Open access peer-reviewed chapter

Spark Plasma Sintered High-Entropy Alloys: An Advanced Material for Aerospace Applications

By Ayodeji Ebenezer Afolabi, Abimbola Patricia I. Popoola and Olawale M. Popoola

Submitted: March 6th 2019Reviewed: May 14th 2019Published: October 10th 2019

DOI: 10.5772/intechopen.86839

Downloaded: 461


High-entropy alloys (HEAs) are materials of high property profiles with enhanced strength-to-weight ratios and high temperature-stress-fatigue capability as well as strong oxidation resistance strength. HEAs are multi-powder-based materials whose microstructural and mechanical properties rely strongly on stoichiometry combination of powders as well as the consolidation techniques. Spark plasma sintering (SPS) has a notable processing edge in processing HEAs due to its fast heating schedule at relatively lower temperature and short sintering time. Therefore, major challenges such as grain growth, porosity, and cracking normally encountered in conventional consolidation like casting are bypassed to produce HEAs with good densification. SPS parameters such as heating rate, temperature, pressure, and holding time can be utilized as design criteria in software like Minitab during design of experiment (DOE) to select a wide range of values at which the HEAs may be produced as well as to model the output data collected from mechanical characterization. In addition to this, the temperature-stress-fatigue response of developed HEAs can be analyzed using finite element analysis (FEA) to have an in-depth understanding of the detail of inter-atomic interactions that inform the inherent material properties.


  • spark plasma sintering
  • high entropy alloys
  • advance material
  • aerospace application

1. Introduction

1.1 Background/motivation

In the aerospace industry, the landing gear is essential for support during landing and ground operations in an aircraft. Manufacturers attach the landing gear to primary structural members of an aircraft and must bear the heavy compressive load. Therefore, when landing, the impact energy of the aircraft will be absorbed through the design and a minimized load transmitted to the airframe. Thus, materials used for landing gear application must be able to withstand high operating temperatures, fatigue, creep, cyclic and translational movement of parts at high-speed, and chemical, erosion, wear, and oxidation degradations [1, 2, 3]. The development of high-performance materials with superior characteristics for aerospace application has continually been the challenge faced by material engineers and scientists over the years. However, materials engineers constantly create and improve properties of materials by applying the existing knowledge of science to develop advanced engineering materials exhibiting better service performance through the development of various manufacturing techniques for different applications as shown in Figure 1 [4, 5, 6]. The traditional alloys used for commercial purposes were designed by choosing a core element which made up the matrix of the part and addition of elemental solutes to the primary base element [7, 8]. This basic element, which made up the matrix, was primarily titanium [9, 10, 11], vanadium [12], iron [13], aluminum [14], or nickel [15], amongst others, produced for the aerospace industry with outstanding benefits. According to the conventional alloying system, each element compensates each other’s deficiencies to give better properties of the alloy than to give the existence of the materials separately [16, 17]. However, the economy of the fabricated part with the conventional melting approach is the primary drive for research and development of powder metallurgy [18, 19, 20, 21].

Figure 1.

The evolution and characteristics of alloys.

Landing gear components are typically manufactured with advanced materials using conventional metallic materials such as aluminum alloy 7075 [22, 23, 24, 25, 26, 27, 28, 29, 30], alloys steel 4340 [31, 32, 33, 34, 35, 36], titanium 6Al-4V [37, 38, 39, 40, 41, 42], titanium 6Al-6V-2Sn [43, 44], titanium 15Al-3Cr-3Al-3Sn [45, 46, 47], and titanium 10Al-2Fe-3V [48, 49, 50, 51, 52]. The most versatile titanium alloys in the aerospace industry are titanium 6Al-4V, titanium 6Al-6V-2Sn, titanium 15Al-3Cr-3Al-3Sn, and titanium 10Al-2Fe-3V because of their excellent properties. In the class of beta titanium alloys, Ti-15Al-3Cr-3Al-3Sn and Ti-10V-2Fe-3Al have been adopted for different airframe applications and landing operations [53]. The alloy Ti-10V-2Fe-3Al has the capability to substitute precipitation-hardening steels due to its in-depth hardenability and exceptional ductility. When it was successfully used in a Boeing 777 aerospace landing gear, the alloy Ti-10V-2Fe-3Al came to limelight. Initially, the alloy cost was higher than that of 4340 steel used in applications for landing gear [35]. However, the cost-benefit of using the alloy was achievable in the long run as the steel parts needed to be replaced due to potential susceptibility to stress corrosion cracking [54]. The alloy is therefore applied in many airframe applications of landing gear, wings, fuselage, doors, and cargo handling structures. Similarly, titanium alloys were not impressive for load-bearing components because of uneven stress distribution on parts during operation [55]. The nomenclature of typical landing gear is shown in Figure 2, comprising axie, shock, and drag strut, walking beam, and torsion links which are made up of Ti-10V-2Fe-3Al.

Figure 2.

The nomenclature of main landing gear bogie truck.

Ti-10V-2Fe-3Al popularly used in landing gear and slat/flap tracks was successfully fabricated using alloy forgings [56, 57]. Tracks are the dynamic beams allowing load transmission and movement between wings and moving slats. They are generally produced from maraging steel. Recently, Ti-10V-2Fe-3Al has been made of flap tracks fitted on the trailing side of the wings to perform similar functions. The total weight saving in Boeing 777 was about 40 kg by using six 5 ft. long flap tracks. The assessment of Ti-10V-2Fe-3Al’s corrosion resistance is very important given its widespread use as structural parts that are susceptible to wear and corrosion in simulated environments through which an aircraft flies, which also makes the material not exceptional, and surface damage occurs in applications involving contact loading. In regard to this, Arya et al. [58] investigated the electrochemical corrosion performance of Ti-10V-2Fe-3Al alloy in different corrosive media namely, artificial seawater solution, Hank’s solution, 0.5 M sulfuric acid, and 0.5 M hydrochloric acid solution. The authors used open circuit potential, current transient time, Tafel extrapolation potentiodynamic polarization curves, and electrochemical impedance spectroscopy to evaluate the corrosion rates. The results show that due to the formation of thick, compact, and stable passive film, this alloy has a lower corrosion rate in alkaline solution. Corrosion rate in acid solution is higher because the passive film is less compact, porous, and unstable. Li et al. [59] used a high-frequency push-pull fatigue testing machine to report the effect of fretting on the fatigue performance of Ti-6Al-4V and Ti-10V-2Fe-3Al alloys. For comparative analysis of the fretting effect on the fatigue performance of the different titanium alloy, the author obtained both plain and fretting fatigue curves. The result shows that Ti6Al4V titanium strength and plain fatigue are lower than Ti-10V-2Fe-3Al titanium strength. But the fretting fatigue of Ti6Al4V titanium is higher under each contact stress. The fatigue source depth of Ti-10V-2Fe-3Al alloy is greater than that of Ti6Al4V alloy. Hardening of Ti-10V-2Fe-3Al alloy is more serious after fretting. The wear mechanism of two titanium alloys is different; Ti1023 titanium alloy is more sensitive to fretting wear. According to Li et al. [60], the mechanical behavior of the Ti-10V-2Fe-3Al alloy under the high-temperature and dynamic loading conditions and the microscopic observations show that the microstructure of Ti-10V-2Fe-3Al alloy is sensitive to the external thermal loading. As the testing temperature is lower than the β phase transus, the β phase concentration almost remains unchanged besides a few of the refinement and spheroidize of β phase grains, which results in maintaining the high yield strength of the alloy. When the testing temperature is higher than the β phase transus, the thermal loading and mechanical loading can respectively cause various refinements and spheroidize of the β phase grain of alloy, which remarkably decreases the yield strength of the alloy. Based on the resulting stress and strain data obtained in simple shear, the high-temperature dynamic shear deformation mechanisms have been evaluated by using the characteristics of stress-strain behavior caused by thermal loading and mechanical loading. The high-temperature dynamic constitutive model is established based on the experimental results.

Utama et al. [61] reported surface height irregularities that occurred during machining Ti-10V-2Fe-3Al beta (β) titanium alloy. The author observed the height differences in two different regions, “soft region” and “hard region.” The hard region has higher Fe and lower Al content, resulting in higher β-phase stability to resist the precipitation of the primary alpha (αp) phase caused by a solution treatment process failure. By contrast, a higher volume fraction of the αp phase and a lower volume fraction of the matrix consisted of a combination of β and secondary alpha (αs) phase.

A high number of αs/β interfaces in the matrix with a predicted 520 HV hardness resulted in harness improvement of the hard region. Hence, the hard and soft regions had different wear resistance capabilities during the machining process, resulting in surface height irregularities. Jiao et al. [62] reported that a complicated and unique phase transformation process takes place with forming different microstructures from forging and reconstruction method to study the spatial distribution of α phase in different grains present in the Ti-10V-2Fe-3Al alloy specimen. Since the process involves repeated heating and cooling during deposition, there was development of the complex and unique phase transformation process in the different microstructures. Their results showed plate-like morphology formation of α laths in the deposited alloy, and a tetrahedral relationship followed their precipitation from the β phase. The different orientation of the grain results in different specific morphologies. The α laths are perpendicular to each other when the cutting plane is parallel to the (100) plane of the BCC cell. If the cutting plane is parallel to the plane (111), a special morphology is established with a mixture of plate-like and rod-like phase α. Liu et al. [63] examined the evolution of microstructure and compression properties of Ti-10V-2Fe-3Al titanium alloy and solution treatments at temperatures ranging from 710 to 830°C, followed by treatment with aging. Ti-10V-2Fe-3Al alloys with α + β-phase have higher mechanical properties than single β-phase alloys. The content of the equiaxed α phase decreases with the increase in solution temperature. As a result, the alloy strength increases as the plasticity decreases. The highest yield strength value of 1668 MPa was obtained in the sample treated with a solution of 770°C treated for 2 hours, then water quenched and 520°C aging for 8 hours followed by air cooling. The stress-induced phase of martensite α” appeared in the sample solution treated at 830°C after dynamic compression of SHPB.

Tabachnikova et al. [64] measured the influence of temperature on Young’s modulus for different structural states by mechanical resonance spectroscopy. The heat treatment of the samples led to an increase (∼25%) of Young’s modulus. Ren et al. [65] established that “Ti-10V-2Fe-3Al has the tendency to spall in a brittle-ductile mixed fracture manner with very rough fracture surfaces covered by ductile dimples”. The authors investigated the spall fracture behavior of a typical metastable β-titanium alloy, Ti-10V-2Fe-3Al, by subjecting it to shock loaded through a series of plate impact tests. The microstructural characteristics of the spall planes were systemically investigated for the influence of the shock-induced SIM phase transformation on the fracture behavior of the β-titanium alloy. The authors concluded that the spall strength of Ti-10V-2Fe-3Al is ca. 3.1 GPa at shock pressure below 8.5 GPa dropped by nearly 20% as the shock pressure exceeds 9 GPa due to the abundance of SIM phases with increased shock pressure. The microvoids in the spalled Ti-10V-2Fe-3Al mainly nucleate at the intersections of the grain boundary and the α martensite lath, which obviously showed that the shock-induced β-to-α martensite phase transformation strongly affected the spall fracture behavior of this alloy. The shock-induced β-to-α phase transformation has a detrimental effect on the spallation resistance of titanium alloys, which should be minimized in structural materials of titanium alloys that need to withstand shock wave loading. Srinivasu et al. [53] reported the presence of continuous grain boundary in Ti-10V-2Fe-3Al which is surrounded by a softer precipitate-free zone that leads to flow localization, thereby influencing fatigue crack propagation. The authors therefore studied the effect of processing and heat treatment on the tensile properties and fracture toughness of Ti-10V-2Fe-3Al, a high-strength metastable beta titanium alloy. The alloy was subsequently subjected to thermomechanical processing that included combinations of rolling and solution heat treatment in both α-β and β phase fields. The rolling temperatures ranged from 710°C (sub-transus) to 860°C (super-transus) and the temperatures of the solution treatment ranged from 710°C (sub-transus) to 830°C (super-transus). A systematic microstructural investigation (optical as well as scanning electron microscopy) was undertaken to correlate the property trends with the underlying microstructure, which is strongly dependent on the sequence of thermomechanical processing. A subtransus rolling followed by subtransus solution treatment resulted in a morphology being equiaxed while a super transus rolling followed by subtransus solution treatment resulted in a phase being more acicular/lenticular in morphology. While α-β rolling followed by α-β heat treatment gave better tensile properties, α-β heat treatment followed by β rolling resulted in superior fracture toughness.

In recent years, research has shown that advanced engineering materials used in industries are susceptible to corrosion and fatigue-related failures [66]. Authors attribute these challenges to design shortcomings, poor selection of materials, beyond the design limits, overloading, insufficient maintenance, and manufacturing defects [67]. The resulting repair and replacement costs take up almost half of the total budget; therefore, the performance of materials, particularly fatigue and corrosion resistances, has received widespread attention. According to Hemphill [68], the major drawback of this material is the formation of microcracks, which developed during fabrication as a manufacturing defect causing severe fatigue challenges. Current applications of Ti-10V-2Fe-3Al mainly in the wide range of aircraft structural components [69] are exceeding 200 flying components in each Boeing 777 alone [70, 71]. These applications were made by ingot metallurgy and forging [72], based on Boeing’s original development for use in the Boeing 757 [73]. However, a primary problem with the process is the high buy-to-fly ratio [74], which results in about 90% scrap or a material utilization factor of just as much as 10%. Another issue is the severe segregation of α and β phases in the Ti-10V-2Fe-3Al as-cast ingot due to the presence of α and β stabilizers at 15 wt.%. This results in the so-called “beta flecks” in the forged microstructures [69].

Powder metallurgy (PM) allows the manufacture of near-net shape and effectively eliminates segregation by using micrometer-sized powder materials [69, 75]. There are many advantages of powder metallurgy compared to the conventional process in terms of fabricate titanium-based composite, low cost, full densification, no segregation, no inner defect, internal stress, excellent stability, and uniform microstructure. The high buy-to-fly ratio associated with many titanium components, combined with difficulties in forging and machining and recent availability issues, has resulted in a strong drive for near-net titanium manufacturing. PM [76]. is a very promising way to achieve this goal. Accordingly, a variety of PM-based techniques have been implemented to fabricate Ti-10V-2Fe-3Al using either pre-alloyed powder or titanium or TiH2 and master alloy powder blends [71, 77]. Generally, fully dense Ti-10V-2Fe-3Al alloy consolidated by hot isostatic pressing (HIP), or HIP + forging, with or without subsequent solid solution treatment and aging [78], can achieve tensile properties such as wrought alloys. Technically, the simplest and most attractive PM manufacturing route is the cold compaction and sinter approach [69]. Its potential for titanium manufacturing on a variety of titanium materials [79] has been well demonstrated. Although Ti-10V-2Fe-3Al’s tensile properties were previously reported [80], the densification process, sintering mechanism, microstructural evolution during sintering, and their correlations with sintered mechanical properties were not given sufficient details. In contrast, the literature on powder-based titanium alloy manufacturing has focused largely on Ti-6Al-4V, with a focus on achieving full densification with respect to different manufacturing conditions [80, 81]. Therefore, there is an ultimate need to understand and establish the fundamentals of the cold-compaction-and-sinter PM approach for the fabrication of high strength or specialty solute rich titanium alloys such as Ti-10V-2Fe-3Al.

Spark plasma sintering (SPS) has been applied in the preparation of alloys, functional materials, ceramics, cermets, nanocomposites, and intermetallic compounds [82]. In recent times, extensive efforts were made towards research and development of SPS as a promising technique for high entropy alloys. Unlike conventional sintering methods, which usually use alternating heat current [83], SPS uses an on-off pulse current to heat the graphite die directly to complete the sintering process. Considering the SPS sintering mechanism, it is specifically assumed that an electrical field is formed between grains during sintering and high-temperature plasmas are excited under the action of pulse current to cause a cleaning effect on the surface of particles, leading to a sintering enhancement [84]. The spark plasma sintering method has several advantages over other conventional sintering techniques like hot pressing, mechanical alloying, and isostatic pressing due to high chances of sintering materials of near full densification and little grain growth [85]. SPS unique features also include a low heating profile, which makes it possible to sinter powders with controlled grain size and limited chemical interaction with other constituents [86]. The SPS method has proven its high effectiveness in fabricating ceramic composites and alloy materials for nano-applications, biomaterials, and electronic materials. From the traditional alloy design concept of titanium 10Al-2Fe-3V, however, HEAs are not based on a single element but on multi-component systems consisting of at least five main elements in an equal or near-equal atomic percentage (at.%) with no noticeable difference between the solute and the solvent [87]. According to existing physical metallurgy and phase diagrams, such multi-element alloys can produce many phases and intermetallic compounds, resulting in complex and fragile microstructures that are difficult to analyze and engineer but are likely to have finite practical values [88]. Experimental results indicate, beyond expectations, that the higher mixing entropy in these alloys enhances the formation of random solid-solution phases with simple structures such as face-centered cubic (FCC) structures [89], body-centered cubic (BCC) structures [90]), or hexagonal close packing (HCP) structures [91], thereby reducing the number of phases [89, 92, 93]. The new alloy design strategy has since opened up an enormous, unexplored multi-component alloy field. The alloy design strategy has achieved unimaginable successes, and great efforts have been devoted to the development and application of many HEAs [94], in various fields because of their excellent performance, such as unique wear resistance [95], excellent strength and thermal stability at elevated temperatures [96], superior high elongation [93], high fatigue, and fracture toughness [97]. Han et al. [98] showed that the “addition of Ti is beneficial to the strength and the compressive ductility of the HEAs at room temperature”. The authors presented a new refractory HEA alloy of TiNbMoTaW fabricated from addition of Ti to NbMoTaW alloy. The new TiNbMoTaW HEA was found to have a BBC phase structure that can be maintained even after 24-hour annealing at 1200°C. The room temperature yield strengths and compressive plastic strains of the developed TiNbMoTaW and TiVNbMoTaW HEAs have been significantly enhanced in comparison with the mechanical performance of HEAs NbMoTaW and VNbMoTaW. Also, with impressive yield strengths of ~586 and ~659 MPa at 1200°C, the TiNbMoTaW and TiVNbMoTaW HEAs showed very promising high-temperature strength. As a result of these property profiles, it was suggested that the newly developed TiNbMoTaW and TiVNbMoTaW HEAs have potentials in applications of high-temperature structural materials.

Consequently, extensive research has been conducted to develop next-generation aerospace materials with high mechanical performance and superior corrosion resistance to achieve improvements in both performance and cost repetition. For traditional alloys, one or two principal components are selected based on a specific property requirement, and other alloying components are added to further improve their properties because of the huge formation of bulk intermetallic compounds which occurred as a result of the atomic ratios of elements reaching a 40% mark and above. Thus, this depletes the reliability of the alloy during service. Therefore, the search for an alloy with atomic ratios lower than 35% commenced in 1996 [99]. Hence, the possibility of combining several metallic principal elements in equal atomic compositions was explored and it was named high-entropy alloys (HEAs). HEAs always have the combination of at least five principal elements, each with an atomic percentage (at. %) between 5 and 35%. Generally, the atomic percentage of each minor element, if present at all, is always smaller than 5. The definition is expressed as follows in Eqs. (1) and (2) [94, 102]:


where nmajor represents the major elements, nminor represents the minor elements, ci represents the atomic percentages of the major element, and cj represents the atomic percentages of the minor element.

This definition shows that HEAs need not to be equimolar or near-equimolar, and even contain minor elements to balance various material properties [100]. HEAs can easily be formed into simple FCC phase structures [101], BCC [102], and HCP [91] solid-solution structures. One renowned HEA is an equimolar-shaped Cantor alloy [102] consisting of Fe (BCC), Co (HCP), Cr (BCC), Mn (BCC), and Ni (FCC), with a solid-solution FCC phase when dendritically cooled in the as-shaped sample. Then, by adding Cu (FCC), Nb (FCC), or V (BCC), the five-component alloy was extended to a six-component alloy system, showing the simple solid-solution FCC structure in the as-cast alloy with different lattice parameters. When the HCP type Ti was added, a solid-solution phase of the FCC formed a BCC structure [103]. Another typical example is the AlxCoCrFeNi (molar percentage, 2 ≥ x ≥ 0) system prepared by arc melting [104]. The CoCrFeNi as-cast alloy has a solid-solution phase of pure FCC. The AlxCoCrFeNi system changes the crystal structure from FCC to FCC + BCC phases by increasing the Al molar percentage from 0 to 2 and finally to a single BCC phase [104]. A typical TaNbHfZr alloy has a structure with only BCC [105].

Alloy design is a novel means of maximizing and synergizing metal counterparts in HEA multi-material systems. The design encompasses several considerations such as atomic radius, solid solution solubility, powder stoichiometry, processing technique, and the processing conditions or parameters chosen. Thus, HEAs possess dynamic and exceptional properties, such as high hardness and strength profiles, good oxidation and corrosion resistance, and high-temperature softening resistance, which are crucial in prospective engineering applications. HEAs fabricated by SPS have been reported to possess excellent densification properties, as well as high strength and hardness profile. Mohanty et al. [106] research output on a multicomponent equiatomic AlCoCrFeNi high entropy alloy developed by spark plasma sintering established a high mechanical strength. The sintered samples at the optimum temperature of 1273 K displayed the highest microhardness. Fang et al. [85] also researched the mechanical behavior of Al0.5CrFeNiCo0.3C0.2 high entropy alloy. They recorded a compressive strength of 2131 MPa and a Vickers microhardness of 617 HV of the Al0.5CrFeNiCo0.3C0.2 high entropy alloy. Zhao et al. [107] fabricated HEAs on a carbon steel substrate via spark plasma sintering, which are considered as excellent coating materials due to their high hardness, good wear, and corrosion resistance. The microstructure evolved from FCC to FCC + BCC mixed structure. AlxCrFeCoNiCu (x = 0, 1, 2, 3) coating has an average hardness of approximately 682 HV0.2, which is the highest hardness in all the HEA coatings. Compared with AISI 52100 steel, spark plasma sintered Al2CrFeCoNiCu and Al3Cr-FeCoNiCu HEA coatings show exceptional sliding wear resistance and extremely low friction coefficient in comparison with AISI 52100 steel. Al3CrFeCoNiCu HEA coating wear resistance is approximately four times better than that of bearing steel, showing a promising application as a wear-resistant material According to Chen et al. [108], research outputs of several literature studies indicate that the addition of Ni to Ti-10V-2Fe-3Al is beneficial to the improved mechanical performances of the HEA, making the HEA a good material for high-temperature applications. Nickel is the fifth most common element on earth’s crust. As a high-profile element with a good property suited for diverse applications especially that of the aerospace industry, there is no substitute for Ni without reducing performance or increasing cost. The biggest use of nickel is in alloying, particularly with chromium and other metals to produce stainless and heat-resisting steels constituting 65% production [109]. Another 20% is mostly used for highly specialized industrial, aerospace, and military applications. With characteristic melting point of 1453°C, Ni has reliable corrosion and oxidation properties, and readily forms alloys [110, 111].

Chromium, on the other hand, is generally used in metallurgy to impart corrosion resistance, and it also has good strengthening effect of forming stable metal carbides at the grain boundaries of its alloying counterpart [112, 113]. Chromium has excellent mechanical properties such as high corrosion and wear resistance. Therefore, in alloying, it finds a good match with Ni to form Ni-Cr alloys when used with Ti-10V-2Fe-3Al for making landing gear, wind turbine, engine components, and many other industrial and mechanical components where high wear-resistance is needed such as in aerospace applications. The structure of Ni-Cr alloys depends on the percentage composition of nickel or chromium, and the temperature. It is noteworthy that Ni-Cr alloys will be dominated by the π phase, which tends to be brittle at about 60–75% Ni addition. The crystal structure of the FCC is found in the γ phase, and the γ phase shows improved strength and ductility in comparison with the σ phase. The FCC crystal structure is commonly found in Ni-rich alloys, while the BCC crystal structure tends to be found in Cr-rich alloys. The γ phase Ni-Cr alloy can be converted into the ε phase at high pressures, which shows an HCP crystal structure. The alloying element helps stabilize the BCC structure of Ti-10V-2Fe-3Al HEA, increasing the hardness and plastic strain of the alloy. However, there are limited publications in the literature on Ti-10V-2Fe-3Al alloy with Ni and Cr additions, despite the different manufacturing routes that had been established. Moreover, reports investigating the fatigue, corrosion, and oxidation behaviors of spark plasma sintered Ti-10V-2Fe-3Al-Ni-Cr HEAs with their potential applications are scarce. Therefore, this work proposes to use the spark plasma sintering manufacturing technique to synthesize novel Ti-10V-2Fe-3Al-Ni, Ti-10V-2Fe-3Al-Cr, Ti-10V-2Fe-3Al-Ni-Cr, and Ti-V-Fe-Al-Ni-Cr high entropy alloys (HEAs) for making landing gear. Thereafter, the synthesized alloys will be characterized in terms of microstructure, composition, and phase transformation using optical microscopy (OM), X-ray diffraction (XRD), and scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDX), respectively. Also, the mechanical and electrochemical properties of the materials will be carried out, and the effects of temperature and stress distributions of the high entropy alloy material during the SPS process will be modeled.


2. Conclusion

From the open literature above, the authors agreed that the current market material (Ti-10V-2Fe-3Al) used in high-temperature applications such as gas turbine and turbine engine in the aerospace industry experience several failures such as high-temperature oxidation and corrosion, limited hardness, and wear resistance. It is confirmed that spark plasma sintering is a potential way to fabricate HEAs which possess properties such as improved microhardness, compressive/tensile strength, tribology, thermal properties, and corrosion resistance properties for low and high-temperature applications as generally agreed by all the authors. Also, it is generally accepted by the authors that SPS processing parameters play a significant role in the mechanical properties of the final developed alloys. The authors concluded that HEAs are the potential replacement for nickel-based superalloys in high-temperature applications. Furthermore, the authors agreed that it is possible to simulate the SPS process by means of finite element modeling. However, SPS simulation of thermal distribution and stress distribution analysis for the development of HEAs are limited in the open literature. Thus, this paper exposes the influence of spark plasma sintering parameters on the mechanical properties of the synthesized alloy.

© 2019 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Ayodeji Ebenezer Afolabi, Abimbola Patricia I. Popoola and Olawale M. Popoola (October 10th 2019). Spark Plasma Sintered High-Entropy Alloys: An Advanced Material for Aerospace Applications, Recent Advancements in the Metallurgical Engineering and Electrodeposition, Uday Basheer Al-Naib, Dhanasekaran Vikraman and K. Karuppasamy, IntechOpen, DOI: 10.5772/intechopen.86839. Available from:

chapter statistics

461total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

Related Content

This Book

Next chapter

Cutting Superhard Materials by Jet Methods (on Functional Approach)

By Alexandr Salenko, Viktor Shchetynin, Galina Gabuzian, Evgeny Lashko, Mohamed R.F. Budar, Sergey Klimenko and Alexandr Potapov

Related Book

First chapter

Introductory Chapter: A Brief Introduction to Porous Ceramic

By Uday M. Basheer Al-Naib

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us