Open access peer-reviewed chapter

Recent Advances in Environment-Friendly Alkyd Nanocomposites Towards “Greener” Coatings

Written By

Eram Sharmin, Fahmina Zafar, Nahid Nishat and Sharif Ahmad

Submitted: October 17th, 2015 Reviewed: February 10th, 2016 Published: June 1st, 2016

DOI: 10.5772/62448

Chapter metrics overview

3,837 Chapter Downloads

View Full Metrics


Alkyd nanocomposites have attracted great attention in the field of heavy duty coating materials. This is due to the synergistic action of both alkyds (flexibility, biodegradability, compatibility, good gloss retention, durability, weathering resistance) and nanofillers (large surface area to volume ratio). Alkyd nanocomposites show good physico-mechanical, physico-chemical, anticorrosive, and antimicrobial performances and thermal stability, with application as anticorrosive, anti-fog, self-cleaning, self-healing, and antimicrobial coatings. In view of present drives and legislations towards environment-friendly coatings, alkyds have undergone modifications as waterborne, high solids, hyperbranched “greener” nanocomposites. The present chapter deals with a brief overview of alkyds, recent advances in environment-friendly alkyd nanocomposite coatings, and the effects of nanofillers on the performance (physico-mechanical, chemical/corrosion resistance, thermal stability, and others) of “greener” alkyd nanocomposite coatings.


  • alkyds
  • nanocomposites
  • coatings
  • physico-mechanical
  • chemical resistance
  • thermal stability

1. Introduction

Alkyd resins are the most versatile vegetable seed oil (VSO)-based polymeric binders find applications paints and coatings industry. They are polyester-based materials modified with oil or oil derived fatty acids. Alkyd resins owe their wide applications to their versatility and capability to engineer a wide variety of acceptable properties in terms of usage by the Coatings industry. Alkyds now account for approximately half of all the resins consumed in the field of protective coatings [16]. Chemically, alkyd resins have been defined as reaction product of condensation polymerization of polyhydric alcohol, polybasic acid, and monobasic fatty acid (saturated or unsaturated; Figure 1). They are best classified according to the amount of fatty acid and phthalic anhydride present (Table 1) [1].

Short alkydMedium alkydLong alkydVery long alkyd
Fatty acid content30–4243–5455–68>68
Phthallic anhydride3730–3720–30<20

Table 1

Alkyd classification.

Figure 1.

Alkyd synthesis, where R=fatty acid chain (saturated or unsaturated). Where PA:Phthalic anhydride, Gly:Glycerol and TMPTMA: Trimethylolpropane Trimethacrylate.

The reaction of alkyd (Figure 1) is based on three basic fundamental building blocks:

  1. VSO or corresponding fatty acids (in percentage): linseed (linolenic/linoleic 40/35), soybean (linoleic/oleic 55/28), tall (fatty acid/rosin 50/40), castor (ricinoleic/linoleic 90/4), dehydrated castor (conjugated fatty acid/ricinoleic 80/10), safflower (linoleic/oleic 59/37), tung (elaeostearic/oleic 79/11), coconut (saturated/monounsaturated fatty acid 91/6), as well as other nontraditional seeds oils;

  2. Polyhydric alcohols (polyols): glycerol, pentaerythritol, sorbitol, ethylene glycol, neopentyl glycol, trimethylol propane, and others; and

  3. Polybasic acids (or corresponding anhydride): phthalic, isophthalic, adipic, maleic, fumaric acids, and trimellitic anhydride [1].

Alkyd resins have good color retention, durability in exterior finishes, good weathering resistance, and moderate resistance to corrosive fumes but show poor resistance to chemical splash and spillage, especially in alkaline medium. The thermal stability of these resins goes up to 105°C [3]. The properties of alkyd coatings are derived mainly from the properties of drying oils used in the manufacture of the resins. The extent and kind of unsaturation in drying oil fatty acids have a profound effect on the properties of finished alkyd. The drying time, hardness, color, and moisture resistivity of the resin depends on the degree of unsaturation of the oil used [1,4]. These unsaturation sites are responsible for the curing of alkyd resins through auto-oxidation process (Figure 2). The process creates the active free radicals leading to the formation of a three-dimensional cross-linked network. [1,7].

Figure 2.

Autoxidation of alkyd.

The standard alkyds are usually soybean and linseed oil alkyds, which show moderate and faster drying rates, respectively. The former has good color retention, whereas the latter reduces the color retention requirement. Dehydrated castor and soybean oil-based alkyds are used for baked finishes. These alkyds in combination with urea formaldehyde and melamine formaldehyde resin exhibit shorter baking time and produce harder film. For light color and maximum color retention, nondrying oils, such as coconut, castor, and cottonseeds, may be used. The alkyd of this type does not dry because of the nonoxidizing character of the parent VSO. They must be blended with some cross-linkers and baked with amine resin, such as urea or melamine formaldehyde, at high temperature (Figure 3).

Figure 3.

Curing reactions of alkyd resins with amino resins.

Nondrying VSO-based alkyds are also used as resinous plasticizers and other lacquer-type polymers. Tung and oiticica in combination with other VSO-based alkyds show faster drying and achieve earlier hardness. Safflower oil-based alkyd has excellent drying properties and color retention [1,8]. Besides these, some nontraditional VSO-based alkyds, such as nahar (Mesua ferreaLinn), kamala (Mallotus phillipinensis), mahua (Madhuca longifolia), barbados nut (Jatropha curcas), burra gokharu (Tribulus terrestris), undi (Calophylum inophyllum), karanja (Pongamia glabra), karinotta (Samera indica), nigerseed (Guizotia abyssinica), babul (Acacia arabica), and neem (Azardirachta indica), have been reported and used as coating materials [4,911]. Tobacco seed oil has been reportedly used in alkyd preparation for wrinkled finish paints [10]. The use of pentaerythritol as a polyhydric alcohol produces faster drying, greater hardness, better gloss, and better water resistance than alkyds based on glycerol of equal fatty acid content [12].

Modifications of alkyd resins are continuously carried out to achieve improved mechanical and chemical resistance properties and these systems find a wide scope of application as corrosion protective coatings. The modification with acrylic monomer, such as styrene, methyl methacrylate, vinyl toluene, and others, has been extensively done by researchers through unsaturation to improve the performance of resins up to the desired level [13]. Butylmethacrylate-co-maleic anhydride copolymer modified linseed and rubber seed oil alkyds through functional groups are used as co-curing resins with melamine formaldehyde resin to prepare baking-type coating compositions, whereas Albizia benthmedium oil-based alkyd gives room temperature cured resin, with superior film properties [3,14,15]. The modification of alkyd with chlorinated rubber resulted in improved adhesion as well as improved acid, alkali, and water resistance. The chlorination of soybean and A. benthoil-based alkyd transforms into an air-drying, nonconvertible film former with improved mechanical properties [3,16,17]. Chain-stop alkyds from solvent fractionated Argemoneand rubber seed oil are used for specialty alkyd [18]. Heated rubber seed oil-based films show excellent resistance to acid and salt solution. Its combination with cashew nut shell liquid formaldehyde resin has improved the drying ability and chemical resistance [19]. The phenol-modified alkyd resin improves gloss retention as well as water and alkali resistance. Waterborne-baked and air-drying alkyds have also been developed from different VSO having properties similar to their solvent-borne counterparts and found application in paint and coatings [20,21]. In addition, alkyd resins can be modified with epoxies and polyurethanes or other thermoplastic resins to give coatings of improved performance. For example, urethane oils are prepared by reacting diglycerides with toluene diisocynate. The resulting oils are used in alkyd resin preparation or as additive for coatings. Besides these, other alkyds are also prepared, such as imide-modified alkyd, amide-modified alkyd, tetrachlorophthalic anhydride-based alkyd resin with fire-retardant properties, ketene and acetic anhydride modification with terminal hydroxyl groups of alkyd, zinc chromate containing alkyd resin, triphenyl phosphite containing alkyd resin with improved color and drying properties, oil-less alkyds, ultraviolet (UV) light hardenable pigmented alkyd resin laquer preparation, and maleic anhydride-cyclopentadiene adduct in alkyd preparations [2224].

In recent years, due to concerns related to energy consumption and environmental contamination, regulations, and legislations directing us towards “sustainable development” and innovations, efforts are being focused towards the development of (i) “greener” environmentally benign materials (ii) with improved performance characteristics to meet the present-day demands. Environment-friendly technologies such as high solids, hyperbranched, waterborne, and UV curable, are being used to eliminate the use and/or generation of hazardous chemicals and emissions harmful to environment. For improvement in performance, the inclusion of nanosized fillers as nanoreinforcements is being accomplished. In this context, the world of alkyds has also witnessed greater modifications such as switching to high solids, hyperbranched, waterborne and UV curable alkyds (Figure 1)[22,23,2529]. In our recent review articles, we have described alkyds and their modifications in terms of both in property enhancements and environment-friendly approaches, occurring in the last decade [22,23]. This manuscript provides a brief overview of environment-friendly recent advances that have taken place in the field of alkyds and also focuses on the properties and performance characteristics of high solids, hyperbranched, and waterborne alkyd nanocomposites along with the unexplored areas in the field and possible future research directions.


2. Environment-friendly recent advances in alkyds towards “greener” coatings

Considering the future predictions, energy concerns, associated hazards, and legislations, research progresses in the quest for improved and updated performance characteristics in every field. Alkyds have undergone several modifications recently in consideration of the aforementioned, such as the use of reactive diluents, resorting to solvent free approaches, and others. In alkyd-based coatings, towards the step to eliminate the use of organic solvents, which are often added to achieve the desired viscosity for application over the substrate, tung oil (TO)-based reactive diluents were added to soy alkyd formulations. TO-reactive diluents were modified with alkyoxylsilane, tetraallyl ether, and fluororinated side chain. These diluents participated in the film formation process and significantly reduced the viscosity of alkyds, thereby serving as effective diluents. Alkoxysilane-modified diluents showed somewhat enhanced performance due to in situpolycondensation of silicon alkoxide within the organic polymer matrix, which provided an additional functionality for cross-linking [30]. To reduce the content of solvents and to achieve desirable viscosity, carboxymethyl cellulose nitrate ester/coconut alkyd blends were prepared, which resulted in hydrophilic transparent films [31,32].

In a recent “greener” approach, Jatrophaoil (JO)-based alkyd was blended with citric acid cured JO-derived epoxy. The final product showed enhanced tensile strength, elongation at break, hardness, increment in gloss due to uniform and smooth surface morphology, good scratch hardness and adhesion conferred by highly cross-linked networks, flexibility of oil chains, and the presence of polar functionalities in the backbone, which also contributed to excellent resistance to solvents (water and ethanol), salt solution, and good acid and alkali resistance [33]. An interesting research includes the synthesis of alkyds from postconsumer polyethylene terephthalate (PET) bottles. Herein, waste PET was glycolyzed using glycerol, trimethylolethane, trimethylolpropane, and pentaerythritol, giving tetra- and hexafunctional glycolyzates. PET glycolyzates were then used as hydroxyl components in the synthesis of alkyd resins. The approach has multiple advantages: (i) value addition to a waste material (i.e., PET), (ii) reduction in the amount of waste PET in dumps and landfills, (iii) reduction in amount of phthalic anhydride, and (iv) improved performance of alkyd. The best performance was achieved by the inclusion of trimethylolethane and trimethylolpropane, as they had four sterically unhindered primary hydroxyl groups that produced alkyds with higher degree of branching, consequently higher molar mass, which led to improved mechanical, drying, and chemical resistance properties [34].

Laccases are enzymes first discovered in Japanese lacquer tree Rhus verniciferaby Yoshida in 1883, which are found in fungi, different bacteria, and plants. In an effort to completely replace the toxic heavy metals by nontoxic and environment-friendly catalysts, laccase-mediator systems have been considered as potential cross-linking and functionalizing agents for alkyds [35]. In the synthesis of alkyds, heterogeneous base catalysts are used such as hydroxides of calcium, potassium, sodium, lithium, oxides of calcium, zinc, and others. Recently, CuO nanocatalyst was introduced, which had dual effects: (i) it catalyzed the alcoholysis-polyesterification reaction, reducing the reaction time, and (ii) it conferred antimicrobial properties to the resin [36]. Thus, the addition of nanofillers leads to enhancement in several properties, often drastically, such as aesthetic appeal, UV resistance, corrosion resistance, scratch resistance, impact resistance, thermal stability, and others, thus reinforcing the matrix, without losing transparency and other properties. The enhancement in properties is a consequence of the much greater surface-to-volume ratio of the nanofiller. The incorporation of nanoparticles in the polymer matrix offers significant barrier properties for corrosion protection. It reduces blistering or delamination and also enhances the integrity and durability of coatings (the fine particles uniformly dispersed in coatings can fill cavities and can cause crack bridging, crack deflection, and crack bowing) [37,38]. After having a brief idea of the recent advances in the field towards environment-friendly “greener” coatings, in the proceeding sections, we will discuss about some of the recent developments in alkyd-based environment-friendly (waterborne, high solids, hyperbranched) nanocomposite coatings.


3. Waterborne alkyd nanocomposite coatings

In these types of coatings, the alkyd matrix selected is waterborne and is further modified with nanoreinforcements depending on the property that needs improvement (Figure 4). Thus, the choice of nanofillers for modification depends on the property that is needed to be augmented or enhanced. The inclusion of nanoalumina improved the scratch, corrosion, UV, and abrasion resistance of coatings. The increased content of nanoalumina reduced the pinhole formation tendency and defended the coatings against humidity [37]. The corrosion protection Occurred by (a) nanoparticles occupying the vacant spaces in the coating matrix, (b) reducing porosity, (c) bridging and interconnecting the constituents of matrix, (d) increasing cross-linking, (e) providing longer diffusion paths to corrosive ions, and (f) improving barrier performance [39]. A similar enhancement in the performance of coatings was also observed when waterborne alkyd coatings were modified with nano-Fe2O3 by the described corrosion protection mechanism. Even at the lower loading of nano-Fe2O3 (0.05%, 0.1%, and 0.2%), the corrosion process was delayed, whereas, at 0.3% loading of nano-Fe2O3, adequate coating performance was achieved [40,41]. Nano-silica modification improved scratch resistance, abrasion resistance, adhesion properties, impact resistance, glass transition temperature, and thermal stability [42,43]. The introduction of ZnO nanoparticles improved film compactness and abrasion resistance and had a catalytic influence on curing reaction, thus facilitating the formation of hard and complex network. The stronger interactions between nanoparticles and alkyd matrix also conferred enhancement in mechanical properties. As nano-ZnO has UV blocking properties, the incorporation of nano-ZnO also improves the UV resistance of coatings [4446].

Figure 4

Waterborne alkyd nanocomposites.

Poly(methylmethacrylate-butylacrylate)/nanocalcium carbonate, prepared by emulsion polymerization, was blended with alkyd coating with 50 wt% water as solvent, in various ratios, with dual objectives: (i) using polymer nanocomposite as partial binder and (ii) As a filler to improve the properties. The coatings showed good gloss, mechanical and thermal properties; however, impact resistance was found to be lower. The highly crystalline calcium carbonate nanoparticles deteriorate the impact strength at locations in coatings where the aggregation of particles occurs, thus generating stress at these specific sites [47].


4. Hyperbranched alkyd nanocomposite coatings

The use of dendritic or hyperbranched polymers as binders in coatings is considered as one of the effective ways to reduce volatile organic compounds (VOCs; Figure 5).

Figure 5

Hyperbranched alkyd, where I=dimethylolpropionic acid, II–IV=hyperbranched polyesters (HBPs), andV– VII=their respective hyperbranched alkyds; a–c are dipentaerythritol, pentaerythritol, and 1,3,5-tris(2-hydroxyethyl)cyanuric acid, respectively; and R=fatty acid chain (unsaturated or saturated).

These polymers have three-dimensional compact structures. They show low viscosity even at higher molecular weight. Thus, the development of hyperbranched nanocomposites has double advantages: (i) overcomes the use of VOCs and (ii) leads to property enhancement.

Figure 6

Hyperbranched alkyd/silicone or silver nanocomposites.

In a recent research, nanosilver was embedded in hyperbranched urethane alkyd by an in situapproach that prevented agglomeration of nanoparticles (Figure 6). The nanocomposites showed good antibacterial activity against Serratia marcescens, as studied by using agar overlay and disk diffusion methods, and the coatings were gloss retentive and nonleaching. The resin required much lesser solvent for coating formulation and showed improved mechanical properties [48].

An interesting research work was performed on carbon nanofiller modification of hyperbranched alkyd. Here, three geometrically different carbon nanofillers, carbon black (CAB), multiwall carbon nanotubes (MWCNT), and graphene (GR), were treated with a surfactant Nonidet P-40 (Figure 7). This led to the uniform dispersion of carbon fillers as facilitated by the interactions of π-electron clouds of carbon nanofillers with the delocalized π-electrons of the surfactant and H-bonding interactions between surfactant and hyperbranched alkyd backbone. The former interactions reduce the van der Waals forces present between carbon nanofillers, and the latter interactions improve the interfacial adhesion between the matrix and nanofillers. Due to their stronger interactions with the alkyd backbone and the high aspect ratio and surface area, MWCNT and GR showed better dispersion in the matrix relative to CAB. Thus, modifications with MWCNT and GR provided relatively higher scratch resistance, adhesion, and tensile strength to alkyd coating as well as higher thermal stability. The water vapor transmission rate was found to be lower in nanocomposite alkyd, and least in GR alkyd (due to its plate-like structure), compared to the unmodified alkyd, as the nanofillers provided tortuous path to water and oxygen molecules hindering them to reach the substrate of the coating easily. However, compared to others, GR-alkyd showed the highest corrosion resistance performance due to good dispersion and adhesion of GR; moreover, its plate-like structure also proved advantageous in enhancing the corrosion resistance [49]. The modification with silicones reduces the drying times and improves the adhesion to the substrate, hardness, and gloss of coating (Figure 6) [50].

Figure 7

Hyperbranched alkyd urethane/GR or MWCNT nanocomposites.


5. Future suggestions and conclusion

Environment-friendly alkyd nanocomposites are an emerging field of research. They comprise a vast field for commercial coating applications. They find promising applications as corrosion-protective, antimicrobial, eco-friendly coatings. However, more efforts are required in the field to be established further as “greener” coatings in terms of performance, cost, and environment-friendly applications. A lot of modifications have been accomplished and much remains unexplored.

The synthesis of alkyds requires higher temperatures and longer reaction times. In view of this, alkyd synthesis can be performed via microwave-assisted methods that reduce reaction times and often temperatures. Another alternative is the synthesis by enzymatic approach. Hydroxylated oils (or polyols) can be used to prepare monoglycerides, which would introduce extra hydroxyl functionality in alkyd backbone increasing the adhesion of coatings produced due to polar hydroxyls. The alkyd with extra hydroxyls in its backbone will serve as alkyd polyol. Considering the present drives towards environment-friendly coatings, efforts should be laid on the development of low solvent or solvent-free alkyd nanocomposite coatings to reduce the use of harmful solvents during the synthesis, processing, formulation, and application of coatings. More emphasis should be laid on the development of waterborne, high solids, hyperbranched, and UV curable alkyd nanocomposites using different nanofillers. A completely water-soluble alkyd nanocomposite would be a significant achievement in the field. Greener isocyanates may be used as curing agents for alkyd polyurethane nanocomposites. The introduction of nanoparticles by in situapproach may reduce reaction steps and also the problems associated with the agglomeration of nanoparticles. Blending with cost-effective reinforcing components will also effectively reduce cost and improve performance characteristics. The greater utilization of nonedible and nonmedicinal oils in the preparation of alkyds must be encouraged to add value to underutilized oil as a bioresource. Efforts may also be focused on studying the biodegradation behavior of these materials to determine their eco-friendly disposal.



Dr. Fahmina Zafar is thankful to the University Grants Commission, India, for the Dr. D.S. Kothari postdoctoral fellowship, Ref. #F.4/2006(BSR)/13-986/2013(BSR), with Prof. Nahid Nishat.


  1. 1. Lanson H. Chemistry and technology of alkyd and saturated reactive polyester resins. ACS Symposium Series. Oxford University Press; 1985. pp. 1181–1204.
  2. 2. El-Hai FA, Sabbah I, Naser A, Abdel-Rehim N. High performance alkyd resin compositions for coating. Int J Polym Mater 2004;53:871–878.
  3. 3. Akintayo C, Adebowale K. Synthesis and characterization of acrylatedAlbizia benthmedium oil alkyds. Prog Org Coat 2004;50:207–212.
  4. 4. Tiwari S, Saxena M, Tiwari S. Preparation and characterization of penta alkyds based on mahua oil. J Sci Ind Res 2002;61:110–116.
  5. 5. Chandra S, Pasari S. Synthesis of styrenated alkyds. J Sci Ind Res 1982;41:248–257.
  6. 6. Igwe IO, Ogbobe O. Studies on the alcoholysis of some seed oils. J Appl Polym Sci 2000;78:1826–1832.
  7. 7. van Gorkum R, Bouwman E, Reedijk J. Fast autoxidation of ethyl linoleate catalyzed by [Mn(acac)3] and bipyridine: a possible drying catalyst for alkyd paints. Inorg Chem 2004;43:2456–2458.
  8. 8. Thurmond C, Hempel A, Marling P. Safflower oil in alkyd resins and treated oils. J Am Oil Chem Soc 1951;28:354–356.
  9. 9. Dutta N, Karak N, Dolui S. Synthesis and characterization of polyester resins based on Nahar seed oil. Prog Org Coat 2004;49:146–152.
  10. 10. Tiwari S, Saxena M, Tiwari SK. Mahua-oil-based resins for the high-temperature curing of fly ash coatings. J Appl Polym Sci 2003;87:110–120.
  11. 11. Boruah M, Gogoi P, Adhikari B, Dolui SK. Preparation and characterization ofJatropha curcasoil based alkyd resin suitable for surface coating. Prog Org Coat 2012;74:596–602.
  12. 12. Rokicki G, Lukasik L, Florjańczyk Z, Żukowska G. Water-based air-drying alkyd polyester resins modified with glycerol allyl ether. J Macromol Sci Pt A Pure Appl Chem 1996;33:509–521.
  13. 13. Duhon M. Vinyl toluene modified alkyd resins. Paintindia 2002;52:82–84.
  14. 14. Raval D, Patel P, Mannari V, Sinha T. Acid-functional acrylic copolymer modified alkyds for applications in surface coatings. J Sci Ind Res 1996;55:806–810.
  15. 15. Patel P, Raval D, Mannari V, Patel R. Acid functional acrylic copolymer modified alkyds for applications in surface coatings-II. J Sci Ind Res 1998;57:70–78.
  16. 16. Bhandari S, Chandra S. Synthesis, characterization and evaluation of chlorinated soybean oil alkyds. Indian J Chem Technol 1994;1:45–45.
  17. 17. Akintayo C, Adebowale K. Synthesis, characterization and evaluation of chlorinatedAlbizia benthmedium oil alkyds. Prog Org Coat 2004;50:138–143.
  18. 18. Dighe A, Toliwal S, Kotpal R. Chain stop alkyds from solvent fractionatedArgemoneand rubber seed oils. J Sci Ind Res 2000;59:808–813.
  19. 19. Aigbodion A, Pillai C, Bakare I, Yahaya L. Synthesis, characterization and evaluation of heated rubber seed oil and rubber seed-oil modified alkyd resins as binders in surface coatings. Indian J Chem Technol 2001;8:378–384.
  20. 20. Wang C, Jones FN. Stability and film properties of tung oil modified soybean alkyd emulsion. J Appl Polym Sci 2000;78:1698–1706.
  21. 21. Majumdar S, Kumar D, Nirvan Y. Acrylate grafted dehydrated castor oil alkyd—A binder for exterior paints. J Coat Technol 1998;70:27–33.
  22. 22. Alam M, Akram D, Sharmin E, Zafar F, Ahmad S. Vegetable oil based eco-friendly coating materials: A review article. Arab J Chem 2014;7:469–479.
  23. 23. Sharmin E, Zafar F, Akram D, Alam M, Ahmad S. Recent advances in vegetable oils based environment friendly coatings: A review. Ind Crops Prod 2015;76:215–229.
  24. 24. Wright HJ, Puis RND. Imide-modified alkyd resins. Ind Eng Chem 1946;38:1303–1308.
  25. 25. Dhoke SK, Sinha TM, Dutta P, Khanna A. Formulation and performance study of low molecular weight, alkyd-based waterborne anticorrosive coating on mild steel. Prog Org Coat 2008;62:183–192.
  26. 26. Pirvu C, Demetrescu I, Drob P, Vasilescu E, Vasilescu C, Mindroiu M, et al. Electrochemical stability and surface analysis of a new alkyd paint with low content of volatile organic compounds. Prog Org Coat 2010;68:274–282.
  27. 27. Ang DTC, Khong YK, Gan SN. Novel approach to enhance film properties of environmentally friendly UV-curable alkyd coating using epoxidised natural rubber. Prog Org Coat 2013;76:705–711.
  28. 28. Ang DTC, Gan SN. Novel approach to convert non-self drying palm stearin alkyds into environmental friendly UV curable resins. Prog Org Coat 2012;73:409–414.
  29. 29. Soucek M. Synthesis of UV-curable tung oil and UV-curable tong oil based alkyds. 2012.
  30. 30. Wutticharoenwong K, Dziczkowski J, Soucek MD. Tung based reactive diluents for alkyd systems: Film properties. Prog Org Coat 2012;73:283–290.
  31. 31. Duan H, Shao Z, Zhao M, Zhou Z. Preparation and properties of environmental-friendly coatings based on carboxymethyl cellulose nitrate ester and modified alkyd. Carbohydr Polym 2016;137:92–99.
  32. 32. Aulin C, Ström Gr. Multilayered alkyd resin/nanocellulose coatings for use in renewable packaging solutions with a high level of moisture resistance. Ind Eng Chem Res 2013;52:2582–2589.
  33. 33. Gogoi P, Boruah M, Sharma S, Dolui SK. Blends of epoxidized alkyd resins based onJatrophaoil and the epoxidized oil cured with aqueous citric acid solution: A green technology approach. ACS Sustain Chem Eng 2015;3:261–268.
  34. 34. SpasojevićP, PanićV, DžunuzovićJ, MarinkovićA, Woortman A, Loos K, et al. High performance alkyd resins synthesized from postconsumer PET bottles. RSC Adv 2015;5:62273–62283.
  35. 35. Greimel KJ, Perz V, Koren K, Feola R, Temel A, Sohar C, et al. Banning toxic heavy-metal catalysts from paints: enzymatic cross-linking of alkyd resins. Green Chem 2013;15:381–388.
  36. 36. Ong HR, Khan MMR, Ramli R, Rahman MW, Yunus RM. Tailoring base catalyzed synthesis of palm oil based alkyd resin through CuO nanoparticles. RSC Adv 2015;5:95894–95902.
  37. 37. Dhoke SK, Sinha TJM, Khanna A. Effect of nano-Al2O3 particles on the corrosion behavior of alkyd based waterborne coatings. J Coat Technol Res 2009;6:353–368.
  38. 38. Deyab M. Effect of carbon nano-tubes on the corrosion resistance of alkyd coating immersed in sodium chloride solution. Prog Org Coat 2015;85:146–150.
  39. 39. Dhoke SK, Khanna A. Electrochemical impedance spectroscopy (EIS) study of nano-alumina modified alkyd based waterborne coatings. Prog Org Coat 2012;74(1):92-99.
  40. 40. Dhoke SK, Khanna A. Effect of nano-Fe2O3 particles on the corrosion behavior of alkyd based waterborne coatings. Corros Sci 2009;51:6–20.
  41. 41. Dhoke SK, Khanna A. Electrochemical behavior of nano-iron oxide modified alkyd based waterborne coatings. Mater Chem Phys 2009;117:550–556.
  42. 42. Nikolic M, Barsberg S, Larsen FH, Löf D, Mortensen K, Sanadi AR. Mechanical characteristics of alkyd binder reinforced by surface modified colloidal nano silica. Prog Org Coat 2016;90:147–153.
  43. 43. Kurtİ, Acar I, GüçlüG. Preparation and characterization of water reducible alkyd resin/colloidal silica nanocomposite coatings. Prog Org Coat 2014;77:949–956.
  44. 44. Dhoke SK, Bhandari R, Khanna A. Effect of nano-ZnO addition on the silicone-modified alkyd-based waterborne coatings on its mechanical and heat-resistance properties. Prog Org Coat 2009;64:39–46.
  45. 45. Dhoke SK, Khanna A. Study on electrochemical behavior of nano-ZnO modified alkyd-based waterborne coatings. J Appl Polym Sci 2009;113:2232–2237.
  46. 46. Dhoke SK, Khanna A, Sinha TJM. Effect of nano-ZnO particles on the corrosion behavior of alkyd-based waterborne coatings. Prog Org Coat 2009;64:371–382.
  47. 47. Gumfekar S, Kunte K, Ramjee L, Kate K, Sonawane S. Synthesis of CaCO3-P (MMA-BA) nanocomposite and its application in water based alkyd emulsion coating. Prog Org Coat 2011;72:632–637.
  48. 48. Naik RB, Ratna D. Synthesis of silver nanoparticles embedded novel hyperbranched urethane alkyd-based nanocomposite for high solid antimicrobial coating application. J Coat Technol Res 2015;12:1073–1083.
  49. 49. Naik RB, Jagtap S, Ratna D. Effect of carbon nanofillers on anticorrosive and physico-mechanical properties of hyperbranched urethane alkyd coatings. Prog Org Coat 2015;87:28–35.
  50. 50. Murillo EA, Lopez BL, Brostow W. Synthesis and characterization of novel alkyd–silicone hyperbranched nanoresins with high solid contents. Prog Org Coat 2011;72:292–298.

Written By

Eram Sharmin, Fahmina Zafar, Nahid Nishat and Sharif Ahmad

Submitted: October 17th, 2015 Reviewed: February 10th, 2016 Published: June 1st, 2016