1. Introduction
Ferroelectric perovskites based on Na0.5Bi0.5TiO3 (NBT) are considered among the most promising lead-free candidate materials to substitute Pb(Zr
Solid-solution systems based on lead-free perovskites like Na0.5K0.5NbO3 (NKN), BaTiO3 (BT), Na0.5Bi0.5TiO3 (NBT) or bismuth layered-structured SrBi2Ta2O9 (SBT), and SrBi2Nb2O9 (SBN) are considered as viable alternatives for replacing lead-based materials. For example, (K,Na)NbO3–LiTaO3–LiSbO3 alkaline niobate ceramics exhibit a
The solid solution with BaTiO3, (1-x) NBT-x BT shows a morphotropic phase boundary (MPB) between the rhombohedral and the tetragonal phase, at x between 0.06 and 0.07 for which the material properties are considerably improved. Indeed d33 values up to 450 pC/N, and huge electric field-induced strain have been reported [4, 5]. Figure 1 shows the crystalline structures of the NBT and BT end members at room temperature. Perovskite structure deformations include oxygen octahedral rotations around different axis and cation shifts, therefore giving rise to a complex succession of ferroelastic and ferroelectric phase transformations with temperature variation.
Due to this polymorphic structure, NBT and NBT-BT have been also intensively studied in order to clarify their complicated phase transitions, which still pose questions [6]
For NBT-BT thin films growth many techniques have been used. Guo
However, despite the fact that ferroelectric materials with MPB have enhanced ferroelectric and piezoelectric properties, it is difficult to transpose them in thin films since MPB is limited to a small composition range. Almost all the physical parameters involved in thin films deposition like the substrate type, the microstructure and stress have strong impact on their physical properties [17]. In some previous papers we have investigated the role of different deposition parameters on NBT-BT film growth and properties [18, 19]. In this chapter, we discuss the role of certain experimental conditions like deposition temperature and substrate type, as well as of the amount of BT present in the target on crystalline structure, microstructure, dielectric properties, phase transition temperatures and stability limits of ferroelectric phases in NBT-BT thin films produced by PLD.
2. Experimental method
Pulsed laser deposition (PLD) was used for the film growth. The targets with composition (NBT)1-
For the film deposition, a Surelite II Nd:YAG pulsed laser with wavelength of 265 nm, pulse duration of 5 ns and frequency 10 Hz, has been employed. The laser fluence was set at 1.6 J/cm2. The films were grown on Nb:STO and Pt/TiO2/SiO2/Si substrates, placed at a distance of about 4.3 cm from the target. Different sets of films have been grown at different substrate temperatures, ranging between 650-730 oC. Deposition and after-deposition cooling were performed in flowing oxygen atmosphere (0.3-0.6 mbar) to favour the formation of perovskite phase without oxygen vacancies. Chemical composition was checked via SIMS technique using a Hiden SIMS/SNMS system. The thickness of the thin films, evaluated by spectroellipsometry, was between 300-500 nm.
For the investigation of the crystalline structure of the targets and films, a PANalytical X’pert MRD diffractometer in Bragg-Brentano geometry was used. The measurements were performed with a step size of 0.020 and with a scanning time on step of 25 s or 250 s, depending on the angular range.
The film surface morphology was examined by AFM (model XE100, Park Systems). Piezoelectric force microscopy measurements were performed with a PFM system which includes a lock-in amplifier SR-830 and a dc- high voltage amplifier WMA-280. Conductive all-metal Pt tips were employed for these measurements were the switching characteristcs of the films have been tested.
Several Au electrode dots with an area of about 0.22 mm2 have been evaporated through a mask on the films for electrical characterization. Polarization hysteresis was measured by using a Radiant Technology RT66A ferroelectric test system, in the virtual ground mode. The dielectric measurements were carried out in a frequency range between 200 Hz and 1 MHz using an HP 4194A impedance analyzer and an HP 4284A LCR meter with a four wire probe. The measurements were performed at 1.5 K/min between 300 and 570 K in a Delta Design climatic chamber model 9023 A (on targets) and in a Linkam variable-temperature stage (model HFS 600E) on films.
3. Results and discussion.
3.1. Growth mode of NBT-BT thin films.
The microstructure of ceramic thin films is one of the most important factors that influence their physical properties. Since the growth mode of thin films is strongly dependent on the substrate type, we investigated the deposition of NBT-BT thin films on two different types of substrates:
single crystal SrTiO3: Nb (Nb:STO) and
Pt/TiO2/SiO2/Si.
The AFM pictures obtained on the two sets of films show important microstructural differences, mainly due to different growth mechanisms. In Figure 2 we show AFM images taken on a NBT-BT6 film deposited on Nb: STO monocrystalline substrate at 650 0C. It can be observed that a first stage of growth resulting into a continuous layer stops when the critical thickness for misfit dislocations (probably a few tens of nm) is reached. After that, the growth continues in platelet-like form (see details in Fig. 2 b). If the deposition temperature is not sufficiently high to favor material exchange between platelets via surface migration, successive layers will grow on the top of the first islands and the growth will result into a discontinuous layer. This explains the platelet-like aspect of the film shown in Figure 2.
However, raising the substrate temperature to 700 0C during the deposition of a second set of films while keeping constant all the other parameters, including the number of laser pulses, produces a uniform layer of continuous platelets, on top of which new islands nucleate (Figure. 3).
A rather different morphology is displayed by NBT-BT films grown on Pt/TiO2/SiO2/Si (Fig. 4 and 5). In this case, the growth progresses from the beginning in island-like form since the polycrystalline Pt layer provide the nucleation sites for their formation. Moreover, these NBT-BT islands grow on the Pt layer without preserving a unique orientation, due to the same reason. Instead films grown on Nb:STO monocrystalline structures are uniaxially (001)-oriented, as it will be shown in the next section.
A fine microstructure with grain size ranging from a few tens of nm up to a few hundred of nm is displayed by NBT-BT6 films (Fig. 4). We note the striking difference with bulk samples microstructures (not shown here), which consists of crystallites of 1-10 μm size.
A similar fine microstructure is displayed by NBT-BT8% films grown on Pt/TiO2/SiO2/Si (Fig. 5 a). However, the enlarged AFM image displayed in Fig 5 b) reveales a somewhat different aspect with triangular nanograins lying in plane.
3.2. Crystalline structure
The XRD spectrum of NBT-BT6 target corresponds to a mixture of rhombohedral R3c and tetragonal P4mm phases, as shown by the splitting of (111) and (200), (012) and (024) rhombohedral peaks in the bottom pattern in Fig. 6 [20]. The main Miller index of the rhombohedral phase are depicted horizontally on the bottom of the figures while those of the tetragonal phase vertically above. On the same graph, the pattern corresponding to the NBT-BT6 film grown on Pt/TiO2/SiO2/Si at 700 0C is given. The curve corresponding to NBT-BT6/Pt/TiO2/SiO2/Si film deposited in the same conditions but at a substrate temperature of 6500 exhibits similar features as we had reported and is not presented here [18].The as deposited thin films exhibit pure perovskite phase with symmetry congruent with that of the target. The reflection peaks indicate a randomly oriented structure, consistent with the polycrystalline nature of the films.
Figure 7 displays the XRD patterns of NBT-BT6 films deposited at two temperatures, 650 0C and 700 0C, around the (100)/(001) and (200)/(002) reflections of the Nb:STO substrate. The spectra indicate the epitaxial growth of NBT-BT6% films on the Nb:STO substrate at the two temperatures. This feature is congruent with the microstructure shown in the previous section (Fig. 2 and Fig. 3), consisting of large platelet-like crystallites which preserve the same axis of orientation with the monocrystalline substrate.
Figure 8 shows the XRD patterns of NBT-BT8 films grown on Pt/TiO2/SiO2/Si and Nb:STO substrates at 700 0C. The grey pattern represents the NBT-BT8 target spectrum, which corresponds to the tetragonal P4mm symmetry. It can be observed that, similar to the previous composition, the growth on single crystal Nb:STO substrate produces an epitaxial film, while the growth on Pt/TiO2/SiO2/Si substrate results into a polycrystalline randomly oriented film.
3.3. Dielectric and ferroelectric properties
The dielectric and ferroelectric properties of NBT-BT thin films have been evaluated on capacitors formed by evaporating through a mask an array of gold electrode dots with an area of about 0.22 mm2 on the surface of films grown on Pt/TiO2/SiO2/Si and Nb:STO substrates. The bottom electrode was formed by the Pt layer in the first case or by the Nb:STO substrate itself in the second case.
The piezoresponce force microscopy results are presented in Figure 9. The full-Pt tips were brought in contact with the surface of the sample and then a
In Fig. 10 the room temperature dielectric properties of NBT-BT6 films deposited on Pt/TiO2/SiO2/Si at different substrate temperatures, 650 0C and 730 0C, have been compared in the frequency range 100 Hz-1 MHz. Films grown at 650 0C show a higher dielectric constant (ε’ ~ 1000), in the order of magnitude of the bulk values (ε’bulk ~ 1900), while films grown at 730 0C show lower values (ε’ ~ 700). The dielectric loss values are instead comparable in the two samples, and similar to bulk values.
Figure 11 displays the room temperature dielectric constant and dielectric loss in the frequency range 100 Hz-1 MHz for NBT-BT8 films grown on Pt/TiO2/SiO2/Si at different temperatures: 650, 700 and 730 0C. Unlike the previous composition, in this case growth at higher substrate temperatures was beneficial for the improvement of dielectric properties, at least in the frequency domain up to a few hundred kHz. Above this frequency there is a strong increase of dielectric loss. Since an increase is registered also in the dielectric constant, this could be caused by a relaxation mechanism which is active at room temperature at these frequencies, like e.g. free charge relaxation.
Polarization hysteresis measurements on NBT-BT6 films grown on Pt/TiO2/SiO2/Si are shown in Fig. 12. Spontaneous polarization was about 30 μC/cm2 and the remnant polarization was about 10 μC/cm2. The rather high value of coercive field (100 kV/cm) could be explained by the presence of intrinsic strain and pinning defects.
Dielectric and ferroelectric properties measurements on films deposited on Nb:STO substrates have been less reliable, probably due to the presence of a non-ohmic contact at the NBT-BT film – semiconductor Nb:STO interface. However PFM measurements (not shown here) evidenced good piezoelectric response, which indicates good intrinsic dielectric and ferroelectric properties, although quantitative values are difficult to extract.
3.4. Phase transitions
Phase transitions in ferroelectric materials are accompanied by anomalies of complex dielectric permittivity variation with temperature, generally narrow peaks or steps, depending on the type of phase transformation. However NBT-BT compositions near the morphotropic phase boundary behave as relaxors, due to the cation disorder. This is evidenced in Fig. 13 for NBT-BT8 bulk material. The main characteristic of a relaxor ferroelectric is a broad dielectric peak at a temperature Tm which is not related to a structural transformation. This is due to a wide distribution of relaxation times which characterizes the dielectric response of polar nanoregions. This peak shifts with the increasing of the measurement frequency toward higher temperatures. Thus the dielectric maximum of NBT-BT8 shifts from about 497 K at 200 Hz to about 512 K at 100 kHz. A similar dependence is obeyed also by the dielectric loss.
In Fig. 14 the variation of dielectric constant and loss with temperature for a NBT-BT8 film deposited on Pt/TiO2/SiO2/Si is shown. The maximum of the dielectric constant occurs at about 485 K, not far from bulk Tm. However the anomaly is characteristic of a well-behaved phase transition, since the peak temperature Tm does not shift with frequency. A similar qualitative behavior was observed also on the dielectric permittivity variation with temperature for NBT-BT6 films (not shown here).
While the dielectric permittivity peak position Tm ~ 485 K does not shift with measuring frequency, peak height is strongly dependent on it, decreasing for higher frequencies. This can be attributed to the possible presence of a non-polar dielectric layer, which does not influence the general behavior at phase transition, but can modify the value of the dielectric constant [23]. Generally these interface layers can have strong frequency-dependent dielectric properties which influence the overall properties of the heterostructures. However we stress again that the dependence on temperature and phase transition temperatures can be influenced only in the limits of a monotonous contribution, since the dielectric behaviour of non-polar layers is free of temperature anomalies. Indeed the stronger variation with temperature of the peak intensity at Tm could be attributed to the non-polar layer contribution at higher temperatures due to conductivity variation.
The temperature Td where a strong increase of dielectric loss and dielectric constant occurs marks the ferroelectric – antiferroelectric phase transition which, in bulk samples with the same composition is visible only in the poled state. It is called also depolarization temperature.
An apparent frequency dependence of the step increase in tanδ which marks Td is visible on the lower curves in Fig. 14. This could be attributed to a partial relaxor behavior due to mixed nanodomains-normal ferroelectric domains, which can be find also, but in proportion displaced to the nanodomain limit, in bulk samples. We must remark that the films were not poled, since no bias electric field was applied. Therefore the occurrence of a ferroelectric ground state in the NBT-BT films, in striking contrast with relaxor bulk samples with the same composition, must be generated by some intrinsic differences between ceramic bulk samples and ceramic thin films. The first and most obvious reason could be related to the constraining stress of the substrate on the thin films. This is strong in epitaxially grown thin films with a thickness generally below 100 nm, but it should be almost absent in polycrystalline films, randomly oriented and with a thickness of several hundreds of nm. This last one is the case for NBT-BT thin films deposited on Pt/TiO2/SiO2/Si substrates. The second reason could be related to the strong differences in the microstructures of ceramic thin films and bulk materials with the same composition. Therefore the occurrence of a ferroelectric ground state instead of a relaxor state in NBT-BT films, as well as the occurrence of a true ferroelectric phase transition could be due to the constrainig imposed by the nanograin boundaries on the ensemble of polar nanoregions.
4. Conclusions
In summary, we have investigated the role of deposition temperature and substrate type as well as the amount of BT present in the target on crystalline structure, microstructure, dielectric properties, phase transition temperatures and stability limits of ferroelectric phases in NBT-BT thin films grown by pulsed laser deposition. We have successfully deposited pure perovskite epitaxial films on single-crystal Nb:STO substrates. Successful growth of NBT-BT films on platinized silicon substrates has been achieved. Good dielectric and ferroelectric properties, comparable with bulk values, have been obtained. The NBT-BT6/Pt/Si thin films show a classic switching behavior, the piezoelectric hysteresis and pronounced imprint confirming the piezoelectric and ferroelectric characteristics. The locally measured value of effective piezoeletric coefficient d33 eff was around 83 pm/V, higher to the previouslly reported values for pure NBT or lead-based thin films. An enhanced stability of ferroelectric phase in thin films with respect to bulk has been observed and explained by their peculiar nanocrystalline microstructure.
References
- 1.
Saito Y. Takao H. Tani T. Nonoyama T. Takatori K. Homma T. Nagaya T. Nakamura M. 2004 Lead-free piezoceramics 432 84 - 2.
Smolenski G. A. Isupov V. A. Agranovskaya A. I. Krainik N. N. 1961 New ferroelectrics of complex composition, Sov. 2 2651 196 - 3.
Chiang Y. M. Farrey G. W. Soukhojak A. N. 1998 Lead-free high-strain single-crystal piezoelectrics in the alkaline-bismuth-titanate perovskite family 73 3683 - 4.
Takenaka T. Nagata H. 1999 Present Status of Non-Lead-Based PiezoelectricCeramics 157/158 57 - 5.
Takenaka T Maruyama K.-I. Sakata K 1991 (Bi1/2Na1/2)TiO3-BaTiO3 System for Lead-Free Piezoelectric Ceramics 30 2236 2239 - 6.
Jones G. O. Thomas P. A. 2002 Investigation of the structure and phase transitions in the novel A-site substituted distorted perovskite compound Na0.5Bi0.5TiO3, Acta Crystallogr 58 168 178 - 7.
Hiruma Y. Watanabe Y. Nagata H. Takenaka T. 2007 Phase Transition Temperatures of Divalent and Trivalent Ions Substituted (Bi1/2Na1/2)TiO3 Ceramics, Key Eng 350 93 - 8.
Glazer A. M. 1972 The classification of tilted octahedra in perovskites, Acta Crystallogr 28 3384 - 9.
W.-van B. Eerd D. Damjanovic N. Klein N. Setter Trodhal J. 2010 Structural complexity of (Na0.5Bi0.5)TiOP3BaTiO3 as revealed by Raman spectroscopy 82 104112 - 10.
Ma C. Tan X. 2010 Phase diagram of unpoled lead-free (1-x)(Bi/sub 1/2/Na/sub 1/2/)TiO/sub 3-x/BaTiO/sub 3/ ceramics 150 1497 1500 - 11.
Cordero F. Craciun F. Trequattrini F. Mercadelli E. Galassi C. 2010 Phase transitions and phase diagram of the ferroelectric perovskite (Na0.5Bi0.5)1−xBaxTiO3 by anelastic and dielectric measurements 81 144124 - 12.
Guo Y. P. Akai D. S. Sawada K. Ishida M. 2008 Dielectric and ferroelectric properties of highly (100)-oriented (Na0.5Bi0.5)0.94Ba0.06TiO3 thin films grown on LaNiO3/γ-Al2O3/Si substrates by chemical solution deposition 10 929 - 13.
Guo Y. P. Akai D. S. Sawada K. Ishida M. Gu M. Y. 2009 Structure and electrical properties of trilayered BaTiO3/(Na0.5Bi0.5)TiO3BaTiO3/BaTiO3 thin films deposited on Si substrate 149 14 - 14.
Duclère J.R. Cibert C. Boulle A. Dorcet V. Marchet P. Champeaux C. Catherinot A. Députier S. Guilloux-Viry M. 2008 Lead-free Na0.5Bi0.5TiO3 ferroelectric thin films grown by Pulsed Laser Deposition on epitaxial platinum bottom electrodes 517 592 - 15.
Bousquet M. J. Ducle`re R. Gautier B. Boulle A. Wu A. De´ S. putier D. Fasquelle F. Re´mondie` re. D. Albertini C. Champeaux P. Marchet M. Guilloux- Viry Vilarinho P. 2012 Electrical properties of (110) epitaxial lead-free ferroelectric Na0.5Bi0.5TiO3 thin films grown by pulsed laser deposition: Macroscopic and nanoscale data 111 104 106 - 16.
Qin W. Guo Y. Guo B. Gu M. 2012 Dielectric and optical properties of BiFeO3-(Na0.5Bi0.5)TiO3 thin films deposited on Si substrate using LaNiO3 as buffer layer for photovoltaic devices 513 154 158 - 17.
Shaw T. M. Trolier Mc Kinstry S. Mc Intyre P. C. 2000 The properties of ferroelectric thin films at small dimensions 30 263 - 18.
Scarisoreanu N. Craciun F. Chis A. Birjega R. Moldovan A. Galassi C. Dinescu M. 2010 Lead-free ferroelectric thin films obtained by pulsed laser deposition 101 747 751 - 19.
Scarisoreanu N. Craciun F. Ion V. Birjega S. Dinescu M. 2007 Structural and electrical characterization of lead-free ferroelectric Na/sub 1/2/Bi/sub 1/2/TiO/sub 3/-BaTiO/sub 3/ thin films obtained by PLD and RF-PLD 254 1292 - 20.
Picht G. Töpfer J. Henning E. 2010 Structural properties of (Bi0.5Na0.5)1−xBaxTiO3 lead-free piezoelectric ceramics 30 3445 - 21.
Takenaka T 1999 Piezoelectric Properties of Some Lead-Free Ferroelectric Ceramics 230 87 98 - 22.
Morelli A. Sriram Venkatesan Palasantzas Palasantzas Kooi, G De Hosson J. Th. M 2009 Piezoelectric properties of PbTiO3 thin films characterized with piezoresponse force and high resolution transmission electron microscopy 105 064106 - 23.
Craciun F. Dinescu M. 2007 Piezoelectrics”, in “Pulsed laser deposition of thin films: applications-led growth of functional materials” 487 532