semiconductor, such as the III-V materials.This effect can be identified by the distinctive dependence that it shows on the crystallographic orientation of the sample.Optical rectification using an ultra-short femto laser in the periodically poled structure can be considered as a special case of difference frequency mixing where terahertz radiation emitted from the polarization change that follows the transport of excited carriers in an applied or surface electric field.The physics of optical rectification leading to THz generation is well understood [Blanchard et. al, 2011].The nonlinear coefficient of the second order susceptibility is an extremely important material property when high-power output THz emitters are considered.The output power is also predominantly determined by intensity of the excitation pulse and the phase matching conditions.The major disadvantage of this technique is low power output, broad line-width, velocity mismatch and requirement of expensive femto second laser sources.In addition, there are the restrictions implied by other nonlinear processes like two-photon absorption, competing with optical rectification and limiting its efficiency.The process of two-photon absorption not only influences efficiency of terahertz generation but also impacts the terahertz spectrum [Vidal et al., 2011].THz generation via optical rectification of x-mode laser in a rippled density magnetized plasma has been demonstrated [Bhasin and Tripathi [Bhasin & Tripathi, 2009].Fiber lasers are attractive as terahertz emitters because of their low cost, small size, high repetition rate, high pulse energy, and short pulse duration [Hoffmann et al., 2008].
Relativistic optical rectification, has opened up the potential realization of high frequency range terahertz emitter [Tsaur & Wang, 2009].It is should be noted that bandwidth of emitter is sharply reduced in optical rectification due to the phase-matching condition.For EO sampling and optical rectification, the spectral response of the material is strongly sensitive to reststrahlen band absorption/reflection, phase matching, dispersion of refractive index and dispersion of EO coefficients, which can be expressed as () is the velocity mismatch in time, n g (), is the optical group index, n(), is the terahertz refractive index, d is crystal thickness, t() and r() are the Fresnel transmission and reflection coefficients and the multi-reflection of terahertz field inside the sensor material.
The velocity mismatch between phase velocity of terahertz pulse and group velocity of laser beam hampers output power of these sources.This could be eliminated by placing nonlinear crystal in hollow metallic waveguide structure [Nikoghosyan, 2010].The conversion efficiency in optical rectification depends primarily on the material nonlinear coefficient and the phase-matching conditions and various schemes for power enhancement have been reported [Radhanpura et al., 2010;Bugay & Sazonov, 2010;He et al., 2008;Reid et al., 2008].
To overcome the problem of phase mismatch, interaction of pump optical pulse with a twolevel resonant impurities, for the terahertz wave is proposed [Bugay & Sazonov, 2010].
Alternatively, phase mismatching can also be effectively used to tune the operating frequency from 4.2 to 1.1 THz of a (110) oriented ZnTe crystal terahertz emitter.Materials with large drift velocity and short carrier lifetime such as GaAs and ZnTe are popularly used in optical rectification techniques.However, they are limited by large band gap which hampers their efficiency [Li & Ma, 2008].In combination with second order susceptibility, effective second-order processes such as electric field induced optical rectification (EFIOR) has been shown to yield terahertz generation in centrosymmetric Ge crystals [Urbanowicz et al., 2007].This effect has been termed EFIOR, because it is easily explained in the framework of third-order nonlinearity (χ (3) ) contributed to effective second order process by DC surface electric field.

Quantum cascade laser emitters
Energy levels in semiconductor quantum wells can be designed and engineered to be of any value, with ease.In such systems, inter sub band transitions involving electrons that make lasing transitions between subband levels within the conduction band can be exploited to realize emissions in the far infrared and THz regions.Such lasers are called quantum cascade lasers (QCLs).Simple calculations show that energy level separation to achieve emission in the THz region from QCLs is in the meV region (1 THz = 4 meV).Design of quantum well structures for selective injection to the upper level and selective depopulation of electrons from the lower level is a challenge since, due to the narrow separation between subband levels, heating and electron-electron scattering have a great effect.Some of the other challenges that need to be overcome include detection and analysis of spontaneous emission; mode confinement at longer wavelengths; dielectric waveguide confinement (as the evanescent field penetration, which is proportional to the wavelength is of the order of several tens of microns>> the active gain medium of several microns.The physical origin of the THz emission of the quantum cascade laser, as stated above, can be traced to intersubband transitions.The quantum well thickness in QCL is one of the key parameters to control in order to finely tune laser energy.The background blackbody radiation and/or emissions from impurity levels may lead to poor reproducibility of the results.The microprobe photoluminescence has been shown to provide a powerful tool for this purpose which can probe emission from individual states in the active region with the high spatial resolution [Freeman et al., 2011]. Unfortunately, it has been observed that QCL are not popular for THz source due to low energy (long wavelength) output.This is a consequence of the poor coupling between the small gain medium and the optical field.In fact, high optical losses are caused due to free electrons in the material at low energy.Recent developments in QCL technology have raised the hope for their application in terahertz devices.The nonequilibrium Green's function calculations performed by Yasuda et al. [Yasuda et al., 2009] predict that the 4L QCL has a larger terahertz gain than the conventional resonant phonon QCL.They have attributed it to the large number of electrons accumulate in the upper lasing level and contribute to lasing in the new scheme.They have found that the advantage of gain deteriorates at 200 K due to thermally activated phonon scattering.
Another major limitation of QCL is their low operation temperature.The maximum operating temperature of 178 K is currently the highest operating temperature achieved in a THz QCL.The need to use cryogenic cooling is considered to be a major obstacle to the introduction of room temperature QCL in terahertz devices.Ambient temperature operation can be achieved by integrating the optical nonlinearity for difference-frequency generation(DFG) into the active region of a dual-wavelength mid-IR QCL using band structure engineering of the QCL active region [Belkin et al., 2009].However, the disadvantage of DFG QCLs is that they provide less terahertz power than normal QCL.Alternatively, it is also possible to improve temperature performance of QCL by implementation of a second type of waveguide (metal-metal (MM)) design which consists of metal films on both sides of the active region, and provides a mode confinement factor of nearly 100% [Belkin et al., 2009].Optimized Second Harmonic Generation (SHG) in QC lasers, in which the QWs of the active regions simultaneously function as nonlinear oscillators, have led to high absolute SHG power levels of up to 2 µW and large linear-tononlinear power conversion efficiency of around 50-100 µW/W 2 [Gmachl et al., 2003].
The present trend in the search of materials for QCL is to use silicon, which can offer the prospect of integrating coherent terahertz (THz) radiation sources with silicon microelectronics.Silicon is the only material that allows mature processing technology which may reduce costs and allow integration with conventional electronic devices.A recent report on silicon based QCL focused on a variety of n-type SiGe-based heterostructures as design candidates [Valavanis et al., 2011].They have carried out theoretical studies on (001) Ge/GeSi, (111) Si/SiGe, and (001) Si/SiGe material configurations where they have found that (001) Ge/GeSi is the most promising system for development of a Si-based QCL

Photomixers
Modulated infrared radiation can cause the resonant excitation of plasma oscillations in quantum well diode and transistor structures with high electron mobility.This effect provides a mechanism for the generation of tunable terahertz radiation using photomixing of infrared signals [Preu et al., 2011] .
In terahertz photomixer, the outputs of two continuous-wave sources with frequency difference falling in the terahertz range mix in a photoconductors.The laser induced photocarriers short the gap of device producing photocurrent which is modulated at the laser difference frequency.The generated signal is usually fed to the antenna to transmit into free space.The photomixers are tuneable, coherent, compact, low cost and narrow-band THz radiation sources.Photomixers have the greatest tuning range among all the coherent sources in terahertz region.Note that photomixing is fundamentally different from difference frequency mixing.Photomixing is more efficient than difference frequency generation at low THz frequencies.At higher THz frequencies, nonlinearities are more efficient due to parasitic impedances which limit the THz bandwidth of photomixers [Mittleman, 2003].In difference frequency mixing, the outputs of two laser sources are mixed in nonlinear medium like ZnTe or LiNbO 3 , where, an intense laser field can cause the polarization of the nonlinear medium to develop new frequency components.These resultant frequency components of polarization act as source of terahertz radiations.
The frequency and power of the generated terahertz signal can be tuned by tuning the central frequency of one of the lasers.Based on model calculations for LT-GaAs photomixer, it has been proposed [Pilla, 2007] that photomixing efficiency can be enhanced by reducing the transit time of majority of carriers in photomixers and photodetectors to < 1 ps.The model indicated that the output terahertz power, P f is proportional to difference frequency of incident lasers (f) which is given by relation Pf α f -2.77 in the 0.5-6.5 THz range.
In difference frequency mixing, an intense pulsed laser induces a significant polarization in non-centrosymmetric structured materials, which can be written as where first term on the right hand side represents linear polarization while second term is responsible for SHG (second harmonic generation), dc rectification, Pockels effect, parametric generation etc In nonlinear crystals, sum frequency generation (SFG) or difference frequency generation (DFG) can occur, where two pump beams generate another beam with the sum or difference of the optical frequencies of the pump beams.If the incident electric field contains two different frequency components  p and  s and amplitudes E g and E p respectively, the resultant intensity can written as It is clearly seen from equation (4) that the second order nonlinear susceptibility will give rise to a nonlinear polarization and reemit radiation at sum ( p +  s ) and difference ( p - s ) frequencies.
Advantages associated with a difference frequency generation include simple frequency control, narrow linewidth and wide tuning ranges based on low loss and phase matched NLO crystals and tunable pump lasers.Diode lasers are sometimes used in difference frequency generation sources for large band width THz signals.Narrow-band terahertz pulse generation via difference frequency mixing using fs laser irradiation of periodically poled lithium niobate (PPLN) and stoichiometric lithium tantalate (PPSLT) crystals [Yu et al., 2011].The bandwidth of output terahertz radiation obtained was as low as 32 GHz for 1.38 and 0.65 THz for forward and backward THz pulses respectively.The phase mismatch is another critical factor affecting performance of difference frequency generation sources.The conversion efficiency in difference frequency generation process depends primarily on the material's nonlinear coefficient and the phase (velocity) matching conditions.The wave vector of the applied field and the generated field must have the same relation as their frequencies.Unfortunately in nonlinear crystals, the optical beam always travels faster than the THz beam, which makes the phase matching unachievable.Several phase matching techniques been explored to improve output power of terahertz emitters.The phase matching techniques can reduce decay of terahertz radiation in the crystals by techniques like reducing beam diameter [Shibuya et al., 2010] or artificially introducing reversed domain structures (quasi-phase matching, QPM) [Marandi et al., 2008] 4. THz detectors and sensors

Detectors
THz detectors have been developed based on a variety of principles as described below.
However there are two generalized performance parameters that characterize THz detectors.These are Noise Equivalent Power (NEP) and detectivity.
Noise Equivalent Power (NEP) is defined the incident RMS optical power required in order to obtain signal-to-noise ratio of 1 in a bandwidth of 1 Hz.NEP is related to the minimum power that the photodetector can detect Where i n is the noise current, and R is the detector responsivity.The related figure of merit is detectivity defined as where B is the bandwidth and S is the detector area.[Sizov & Rogalski, 2010]

Direct and heterodyne THz detection based on the principle of bolometer
Hot electron bolometers are very commonly used for THz detection.The term hot electron describes electrons which are not in thermal equilibrium with the lattice.In metals the heating of electrons does not change the electron mobility and therefore it does not affect the resistance value.The hot electron approach is very productive for semiconductors, where the mobility of electrons depends on their effective temperature.In a superconductor, the hot-electron phenomenon consists of the heating of electrons by radiation.A photon incident on a superconductor is absorbed by a Cooper pair.Due to the large coherence length only one of the electrons of the Cooper pair absorbs the photon.The Cooper pair breaks apart and one highly excited electron with energy close to the incident photon energy and one low-energy quasiparticle are created.Next the quasiparticle loses its energy via electron-electron scattering and creates a secondary excited electron.This process continues so long as the incident radiation is switched on.There are two different techniques to detect the power of submillimeter and far-infrared wavelengths.The first approach is to detect the radiation directly by creating charged carriers or converting the incoming energy to heat proportional to the flux of the incoming photons.The first method is direct detection which is also called an incoherent detection.Direct detectors do not have a fundamental limit of the sensitivity.A direct detector does not produce any noise power unless photons are absorbed.The second method is to shift the incoming radiation to a lower frequency band and then amplify and detect the power of the radiation.The method of shifting the incoming radiation to a lower frequency is called heterodyne principle or coherent detection.In a heterodyne receiver a locally generated frequency is mixed with a signal frequency to produce a signal at a much lower frequency.This frequency conversion is done by a mixer element.The locally generated frequency and the signal frequency are added together to produce a beat frequency, the difference between the signal and the locally generated frequency.The HEB can be used as a heterodyne mixer.The incident radiation and the local oscillator (LO) radiation excite a voltage across the bolometer.The dissipated power of the bolometer is a function of the average absorbed signal power and the average absorbed LO power.The output power consists of a component equal to the difference frequency of the electronic diode.Thus, a HEB can be used as a heterodyne mixer, if it is fast enough to follow the IF [Cherednichenko et al., 2002, Zmuidzinas & Richardds, 2004] .
Superconductor-insulator-superconductor (SIS) tunnel junctions are extremely sensitive heterodyne mixers and have been widely used for frequencies below 1 THz.The upper frequency limit of these devices is determined by the gap frequency of the superconductor defined by fgap = Δ/h with Δ the superconducting gap energy and h the Planck's constant.Drastic losses above the gap frequency of the superconductor (about 700 GHz for niobium) occur inside the superconducting tuning circuit which is used to match the impedance of the SIS device to the antenna impedance.Using superconductors (like NbN or NbTiN) having a higher gap frequency than Nb has increased the upper frequency limit of SISmixers to about 1.2 THz.The main advantage of SIS mixers is the wide Intermediate Frequency (IF) bandwidth provided by this type of mixer.HEB mixers do not have an upper frequency limit and provide a very high sensitivity (T rec < 2000 K) and require very low LO power (< 1 μW).Although the IF bandwidth of HEB mixers is rather limited compared to Schottky and SIS mixers, HEB mixers are the most competitive devices for heterodyne detection in the THz range.When compared by characteristics like response time and dynamic range, SIS detectors are found to be much superior to their TES counterparts [Matsuo, 2006].
The use of low temperatures based on Nb, NbN and a number of related compounds have been reported .In these cases while the fabrication of the bolometer structures is routine since feature sizes are large, the very low operating temperatures (<20 K, in some cases) is a major drawback [Chen et al., 2009;Tretyakov et al. ;Stern et al., 2005;Schultz & Lichtenberger, 2007;Ilin et al., 2010;Liu et al., 2009;Kleinschmidt et al., 2007;Cherednichenko et al., 2007 ] .In addition, these bolometers work in the range < 5 THz, generally.The typical schematic view of a HEB structure is shown in figure 2. Bolometers have also shown potential for application in space and astronomy [Meledin et al., 2004;Caumes et al., 2009;Putz et al., 2011].The discovery of high temperature superconductors has helped in increasing the operating temperature of the HEBs to liquid nitrogen temperatures.For example, an ultrathin PBCO/YBCO/PBCO HEB [Peroz et al., 2007] constructed by ultra-thin (10 nm thick) superconducting micro-bridge coupled with a planar antenna was demonstrated.However, the limitation on mixing operation of HEB is observed causing by aging of thinner layer and nano bridge structure.Tonouchi et al [Tonouchi et al, 2005] have reported extensively on the use of YBCO based antennae for THz detection.There are many other reports on the use of high Tc superconductors as bolometers, but only a few are listed [Du et al, 2011;Aurino et al., 2010;Laviano et al., 2010;Jagtap et al., 2009] There are some disadvantages of bolometric type of detectors, such as they are extremely sensitive to background radiation, temperature fluctuation, mechanical vibration and electrical interference, and the performance deteriorates with increasing frequencies in the THz range.Further, bolometers are insensitive to phase which does not allow the reconstruction of the pulse shape in the time domain.It should be noted that background radiation defines the limiting condition of sensitivity of detector.The sensitivityof the bolometer is mainly determined by the system noise temperature.System noise includes noise from the input source and noise generated in the receiver.

Schottky barrier detectors
Schottky-diodes have been the only available technology for the detection of THz radiation for a long time {Roeser et al, 1994].They do not require cooling to cryogenic temperatures and cover a wide frequency range up to several THz.The main disadvantages are the poor sensitivity and the high local oscillator (LO) power requirement.The LO is still a critical element for heterodyne detection in the THz frequency range.Solid state sources often do not provide enough power for the heterodyne operation in the THz range but are under development right now.One of the early reports on Schottky diodes for THz applications was by Suzuki etal [Suzuki et al 1999].They presented results on submicrometer Pt/GaAs diode fabrication process that resulted in a significant reduction in low-frequency noise.Noise performance was optimized by establishing an even distribution of gallium and arsenic (stoichiometric surface) at the contact surface.Diodes fabricated with the optimized procedure exhibited a signal-to-noise ratio that was better than that of commercially available diodes at 0.9 THz.Rinzan et al [Riznan et al., 2005] demonstrated a heterojunction interfacial work function internal photoemission (HEIWIP) detector with a threshold frequency (f 0 ) of 2.3 THz ( 0 = 128 m).The threshold limit of ∼ 3.3 THz (92 μm) was surpassed using AlGaAs emitters and GaAs barriers.The peak values of responsivity, quantum efficiency, and the specific detectivity at 9.6 THz and 4.8 K for a bias field of 2.0 kV/cm are 7.3 A/W, 29%, 5.3×10 11 , respectively.Yasui et al [Yasui et al, 2006] developed a wide-bandwidth, high-sensitivity, continual terahertz-wave sensor that utilizes a quasioptical parabolic mirror and a Schottky barrier diode and successfully applied it at up to 7 THz range.This sensor utilized a parabolic cylindrical mirror, a long-wire antenna, and a Schottky barrier diode.The antenna, placed at the focal point of the parabolic mirror, quasioptically collects the terahertz signalleading to superior performance.Ryzhii et al., [Ryzhii et al., 2006] investigated the plasma oscillations in a two-dimensional electron channel with a reverse-biased Schottky junction.They show that the plasma instability can www.intechopen.comPhotodetectors 128 be used in a novel diode device -lateral Schottky junction tunneling transit-time terahertz oscillator.Magno et al grew [Magno et al., 2008] Antimonide-based p + N junctions.The diodes had good rectification with ideality factors near 1, and high saturation current densities of 2.5×10 −2 A/cm 2 .A cutoff frequency of 6.5 THz is estimated from the RC product.The high saturation current indicates that this diode could be used as a terahertz mixer.Maestrini et al [Maestrini et al, 2010] reviewed some aspects of the technology of terahertz heterodyne receiver front-ends dedicated to astrophysics, planetary and atmospheric sciences with focus on frequency multipliers and Schottky mixers.It is clear from this review that there is much potential for research in the area of novel architectures of power-combined frequency multipliers at submillimeter-wavelengths, THz planar fundamental mixers, and integrated receivers and the fabrication of submillimeter-wave planar Schottky diodes.Chen et al. [Chen et al, 2010] demonstrated high performance nanometer NiSi 2 -Si Schottky barrier diode arrays (SBDA) with various isolation designs, including poly Si gate (PSG) and resist protection oxide (RPO) for advanced radio frequency applications.The SBDAs could achieve a cutoff frequency of up to 4.6 THz.
It is evident from a brief survey of literature that Schottky diode structures have great potential for application in THz detectors impacting a variety of fields.However, there are several challenges in design, fabrication and operation of these device structures that remain unresolved

Field-effect transistor detectors
A channel of a Field Effect Transistor (FET) can act as a resonator for plasma waves.The plasma frequency of this resonator depends on its dimensions and for gate lengths of a micron and sub-micron (nanometer) size, can reach the Terahertz (THz) range {Dyakanov, 2008].The interest in the applications of FETs for THz spectroscopy started at the beginning of 90s with the work of Dyakonov and Shur [Dyakanov and Shur, 1996] who predicted that plasma oscillations in a FET channel can lead to the THz emission.Recently, non-resonant plasma properties were successfully used for the room temperature broadband THz detection and imaging by silicon FETs.Both THz emission and detection, resonant and nonresonant, were observed experimentally at cryogenic, as well as at room temperatures, clearly demonstrating effects related to the excitation of plasma waves.The possibility of the detection is due to nonlinear properties of the transistor, which lead to the rectification of an ac current induced by the incoming radiation.As a result, a photoresponse appears in the form of dc voltage between source and drain which is proportional to the radiation power (photovoltaic effect).There are three distinct regions of operation of the FETs depending on gate lengths.It has been demonstrated that for gate lengths of the order of 0.1 μm the plasma oscillations will be in the low THZ region [Dyakanov, 2008].Otherwise the FET can operate as a broad-band THz detector.There are a few other reports on the use of FETs as THz detectors, signifying again the potential of these structures as wellas the number of fabrication issues that need to be overcome [Knap et al., 2011].The use of nitride based FETs for THz detection has also been demonstrated.[Shur, 2007]
Otsuji et al. [Otsuji et al., 2010] reviewed recent advances in emission of terahertz radiation from 2D electron systems in semiconductor heterostructures.A self-consistent spatiotemporal variation of quantum confined electron gas with sufficiently high electron mobility in the channel of HEMT has been proved to be an efficient mechanism for the detection and emission of terahertz radiations.The main advantage of the HEMT over the non-laser based sources is in working temperature and hence hardware requirement for operation.Another major advantage of HEMT terahertz emitters are their high tunability and low fabrication cost.The introduction of closely-spaced heterojunction interfaces under the right conditions produces a two-dimensional electron gas (2 DEG).This low dimensional plasmon (electron gas) is favourable for solid-state far-infrared and THz sources.The strong confinement of charge carriers in the quantum well is believed to be the cause of large electron mobility.Further, the small channel length of the device, leading to an increase in transconductance with an increase in carrier mobility, is well known for HEMT.However, the high losses caused by free carrier absorption and small confinement factor of heterostructure are the factors which restricts use of HEMT at longer THz wavelengths.
Monte Carlo simulation performed to study of transient electron transport in wurtzite GaN, InN, and AlN shown that, for ideal transistors with L = 0.1 μm, by replacing the GaN channel with InN, can be expected increase frequency of operation from 0.48 to 0.68 THz.Moreover, low m e (effective electron mass) in the InN channels also gives a prospect for electron nonstationary dynamics, and operating frequency over 1 THz has been predicted for 0.1 μm gates in that case [Foutz et al., 1999].Further increase in operating frequency (THz range) is, in fact, expected in ultrathin gate structured HEMT.Fatimy et al. [Fatimy et al., 2010] have demonstrated room temperature terahertz generation by a submicron size AlGaN/GaN-based high electron mobility transistor.They have showed that these transistors are tunable by the gate voltage between 0.75 and 2.1 THz.It is also possible to tune operating frequency by manipulating cap, window, and gate lengths and other structural parameters [Ryzhii et al., 2006].
Understanding the physics of plasma wave resonant line broadening is essential to improve performance of HEMT based plasma wave detectors of terahertz radiation.Properties of HEMT terahertz detectors are defined by plasma wave excitations of two dimensional electron gas [Tsaur & Wang, 2009].Recently it has been demonstrated that narrow terahertz plasma wave resonant detection at low temperature in 200 nm gate length InGaAs/InAlAs multichannel HEMT.To achieve selective resonant and voltage tunable terahertz emission, they have maintained the gate width is in the order of the gate length [Shchepetov et al., 2008].The typical schematic of a High electron mobility transistor used for THz detection is shown in fig. 3.

Sensors
The state of technology in THz sensors is briefly reviewed.A variety of THz sensors have been developed recently mainly for use in biological and medical applications .Federici et al have reviewed the developments in THz sensing [Federici et al, 2005] technology, spectroscopy and imaging for security applications.The typical view of a THz imaging set up is shown in fig. 4. The authors state that since, (a) THz radiation can detect concealed weapons since many non-metallic, non-polar materials are transparent to THz radiation; (b) target compounds such as explosives and illicit drugs have characteristic THz spectra that can be used to identify these compounds and (c) THz radiation poses no health risk for scanning of people stand-off interferometric imaging and sensing for the detection of explosives, weapons and drugs is critical.Future prospects of THz technology are discussed.Nagel et al [Nagel et al, 2003] first reported a novel resonant THz sensor for the label-free analysis of DNA molecules.The sensor allows the direct detection of DNA-probe molecules at functionalized electrodes via hybridization.Subsequent time resolved photoconductive sampling of the THz transmission identifies the binding state between probe and target DNA.Integrating neighbouring sensors on a chip, this technique can be extended to a parallel analysis of multiple DNA sequences.Nagel et al [Nagel et al, 2006] then reviewed the state of biological THz technology applications and conclude that success in this area will strongly depend on the development of compact, low-cost and flexible systems.They have reported on different approaches for THz biosensor systems based on femtosecond lasers and discussed the technology for generation, transmission and detection of THz signals as well as their application formarker-free biomolecule detection on functionalized www.intechopen.comsurfaces in dry and fluid environments.Kitagawa et al [Kitagawa et al , 2006] demonstrated the THz spectroscopic performance of highly integrated sensor chips based on microstrip lines by measuring biomolecule/water systems.The concentration resolution of the chips reaches down to 0.05 g/ml.They have confirmed that the number of bound water molecules per biomolecule can be obtained with precision using solid state transmission lines.The chips are highly suitable for the inspection of small amounts of specimen and for the application to a wide range of water rich materials.McLaughlin et al [McLaughlin et al , 2008] employed poled polymer films 10-15 m thick with electro-optic coefficients as high as 160 pm/V at 1300 nm are used to generate and sense subpicosecond pulses with continuous bandwidth up to 15 THz.The use of the poled polymer as the terahertz sensor for the identification of DAST phonons at 1.1, 3.0, 5.3, 8.5, and 12.5 THz was demonstrated.
Kawase etal [Kawase etal , 2010] have suggested a wide range of real-life applications using novel terahertz imaging techniques.A high-resolution terahertz tomography has been demonstrated by ultra short terahertz pulses using optical fiber and a nonlinear organic crystal.They, further, describe a nondestructive inspection system that can monitor the soot distribution in a ceramic filter using millimeter-to-terahertz wave computed tomography.Another proposed application is in the area of thickness measurement of very thin films using the high-sensitivity metal mesh filter.Abbas et al [Abbas et al , 2009] describe the development, functionalization and functionality testing of a TeraHertz (THz) Bio-MicroElectroMechanical System (BioMEMS) dedicated to enzyme reaction analysis.The microdevice was fabricated by mixing clean room microfabrication with cold plasma deposition.The progression of the hydrolysis reaction over time was monitored by the THz sensor connected to a vectorial network analyzer.Preliminary results showed that sub-THz transmission measurements are able to discriminate different solid films, various aqueous media and exhibit specific transmission behavior for the enzyme hydrolysis reaction in the spectral range 0.06-0.11THz.Rau et al [Rau et al., 2005] reported on a simple THz waveguide element used as a sensitive sensor for adsorbates on surfaces.The evanescent wave from total internal reflection off a silicon prism was used to couple pulsed THz radiation frequency selectively into the waveguide.The coupled frequencies were determined via time domain spectroscopy and react sensitively to any changes of thickness or phase shift upon reflection.In particular, the sensitivity to phase shifts makes this waveguide sensor attractive for the detection of very thin adsorbates.Xiao-li and Jiu-sheng [Xiao-li & Jiu-sheng,2011] used terahertz time-domain spectroscopy technique to test flour/talc powder mixture samples.They found that the two samples have distinct absorption peaks and different refractive index in the THz region leading to the possibility of THz applications to the field of food safety.Mendis et al [Mendis et al, 2009] describe a terahertz optical resonator suited for highly sensitive and noninvasive refractive-index monitoring.The resonator is formed by machining a rectangular groove into one plate of a parallel-plate waveguide, and is excited using the lowest-order transverse-electric (TE 1 ) waveguide mode.Since the resonator can act as a channel for fluid flow, it can be easily integrated into a microfluidics platform for real-time monitoring.Using this resonator with only a few microliters of liquid, a refractive-index sensitivity of 3.7×10 5 nm/refractive-indexunit was demonstrated in the THz range.Lu et al [Lu et al., 2008] discuss broadband terahertz wave detection through field-induced second harmonic generation using selected gases.The dependences of the detected second harmonic intensity on probe pulse energy, bias field strength, gas pressure, and third order nonlinear susceptibility are systematically investigated with xenon, nitrogen, SF 6 , and alkanes.Experiment results reveal that the detected second harmonic intensity quadratically depends on the third order nonlinear susceptibility of the gas.Two orders of magnitude enhancement in the dynamic range of broadband terahertz wave detection are observed with alkane gas (C 4 H 10 ) sensor.Foltynowicz et al [ Foltynowicz et al, 2006] reported the vapor-phase spectrum of 2,4dinitrotoluene (DNT) from 0.05 THz to 2.7 THz utilizing pulsed terahertz time-domain spectroscopy.They observed a broad-band absorption profile from 50 GHz to 600 GHz, peaking at 240 GHz.This broad absorption profile corresponds to DNTs pure rotational spectrum, which was confirmed by asymmetric top model calculations.Superimposed on the broad absorption profile, we observed discrete structure that extended to the higher THz frequencies.Leahy-Hoppa et al [Leahy-Hoppa et al, 2007] have shown Time-domain terahertz spectroscopy (TDTS) to be a promising tool in detection of explosives and explosive related compounds.The THz absorption spectra over an extended frequency band from 0.5 to 6 THz were reported for four explosives: RDX (1,3,5-trinitroperhydro-1,3,5triazine), HMX (1,3,5,7-tetranitroperhydro-1,3,5,7-tetrazocine), PETN (pentaerythritol tetranitrate), and TNT (2,4,6-trinitrotoluene). New distinctive spectral features are shown in these materials between 3 and 6 THz.Zhang et al [Zhang et al, 2008] present terahertz reference-free phase imaging for identification of three explosive materials (HMX, RDX, and DNT).They propose a feature extraction technique to locate the spectral position of an unknown material's absorption lines without using the reference signal.The samples are identified by their absorption peaks extracted from the negative first-order derivative of the sample signal phase divided by the frequency at each pixel.Hu etal [ Hu et al, 2006] report experimental measurement and theoretical analysis of THz spectrum for five different explosives and related compounds are introduced.The refractive index and absorption coefficient of the samples are measured in the region of 0.2-2.6 terahertz by time-domain spectroscopy.The simulated spectrum of γ-HNIW is in agreement with the experimental data.
It is thus evident that there are many significant developments in the area of THz sensors that impact various aspects of biology, medicine and security.

New materials and device structures
A large variety of new types of materials and device structures have been proposed recently for THz applications.These include the use of carbon nanotubes [Costa et al., 2009], GaAs based nanotransistors [Łusakowski, 2007] and polar optical phonons in quantum wells [Liu et al., 2011].Sputter deposited zinc oxide photoconductive antenna have also been proposed for THz detection applications [Iwami et al., 2009].

ZnTe coatings for THz applications
In this section we present a review of the work being carried out by the present authors in the area of THz materials development.Since most of the THz related work on ZnTe is on single crystals, the main objectives of our work is to fabricate ZnTe coatings that are 10-12 microns thick as well as stabilizing the wurtzite form of ZnTe and investigate its optical and electronic properties.The coatings were produced by either thermal or electron beam evaporation in high vacuum (10 -6 Torr).The source material is zinc blende or wurtzite ZnTe.The substrates are borosilicate glass or fused silica and the films were deposited at room temperature.Spectral transmittance curves of the films in the wavelength range from 190 to 2500 nm were measured using a spectrophotometer and from these spectra the refractive index and optical band gaps were extracted.Crystal structure was determined suing a powder x-ray diffractometer and electron diffraction while microstructure and morphology was examined under an Atomic force microscope.The measured spectral transmission curves for zinc blende ZnTe films of thicknesses upto 1200 nm and typical x-ray diffraction pattern of the 1200 nm film is shown in figs.5 and 6 respectively.The transmission of the films is close to 90% in the near IR region and calculated refractive indices were between 2.0 and 2.6.The optical band gaps were between 2 and 2.2 eV.These values compared favourably with earlier reports.Significantly the 1200 nm thick film was nanocrystalline ( with a crystallite size of 24 nm) and showed a preferred (111) orientation.
The thickest films achieved using this technique had a thickness of 10-12 microns The atomic force microscope image of a 2000 nm thick zinc blende ZnTe film is shown in fig.
7. The film is clearly very smooth with roughness less than 10 nm even at this thickness.The grain sizes are of the order of 100 nm.ZnTe also crystallizes in the wurtzite structure wherein the stacking sequence of the cation and anion is ABABABAB. . .with each repeated period perpendicular to the basal plane, whereas in the zinc blende structure the sequence is ABCABCABC.Therefore, the distance between the third nearest-neighbor (NN) atoms is small in wurtzite ZnTe.In contrast, the distance between the first and second NN atoms is invariable in both structures.In addition,  The charge carrier concentration in wurtzite phase (5 x10 25 m -3 ) is lower than the zinc blende structure (4.17 x 10 26 m -3 ) This may make the wurtzite phase suitable for the development of n-type ZnTe, which has been a long standing challenge.Evidently the wurtzite phase has the potential to be employed as an n-type material leading to the formation of ZnTe p-n junctions for THz applications.Further developments in this direction are ongoing Our work thus demonstrates the growth of thick ZnTe coatings in both the zinc blende and wurtzite polymorphs.Their optical properties are substantially different, signifying the possibility of applications in different frequencies regimes of the THz region [Kiran et al, 2010;Kshirsagar et al, 2011].

Conclusions and future prospects
In summary, a number of technologies for THz emitters, detectors and sensors have been reviewed.It is obvious that, while much progress has been made in all three areas, there is scope for new science and technology to emerge in all these areas.Significantly, the progress in the area of THz electronics has been much more rapid than that in the area of THz photonics.This is mainly due to the lack of cost effective so-called "table top" femto second laser sources.THz electronics, on the other hand, relies solely on existing mature technologies for materials and device fabrication.Much of the materials development has focused on single crystals.However, for miniaturization of THz technologies (Photonics and electronics) to succeed, the area of coatings, films and micro-nano devices has to be focused upon, in addition to development of compact THz sources.A report on the development of a high-resolution terahertz (THz) imaging beyond the diffraction limit by using a twodimensional electron gas (2DEG) in a GaAs/AlGaAs heterostructure, points to effort in this direction[.Kawano & Ishibashi, 2010].In the area of materials, strongly correlated electron systems have shown great potential [Ge et al, 2010].In addition, novel device structures to exploit the plasma instability for THz emission and detection is another area that is receiving greater attention.Interestingly, access to fs laser sources has led to better understanding of physical and chemical phenomena in the THz region, that will eventually lead to new materials and device structures.Two examples exemplify this theme.It has recently been shown [Chan et al., 2011] that a nano mechanical oscillator coupled to single mode electromagnetic oscillator in a nano optical cavity can be designed to have oscillations in THz frequency domain.The physics of this domain of energy storage as envisaged by the Debye model has to be examined and the modes of vibrations at phase boundaries, and domain boundaries studied through THz experiments.These will reveal new materials and methods of generation and detection and sensing in the THz range.In another report [Chen et al, 2011], impulsive stimulated Raman scattering and Time-domain THz spectroscopy of coherent optical phonons in bismuth germinate (Bi 4 Ge 3 O 12 ) revealed more than 12 unique vibrational states ranging in frequency from 2 to 11 THz, each with coherent lifetimes ranging from 1 to 20 ps.Such studies on other systems can be expected have a profound impact on the developments in THz sources, emitters, detectors and sensors.

Fig. 2 .
Fig. 2. The typical schematic view of a HEB structure

Fig. 3 .
Fig. 3.The typical schematic view of a high electron mobility transistor structure

Fig. 4 .
Fig. 4. Typical schematic view of a THz imaging set up.
www.intechopen.comTerahertzEmitters, Detectors and Sensors: Current Status and Future Prospects 135 the Zn-Te bond in zinc blende ZnTe has greater ionic character than that in wurtzite ZnTe.Due to these differences it has been shown from ab-initio calculations that the band gaps of the structures should be different.Similarly, it is also expected that the electronic properties will be different.There are, however, very limited studies on the growth and stabilization of wurtzite ZnTe films.The present authors have grown wurtzite ZnTe films by electron beam evaporation of a wurtzite ZnTe source material.Typical x-ray diffraction patterns of the wurtzite films are shown in fig.8for different thicknesses.The measured spectral transmittance for the zinc blende and wurtzite films are shown in fig.9.Detailed dispersion analysis of the films and comparison with zinc blende films has been carried out.ZnTe thin films exhibit either the wurtzite or zinc blende structure depending on the chemical nature of the source material.The formation of the structural phases is confirmed by a combination of x-ray diffraction and selected area electron diffraction.The films were nanocrystalline and randomly textured.The refractive index of the wurtzite phase (3.87 at 2000 nm) is higher than that for the zinc blende phase (3.03 at 2000 nm).The optical band gap, however, is lower for the wurtzite phase (1.1 eV) than the zinc blende phase (2.26 eV).The optical dispersion behavior has been investigated within the framework of the single effective oscillator model.It is shown that the oscillator strength, dispersion energy and optical charge carrier concentrations are all lower for the wurtzite phase than the zinc blende phase.

Fig. 8 .
Fig. 8. XRD patterns of wurtzite ZnTe films of different thickness Komiyama, 2010]2010]demonstrated Si MOSFET structures as THz detectors[Videlier et al].The possibility of utilizing twodimensional plasmons in semiconductor heterostructures for THz detection has been also been proposed[Otsuji et al, 2010].Cox et al[Cox et al., 2011} demonstrated a MEMS based uncooled THz detector.The development of novel single photon detectors that work in the range of 10-50um based on double quantum weel structures have been reported recently {Ueda&Komiyama, 2010].There are many other reports on novel materials and structures, these are however beyond the scope of the current review.
[Turchinovich & Dijkhuis, 2007;photonics depends www.intechopen.comcriticallyontwodevelopmentscompact THz sources and elimination of the dependence on crystals as emitters and detectors.The focus is, therefore, mainly on the development of thick ZnTe coatings for use in THz emitter and detector applications, based on the principle of optical rectification.As stated in section 3.2, optical rectification can be controlled by manipulating the crystal structure and orientation.It is, however, a weak non-linear response.Hence, material thicknesses have to be high to generate a measurable response.Semiconductors from the II-VI group, especially ZnTe crystals[Turchinovich & Dijkhuis, 2007;  ], have drawn considerable interest in recent years for THz applications.ZnTe is intrinsically a p-type semiconductor from the II-VI family with a direct bandgap of 2.26 eV.The growth of ntype ZnTe is still a challenge, which must be overcome before p-n junction devices can be realized.Incorporation of excess Zn during growth may increase donor concentration favoring the formation of n-type ZnTe.The more commonly encountered polymorph of ZnTe is the zinc blende structure which has four asymmetric units in its unit cell as against two in the wurtzite form.The higher degree of asymmetric coordination in zinc blende ZnTe favors formation of non-centrosymmetric structure which is very useful in terahertz generation and detection applications[4].The applications of wurtzite ZnTe, on the other hand, are less well reported.Information on properties like spectral transmission, refractive index, optical band gap, and electronic structure of wurtzite ZnTe thin films is very sparse.