Open access peer-reviewed chapter

Analysis of the Creep and the Influence on the Modulus Improvement Factor (MIF) in Polyolefin Geocells Using the Stepped Isothermal Method

By Juan Carlos Ruge, Julian Gonzalo Gomez and Carlos Andres Moreno

Submitted: February 25th 2019Reviewed: July 10th 2019Published: December 4th 2019

DOI: 10.5772/intechopen.88518

Downloaded: 306


The article shows the analysis of the behavior at long-term deformation of geocells for a set time period, due to its importance on the modulus improvement factor (MIF), which is considered in the design stage of a reinforced pavement structure with geocells. When inquiring into the research about the structural behavior that exists in the geocells, as well as the distribution of stresses that this generates, in order to determine how important the existence of a deformation in the geocell is. We proceeded with the sampling and execution of the test “modified stepped isothermal method (SIM) for geocells.” The test was carried out under the comparison of the materials and thicknesses of the sample, with the purpose to analyze the influence on the behavior of a pavement structure. The stresses generated at the level of the granular subbase layer of a pavement are taken into account as load effects.


  • creep
  • geocells
  • modulus improvement factor
  • stepped isothermal method

1. Introduction

One of the most common problems in road geotechnics projects is encountering subgrade soils of low carrying capacity. Multiple solutions are proposed to improve the unfavorable conditions of this type of soil; however, a large part of them can be harmful to the environment. In this sense, alternatives based on design with geosynthetics are important and allow for adequate reinforcement of the unsuitable soft subgrade as a supporting layer of the pavement structure.

However, with the implementation of geosynthetics, problems associated with the stresses experienced by the material were observed, such as UV degradation and long-term plastic deformation. These effects occur in almost all geosynthetics, even in geocells, which will be analyzed in detail in this article.

The first need to reinforce highly compressible soils arose during wartime at the beginning of the twentieth century, when the transport of heavy machinery was required. For this reason, the US Army Corps of Engineers was the first to use and develop the cellular confinement system in the late 1970s, as a means to help build roads, runways, platforms, and others; all these solutions were made on very soft soils and under humid conditions.

The main large-scale use of this system of cellular confinement was during the Gulf War, in “Operation Desert Storm”, where it transported heavy military material with speed and efficiency. For the purpose of mobilizing large troops, according to the company Geoceldas SA, the defense department of the United States “acquired 6.4 million square feet (600,000 square meters) of cellular geosynthetics for use in various military applications [1].”

In terms of its implementation in design tasks, pavement structure with geocells uses a coefficient of increase for the modules of the materials (MIF), which depends on several factors. Among these is resistance to long-term deformation of the material that makes up the panel of geocells. This generates a mechanism of confinement, which creates an apparent cohesion of the material incorporated therein. If the geocells yield, it is susceptible to losing its properties and begins to deform causing a settlement in the pavement structure, in addition to providing a deconfinement in the geocell filling material [2, 3].

Therefore, some consequences of deformation in the geocell are the reduction of the apparent cohesion in the filling material due to the loss of confinement, according to which there is a high decrease in the MIF coefficient taken into account during the design of the structure.

For these reasons, it is important to know the properties of the materials that are involved in the pavement structures and the veracity of the calculations that are made in the analyses. Therefore, when calculating the MIF, it is important to know the long-term deformation of material to give support and certainty in the analyses. Consequently, a modified test based on the SIM for geocells was developed. A test program was carried out using different samples of geocells, exposing results for each one of them.

The definition of the MIF factor refers to the material modulus with reinforcement vs. the material without reinforcement. This value is obtained at the moment of designing a structure with geocell, applying five characteristics of the material-geocell set, among which is the long-term deformation of geosynthetic. The MIF value depends on the analysis of the creep in the geocells, because if the material becomes deconfined, the increase of the modulus considered in the design will be reduced. For this reason, a safety factor is applied to the MIF, due to the creep in the geocells.

The samples were analyzed under load effects, which contemplate those generated at the level of the granular subbase layer of pavement, thus showing the feasibility of use in this layer and the possible behavior of these over its usable life.


2. Methodology

This research was based on the stepped isothermal method (SIM) which is standardized by ASTM D6992 [4, 5]. It was modified to prove the long-term deformation of the geocells and to learn the incidence that this property has when calculating the MIF, which is described as the relationship that exists between the module of a granular material confined with geocells and the same granular material without confinement, determined from Eq. (1) [6]. Basically, the adjustment on the test was based in terms of the width and length of the specimens, which depends on the type of geocell that is being analyzed.


The SIM test determines the long-term deformation of polymers by time-temperature superposition, whose effect was modified for use in polyolefin geocells. This method, known as the “time-temperature superposition principle (PSTT),” establishes that material having a viscoelastic property (V) measured in a time interval coincides with the same measurement in greater times at a lower temperature. Because this method is clearly empirical, it is defined as a principle, because not even theoretical concepts have been developed to sustain it [7].

With the aforementioned considerations, an increase in temperature according to Billmeyer [8], accelerates molecular and segmental movement, leading the system to equilibrium more quickly or “apparent equilibrium,” accelerating all viscoelastic processes.

To that extent, the modification proposal is based on systematically dividing the trial into five steps, in which the temperature will be increased with a specific duration for each step. In addition to applying a constant load throughout the trial of 4.4 kN/m, the temperatures reached for each step are 21 ± 1, 44, 51, and 65°C, respectively.

The first part of the test refers to the simulation of the load exerted on the geocell at the time of compaction of the filling material. It is possible to find a mean of time-temperature superposition according to [9], a temperature of 51°C and 1 hour of testing, equivalent to 100,000 hours of use (4166 days or 11 years).

The load of 4.4 kN/m, to which the material is subjected throughout the test, replicates the force supported by the geocell in the granular subbase of a pavement structure. This necessitates implementation of a series of charges which will be imposed through weights that will transmit this force to the geocells.

2.1 Sampling

All samples used came from polyolefin geocells available in the Colombian market. The sampling was conducted randomly from a bank of specimens supplied by the manufacturer. For the high-density polyethylene (HDPE) geocells, its polymer contents are not mentioned in this document, since it is known as high-density polyethylene in all the state of the art. While for the Neoloy® Geocell, no typology is obtained since its raw material is patented and there is no information about its polymer composition.

For the first type of HDPE polyolefin geocells from Provider 1, the properties are shown in Table 1.

Properties of the materialTesting methodUnitValues MARV
Polymer densityASTM D-1505g/cm30.935–0.965
Black smoke contentASTM D-1603% weight1.5% min
Nominal thickness of the cell wall before texturingASTM D-5199mm1.1 ± 10%
Nominal thickness of the cell wall after texturingASTM D-5199mm1.52 ± 10%
Physical propertiesTesting methodUnitTypical values
Nominal size of the expanded cellMeasuredmm320 × 287
Nominal area of the expanded cellMeasuredcm2460
Nominal size of the expanded panelMeasuredm2,56 × 8,35
Nominal size of the expanded panelMeasuredm221,04
Height of the cellMeasuredmm (in)75(3) 100(4) 150(6) 200(8)
Resistance of the joints by ultrasoundUSAGE GL-86-19N1065 1420 2130 2840
Ultimate resistance to joints tensionISO 13426-1 method BkN/m15
Ultimate resistance to tension wide strip methodISO 10319kN/m25
% of perforations per unit areaMeasured%12±2

Table 1.

Properties of geocell type 1, Provider 1.

For the second type of HDPE polyolefin geocells from Provider 2, the properties are shown in Table 2.

Physical propertiesNormUnitTypical values
Density of the materialASTM D-1505g/cm30.950 ± 0.015
Thickness of the sheet (textured)ASTM D-5199mmmin. 1.52 ± 0.15
Black carbon contentASTM D-1603%2.0 ± 0.5
Resistance to environmental cracking (ESCR)ASTM D-1693hours>3000
Resistance of the joints to the takeoffASTM D-4437N/cm>150
Height of the unitmm150
Minimum values of resistanceISO 13426-1 method A: shear testkN/joint2.7
ISO 13426-1 method B: takeoff testkN/joint2.25
Number of cells#/m21.7
Diagonal lengthcm30.4
Cell areacm2461
Distance between jointsmm445
Width of the expanded unitm2.43
Expanded unit lengthm5.5
Weight of the unitkg20.8

Table 2.

Properties of geocell type 2, Provider 2

For the third type of polyolefin geocell from Neoloy® of Provider 3, the properties shown in Table 3 are available, for categories A, C, and D.

Dimensions of the cells and panels
Distance between ribs445 mm (±2.5%)
Height of the cells150–200 mm (±5%)
Dimensions of the open cell340 × 290 mm (±3%)
# of cells/m222
Expanded section size2.8 × 10.7–17.3 m (±3%) (máx.)
Expanded section area30–48 m2 (±3%)
Categories of the geocell
PropertyNormCat. ACat. CCat. D
Resistance to welding (kN/m)ISO 13426-191518
Ultimate resistance of the material (MPa)ASTM D638, ISO 527222428
Ultimate resistance (wide strip with perforations) (kN/m)ISO 10319291522
Dimensional stabilityNormValue
Coefficient of thermal expansion (ppm/°C) measuring range of −30°C to +30°CASTM E-831≤95
Time of induction to oxidation (OIT at 200°C) (mpn.) (virgin material before any modification)ASTM D-3895≥125
Resistance to ultraviolet degradation (HPOIT at 200°C) (min.)ASTM D-5885≥1250
Durability of the cell to long-term cyclical loads (pass)Accelerated radial pressure test (TRI)Cells, joints, and perforations remained intact without evidence of plastic deformation at the end of the cyclic loading
Efficiency of the internal friction angleASTM D-5321≥0.84
Flexural module for each temperature (MPa)ISO 672 ASTM E2254 (DAM)
Reduction factor due to permanent deformation(creep)ASTM D-6992 (SIM)
5 years<1.2
10 years<1.4
25 years<1.9
50 years<2.9

Table 3.

Geocell of types 3 and 4 properties, Provider 3.

3. Procedure of the test

The laboratory procedure is divided into three parts.

Part I: To start the test, it is necessary to take the measurements of the samples; for this reason the length, width, and thickness of the geocell must be taken.

Part II: The specimen is adjusted to the metal jaws, generating a total interaction between the geocell and the jaws (Figure 1), while Figure 2 shows how the jaws should be placed on both the upper and lower halves to generate the desired load transfer.

Figure 1.

Adjustment of the sample to the clamp.

Figure 2.

Placement of the sample to the upper and lower jaws.

Part III: In this step, the samples are hoisted in the oven support, complementing the union of the jaw of the lower part of the sample to the stem (Figure 3). After this it is necessary to place the deformimeters in the base that supports the oven (Figure 4, left).

Figure 3.

Installation of the sample in the oven.

Figure 4.

Deformimeters in the base of the oven (left) and placement of weights in the stems (right).

Part IV: The hydraulic jack is placed in the lower part of the rods, generating a support so as not to exert preliminary efforts on the geocells, and then all the necessary weights are placed to reach the force required in the test (Figure 4, right). The oven is subsequently closed.

Part V: The oven is turned on at room temperature (21 ± 1°C), then the hydraulic jack is lowered by hanging the stems with the weights, and the first reading of the deformimeter is recorded, after which the steps with the pre-established times begun.

4. Results

To obtain the time-temperature superposition data that is necessary in the production of the SIM assay graphs, it was necessary to create an accurate graph, where equivalences (see Table 4) are determined between temperature and time superimposed by every minute that elapsed in temperature; see [10].

Temperature (°C)Equivalent time (min.)

Table 4.

Equivalent times.

An exponential behavior is observed in these correlations, where time depends on temperature (Figure 5). For this reason, an exponential regression shown on the same graph is generated, in order to determine the total time that the geocell was exposed throughout the trial.

Figure 5.

Time-temperature superposition.

The following equation is the result:


in which.

T: equivalent time in minutes per minute elapsed in temperature t°.

t°: temperature (°C).

The data for the time equivalent to the temperature were obtained based on the above equation, during the course of the different isothermal steps of the test. These equivalent times are shown in Table 5.

StepTime (min.)Accumulation of time (years)
Increase to 44°C
Increase to 51°C
Increase to 58°C
Increase to 65°C
65 °C6078.78

Table 5.

Equivalent times for the SIM test.

After the development of the different graphs made from the tests, it was possible to subtract and make a comparison between the materials that were used in each of the tests, in order to determine which behaved better in the long-term deformation. Figure 6 shows the comparative graph of materials. A red line is again observed, which indicates 3% of the deformation, which generates a fault in the ground and the possible breakage of the pavement structure.

Figure 6.

Comparison of samples tested.

For the comparative graph of materials, the samples that had been exposed for a while were not considered, given that the other materials did not have this previous exposure and therefore leading to a possible erroneous comparison.

It is important to consider the effect that occurs in the geocells of Neoloy® from exposure to the environment (Figure 7), since these demonstrate the best behavior against long-term deformation [11, 12, 13, 14, 15].

Figure 7.

Behavior according to environmental exposure time (Neoloy®).

Based on the previous results, it is important to make a new comparison in the Neoloy® Geocells, for its ultimate resistance to the wide strip test ISO 103192. Figure 8 shows the incidence of this property in the behavior to the long-term deformation and the affectation on the MIF.

Figure 8.

Behavior of Neoloy® geocells according to resistance of wide strip ISO 103192.

Continuing with the analysis of the behavior of the polyolefin geocells in long-term deformation, a different behavior was observed among the materials of the HDPE samples, where the thickness determined in part the behavior that was observed throughout the tests. Because of this, the evolution of the specimens in terms of thickness is shown in Figure 9, revealing that the material with greater thickness presents a better response to this type of long-term stress.

Figure 9.

Behavior HDPE geocells according to thickness.

As it is possible to extract from the different graphs in categories C and D composed of Neoloy® from Provider 3, an acceptable behavior was observed against the long-term deformation, this being the material that behaved better during the trials without reaching the 3% deformation failure in any of the two categories mentioned. Therefore, the geocells would have an MIF factor of high incidence in the module of the material to be confined, as shown in the Mohr circle (see Figure 10).

Figure 10.

Mohr circle of granular material with and without reinforcement [7].

According to Han [16], the confinement creates an apparent cohesion considering the modification in the normal stresses caused to the granular material. This is only available if the material of the geocell resists the deformations produced by the stresses over the life of the project. Only the Neoloy® Geocells of categories C and D of Provider 3 manage to comply with the limitation of the MIFs.

When comparing the categories of the Neoloy® material, the great importance of both the thickness of the material and the resistance to the wide strip is observed. The results show better behavior in the geocell that has a greater resistance and greater thickness, displaying a high creep behavior and consequently increasing the MIF, which is significant when designing structures with this geocell methodology.

However, at the end of the tests, a rational time was determined to discharge the geocells. At this time an important behavior was observed in which the samples began to regenerate, decreasing the deformations that were at the end. The effect was established for the geocells that did not fail, showing an “elastic” behavior but also maintaining a degree of plastic deformation. Therefore, a linear viscoelastic behavior can be determined, in which there is an initial elastic deformation caused by the stresses generated upon it, followed by a time-dependent delayed deformation, known as material creep. There may be some permanent flow in the material, especially when high loads are applied.

When the unload is permitted to the material, within linear viscoelastic behavior, an inverse process begins, with a certain recovery at the moment, continued by a recovery along the time recovering fluence dependent on the time. The material may or may not reach the original dimensions. If permanent flow occurs in the charging process, there will be a residual deformation even when the load application is no longer allowed [17, 18, 19].

5. Conclusions

Polyolefin geocells can be considered an excellent reinforcement in the structures of the roads as long as they meet certain specifications, such as resistance to long-term deformation. For the geocells tested, the best performance was obtained by the Neoloy® composite material.

Taking into account the results of the laboratories, the increase factor of MIF modules is directly connected to creep resistance. When confinement is eventually lost due to large deformations in the geocells, the increase will be zero, and the behavior of the granular material belonging to the pavement structure will be the same as if it were not considered reinforced, decreasing its modulus, requiring a greater thickness to comply with the conditions of the structure.

All polymeric material that is exposed to weather, for greater resistance that it possesses, suffers the loss of properties. This could be evidenced when comparing tests with the same material and category, but with different time of exposure to the effects caused by nature (UV rays, air, water, etc.). A lesser deformation was displayed in the sample that had been under condition for a year.

The deformation behavior of HDPE exposed to high temperatures is low compared to Neoloy® material. For this reason, it could be determined that the HDPE geocells, although they have a regular behavior, cannot be located in the base layer of the pavement structures, since these could have temperatures as tested in the “SIM test” or higher, generating a double deformation. One of them would be due to time and the other due to temperature, leading to failure in a very short period of time.

To determine the MIF, it is necessary to know the resistance of the material of the geocell to the long-term deformation, since it is a vital part of achieving high performance, during the entire life of the structure of pavement reinforced with geocells.

The geocells, composed by Neoloy® with a resistance to the wide strip of 15 kN/m, are the most suitable to achieve a subgrade improvement. These geocells have the ability to be used in the granular layers adjacent to the asphalt folder, decreasing thicknesses. The use of these minimum aspects is recommended to guarantee the functionality, serviceability, and long-term operability of structures where geocells are involved.

© 2019 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution 3.0 License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Juan Carlos Ruge, Julian Gonzalo Gomez and Carlos Andres Moreno (December 4th 2019). Analysis of the Creep and the Influence on the Modulus Improvement Factor (MIF) in Polyolefin Geocells Using the Stepped Isothermal Method, Geopolymers and Other Geosynthetics, Mazen Alshaaer and Han-Yong Jeon, IntechOpen, DOI: 10.5772/intechopen.88518. Available from:

chapter statistics

306total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

Related Content

This Book

Next chapter

The Assessment Strategy for Selecting and Evaluating Geoenvironmental Remediation

By Meshari Almutairi

Related Book

First chapter

Introductory Chapter: A Brief Introduction to Porous Ceramic

By Uday M. Basheer Al-Naib

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us