Open access

Advances in Resistive Switching Memories Based on Graphene Oxide

Written By

Fei Zhuge, Bing Fu and Hongtao Cao

Submitted: 03 June 2012 Published: 27 March 2013

DOI: 10.5772/51260

From the Edited Volume

New Progress on Graphene Research

Edited by Jian Ru Gong

Chapter metrics overview

5,237 Chapter Downloads

View Full Metrics

1. Introduction

Memory devices are a prerequisite for today’s information technology. In general, two different segments can be distinguished. Random access type memories are based on semiconductor technology. These can be divided into static random access memories (SRAM) and dynamic random access memories (DRAM). In the following, only DRAM will be considered, because it is the main RAM technology for standalone memory products. Mass storage devices are traditionally based on magnetic- and optical storage. But also here semiconductor memories are gaining market share. The importance of semiconductor memories is consequently increasing (Mikolajick et al., 2009). Though SRAM and DRAM are very fast, both of them are volatile, which is a huge disadvantage, costing energy and additional periphery circuitry. Si-based Flash memory devices represent the most prominent nonvolatile data memory (NVM) because of their high density and low fabrication costs. However, Flash suffers from low endurance, low write speed, and high voltages required for the write operations. In addition, further scaling, i.e., a continuation in increasing the density of Flash is expected to run into physical limits in the near future. Ferroelectric random access memory (FeRAM) and magnetoresistive random access memory (MRAM) cover niche markets for special applications. One reason among several others is that FeRAM as well as conventional MRAM exhibit technological and inherent problems in the scalability, i.e., in achieving the same density as Flash today. In this circumstance, a renewed nonvolatile memory concept called resistance-switching random access memory (RRAM), which is based on resistance change modulated by electrical stimulus, has recently inspired scientific and commercial interests due to its high operation speed, high scalability, and multibit storage potential (Beck et al., 2000; Lu & Lieber, 2007; Dong et al., 2008). The reading of resistance states is nondestructive, and the memory devices can be operated without transistors in every cell (Lee et al., 2007; Waser & Aono, 2007), thus making a cross-bar structure feasible. A large variety of solid-state materials have been found to show these resistive switching characteristics, including solid electrolytes such as GeSe and Ag2S (Waser & Aono, 2007), perovskites such as SrZrO3 (Beck et al., 2000), Pr0.7Ca0.3MnO3 (Liu et al., 2000; Odagawa et al., 2004; Liao et al., 2009), and BiFeO3 (Yang et al., 2009; Yin et al., 2010), binary transition metal oxides such as NiO (Seo et al., 2004; Kim et al., 2006; Son & Shin, 2008), TiO2 (Kim et al., 2007; Jeong et al., 2009; Kwon et al., 2010), ZrO2 (Wu et al., 2007; Guan et al., 2008; Liu et al., 2009), and ZnO (Chang et al., 2008; Kim et al., 2009; Yang et al., 2009), organic materials (Stewart et al., 2004), amorphous silicon (a-Si) (Jo and Lu, 2008; Jo et al., 2009), and amorphous carbon (a-C) (Sinitskii & Tour, 2009; Zhuge et al., 2010) (Zhuge et al., 2011).

In last decades, carbon-based materials have been studied intensively as a potential candidate to overcome the scientific and technological limitations of traditional semiconductor devices (Rueckes et al., 2000; Novoselov et al., 2004; Avouris et al., 2007). It is worthy mentioning that most of the work on carbon-based electronic devices has been focused on field-effect transistors (Wang et al., 2008; Burghard et al., 2009). Thus, it would be of great interest if nonvolatile memory can also be realized in carbon so that logic and memory devices can be integrated on a same carbon-based platform. Graphene oxide (GO) with an ultrathin thickness (~1 nm) is attractive due to its unique physical-chemical properties. A GO layer can be considered as a graphene sheet with epoxide, hydroxyl, and/or carboxyl groups attached to both sides. GO can be readily obtained through oxidizing graphite in mixtures of strong oxidants, followed by an exfoliation process. Due to its water solubility, GO can be transferred onto any substrates uniformly using simple methods such as drop-casting, spin coating, Langmuir-Blodgett (LB) deposition and vacuum filtration. The as-deposited GO thin films can be further processed into functional devices using standard lithography processes without degrading the film properties (Eda et al., 2008; Cote et al., 2009). Furthermore, the band structure and electronic properties of GO can be modulated by changing the quantity of chemical functionalities attached to the surface. Therefore, GO is potentially useful for microelectronics production. Considering that although a large variety of solid-state materials have been found to show resistive switching characteristics, none of them can fully meet the requirements of RRAM applications, exploration of new storage media is still a key project for the development of RRAM (Zhuge et al., 2011). This review focuses on GO-based RRAM cells, highlighting their advantages as the next generation memories. Section 2 describes the basic concepts of resistive switching and resistance-switching random access memory and physical storage mechanisms. In section 3, the resistive switching mechanisms of GO thin films and memory properties of GO-based RRAM cells are presented. Detailed current–voltage measurements show that in metal/GO/metal sandwiches, the resistive switching originates from the formation and rupture of conducting filaments. An analysis of the temperature dependence of the ON-state resistance reveals that the filaments are composed of metal atoms due to the diffusion of the top electrodes under a bias voltage. Moreover, the resistive switching is found to occur within confined regions of the metal filaments. The resistive switching effect is also observed in GO/metal structures by conducting atomic force microscopy. It is attributed to the redox reactions between GO and adsorbed water induced by external voltage biases. The GO-based RRAM cells show an ON/OFF ratio >100, a retention time >105 s, and switching threshold voltages <1 V. In section 4, the resistive switching mechanisms of conjugated-polymer-functionalized GO thin films and memory properties of corresponding RRAM cells are described. In this case, the resistive switching is ascribed to electron/hole transfer between graphene sheets and polymer molecules. The RRAM cells exhibit excellent memory performances, such as large ON/OFF ratio, good endurance, and high switching speed. In the last section, it is proposed that the realization of bidirectional or reversible electron transfer in graphene-based hybrid systems is expected to overcome the “voltage–time dilemma” (i.e., one could not realize high write/erase speed and long retention time simultaneously) in pure electronic mechanism-based RRAM cells (Schroeder et al., 2010). Pure electronic mechanisms in RRAM cells postulate the trapping and detrapping of electron in immobile traps as the reason for the resistance changes, also known as Simmons & Verderber model (Simmons & Verderber, 1967). While in graphene-based hybrid systems, the electron transfer occurs between graphene sheets and functional molecules covalently or non-covalently bonded to graphene, which may avoid the “voltage–time dilemma”.

Advertisement

2. Resistive switching and RRAM

A resistive switching memory cell in an RRAM is generally composed of an insulating or resistive material sandwiched between two electron-conductive electrodes to form metal-insulator-metal (MIM) structure. By applying an appropriate voltage, the MIM cell can be switched between a high-resistance state (HRS or OFF-state) and a low-resistance state (LRS or ON-state). Switching from OFF-state to ON-state is called the SET process, while switching from ON-state to OFF-state is called the RESET process. These two states can represent the logic values 1 and 0, respectively. Depending on voltage polarity, the resistive switching behavior of an RRAM device is classified as unipolar and bipolar. For unipolar switching, resistive switching is induced by a voltage of the same polarity but a different magnitude, as shown in Fig. 1(a) (Waser & Aono, 2007). For bipolar switching, one polarity is used to switch from HRS to LRS, and the opposite polarity is used to switch back into HRS, as shown in Fig. 1(b) (Waser & Aono, 2007). A current compliance (CC) is usually needed during the SET process to prevent the device from a permanent breakdown. (Li et al., 2011)

In the simplest approach, the pure memory element can be used as a basic memory cell, resulting in a configuration where parallel bitlines are crossed by perpendicular wordlines with the switching material placed between wordline and bitline at every cross-point. This configuration is called a cross-point cell. Since this architecture will lead to a large parasitic current flowing through nonselected memory cells, the cross-point array has a very slow read access. A selection element can be added to improve the situation. A series connection of a diode in every cross-point allows to reverse bias all nonselected cells. This can be arranged in a similar compact manner as the basic cross-point cell. Finally a transistor device (ideally a MOS Transistor) can be added which makes the selection of a cell very easy and therefore gives the best random access time, but comes at the price of increased area consumption. Figure 2 illustrates the different cell type possibilities. For random access type memories, a transistor type architecture is preferred while the cross-point architecture and the diode architecture open the path toward stacking memory layers on top of each other and therefore are ideally suited for mass storage devices (Mikolajick et al., 2009; Pinnow & Mikolajick, 2004).

Figure 1.

(a) Unipolar switching. The SET voltage is always higher than the voltage at which RESET takes place, and the RESET current is always higher than the CC during SET operation. (b) Bipolar switching. The SET operation takes place on one polarity of the voltage or current, and the RESET operation requires the opposite polarity. (Waser & Aono, 2007)

Figure 2.

Three different cell architectures for RRAM cells: (a) cross-point cell, (b) diode cell, and (c) transistor cell together with their respective area consumption in F2. F denotes the minimum feature size of the fabrication technology. (Mikolajick et al., 2009)

Based on the circuit requirements of high-density NVM today such as Flash and taking predictions about technology scaling of the next 15 years into account, one can collect a number of requirements for RRAM cells (Waser et al., 2009):

2.1. Write operation

Write voltages should be in the range of a few hundred mV to be compatible with scaled CMOS to few V (to give an advantage over Flash which suffers from high programming voltages). The length of write voltage pulses is desired to be <100 ns in order to compete with DRAM specifications and to outperform Flash which has a programming speed of some 10 ms, or even <10 ns to approach high-performance SRAM.

2.2. Read operation

Read voltages need to be significantly smaller than write voltages in order to prevent a change of the resistance during the read operation. Because of constraints by circuit design, read voltage cannot be less than approximately one tenth of write voltage. An additional requirement originates from the minimum read current. In the ON-state, read current should not be less than approximately 1mA to allow for a fast detection of the state by reasonably small sense amplifiers. The read time must be in the order of write time or preferably shorter.

2.3. Resistance ratio

Although an ON/OFF (ROFF/RON) ratio of only 1.2 to 1.3 can be utilized by dedicated circuit design as shown in MRAM, ON/OFF ratios >10 are required to allow for small and highly efficient sense amplifiers and, hence, RRAM devices which are cost competitive with Flash.

2.4. Endurance

Contemporary Flash shows a maximum number of write cycles between 103 and 107, depending on the type. RRAM should provide at least the same endurance, preferably a better one.

2.5. Retention

A data retention time of >10 years is required for universal NVM. This retention time must be kept at thermal stress up to 85 ºC and small electrical stress such as a constant stream of read voltage pulses.

Despite a bursting body of experimental data that is rapidly becoming available, the precise mechanism behind the physical effect of resistive switching remains elusive. A few qualitative models have been proposed emphasizing different aspects: electric-field-induced defect migration (Baikalov et al., 2003; Nian et al., 2007), phase separation (Tulina et al., 2001), tunneling across interfacial domains (Rozenberg et al., 2004), control of the Schottky barrier’s height (Jeong et al., 2009), etc., as shown in Fig. 3. A general consensus has emerged on the empirical relevance of three key features: (i) a highly spatially inhomogeneous conduction in the low resistive state, (ii) the existence of a significant number of defects, and (iii) a preeminent role played by the interfaces, namely, the regions of the oxide that are near each of the metallic electrodes which often form Schottky barriers. (Rozenberg et al., 2010)

Figure 3.

Reported several resistive switching mechanisms. (a) Filamentary model (Yang et al., 2009). (b) Domain model (Rozenberg et al., 2004). (c) Electrical field induced oxygen vacancy migration model (Szot et al., 2006). (d) Schottky barrier modulation model (Sawa et al., 2004).

Advertisement

3. Resistive switching and memory properties in GO-based RRAM cells

He et al. firstly reported reliable and reproducible resistive switching behaviors in GO thin films prepared by the vacuum filtration method on 2009 (He et al., 2009). The Cu/GO/Pt structure showed an ON/OFF ratio of about 20, aretention time of more than 104 s, and switching threshold voltages of less than 1 V, as shown in Fig. 4.

Figure 4.

(a) A schematic configuration of the Cu/GO/Pt sandwiched structure. (b) I–V characteristics of the Cu/GO/Pt structure. The arrows indicate the sweep direction. The inset shows the I–V characteristics in semilogarithmic scale. (He et al., 2009)

It indicates that GO is potentially useful for future nonvolatile memory applications. At a later time, Zhuge et al. achieved larger ON/OFF ratios of more than 100 in metal (Cu, Ag, Ti, and Au)/GO/Pt devices (Zhuge et al., 2011). They considered that the moisture in air affects the ON/OFF ratio of metal/GO/Pt memory cells severely. Furthermore, Jeong et al. presented a GO based memory that can be easily fabricated using a room temperature spin-casting method on flexible substrates and has reliable memory performance in terms of retention and endurance, as shown in Fig. 5 (Jeong et al., 2010). Therefore, the GO memory is an excellent candidate to be a memory device for future flexible electronics (Hong et al., 2010).

Figure 5.

(a) A schematic illustration of a GO based flexible crossbar memory device. (b) Typical I–V curve of a Al/GO/Al/PES device plotted on a semilogarithmic scale. The arrows indicate the voltage sweep direction. The left inset is a real photo image of a device. (c) Continuous bending effect of a Al/GO/Al/PES device. The insets show photographs of repeated two bending states. (d) The resistance ratio between the HRS and LRS as a function of the bending radius (R). The inset is a photograph of an I-V measurement being performed under a flexed condition. (e) Retention test of Al/GO/Al/PES device read at –0.5 V. (f) Endurance performance of an Al/GO/Al/PES device measured during 100 sweep cycles. (Jeong et al., 2010)

As to the mechanism of the resistive switching effect in GO thin films, Zhuge et al. pointed out that in metal/GO/Pt sandwiches, the resistive switching originates from the formation and rupture of conducting filaments, as schematically shown in Fig. 6 (Zhuge et al., 2011).

Figure 6.

A schematic diagram for the mechanism of the resistive switching in metal/GO/Pt memory cells. (Zhuge et al., 2011)

Figure 7.

(a), (b) and (c) AFM images of virgin GO films, GO films in LRS, and GO films in HRS. The light-colored ribbons represent folded regions. (d), (e) and (f) the corresponding CAFM images under a read voltage of 1 V. (Zhuge et al., 2011)

An analysis of the temperature dependence of the ON-state resistance reveals that the filaments are composed of metal atoms due to the diffusion of the top electrodes under a bias voltage. Tsuruoka et al. pointed out that the formation of a metal filament is due to inhomogeneous nucleation and subsequent growth of metal, based on the migration of metal ions in the oxide matrix (Tsuruoka et al., 2010). Recently, they reported that the ionization of metal at the anode interfaces is likely to be attributed to chemical oxidation via residual water in the oxide layer, and metal ions migrate along grain boundaries in the oxide layer, where a hydrogen-bond network might be formed by moisture absorption (Tsuruoka et al., 2012). Moreover, the switching occurs within confined regions of the metal filaments. The RESET process is considered to consist of the Joule-heating-assisted oxidation of metal atoms at the thinnest part of the metal filament followed by diffusion and drift of the metal ions under their own concentration gradient and the applied electric field, disconnecting the metal filament (Tsuruoka et al., 2010). Zhuge et al. also observed the resistive switching effect in GO/Pt structures by conducting atomic force microscopy (CAFM), as shown in Fig. 7 (Zhuge et al., 2011). It is attributed to the redox reactions between GO and adsorbed water induced by external voltage biases. While for Al/GO/Al memory cells, Jeong et al. attributed the bipolar resistive switching behavior to rupture and formation of conducting filaments at the top amorphous interface layer formed between the GO film and the top Al metal electrode, as shown in Fig. 8 (Jeong et al, 2010).

Figure 8.

Schematic of the proposed bipolar resistive switching model for Al electrode/GO/Al electrode crossbar memory device. (a) The pristine device is in the OFF-state due to the (relatively) thick insulating top interface layer formed by a redox reaction between vapor deposited Al and the GO thin film. (b) The ON-state is induced by the formation of local filaments in the top interface layer due to oxygen ion diffusion back into the GO thin film by an external negative bias on the top electrode. (Jeong et al., 2010)

Furthermore, Hong et al. pointed out that for Al/GO/metal memory devices, the resistive switching operation is governed by dual mechanism of oxygen migration and Al diffusion (Hong et al., 2011). The Al diffusion into the graphene oxide is the main factor to determine the switching endurance property which limits the long term lifetime of the device. The electrode dependence on graphene oxide RRAM operation has been analyzed as well and is attributed to the difference in surface roughness of graphene oxide for the different bottom electrodes, as shown in Fig. 9 (Hong et al., 2011). Interestingly, Panin et al. observed both diode-like (rectifying) and resistor-like (nonrectifying) resistive switching behaviors in an Al/GO/Al planar structure, as shown in Fig. 10 (Panin et al., 2011). Electrical characterization of the Al/GO interface using the induced current identifies a potential barrier near the interface and its spatial modulation, caused by local changes of resistance at a bias voltage, which correlated well with the resistive switching of the whole structure. Recently, Wang et al. found that the speed of the SET and RESET operations of the Al/GO/ITO resistive memories is significant asymmetric (Wang et al., 2012). The RESET speed is in the order of 100 ns under a –5 V voltage while the SET speed is three orders of magnitude slower (100 μs) under a 5 V bias. The behavior of resistive switching speed difference is elucidated by voltage modulated oxygen diffusion barrier change, as shown in Fig. 11 (Wang et al., 2012).

Figure 9.

The contact angles of graphene oxide solution on four different surfaces of ITO, TaN, Su, and Pt. UV treatment is done to promote adhesion. (Hong et al., 2011)

Figure 10.

I–V curves of Al/GO/Al structures pre-formed at different forming voltages. (Panin et al., 2011)

Figure 11.

Pulse behavior of the Al/GO/ITO/PET memory cell, HRS and LRS is read at 0.3 V. (a) the SET and RESET operations of the devices with different pulsing width at ±5. The HRS and LRS of the devices are measured at 0.3V and the SET operation is found to be three orders of magnitude slower than the RESET operation; (b) a schematic of oxygen hopping barrier change model. (Wang et al., 2012)

Advertisement

4. Resistive switching and memory properties in GO-polymer hybrid RRAM cells

Liu et al. prepared a solution-processable and electroactive complex of poly(N-vinylcarbazole)-derivatized graphene oxide (GO-PVK) via amidation of end-functionalized PVK, from reversible addition fragmentation chain transfer polymerization, with tolylene-2,5-diisocyanate-functionalized graphene oxide (Liu et al., 2009). The Al/GO-PVK/ITO device exhibits bistable electrical conductivity switching and nonvolatile rewritable memory effects. The resistive switching is attributed to electron transfer between GO and PVK, as shown in Fig. 12 (Liu et al., 2009).

Figure 12.

Plausible switching mechanism of GO-PVK. RGO stands for reduced graphene oxide. (Liu et al., 2009)

Zhuang et al. synthesized a novel conjugated-polymer-modified graphene oxide (TPAPAM-GO), which was successfully used to fabricate a TPAPAM-GO-based RRAM device (Zhuang et al., 2010). The device exhibits a typical bistable electrical switching and nonvolatile rewritable memory effect, with a SET voltage of about–1V and an ON/OFF ratio of more than 103, as shown in Fig. 13 (Zhuang et al., 2010).

Figure 13.

J–V characteristics and stability tested in either ON- or OFF-state under stimulus by read pulses of a 0.16-mm2 ITO/TPAPAM-GO/Al device. Inset: schematic diagram of the single-layer memory devices. (Zhuang et al., 2010)

Both the ON- and OFF-state are stable under a constant voltage stress and survive up to 108 read cycles at a read voltage of –1 V. As to the switching mechanism, they deduced that at the switching threshold voltage, electrons transit from the hole transporting (electron donating) polymer TPAPAM (highest occupied molecular orbital, HOMO) into the graphene monoatom layer (lowest unoccupied molecular orbital, LUMO) via intramolecular charge-transfer (CT) interaction (Ling et al., 2008). The transferred electrons can delocalize effectively in the giant p-conjugation system, and reduce graphene oxide to graphene (Elias et al., 2009; Robinson et al., 2008). Upon electrochemical reduction of the functionalized graphene oxide, electrons can propagate with less scattering, giving rise to a substantially enhanced room temperature conductivity (~102 S m–1) of the composite material (Robinson et al., 2008; Stankovich et al., 2006). Along with the increase of CT interaction, dual-channel charge-transport pathways will form via interplane hopping in graphene films and switch the ITO/TPAPAM-GO/Al device from the OFF-state to the ON-state (Ling et al., 2008). The application of a reverse positive bias to the device can, however, extract electrons from the reduced graphene nanosheet, returning it to the initial less-conductive form and programming the device back to the OFF-state (Zhuang et al., 2010). Wu et al. fabricated GO-polyimide (PI) hybrid RRAM cells, as shown in Fig. 14 (Wu et al., 2011). The functionalization of GO sheets with PI enables the layer-by-layer fabrication of a GO-PI hybrid resistive-switch device and leads to high reproducibility of the memory effect. The current-voltage curves for the as-fabricated device exhibit multilevel resistive-switch properties under various reset voltages. The capacitance-voltage characteristics for a capacitor based on GO-PI nanocomposite indicate that the electrical switching may originate from the charge trapping in GO sheets. The high device-to-device uniformity and unique memory properties of the device make it an attractive candidate for applications in next-generation high-density nonvolatile flash memories (Wu et al., 2011). Yu et al. reported bistable resistive switching characteristics for write-once-read-many-times (WORM) memory devices using a supramolecular hybrid route to hydrogen-bonded block copolymers (BCP) and GO as charge storage materials (Yu et al., 2012). The ITO/7 wt% GO composite/Al device exhibits a one-time programmable effect with an ON/OFF ratio of 105 at –1.0 V, a retention of 104 s and a 108 read pulse of –1.0 V, as shown in Fig. 15 (Yu et al., 2012). The switching phenomena were attributed to the charge trapping environment operating across the BCP/GO interface and from the GO intrinsic defect. Controlling the physical interaction of BCP and functional GO sheets can generate a well-dispersed charge storage composite device for future flexible information technology.

Figure 14.

(a) FE-SEM image of the cross sectional view for the GO-PI film. (b) Schematic of Ag/PI/GO:PI/PI/ITO memory device. (Wu et al., 2011)

Recently, Hu et al. prepared a novel RRAM device based on reduced GO noncovalently functionalized by thionine (Hu et al., 2012). The device shows nonvolatile resistive switching behaviors with an ON/OFF ratio of more than 104, fast switching speed of <5 ns, long retention time of >105 s, and good endurance. The resistive switching in such memory device is attributed to electron transfer reaction between reduced graphene oxide sheets and thionine molecules.

Noting that besides GO, graphene can also be used for resistive switching memory devices. Standley et al. developed a nonvolatile resistive memory element based on graphene break junctions which demonstrates thousands of writing cycles and long retention times (Standley et al., 2008). They proposed a model for device operation based on the formation and breaking of carbon atomic chains that bridges the junctions, as shown in Fig. 16 (Standley et al., 2008). Recently, He et al. reported a planar graphene/SiO2 nanogap structure for multilevel resistive switching (He et al., 2012). Such two-terminal devices exhibited excellent memory characteristics with good endurance up to 104 cycles, long retention time more than 105 s, and fast switching speed down to 500 ns. At least five conduction states with reliability and reproducibility were demonstrated in these memory devices, as shown in Fig. 17 (He et al., 2012). The mechanism of the resistive switching was attributed to a reversible thermal-assisted reduction and oxidation process that occurred at the breakdown region of the SiO2 substrate.

Figure 15.

(a) I–V characteristics of 7 wt% GO composite device. The inset shows the switching behavior in different memory cells. (b) Retention time test. (c) Stimulus effect of read pulses. (Yu et al., 2012)

Figure 16.

(a) SEM image of the device before (left panel) and after breakdown (right panel). The arrows indicate the edges of the nanoscale gap. (b) Proposed schematic atomic configurations in the ON and OFF states. (Standley et al., 2008)

Figure 17.

Multilevel resistive switching properties of graphene/SiO2 nanogap structures. (a) Typical I–V characteristics of a device with a width of 1 μm, length of 0.4 μm, and thickness of 2.3 nm. The vertical line cut at 1 V indicates five resistance states. By sweeping the reset voltage from 0 to 5 V, the OFF1 state (red) was established. The subsequent reset voltages sweep up to higher voltage of 7 V (purple), 9 V (orange), and even higher to 11 V (olive) from 0 V, and lower conduction states of OFF2, OFF3, and OFF4 were achieved subsequently. (b) Top: series of bias pulses with different magnitudes of 3, 5, 7, 9, and 11 V, corresponding to the sweep voltages in (a) with three reading pulses of 1 V after each programming pulse was applied. Bottom: resistance changes corresponding to the each voltage pulse in the top panel. (c) Cycled switching of the device under various reset voltages. (d) Retention time of more than 104 s for each conduction state tested by a continuous 1 V pulse. (He et al., 2012)

Advertisement

5. Summary and prospect

Resistive random access memory based on the resistive switching effect induced by electrical stimulus has inspired scientific and commercial interests due to its high operation speed, high scalability, and multibit storage potential. The reading of resistance states is nondestructive, and the memory devices can be operated without transistors in every cell, thus making a cross-bar structure feasible. Although a large variety of solid-state materials have been found to exhibit the resistive switching effect, GO is a very promising material for RRAM applications since due to an ultrathin thickness (~1 nm) and its unique physical–chemical properties. Both GO and GO-polymer hybrid exhibit good memory performances, such as high ON/OFF ratio and long retention time. The resistive switching of GO is always related to defect migration, such as metal ions and oxygen vacancies, whereas the switching of GO-polymer hybrid is considered to be attributed to charge transfer reaction between GO sheets and polymer molecules. Since both high switching speed and good retention could be simultaneously achieved in GO-polymer hybrid RRAM device, such memory device is expected to overcome the “voltage–time dilemma” (i.e., one could not realize high write/erase speed and long retention time simultaneously in pure electronic mechanism-based RRAM cells). Pure electronic mechanisms in RRAM cells postulate the trapping and detrapping of electron in immobile traps as the reason for the resistance changes, also known as Simmons & Verderber model. While in GO-polymer hybrid systems, the electron transfer occurs between graphene sheets and functional molecules covalently or non-covalently bonded to graphene, which may avoid the “voltage–time dilemma”.

However, to meet the requirements of future memory applications, GO-based resistance memories should overcome several hurdles. Firstly, the size and chemical composition of GO sheets must be controllable, for example, the type, number and distribution of oxygen functional groups attached to both sides of graphene sheets. Secondly, the resistive switching mechanism of GO is still not clear. For metal/GO/metal sandwiches, although the formation/rupture of metal filaments is considered to be responsible for the resistive switching, the filament growth and inhibition kinetics remains ambiguous. As to the switching of GO-polymer hybrid, no direct evidences have been provided to support the charge transfer hypothesis so far. Thirdly, it is a real challenge to improve the thermal stability of GO and GO-polymer hybrid since memory devices may work at elevated temperature.

References

  1. 1. Avouris P. Chen Z. H. Perebeinos V. 2007 Carbon-based electronics Nature Nanotechnology 2 10 1748-3387
  2. 2. Baikalov A. Wang Y. Q. Shen B. Lorenz B. Tsui S. Sun Y. Y. Xue Y. Y. Chu C. W. 2003 Field-driven hysteretic and reversible resistive switch at the Ag-Pr0.7Ca0.3MnO3 interface Applied Physics Letters 83 5 957 959 0003-6951
  3. 3. Beck A. Bednorz J. G. Gerber Ch. Rosse C. L. Widmer D. 2000 Reproducible switching effect in thin oxide films for memory applications Applied Physics Letters 77 1 139 141 0003-6951
  4. 4. Burghard M. Klauk H. Kern K. 2009 Carbon-Based Field-Effect Transistors for Nanoelectronics Advanced Materials 21 25-26 2586 2600 0935-9648
  5. 5. Chang W. Y. Lai Y. C. Wu T. B. Wang S. F. Chen F. Tsai M. J. 2008 Unipolar resistive switching characteristics of ZnO thin films for nonvolatile memory applications Applied Physics Letters 92 2 22110 0003-6951
  6. 6. Cote L. J. Kim F. Huang J. X. 2009 Langmuir−Blodgett Assembly of Graphite Oxide Single Layers Journal of the American Chemical Society 131 3 1043 1049 0002-7863
  7. 7. Dong Y. Yu M. G. Mc Alpine C. Lu W. Lieber C. M. 2008 Si/α-Si core/shell nanowires as nonvolatile crossbar switches Nano Letters 8 2 386 391 1530-6984
  8. 8. Eda G. Fanchini G. Chhowalla M. 2008 Large-area ultrathin films of reduced graphene oxide as a transparent and flexible electronic material Nature Nanotechnology 3 5 270 274 1748-3387
  9. 9. Elias D. C. Nair R. R. Mohiuddin T. M. G. Morozov S. R. Blake P. Halsall M. P. Ferrari A. C. 2009 Control of graphene’s properties by reversible hydrogenation: Evidence for graphane Science 323 5914 610 613 0036-8075
  10. 10. Guan W. H. Long S. B. Jia R. Liu M. 2007 Nonvolatile resistive switching memory utilizing gold nanocrystals embedded in zirconium oxide Applied Physics Letters 91 6 062111 0003-6951
  11. 11. Guan W. H. Liu M. Long S. B. Liu Q. Wang W. 2008 On the resistive switching mechanisms of Cu/ZrO2:Cu/Pt Applied Physics Letters 93 22 223506 0003-6951
  12. 12. He C. L. Zhuge F. Zhou X. F. Li M. Zhou G. C. Liu Y. W. Wang J. Z. Chen B. Su W. J. Liu Z. P. Wu Y. H. Cui P. Li R. W. 2009 Nonvolatile resistive switching in graphene oxide thin films Applied Physics Letters 95 23 232101 0003-6951
  13. 13. He C. L. Shi Z. W. Zhang L. C. Yang W. Yang R. Shi D. X. Zhang G. Y. 2012 Multilevel resistive switching in planar graphene/SiO2 nanogap structures ACS Nano 6 5 4214 4221 1936-0851
  14. 14. Hong S. K. Kim J. E. Kim S. O. Choi S. Y. Cho B. J. 2010 Flexible resistive switching memory device based on graphene oxide IEEE Electron Device Letters 31 9 1005 1007 0741-3106
  15. 15. Hong S. K. Kim J. E. Kim S. O. Cho B. J. 2011 Analysis on switching mechanism of graphene oxide resistive memory device Journal of Applied Physics 110 4 044506 0021-4922
  16. 16. Hu B. L. Quhe R. G. Chen C. Zhuge F. Zhu X. J. Peng S. S. Chen X. X. Pan L. Wu Y. Z. Zheng W. G. Yan Q. Lu J. Li R. W. Electrically controlled electron transfer and resistance switching in graphene oxide noncovolently functionalized with dye unpublished
  17. 17. Jeong D. S. Schroeder H. Waser R. 2009 Abnormal bipolar-like resistance change behavior induced by symmetric electroforming in Pt/TiO2/Pt resistive switching cells Nanotechnology 20 37 375201 0957-4484
  18. 18. Jeong D. S. Schroeder H. Waser R. 2009 Mechanism for bipolar switching in a Pt/TiO2/Pt resistive switching cell Physical Review B 79 19 195317 1098-0121
  19. 19. Jeong H. Y. Kim J. Y. Kim J. W. Hwang J. O. Kim J. E. Lee J. Y. Yoon T. H. Cho B. J. Kim S. O. Ruoff R. S. Choi S. Y. 2010 Graphene oxide thin films for flexible nonvolatile memory applications Nano Letters 10 11 4381 4386 1476-1122
  20. 20. Jo S. H. Lu W. 2008 CMOS Compatible Nanoscale Nonvolatile Resistance Switching Memory Nano Letters 8 2 392 397 1476-1122
  21. 21. Jo S. H. Kim K. H. Lu W. 2009 Programmable Resistance Switching in Nanoscale Two-Terminal Devices Nano Letters 9 1 496 500 1476-1122
  22. 22. Jo S. H. Kim K. H. Lu W. 2009 High-Density Crossbar Arrays Based on a Si Memristive System Nano Letters 9 2 870 874 1476-1122
  23. 23. Kim D. C. Lee M. J. Ahn S. E. Seo S. Park J. C. Yoo I. K. Baek I. G. Kim H. J. Yim E. K. Lee J. E. Park S. O. Kim H. S. In Chung. U. Moon J. T. Ryu B. I. 2006 Improvement of resistive memory switching in NiO using IrO2 Applied Physics Letters 88 23 232106 0003-6951
  24. 24. Kim K. M. Choi B. J. Shin Y. C. Choi S. Hwang C. S. 2007 Anode-interface localized filamentary mechanism in resistive switching of TiO2 thin films Applied Physics Letters 91 1 012907 0003-6951
  25. 25. Kim S. Moon H. Gupta D. Yoo S. Choi Y. K. 2009 Resistive Switching Characteristics of Sol-Gel Zinc Oxide Films for Flexible Memory Applications IEEE Transactions on Electron Devices 56 4 696 699 0018-9383
  26. 26. Kwon D. H. Kim K. M. Jang J. H. Jeon J. M. Lee M. H. Kim G. H. Li X. S. Park G. S. Lee B. Han S. Kim M. Hwang C. S. 2010 Atomic structure of conducting nanofilaments in TiO2 resistive switching memory Nature Nanotechnology 5 2 148 153 1748-3387
  27. 27. Lee M. J. Park Y. Suh D. S. Lee E. H. Seo S. Kim D. C. Jung R. Kang B. S. Ahn S. E. Lee C. B. Seo D. H. Cha Y. K. Yoo I. K. Kim J. S. Park B. H. 2007 Two Series Oxide Resistors Applicable to High Speed and High Density Nonvolatile Memory Advanced Materials 19 22 3919 3923 0935-9648
  28. 28. Li Y. T. Long S. B. Liu Q. Lv H. B. Liu S. Liu M. 2011 An overview of resistive random access memory devices Chinese Science Bulletin 56 28-29 3072 3078 1001-6538
  29. 29. Liao Z. L. Wang Z. Z. Meng Y. Liu Z. Y. Gao P. Gang J. L. Zhao H. W. Liang X. J. Bai X. D. Chen D. M. 2009 Categorization of resistive switching of metal-Pr0.7Ca0.3MnO3-metal devices Applied Physics Letters 94 25 253503 0003-6951
  30. 30. Ling Q. D. Liaw D. J. Zhu C. X. Chan D. S. H. Kang E. T. Neoh K. G. 2008 Polymer electronic memories: Materials, devices and mechanisms Progress in Polymer Sciecne 33 10 917 978 0079-6700
  31. 31. Liu S. Q. Wu N. J. Ignatiev A. 2000 Electric-pulse-induced reversible resistance change effect in magnetoresistive films Applied Physics Letters 76 19 2749 2751 0003-6951
  32. 32. Liu Q. Long S. B. Wang W. Zuo Q. Y. Zhang S. Chen J. N. Liu M. 2009 Improvement of resistive switching properties in ZrO2-based ReRAM with implanted Ti ions IEEE Electron Device Letters 30 12 1335 1337 0741-3106
  33. 33. Liu G. Zhuang X. D. Chen Y. Zhang B. Zhu J. H. Zhu C. X. Neoh K. G. Kang E. T. 2009 Bistable electrical switching and electronic memory effect in a solution-processable graphene oxide-donor polymer complex Applied Physics Letters 95 25 253301 0003-6951
  34. 34. Lu W. Lieber C. M. 2007 Nanoelectronics from the bottom up Nature Materials 6 11 841 850 1476-1122
  35. 35. Mikolajick T. Salinga M. Kund M. Kever T. 2009 Nonvolatile memory concepts based on resistive switching in inorganic materials Advanced Engineering Materials 11 4 235 240 1438-1656
  36. 36. Nian Y. B. Strozier J. Wu N. J. Chen X. Ignatiev A. 2007 Evidence for an oxygen diffusion model for the electric pulse induced resistance change effect in transition-metal oxides Physical Review Letters 98 14 146403 0031-9007
  37. 37. Novoselov K. S. Geim A. K. Morozov S. V. Jiang D. Zhang Y. Dubonos S. V. Grigorieva I. V. Firsov A. A. 2004 Electric field effect in atomically thin carbon films Science 306 5696 666 669 0036-8075
  38. 38. Odagawa A. Sato H. Inoue I. H. Akoh H. Kawasaki M. Tokura Y. 2004 Colossal electroresistance of a Pr0.7Ca0.3MnO3 thin film at room temperature Physical Review B 70 22 224403 1098-0121
  39. 39. Panin G. N. Kapitanova O. O. Lee S. W. Baranov A. N. Kang T. W. 2011 Resistive switching in Al/graphene oxide/Al structure Japanese Journal of Applied Physics 50 7 070110 0021-4922
  40. 40. Pinnow C. U. Mikolajick T. 2004 Material aspects in emerging nonvolatile memories Journal of the Electrochemical Society 151 6 K13 K19 0013-4651
  41. 41. Robinson J. T. Perkins F. K. Snow E. S. Wei Z. Sheehan P. E. 2008 Reduced graphene oxide molecular sensors Nano Letters 8 10 3137 3140 1476-1122
  42. 42. Rozenberg M. J. Inoue I. H. Sanchez M. J. 2004 Nonvolatile memory with multilevel switching: A basic model Physical Review Letters 92 17 178302 0031-9007
  43. 43. Rozenberg M. J. Sanchez M. J. Weht R. Acha C. Gomez-Marlasca F. Levy P. 2010 Mechanism for bipolar resistive switching in transition-metal oxides Physical Review B 81 11 115101 1098-0121
  44. 44. Rueckes T. Kim K. Joselevich E. Tseng G. Y. Cheung C. L. Lieber C. M. 2000 Carbon nanotube-based nonvolatile random access memory for molecular computing Science 289 5476 94 97 0036-8075
  45. 45. Sawa A. Fujii T. Kawasaki M. Tokura Y. 2004 Hysteretic current-voltage characteristics and resistance switching at a rectifying Ti/Pr0.7Ca0.3MnO3 interface Applied Physics Letters 85 18 4073 4075 0003-6951
  46. 46. Schroeder H. Zhirnov V. V. Cavin R. K. Waser R. 2010 Voltage-time dilemma of pure electronic mechanisms in resistive switching memory cells Journal of Applied Physics 107 5 054517 0021-4922
  47. 47. Seo S. Lee M. J. Seo D. H. Jeoung E. J. Suh D. S. Joung Y. S. Yoo I. K. Hwang I. R. Kim S. H. Byun I. S. Kim J. S. Choi J. S. Park B. H. 2004 Reproducible resistance switching in polycrystalline NiO films Applied Physics Letters 85 23 5655 5657 0003-6951
  48. 48. Simmons J. G. Verderber R. R. 1967 New conduction and reversible memory phenomena in thin insulating films Proceedings of the Royal Society of London Series A-Mathematical and Physical Sciences 301 1464 77 1364-5021
  49. 49. Sinitskii A. Tour J. M. 2009 Lithographic graphitic memories ACS Nano 3 9 2760 2766 1936-0851
  50. 50. Son J. Y. Shin Y. H. 2008 Direct observation of conducting filaments on resistive switching of NiO thin films Applied Physics Letters 92 22 222106 0003-6951
  51. 51. Standlety B. Bao W. Z. Zhang H. Bruck J. Lau C. N. Bockrath M. 2008 Graphene-based atomic-scale switches Nano Letters 8 10 3345 3349 1476-1122
  52. 52. Stankovich S. Dikin D. A. Dommett G. H. B. Kohlhaas K. M. Zimney E. J. Stach E. A. Piner R. D. Nguyen S. T. Ruoff R. S. 2006 Graphene-based composite materials Nature 442 7100 282 286 0028-0836
  53. 53. Stewart D. R. Ohlberg D. A. A. Beck P. A. Chen Y. Williams R. S. Jeppesen J. O. Nielsen K. A. Stoddart J. F. 2004 Molecule-Independent Electrical Switching in Pt/Organic Monolayer/Ti Devices Nano Letters 4 1 133 136 1476-1122
  54. 54. Szot K. Speier W. Bihlmayer G. Waser R. 2006 Switching the electrical resistance of individual dislocations in single-crystalline SrTiO3 Nature Materials 5 4 312 320 1476-1122
  55. 55. Tsuruoka T. Terabe K. Hasegawa T. Aono M. 2010 Forming and switching mechanisms of a cation-migration-based oxide resistive memory Nanotechnology 21 42 425205 0957-4484
  56. 56. Tsuruoka T. Terabe K. Hasegawa T. Valov I. Waser R. Aono M. 2012 Effects of moisture on the switching characteristics of oxide-based, gapless-type atomic switches Advanced Functional Materials 22 1 70 77 1616-301X
  57. 57. Tulina N. A. Zver’kov S. A. Mukovskii Y. M. Shulyatev D. A. 2001 Current switching of resistive states in normal-metal manganite single-crystal point contacts Europhysics Letters 56 6 836 841 1286-4854
  58. 58. Wang L. H. Yang W. Sun Q. Q. Zhou P. Lu H. L. Ding S. J. Zhang D. W. 2012 The mechanism of the asymmetric SET and RESET speed of graphene oxide based flexible resistive switching memories Applied Physics Letters 100 6 063509 0003-6951
  59. 59. Wang X. R. Ouyang Y. J. Li X. L. Wang H. L. Guo J. Dai H. J. 2008 Room-Temperature All-Semiconducting Sub-10-nm Graphene Nanoribbon Field-Effect Transistors Physical Review Letters 100 20 206803 0031-9007
  60. 60. Waser R. Aono M. 2007 Nanoionics-based resistive switching memories Nature Materials 6 11 833 840 1476-1122
  61. 61. Waser R. Dittmann R. Staikov G. Szot K. 2009 Redox-based resistive switching memories-Nanoionic mechanisms, prospects, and challenges Advanced Materials 21 25-26 2632 2663 1476-1122
  62. 62. Wu X. Zhou P. Li J. Chen L. Y. Lv H. B. Lin Y. Y. Tang T. A. 2007 Reproducible unipolar resistance switching in stoichiometric ZrO2 films Applied Physics Letters 90 18 183507 0003-6951
  63. 63. Wu C. X. Li F. S. Zhang Y. A. Guo T. L. Chen T. 2011 Highly reproducible memory effect of organic multilevel resistive-switch device utilizing graphene oxide sheets/polyimide hybrid nanocomposite Applied Physics Letters 99 4 042108 0003-6951
  64. 64. Yang C. H. Seidel J. Kim S. Y. Rossen P. B. Yu P. Gajek M. Chu Y. H. Martin L. W. Holcomb M. B. He Q. Maksymovych P. Balke N. Kalinin S. V. Baddorf A. P. Basu S. R. et al. 2009 Electric modulation of conduction in multiferroic Ca-doped BiFeO3 films Nature Materials 8 6 485 493 1476-1122
  65. 65. Yang Y. C. Pan F. Liu Q. Liu M. Zeng F. 2009 Fully Room-Temperature-Fabricated Nonvolatile Resistive Memory for Ultrafast and High-Density Memory Application Nano Letters 9 4 1636 1643 1476-1122
  66. 66. Yin K. B. Li M. Liu Y. W. He C. L. Zhuge F. Chen B. Lu W. Pan X. Q. Li R. W. 2010 Resistance switching in polycrystalline BiFeO3 thin films Applied Physics Letters 97 4 042101 0003-6951
  67. 67. Yu A. D. Liu C. L. Chen W. C. 2012 Supramolecular block copolymers: graphene oxide composites for memory device applications Chemical Communications 48 3 383 385 1359-7345
  68. 68. Zhuang X. D. Chen Y. Liu G. Li P. P. Zhu C. X. Kang E. T. Neoh K. G. Zhang B. Zhu J. H. Li Y. X. 2010 Conjugated-polymer-functionalized graphene oxide: Synthesis and nonvolatile rewritable memory effect Advanced Materials 22 15 1731 1735 1476-1122
  69. 69. Zhuge F. Dai W. He C. L. Wang A. Y. Liu Y. W. Li M. Wu Y. H. Cui P. Li R. W. 2010 Nonvolatile resistive switching memory based on amorphous carbon Applied Physics Letters 96 16 163505 0003-6951
  70. 70. Zhuge F. Hu B. L. He C. L. Zhou X. F. Liu Z. P. Li R. W. 2011 Mechanism of nonvolatile resistive switching in graphene oxide thin films Carbon 49 12 3796 3802 0008-6223
  71. 71. Zhuge F. Li R. W. He C. L. Liu Z. P. Zhou X. F. 2011 Non-volatile resistive switching in graphene oxide thin films Physics and Applications of Graphene-Experiments 421 438 Print 978-953-307-217-3 Croatia Mar. 2011 InTech

Written By

Fei Zhuge, Bing Fu and Hongtao Cao

Submitted: 03 June 2012 Published: 27 March 2013