Table 1. Textural properties and crystalline structures and of the prepared porous samples.
1. Introduction
High air contaminant levels in the indoor environment come from either the ambient air or from indoor sources. (Cao, 2001) Nitrogen oxide is one of the most common gaseous pollutants found in the indoor environment with the concentration in the range of 70-500 parts-per-billion (ppb) levels. This has serious implications on the environment and health of the mankind. (Huang et al., 2009) Conventional techniques to treat nitric oxide in industrial emission mainly include physical adsorption, biofiltration, and thermal catalysis methods. However, these methods usually suffer from some disadvantages, such as the low efficiency for pollutants at the parts per billion level and the difficulty in solving the postdisposal and regeneration problems. (Huang et al., 2008)
As a promising environmental remediation technology, semiconductor-mediated photocatalytic technology has been widely used to purify contaminated air and wastewater. (Fox & Dulay, 1993 ) Titanium dioxide is the most widely used photocatalyst because of its superior photoreactivity, nontoxicity, long-term stability and low price. Recently, great attention has been paid to macro/mesoporous TiO2 for its interconnected macroporous and mesoporous structures. Such hierarchical material may enhance properties compared with single-sized pore materials due to increased mass transport through the material and minimized pressure drop over the monolithic material.(Yuan et al. 2006) Meanwhile the macroporous channels could serve as light-transfer paths for the distribution of photon energy onto the large surface of inner photoactive mesoporous frameworks. Therefore, higher light utilization efficiency could be obtained for heterogeneous photocatalytic systems including photooxidation degradation and solar cells. In addition, the hierarchical structure-in-structure arrangement of mesopore and macropore is benefit for the molecule traffic control and for the resistance of the photocatalyst to poisoning by inert deposits.(Rolison 2003)
Though such structure contributes great advantages to TiO2, such as a readily accessible pore-wall system and better transport of matter compared to the traditional TiO2 photocatalysts, the anatase TiO2 semiconductor has a relatively large band gap of 3.2 eV, corresponding to a wavelength of 388 nm.(Yu et al., 2006) The requirement of UV excitation impedes the development of solar-driven photocatalytic systems. As a promising way, doping method can effectively extend the light absorption of TiO2 to the visible region and reduce the recombination of photoinduced electrons and holes.(Zhu et al., 2007) Among various dopants, the Fe3+-dopant is most frequently employed owing to its unique half-filled electronic configuration, which might narrow the energy gap through the formation of new intermediate energy levels and also diminish recombination of photoinduced electrons and holes by capturing photoelectrons. However, calcination of the photocatalysts at high temperature is usually indispensable for removing organic templates, enhancing structural crystallization, and allowing doped ions to enter into the frameworks of TiO2.(Wang et al., 2009) Such treatment at high temperature will result in great loss of surface area and destroying the pore systems owing to the grain growth, especially for porous materials. Thus, the photoactivity of the calcined samples with low specific area will be greatly reduced for the poor light-harvesting capability.(Yu et al., 2006) Fortunately, using inorganic structure stabilizers (SiO2, ZrO2, and Al2O3) could allow the anti-sintering properties of porous materials to be promoted greatly enough for application in high temperature environment, such as treating automotive exhaust.( Wang et al., 1999)
In this chapter, we describe a detailed study of the effect of Al2O3 as a promoter in enhancing a macro/mesoporous visible-light photocatalyst, Fe/TiO2, for the oxidation of nitric oxide (NO). The photocatalysts are synthesized through directing the formation of inorganic phases (Al2O3-Fe/TiO2) with multidimensional pore systems through the self-assembly of a single surfactant under hydrothermal conditions. The experimental results showed that doping Fe3+ into the framework of TiO2 can effectively extend the optical absorption spectrum to visible light range. Introducing highly dispersed amorphous Al2O3 species into the Fe/TiO2 system could greatly increased the thermal stability of the Fe/TiO2 framework with higher surface area and larger pore volume. It is surprising that the Al2O3-Fe/TiO2 sample treated at 700° C possessed a high specific surface area (ca. 130 m2/g), about 6 times of that of the Al2O3-free sample. The photooxidation of NO in air over the 3D macro/mesoporous Al2O3-Fe/TiO2 photocatalysts was studied. These products were utilized to remove gaseous NO at 400 parts-per-billion level in air under visible-light irradiation. These Al2O3-Fe/TiO2 photocatalysts exhibited very strong ability to oxidize the NO gas in air under visible-light irradiation. Importantly, these 3D macro/mesoporous Al2O3-Fe/TiO2 photocatalysts showed excellent stability and maintained a high level of photocatalytic activity after multiple reaction cycles.
2. Experiment section
2.1. Preparation of 3D macro/mesoporous Al2O3-Fe/TiO2 photocataltsts
Brij 56 [C16(EO)10], titanium isopropoxide, aluminum sec-butoxide, and ferric (III) nitrate are purchased from Aldrich. All chemicals were used as received. In a typical synthesis of macro/mesoporous visible light photocatalysts Al2O3-Fe/TiO2, required amount of ferric (III) nitrate was dissolved in a aqueous solution of Brij 56 (15 wt %) with pH = 2 adjusted by sulfuric acid under ultrasonic irradiation in an ultrasonic clean bath (Bransonic ultrasonic cleaner, model 3210E DTH, 47 kHz, 120 W, USA). 18 ml mixture of aluminum sec-butoxide and titanium isopropoxide with a metal-to-metal molar ratio (MAl/MTi = 20:100) was added drop by drop into the above medium under stirring, followed by further stirring for 0.5 h. The obtained mixture was then transferred to a Teflon-lined autoclave and heated at 80° C for 36 h under static condition during which the inorganic precursor hydrolyses and polymerizes into a metal oxide network. Finally, the as-prepared white samples were clacined at 400-700° C for 8 h at 1 C/min to remove the surfactant species and improve the crystallinity. The as-prepared Al2O3-Fe/TiO2 samples were denoted as Al-Fe/TiO2-400, Al-Fe/TiO2-500, Al-Fe/TiO2-600 and Al-Fe/TiO2-700, where 400-700 refers to the calcinations temperature. For comparation, macro/mesoporous photocataltsts, pure TiO2 and Fe/TiO2, were also prepared by the same procedure. The molar ratio of Fe/Ti is 0.25 % for all the Fe doped samples.
2.2. Characterization
X-ray diffraction (XRD) measurements were carried out using a Bruker D8 Advance X-ray diffractometer (Cu Kα1 irradiation, λ = 1.5406 Å) at a scanning rate of 0.02 Degree/Second. The Schrerrer equation (Ф =
2.3. Photocatalytic activity testing
The photocatalytic experiments for the removal of NO gas in air were performed at ambient temperature in a continuous flow rectangular reactor (10 H cm*30 L cm*15Wcm). A 300Wcommercial tungsten halogen lamp (General Electric) was used as the simulated solar light source. A piece of Pyrex glass was used to cut off the UV light below 400 nm. Four minifans were used to cool theflowsystem. Photocatalyst (0.2 g) was coated onto a dish with a diameter of 12.0 cm. The coated dish was then pretreated at 70° C to remove water in the suspension. The NO gas was acquired from compressed gas cylinder at a concentration of 48 ppm NO (N2 balance, BOC gas) with traceable National Institute of Stands and Technology (NIST) standard. The initial concentration of NO was diluted to about 400 ppb by the air stream supplied by a zero air generator (Thermo Environmental Inc. model 111). The desired humidity level of the NO flow was controlled at 70% (2100 ppmv) by passing the zero air streams through a humidification chamber. The gas streams were premixed completely by a gas blender and the flow rate was controlled at 4 L.min-1 by a mass flow controller. After the adsorption-desorption equilibrium among water vapor, gases and photocatalysts was achieved, the lamp was turned on. The concentration of NO was continuously measured by a chemiluminescence NO analyzer (Thermo Environmental Instruments Inc. model 42c), with a sampling rate of 0.7 L/min.
3. Results and discussion
3.1. X-ray diffraction and N2 sorption
The crystal composition, thermal stability and mesoporous structure of the as-prepared samples were investigated by X-ray diffraction (XRD) and N2 sorption analyses. Figure 1a shows the wide-angle XRD patterns of the Fe-doped TiO2 calcined at different temperatures. For the 400° C sintering sample, a broad peak corresponding to (101) diffraction of anatase-TiO2 (JCPDS 21-1272) was observed. The broadening of the diffraction peak may have been caused by the small crystalline grain size (6.1 nm). Upon increasing the temperature to 500 C, the intensity of this peak became stronger and sharper, indicating that larger particles (8.0 nm) were formed. However, when the calcination temperature was increased to 600 C, the intensity of the anatase-TiO2 diffraction peak decreased. Meanwhile, weak peaks indexable as diffractions of rutile-TiO2 (JCPDS 87-920) appeared. About 4.5 % of the anatase-TiO2 was converted to rutile-TiO2.
After calcinations at 700° C, the size of anatase-TiO2 increased dramatically to 20.0 nm, and nearly 43.3 % of the anatase-TiO2 was converted to rutile-TiO2. Nevertheless, introducing Al2O3 species into the Fe-doped TiO2 system greatly inhibited the crystal growth and the phase-transition. As shown in Figure 1b, all of the Al2O3 modified Fe/TiO2 samples exhibited pure anatase phase at different temperatures. More interestingly, the crystal size of the anatase TiO2 was greatly decreased after modifying Al2O3. Even after 700° C calcination, the grain size can be maintained about 7.2 nm, much smaller than that (20.0 nm) of Fe/TiO2 sample calcined at 700° C. These wide-angle XRD results revealed that thermal treatment induced the growth of crystal size and subsequent phase transition could be effectively prohibited by doped Al2O3 species acting as structural agents. As known, thermal-induced changes in crystal composition and size also had remarkable effects on the textural properties of TiO2 framework. N2 sorption analyses were utilized to confirm the change of textural properties.
N2 sorption analyses were utilized to investigate the change of textural properties of the as-prepared products. Figure 2 shows the N2 sorption isotherms and pore size distributions for the modified titanium dioxide calcined at different temperatures. Upon 400° C calcinations, both of Fe/TiO2-400 and Al-Fe/TiO2-400 samples exhibited stepwise adsorption and desorption (type IV isotherms) as shown in Figure 2a and b, indicative of a typical mesoporous structure within the as-prepared samples. As shown in Table 1, Al-Fe/TiO2-400 sample possesses a surface area of 340.0 m2/g, much higher than that (153.6 m2/g) of Fe/TiO2-400 owing to the anti-agglutination effect of induced Al2O3 species. The modification of Al2O3 also contributed a super lager pore volume (0.53 cm3/g) to Al-Fe/TiO2-400 sample. It is about two times of that (0.27 cm3/g) of Fe/TiO2-400. Such high surface area and large pore volume will make this material an excellent photocatalyst for its strong adsorption capability. With increase the calcinations temperature, the mesoporous structure of Fe/TiO2 sample was destroyed. When the calcinations temperature was increased to 700° C, the surface area was decreased to 22.6 m2/g, and the pore volume was decreased to 0.11 cm3/g. This is an indication of the collapse of the pore. However, Al-Fe/TiO2 still owns a high surface area of 131.8 m2/g and pore volume of 0.44 cm3/g. To the case of the pore-size distribution, the modification of Al2O3 also inhibited the pore size changing owing to its porous structure-stabilizing capability.
Sample | Surface Area/m2/ga | Pore Volume/mL/gb | Pore Size/nmc | Rutile content/Wt% | Crystal Size/nmd |
Fe/TiO2-400 | 153.6 | 0.27 | 5.9 | 0 | 6.1 |
Fe/TiO2-500 | 109.5 | 0.24 | 7.6 | 0 | 8 |
Fe/TiO2-600 | 64.9 | 0.20 | 11.3 | 4.5 | 13.4 |
Fe/TiO2-700 | 22.6 | 0.11 | 31.2 | 43.3 | 20.0 |
Al-Fe/TiO2-400 | 340.0 | 0.53 | 5.3 | 0 | 3.2 |
Al-Fe/TiO2-500 | 254.7 | 0.52 | 6.8 | 0 | 4.0 |
Al-Fe/TiO2-600 | 197.1 | 0.46 | 8.1 | 0 | 5.3 |
Al-Fe/TiO2-700 | 131.8 | 0.44 | 12.4 | 0 | 7.2 |
BET surface area is calculated from the linear part of the BET plot (
3.2. Scanning Electron Microscopy (SEM)
The N2 sorption analyses could provide mesoporous structure information of the as-prepared materials. To the case of the macroscopic properties, scanning electron microscopy (SEM) should be utilized to examine the macrostructure of the modified TiO2 monolithic particles. Meanwhile, the high-resolution state of SEM images could also give information on the mesoscopic properties. As shown in Figure 3a, Al-Fe/TiO2-400 is typically in a large monolithic form (> 30 μm), and exhibits macroscopic network structure with relatively homogeneous macropores of 1~2 μm (size) and about 20 μm (length) in dimension as shown Figure 3b. It is more interesting that these ultralong macroscopic channels are arranged parallel to each other. Figure 3b also demonstrates the extension of the parallel-arrayed macropores completely through the material from the side view of the sample. Such open-ended tubelike macrochannels could serve as ideal light-transport routes for introducing more photoenergy into the interior of the framework of TiO2. Meanwhile, the high-resolution SEM images (Figure 3c) shows that the walls of the macroporous TiO2 frameworks are composed of small interconnected TiO2 particles. The mesoporous structure of the as-prepared materials is probably partly due to the intraparticle porosity and partly due to the interparticle porosity of these fine particulates.(Wang, Yu et al. 2005) The macro/mesoporous structure nearly can be maintained even after 600 °C calcinations.
3.3. UV-vis spectra
UV-visible diffuse reflectance spectroscopy (DRS) was utulized to investigate the electronic states of the as prepared samples. Figure 4a shows the UV-visible absorption spectra of TiO2-400, Fe/TiO2-400, Al-Fe/TiO2-400 and Al-Fe/TiO2-700 samples. For large energy gap of anatase (3.2 eV), TiO2-400 sample has no significant absorbance for visible-light. Upon doping Fe3+ ions, the light absorption edge of Fe/TiO2-400 sample was extended to visible light region ( < 650 nm) attributed to the formation of Fe-intermediate energy levels, resulting in a decrease in the energy band. The other three samples exhibit a broad absorption bands from 200 to 600 nm with respect to the pure TiO2, indicating the effective photo-absorption property for this macro/mesoporous structure oxide composite photocatalyst system. This is because Fe-doping induces the absorbance for visible light owing to, leading to a decrease in the energy band gap.(Nahar, Hasegawa et al. 2006)
Compared to Fe/TiO2-400 sample, Al-Fe/TiO2 shows a higher light-absorbance ability located in 200~400 nm. This is because the macro/mesoporous structure, enlarged surface area and multiple scattering enable it to harvest light much more efficiently.(Yu, Wang et al. 2004) This enhanced light-trapping effect is the result of the reflection or transmission of the light scattered by the macroporous tunnels or mesopores implanted in the body of Al, Fe co-doped TiO2 matrix. It is also noted that the modification of Al2O3 did not change the light
sensitization region. However, a very weak blue shift to short wavelength was observed for Al-Fe/TiO2 sample after 700° C calcining treatment. The band energy gap of the as-prepared samples could be calculated by using (α
To evaluate the photocatalytic performance of the as-prepared materials. The photo-oxidation of NO gas under visible light irradiation (λ > 400 nm) in a single pass flow was used as a photoreaction probe. Figure 5a shows the relative of NO removal rate against irradiation time in the presence of photocatalysts under visible-light irradiation. In the absence of the photocatalyst, no obvious removal rate of NO can be observed. The Photocatalytic performance of pure TiO2 can be nearly neglected. The NO removal rate over Fe/TiO2-400 sample reaches 17 % after 20 min irradiation, indicating the promotion effect of Fe-doping. Compared to Fe/TiO2-400, Al-Fe/TiO2-400 exhibits a much higher removal rate (about 28 % after 20 min irradiation). Such high photocatalytic performance maybe attributed to the high surface area, large pore volume. Besides, 3D connected pore tunnels are also very important because they can allow the NO molecule to transport very conveniently in the body of the catalyst. Further increasing the calcinations temperature to 700° C quickly decreased the removal rate to about 10 %.
For a clear quantitative comparison, we use the Langmuir-Hinshelwood model (L-H) to describe the initial rates of photocatalytic removal of NO. The photocatalytic oxidation of NO was recognized to follow a first-order-kinetics approximately as a result of low concentration target pollutants, as evidenced by the linear plot of ln (C/C0) versus photocatalytic reaction time t (Figure 5b). The rate constants of the TiO2-400, Fe/TiO2-400, Al-Fe/TiO2-400 and Al-Fe/TiO2-700 samples are 0.119 h-1, 1.368 h-1, 1.762 h-1 and 0.893 h-1 respectively. Figure 5c shows the relationship between reaction rate constants and BET surface areas. Al-Fe/TiO2-400 sample owns the highest surface area of 340 m2/g, resulting in an excellent photocatalytic performance in oxidation of NO. Though the surface area of Al-Fe/TiO2-700 is similar to that of Fe/TiO2-400, the reaction rate constant of the formed is much lower that of the latter. Except for the effect of surface area, other factors such as the band gap and light adsorption capability also play an important role in controlling the photocatalytic performance of the catalysts. As shown in Figure 4b, the band gap of Al-Fe/TiO2-700 is 2.66 eV is higher than that of Fe/TiO2-400. Meanwhile, the light adsorption intensity of Al-Fe/TiO2-700 is much lower than that of Fe/TiO2-400.
4. Conclusions
Macro/mesoporous Fe/TiO2 was fabricated by soft-chemical synthesis in the presence of surfactants, followed by calcination. Such materials have been proved as a good photocatalyst for treating NO at air conditions for its special macro/mesoporous structures. The modification of Al2O3 can effectively increase the thermal stability of Fe/TiO2 with a very high surface area, resulting in an excellent photocatalytic performance during the oxidation of 400 ppb level of NO in air under visible light irradiation. The present work demonstrates that the hierarchical macro/mesoporous Fe/TiO2 photocatalysts are effective visible-light-driven photocatalytic functional materials for air purification.
Acknowledgments
This work was supported by the Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning, the National Natural Science Foundation of China (21007040, 21047009), Natural Science Funding of Shanghai (11ZR1426300), the Research Fund for the Doctoral Program of Higher Education (20103127120005), the Project supported by the Shanghai Committee of Science and Technology (10160503200), and by a Scheme administrated by Shanghai Normal University (8K201104).
References
- 1.
Chen X. Wang X. Fu X. 2009 Hierarchical Macro/Mesoporous TiO2/SiO2 and TiO2/ZrO2 Nanocomposites for Environmental Photocatalysis. Energy & Environmental Science, 2 8 (May 2009),872 877 , ISSN: 1754-5692 - 2.
Li G. Zhang D. Yu J. 2009 Thermally Stable Ordered Mesoporous CeO2/TiO2 Visible-Light Photocatalysts . ,11 19 (February 2009),3775 3782 ,1463-9076 - 3.
Machida M. Norimoto K. Watanabe T. Hashimoto K. Fujishima A. 1999 The Effect of SiO2 Addition in Super-Hydrophilic Property of TiO2 Photocatalys t. ,34 11 (June 1999),2569 2574 .0022-2461 - 4.
Nahar S. Hasegawa K. Kagaya S. 2006 Photocatalytic Degradation of Phenol by Visible Light-Responsive Iron-Doped TiO2 and Spontaneous Sedimentation of the TiO2 Particles . ,65 11 (December 2006),1976 1982 .0045-6535 - 5.
Rolison D. 2003 Catalytic Nanoarchitectures- The Importance of Nothing and the Unimportance of Periodicity. Science,299 5613 (May 2003),1698 1701 .0036-8075 - 6.
Wang X. Yu J. Chen Y. Wu L. Fu X. 2006 ZrO2-Modified Mesoporous Manocrystalline TiO2-xNx as Efficient Visible Light Photocatalysts. Environmental Science & Technology,40 7 (April 2006),2369 2374 ,0001-3936 X - 7.
Wang X. Yu J. Ho C. Hou Y. Fu X. 2005 Photocatalytic Activity of a Hierarchically Macro/Mesoporous Titania . ,21 6 (March 2005),2552 2559 ,0743-7463 - 8.
Wu N. Wang S. Rusakova I. 1999 Inhibition of Crystallite Growth in the Sol-Gel Synthesis of Nanocrystalline Metal Oxides . ,285 5432 (August 1999),1375 1377 ,0036-8075 - 9.
Yu J. Li G. Wang X. Hu X. Leung C. Zhang Z. 2006 An Ordered Cubic Im3m Mesoporous Cr-TiO2 Visible Light Photocatalyst. ,25 (September 2006),2717 2719 ,1359-7345 - 10.
Yu J. C. Wang X. Fu X. 2004 Pore-Wall Chemistry and Photocatalytic Activity of Mesoporous Titania Molecular Sieve Films . ,16 8 (April 2004),1523 1530 ,0897-4756 - 11.
Yuan Z. . Su L. 2006 Insights into Hierarchically Meso-Macroporous Structured Materials . ,16 7 (Febrary2006),663 677 ,0959-9428 - 12.
Zhu J. Ren J. Huo Y. Bian Z. Li H. 2007 Nanocrystalline Fe/TiO2 Visible Photocatalyst with a Mesoporous Structure Prepared via a Nonhydrolytic Sol-Gel Route. ,111 51 (December 2007),18965 18969 ,1932-7447