Open access peer-reviewed chapter

Potential-pH Diagrams for Oxidation-State Control of Nanoparticles Synthesized via Chemical Reduction

By Shunsuke Yagi

Submitted: November 15th 2010Reviewed: April 26th 2011Published: September 15th 2011

DOI: 10.5772/21548

Downloaded: 4425

Keywords

1. Introduction

In the past, many synthesis methods of nanoparticles have been reported, but the synthesis processes have not been well discussed from the viewpoint of thermodynamics. In this chapter, a general concept using potential-pH diagrams is described for oxidation-state control of nanoparticles synthesized via chemical reduction (also called electroless deposition or liquid-phase reduction). By comparing kinetically determined mixed potential measured in reaction solution and thermodynamically drawn potential diagrams, e.g., potential–pH diagram, it is possible to know “what chemical species is stable in the reaction solution?.” It is predicted from potential-pH diagrams that nanoparticles in different oxidation states can be selectively synthesized by controlling the mixed potential. This concept is verified by selectively synthesizing Cu and Cu2O nanoparticles from CuO aqueous suspension via chemical reduction using the concept as an example. The advantage of this chemical reduction method is that abundant nanoparticles can be obtained for a short time by a simple operation. An extremely small activity of Cu2+ aquo ion is achieved by using insoluble CuO powder as a Cu(II) ionic source, which is a key for the synthesis of nanosized particles. The dependency of mixed potential on pH and temperature is discussed in the verification process. This chapter is written based on the result of the authors’ paper (Yagi et al., 2009) with further detailed information on practical thermodynamic calculation and drawing procedure of potential-pH diagrams.

2. Brief overview of objective materials and their synthesis

2.1. Copper (Cu) nanoparticles

Copper (Cu) nanoparticles are of great interest in various fields, specifically that of printable electronics. Cu interconnects less than 20 μm wide can be made with a high resolution screen printer or a super inkjet printer using an ink which contains dense Cu nanoparticles. Cu nanoparticles have been synthesized by various reduction processes from cuprous (Cu(I)) or cupric (Cu(II)) compounds, including direct electrochemical reduction (Han et al., 2006; L. Huang et al., 2006; Yu et al., 2007), chemical reduction (Lisiecki & Pileni, 1993; Lisiecki et al., 1996; H. H. Huang et al., 1997; Qi et al., 1997; Ohde et al., 2001), thermal reduction (Dhas et al., 1998), sonochemical reduction (Dhas et al., 1998; Kumar et al., 2001), laser irradiation (Yeh et al., 1999), and gamma radiolysis (Joshi et al., 1998). Many of these methods are conducted in liquid phase, which has the important advantage that nanoparticles can be formed in the presence of dispersing agents and no additional process for the addition of dispersing agents is required for the fabrication of inks to avoid the agglomeration.

In recent years, Cu nanoparticle also has drawn a lot of attention due to its novel optical properties from surface plasmon resonance (SPR), which occurs when a light electromagnetic field drives the collective oscillation of free electrons in Cu nanoparticles (J. Li et al., 2011). This resonance creates large local electric field enhancement on the nanoparticle surface, which can be used to manipulate light–matter interactions and boost non-linear phenomena. The SPR of Cu nanoparticles is observed at 560-580 nm, which is slightly changed by a medium and a dispersing/protecting agent (Singh et al., 2010; X.D. Zhang et al., 2011), and Pileni and Lisiecki demonstrated the strong broadening of the plasmon peak for Cu nanoparticles with decreasing the particle size (Pileni & Lisiecki, 1993). In addition, Cu nanoparticles display fluorescence. Siwach and Sen reported fluorescence peaks at ca. 296 nm for excitation wavelength at 213 nm and 270 nm using Cu nanoparticles about 13 nm in diameter in water (Siwach & Sen, 2010).

2.2. Cuprous oxide (Cu2O) nanoparticles

Cuprous oxide (Cu2O) is a p-type semiconductor (Young & Schwartz, 1969) with unique optical and magnetic properties (Mahajan et al., 2009) and is also a promising material with potential applications in solar energy conversion, microelectronics, magnetic storage, catalysis, photocatalysis (Gu et al., 2010), and gas sensing (Zhang et al., 2006). Cu2O is also used for the investigation into Bose–Einstein condensation of excitons (Snoke, 2002). Many methods have been reported to synthesize Cu2O nanoparticles (Zhang et al., 2006; Muramatsu & Sugimoto, 1997; X. Liu et al., 2007), nanocubes (Gou & Murphy, 2003; R. Liu et al., 2003), octahedral nanocages (Lu et al., 2005), nanorods (Cheng et al., 2011), and nanowires (Wang et al, 2002). For example, Muramatsu and Sugimoto reported that Cu2O particles with an average diameter of 270 nm were synthesized in large quantities from a CuO aqueous suspension using hydrazine as the reducing agent (Muramatsu & Sugimoto, 1997). Liu et al. formed CuO, Cu2O, and Cu nanoparticles using copper(II) acetylacetonate [Cu(acac)2] as a precursor in oleylamine by controlling temperature (Liu et al., 2007).

It is noteworthy that nanoparticles of transition-metal oxides including Cu2O and CuO are also expected as a negative electrode material with a high specific capacity and extraordinary large surface area for lithium ion battery (Poizot et al., 2000). The cycle property of Cu2O nanoparticles is strongly dependent on the particle size, shape, and structure; there is an optimum condition, displaying the highest electrochemical performance (C.Q. Zhang et al., 2007).

In the next section, a general guideline is introduced for the selective synthesis of Cu and Cu2O nanoparticles possessing superior properties described above from the same CuO aqueous suspension.

3. Theory for oxidation-state control of nanoparticles

3.1. Mixed potential

At any point within the reaction volume during nanoparticle synthesis via chemical reduction, several partial reactions occur in parallel (e.g. oxidation of a reducing agent, reduction of metallic ion, reduction of dissolved oxygen, and solvent reduction decomposition). The potential at a point is determined at the value where the total of anodic currents I a,total (currents for oxidation reaction) balances the total of cathodic currents I c,total (currents for oxidation reaction) unless current flows outside (Fig. 1). This potential is called the mixed potential. Stable chemical species in the reaction solution can be determined by comparing measured mixed potential and calculated potential diagrams, and chemical species synthesized can be changed by controlling mixed potential. As an example, considering a reaction system for the synthesis of Cu or Cu2O nanoparticles from a CuO aqueous “suspension” of pH 9 via hydrazine reduction, anodic reactions are mainly the oxidation reactions of hydrazine as follows

N2H4+4OHN2+4H2O+4eE1
N2H4+OH1/2N2+NH3+H2O+eE2

Cathodic reactions are mainly the deposition of Cu or Cu2O and hydrogen generation as follows

Figure 1.

Schematic current-potential curves: mixed potential is determined at the value where the total of anodic currents I a,total, balances the total of cathodic currents I c,total, unless current flows outside.

Deposition of Cu

Cu(II)+2eCuE3

Deposition of Cu2O

2Cu(II)+2OH+2eCu2O+H2OE4

Hydrogen generation

2H2O+2eH2+2OHE5

where Cu(II) represents all the copper(II) species and is distinguished from a copper(II) aquo ion, Cu2+. The overall deposition reactions of Cu and Cu2O in this system can be expressed using the following equations

Deposition of copper

CuO+1/2N2H4Cu+1/2N2+H2OE6
CuO+2N2H4Cu+N2+2NH3+H2OE7

Deposition of cuprous oxide

2CuO+1/2N2H4Cu2O+1/2N2+H2OE8
2CuO+2N2H4Cu2O+N2+2NH3+H2OE9

In practice, the “absolute” mixed potential cannot be measured because of the following experimental reason (Bockris et al., 2000). When one tries to measure the mixed potential using potentiometers, two metallic terminals of the potentiometers must be connected to the two electrodes immersed in the reaction solution (electrolyte). In this case, all one can measure is the potential “difference” across the two electrode/electrolyte interfaces. Each electrode/electrolyte interface has a potential difference due to a double layer between the electrode and electrolyte, and thus, the measured potential difference includes at least two potential differences at different interfaces. In other words, when one tries to measure one potential difference, one must create at least one additional potential difference. This is not favorable, but inevitable. However, by using a nonpolarizable electrode as one electrode, the measured potential difference directly reflects the change in the potential difference of the other electrode/electrolyte interface because the potential difference of the nonpolarizable electrode/electrolyte interface does not change. Therefore, the measured potential difference can be treated as the “relative” mixed potential by using a nonpolarizable electrode as a reference electrode, e.g. standard hydrogen electrode, Ag/AgCl electrode, and saturated calomel electrode. In addition, the other measuring electrode should not have a strong catalytic activity for possible reactions in order not to affect the original balance of anodic currents and cathodic currents so much, which can cause the change in the mixed potential. In the present system, a gold electrode is appropriate as a measuring electrode since gold has a low catalytic activity for hydrazine decomposition or hydrogen generation.

3.2. Potential-pH diagram (Pourbaix diagram)

Potential-pH diagram is a kind of phase diagram showing possible stable phases of an electrochemical system in equilibrium. Potential-pH diagram was invented by Marcel Pourbaix (1904-1998) and is also known as Pourbaix diagram (Pourbaix, 1966). In the potential-pH diagram, the vertical axis is potential normally with respect to the standard hydrogen electrode (SHE) and the horizontal axis is pH(=−loga H+), where a H+ is the activity of proton. By comparing the potential-pH diagram and the mixed potential described above, it is possible to know the stable or obtainable chemical species in the reaction solution.

3.3. How to draw potential-pH diagram

In order to draw potential-pH diagram, it is necessary to determine the activity of ionic species. For example, consider an equilibrium reaction of metallic oxide M x O y and Mz+ aquo ion in an aqueous solution as follows;

MxOy+2yH+=xMz++yH2OE10

where M is a metal and Mz+ is a metallic aquo ion. There is a relationship 2y=xz, which is derived from the charge balance of the reaction 10. The following equation indicates the change in Gibbs free energy, ΔGTof the reaction 10 at absolute temperature T in kelvins and 1 atm.

ΔGT=ΔGT0+RTlnaMZ+xaH2OyaMxOyaH+2yE11

whereΔGT0is the change in Gibbs free energy at a standard state and a temperature T (K), and R is the gas constant. In equilibrium, the change in Gibbs free energy is zero and thus

0=ΔGT0+RTlnaMZ+xaH2OyaMxOyaH+2yE12
ΔGT0can be calculated by the following equation using thermodynamic data;
ΔGT0=ΔHT0TΔST0=ΔH2980+298TΔCPdTT(ΔS2980+298TΔCPTdT)E13

where ΔHT0and ΔST0are the changes in enthalpy and entropy that accompanies the formation of 1 mole of a product from its component elements at a temperature T (K) and 1 atm. ΔCpis the change in specific heat at constant pressure (1 atm). The absolute value of enthalpy H cannot be measured but chemical reaction system is a closed reaction system, and the change in enthalpy can be obtained by just subtracting the sum of the heat of formation, which is measurable, of the components in the left-hand side from that of the components in the right-hand side. Thermodynamic databooks include the list of the standard heat of formation, standard entropy at 298 K, and specific heat (Kubaschewski & Alcock, 1979; Latimer 1959; Stull & Prophet, 1971). Going back to the equation 12, the activities of water and oxide are both 1, and the equation 12 is simplified into the relationship between pH and the activity of the metallic aquo ion.

2ypH=ΔGT0ln(10)RTxlogaMZ+E14

Thus, the pH value, at which M x O y and Mz+ are in equilibrium, is determined by the activity of the metallic aquo ion. Conversely, the activity of the metallic aquo ion in equilibrium can be determined by measured or maintained pH of a metallic oxide reaction suspension.

In the present system, CuO powder is dispersed in the reaction solution. When the pH of the reaction solution is 9 and the temperature is 298 K, the activity of Cu2+ aquo ion is calculated to be about 7.5 x 10-11 using the thermodynamic data shown in Table 1 (Criss & Cobble, 1964; Kubaschewski & Alcock, 1979; Latimer 1959; Stull & Prophet, 1971). This value itself does not have a precise meaning; the calculated value of the activity of Cu2+ aquo ion can be significantly affected by an experimental error of thermodynamic data, e.g. the standard entropy of CuO. Normally, this value just indicates that CuO does not dissolve into the solution in a practical sense. However using this value, one can calculate other important thermodynamic values such as the oxidation-reduction (redox) potential of Cu2+/Cu redox pair in this reaction system using the same thermodynamic data set.

Chemical speciesStandard heat of formation (kJ mol-1)Standard entropy (J K-1 mol-1)Specific heat at constant pressure (J K-1 mol-1)Cp = a + bx10-3T + cx105T2
H+(aq)0.00.0129.7
Cu2+(aq)64.4−98.7267.8
H2O(l)−285.870.075.4
H2(g)0.0130.627.33.30.50
Cu(s)0.033.122.66.3
Cu2O(s)−167.493.162.323.9
CuO(s)−155.242.738.820.1
N2(g)0.0191.527.94.3
NH3(g)−45.9192.737.318.7−6.49
N2H4(l)50.6121.672.787.20.60

Table 1.

List of standard heat of formation, entropy at 298 K and 1 atm, and specific heat at constant pressure (1 atm) considered and used for thermodynamic calculation. The units of the original data are converted to match the SI units using the thermochemical calorie, 1 calth=4.184 J. All the data considered and used for thermodynamic calculation are listed in this table. Only the constant a and coefficients b and c for the specific-heat capacity of hydrazine are estimated by fitting the discrete data of the specific heat capacity of hydrazine in the temperature range from 100 to 600 K. The data of liquid hydrazine N2H4(l), are used instead of those of hydrated hydrazine N2H4(aq), because of the lack of the data of N2H4(aq).

The procedure to draw potential–pH diagram is shown in Fig. 2. In this system, the equilibrium pH between Cu2+ aquo ion with the activity of 7.5 x 10-11 and CuO is 9, which is obvious and can also be checked by substituting the activity of Cu2+ ions into the equation 14. This equilibrium relationship can be represented by the vertical line 1 (Fig. 2a). The equilibrium activity of Cu2+ ions exceeds the determined value (7.5 x 10-11) in the left region of the line 1 and underruns it in the right region. On the other hand, the redox potential of Cu2+/Cu redox pair with respect to the standard hydrogen electrode can be determined by considering the electromotive force between the following half-cell reactions:

Copper deposition

Cu2++2e=CuE15

Hydrogen generation at a standard state (the activities of proton and hydrogen gas are both 1)

2H++2e=H2E16

The total cell reaction is obtained by subtracting the equation 16 from the equation 15 to erase the electron term.

Cu2++H2=Cu+2H+E17

Figure 2.

Procedure to draw potential–pH diagram at pH 9 and 298 K in a CuO aqueous suspension. Vertical line indicates the equilibrium relationship of an acid-base reaction and horizontal line indicates that of a redox reaction. Diagonal line indicates an equilibrium relationship of the reaction including both an acid-base reaction and a redox reaction. In this procedure, the equilibrium activities of Cu2+ aquo ion was set to be 7.5 x 10-11 considering the following copper species; Cu2+, CuO, Cu2O, and Cu. Oxyanions of copper, HCuO2 − and CuO2 2−, or hydroxyanions of copper, Cu(OH)3 − and Cu(OH)4 2− (Beverskog, 1997), are not considered for simplicity. In order to include such ions, one should consider all the additional possible equilibrium relationships.

The redox potential E T at a temperature T and 1 atm of Cu2+/Cu redox pair is calculated using the following Nernst equation

ET=ΔGTnF=1nF(ΔGT0+RTlnQ)=1nF[(ΔHT0TΔST0)+RTlnQ]=1nF[(ΔH2980+298TΔCPdT)T(ΔS2980+298TΔCPTdT)+RTlnQ]E18

where, n is the number of electrons transferred in the reaction, F is the Faraday constant. Q is the reaction quotient, which is expressed as the following equation 19 for the calculation of the redox potential of Cu2+/Cu redox pair considering that the activities of metallic copper, proton and hydrogen gas in the standard hydrogen electrode are all 1:

Q=aCuaH+2aCu2+aH2=1aCu2+E19

It should be noted that ΔG T is the “total” Gibbs free energy change, including hydrogen oxidation as in the total cell equation 17. When CuO and Cu2+ ions are in equilibrium at pH 9 (the activity of Cu2+ ions is 7.5 x 10-11), the redox potential is calculated to be 0.036 V vs. SHE using the equation 18. This equilibrium relationship is represented by the horizontal line 2 (Fig. 2b). The region above the line is the stability region of Cu2+ ions (with a higher oxidation number +II) and the region below the line is the stability region of Cu (with a lower oxidation number 0).

Equation 10 is a simple acid-base reaction (proton exchange reaction), and a unique equilibrium pH is determined. Similarly, equation 15 is a simple redox reaction (electron exchange reaction), and a unique equilibrium potential is determined. There is also a combination reaction of an acid-base reaction and a redox reaction (proton and electron exchange reaction). In this case, the equilibrium relationship is expressed also by Nernst equation (equation 18), which provides a relational expression between potential E T and pH. In the present system, equilibrium relationships of Cu2+/Cu2O, CuO/Cu2O, and Cu2O/Cu are all categorized as this kind of reaction (proton and electron exchange reaction), corresponding to the diagonal lines 3, 4, and 5 in Fig. 2c, respectively.

After all of the possible equilibrium lines are drawn in the diagram, a part of the equilibrium lines are deleted to leave the common stability regions. Figure 2d is a potential-pH diagram drawn by the above procedure. As can be seen from this procedure, potential-pH diagram can be altered by a set of chemical species and conditions considered, e.g. temperature, activity of ions. Therefore, the selection of chemical species in addition to the activity settings is important and should be done according to an intended purpose: for example, dissolution of chemicals, corrosion proof, electrolysis, and electroless deposition.

3.4. Potential-pH diagrams for Cu and Cu2O nanoparticles formation system

Figure 3 shows potential–pH diagrams drawn at an equilibrium activity of the Cu2+ aquo ion in the presence of abundant CuO at pH 9 in accordance with the procedure written in the section 3.3. The equilibrium activity of Cu2+ aquo ion is determined by considering an equilibrium reaction of Cu2+ and CuO, where the activities of CuO and H+ are assigned to 1 and 10−9, respectively. The species Cu2+, CuO, Cu2O, and Cu are only considered, and oxyanions of copper, such as HCuO2 and CuO2 2−, or hydroxyanions of copper, Cu(OH)3 and Cu(OH)4 2−, are not considered. This is only for simplicity because the redox potentials of CuO/Cu2O and Cu2O/Cu redox pairs at pH 9 are important for the prediction of synthesized chemical species in the present system. For instance, the redox potentials of Cu2O and any Cu(II) ionic species in equilibrium are the same at a constant pressure, pH, and temperature in the presence of abundant solid CuO powder, resulting in the same redox potential of the Cu2O/Cu redox pair. The equilibrium activity of Cu2+ aquo ion changes with pH and therefore, the potential–pH diagram is only valid at the constant pH considered. Fortunately, pH of the solution barely changes during the reaction in the present case, and it is possible to determine the most stable chemical species throughout the reaction by comparing the measured mixed potential to the vertical line of a constant pH (in this case, pH 9) in the potential–pH diagrams. In other words, the kind of chemical species synthesized can be controlled if the mixed potential is changed as expected.

Figure 3.

Potential–pH diagrams drawn at the equilibrium activities of Cu2+ aquo ion at pH 9 and (a) 298, (b) 323, and (c) 353 K considering the species Cu2+, CuO, Cu2O, and Cu. Oxyanions of copper, HCuO2 − and CuO2 2−, or hydroxyanions of copper, Cu(OH)3 − and Cu(OH)4 2−, are not considered for simplicity. These potential–pH diagrams are only valid at the vertical line of pH 9 because the equilibrium activity of Cu2+ aquo ion changes with pH in this system.

Redox potential at pH 9 (V vs. SHE)Redox potential at pH 12 (V vs. SHE)Reaction no.
Partial reaction298 K323 K353 K298 K323 K353 K
N2 + 4H2O + 4e = N2H4 + 4OH−−0.92−0.98−1.06−1.09−1.17−1.27(1)
1/2N2 + NH3 + H2O + e = N2H4 + OH−−2.59−2.72−2.88−2.77−2.91−3.09(2)
Cu(II) + 2e = Cu0.04−0.02−0.08−0.14−0.21−0.29(3)
2Cu(II) + 2OH− + 2e = Cu2O + H2O0.130.070.01−0.05−0.12−0.20(4)
2H2O + 2e = H2 + 2OH−−0.18−0.19−0.21−0.35−0.38−0.42(5)

Table 2.

List of redox potentials calculated for partial reactions considered in this system. Activity of each chemical species is substituted by the actual molar concentration in the present reaction system, and specifically, activities of H2 and NH3 are both substituted by 10−6 to obtain reference values.

3.5. How to control the mixed potential?

As described in the section 3.1, the mixed potential is determined by the balance of each partial current. Therefore, the mixed potential is altered when the redox potential of each partial reaction is changed. The redox potential E T at a temperature T and 1 atm is calculated using the Nernst equation (equation 18). Table 2 shows calculated results of the redox potentials of all the partial reactions considered. Activity of each chemical in the reaction quotient is substituted by the same value as the actual molar concentration of the chemical in the present reaction system, and specifically, both activities of H2 and NH3, which cannot be determined exactly, are substituted by 10−6 to obtain referential values. As shown in Table 2, all the redox potentials shift to the negative direction with increasing both pH and temperature, which can result in a negative shift of the mixed potential. Even the redox potentials of reactions 3 and 4 shift to the negative direction with increasing pH; the former is normally constant with pH and the latter increases with the increase in pH at a constant activity of Cu(II) ions. This is because the equilibrium activity of Cu2+ aquo ion decreases with increasing pH under the coexistence of abundant solid CuO in equilibrium, which brings about the negative shift of the redox potentials of reactions 3 and 4. Thus, possibly the mixed potential is shifted to the negative direction with increasing pH and temperature because the redox potentials of all the partial reactions shift to the negative direction. Consequently, factors to change the mixed potential are pH and temperature, which are easily controllable.

4. Experimental confirmation

Is it actually possible to control oxidation state of nanoparticles by controlling the mixed potential? This query was substantiated through the following experimental procedure.

4.1. Procedure

Reaction solutions were prepared using cupric oxide (CuO) (Kanto Chemical, Inc.), sodium hydroxide (NaOH), hydrazine monohydrate (N2H4 H2O) (Nacalai Tesque, Inc.), and gelatin (Jellice Co. Ltd., P459) as received. All chemicals except for gelatin were of reagent grade. Gelatin was added as a dispersing agent to avoid agglomeration and for the suppression of particle growth. Gelatin blocked oxygen and was also effective in preventing the oxidation of the resulted nanoparticles. Reactions were conducted in a Pyrex beaker 250 cm3 in capacity by the following procedure. First, a CuO colloidal aqueous suspension was prepared by dispersing 0.060 moles of CuO particles in 42.0 cm3 of distilled water using ultrasound. Next, 18.0 cm3 of 10 wt % gelatin aqueous solution was added into the solution as a dispersing agent. The initial pH of the mixed solution was adjusted to the reaction pH (9.0–12.0) at 298 K by 1.0 mol dm−3 sodium hydroxide aqueous solution with a pH meter (Horiba, Ltd., D-21). The temperature of the solution was kept at the reaction temperature (298–353 K) in a water bath with nitrogen gas bubbling (50 cm3 min−1), which started 30 min before the reaction and lasted throughout the reaction to eliminate the effect of dissolved oxygen. The solution was agitated at a rate of 500 rpm with a magnetic stirring unit. Then, 42.0 cm3 of 1.43 mol dm−3 hydrazine aqueous solution was added to 18.0 cm3 of 10 wt % gelatin aqueous solution, and this solution was kept at the reaction temperature (298–353 K) with nitrogen gas bubbling (50 cm3 min−1) for 30 min. The initial pH of the hydrazine solution was adjusted to the reaction pH (9.0–12.0) by 1.0 mol dm−3 sodium hydroxide aqueous solution at 298 K. Next, the hydrazine solution was added to the CuO aqueous suspension as a reducing agent to start the reaction. The total amount of the reaction suspension was 120.0 cm3, and thus the reaction suspension was 0.50 mol dm−3 hydrazine aqueous solution with 0.50 mol dm−3 dispersed CuO. Gelatin was not added in the reaction suspension at 298 K because gelatin became a gel at 298 K, inhibiting the reaction. The crystalline structure of precipitates was investigated by X-ray diffraction (XRD: MAC Science Co., Ltd., M03XHF22) using a molybdenum X-ray tube. The morphology of precipitates was observed using a field-emission scanning electron microscope (JEOL Ltd., JSM-6500F). The immersion potential of Au-sputtered round quartz-crystal substrates 5.0 mm diameter was measured during several experimental runs by a potentiostat/ galvanostat (Hokuto Denko Co., Ltd., HA-151), and it was assumed that the measured immersion potential was almost the same as the mixed potential in reaction suspension in this system. A Ag/AgCl electrode (Horiba, Ltd., 2565A-10T) was used as a reference electrode, and the internal liquid, 3.33 mol dm−3 KCl aqueous solution, was replaced for each experimental run. The measured potential was converted to values vs. SHE using the following empirical equation given by Horiba, Ltd. The potential of the reference electrode could be expressed as a function of temperature T (K) as E (mV) vs. SHE = +206 − 0.7(T – 298).

4.2. Results

In the present method, pH of the reaction suspension is initially adjusted at 298 K, and actual pH at reaction temperatures differs from the adjusted value. This is ascribable to the change in the ionic product for water, K w = [H+][OH]; for example, the value of K w (mol2 dm−6) is 1.008 x 10−14 at 298.15 K and 5.476 x 10−14 at 323.15 K. Figure 4 shows the change with temperature in pH, which is initially adjusted to 9.0 at 298 K. pH linearly decreases with increasing temperature, and the values are 9.0 at 298 K, 8.5 at 323 K, and 7.6 at 353 K. Figure 5 shows the change in the mixed potential during the reaction for 2 h. At the same temperature of 323 K, the mixed potential at pH 10.4 (Fig. 5d) is lower than that at pH 8.5 (Fig. 5b). This agrees well with the discussion in the previous theory section.

Figure 4.

Change in pH of the reaction suspension with temperature; pH of the reaction suspension was initially adjusted to 9.0 at 298 K.

Figure 5.

Mixed potentials measured during the reaction at (a) pH 9.0, 298 K (without gelatin), (b) pH 8.5, 323 K, (c) pH 7.6, 353 K, and (d) pH 10.4, 323 K.

Figure 6.

Potential–pH diagrams drawn at the equilibrium activities of Cu2+ aquo ion at (a) pH 9.0, 298 K, (b) pH 8.5, 323 K, and (c) pH 7.6, 353 K considering the species Cu2+, CuO, Cu2O, and Cu. Bars and circles indicate the range and average value of the measured mixed potential, respectively.

Figure 7.

XRD patterns of precipitates obtained during the reaction at (a) pH 9.0, 298 K (without gelatin), (b) pH 8.5, 323 K, and (c) pH 7.6, 353 K for 2 h.

Moreover, the mixed potential shifts to the negative direction with increasing temperature although pH slightly decreases, indicating that the mixed potential can be lowered just by increasing temperature without fixing pH. By comparing the mixed potential and the potential–pH diagrams shown in Fig. 6, the mixed potential was in the stability region of Cu2O both at pH 9.0, 298 K (Fig. 6a) and pH 8.5, 323 K (Fig. 6b), whereas the mixed potential was in the stability region of metal Cu at pH 7.6, 353 K (Fig. 6c). Figure 7 shows the change with time in XRD patterns of precipitates during the reaction for 2 h. CuO powder was reduced to Cu2O after 1 h at pH 9.0, 298 K although slight Cu peaks are recognized in the XRD pattern taken at 2 h. At pH 7.6, 353 K, CuO powder was completely reduced to metal Cu after 0.5 h. These results are almost consistent with the result that the mixed potentials measured at pH 7.6, 353 K and pH 9.0, 298 K were always in the stability region of Cu and Cu2O, respectively. In contrast, at pH 8.5, 323 K, all CuO powder was reduced to Cu2O after 0.5 h and then the resulting Cu2O was gradually reduced to Cu metal. This is not consistent with the measurement result of the mixed potential. By carefully observing the change in the mixed potential at pH 8.5, 323 K, the initial mixed potential is −0.045 V vs. SHE and in the stability region of Cu2O, and the mixed potential gradually decreases to −0.072 V with reaction time, which is just beside the calculated redox potential of Cu2O/Cu, −0.077 V vs. SHE; i.e., as CuO is reduced to Cu2O, the mixed potential approaches the redox potential of Cu2O/Cu redox pair, where Cu2O and Cu coexist. Nevertheless, the mixed potential is 5 mV higher than the calculated redox potential of Cu2O/Cu and it is difficult to adequately elaborate on the result that the deposition of Cu completely proceeded after 2 h. Here, pH of the solution tends to slightly decrease during the reaction, although ideally, pH would not be changed by taking into account the overall reaction in the present reaction system. For example, pH actually decreased from 8.5 to approximately 8 at 323 K, resulting in a slight increase in the redox potential of a Cu2O/Cu redox pair. The extra pH change is caused by the decrease in the equilibrium concentration of protonated hydrazine N2H5 + due to the decrease in the total amount of hydrazine species by decomposition or oxidization during the reaction. Furthermore, there can be a slight difference between the mixed potential measured using Au electrode and the actual mixed potential in the reaction suspension. Therefore, the actual mixed potential is slightly lower than the redox potential of the Cu2O/Cu redox pair. Nonetheless, a Au electrode is preferable for the measurement of the mixed potential in this reaction system because a Au electrode does not have intense catalytic activity for a specific partial reaction possible in the reaction system, and the effect of the immersion of the Au substrate is extremely low (Iacovangelo, 1991; Iacovangelo & Zarnoch, 1991).

The scanning electron microscopy (SEM) images of the precipitates obtained by the reaction are shown in Fig. 8. Relatively large Cu2O particles with an average diameter of 475 nm are observed in the precipitates obtained after 2 h at pH 9.0, 298 K. These large particles are attributable to the absence of a dispersing agent, gelatin. At pH 8.5, 323 K, Cu2O particles with an average diameter of 97 nm are observed after 0.5 h and Cu particles with an average diameter of 82 nm are observed after 2 h. Cu particles with an average diameter of 55 nm are observed after 2 h at 353 K. As above, the mean particle size is decreased with the increase in temperature because nucleation site increases with the increase in temperature and an inordinate number of nucleation sites at high temperatures leads to the absence of reactant ions (Cu(II) or Cu(I) ions) for the growth.

Figure 8.

SEM images of precipitates obtained by the reaction at (a) pH 9.0, 298 K (without gelatin), (b) pH 8.5, 323 K, (c) pH 7.6, 353 K for 2 h, and (d) pH 8.5, 323 K for 0.5 h.

5. Conclusions

Mixed potential is the most effective indicator of solution circumstances, indicating the most stable chemical species in the reaction solution, i.e., thermodynamic considerations in conjunction with monitoring of mixed potential is useful for the in situ prediction of “what chemical species will be synthesized.” Solution pH and temperature are the factors which affect the mixed potential, and thus, the most stable chemical species can be changed by pH and temperature. Specifically in this system, the mixed potential decreases with the increase both in pH and temperature. Using this concept, the selective synthesis of Cu and Cu2O nanoparticles was demonstrated. This concept is also effective in other reaction systems where thermodynamic data are available. Furthermore in another journal (Yagi et al, 2010), the authors also reported that this concept can be widely applied and helps us to thermodynamically consider even those systems where insufficient or no thermodynamic data are available by experimentally measuring the redox potential with voltammetry combined with quartz crystal microbalance.

Acknowledgments

The author thanks Mr. Shohei Shiomi and Mr. Hidetaka Nakanishi from Kyoto University for their experimental help. The author is also grateful to Professor Tetsu Ichitsubo, Professor Eiichiro Matsubara from Kyoto University, Professor Emeritus Yasuhiro Awakura at Kyoto University, and Professor Takuya Iida from Osaka Prefecture University for fruitful discussions. This research was supported by a grant-in-aid for Knowledge Cluster Initiative (Kyoto Nanotechnology Cluster), Grant-in-Aid for the Global COE Program (International Center for Integrated Research and Advanced Education in Materials Science), and Grant-in-Aid for Young Scientists (B 20760505), all from the Japan Society for the Promotion of Science, Ministry of Education, Culture, Sports, Science and Technology (MEXT) of Japan. This research was also supported by the Kurata Memorial Hitachi Science and Technology Foundation and Shorai Foundation for Science and Technology. The publication cost of this article was assisted by Special Coordination Funds for Promoting Science and Technology commissioned by MEXT of Japan.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Shunsuke Yagi (September 15th 2011). Potential-pH Diagrams for Oxidation-State Control of Nanoparticles Synthesized via Chemical Reduction, Thermodynamics - Physical Chemistry of Aqueous Systems, Juan Carlos Moreno-Piraján, IntechOpen, DOI: 10.5772/21548. Available from:

Embed this chapter on your site Copy to clipboard

<iframe src="http://www.intechopen.com/embed/thermodynamics-physical-chemistry-of-aqueous-systems/potential-ph-diagrams-for-oxidation-state-control-of-nanoparticles-synthesized-via-chemical-reductio" />

Embed this code snippet in the HTML of your website to show this chapter

chapter statistics

4425total chapter downloads

1Crossref citations

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

Related Content

This Book

Next chapter

On the Extremum Properties of Thermodynamic Steady State in Non-Linear Systems

By Gy. Vincze and A. Szasz

Related Book

First chapter

Thermodynamics of Ligand-Protein Interactions: Implications for Molecular Design

By Agnieszka K. Bronowska

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More about us