Growth of Organic Nonlinear Optical Crystals from Solution

Investigations on the growth of good quality single crystals play an important role in the development of modern scientific world with advanced technology. Behind the development in every new solid state device and the explosion in solid state device, there stands a single crystal. Crystal growth is an important field of materials science, which involves controlled phase transformation. In the past few decades, there has been a growing interest in crystal growth process, particularly in view of the increasing demand for materials for technological applications (Brice, 1986). Researchers worldwide have always been in the search of new materials and their single crystal growth. Solids exist in two forms namely single crystals, polycrystalline and amorphous materials depending upon the arrangement of constituent molecules, atoms or ions. An ideal crystal is one, in which the surroundings of any atom would be exactly the same as the surroundings of every similar atom. Real crystals are finite and contain defects. However, single crystals are solids in the most uniform condition that can be attained and this is the basis for most of the uses of these crystals. The uniformity of single crystals can allow the transmission without the scattering of electro magnetic waves. The methods of growing crystals are very wide and mainly dictated by the characteristics of the material and its size (Buckley, 1951).


Introduction
Investigations on the growth of good quality single crystals play an important role in the development of modern scientific world with advanced technology.Behind the development in every new solid state device and the explosion in solid state device, there stands a single crystal.Crystal growth is an important field of materials science, which involves controlled phase transformation.In the past few decades, there has been a growing interest in crystal growth process, particularly in view of the increasing demand for materials for technological applications (Brice, 1986).Researchers worldwide have always been in the search of new materials and their single crystal growth.Solids exist in two forms namely single crystals, polycrystalline and amorphous materials depending upon the arrangement of constituent molecules, atoms or ions.An ideal crystal is one, in which the surroundings of any atom would be exactly the same as the surroundings of every similar atom.Real crystals are finite and contain defects.However, single crystals are solids in the most uniform condition that can be attained and this is the basis for most of the uses of these crystals.The uniformity of single crystals can allow the transmission without the scattering of electro magnetic waves.The methods of growing crystals are very wide and mainly dictated by the characteristics of the material and its size (Buckley, 1951).

Nucleation
Comprehensive study on the growth of crystals should start from an understanding of nucleation process.Nucleation is the process of generating within a metastable phase, initial fragments of a new and more stable phase.In a supersaturated or super-cooled system when a few atoms or molecules join together, a change in energy takes place in the process of formation of the cluster.The cluster of such atoms or molecules is termed as "embryo".An embryo may grow or disintegrate and disappear completely.If the embryo grows to a particular size, critical size known as 'critical-nucleus' then greater is the possibility for the nucleus to grow into a crystal.Thus nucleation is an important event in crystal growth.
artificially.The spontaneous formation of crystalline nuclei within the interior of parent phase is called homogeneous nucleation.On the other hand if the nuclei form heterogeneously around ions, impurity molecules or on dust particles or on surface of the container or at structural singularities such as dislocation or imperfection, it is called heterogeneous nucleation.If the nuclei are generated in the vicinity of crystals present in supersaturated system then this phenomenon is often referred to as "secondary" nucleation.Nucleation can often be induced by external influence like agitation, mechanical shock, friction, spark, extreme pressure, electric and magnetic fields, UV -rays, X-rays, gamma rays and so on.

Classical theory of nucleation
The formation of the crystal nuclei is a difficult and a complex process, because the constituent atoms or molecules have to be oriented into a fixed lattice.In practice, a number of atoms or molecules may come together as a result of statistical incidence to form an ordinary cluster of molecules known as embryo.

Kinetic theory of nucleation
The main aim of the nucleation theory is to calculate the rate of nucleation.Rate of nucleation is nothing but the number of critical nuclei formed per unit time per unit volume.In kinetic theory, nucleation is treated as the chain reaction of monomolecular addition to the cluster and ultimately reaching macroscopic dimensions is represented as follows: Two monomers collide with one another to form a dimer.A monomer joins with a dimer to form a trimer.This reaction builds a cluster having i-molecules known as i-mer.As the time increases the size distribution in the embryos changes and larger ones have increase in size.As the size attains a critical size Aj*, the further growth into macroscopic size is guaranteed, as there is a possibility for the reverse reaction i.e., the decay of a cluster into monomers.

Stability of nucleus
An isolated droplet of a fluid is most stable when its surface free energy and therefore its area is a minimum.According to Gibbs (Gibbs & Longmans, 1982), the total free energy of a crystal in equilibrium would be minimum for a given volume if its surrounding is at constant temperature and pressure.If the volume free energy per unit volume is considered to be constant then, Where, a i is the area of i th face and σ i is the corresponding surface energy per unit area.

Energy formation of spherical nucleus
The total free energy change associated with the process of homogenous nucleation shall be considered as follows.Let ΔG be the overall excess free energy of an embryo between the two phases mentioned above.ΔG can be represented as a combination of volume and surface energies since an embryo possesses both these energies.
Where, ΔG s is the surface excess free energy and ΔGv is the volume excess free energy.
Assuming the second phase to be spherical.
Where ΔG v is the free energy change per unit volume is a negative quantity and 'σ 'is the free energy change per unit area.The quantities ΔG, ΔG s and ΔG v are represented in Fig 1.
The surface excess free energy increases with r 2 and the volume excess free energy decreases with r 3 so the total free energy change increases with increase in size of the nucleus and attains a maximum and then decreases for further increase in the size of nucleus.The size corresponding to the nucleus in which the free energy change is maximum is known as the critical size and can be obtained mathematically by maximizing the equation (3).The free energy change associated with the formation of critical nucleus can be estimated by substituting equation (4) in equation ( 3) Where 'S' is the surface area of the critical nucleus.Though the present phase is at constant temperature and pressure, there will be variation in the energies of the molecules.The molecules having higher energies temporarily favour the formation of the nucleus.The rate of nucleation can be given by Arhenius reaction which is a velocity equation since the nucleation process is basically a thermally activated process.The nucleation rate J is given by Where, 'A' is the pre-exponential constant, 'K' is the Boltzman constant and 'T' is the absolute temperature.

Classification of crystal growth
The growth of the single crystal developed over the years to satisfy the needs of modern technology.The free energy of the growing crystal must be lower than initial stage of the system.It is the common condition for all crystal growth process.The crystal growth method is classified into three types namely growth from melt, from vapour, from the solution.The selection method of crystal growth depending upon the physical properties of material -Growth from solid ------> solid-solid phase transformation -Growth from liquid ------> liquid-solid phase transformation -Growth from vapour ------> vapour-solid phase transformation We can consider the conversion of the polycrystalline piece of a material into a single crystal by causing the grain boundaries to sweep through and pushed out of the crystal in the solidsolid growth of crystals.The crystal growth from liquid falls into four categories namely, i. Gel growth, ii.Flux growth, iii.Hydrothermal growth and iv.Low temperature solution growth.Low temperature solution growth is the most widely practiced next to growth from melt.Crystal growth from solution always occurs under condition in which the solvent and crystallizing substance interact.The expression "solution" is most commonly used to describe the liquid which is the result of dissolving a quantity of given substance in a pure liquid known as solvent.Usually water is used as the solvent rarely other liquid is also used as solvent.

Solvent selection
The solution is a homogeneous mixture of a solute in a solvent.Solute is the component present in a smaller quantity.For a given solute, there may be different solvents.Apart from high purity starting materials, solution growth requires a good solvent.The solvent must be chosen taking into account the following factors: 1.A good solubility for the given solution.
2. A positive temperature co-efficient of solubility.

Solution preparation and crystal growth
After selecting the desirable solvent with high purity solute to be crystallized, the next important part is preparation of the saturated solution.To prepare a saturated solution, it is necessary to have an accurate solubility-temperature data of the material.The saturated solution at a given temperature is placed in the constant temperature bath.Whatman filter papers are used for solution filtration.The filtered solution is taken in a growth vessel and the vessel is sealed by polythene paper in which 10-15 holes were made for slow evaporation.This solution was transferred to crystal growth vessels and crystallization is allowed to take place by slow evaporation at room temperature or at a higher temperature in a constant temperature bath.As a result of slow evaporation of solvent, the excess of solute which got deposited in the crystal growth vessel results in the formation of seed crystals.

Low temperature solution growth methods
Solution growth is the most widely used method for the growth of crystals, when the starting materials are unstable at high temperatures.In general, this method involves seeded growth from a saturated solution.The driving force i.e., the supersaturation is achieved either by temperature lowering or by solvent evaporation.This method is widely used to grow bulk crystals, which have high solubility and have variation in solubility with temperature (James & Kell, 1975).Low temperature solution growth (LTSG) can be subdivided into the following categories: i. Slow cooling method ii.Slow evaporation method iii.Temperature gradient method

Slow cooling method
In this process, supersaturated solution is prepared by keeping quantity of the solution same as that of the initial stage and temperature of the solution is reduced in small step.By doing so, solution which is just saturated at initial temperature will become supersaturated solution.Once supersaturation is achieved, growth of single crystal is possible.The main disadvantage of slow cooling method is the need to use a range of temperature.Wide range of temperature may not be desirable because the properties of the grown crystal may vary with temperature.Even though this method has technical difficulty of requiring a programmable temperature control, it is widely used with great success.

Slow evaporation method
In this process the temperature of the solution is not changed, but the solution is allowed to evaporate slowly.Since the solvent evaporates, concentration of solute increased and therefore supersaturation is achieved.For example 40 g of solute in 100 ml solvent is considered as saturated solution at 50 O C. Now the solution is allowed to evaporate at the same temperature.The 100 ml of the solution is reduced to some lower level say 70 ml.Then 40 g in 70 ml at 50 O C is supersaturated solution.The evaporation technique has an advantage that the crystals grow at a fixed temperature.But inadequacies of the temperature control system still have a major effect on the growth rate.This method can effectively be used for materials having very low temperature coefficient of solubility.

Temperature gradient method
This method involves the transport of the materials from hot region containing the source materials to be grown to a cooler region, where the solution is supersaturated and the crystal grows.The advantages of this method are that [a] the crystal is grown at fixed temperature, [b] this method is insensitive to changes in temperature provided both the source and the growing crystal under go the same change.
[c] economy of the solvent.On the other hand, small changes in temperature difference between the source and the crystal zones have a large effect on the growth rate.In general, crystal growth from solution is mainly influenced by super saturation.Super saturation may be achieved by any methods (described above) which are based on the principle that solution which is saturated at a particular temperature will behave as unsaturated at high temperature.The disadvantages are the slow growth rate and in many cases inclusion of the solvent in to the growing crystal.Materials having moderate to high solubility in temperature range, ambient to 100 O C at atmospheric pressure can be grown by LTSG method.This method is well suitable for those materials which suffer from decomposition in the melt and which undergo structural transformation while cooling from the melting point.The other advantages of LTSG method are the low working temperature, easy operation and feasible growth condition.

Nonlinear optical crystals
Non Linear optics deals with the interaction of intense electromagnetic fields in suitable medium producing magnified fields different from the input field in frequency, phase or amplitude Nonlinear optics is now established as an alternative field to electronics for the future photonic technologies.The fast-growing development in optical fiber communication systems has stimulated the search for new highly nonlinear materials capable of fast and efficient processing of optical signals.Organic nonlinear optical (NLO) materials have been intensely investigated due to their potentially high nonlinearities and rapid response in electro-optic effect compared to inorganic NLO materials.In recent years, there has been considerable interest in the study of organic NLO crystals with good nonlinear properties because of their wide applications in the area of laser technology, optical communication, optical information processing and optical data storage technology (Chenthamarai et al., 2000).Among the organic crystals for NLO applications, amino acids display specific features of interest such as (i) molecular chirality, which secures acentric crystallographic structures, (ii) absence of strongly conjugated bonds, leading to wide transparency ranges in the visible and UV spectral regions, (iii) Zwitterionic nature of the molecule, which favours crystal hardness.Further they can be used as a basis for synthesizing organic compounds and derivatives (Eimerl et al., 1990).In our laboratory, we have grown NLO crystals such as L-Alaninium Succinate (LAS), L-Valinium Succinate (LVS), L-Alaninium Fumarate (LAF), L-Valinium Fumarate (LVF) and reported in the journal of repute (Ramachandra Raja, 2009a, 2009b, 2009c, 2010).I n t h i s c h a p t e r , w e h a v e d i s c u s s e d t h e g r o w th of organic nonlinear optical crystal.L-Alaninium Succinate (LAS) and L-Valinium Succinate (LVS) which have been grown by slow evaporation solution growth technique in detail.The characteristic studies such as single crystal and powder X-ray Diffraction (XRD) analysis, UV-Vis-NIR spectrum, FT-IR, nuclear magnetic resonance studies, TGA/DTA studies and SHG are also discussed.

Growth and characterization of L-Alaninium Succinate (LAS)
10.1 Crystal growth LAS have been grown from aqueous solution by slow evaporation.The starting material was synthesized from commercially available L-Alanine (AR grade) and Succinic acid (AR grade), taken in the equimolar ratio 1:1.In deionized water, L-Alanine and Succinic acids were allowed to react by the following reaction to produce LAS.
Calculated amount of the reactants were thoroughly dissolved in deionized water and stirred well for about 3 hours using a magnetic stirrer to obtain a homogenous mixture.
Then the solution was allowed to evaporate slowly until the solvent was completely dried.The purity of the synthesized salt was further increased by successive recrystallization process.The synthesized powder of LAS was dissolved thoroughly in double distilled water to form a saturated solution.The solution was then filtered twice to remove any insoluble impurities.Growth was carried out by low-temperature solution growth technique by slow evaporation in a constant temperature bath controlled to an accuracy of ±0.01 O C. Crystals begin to grow inside the solution and were removed from the solution after 3 weeks, washed and dried in air.

Characterization studies 10.2.1 Single crystal XRD analysis
In order to estimate the crystal data, the single crystal XRD analysis of grown LAS crystal have been carried out using ENRAF NONIUS CAD-4 X-ray diffractometer equipped with MoK ( = 0.71069 Å) radiation.The X-ray diffraction study on grown crystal reveals that the grown crystal belongs to orthorhombic system with the following unit cell parameters: a = 5.77 Å, b = 6.02Å, c = 12.32 Å and = = = 90 O , the cell volume = 428 Å 3 .These lattice parameters are tabulated in the Table 1.

Powder XRD analysis
The structural property of the single crystals of LAS has been studied by

UV-Vis-NIR analysis
The UV-Vis-NIR transmittance spectrum of grown LAS crystal has been recorded with a Lambda 35 double-beam spectrophotometer in the range 190-1100 nm to find the suitability of LAS crystal for optical applications.The recorded spectrum is shown in Fig. 3.The crystal shows a good transmittance in the visible region which enables it to be a good material for optoelectronic applications.As observed in the spectrum, there is no significant absorption in the entire range tested.A good optical transmittance from ultraviolet to infrared region is very useful for nonlinear optical applications.Most of the nonlinear optical effects are studied using Nd:YAG laser operating at a fundamental wavelength of 1064 nm.Absorption, if any, near the fundamental or the second harmonic at 532 nm, will lead to a loss of conversion efficiency of second harmonic generation (SHG).From the UV-Vis-NIR spectrum, it is clear that the transparency of the grown crystals extends up to UV region.The lower cut-off wavelength is as low at 190 nm.The wide range of transparency suggests that the crystal is a good candidate for nonlinear optical applications (Aravindan et al., 2007).This transmittance window (190-1100 nm) is sufficient for the generation of second harmonic light ( = 532 nm) from the Nd:YAG laser ( =1064nm) (Natarajan et al, 2008).The lower cut-off near 190 nm combined with the very good transparency, makes the usefulness of this material for optoelectronic and nonlinear optical applications.

FT-IR analysis
The infrared spectrum of LAS has been carried out to analyse the chemical bonding and molecular structure of the compound.The FT-IR spectrum of the crystal has recorded in the frequency region from 400 cm −1 to 4000 cm −1 with Perkin-Elmer FT-IR spectrometer model SPECTRUMRX1 using KBr pellets containing LAS powder obtained from the grown single crystals.The observed FT-IR spectrum of LAS is as shown in Fig. 4. The characteristics vibration of LAS has been compared with L-alaninium alanine nitrate (Aravindan et al., 2007) and L-alanine cadmium chloride (Dhanuskodi et al., 2007) as shown in Table 3.The asymmetric stretching vibration of NH 3 + is observed at 3086 cm −1 of LAS is confirming the presence of NH 3 + in compound.The NH 3 + absorption range of amino acids (3130-3100 cm −1 ) is shifted to lower wave number, due to formation of amino salts, and in LAS, it is observed at 3086cm −1 .Amino group absorption bands are noted at 2604 cm −1 (symmetric stretching), 1620cm −1 (bending), and 1111 cm −1 (rocking).These bands are due to NH 3 + ions.During the formation of amino salts, the NH 2 group in amino acids is converted in to NH 3 + ion.The strong absorption at 1413 cm −1 indicates the symmetric stretching vibration frequency of carbonyl group.The bending and rocking vibrations of COO− are observed at 772 cm −1 and 539 cm −1 , respectively.CH 2 wagging (1304cm −1 ) and CH 3 stretching (1204 cm −1 ) vibrations are also observed (Ramachandran & Natarajan, 2007).

NMR studies
The 1 H-and 13 C-NMR spectra of LAS have been recorded using D 2 O as solvent on a Bruker 300MHz (Ultrashield) TM instrument at 23 O C (300 MHz for 1 H-NMR and 75 MHz for 13 C-NMR) to confirm the molecular structure.The spectra are shown in Figures 5 and 6 respectively and the chemical shifts are tabulated with the assignments in Table 4.The resonance peaks at = 1.33 ppm of 1 H-NMR spectrum is due to the CH 3 group and peaks observed at = 3.65 ppm is due to the CH group of L-Alanine.The methyl proton signal at = 1.33 ppm is split into a proton doublet due to the coupling of the neighboring proton (CH) and the signal at = 3.65 ppm is split into a proton quartet due to the coupling of three neighboring protons (CH 3 ).The resonance peak observed as a singlet at = 2.57 ppm exhibits the presence of methylene (CH 2 ) proton of succinic acid.The signal at = 4.69 ppm is due to the solvent (D 2 O).The signals due to NH and COOH do not show up because of fast deuterium exchange reactions takes place in these two groups, with D 2 O being used as solvent (Bruice, 2002).Because of the presence of the methylene (CH 2 ) groups of LAS, electron contributions towards the rest of the compound get enhanced, so that the protons are more protected in LAS.Such property is not noticed in L-alaninium oxalate (LAO), due to the absence of methylene groups so that the proton groups in LAS absorbs signals at the values lesser than the value of LAO (Dhanuskodi & Vasantha, 2004).The 13 C NMR spectrum of LAS contains five signals.The resonance peaks observed at = 16.00 ppm and at = 50.33ppm are due to the carbon environments of CH 3 and CH groups of L-alanine respectively.The signal at = 29.06ppm is due to the presence of two methylene (CH 2 ) groups of succinic acid.The resonance signal observed at = 175.52ppm is due to the free carboxylic acid from L -alanine.In solution, the two carboxyl groups of succinic acid are equivalent due to the fast exchange of H + between them and give rise to a single signal at = 177.41ppm.Fig. 6. 13 C-NMR spectrum of LAS crystal.

Spectra
Chemical Shift (ppm) Group identification 1 H NMR

Second harmonic generation analysis
A preliminary study of the powder SHG measurement of LAS has been performed using Kurtz powder technique (Kurtz & Perry, 1968) with 1064nm laser radiations.An Nd:YAG laser producing pulses with a width of 8 ns and a repetition rate of 10 Hz was used.The crystal was crushed into powder and densely packed in a capillary tube.It is observed that the crystal converts the 1064 nm radiation into green (532 nm) while passing the Nd:YAG laser output into the sample which confirms the SHG.The observed intensity of output light is obtained as 12 mV and for the same incident radiation, the output of KDP is observed as 52 mV.It was found that the efficiency of SHG is 23% when compared with that of the standard KDP (Ramachandra Raja , 2009c).

Growth and characterization of L-Valinium Succinate (LVS)
11.1 Experimental procedure The nonlinear optical crystal L-Valinium Succinate (LVS) were grown by slow evaporation solution growth method.The LVS was synthesized from analar grade L-Valine and Succinic acid which were taken in equimolar ratio 1:1 using following reaction: The calculated amounts of reactants were thoroughly dissolved in double distilled water and stirred continuously using magnetic stirrer.The saturated solution may contain impurities such as solid and dust particles and therefore it was filtered using filter paper.
Then the filtered solution was covered by polythene paper in which 10 to 15 holes were made for slow evaporation.This solution was transferred to crystal growth vessels and crystallization was allowed to take place by slow evaporation at a temperature range of

Powder XRD analysis
The powder X-ray diffraction (XRD) pattern of LVS crystals has been obtained using Rich Seifert X-ray diffractometer.The crushed powder sample was subjected to intense X-rays of wavelength 1.54060 Å (CuK ) at a scan speed of 1 O /minute.The powder X-ray pattern of LVS is shown in Fig. 8.The observed powder XRD pattern has been indexed by Rietveld Index software package.The lattice parameters have been calculated by Rietveld Unit Cell

UV-Vis-NIR analysis
To find the optical transmission range of LVS crystals, the UV-Vis-NIR spectrum has been recorded using Lambda 35 double beam spectrophotometer in the range between 190 nm and 1100 nm and it is shown in Fig. 9.When the transmittance is monitored from longer to shorter wavelengths, LVS is transparent from 190 nm to 1100 nm.Optical absorption with lower cut-off wavelength near 190 nm makes the crystal suitable for UV tunable laser and SHG device applications.

FT-IR analysis
The Fourier transform infrared spectrum of LVS have been recorded in between the region 400 -4000 cm -1 using Perkin Elmer Fourier transforms infrared spectrometer (model SPECTRUM RX1) with the help of KBr pellets as shown in Fig. 10.The presence of functional groups was identified and they are stacked in Table 7.The presence of NH 3 + group in LVS has confirmed by peaks at 3429 cm -1 and 3156 cm -1 .It is due to protonation of NH 2 group by the COOH group of succinic acids (Nakamo, 1978;Sajan et al., 2004).The symmetric and asymmetric bending of NH 3 + was obtained at 1587 and 1508 cm -1 respectively.The strong absorption at 1393 cm -1 indicates that the symmetric bending of CH 2 .The CH 2 wagging vibration produces a sharp peak at 1327 cm -1 .The C-CH bending vibration produced its characteristic peak at 1270 cm -1 .The rocking vibration at 1177 cm -1 establishes the presence NH 3 + group.The peak at around 1137 cm -1 is assigned to NH 3 + wagging.The stretching vibration of C-O-C, C-C-N and C-C are positioned at 2108 cm -1 , 1063 cm -1 and 1029 cm -1 respectively.Meanwhile, for the peaks at 945 cm -1 is due to CH 2 rocking.The bending vibration of COO -is observed at 662 cm -1 .The bending and rocking vibration of COO -are observed at 714 cm -1 and 430 cm -1 respectively.Fig. 10.FT-IR spectrum of LVS crystal.

NMR studies
The  7. Assignments of FT-IR bands observed for LVS crystal.
The 13 C-NMR spectrum is shown in Fig. 12.The characteristic absorption peaks of 13 C-NMR spectrum of LVS are explained as follows.The signals at  = 17.82 ppm and  = 16.55 ppm are attributed to the two methyl group of LVS.An intense signal is observed at  = 28.93 ppm is due to presence of two methylene groups of succinic acid.The signal of (CH) at  = 29.00ppm is integrated for one carbon due to presence of carboxylic acid isopropyl carbon.The peaks at  = 60.12 ppm is due to tertiary carbon connected to amino group.The peak at  = 173.97ppm and  = 177.28ppm are due to deuterium exchange of carbon in carbonyl group.A peak with higher intensity at  = 177.28ppm can be safely attributed to carbonyl carbons of two COOH groups of succinic acid present in the same chemical environment.
The Thermo Gravimetric Analysis (TGA), Differential Thermal Analysis (DTA) spectra of grown LAS crystal have been obtained using the instrument NETSZCH SDT Q 600 V8.3 Build 101.The TGA and DTA have been carried out in nitrogen atmosphere at a heating rate of 20 O C/min from 0 O C to 1000 O C. The TGA curve is presented in Fig.7.The initial mass of the materials to analysis was 2.5720 mg and the final mass left out after the experiment was only 1.729 % of initial mass.The TGA trace shows that the material exhibit very small weight loss of about 1.17 % in the temperature up to 155 O C due to loss of water.TGA curve shows that there is the weight loss (85%) between 178 O C and 274 O C indicating that the decomposition of LAS crystals.From the Fig.7, the appearance of endothermic in the DTA at 178 O C corresponds to TGA results.From the TGA, DTA analyses, it is clearly understood that the LAS is thermally stable upto 178 O C.
35 O C in a constant temperature bath of accuracy ±0.01 O C. As a result of slow evaporation of water, the excess of solute has grown as LVS crystals in the period of two weeks.crystal XRD analysis The X-Ray diffraction pattern of LVS crystals have been studied by ENRAF NONIUS CAD4 single crystal X-Ray diffractometer with MoK radiation ( =0.71069 Å).The single crystal Xray diffraction study of crystals is used to identify the cell parameters.It is observed that the LVS crystal belongs to orthorhombic system with following cell parameters: a = 9.85 Å, b = 5.35 Å, c = 12.26 Å and = = = 90 O , the cell volume = 646 Å 3 .From the lattice parameters it is clear that for grown crystal a ≠ b ≠ c and = = = 90 O and they are compared with powder XRD data and tabulated in 1 H-and 13 C-NMR spectra of LVS have been recorded for the crystals dissolved in water (D 2 O) using BRUKER 300 MHz (Ultrashield) TM instrument at 23 O C (300 MHz for 1 H-NMR and 75 MHz for 13 C-NMR) for the confirmation of molecular structure.The 1 H -NMR spectrum of LVS is shown in the Fig.11.The deuterium exchange proton NMR spectrum of LVS crystal is found to contain resonance signals integrated for a total of 12 protons.From the spectrum, it is observed that the two methyl proton signal is split into two doublets due to the coupling of neighbouring (-CH) proton which is confirmed from the signal at  = 0.84 ppm,  = 0.89 ppm respectively.The -CH group signal is split into a multiplet due to the hyperfine splitting of neighbouring three (-CH 3 ) protons is confirmed from the signal of LVS crystal centered at =  2.13 ppm.The doublet signal observed at  3.48 ppm is attributed to a (-CH) proton next to carboxylic acid.There is one peak found at  = 2.51 ppm due to the -CH 2 -group of succinic acid.The signal at  = 4.69 ppm is due to the solvent D 2 O.The signals due to N-H and COOH do not show up because of fast deuterium exchanges which took place in those two groups, where the D 2 O was used as the solvent(Bruice 2002).The chemical shift values of LVS with assignments are tabulated in Table8.

Table 1 .
The cell parameters of LAS crystal.
X-ray powder diffraction technique.Powder X-ray diffraction studies of LAS crystal is carried out, using Rich Seifert diffractometer with CuK ( =1.54060 Ǻ) radiation.The sample is scanned for 2θ values from 10  to 90 O at a rate of 2 O /min.Figure2shows the Powder XRD pattern of the pure LAS crystal.The diffraction pattern of LAS crystal has been indexed by Reitveld index software package.The lattice parameter values of LAS crystal has been calculated by Reitveld unit cell software package and are matched with single crystal XRD data.The comparison of lattice parameters between single crystal and powder XRD is shown in Table1.Fig. 2. Powder XRD pattern of LAS crystal.www.intechopen.com

Table 3 .
Assignments of FT-IR bands observed for LAS crystal.

Table 4 .
The chemical shifts in 1 H-NMR and 13 C-NMR spectra of LAS.
www.intechopen.comModern Aspects of Bulk Crystal and Thin Film Preparation

Table 5 .
The cell parameters of LVS crystal.

Table 8 .
The chemical shifts in 1 H-NMR and 13 C-NMR spectra of LVS. www.intechopen.com