Development of Novel Polymer Nanostructures and Nanoscale Complex Hydrides for Reversible Hydrogen Storage

© 2012 Srinivasan and Sharma, licensee InTech. This is an open access chapter distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/3.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. Development of Novel Polymer Nanostructures and Nanoscale Complex Hydrides for Reversible Hydrogen Storage

Hydrogen, as a molecule, can bond to the material through three main mechanisms. The simplest form is to simply bond weakly to the host material via physisorption as a molecule. This can generally be achieved if the temperature is low enough, and is the main mechanism of storage for physisorption materials, but generally requires temperatures of approximately 77K. If additive materials, such as catalysts, are present, these materials can break up the molecule into ions which then allows for the diffusion through the relatively porous material to then chemically bond with the host material. It is inevitably demonstrated that the vital role of catalyst species such as Ti, Fe, Ni, Pd etc. thus enhances the physico-chemical adsorption of hydrogen atoms on the polyaniline matrices (Skowron´ski & Urbaniak, 2008;Yildirim & Ciraci, 2005). Similarly, hydrogen molecules can also bond the host material. By increasing the surface area as well as the porosity, two main events can occur. The first is that the hydrogen has more bonding sites to the host material. The second is that the diffusion of hydrogen into the material is made possible. Since polyaniline cannot be simply modified to have smaller molecular size, the nanostructure can be altered to increase the surface area and also to increase the hydrogen diffusion pathways. Recently, polyaniline is shown to possess outstanding hydrogen storage properties by carefully modifying the nanostructure of the material. It is found that polyaniline combines both physisorption as well as chemisorption for storing hydrogen, which provides a significant improvement of hydrogen storage properties, since a usable capacity is achieved.
The second mechanism investigated as part of this study is the route of chemisorption, or strong hydrogen atomic bonding, to complex hydride materials. Complex hydrides generally require a high temperature for hydrogen release as the hydrogen bonds are very strong. By reducing the crystallite size of the host material, specifically LiBH4 and LiNH4 and by further destabilizing the structure with MgH2, the temperature can be reduced to allow for reversible hydrogen storage at a lower temperature (Srinivasan et. al., 2012). The reduction of crystallite size, as well as the exact processing technique is shown to be very important and have a large effect on the storage capacity. Figure 2 shows general hydrogen absorption and desorption of complex hydrides.
The unhydrided material absorbs hydrogen from the outside until it is fully charged with hydrogen. By reducing the pressure on the sample or by increasing the temperature, the hydrogen is then released from the outside first until the material is fully discharged again. When the particles are too large, though, a hydrogen passivation layer can form during the initial hydrogen uptake, thereby reducing any further hydrogenation. Additionally, the kinetics, or rate, of hydrogen sorption is increased with particle size, as this means that the hydrogen has a larger distance to diffuse through.
The effects of particle size on hydrogen storage are shown in Figure 3. By employing mechano chemical milling, the particles are not only reduced in size, but dislocations and vacancies are created, thereby increasing the kinetics and capacity of the material. The interaction of the various particles that make up the hydrogen storage material are also of great importance, as this determines the interaction of the various compounds and either facilitates or hinders successful hydrogen sorption as will be shown.  The complex hydrides that are developed are carefully investigated employing varying processing techniques, a deviation of the traditional means of producing complex hydrides. The nanostructure created with the varying techniques is carefully analyzed and correlated with the material's hydrogen performance. Additionally, the hydrogen storage properties are significantly improved by using optimized quantities of nano sized additives.

Hydrogen sorption characteristics of polyaniline nanofibers
The conducting polymer nanostructures combine the advantages of organic conductors and low dimensional systems possessing interesting physicochemical properties (Macdiarmid & Epstein, 1989;Stejskal et. al., 1996;Stejskal & Gilbert, 2002;Trivedi, 1997) and useful applications (Fusalba et. al., 2001;Rossberg et. al., 1998;Virji et. al., 2006). Among the conducting polymers, polyaniline is considered important because of its extraordinary properties of electrical and optical behavior. It was recently reported that polyaniline could store as much as 6 to 8 weight percent of hydrogen (Cho et. al., 2007), which was later refuted. (Panella et al., 2005). Though many controversial results were reported in terms of hydrogen uptake (Cho et. al., 2007;Germin et. al., 2007;McKeown et. al., 2007) in polymer nanocomposites, there are still a number of parameters, tailor-made properties, surface morphologies and their correlation with hydrogen sorption behavior to be investigated before these materials can be commercially deployed for on-board hydrogen storage. Similarly, nanotubes (Dillon et. al., 1997;Nikitin et. al., 2008) or nanofibers (Hwang et. al., 2002) have attracted more interest because of their novel properties and wide potential for nanometer-scale engineering applications.
It is known that the nanofibrillar morphology significantly improves the performance of polyaniline in many conventional applications involving polymer interactions with its environment (Wang & Jing, 2008). This leads to faster and more responsive chemical sensors (Sadek et. al., 2005;Virji et. al., 2006), new organic/polyaniline nanocomposites (Athawale & Bhagwat, 2003) and ultra-fast non-volatile memory devices (Yang et. al., 2006). Nanofibers with diameters of tens of nanometers appear to be an intrinsic morphological unit that was found to naturally form in the early stage of chemical oxidative polymerization of aniline. In conventional polymerization, nanofibers are subject to secondary growth of irregularly shaped particles that form the final granular agglomerates. The key to producing pure nanofibers is to suppress secondary growth. Based on this, many methods (interfacial polymerization, rapidly mixed reactions, controlling pH and oxidizing agent) have been developed that can readily produce pure nanofibers with uniform growth, chemical composition and morphology (Ding & Wei, 2007;Rahy et. al., 2008). With this nanofiber morphology, dispensability and processbility of polyaniline are now greatly improved. On the other hand, the template synthesis method is an effective way to grow the nanotubes of various conducting polymers (Huczko, 2000). The preparation conditions and their effect on morphology, size, and electrical properties of nanofibers have been reported elsewhere (Zhang & Wang, 2006). Recently, a novel, simple, and scalable technique to control the formation of the nanofibers of polyaniline and its derivatives via porous membrane controlled polymerization (PMCP) was reported (Chiou et. al., 2008). Through appropriate synthesis conditions, nearly 100% nanofibers are formed with diameters tunable from 20nm to 250nm via the selection of pore diameter, monomer, counter ions, and polymerization conditions. The nanofiber lengths vary from sub-micrometer to several micrometers.
Conducting polyaniline nanofibers were synthesized using chemical templating method followed by electrospun process. These nanofibers have been compared with their standard bulk counterpart and found to be stable up to 150 o C. Polyaniline nanofibers prepared by electrospun method reveal high hydrogen uptake of 10wt.% at around 100 o C in the first absorption run. However, in the consecutive hydrogenation and dehydrogenation cycles, the hydrogen capacity diminishes. This is most likely due to hydrogen loading into the polymer matrix, chemisorption and saturation effects. A reversible hydrogen storage capacity of ~3-10 wt.% was also found in the new batch of electrospun nanofibers at different temperatures. The surface morphologies before and after hydrogen sorption of these PANI nanofibers encompass significant changes in the microstructure (nanofibrallar swelling effect) which clearly suggest effective hydrogen uptake and release.
Fourier Transform Infrared (FTIR) spectra of PANI-NF-CM and PANI-NF-ES prepared confirmed the formation of PANI in its emeraldine form. The major bonding environment remains unchanged for both structures (see Figure 4). The presence of two bands in the vicinity of 1500cm -1 and 1600cm -1 are assigned to the non-symmetric C6 ring stretching modes. The higher frequency vibration at 1600cm -1 is for the quinoid rings, while the lower frequency mode at 1500cm -1 depicts the presence of benzenoid ring units. Furthermore, the peaks at 1250cm -1 and at 800cm -1 are assigned to vibrations associated with the C-N stretching vibration of aromatic amine out of plane deformation of C-H of 1,4 disubstituted rings. The aromatic C-H bending in the plane (1167cm -1 ) and out of plane (831cm -1 ) for a 1,4 disubstituted aromatic ring indicates a linear structure.  shows the structure of the PANI-NF-ES sample. It is clear that the electrospun nanofibers exhibit a smoother surface as opposed to the rough surface of the chemically grown nanofibers. Figure 6 shows the cycle life kinetics of the electrospun PANI nanofibers. No hydrogen uptake was observed until the sample was heated to 100 o C. The initial high capacity of 11wt.% is not fully observed when desorbing the hydrogen, as only 8wt.% is released. This occurs in a two-step process characterized by a fast (physisorption) hydrogen release and a slower (chemisorption) hydrogen release step. The full capacity of hydrogen desorbed is then reabsorbed and with each consecutive cycle the amount of hydrogen dwindles until finally no more hydrogen is released of absorbed. This hydrogen behavior is due to hydrogen bonding with both unterminated bonds as well as with the surface of the nanofibers.   From the same figure, the hydrogen desorption was plotted after 66 cycles at 100 o C and reveals that the kinetics are rather rapid, with most of the hydrogen being released in less than 30 min for a total hydrogen release of close to 6 wt.%. Additionally, the absorption kinetics in the 64 th cycle of hydrogen at 80 bar pressure with varying temperature is shown in Figure 8(b). Initially, the hydrogen is absorbed at 125 o C with saturation occurring after approximately 2 h (solid line). After 18 h, the temperature (dotted line) is reduced to 30 o C, whereupon another 3 wt.% of hydrogen is absorbed. This may be due to both chemisorption and physisorption phenomena occur in these materials and the mechanism is yet to be investigated.  The PANI-NF-CM, however, absorbed hydrogen at 30 o C and did so reversibly with a capacity of approximately 3wt.%, as seen in Figure 9. Unlike the electrospun nanofibers, the hydrogen was absorbed and released in a one-step process with very rapid kinetics of less than 10min. This fast hydrogen sorption is most likely due to the higher surface area of the Development of Novel Polymer Nanostructures and Nanoscale Complex Hydrides for Reversible Hydrogen Storage 11 chemically grown nanofibers as opposed to the electrospun nanofibers that exhibit a much smoother surface.
When looking at the microstructure of both types of polyaniline nanofibers, it is interesting to note that the nanofibers that were initially present, for the chemically grown samples have disappeared completely, as shown in Figure 10(a). BET surface area measurements, however, have shown that the surface area of the PANI-NF-CM has actually stayed constant, which is explained by the porous nature of the sample of hydrogen cycling. The hydrogen interacted with the PANI-NF-CM and created diffusion pathways for it to pass through the sample reversibly.  The microsturcture of the hydrogen cycled PANI-NF-ES, on the other hand, as shown in Figure 10(b), clearly show that the nanofibrallar structure is still intact, although the nanofibers show clear evidence of swelling and also of breaking apart. This further confirms the point that the hydrogen interacted more in a chemisorption manner with the sample, rather than physisorption.

Nanoscale complex multinary hydrides for reversible hydrogen storage
Advanced complex hydrides that are light weight, low cost and have high hydrogen density are essential for on-board vehicular storage (Grochala & Edwards, 2004;Schlapbach & Zuttel, 2001;; US Department of Energy (DOE) Report 2003) Some of the complex hydrides with reversible capacities achieved are Alanates (Bogdanovic & Schwickardi, 1997;Jensen & Zidan, 2002;Srinivasan et. al., 2004), Alanes (Graetz et. al., 2005), Amides (Chen et. al., 2002;Hu & Ruckenstein, 2005) and Borohydrides (Au, 2006;Srinivasan et. al., 2008;Vajo et. al., 2005) magnesium based hydrides (Orimo et. al., 2005; and mixed complex hydrides  have been recently reported with improved hydrogen storage characteristics. The challenging tasks to design and develop the complex hydrides mandate an optimization and overcoming of kinetic and thermodynamic limitations (Fitchner, 2005;Zuttel, 2004). The enhancement of reaction kinetics at low temperatures and the requirement for high hydrogen storage capacity (> 6.5 wt.%) of complex hydrides could be made possible by either adopting destabilization strategies or catalytic doping. If nanostructured materials with high surface area are used as the catalytic dopants, they may offer several advantages for the physicochemical reactions, such as surface interactions, adsorption in addition to bulk absorption, rapid kinetics, low temperature sorption, hydrogen atom dissociation and molecular diffusion via the surface catalyst.
The intrinsically large surface areas and unique adsorbing properties of nanophase catalysts can assist the dissociation of gaseous hydrogen and the small volume of individual nanoparticles can produce short diffusion paths to the materials' interiors. The use of nanosized dopants enables a higher dispersion of the catalytically active species (Joo et. al., 2001) and thus facilitates higher mass transfer reactions. Recently, it is claimed that an enhancement of reaction kinetics has been demonstrated with CNT catalyzed NaAlH4 as represented in Figure 14a and 14b (Dehouche et. al., 2005). It was speculated that the repeated interactions of CNT with NaAlH4 during mechanical milling causes an insertion of nanotube bundles (~100-200 nm) in NaAlH4 matrix and accompanying deformation as shown in Figure 14c (Pukazhselvan et, al., 2005).
In addition, the structure of carbon plays an important role on the hydrogenation and dehydrogenation behavior of NaAlH4. Improvement of reaction rate and hydrogen storage capacity has also been reported for the Alanates doped with Ti-nanoparticles (Bogdanovic et. al., 2003). Apparently, the use of nanosized doping agents enables one to achieve a higher dispersion of the catalytically active Ti species than their bulk counterparts. Though the catalytic enhancement of decomposition of sodium aluminum hydride leads to fast sorption kinetics at moderate temperatures, its usable hydrogen storage capacity is rather limited (~5.6 wt%). Lithium borohydride (LiBH4) on the other hand, possesses theoretical hydrogen content of ~18.3 wt%, exhibiting potential promise for on-board applications. However, hydrogen decomposition from LiBH4 starts at an elevated temperature of 380 °C and also shows little or no reversible hydrogenation behavior. It has been reported that catalytically doping SiO2 lowers the temperature of hydrogen evolution to 300 °C (Zuttel et. al., 2003). In addition to improving the kinetics of LiBH4, tailoring the thermodynamic property is of vital importance for developing an ultimate "holy grail" material for hydrogen storage.
In this direction, the hydrogenation/dehydrogenation enthalpy has been reduced by 25 kJ/mol of H2 for the (LiBH4+½ MgH2) system (Vajo et. al., 2005). Magnesium hydride destabilizes the LiBH4 structure and forms an intermediate MgB2 phase (Barkhordarian et. al., 2007;Cho et. al., 2006) during the hydrogen charging and discharging reactions. In a very recent study on the LiBH4/MgH2 system, it was demonstrated that the hydrogenation and dehydrogenation of LiBH4 occurs via the Li-Mg alloy phase (Yu et. al., 2006) and not through MgB2 formation. It is generally known that pristine MgH2 theoretically can store content of ~7.6 wt.% hydrogen (Zaluska et. al., 2001). However, so far, magnesium hydride based materials have limited practical applications because both hydrogenation and dehydrogenation reactions are very slow and hence relatively high temperatures are required (Schlapbach & Zuttel, 2001). Magnesium hydride forms ternary and quaternary hydride structures by reacting with various transition metals (Fe, Co, Ni, etc) and thus improved kinetics (Jeon et. al., 2007). Moreover, the nanoscale version of these transition metal particles offers an additional hydrogen sorption mechanism via its active surface sites (Jeon et. al., 2007;Zaluska et. al., 2001). In a similar way, the synergistic approach of doping nanoparticles of Fe and Ti with a few mol% of CNT on the sorption behavior of MgH2 has recently been investigated . The addition of Carbon Nanotubes (CNT) significantly promotes hydrogen diffusion in the host metal lattice of MgH2 due to the short pathway length and creation of fast diffusion channels .
The dramatic enhancement of kinetics of MgH2 has also been explored through reaction with small amounts of LiBH4 (Johnson et. al., 2005). Though the MgH2 ad-mixing increases the equilibrium plateau pressure of LiNH2 (Luo, 2004) or LiBH4 Vajo et. al., 2005), catalytic doping of these complex hydrides had not been investigated. It is generally believed that the role of the nanocatalyst on either NaAlH4 or MgH2 is to stabilize the structure and facilitate a reversible hydrogen storage behavior. However, the actual mechanism by which transition metal nanoparticles enhance the dehydrogenation kinetics of complex hydrides is not yet understood very well. Thus, it is desirable to investigate the effects of catalysts, defects, grain boundaries, interface boundaries and impurity atoms on the surface. Based on an extensive literature search, we found no reports on the synergistic effects of transition metal nanoparticles on the complex composite hydrides such as LiBH4/MgH2, LiNH2/LiH/MgH2 or LiBH4/LiNH2/MgH2 etc.
The present work addresses the grand challenge of hydrogen storage by mechanochemically milling LiBH4 and LiNH2 with MgH2 to produce a new complex quaternary Li-Mg-B-N-H structure. This Li-Mg-B-N-H structure possesses storage capacity of more than 10 wt.% at around 150 o C. The parent compounds, LiBH4 and LiNH2, were purchased from Sigma Aldrich with a purity of at least 95%, while MgH2 was obtained from Alfa Aesar with a purity of 98%. All materials were kept in an inert atmosphere in a glove box and used without further purification. The investigated samples were created in 4g batches with a constant molar ratio of 2LiNH2:LiBH4:MgH2, while taking into account the purity of the parent compounds, by employing high energy ball milling (Fritsch Pulverisette 6) for 5 hours at 300rpm with intermittent hydrogen/argon (5%/95%) purges for 20 minutes before milling and after 2 and 4 hours. This was done to ensure that as little hydrogen as possible was released during the milling process and to reduce the agglomeration of the hydride that occurs when pure hydrogen is used as compared to the hydrogen/argon mixture. The MgH2 was either added as received or was added as a so-called nano MgH2. The nano MgH2 (nMgH2) was created by ball milling the commercial MgH2 (cMgH2) for 12 hours with intermittent hydrogen/argon purges every 2 hours. This ensured the reduction of particle size as well as the decrease in hydrogen release temperature, as previously reported. The two main processing schemes that were used are shown in Figure 11.
The first processing scheme was to add all parent compounds and mill for 5 or 10 hours using either commercial or nano MgH2. This is the scheme that is generally used in reported literature and the materials serve as a kind of reference material. The second processing scheme was to first create the quaternary structure LiBNH by milling LiBH4 with 2LiNH2 for five hours and then adding either commercial or nano MgH2, after which the quaternary and the MgH2 were milled for an additional 5 hours. All milling was carried out in an inert atmosphere and the samples were purged with the hydrogen/argon mixture every 2 hours. In total, five different samples were created. The samples are referred to in this paper according to the naming convention shown in the bold boxes of Figure 11. X-Ray Diffraction. Figure 12 shows the XRD pattern comparing the five differently processed complex hydrides. The parent compounds, LiBH4, LiNH2, as well as both commercial and nano MgH2 are in the lower half of the figure as a reference. Neither LiBH4 nor LiNH2 peaks are observed in any of the five samples. This confirms that these two materials are fully consumed during the milling process and actually form a new quaternary structure, referred to as LiBNH. The addition of commercial MgH2 does not cause the formation of a new complex structure, but instead indicates that the quaternary structure is preserved, while the MgH2 simply intermixes with the material. When the nano MgH2 is added to LiBH4 and LiNH2 or to the quaternary LiBNH, the MgH2 peaks are barely picked up by the XRD. This indicates that the small size of the MgH2 causes the material to intermix and fill voids of the quaternary structure, which results in a nanocrystalline particle distribution, while still preserving the quaternary structure formed by the LiNH2 and LiBH4. All samples are a physical, rather than a chemical, mixture of the quaternary structure LiBNH with MgH2.
Thermal programmed desorption. Upon producing the complex hydrides, each sample was characterized for its thermal desorption characteristics using TPD with a heating rate of 1, 5, 10, and 15 o C/min. As compared to the quaternary structure, the multinary structure containing MgH2 showed a 3-step hydrogen release mechanism, as is shown in Figure 13. Our TPD analysis of LicMgBNH sample confirms the previously reported data (Yang et al.), but also shows that the processing condition of the material does have an effect on the thermal decomposition characteristics. The first hydrogen release peaks between 157.7 o C for 10hr LicMgBNH and 165.2 o C for LinMgBNH, which is a relatively small difference in temperature. When investigating the second, or main, peak of the various samples, it is interesting to note that the temperature range for main hydrogen release varies from 287 o C for the 10hr LicMgBNH to 306.6 o C for LinMgBNH. MgH2 interacts with the quaternary structure and destabilizes it, thereby releasing hydrogen. In the case of the LinMgBNH and LicMgBNH samples, it takes the entire milling duration (5hr) to form the quaternary phase, thereby giving the MgH2 little time to allow for the release of hydrogen during milling. In the case of 10hr LicMgBNH, the MgH2 has 5hr of milling duration (after the formation of the quaternary) to destabilize the material and allow for hydrogen release.
Finally, in the case of LiBNH+cMgH2, the MgH2 has to first be reduced in size to allow for the destabilization and the resultant hydrogen release. LiBNH+nMgH2, however, releases hydrogen during the milling process, as the smaller size of nano MgH2 allows for immediate destabilization of the already present quaternary. Either prolonged milling duration or reduction in particle size will lead to release of hydrogen in the milling process Activation energy. The activation energy of each sample was experimentally determined using Kissinger's method, based on TPD data ( Figure 13) taken at 1, 5, 10, 15 o C/min for the two peaks and correlated to the hydrogen peak release temperature as described by: where β is the heating rate of the sample in K/min, Tm is the peak temperature in K, E is the activation energy of the hydrogen release, and R is the gas constant. When investigating the first peak, around 160 o C, it is interesting to note that the 10hr LicMgBNH sample has the lowest activation energy (109.8 kJ/mole) at 157.7 o C as seen in Figure 14. Although all samples exhibit comparable decomposition temperatures, their activation energies vary by ~20 kJ/mole.   A plausible reason is that the reaction pathways of ad-mixing MgH2 either in the first place (10hr LicMgBNH) or after the quaternary formation (e.g. LiBNH+nMgH2) proceeds with fine distribution of nanocrystalline MgH2 in the host matrix of multinary hydrides. It has been recently claimed that the nanocrystallization of MgH2 has significant impact on lowering the enthalpy of formation and enhancement of the reaction kinetics. The high temperature main hydrogen release peak (300 o C) for all the processed materials and the reference LiBNH quaternary hydride are shown in Figure 6. While comparing the activation energies and decomposition temperatures of all the samples, it can be clearly inferred that the quaternary hydrides LiBNH combined with either commercial (LiBNH+cMgH2) or nanocrystalline MgH2 (LiBNH+nMgH2) milled for 5 hours show lower values, e.g. 145-148 kJ/mole at ~300 o C. Simply based on this data, it is difficult to justify from both Figures 15  and 6, which sample possesses an optimum hydrogen release characteristic at these two main decompositions. However, it is undoubtedly clear that both the steps occur at two different temperature regimes, namely 160 and 300 o C, at which either surface adsorbed or bulk absorbed hydrogen is released.
At the low temperature hydrogen release step, the nano MgH2 acts as a facilitator in speeding up the reaction; hence both the 10hr LicMgBNH and LiBNH+nMgH2 materials demonstrate lower activation energies (Figure 14). On the other hand, in the high temperature hydrogen release step (Figure 15), the temperature of 300 o C acts as a driving force to release hydrogen from the bulk structures of both LicMgBNH and LinMgBNH milled only for 5 hours. Hence, these materials exhibit lower activation energies which are comparable to pristine LiBNH. Based on the detailed analysis, we draw the conclusion that an additional 5 hours of ball milling, either of the all-in-one hydride (10hr LicMgBNH) or the quaternary/nanocrystalline hydride mixture (LiBNH+nMgH2), will alter the decomposition characteristics, especially the activation energy which is vital for hydrogen storage.
Pressure-composition-isotherms. Figure 16 represents the PC isotherms of the multinary complex hydrides created with different processing conditions. The PCT studies of the multinary samples are carried out under the following conditions: temperature, T=150-175 o C; pressure difference between aliquots, ΔP=3bars (0.3 MPa); absorption pressure limit, Pa=80bars (8 MPa); desorption pressure limit, Pd=0bar (0 MPa); and reservoir volume, Vr=160cm 3 . Since all these samples are in hydride phases, the dehydrogenation experiment was followed by the rehydrogenation for at least 10 hours.
The PCT characteristics and their observations are given with respect to the sample processing conditions as follows.
LicMgBNH and LinMgBNH: The multinary complex hydrides processed with either commercial or nanocrystalline MgH2 and milled all-in-one for 5 hours reveal reproducible hydrogen capacity of 3 to 4wt.%. It is noteworthy to mention that LinMgBNH possesses at least 1wt.% higher capacity and 25 o C reduction in temperature as compared to the LicMgBNH counterpart, as also seen from the initial ramping kinetic profiles in Figure 7b. This could be achieved because of the uniform distribution of fine MgH2 nanoparticles which likely act as hydrogen diffusion enhancement sites, increasing the amount of hydrogen released. Yet another difference between these two processed materials is the tailoring of the plateau pressure (hydrogen/hydride equilibrium region), which is crucial for a hydrogen storage system to be viable for mobile applications. The LinMgBNH material exhibits reduction in the absorption plateau pressure by 20 bars (2 MPa) in contrast to the LicMgBNH due to nanoparticulate formation.
LiBNH+cMgH2 and LiBNH+nMgH2:A greater reversible hydrogen storage capacity of 5.3-5.8wt.% was found at temperatures of 150 o C to 175 o C for the quaternary hydrides LiBNH either milled with commercial or nano MgH2 for 5 hours. The nano MgH2 loaded LiBNH outperformed its commercial counterpart with a higher hydrogen capacity of 5.8wt.%. at 150 o C as compared to 175 o C (refer to Figure 16b). Figure 16a shows that there are plateau pressure regions, which are not as clearly defined as the LicMgBNH and LinMgBNH samples. Moreover, the sorption plateau of these samples resembles greatly the pristine LiBNH (not shown here), which is the precursor material for the multinary hydride formation. Overall, it is unambiguously claimed that LiBNH admixed either with commercial or nano MgH2 and milled for 5 hours, exhibits a high reversible hydrogen storage capacity of ~6wt.% at temperatures less than 175 o C. Figure 16. Comparison of the hydrogen sorption characteristics of the various processing conditions at the lowest hydrogen release temperature.
10hr LicMgBNH: The extended milling duration of 10 hours for the three component systems, 2LiNH2+cMgH2+LiBH4 show poor hydrogen performance as depicted in Figure16a. A low hydrogen desorption capacity of 2wt.% at a plateau pressure of less than 5bars (0.5 MPa) with little or no reversibility is obtained in this material. The crystallite agglomeration during the prolonged milling is expected to be the limiting factor for the absence of plateau pressure and overall storage capacity. Though this sample exhibits a lower activation energy (~109 kJ/mole) in the first hydrogen release (see Figure 14), the effective hydrogenation needs systematic optimization strategies which are currently under investigation.
Crystallite size effects on hydrogen release characteristics. In order to better understand the hydrogen performance of the differently processed materials, the hydrogen capacity was correlated with the crystallite sizes of the quaternary phase, LiBNH, and the MgH2. The crystallite sizes were calculated from the XRD data ( Figure 12) of each material using Scherrer's method. The initial crystallite sizes of LiNH2, LiBH4, MgH2, nano MgH2 and LiBNH were determined to be 138nm, 152nm, 212nm, 27nm, and 60nm, respectively. As seen from Figure 16b, the nano size MgH2 has a definite effect on the initial hydrogen release temperature. Both samples synthesized with nano MgH2 release hydrogen at 150 o C as compared to 175 o C for all the other samples, which were synthesized with its commercial counterpart. The MgH2 crystallite size for the nano MgH2 samples are both approximately 10nm, whereas the crystallite size of the commercial MgH2 samples vary from 35nm to 75nm, as seen in Figure 17. It is important to note that the crystallite size of both MgH2 and LiBNH are largest for the 10hr LicMgBNH sample, which explains the poor hydrogen performance. This is because of the well known fact that larger particles, and therefore a smaller surface area, can limit hydrogen performance (less than 2wt.% capacity) due to diffusion inhibition and passivation effects.
A milling duration of more than 5 hours is in fact counterproductive and allows for the crystallite size to increase, as both the LiBNH and MgH2 agglomerate. When looking at the correlation between crystallite size and hydrogen concentration, as shown in Figure 17, it becomes evident that the size of the LiBNH crystallites plays an important role on the amount of hydrogen released. If the LiBNH crystallites have a size of approximately 28nm and the MgH2 crystallites are approximately within 15nm (13nm to 43nm) of this size, the highest possible hydrogen release is achieved (5.5wt.%). When the MgH2 and LiBNH crystallites are either too similar in size, as in the case for the LicMgBNH sample (3.3nm difference), or if they are too different in size, as in the case for the 10hr LicMgBNH sample (32.9nm difference), the amount of hydrogen released by the sample is reduced. Overall, the new multinary complex hydrides show potential promise on the reversible hydrogen storage characteristics as elucidated in Figure 18. The cyclic kinetics of Li-nMg-B-N-H reveals a reversible hydrogen storage capacity of 6-8wt.% with fast sorption kinetics around 200-250 o C which matches or exceeds with the set-forth DOE technical targets. Thus a reversible hydrogen storage capacity of 5-7 wt.% was reproducibly obtained for these materials. With respect to the mass spec analyses, note that the scans did not reveal any evidence for potential parent (or daughter) species (ions); namely, NH3, BH3, BH2NH2, N2H4.
Destabilization of LiBH4/LiNH2/MgH2 with Nano Sized Additives. Based on the previous experimental work on the optimization of the processing conditions as well as some previous insight into the role of nano sized additives on the quaternary LiBNH structure, it was decided to systematically investigate the effect of various nano sized additives on the multinary structure LiBNH + nMgH2, as described in the previous section. TPD was used to obtain information about changes in the parent material's hydrogen characteristics. Specifically, the temperature of hydrogen release as well as some general information about the kinetics of hydrogen release can be ascertained from this type of measurement. The peak temperature indicates the optimal hydrogen release temperature, whereas the width of the peak can be used to get insight into the rate at which hydrogen is released, at least qualitatively. A wide peak indicates a low rate of hydrogen release, whereas a narrow and sharp peak indicates rapid hydrogen release. Figure 19 demonstrates the lower temperature release of hydrogen by nanoadditve doping when compared to the pristine complex hydride. As previously described, the parent compound, LiBNH + nMgH2, exhibits a three-step hydrogen release. While the TPD measurements are used for quickscreening the effect of the additives on the hydrogen performance of the material, it can be seen that each additive material either affects the rate of hydrogen release, as depicted by a sharp and narrow peak (especially iron) or significantly lowers the temperature required for hydrogen release.
Since the TPD measurements only give an indication of the hydrogen sorption results, ramping kinetic measurements, where approximately 0.1g of sample are loaded into the PCT and then ramped at a rate of 1 o C/min, were performed on all samples. Figure 20 shows the more detailed hydrogen performance of the standard sample, LiBNH+nMgH2 without any additives, as well as with 2mol% of the aforementioned additives.  It becomes clear that while cobalt seemed promising from the TPD data, it in fact has such slow kinetics, that cobalt is no longer of interest as an additive. The kinetics measurement do confirm the TPD data in that manganese and iron have the fastest kinetics, as indicated by the slope of the desorption curves. Furthermore, the significant reduction in hydrogen release temperature of nickel is confirmed. Figure 21 shows a comparison of the hydrogen release rate and hydrogen release temperature of the standard sample without and with 2mol% of nano sized additives. Since the nano sized nickel showed the lowest hydrogen release temperature of just under 200 o C and nano sized iron showed the highest release rate (0.2wt.%/min) at a comparatively low temperature of 245 o C, these two additives were chosen to be optimized in terms of their concentration.