Variation of film thicknesses d (nm) with solution viscosity.
1. Introduction
Sol–gel process [1-3] is an attractive alternative to other methods for synthesis of ceramics and glasses for many reasons: for example, low temperature synthesis, simple equipment’s to be used, thin film formability and so on. Particularly, sol–gel process is very useful for thin film deposition because of the capability to coat materials of various shapes and/or large area, to control the composition easily for obtaining solutions of homogeneity and controlled concentration without using expensive equipment.
Historically, metal alkoxides have been employed in sol–gel process, which readily undergo catalyzed hydrolysis and condensation to form nanoscale oxide or hydroxide particles. Still in general, metal alkoxides are often used as raw materials in sol–gel process, but many of the alkoxides are very difficult to be obtained because of the high sensitivity to the atmospheric moisture [4-9]. In ordinary sol–gel processing, starting compositions as well as reaction conditions are selected so as to maintain the mixture in a homogeneous state throughout the processes including mixing of starting compounds, gelation, aging, drying and heat-treatment.
Titanium and zirconium oxides are very promising candidates for future technology of thin layers because of their interesting mechanical, thermal and chemical properties. Titanium oxide (TiO2) is a cheap, non-toxic, and non-biodegradable material, besides their widely uses in various industries [10]. Moreover, it is a semiconductor under the form of thin films. Its insensitivity to visible light due to its band gap (3.2 eV) enables it to absorb in the near ultraviolet region [11], even though its low efficiency. Hence, it can be sensitized by a great number of dyes; some of them allow a conversion rate incident photon–electron approaching unity. Thus, these various applications arouse great interest in the study of titanium oxide thin films. The significant uses of TiO2 thin films are in solar cells [12], photo-catalytic [13] and electro-chromic systems [14], in other words, they are mainly found their use in optics.
TiO2 thin films are extensively studied because of their interesting chemical, electrical and optical properties [15,16]. TiO2 film in anatase phase could accomplish the photocatalytic degradation of organic compounds under the radiation of UV. So, it has a variety of application prospects in the field of environmental protection [17,18]. TiO2 thin film in rutile phase is known as a good blood compatibility material and can be used as artificial heart valves [19]. In addition, TiO2 films are important optical films due to their high reflective index and transparency over a wide spectral range [16].
During the two last decades, several methods have been used for the TiO2 thin films preparation, such as chemical vapor deposition [20], chemical spray pyrolysis [21], pulsed laser deposition [22] and sol–gel method [23]. In comparison with other methods, the sol–gel method has some advantages such as controllability, reliability, reproducibility and can be selected for the preparation of nano-structured thin films [23,24]. Sol–gel coating has been classified as two different methods such as dip and spin coating.
The dip-coating has considerably been used for preparation TiO2 nanostructured thin films [25–27]. Experimental results have shown that the preparation of high transparent TiO2 thin film by dip-coating method needs to control morphology, thickness of the film and the anatase-brookite-rutile phase transformation [26,28].
Additions of another semiconductor have been used to improve the properties of titanium dioxide. In principle, the coupling of different semiconductor oxides seems useful in order to achieve a higher photocatalytic activity [29]. Various composites formed by TiO2 and other inorganic oxides such as SiO2 [30], ZrO2 [31] SnO2 [32], Cu2O [33], MgO [34], WO3 [35], In2O3 [36], ZnO [37], MoO3 [38], CdS [39], PbS [40], and so on, have been reported.
Zirconium oxide (ZrO2) has good dielectric and optical properties [41,42] it has a high refraction index [43]. Additionally, it has a very good transparency on a broad spectral field [44], a great chemical stability and a threshold of resistance to high laser flow. All these properties led to miscellaneous applications such as optical filters, laser mirrors [45] or barriers layers from the heat [46]. ZrO2 films are also employed as plug layer for super-conducting ceramics [47,48], like biomaterial for prostheses [49,50], as gas sensor [51] or like component in combustible batteries [52]. Basically, ZrO2 itself is an insulating direct wide gap metal oxide, with an optical band gap in the range 5.0-5.85 eV [53].
The aim of the present work is to investigate the transformation behaviors and the effect; of a smaller ratio range of ZrO2; doping on the surface area of TiO2 thin films, light absorption, band gap energy, variations of crystal granularity, phase composition and especially on the evolution of the crystallite size and defects concentration with annealing treatments (heat treatments) and layers thickness of the samples produced. So that in this chapter, we report the study of structural, thermal and optical properties of ZrO2-doped TiO2 thin films deposited by the sol–gel process. Several experimental techniques were used to characterize structural and optical properties resulting from different annealing treatments and different layer thicknesses: X-ray powder diffraction, Fourier transforms infrared (FTIR), Raman spectroscopy, Scanning electron microscopy (SEM), differential scanning calorimetric (DSC), Scanning electron microscopy (SEM), the energy dispersive X-ray spectrometry (EDX) and UV spectroscopy.
To obtain nanomaterial’s with controlled properties, it is most often involves the use of mineral additives (dyes, semiconductors, metal particles, rare earth, etc.) in small quantities. These additions can promote densification or control the phenomenon of grain growth, or to change the structural, physical and optical properties. So the presence of impurities in a matrix can stabilize, improve or modify the various properties of a material. Generally, thin layers of doped TiO2 give hope of significant performance gains and new applications.
2. Experiments
Our 5% ZrO2-doped TiO2, thin films were prepared by dip coating, in three steps. The first step: the dissolution of 1 mol of butanol (C4H9OH) as solvent, 4 mol of acetic acid (C2H4O2), 1mol of distilled water and 1 mol of tetrabutylorthotitanate (C4H9O)4Ti. In the second step, the solution of ZrO2 was prepared from the dissolution of 1 mol of zirconium oxychloride salt (ZrOCl2•8H2O) in distilled water and 2 mol of ethanol (95%) as catalyst. Finally, the solution of TiO2 was doped with ZrO2. Then, the resultant yellowish transparent solutions were ready for use. The substrates were dip-coated in the solutions at a constant rate of 6.25 cm.s-1. After each dipping, thin films were dried for 30 min at a distance of 40 cm from a 500 W light source. The drying temperature of the light source is approximately equal to 100 °C. Subsequently, thin films were heat treated in the temperature range 350–450 °C, with a temperature increase rate of 5°C.min-1, for 2 h in the furnace. The powders obtained from the xerogel were prepared in room temperature and under air atmosphere.
After each dipping, the thin films were dried for 30 min, at a distance of 40 cm from a 500 Wight source. The drying temperature of the light source is approximately equal to 100 °C. Subsequently, thin films were heat treated in the temperature range 350–450 °C, with a temperature increase rate of 5 °C min-1, for 2 h in the furnace. The powders obtained from the xerogel were prepared with an annealing till three months in room temperature and under air atmosphere.
To investigate the transformation behaviors and the effect; of a smaller ratio range of ZrO2; doping on the surface area of TiO2 thin films, light absorption, band gap energy, variations of crystal granularity, phase composition and especially on the evolution of the crystallite size and defects concentration with annealing treatments (heat treatments) and layers thickness of the samples produced.
So that in this chapter, we report the study of structural, thermal and optical properties of ZrO2-doped TiO2 thin films deposited by the sol–gel process.
Several experimental techniques were used to characterize structural and optical properties resulting from different annealing treatments and different layer thicknesses: X-ray powder and films diffraction, Fourier transforms infrared (FTIR), Scanning electron microscopy (SEM), Raman spectroscopy, differential scanning calorimetric (DSC), Scanning electron microscopy (SEM), the energy dispersive X-ray spectrometry (EDX) and UV spectroscopy.
To determine the transformation points, the obtained powdered xerogels were analyzed by Differential Scanning Calorimetry (DSC) using a SETARAM DSC–92 analyzer equipped with a processor and a measuring cell. The thermal cycle applied consists of heating from room temperature to 520°C, holding for 5min at this temperature and finally cooling back to room temperature with the same rate (5°C/min). X-ray powder diffraction was performed by Siemens D5005 diffractometer using a Cu Kα1 radiation. The patterns were scanned at room temperature, over the angular range 10-70° 2
3. Results
3.1. Solution properties
3.1.1. Viscosity
This part is devoted to study the effect of solution aging and its viscosity on the films thickness. To do this study, five samples are developed, successively on the day, the next day, after seven days, after 10 days, and after fourteen days of solution synthesis. The conservation of the sol during the 14 days is made at room temperature.
Table 1 shows an important change of layers thickness with the increasing of the solution viscosity. After a repose period of 14 days of synthesis solution doped with ZrO2, the thickness of layer changes from 32 nm, with a viscosity 10 mPa.s, to 81 nm when the viscosity is 180 mPa.s. We notice that the ZrO2-doped TiO2 solution becomes more viscous over time (Figure 1). This reflects the rate of polycondensation reaction progress.
10 | 32 | |
20 | 33 | |
60 | 39 | |
110 | 61 | |
180 | 81 |
3.2. Powder Properties (Xerogel)
3.2.1. X-Ray Diffraction (XRD)
Figure 2a and b shows the X-ray diffraction (XRD) patterns of TiO2 xerogels of undoped (Figure 2a) and 5% ZrO2-doped TiO2 (Figure 2b). The XRD pattern evolution of titanium xerogel obtained after the evaporation of the organic compounds during 3 months of aging at ambient temperature shows that it is an amorphous phase as reported in [54].
It has been reported that the used acid catalyst, during sol–gel preparation, plays a crucial role for determining the TiO2 phase, in literature [54, 55], they found that powder is amorphous when they use acetic acid as catalyst. However, when using formic acid they found that, in addition to amorphous phase, there is an amount of the anatase nanoparticles. This analysis of the doped TiO2 xerogel exhibits that the addition of 5% ZrO2 (Figure 2b) would be largely sufficient to form nanoparticles of anatase which crystallizes with (101) plane. It is interesting to note that the addition of a minor amount of ZrO2 starts crystallization of anatase. Whereas, A. Kitiyanan et al. [56] B. Neppolian et al. [57] reported that addition of ZrO2 has no effect on TiO2 oxide morphology..
3.2.2. Thermal analysis
The differential scanning calorimetric (DSC) curves of undoped TiO2 and 5% ZrO2-doped TiO2 xerogels are shown in Figure 3 It is interesting to note that both doped and undoped xerogels showed a similar thermal behavior in the temperature range 20–250 °C. Generally, weight loss corresponds to the evaporation of water, thermal decomposition of butanol as well as carbonization or combustion of acetic acid and other organic compounds [58-60] which constitute metal alkoxides. Hence, the above thermal events were represented by an endothermic peak spreading from 50 to 250 °C.
A double exothermic peak in the 260–450 °C temperature range of TiO2 xerogel can be attributed to the crystallization of titanium oxide [61].
The addition of 5% of zirconium oxide led to a shift of exothermic peak phase towards lower temperatures. This may be due to the speeding up of the crystallization of titanium oxide compared to the undoped one.
3.3. Thin films properties
3.3.1. Structural Properties
3.3.1.1. Thin films thickness
The measured values of thin films thickness, given in Figure 4, were determined with a surface profiler for various layers and at different annealing temperatures. It is clearly observed that the film thickness increases with the number of dipping and annealing temperatures.
3.3.1.2. Study of deposition rate
A thin film deposited by dip-coating method has a thickness which can be controlled by the deposition rate. To simplify, d thickness depends on the speed according to the following relationship:
Where:
Vd is the deposition rate, k is the empirical factor depending on the viscosity, surface tension and density of the solution used and a is the exponent with 2/3 value according to Landau and Levich [62], and 1/2 according to Michels et al. [63] or even proportionately at the speed of dipping Hewak et al. [64].
We then set the objective of determining this factor to validate one of these different models. So, we have prepared six samples with different deposition rate from 0.6 cm.s-1 to 2 cm.s-1 in the same conditions (deposited in solution with a viscosity 40 mPa.s at 21°C and treated at 400°C); we measured their thicknesses by profilometer and the results are grouped in table 2 and represented in figure 5.
This curve shows a linear increase in ln(d) versus ln(Vd). For the exponent a, values of 0,965 have been obtained, which is in good agreement with the exponent obtained by Hewak et al. [64]. This simple comparison shows that the increase in the speed of dipping, results an increase in the thickness of doped thin films.
0.6 | 0.8 | 1 | 1.4 | 1.8 | 2 | |
38 | 56 | 74 | 93 | 116 | 143 |
3.3.1.3. X-Ray Diffraction (XRD)
3.3.1.3.1. Crystallization
Influence of annealing temperature
Our samples were analyzed using X-ray diffraction (XRD) to investigate the transformation behaviors. We have studied the structural properties of undoped TiO2, and doped with 5% ZrO2 thin films and deposited by the sol–gel method. The dip-coated thin films have been examined at different annealing temperatures (350 to 450 °C).
Figure 6 shows XRD patterns of 5% ZrO2-doped TiO2 thin film obtained after different dipping and treated at 450 °C. However, Figure 7 shows XRD patterns of 5% ZrO2-doped TiO2 thin film obtained after 2 dipping and treated at various annealing temperatures at 350 °C, 400 °C and 450 °C. Clearly, titanium oxide starts to crystallize starting from annealing at 350 °C.
This analysis of the doped TiO2 thin films exhibits that the addition of a minor amount of ZrO2 would be largely sufficient to form 4 sharp diffraction peaks at 25.35°, 35.51°, 50.90° and 60.76°, these are assigned to (101), (112), (200), and (105) planes which are attributed to anatase nanoparticles (crystalline) phase of TiO2.
Furthermore, all XRD patterns show a peak at 30.41° corresponding to (111) plane which is attributed to the brookite formation whatever the annealing temperature.
Peak intensities corresponding to characteristic planes of anatase (101) and brookite (111) phases are obviously increased with the increase of annealing temperature and number of dipping. This latter is interpreted as due not only to increase in proportion of titanium oxide but also to the improvement of the crystalline quality.
However, in the same conditions Kitiyanan et
Influence of doping with ZrO2
Comparison between XRD patterns (Figure 8) of both undoped and doped with 5% ZrO2 thin films obtained after 2 dippings and annealed at 400 °C temperature showed a similar behavior, so characteristic peaks correspond to the crystallization of anatase and brookite phases of the doped state is shifted to larger angles compared to the undoped one.
3.3.1.3.2. Surface morphology and grain size
The crystallite size D of TiO2 doped with ZrO2 thin films can be deduced from XRD line broadening using Scherrer equation [65]:
λ is the wavelength of X-ray beam (Cu Kα=1.5406 Å), Δhkl is the full width at half maximum (FWHM) of (hkl) diffraction peak, Δinstr is the FWHM corresponding to the instrumental limit, and θ is the Bragg angle.
Using the size of the crystallites, the dislocation density (δ) [66], the number of crystallites per unit surface area (N) and strain in the films (ε), which are newly introduced by Ray et al. [66], has been determined:
Where d is the film thickness.
The calculated structural parameters are presented in Table 3.
Annealed at | Phase | (hkl) | L (nm) | δ (10-4 traits/nm2) | N (10-3 nm-2) | ε (10-4) | ||
Undoped TiO2 | Xerogel | 3 months at T ambient | Amorphous | - | - | - | - | - |
5% ZrO2-doped TiO2 | Xerogel | 3 months at T ambient | Anatase | (101) | 14,80 | - | - | - |
Same thickness | 350 °C | Anatase | (101) | 8,58 | 135,84 | 99,74 | 3,11 | |
Brookite | (111) | 17,50 | 32,65 | 11,76 | 3,89 | |||
Anatase | (112) | 16,66 | 36,03 | 13,62 | 4,52 | |||
Anatase | (200) | 14,74 | 46,03 | 19,67 | 6,69 | |||
Anatase | (105) | 16,33 | 37,50 | 14,47 | 7,53 | |||
400 °C | Anatase | (101) | 10,09 | 98,22 | 73,01 | 3,07 | ||
Brookite | (111) | 17,61 | 32,25 | 13,73 | 3,82 | |||
Anatase | (112) | 17,27 | 33,53 | 14,56 | 4,44 | |||
Anatase | (200) | 15,57 | 41,25 | 19,87 | 6,37 | |||
Anatase | (105) | 18,71 | 28,57 | 11,45 | 7,58 | |||
450 °C | Anatase | (101) | 13,92 | 51,61 | 29,29 | 2,98 | ||
Brookite | (111) | 18,06 | 30,66 | 13,41 | 3,74 | |||
Anatase | (112) | 19,09 | 27,44 | 11,36 | 4,38 | |||
Anatase | (200) | 18,63 | 28,81 | 12,22 | 6,34 | |||
Anatase | (105) | 20,56 | 23,66 | 9,09 | 7,47 |
The computed values of grain sizes, given in Table 3, were calculated for different annealing temperatures with the same thickness. Thus, the obtained grain sizes of anatase and brookite increase from 8.58 nm to 20.56 nm and from 17.50 nm to 18.06 nm, respectively. In fact, as annealing temperature increases grain sizes also increases.
It is interesting to note that the grain size improves and the defects like dislocation density and strain in the films decrease with film thickness. This may be due to the improvement in crystallinity in the films with film thickness. As we also note that the variation of the strain is perfectly correlated with that of the dislocation density δ. When these increase, they cause the decrease in grain size and leads to recrystallization of the nanoparticles. Furthermore, the stages of nucleation, growth and coalescence become stable, which causing the reduction of constraints in the film formed.
The evolution of the grain size D according the annealing temperature can be interpreted by the Arrhenius law (figure 9):
Where:
Ea is the energy activation of crystallization;
KB the Boltzmann constant;
D0 pre-exponential factor.
The size D tends towards the infinite for high temperatures [67].
The values of activation energies of crystallization corresponding respectively to anatase and brookite phases are calculated from the curve showed in figure 9, we note that the activation energy of the anatase Ea=0,096 eV crystallization is lower than that of the brookite Ea=0,012 eV. This means that the formation of anatase requires more energy than that of brookite.
3.3.1.4. RAMAN
The Raman spectra of undoped and 5% ZrO2-doped TiO2 thin films annealed at 450°C for different dipping (figure 10) display various peaks related to titanium oxide as anatase and brookite phases. These spectra exhibit bands at around 138 (strong), 235 (weak), 514 (weak) and 632 cm-1 (medium)) for the thin layers of ZrO2-doped TiO2 corresponding to the Eg modes of vibration. The above bands can be assigned to anatase phase except the band 235 cm-1 corresponding to the B1g modes of vibration, which is due to the crystallization of brookite phase. While bands of 144, 188 and 651 cm-1 can be assigned to both anatase and brookite phases [68,69].
A slight shift of the most intense peak, Eg, to smaller wavenumber is observed for all thin films doped with ZrO2 by comparison with anatase of undoped phase (figure 11). Similar displacements have been previously reported in XRD patterns and they can be correlated with the confinement effects in nano-structured anatase crystallites.
3.3.1.5. FTIR
Figure 12 shows the infrared absorption spectrum of the 5% ZrO2 -doped TiO2 films annealed at different temperature. The peak at 2360 cm-1 resulted from the adsorbed H2O molecules, which were not removed completely after sol–gel coating. The peaks at 1242 cm-1, 1111 cm-1, 1035 cm-1 and 860 cm-1 correspond to the vibration mode of Ti-OH [70, 71].
The band around 665 cm-1 was attributed to the vibration mode of Ti-O-Ti bond [72] and another bond appears around 455 cm-1, this is the O-Ti-O band corresponding to the crystalline titania in the anatase form [73-76].
We find that the vibration bands intensity located in the vicinity of 665 cm-1 and 455 cm-1 increase when annealing temperature increases. This indicates that the number of Ti-O-Ti and O-Ti-O links of titanium dioxide crystallization is also growing.
3.3.1.6. Scanning electron microscopy (SEM) and EDX
5% ZrO2-doped TiO2 thin films deposited on ITO substrates and obtained after various annealing temperature at 350°C and 450°C were coated and examined in a scanning electron microscope (SEM) to investigate their structure and surface characteristics. We observed that the coating was homogeneous without any visual cracking over a wide area. The increase in the treatment temperature, did not affect the uniformity of the film.
The surface composition of films is further identified by EDX measurement. EDX result shown in Figure 13 demonstrates that the peaks of Ti, O and Zr can be clearly seen in the survey spectrum. While the other elements as Si, In, Ca, Na and Mg are the components of ITO substrate.
The chemical compositions of thin film analyzed are given in table 4.
40,13 | 2,03 | 3,15 | 37,83 | 3,07 | 4,39 | 1,23 | 8,17 | 100 |
3.3.2. Optical properties
3.3.2.1. UV absorption analysis
Figure 14 display diffused scattering UV-VIS transmittance spectra of TiO2 thin films undoped and 5% ZrO2-doped TiO2, for different annealing temperatures from 350°C to 450°C and different numbers of dipping (3, 4, 6, 8 dipping) in the wavelength range 300–800 nm, where the film due to interference phenomena between the wave fronts generated at
the two interfaces (air and substrate) defines the sinusoidal behavior of the curves’ transmittance versus wavelength of light. The curves showed a similar behavior in the temperature range:
A region characterized by a strong absorption at λ< 380 nm, this absorption is due to the transition electronic inter-band.
High transmittance region, from 60 to 95% on a wide range of wavelength in the visible region (from 380 to 800 nm) has been observed which may be used in applications in solar cells. High transparency is one of the most important properties that explain the interest in undoped or doped TiO2 thin films.
As can be seen, all the spectrums exhibit interference fringes, which are due to the multiple reflections at the two film edges, i.e. at the film/air and the film/substrate interfaces. This indicates that the top film surface is smooth and uniform and exhibits a good transparency in the visible region. So that the excellent surface quality and homogeneity of the film were confirmed from the appearance of interference fringes in the transmission spectra. This occurs when the film surface is reflecting without much scattering/absorption in the bulk of the film.
If the film surface is rough, the radiation in film/air interface undergo scattering in all directions instead of a reflection. Oh et al. [28], Kim et al. [77] show that the interference fringes are due the increase in thin films thickness. The occurrence of such fringes means that our films are sufficiently thick
Analysis of UV– VIS transmission spectra shows that the 5% ZrO2-doped TiO2 thin films are transparent in the visible range and opaque in the UV region, whatever are the annealing temperature and number of dipping
The amplitude of interference spectra increased with increasing calcination temperature. These results show that the refractive index of TiO2 thin films is increased while the film thickness is decreased. This can be due to the formation stage of anatase and with the increase in the grain size [28].
A slight shift of transmission curves to lower wavelengths is observed for curves of ZrO2-doped thin films in comparison with those undoped (figure 14) This shift is ascribed to the increase in band gap energy.
3.3.2.2. Refractive index, density, thickness and porosity
The refractive index of TiO2 thin films was calculated from measured UV–VIS transmittance spectrum. The evaluation method used in this work is based on the analysis of UV–VIS transmittance spectrum of a weakly absorbing film deposited on a non-absorbing substrate [78]. The refractive index n (λ) over the spectral range is calculated by using the envelopes that are fitted to the measured extreme:
Where n0 is the refractive index of air, ns is the refractive index of the film, Tmax is the maximum envelope, and Tmin is the minimum envelope. The thickness of the films was adjusted to provide the best fits to the measured spectra. In this study, all the deposited films are assumed to be homogeneous.
The porosity of the thin films is calculated using the following equation [79]
Where nd is refractive index of pore-free anatase (nd = 2.52) [80], and n is refractive index of porous thin films.
The relationship between density, and refractive index for the polymorphs was proposed by Gladstone-Dale [81]. This relationship is as follows:
Where :
n: mean index of refraction,
d: density
0,40: Gladstone-Dale constant for TiO2
The thickness of the films was calculated using the equation:
Where
The results of the computed refractive index (n) (figure 15), density (
This phenomenon is related to crystallization, pores destruction and densification of associated film, as well as the elimination of organic compounds.
However, the porosity decreases with increasing annealing temperature and film thickness.
2,19 | ||||||||||
The calculated values of thin films thickness are given in table 6. It is clearly observed that the film thickness increases with the number of dipping and annealing temperatures, which is in good agreement with results obtained previously of thickness determined with a surface profiler.
127 | 194 | 268 | |
139 | 216 | 274 | |
158 | 233 | 289 |
3.3.2.3. Optical band gap:
The band gap is then found as the intercept of the linear portion of the plot. For a direct band gap semi-conductor, the absorption near the band edge can be estimated from the following equation known as the Tauc plot [83]:
Where C is a constant, Eg the optical band, α is the optical absorption coefficient, h
The energy band gap (Eg) of the films can be estimated by plotting (αh
This decrease was correlated with grains size increases with temperature, when the latter increases the defects and impurities tend to disappear causing a reorganization of the structure. We find that doping with ZrO2 causes an increase in the band gap by contrast to that of undoped TiO2 (3.50 eV).
3,79 | 3,74 | 3,71 | 3,65 | |
3,73 | 3,70 | 3,68 | 3,59 | |
3,67 | 3,63 | 3,61 | 3,54 |
4. Conclusion
In this study, we investigated the transformation behaviors and the effect; of a smaller ratio range of ZrO2; doping on the surface area of TiO2 thin films, band gap energy, variations of crystal granularity, phase composition and especially on the evolution of the crystallite size and defects concentration with annealing treatments and layers thickness of the samples produced. So that in this chapter, we report the study of structural, thermal and optical properties of ZrO2-doped TiO2 thin films deposited by the sol–gel process
Analyses of doped TiO2 xerogel show that addition of 5% ZrO2 would be largely sufficient to form nanoparticles of anatase (size of grain of 14.78 nm) by contrast to that of undoped TiO2. X-ray diffraction and Raman spectroscopy analyses exhibit that doped thin films obtained starting from annealing at 350°C crystallize in both anatase and brookite phases. Calculation of grain sizes by Scherrer's formula, gives sizes ranging from 8.58 to 20.56 nm and we note an increase in grain sizes by increasing the annealing temperature for all structures. Raman spectroscopy studies confirms the results found by XRD and reveal that the films annealed from 350 to 450◦C crystallizes in anatase and brookite structure. From the DSC analysis, we have demonstrated that an annealing temperature equal or higher than 340 °C for undoped and 260 ◦C for 5% ZrO2-doped would be sufficient to form titanium oxide. The addition of 5% of zirconium oxide led to a shift of exothermic peak phase towards lower temperatures, due to the speeding up of the crystallization of titanium oxide compared to the undoped one.
Analysis of UV-VIS transmission spectra shows that the 5% ZrO2-doped TiO2 thin films are transparent in the visible range and opaque in the UV region, whatever the annealing temperature and the number of dipping. Refractive index of the thin films of titanium oxide increases with increasing annealing temperature and number of dipping, but the porosity decreases, due to phase transition (anatase, anatase–brookite), which increases grain sizes and/or density of layers. Energy band gap of 5% ZrO2-doped TiO2 films decrease owing to an increase in annealing temperatures, also we find that doping with ZrO2 causes an increase in the band gap by contrast to that of undoped TiO2.
The optical properties of the films are found to be closely related to the microstructure and crystallographic structure which depend on the annealing temperature. In summary, In this study, we successfully fabricated ZrO2-doped TiO2 thin films, with desired structural and optical properties by sol–gel dip coating using the titanium alkoxide (tetrabutyl-orthotitanate) as a starting material.
References
- 1.
Hu L. Yoko T. Kozuka H. Sakka S. 1992 Thin Solid Films j. 18: 219. - 2.
Brinker C.J, Scherer G.W 1990 Sol-Gel Science, Academic Press, San Diego, CA. - 3.
Brinker C.J, Frye G.L, Hurd A.J, Ashlet C.S 1991 Thin Solid Films j. 97: 201. - 4.
Nishio K. Sei T. Tsuchiya T. 1996a Preparation and electrical properties of ITO thin films by dip-coating process. Mater. Sci. Tech. J.31 1761 1766 - 5.
Nishio K. Miyake S. Sei T. Watanabe Y. Tsuchiya T. 1996b Preparation of highly oriented thin film exhibiting transparent conduction by the sol-gel process. Mater. Sci. J.31 3651 3656 - 6.
Nishio K. Seki N. Thongrueng J. Watanabe Y. Tsuchiya T. 1999a Preparation and properties of highly oriented thin films by a sol-gel process. Sol-Gel Sci. Tech J.16 37 45 - 7.
Nishio K. Kudo C. Nagahama T. Manabe T. Yamaguchi I. Watanabe Y. Tsuchiya T. 2000b Preparation and characterzation of epitaxial thin films prepared by sol-gel process. Mater. Res. Soc. J.623 377 382 - 8.
Nishio K. Watanabe Y. Tsuchiya T. 2003 Epitaxial growth of thin films prepared from sol-gel process. Sol-Gel Sci. Tech. J.26 245 250 - 9.
Kodaira T. Nishio K. Yamaguchi I. Suzuki S. Tsukada K. Tsuchiya T. 2003 Synthesis and properties of highly conductive thin films as buffer layer from sol-gel process. Sol-Gel Sci. Tech. J.26 1049 1053 - 10.
Larson S.A, Falconer J.L 1994 Appl. Catal. B: Environ. j. 4: 149. - 11.
Pas Y. Heller A. 1997 Mater. Res. J. 12: 2759. - 12.
Hara K. T. Hariguchi T. Kinoshita K. Sayama H. Arakawa Solar. Energy Mater. Solar Cell. . 2001 - 13.
Sakha V. A. Arabatzis I. M. Konstantinou I. K. Dimou A. D. Albanis T. A. Falaras P. 2004 Appl. Catal. B: Environ. J. 49: 195. - 14.
Tachibana Y. Ohsaki H. Hayashi A. Mitsui A. Hayashi Y. 2000 Vacuum j. 59: 836. - 15.
Zheng S. K. Wang T. M. Xiang G. Wang C. 2001 Vacuum j. 62: 361. - 16.
Radecka M. Zakrzewska K. Czternastek H. Stapinéski T. Debrus S. 1993 Appl. Surf. Sci. j. 65: 227. - 17.
Dumitriu D. Bally A. R. Ballif C. Hones P. Schmid P. E. Sanjinés R. Lévy F. Pârvulescu V. I. 2000 Appl. Catal. B: Environ. J. 25: 83. - 18.
Takeda S. Suzuki S. Odaka H. 2001 Thin Solid Films j. 392: 338. - 19.
Zhang F. Huang N. Yang P. 1996 Surf. Coat. Technol. J. 84: 476. - 20.
Aidla A. Uustare T. Kiisler A. A. Aarik J. Sammelselg V. 1997 Thin Solid Films j. 305: 270. - 21.
Abou-Helal M.O, Seeber W.T 2002 Appl. Surf. Sci. j. 195: 53. - 22.
Choi Y. Yamamoto S. Umebayashi T. Yoshikawa M. 2004 Solid State Ionics j. 172: 105. - 23.
Hu L. Yoko T. Kozuka H. 1992 Thin Solid Films j. 219: 18. - 24.
Chrysicopoulou P. Davazoglou D. Trapalis C. Kordas G. 1998 Thin Solid Films j. 323: 188. - 25.
Kim D.J, Hahn S.H, Oh S.H, Kim E.J 2002 Mater. Lett. j. 57: 355. - 26.
Yang J. Li D. Wang H. Wang X. Yang X. Lu L. 2001 Mater. Lett. j. 50: 230. - 27.
Huber B. Brodyanski A. Scheib M. Orendorz A. Ziegler C. Gnaser H. 2005 Thin Solid Films j. 472: 114. - 28.
Oh S.H, Kim D.J, Hahn S.H, Kim E.J 2003 Mater. Lett. j. 57: 4151. - 29.
Wang C. Xu B. Q. Wang X. M. Zhao J. C. 2005 Solid State Chem J. 178:3500. - 30.
Hu C. Tang Y. C. Yu J. C. Wong P. K. 2003 J photocatalyst Appl Catal B Environ 40:131. - 31.
Bensouyad H. Sedrati H. Dehdouh H. Brahimi M. Abbas F. Akkari H. Bensaha R. 2010 Thin Solid Films J. 519:96. - 32.
Yang J. Li D. Wang X. Yang X. J. Lu L. D. 2002 J Solid State Chem 165:193. - 33.
Li J. L. Liu L. Yu Y. Tang Y. W. Li H. L. Du F. P. 2004 Electrochem Commun J. 6:940. - 34.
Bandara J. Hadapangoda C. C. Jayasekera W. G. 2004 J Appl Catal B Environ 50:83. - 35.
Li XZ, Li FB, Yang CL, Ge WK 2001 Photochem Photobiol A Chem J. 141:209. - 36.
Shchukin D. Poznyak S. Kulak A. Pichat P. 2004 Photochem Photobiol A Chem J. 162:423. - 37.
Bensouyad H. Adnane D. Dehdouh H. Toubal B. Brahimi M. Sedrati H. Bensaha R. 2011 Sol-Gel Sci Technol J. 59: 546. - 38.
Takahashi Y. K. Ngaotrakanwiwat P. Tatsuma T. 2004 photocatalysts Electrochim Acta J. 49: 2025. - 39.
Wu L. Yu J. C. Fu X. Z. 2006 Mol Catal A Chem J. 244:25. - 40.
Su H. Xie Y. Gao P. Xiong Y. Qian Y. 2001 J Mater Chem 11:684. - 41.
Zelner M. Minti H. Reisfeld R. Cohen H. Tenne R. 1997 Preparation and characterization of CdS films synthesized in situ in zirconia sol-gel matrix, Chem. Mater. J. 9: 2541. - 42.
Sashchiuk A. Lifshitz E. Reisfeld R. Saraidarov T. Zelner M. Willenz A. 2001 Optical and conductivity properties of PbS nanocrystals in amorphous Zirconia sol-gel films, of Sol-Gel Science and Technology J. 24: 31. - 43.
Wang M. T. Wang T. H. Lee J. 2005 Electrical conduction mechanism in high-dielectric-constant ZrO2 thin films, Microelecton. Reliability j. 45: 969. - 44.
Harrison H.D.E, McLamed N.T, Subbaro E.C 1963 A new family of self-activated phosphors, Electrochem. Soc J. 110: 23. - 45.
Lowdermilk W. H. Milam D. Rainer F. 1980 Optical coatings for laser fusion applications, Thin Solid Films j. 73: 155. - 46.
Meier S.M, Gupta D.K 1994 The evolution of thermal barrier coatings in gas turbine engine applications, Eng. Gas Turbines Power Trans. ASME J. 116: 250. - 47.
Wendel H. Holzschuh H. Suhr H. Erker G. Dehnicke S. Mena M. 1990 Thin zirconium dioxide and yttrium oxide-stabilized zirconium dioxide films prepared by plasma-CVD, Mod. Phys. Lett. B j. 4: 1215. - 48.
Fork D.K, Fenner D.B, Connell G.A.N, Phillips J.M, Geballe T.H 1990 Epitaxial yttria-stabilized zirconia on hydrogen-terminated Si by pulsed laser deposition, Appl. Phys. Lett. j. 57: 1137. - 49.
Patel A. M. Spector M. 1997 Tribological evaluation of oxidized zirconium using an articular cartilage counterface: a novel material for potential use in hemiarthroplasty, Biomaterials j. 18: 441. - 50.
Balamurugan A. Kannan S. Rajeswari S. 2003 Structural and electrochemical behaviour of sol-gel zirconia films on 316L stainless-steel in simulated body fluid environment, Mater. Lett. j. 57: 4202. - 51.
Ritala M. Leskela M. 1994 Zirconium dioxide thin films deposited by ALE using zirconium tetrachloride as precursor, Appl. Surf. Sci. j. 75: 333. - 52.
Cao G. Z. Brinkman H. W. Meijerink J. De Vries K. J. Burgraaf A. J. 1993 Pore narrowing and formation of ultrathin yttria-stabilized zirconia layers in ceramic membranes by chemical vapor deposition/electrochemical vapor deposition, Am. Ceram. Society. J. 76: 2201. - 53.
Emeline A. Kataeva G. V. Litke A. S. Rudakova A. V. Serpone N. 1998 Langmuir j. 14: 5011. - 54.
Mechiakh R. Bensaha R. 2006 C.R. Phys j. 7: 464. - 55.
Ivanda M. Music S. Popovic S. Gotic M. 1999 J Mol Struct 480: 645. - 56.
Kitiyanan A. Yoshikawa S. 2005 Materials Letters J. 59: 4038. - 57.
Neppolian B. 2007 Applied Catalysis A: General j. 333: 264. - 58.
Pérez-Hernandez R. Gomez-Cortes A. Arenas-Alatorre J. Rojas S. Mariscal R. Fierro J. L. G. Diaz G. 2005 Catal. Today j. 107: 149. - 59.
Perdew J. P. Wang Y. 1992 Phys. Rev. B j. 45: 13244. - 60.
Montoya I. A. Viveros T. Dominguez J. M. Channels L. A. Schifter I. 1992 Catal. Lett. J. 15: 207. - 61.
Mechiakh R. Meriche F. Kremer R. Bensaha R. Boudine B. Boudrioua A. 2007 Opt. Mater. J. 30: 645. - 62.
Landau L. D. Levich B. 1942 Acta Physicochim. J. 17: 42. - 63.
Michels A. F. Manegotto T. Horowitz F. 2004 Appl. Opt. j. 43: 820. - 64.
Hewak D. W, Lit J. W. Y 1988 Can. J. Phys, 66: 861. - 65.
Cullity B.D 1978 Elements of X-Ray Diffraction, 2nd ed.Addison-Wesley, Reading, MA. - 66.
Ray S. Banerjee R. Baraua A. K. 1980 Jpn J. of Appl Phys 19:1889. - 67.
Yang H. Huang C. Tang A. Zhang X. Yang W. Materials Research. Bulletin . 2005 - 68.
Lottici P. P. Bersani D. Braghini M. Montenero A. 1993 Mater. Sci. J. 28: 177. - 69.
Djaoued Y. Badilescu S. Ashrit Bersani. D. Lottici P. P. Robichaud J. 2002 Sol-Gel Sci Technol J. 24: 255. - 70.
Liao M.H, Hsu C.H, Chen D.H 2006 J Solid State Chem 179: 2020. - 71.
Xie Y. Liu X. Huang A. Ding C. Chu P. K. 2005 J Biomaterials 26: 6129. - 72.
McDevitt N.T, Baun W.L 1964 J Spectrochim Acta 20: 799. - 73.
Music S. Gotic M. Ivanda M. Popovic S. Turkovic A. Trojko R. Sekulic A. Furic K. 1997 Mater Sci Eng B 47: 33. - 74.
Ocana M. Fornes V. Serna J. V. 1988 J Solid State Chem 75: 364. - 75.
Djaoued Y. Badilescu S. Ashrit P. V. 2002 Sol-Gel Sci Technol J. 24: 247. - 76.
Tian J. 2009 Surface & Coatings Technology j. 204: 723. - 77.
Kim S. Yum J. Sung Y. 2005 Photochem Photobiol A: Chem J. 171: 269. - 78.
Manifacier J. C. Gasiot J. Fillard J. P. 1976 Phys. E J. 9: 1002. - 79.
Yoldas B.E, Partlow P.W 1985 Thin Solid Films j. 129: 1. - 80.
Kingery W.D, Bowen H.K, Uhlmann D.R 1976 Introduction to Ceramics, Wiley, New York. - 81.
Gladstone, Dale 1863 Phil. Trans. J. 153: 317 - 82.
Swanepoel R. 1983 Phys. E: Sci. Instrum. J. 16: 1214. - 83.
Pankove J.I 1971 Optical Process in Semiconductors; Prentice Hall; Englewood; Cliffs; NJ; 34. p. - 84.
Zhao X. K, Fendler J. H 1991 Phys. Chem. J. 95: 3716. - 85.
Tang H. Prasad K. Sanjines R. Schimid P. E. Levy F. 1994 App. Phys. J. 75: 2042.