Open access

Electroreductive Synthesis of Polysilanes with Ordered Sequences

Written By

Manabu Ishifune

Submitted: 17 November 2011 Published: 12 September 2012

DOI: 10.5772/46243

From the Edited Volume

New Polymers for Special Applications

Edited by Ailton De Souza Gomes

Chapter metrics overview

2,855 Chapter Downloads

View Full Metrics

1. Introduction

Polysilanes (Scheme 1) [1] have attracted considerable attention due to their usefulness as the precursors for thermally stable ceramics [2, 3] or a material for microlithography [4, 5], and also due to their potentiality in the preparation of new types of material showing semiconducting, photoconducting, or nonlinear optical property [6-8].

Scheme 1.

In contrast to the growing interest with the polysilane, the method of preparation hitherto known is highly limited. So far, the almost only practical method is the condensation of organodichlorosilane with alkali metal (Wurtz type condensation). This method, however, requires drastic reaction conditions and hence, is very much limited in the type of substituent that is allowed to be located on the monomer. Although several modified or alternative methods such as sonochemical coupling of dichlorosilane promoted by alkali metal [9-11], transition metal catalyzed reaction of hydrosilane [12, 13], anionic polymerization of masked disilene [14, 15], and ring opening polymerization of cyclic organosilane [16, 17] have been proposed, they are not always extensively effective as preparative methods.

The electroreductive coupling of dichlorosilanes with mercury electrode has been reported by Hengge in 1976 as a method to form disilanes [18], though this method was not effective in the preparation of polysilanes [19, 20].

On the other hand, we have recently found that the electroreduction of organic compounds with Mg electrode promotes a variety of unique reactions which can not be attained without using the Mg electrode. The use of Mg electrodes was highly effective to the formation of Si-Si bond and the synthesis of high molecular weight polysilanes [21, 22].

In this chapter, we describe the details of the electroreductive synthesis of high molecular weight polysilane and some types of functionalized polysilanes and also polygermanes, including the additional information about the effects of electrode material and monomer concentration. We also demonstrate that our electroreduction system is successfully applied for the synthesis of the sequence-ordered oligosilanes and polysilanes.

Advertisement

2. Formation of Si-Si bonds by electroreductive coupling of chlorosilanes [21, 22]

The electroreduction of chlorodimethylphenylsilane (1a) was studied as the model reaction (Scheme 2) and carried out under a variety of reaction conditions. In the first place, the cathodic reduction was performed in a divided cell since Si-Si bond is electrochemically oxidized at the potential range 0.7-1.6V vs. SCE. The yield of 1,1,2,2-tetramethyl-1,2-diphenyldisilane (2a) was, however, unexpectedly low under this reaction conditions. In the next place, the idea of using a sacrificial electrode was studied in order to avoid the undesirable anodic oxidation of Si-Si bond in an undivided cell and it was found that the electroreduction of 1a with Mg electrode was highly effective for the formation of Si-Si bond and 2a was obtained in an excellent yield.

The material of electrode is one of the most important factors to control the formation of Si-Si bond (Table 1). When a solution of 1a in dry THF containing LiClO4 as a supporting electrolyte was electrochemically reduced with Mg cathode and anode with a constant current (current density = 30 mA/cm2, supplied electricity = 2.0 F/mol), the coupling product 2a was obtained in 92% isolated yield (entry 1). The results that Pt, carbon, or Zn is not effective electrode in the formation of Si-Si bond (entries 2-4) clearly indicate that Mg plays some important roles in the formation of Si-Si bond. Although details of the role of Mg in the mechanism of formation of Si-Si bond is not always clear at present, the unique reactivity of Mg electrode is undoubtedly shown in this reaction.

The cathodic coupling of other organochlorosilanes was carried out under the optimized reaction condition, that is, Mg cathode and anode were alternated with the interval of 1 min., supporting electrolyte was LiClO4, solvent was THF, and the electricity passed was 2.0 F/mol (Scheme 3). The results summarized in Table 2 show the high potentiality of this method in the synthesis of a variety of disilanes. Moreover, it is remarkable that the extent of contamination with siloxane (Si-O-Si) was less than 2%.

entryanodecathodealternationbyield of 2a, %c
1MgMgyes92
2PtPtyes0
3CCyes0
4ZnZnyestrace
5PtMgno0
6MgPtno93d

Table 1.

Effect of electrode materials in the electroreductive formation of 1,1,2,2-tetramethyl-1,2-diphenyldisilane (2a)a

entrychlorosilanes 1yield of 2, %a
R1R2R3
11bMeMeMe2b82
21cMePhPh2c77
31dPhPhPh2d85

Table 2.

Electroreductive synthesis of disilanes 2

Two types of mechanism may be proposed to this electroreductive Si-Si bond forming reaction. The first prosible mechanism is a radical coupling in which a silyl radical formed by one electron reduction of the starting chlorosilane couples with another silyl radical to give the disilane. In the second mechanism, two-electron reduction of the chlorosilane yields an active species equivalent to silyl anion which reacts with chlorosilane to give a dimer. In order to have an insight into the mechanism, the products obtained in the mixed system of chlorotrimethylsilane (1b) and chlorotriphenylsilane (1d) (1b : 1d = 1 : 1) were studied in detail (Scheme 4). The resulting products were 1 : 1 mixture of the mixed coupling product (2e) and the homocoupling product of 1d (hexaphenyldisilane (2d)), whereas the homocoupling product of 1b, hexamethyldisilane (2b) was not found in the products at all. This result seems to agree with the anionic mechanism. That is, 1d is first reduced to triphenylsilyl anion that reacts with 1b and 1d to afford disilanes 2e and 2d respectively. The electrophilicity of chlorosilanes 1b and 1d are high enough to be attacked equally by the triphenylsilyl anion at the half conversion (supplied electricity = 1 F/mol based on the total amount of 1b and 1d). In the radical mechanism, however, if only 1d is reduced to yield a radical, the formation of 2e is not reasonable, whereas if two types of radical are formed by the reduction of both 1b and 1d, the absence of 2b in the products is unreasonable. Thus, the anionic mechanism is the most reasonable in this coupling reaction. The fact that the reduction potential of 1d is much more positive than that of 1b also supports the above mentioned reaction mechanism.

Advertisement

3. Stepwise synthesis of oligosilanes [22, 23]

This method is also applicable to the synthesis of trisilanes and tetrasilanes. For example, the electroreductive cross coupling of organodichlorosilanes (3) with chlorotrimethylsilane (1b) (5 equivalent to 3) gave the corresponding trisilanes 4 in moderate to good material yields (Scheme 5) and that of 1,2-dichloro-1,1,2-trimethyl-2-phenyldisilane (5) and 1b (5 equivalent to 5) gave tetrasilane 6 in 55% yield (Scheme 6). Trisilane 4c is a key intermediate for the photochemical synthesis of tetramesityldisilene which is known as an isolable disilene.

The mildness of the reaction conditions of this electroreductive method is favorable for the synthesis of oligosilanes having various functionalities such as Si-H bonds which are known to be reactive under radical or anionic condition. The electroreductive cross-coupling reaction of chlorodimethylsilane (7) with dichlorodiphenylsilane (3b), in fact, gave the corresponding trisilane 8 (Scheme 7). The Si-H bond was readily transformed to the Si-Cl bond by the treatment with catalytic amount of benzoylperoxide in carbontetrachloride. Using this method 1,3-dihydro-1,1,3,3-tetramethyl-2,2-diphenyltrisilane (8) was transformed to the corresponding chloride 9 (Scheme 7). The further electroreduction of 1,3-dichloro-1,1,3,3-tetramethyl-2,2-diphenyltrisilane (9) with chlorodimethylsilane (7) gave the corresponding pentasilane 10 (Scheme 8), and these sequences were utilized for the synthesis of the odd-numbered oligosilanes. In the same manner, the even-numbered oligosilanes can be prepared. For instance, 1,4-dichloro-1,1,2,3,3,4,4-heptamethyl-2-phenyltetrasilane (11) can be prepared by the reaction between 7 and 1,2-dichloro-1,1,2-trimethyl-1-phenyldisilane (5) (Scheme 9). Accordingly, the electroreductive cross-coupling reactions followed by the chlorination provided a powerful method for the stepwise elongation of Si-Si bonds and synthesis of sequence-controlled oligosilanes.

Scheme 7.

Scheme 9.

Advertisement

4. Electroreductive polymerization of dichloromethylphenylsilane [22]

Electroreduction of dichloromethylphenylsilane (3a) (Scheme 10) carried out under the above mentioned reaction conditions gave polymethylphenylsilane (13) in low yield (Table 3, entries 1, 2). The sonication of ultrasound was found to be necessary for the electroreductive polymerization of 3a (entry 3). The low yield of 13 may be explained by the difficulty of keeping the electric current in a suitable level due to the increase of the terminal voltage with progress of the reaction. This difficulty was overcome by the alternation of anode and cathode with a suitable interval (15 sec., Table 3, entry 4) and the material yield of 13 was remarkably improved.

entryalternationcsonicationdMneMw/Mneyield of 13, %f, g
1nono---
2yesno40001.47
3noyes39001.417
4yesyes52001.543

Table 3.

Electroreductive synthesis of poly(methylphenylsilane) (13)a, b

Mg is a remarkably effective material of electrode also for the formation of 13 (Table 4), whereas Al gave low yield (entry 4) and other materials such as Cu and Ni were rather ineffective (entries 2, 3). The electroreduction systems using Al or Cu anode in other electrolytes (Al anode/Bu4NCl/DME [24], Al anode/LiCl/THF-HMPT [25], or Cu/Bu4NClO4/DME [26]) have been also reported, however, the molecular weight of the resulting polysilanes is relatively low. Other than Mg electrodes, the use of Ag anode and Pt cathode in DME containing Bu4NCLO4 is also reported to be effective to obtain high molecular weight polysilane [27, 28].

entryelectrode materialsMnbMw/Mnbyield of 13, %c, d
1Mg52001.543
2Cu7001.1-e
3Ni6401.1-e
4Al47001.515

Table 4.

Effect of electrode materials in the electroreductive synthesis of poly(methylphenylsilane) (13)

The effect of monomer concentration was investigated in order to obtain high molecular weight polysilane (Table 5). The molecular weight of 13 becomes higher with the increase in the concentration of 3a. The molecular weight (Mn) of 13 was, for instance, 31,000 when the electroreduction of 3a was carried out under high concentration condition (1.2 mol/L) at 0.5 F/mol of supplied electricity though the material yield of 13 decreased.

The most satisfactory result, in which material yield was 79 % and molecular weight (Mn) was 9900, was obtained when the concentration of 3a was 0.67 mol/L (entry 2). The polysilane 13 obtained here showed relatively sharp monomodal distribution of molecular weight in the elution profile of GPC, whereas the polysilanes prepared by the alkali metal condensation method usually showed broad bimodal distribution.

entrymonomer 3a, mol/Lsupplied electricity, F/molMnbMw/Mnbyield of 13, %c, d
10.334.052001.543
20.674.099002.179
32.52.2180002.143
46.30.8190002.815
5120.5310001.88

Table 5.

Effect of monomer concentration in the electroreductive synthesis of 13a

The mechanism of electroreductive formation of polysilane is not always perfectly clear, though the initial step of reaction is obviously the reduction of 3a to a silyl anion species 14. Two types of reaction patterns may be proposable to the propagation step. In the first case, the reaction of 14 with 3a gives a dimer that yields trimer, tetramer, and finally polymer upon repeated reaction with 14 (Scheme 11). In another pattern of the propagation, the oligomers such as dimer, trimer, and the like 15 are reduced to give the oligomeric active species, which then react with oligomer 15 or 3a to give finally polymer. (Scheme 12). Although it is not always possible to specify the extent of contribution of each pattern to the propagation step, the former reaction probably proceeds mainly, since the electrochemical reduction of oligomeric silyl chloride 15 may be rather difficult when it is analogized with the electroreduction of long chain alkyl chlorides.

Advertisement

5. Electroreductive synthesis of functionalized polysilanes [29]

The mildness of the polymerization conditions of the electroreductive method is favorable for the synthesis of the polysilanes having a variety of hydroxyl-related functional groups. The electroreduction of a mixture of 3a and the dichlorosilanes having protected hydoxyphenyl groups (3d-g) with Mg electrode afforded the corresponding copolymers 16 (16d-g, Scheme 13), and the deprotection of the resulting copolymers gave the polysilanes having hydroxyl groups. The reactivity of 3d-g highly depends on the type of protecting group (Table 6). Homopolymerization of 3g, for example, gave 16g (entry 10), whereas other monomers did not afford polymers but oligomeric compounds (entries 3, 5, 8).

The modification or the property of polysilane must be achieved by using the hydroxyl group located on the polymer 16d as a key functional group. The deprotection of the methoxymethyl group of 16d (Table 6, entry 1) with 10%HCl aqueous solution followed by the reaction with hexamethylene diisocyanate resulted in a remarkable increase in the molecular weight with indicating the linkage of the polymer chain (Scheme 14).

entrycharged mol% of 3d-gbyield of 16, %c, dMneMw/Mne
17 (3d)79 (7)99001.9
210 (3d)57 (12)69001.7
3100 (3d)28 (100)11001.2
410 (3e)36 (11)61001.5
5100 (3e)-f (100)11001.2
610 (3f)50 (6)45001.3
750 (3f)22 (46)46001.3
8100 (3f)-f (100)17001.3
910 (3g)56 (17)46001.3
10100 (3g)57 (100)40001.1

Table 6.

Electroreductive synthesis of functionalized polysilanesa

Advertisement

6. Electroreductive Polymerization of Dichlorooligosilanes [23]

The electroreductive polymerization of the dichlorooligosilanes is highly promising for the synthesis of sequence-ordered polysilanes. The electroreduction of dicholodisilane 5 was found to give the corresponding polysilane 18 consisting of disilane units (Scheme 15). The electroreductive polymerization was carried out under a variety of reaction conditions, however, the yield of the resulting polymer was very low (Table 7). It is probably due to high reactivity of the disilene intermediate formed by the electroreduction of 5. In fact, the addition of naphthalene, which could make a masked disilene intermediate, into the reaction system slightly increased the yield of the polysilane 18 (entry 6).

entrydichlorosilane 5, mol/Lsupplied electricity, F/molpolysilane 18
MnbMw/Mnbyield, %c
10.11429002.72.7
20.33436002.32.7
30.67421002.91.0
40.33228002.73.9
50.33630003.01.0
6c0.33425001.813.0

Table 7.

Electroreduction polymerization of dichlorosilane 5a

Dichlorooligosilanes, such as dichlorotrisilane 9 was found to be good monomers for the electroreductive synthesis of the polysilanes having longer sequence units (Schemes 16). The temperature control is found to be very important in the electroreductive polymerization of 9 (Table 8). The reaction at higher temperature, the backbiting reaction of the propagating polymer proceeded forming cyclohexasilane as a by-product (entry 1). This side reaction was successfully suppressed when the reaction was carried out below 0°C, and polysilanes 19 having relatively high molecular weight were obtained (entries 3, 4). In the optimized reaction conditions, the electroreduction of dichlorotetrasilane 12 gave the corresponding polysilane 20, units of which were ordered in four sequences in satisfactory yield (Scheme 17). The polymerizability of dichlorooligosilanes under the electroreduction conditions seems to be mainly affected by the substituents on the chlorinated terminal silicon atom, and this fact provides a wide possibility to design the oligosilane sequences of the inner silicon atoms.

entrypolymerization temperature, °CMnbMw/Mnbyield of 19, %c
11838001.44(42)d
2047001.8750
3-1055001.5435
4-1544001.4216

Table 8.

Electroreductive polymerization of dichlorosilane 9a

Advertisement

7. Electroreductive polymerization of dichlorosilanes in the presence of disilane additives [30]

The disilane additives, which are generated in situ in electroreductive coupling of the corresponding chlorosilanes, were found to be effective to the promotion of the electroreductive polymerization of dichloromethylphenylsilane (3a) and the control of the molecular weight distribution of the resulting polysilanes (Scheme 18, Table 9). The electroreduction of dichlorosilane 3a in the presence of 1,1,1-trimethyl-2,2,2-triphenyldisilane gives the corresponding polysilane 13 in 56% yield, and the number average molecular weight and the molecular weight distribution are determined by GPC to be 3000, and 1.10 respectively (Table 9, entry 3). The reduction of dichloromethylphenylsilane (3a) by Wurtz type condensation using metal lithium in the presence of catalytic amount 1,1,1-trimethyl-2,2,2-triphenyldisilane affords five- and six-members ring products [31]. On the other hand, the cyclosilanes are not detected under the electroreductive conditions. The use of 1,1,12,2,2-hexaphenyldisilane affords the polysilane 13 in 59% yield, and the Mw/Mn is 1.08 (entry 4). Thus, the polysilanes prepared in the presence of the disilane additive containing triphenylsilyl group show narrower molecular weight distributions than the polysilane prepared without the disilane additive.

The mechanism for the triphenylsilyl substituted disilane to control the electroreductive polymerization suggested is as follows (Scheme 19). The electroreductively generated reactive silyl anion species at the terminus of the propagating polymer is trapped with the disilane forming a relatively stable triphenylsilyl anion and inhibits the undesirable side reactions such as backbiting reaction. The triphenylsilyl anion attacks as a nucleophile to the chlorinated silicon atom at the terminal of the propagating polymer to give the

Scheme 18.

entrydisilane additivesbMncMw/Mncyield of 2a, %d
1-32001.6538
2Me3SiSiMe337001.3954
3Me3SiSiPh330001.1056
4Ph3SiSiPh326001.0859

Table 9.

Electroreductive polymerizartion of dichlomethylphenylsilane (3a) in the presence of disilane additivesa

triphenylsilyl group terminated polysilane. The resulting polysilane is isolable but does not lose its polymerizability completely since the triphenylsilyl group at the terminal position acts as an activator, that is, it probably reacts as a macroinitiator.

Scheme 19.

Advertisement

8. Electroreductive block copolymerization using triphenylsilyl group-terminated polysilane [32]

The triphenylsilyl group terminated polysilanes have been synthesized by the electroreductive polymerization of dichloromethylphenylsilane (3a) in the presence of the electroreductively prepared disilane additives 2. The electroreductive termination with chlorotriphenylsilane (1d) was carried out to ensure the terminus of the resulting polysilane for triphenylsilyl group. The polysilanes were obtained as white powders in 15-32% yields after reprecipitation from benzene-ethanol, and the number average molecular weights were estimated by GPC to be 3000-3740 (Table 10). By using the isolated triphenylsilyl group-terminated poly(methylphenylsilane) 13 as a macroinitiator, the electroreductive polymerization of dibutyldichlorosilane (3h) was carried out (Scheme 20, Table 10). Under these conditions dichlorsilane 3h was first electroreduced to form the corresponding oligomeric silyl anion. Electroreductive copolymerization was found to proceed by the attack of the oligomeric silyl anion to triphenylsilyl group-terminated polysilane 13 and further electroreductive condensation with dichlorosilane 3h affording the corresponding copolymer, polymethylphenylsilane-block-polydibutylsilane (21), in 16-38% yields depending on the disilane additives (entries 1-3). The molecular weight of the copolymer obtained from the polysilane 13 (Mn = 3350) was 4730 (entry 3). The GPC profiles of the resulting copolymers 21 were monomodal and the polydispersity index values (Mw/Mn) were 1.2-1.4. The repeat unit ratio (-Si(Me)Ph- : -SiBu2-) of the resulting copolymer 21 (entry 3) was 75 : 25, which showed a good agreement with the calculated ratio (74 : 26).

Scheme 20.

Polydibutylsilane-block-polymethylphenylsilane (21’) was also obtained by using triphenylsilyl group-terminated polydibutylsilane (22) as a macroinitiator (Scheme 21). The electroreductive polymerization of dibutyldichlorosilane (3h) in the presence of the disilane 2d followed by electroreductive termination with chlorotriphenylsilane (1d) afforded the macroinitiator 22 (Mn = 3950, Mw/Mn = 1.7). The electroreductive polymerization of dichloromethylphenylsilane (3a) was found to initiate from 22 producing the corresponding copolymer 21’ in 25% yield, and the molecular weight of 21’ was 4390 (Scheme 21). The polydispersity index values (Mw/Mn) was 1.3, and the repeat unit ratio (-SiBu2- : -Si(Me)Ph-) was 61 : 39.

entrypreparation of
the macroinitiator 13a
polymethylphenylsilane-block-polydibutylsilane (21)b
disilane additivesMncMw/MncMncMw/Mncm : nyield, %f
observeddcalculatede
1Me3SiSiMe337401.955301.483 : 1770 : 3016
2Me3SiSiPh330001.340801.466 : 3477 : 2328
3Ph3SiSiPh333501.447301.275 : 2574 : 2638

Table 10.

Electroreductive block copolymerization with dibutyldichlorosilane (3h) using triphenylsilyl group-terminated poly(methylphenylsilane) (13) as a macroinitiator

Scheme 21.

The UV absorption spectra of the resulting polysilane 21 (entry 3, Table 10) was compared with those of poly(methylphenylsilane) (Mn = 3350, Mw/Mn = 1.4), poly(dibutylsilane) (Mn = 3950, Mw/Mn = 1.7), and poly(methylphenylsilane-co-dibutylsilane) (random copolymer) (Figure). Poly(methylphenylsilane) showed a π-π* band at 271 nm (εmax = 4831) and a σ-σ* band at 326 nm (εmax = 4766) at 4°C (Figure (a)). Poly(methylphenylsilane) (Mw = 9000) prepared by Wurtz coupling under sonication was reported to show a σ-σ* band at 332 nm (εmax = 4100) [33]. The λmax value of the electroreductively prepared poly(methyphenylsilane) was a little shorter and it is probably due to relatively lower molecular weight. In fact Wurtz coupling-synthesized poly(methylphenylsilane) having 5000 of Mw showed a σ-σ* band at 328 nm [34]. Poly(dibutylsilane) showed only a σ-σ* band at 309 nm, and the εmax value (9611) was two times higher than that of poly(methylphenylsilane) (Figure (b)). The UV absorption spectrum of the helical form of poly(di-n-alkylsilane)s is typically centered near 315 nm, while the more planar conformation is typically centered at 375 nm [35, 36]. Poly(dibutylsilane) obtained in this study showed the λmax value corresponding to helical backbone conformation. The εmax of the σ-σ* band of poly(methylphenylsilane) was observed to decrease with an increase in temperature [5]. The UV spectra of copolymer 5 showed a π-π* band at 273 nm (εmax = 2723) and a σ-σ* band at 306 nm (εmax = 2949) (Figure (d)), while the random copolymer showed a π-π* band at 272 nm (εmax = 2438) and a σ-σ* band at 309 nm (εmax = 2065) (Figure (c)). The εmax value of the σ-σ* band of copolymer 21 was higher than that of the random copolymer, and less temperature dependence of εmax was observed in the spectrum of copolymer 21. These results indicate that copolymer 21 has long sequences of dibutylsilylene units, that is, block structure.

Figure 1.

UV absorption spectra of (a) poly(methylphenylsilane) (Mn = 3350, Mw/Mn = 1.4), (b) poly(dibutylsilane) (Mn = 3950, Mw/Mn = 1.7), (c) poly(methylphenylsilane-co-dibutylsilane) (Mn = 4340, Mw/Mn = 1.5, -Si(Me)Ph- : -SiBu2- = 67 : 33), and (d) poly(methylphenylsilane)-block-poly(dibutylsilane) (Mn = 4080, Mw/Mn = 1.4, -Si(Me)Ph- : -SiBu2- = 66 : 34) in THF at 0, 10, 20, 25, and 30°C.

Advertisement

9. Conclusion

The formation of Si-Si bonds was achievable by the electroreductive condensation of organochlorosilanes with Mg sacrificial electrode. Disilanes, trisilanes, and tetrasilanes were readily obtained in good to moderate yield. Moreover, this method was also remarkably effective to the synthesis of polysilanes. The molecular weight and yield of the polymers was controlled by the concentration of monomers and the supplied electricity. The mildness of the reaction conditions allowed to use a wide variety of monomers, and enabled the synthesis of the functionalized polysilanes and the structure-controlled polysilanes. The electroreductive polymerization of the dichlorooligosilanes was highly useful for the synthesis of sequence-ordered polysilanes. Moreover, this electroreductive method also provided a new procedure to synthesize well-controlled di-block polysilane copolymers. Since the present electroreductive polymerization requires only a single compartment cell, it is undoubtedly one of the simplest and most powerful tools for synthesis of polysilanes.

References

  1. 1. WestR.1986The polysilane high polymersJ. Organomet. Chem. 300(1-2): 327 EOF346 EOF
  2. 2. YajimaS.HasegawaY.HayashiJ.IimuraM.1978Synthesis of continuous silicon carbide fiber with high tensile strength and high Young’s modulusPart 1. Synthesis of polycarbosilane as precursor. J. Mater. Sci. 131225692576
  3. 3. HasegawaY.OkamuraK.1985Silicon carbide-carbon composite materials synthesized by pyrolysis of polycarbosilane. J. Mater. Sci. Lett. 433568
  4. 4. MillerR. D.WillsonC. G.WallroffG. M.ClecakN.SooriyakumaranR.MichlJ.KaratsuT.Mc KinleyA. J.KlingensmithK. A.DowningJ.1989Polysilanes: photochemistry and deep-UV lithography. Polym Eng Sci 2913882886
  5. 5. MillerR. D.MichlJ.1989Polysilane high polymers. Chem. Rev. 89613591410
  6. 6. WestR.DavidL. D.DjurovichP. I.StearleyK. L.SrinivasanK. S. V.YuH.1981Phenylmethylpolysilanes: formable silane copolymers with potential semiconducting propertiesJ. Am. Chem. Soc. 1032473527354
  7. 7. Kepler RG, Zeigler JM, Harrah LA, Kurtz SR1987Photocarrier generation and transport in σ-bonded polysilanes. Phys. Rev. B 35628182822
  8. 8. BaumertJ. C.BjorklundG. C.JundtD. H.JurichM. C.LooserH.MillerR. D.RaboltJ.SoorijakumaranR.JDSwalenTwing. R. J.1988Temperature dependence of the third-order nonlinear optical susceptibilities in polysilanes and polygermanes. Appl. Phys. Lett. 531311471149
  9. 9. MatyjaszewskiK.GresztaD.HrkachJ. S.KimH. K.1995Sonochemical synthesis of polysilylenes by reductive coupling of disubstituted dichlorosilanes with alkali metalsMacromolecules 2815972
  10. 10. Jones RD, Holder SJ2006High-yield controlled syntheses of polysilanes by the Wurtz-type reductive coupling reactionPolym. Int. 557711718
  11. 11. KoeJ.2008Contemporary polysilane synthesis and functionalisationPolym. Int. 583255260
  12. 12. Tilley TD1993The coordination polymerization of silanes to polysilanes by a " σ-bond metathesis" mechanism. Implications for linear chain growth. Acc. Chem. Res. 2612229
  13. 13. MinatoM.MatsumotoT.IchikawaM.ItoT.2003Dehydropolymerization of arylsilanes catalyzed by a novel silylmolybdenum complex.Chem. Commun. (24): 2968 EOF9 EOF
  14. 14. SanjiT.KawabataK.SakuraiH.2000Alkoxide initiation of anionic polymerization of masked disilenes to polysilanesJ. Organomet. Chem. 611(1-2): 32 EOF
  15. 15. SanjiT.IsozakiS.YoshidaM.SakamotoK.SakuraiH.2003Functional transformation of poly(dialkylaminotrimethyldisilene) prepared by anionic polymeriztion of the masked disilenes. The preparation of a true polysilastyrene. J. Organomet. Chem. 685 (1-2): 65-69.
  16. 16. CyprykM.GuptaY.MatyjaszewskiK.1991Anionic ring-opening polymerization of 1,2,3,4-tetramethyl-1,2,3,4-tetraphenylcyclotetrasilaneJ. Am. Chem. Soc. 113310467
  17. 17. SuzukiM.KotaniJ.GyobuS.KanekoT.SaegusaT.1994Synthesis of sequence-ordered polysilane by anionic ring-opening polymerization of phenylnonamethylcyclo-pentasilane. Macromolecules 27823602363
  18. 18. HenggeE.LitscherG.1976A new electrochemical method for the formation of silicon-silicon bonds. Angew] Chem] 88(12): 414.
  19. 19. HenggeE.LitscherG.1978Electrochemical formation of di-, oligo- and polysilanes. Monatsh. Chem. 109512171225
  20. 20. HenggeE.FirgoH.1981An electrochemical method for the synthesis of silicon-silicon bonds. J. Organomet. Chem. 2122155161
  21. 21. ShonoT.KashimuraS.IshifuneM.NishidaR.1990Electroreductive formation of polysilanesJ. Chem. Soc. Chem. Commun. (17): 1160 EOF
  22. 22. KashimuraS.IshifuneM.YamashitaN.BuH. B.TakebayashiM.KitajimaS.YoshiharaD.KataokaY.NishidaR.KawasakiS.MuraseH.ShonoT.1999Electroreductive synthesis of polysilanes, polygermanes, and related polymers with magnesium electrodes. J. Org. Chem. 641866156621
  23. 23. IshifuneM.KashimuraS.KogaiY.FukuharaY.KatoT.BuH. B.YamashitaN.MuraiY.MuraseH.NishidaR.2000Electroreductive synthesis of oligosilanes and polysilanes with ordered sequences. J. Organomet. Chem. 611(1-2): 26-31.
  24. 24. UmezawaM.TakedaM.IchikawaH.IshikawaT.KoizumiT.NonakaT.1991Electroreductive polymerization of mixtures of chloromonosilanes. Electrochim. Acta 36(3-4): 621-624.
  25. 25. BiranC.BordeauM.PonsP.LegerM. P.DunoguesJ.1990Electrosynthesis, a convenient route to di- and polysilanes. J. Organomet. Chem. 382 (3): C17C20.
  26. 26. KunaiA.KawakamiT.ToyodaE.IshikawaM. (1991) Electrochemistry of organosilicon compounds. 2. Synthesis of polysilane oligomers by a copper electrode system. Organometallics 10 6 20012003 .
  27. 27. OkanoM.TakedaK.ToriumiT.HamanoH.1998Electrochemical synthesis of polygermanesElectrochim. Acta 444659666
  28. 28. YamadaK.OkanoM.2006Electrochemical synthesis of poly(cyclotetramethylene-silylene) Electrochemistry 748668671
  29. 29. KashimuraS.IshifuneM.BuH. B.TakebayashiM.KitajimaS.YoshiharaD.NishidaR.KawasakiS.MuraseH.ShonoT.1997Electroorganic chemistry. 153. Electroreductive synthesis of some functionalized polysilanes and related polymers. Tetrahedron Lett. 382646074610
  30. 30. IshifuneM.KogaiY.UchidaK.2005Effect of disilane additives on the electroreductive polymerization of organodichlorosilanesJ. Macromol. Sci. Part A Pure and Appl. Chem. 427921929
  31. 31. ChenS. M.DavidL. D.HallerK. J.WadsworthC. L.WestR.1983Isomers of (PhMeSi)6 and (PhMeSi)5 Organometallics 23409414
  32. 32. IshifuneM.SanaC.AndoM.TsuyamaY.2011Electroreductive block copolymerization of dichlorosilanes in the presence of disilane additivesPolym. Int. 60812081214
  33. 33. TerunumaD.NagumoK.KamataN.MatsuokaK.KuzuharaH.2000Preparation and characterization of water-soluble polysilanes bearing chiral pendant ammonium moietiesPolymer Journal 32113117
  34. 34. HerzogU.WestR.1999Hererosubstituted polysilanes. Macromolecules 3222102214
  35. 35. HuZ.ZhangF.HuangH.ZhangM.HeT.2004Morphology and structure of poly(di-n-butylsilane) single crystals prepared by controlling kinetic process of solvent evaporation. Macromolecules 3733103318
  36. 36. ChunwachirasiriW.KanaglekarI.MJWinokurKoe. J. C.WestR.2001Structure and chain conformation in poly(methyl-n-alkyl)silanes. Macromolecules 3467196726

Written By

Manabu Ishifune

Submitted: 17 November 2011 Published: 12 September 2012