1. Introduction
The discovery of new materials with unique properties often leads to new technology. After discovery of conductive polymers at the end of the 1970s, it opened up a whole new research, which eventually led to a new technology of plastic electronics (Chiang et al., 1978). When interesting material properties are observed in the laboratory, efforts are made to understand their mechanisms, which leads to the fine control of the fabrication process of this new and potentially important material. If future applications are anticipated, optimization of material properties becomes a continuous and sometimes a lifelong process. Doping of materials is one of the ways of modifying their physical properties. For example, a pure silicon (Si), which has a very poor electrical conducting properties can be doped with boron or arsenic to make it a good hole or electron conductor respectively. This opened up a new class of doped-Si materials, which is now the basis of perhaps the largest global electronics industry.
Polymers, which consist of large molecules linked together in repeated fashion to form long chains, have naturally existed for a long time. Examples are tortoise shell, tar and horns. Today synthetic polymers are finding important applications in many areas. Polyolefins, epoxies and engineering resins are crucial materials for construction, commerce, transportation and entertainment. They are very appealing alternative materials because of the simple processing they offer such as drop casting, spray painting and printing. In addition, they almost provide low cost large-area scalability. In most applications however, polymeric materials are multicomponent systems. The integration of fillers such as minerals, ceramics, metals or even air, can generate an infinite variety of new materials with unique physical properties and possibly reduced production cost. Typically, when the filler in these multicomponent systems, which represents a minor constituent, has at least one dimension below 100 nm, the resulting material is termed, “polymer nanocomposite“ (Winey & Vaia, 2007). Reseach in this area is very active and promising, mainly because of many different combinations of polymers and filler materials that can be explored. Few examples of fillers that were recently reported are SrTiO3 (Umeda et al., 2009), fluorinated single walled carbon nanotubes (Bennett et al., 2009) and ZnS-coated CdSe nanocrystals ( Kim et al., 2009 ).
The addition of a small amount of filler material into a host polymer can be considered a doping process if there is an intention of modifying the physical properties of the host. Some fillers, particularly with macroscopic dimensions, do not chemically react with the polymer so they cannot be regarded as dopants. Nanomaterials are attractive dopants to polymers because of their high surface reactivity, which is attributed to very large surface-to-volume ratio. Moreover, they possess intriguing properties associated with quantum confinement effects, making their interaction with different polymers a subject of great interest. They can also be dispersed into water or organic solvents, providing a simple process of doping polymeric solutions. It should be realized that nanomaterial-doped polymers should also be classified as polymer nanocomposite because they are multicomponents systems with a low dimensional non-polymer minor constituent embedded in a host polymer. When the nanomaterial dopant is inorganic, the term “hybrid nanocomposite“ is specifically used for the reason that it becomes an inorganic-organic system. This manuscript focuses on the effect of doping polymers with ZnO nanostructures such as nanowires, nanorods, tetrapods and nanoparticles. Their combination may achieve three goals: 1) tailor the property of ZnO; 2) tailor the property of polymer or 3) create a hybrid nanocomposite with unique or enhanced properties. A discussion of how these goals are relevant for optoelectronic and sensor applications is presented.
2. ZnO as dopant to polymers
2.1. Technological importance of ZnO
ZnO has received much attention in recent years due to its diverse properties. It is a direct wide bandgap semiconductor (Eg = 3.4 eV) with large exciton binding energy (~60 meV), suggesting that it is a promising candidate for stable room temperature luminescent and lasing devices. It exhibits strong ultraviolet (Huang et al., 2001) and visible photoluminescence (Konenkamp et al., 2004). ZnO film can be used as transparent conducting electrode. It is also a piezoelectric material, with potential applications in surface acoustic wave filters (Wang et al., 2008). Ferromagnetism in ZnO has already been reported ( Kim et al., 2009 ) so it is being considered a material for spintronics. With all these important properties, it becomes more attractive because of its abundance in nature. It can be fabricated practically into different forms like thin film and nanowire using a variety of methods such as solution-based approaches, vacuum deposition techniques chemical vapor deposition.
2.2. Fabrication of ZnO nanostructures for dispersion in solution
There are several ways of fabricating ZnO nanostructures on a substrate. Nanowires, nanorods, nanobelts, nanoneedles and nanosprings have been reported by many researchers. For doping polymers, it is advantageous for the nanostructures to be dispersed in a solution since most polymers are prepared via a solution process. ZnO nanostructures grown on a substrate can be scraped and dispersed into a solvent. This approach however does not produce enough amount of nanostructures. Hence, it is not a practical method for obtaining a usable concentration of ZnO in a solvent. Solution-based methods have been widely used to prepare ZnO nanostructures. Nanorods and nanowires with variable-aspect-ratio (length/diameter) have been prepared in alcohol/water solution by reacting a Zn2+ precursor with an organic weak base, tetramethylammonium hydroxide (Me4NOH) at temperature window of 75 – 150 oC (Cheng et al., 2006). In another report, a room temperature wet-chemical approach was employed to synthesize highly regulated, monodispersed ZnO nanorods and derived hierarchical nanostructures such as hexagonally branched, reversed umbrella-type and cactus-like (Liu & Zeng, 2004). These hierarchical nanostructures are comprised of individual
One of the disadvantages of solution-based ZnO fabrication is that it involves successive processes that take a fair amount of time. After the synthesis, the product has to be thoroughly cleaned to remove all traces of chemicals used in the process. In this article, a simple, straightforward method to fabricate ZnO nanostructures with fast turn around is explored. It is based on the oxidation of zinc vapor while a high purity Zn metal is being thermally evaporated. Figure 1 is a diagram that illustrates this method. The Zn source is placed in a crucible, which is then inserted into a vertically-oriented quartz tube. The tube is flushed with argon to remove ambient air and its open end is sealed [Figure 1(a)]. It is inserted into a vertically-oriented furnace set at 600 oC to evaporate the Zn. When the source starts to evaporate, air is allowed to diffuse towards the crucible by opening the seal. With the correct diffusion rate of O2 and evaporation rate of Zn, oxidation can be contained inside the crucible. Thus, the growth of ZnO nanostructures mainly occurs in the crucible. Figure 1(b) shows the actual crucible before and after the growth process. Typically, when the amount of Zn source is 0.03 g, it yields approximately 0.01 g of ZnO, which is the white material that fills the crucible in the picture. The product is like a cotton as shown by the SEM picture in Figure 1(c). It can be easily collected and dispersed in a solution. The entire fabrication process only takes less than 30 minutes. It is highly scalable and can be employed to mass-produce ZnO nanostructures.
The cotton-like ZnO product shown in Figure 1(c) consists of different nanostructures entangled together. They can be separated and size selected if desired. Two solvents were tried to disperse them: water and chlorobenzene. By ultrasonication, they were effectively segregated in both solvents. The solution became whitish after several minutes of agitation. When the procedure was stopped, ZnO structures slowly settled at the bottom and as expected, large entities sank first. This can be used as a simple size-selection method. For example, nanoparticles with lower diameter are the last ones to settle at the bottom. If the solution is allowed to be still for a long time after sonication, then get the top part of it, nanoparticles are obtained. They are shown in Figure 2(a). They are deposited on Si wafer by drop casting. If the large and unwanted entities are already removed, good nanowires can be extracted from the bottom of the solution. These nanowires are shown in Figure 2(b). Their length could exceed 10 m.
3. Polymer-based light emitting devices
3.1. Basic requirements for efficient electroluminescence
Polymeric-based light emitting device is one type of OLED, which stands for organic light emitting diode. Photon is generated in the polymer emissive layer (EL), which should possess excellent photoluminescence (PL) properties. In an efficient device, the EL is sandwiched between an electron transport layer (ETL), which injects electrons into the LUMO (lowest unoccupied molecular orbital) of the EL, and a hole transport layer (HTL), which injects holes into the HOMO (highest occupied molecular orbital) of the EL. The injected electrons and holes undergo radiative recombination due to the applied electric field. The charge transporting layers serve as facilitator for efficient charge transfer from the electrodes to the EL. This is illustrated in Figure 3. When a negative potential is applied to the anode, which is a low work function metal, electrons are injected into the ETL. If the ETL has excellent electron mobility (
3.2. Control of charge transport
One of the benefits of doping polymers in OLED with ZnO nanostructures is the improvement in charge carrier transport. It has been reported that by incorporating ZnO nanorods with the EL material PVK:DCJTB, which represents poly(vinylcarbazole) doped with 4-(dicyanomethylene)-2-
A similar observation has been reported on poly[2-methoxy,5-(2-ethylhexyloxy)-1,4-phenylenevinylene], which is commonly called MEH-PPV for short (Xu et al., 2007). By doping the MEH-PPV with ZnO nanocrystals or tetrapods and employing it to build field effect transistor, the authors showed higher
3.3. Control of optical emission
The high surface reactivity of ZnO nanostructures with certain polymers may provide interactions that can modify polymer properties in a positive way. The interaction of ZnO quantum dots (QDs) with poly(vinyl alcohol) (PVA) has already been demonstrated (Sui et al., 2005). The authors prepared PVA/ZnO hybrid nanofibers with ZnO concentration of 10 wt% and employed differential scanning calorimetry (DSC) to study them with respect to pure PVA. It is known that the two exothermic peaks at about 305 oC and 500 oC are associated with the degradation of side chain (the scission of C-O) and main chain (the scission of C-C) with the delta enthalphy of 3760 and 1188 J g-1, respectively (Koji et al., 1999). For PVA/ZnO nanofibers, the exothermic peak below 450 oC was not observed, while the peak around 500 oC was sharp and strong with delta enthalpy of 3305 J g-1, suggesting that ZnO modifies the property of PVA. Their interaction, which is via the formation of an H bond and an O-Zn-O bond between PVA molecule and ZnO, is believed to be responsible for the novel luminescent properties of PVA/ZnO nanofibers.
Figure 4 shows a typical PL spectrum of ZnO nanowires (NWs) prepared by the physical vapor transport method described in section 2.2. It has two emission bands around 380 and 520 nm, which is consistent with another report using a polymer-assisted route (Li et al., 2003). The UV emission originates primarily from a mixture of free exciton and bound exciton related to impurity or defects (Shan et al., 2005). The visible emission comes from the transition between the electron near the conduction band and the deeply trapped hole at the V0 ** center which is an oxygen vacancy containing no electrons (Dijken et al., 2000). It is also attributed to the transition between the electron at [V0 *, electron] or [V0 **, two electrons] and the hole at vacancy associated with the surface defects. For pure PVA, the PL spectrum consists of two emission bands at about 364 and 440 nm, originating from its organic functional groups (Sui et al., 2005). In PVA/ZnO hybrid film, the PL spectrum is a superposition of the PL of each component. The 440 nm emission from PVA overlaps with the 550 nm from ZnO making the visible emission band broader. In hybrid nanofibers however, this visible emission is much intense possibly due to two factors. In the film, ZnO-QDs can easily form aggregates resulting in bigger particle exhibiting bulk behavior. This is in fact one of the issues in polymer nanocomposites and ways to circumvent it are being explored (Sun et al., 2008). In the nanofiber, QDs align along the PVA matrix, resulting in better dispersion. Individual QD also interacts strongly with the PVA molecule. The other factor is the high surface to volume ratio of the nanofiber, which enhances the visible luminescence due to surface defects (Shalish et al., 2004).
The interaction between ZnO and polymer can also provide several new radiative recombination mechanisms that may be utilized for broadband light emission or wavelength tunable emission. Since these mechanisms are influenced by several factors such as the individual properties of the organic and inorganic components as well as their relative concentration, control of emission properties may be done in a number of ways. The existence of new recombination mechanisms is strongly suggested by the generation of new PL emission lines (420, 460 & 480 nm) when MEH-PPV is doped with ZnO nanoparticles (Aleshin et al., 2009). In this work, the authors prepared the polymer nanocomposite film on a Si substrate with a 200 nm-thick SiO2 layer via drop casting or spin coating. Gold and aluminum electrodes were then deposited on top with separation of 7 – 15 m. With this device structure, they could investigate PL while applying an external electric field. The existence of new emission lines, which could not be generated when ZnO was replaced by Si nanoparticles, was attributed to the formation of interfacial states termed exciplex. These states are formed in a type II heterojunction, such as ZnO/MEH-PPV, where there is an accumulation of electrons and holes on the opposite side. Charge transport is blocked by the barriers that result from the offset of HOMO and conduction band edge of MEH-PPV and ZnO respectively. It was proposed that since the carriers cannot proceed across the heterojunction, they diffuse two-dimensionally along the interface until they encounter an oppositely charged carrier on the opposite side of the interface and these form an exciplex (Morteani et al., 2005). If bulk exciton in the ZnO or MEH-PPV is within the exciton diffusion length, it can excite exciplex emission. It should be mentioned that the influence of ZnO nanoparticles is most dramatic at an optimum concentration of 10 wt%. This could be ascribed to the aggregation of nanoparticles which reduces interaction with polymer.
Another observed phenomena when MEH-PPV is doped with ZnO is the blue shift of its PL emission spectrum accompanied by quenching. At 2 wt% concentration of ZnO nanoparticles, 11 nm shift has been reported ( Ton-That et al., 2008 ). This shift increases with increasing nanoparticle concentration. However, its dependence becomes weaker at concentration greater than 4%. Using Raman spectroscopy, the authors did not observe any changes in the conjugation length, which may have caused the blue shift in PL spectrum. Their results indicate that the chemical structure and the gap energy of MEH-PPV is not affected by the incorporation of ZnO nanoparticles. Thus, they explained their observation in terms of the effect of electric field produced by excess electrons on the nanoparticles surface (Musikhin et al., 2002). The surface of ZnO nanoparticles is a strong perturbation of the lattice where there exists a high concentration of both shallow and deep defect levels ( Ton-That et al., 2008 ). X-ray photoelectron spectroscopy (XPS) analysis of their surface revealed that there is a large number of oxygen vacancies. These vacancies can accept electrons from MEH-PPV, creating an electric field outside the nanoparticles. As a result, the energy of the lowest exciton state is raised resulting in the blue shift of the luminescence.
4. Polymer-based photovoltaics
4.1. Challenges
The highest power conversion efficiency () demonstrated by a polymer-based solar cell is achieved by employing an active layer blend of poly(3-hexylthiophene) and (6,6)-phenyl C61 butyric acid methyl ester (Ma et al., 2005). For convenience, this blend will be referred as P3HT:PCBM. It has a strong optical absorbance in the limited wavelength range of 400 nm to 600 nm mainly due to the P3HT. Because of this narrow band absorption, more than 60% of the photons in the solar spectrum are not harnessed. In fact, even the ones absorbed are not 100% converted to photocurrent because not all electron-hole pairs become free charges. Exciton binding energy of P3HT is so large that it does not lead directly to free charge carriers. However, the high electron affinity of PCBM provides sufficient potential difference that breaks exciton and thus it becomes energetically favourable for the electrons to jump from the LUMO of P3HT to the LUMO of PCBM. This electron donor-acceptor mechanism implies that only excitons near the P3HT/PCBM interface dissociate. The maximum distance for dissociation to occur is determined by the exciton diffusion length (), which is around 10 nm for P3HT. In the blend, phase segregation results in the formation of isolated islands of P3HT and PCBM. The size of P3HT islands could be more than so not all excitons can dissociate. There is another factor in the exciton dissociation process that reduces . Excited electrons in P3HT have excess energy that is dissipated quickly when they transfer to the PCBM. This energy loss, which depends on the energy alignment of the two materials, is reflected in the open circuit voltage (Koster et al., 2006).
In a photovoltaic device, separated holes and electrons need to reach their respective electrodes to have high . This requires the blend to have high values of hole (h) and electron (e) mobilities. Good balance of mobilities is obtained using optimum ratio of P3HT and PCBM, which is estimated to be between 1:1 and 1:0.9 (Chirvase et al., 2004). This could yield values of h ~ 6.5 x 10-6 cm2/V-s and e ~ 5.0 x 10-6 cm2/V-s. However these numbers are still far inferior when compared to their inorganic counterpart, which raises the question of whether doping with inorganic nanostructures such as ZnO would be beneficial. In the blend, PCBM does not provide direct conduction pathways for electrons towards the electrode because of the isolated island formation. Electrons undergo a hopping process between PCBM islands before reaching the electrode. Thus, they become prone to recombination with holes. This limits the thickness of the active layer. High efficient P3HT:PCBM devices are achieved with active layer thickness around 100 nm to 200 nm, which is not the optimum thickness for photon absorption. Increasing the thickness absorbs more photons but it also increases the electron-hole recombination and degrades charge transport. The final stage of charge transport from point of exciton dissociation to the electrode is the crossing of the organic-inorganic interface. Large contact resistance will reduce the fill factor of a device. Potential barriers at the interface originating from impurities or polymer damage during vacuum deposition of the metal electrodes may also limit the open circuit voltage. Controlling the organic-inorganic interfacial properties is an important and urgent challenge in organic electronics. Several ways have already been explored such as insertion of very thin interlayer (Brabec et al., 2002), tuning the work function of the inorganic electrode (Sharma et al., 2009) and surface doping of polymer (Mukherjee et al., 2007).
4.2. ZnO as electron acceptor
PCBM is the most widely used electron acceptor for P3HT in a bulk heterojunction (BHJ) solar cell. It has the right LUMO and HOMO levels for charge separation and exchange. Its electron mobility in the order of 10-2 cm2/V-s, is sufficient for transporting photogenerated electrons towards the electrodes. However, higher mobilities are still demonstrated by inorganic materials. Wurtzite ZnO for example can have electron mobility of 200 cm2/V-s. Its LUMO and HOMO levels are well positioned to accept electrons from P3HT. Thus, doping of conjugated polymers with ZnO nanostructures can be employed to fabricate BHJ solar cells. For example, P3HT doped with ZnO nanoparticles yielded a photovoltaic device with ~ 0.92% at optimum concentration of 26% by volume (Beek et al., 2006). The values of the open circuit voltage (
In another work, ZnO nanofibers were grown on the transparent electrode to achieve fixed morphology before the introduction of the P3HT (Olson et al., 2007). By spin-coating the P3HT on top of the ZnO nanostructure followed by annealing, intercalation into the voids between the nanofibers was induced. In this structure, a huge donor-acceptor interface area is formed between the P3HT and ZnO for exciton dissociation. Photogenerated electrons injected into the ZnO are transported directly towards the collecting electrode, providing pathways with higher electron mobility. The growth of ZnO nanofibers on ITO-coated glass was achieved via a low-temperature hydrothermal route from a solution of zinc nitrate precursor. In this device structure in which Ag is used as back electrode instead of Al, electrons are collected by the ITO while holes are collected by the Ag. The best device they obtained had
4.3. Effect of ZnO nanowire doping on the Fermi level of P3HT
In polymer-based photovoltaics, it is important to obtain the desired junction characteristic of the polymer-metal interface. Depending on the device structure, it may require an Ohmic or a Schottky junction. The junction characteristic, which has a direct influence on the charge transfer from the active layer to the electrode, is determined by the energy level alignment of the polymer and the metal. Fermi level (EF) is the most fundamental parameter that is used to understand polymer-metal junction. It determines the work function (energy difference between EF and vacuum level) of a material. It can be used to predict the built in potential (
In this manuscript, recent results are presented about the change in the Fermi level of P3HT when doped with ZnO nanowires. This system is already being explored as an active layer together with Al as back electrode (Beek et al., 2006). To measure
The device structure is shown on Figure 5(a). Both doped and undoped devices exhibited good rectifying behaviour as depicted by their
Where
The work function of P3HT is around 5.1 to 5.2 eV. For Al, it ranges from 4.0 to 4.3 eV. The ZnO-doped P3HT has Vbi of 1.181V, indicating that EF of the P3HT moved farther from the valence band edge and closer to the EF of Al. One possible explanation for this reduction is the increase in the free electron concentration in the polymer nanocomposite provided by the ZnO. In semiconductors, EF lies closer to the conduction band edge for n-type conductivity and it lies closer to the valence band edge for p – type conductivity. The upward shift in EF due to the ZnO may be the cause of the drop in VOC for P3HT:ZnO nanofibers BHJ (Olson et al., 2007). When the authors compared the photovoltaic performance of ZnO bilayer and ZnO nanofiber devices, they observed higher VOC in the bilayer device (500 mV versus 440 mV). Although the nanofiber device still had better due to its higher JSC. The results shown in Figure 6 may be helpful in optimizing BHJ solar cell based on P3HT and ZnO nanostructures. High values of JSC and VOC may be obtained simultaneously by tailoring the property of the active layer-metal interface or selecting alternative metals or alloys for back electrode.
5. Polymer-based conductivity sensors
5.1. Conductivity sensors for chemical detection
Conductivity sensors for chemical detection are very attractive because of their simple operation. The circuit design required to convert their response to electrical signals is relatively straightforward. These sensors are based on the change in the electrical conductivity of the sensing material due to its interaction with the stimuli. Device fabrication is also not difficult. For example, the sensing material may be deposited on interdigitated or two parallel electrodes, which form the connection for measuring the change in electrical resistance. Three common classes of sensing materials for conductivity sensors are conducting polymer composites, intrinsically conducting polymers and metal oxides (Arshak et al., 2004). The mechanism behind the change in conductivity is different for each class.
In conducting polymer composites, conducting particles such as polypyrrole and carbon black (Albert et al., 2000) are embedded in an insulating polymer matrix. The stimuli can cause expansion of the polymer and the polypyrrole particles resulting in the increase of electrical resistance. If the stimuli interact chemically with the polypyrrole, its intrinsic conductivity will also change, making the resistance change in the composite more difficult to interpret. The operation of intrinsically conducting polymers (ICP) such as polypyrrole, polythiophene and polyaniline, is based on the alteration of intrachain conductivity, intermolecular conductivity and ionic conductivity after interacting with the stimuli. Intrachain conductivity is detrmined by the backbone while intermolecular conductivity is due to electron hopping to different chains. Ionic conductivity is affected by proton tunneling induced by hydrogen bond interaction at the backbone and also by ion migration through the polymer. One reported application of ICP employed an array of conducting polymer sensors incorporating 3-Methylthiophene, Aniline and Pyrrole (Guadarrama et al., 2000). The authors evaluated the sensors to different wine varieties and considered the cross sensitivity of the polymeric films to moisture and ethanol. The operation of a metal oxide sensor is based on the dependence of the conductivity to O2 molecules adsorbed on its surface. For n-type metal oxides such as ZnO or TiO2, O2 molecules capture electrons on the surface or at the grain boundaries resulting in the decrease of conductivity. Trapped electrons at the grain boundaries also produce potential barriers between grains that impede current flow. When exposed to reducing gas like H2, CH4, CO, C2H5 or H2S, the adsorbed O2 molecules react with the gas and release the captured electrons. This increases the conductivity of the sensing material. When exposed to oxidizing gas like O2, NO2 or Cl2, the effect is opposite. Conductivity is decreased because the number of adsorbed O2 molecules that can capture electrons is increased. For p-type metal oxides, their response to oxidizing gas is to increase in conductivity because the capture of electrons produces more holes. In contrast, their conductivity decreases when exposed to reducing gases.
There are still many challenges in conductivity gas sensors. For polymer composites, aging is a concern because this leads to sensor drift. Their applicability is only limited to certain gases because of lack of sensitivity. For ICP, challenges include understanding the mechanism of sensor response, high sensitivity to humidity and drift in conductivity with time. These sensors can also have short lifetimes due to oxidation of the polymer. For metal oxides, one challenge is the low sensitivity at room temperature. They require higher operating temperatures and thus heating element has to be incorporated with the sensor (Roy & Basu, 2002) This increases the power consumption, which is not very appealing for handheld applications. Good selectivity is another challenge for metal oxide conductivity sensors. Their behavior to reducing gases is practically the same. For example, the conductivity of a sensor changed by when exposed to ethanol vapor with concentration C1. The same response can be realized when it is exposed to methanol with a different concentration C2. Thus, the identification of a particular reducing vapor, with a background of different others is almost impossible. Due to the mentioned challenges, there is a continuous effort to develop new materials for conductivity sensors. Reliable sensors with appropriate levels of selectivity and sensitivity will always be in demand. In the standpoint of defense and homeland security, new hazardous compounds or biomaterials that need to be detected is expected to arise. New applications such as self-powered sensors will require excellent energy efficient sensing materials without sacrificing sensitivity and selectivity.
5.2. Sensing with P3HT doped with ZnO nanowires
There is a lack of work in the exploration of ZnO doped polymers as conductivity sensors for chemical detection. Interestingly, only P3HT, which is mostly used in photovoltaics, has been reported to have promising sensing behavior when blended with ZnO-NWs (Saxena et al., 2007). As separate materials, P3HT and ZnO-NWs can both be used as a conductivity gas sensor. But due to the difference in their conductivity type, they have contrasting response to a specific stimulus. For example, they both exhibit high sensitivity to NO2 and H2S (Saxena et al., 2007). P3HT decreases in resistance upon exposure to NO2, which is oxidizing gas, while it behaves oppositely for H2S, a reducing gas. This characteristic is due to its p – type conductivity. The adsorption of an oxidizing compound on P3HT surface captures electrons leading to increased hole carrier concentration. Conversely, the adsorption of a reducing compound leads to the decrease in hole carrier concentration via the release of captured electrons. For n – type ZnO, the effect of oxidizing and reducing compounds is to decrease and increase conductivity respectively.
Doping of P3HT with oxygen defficient ZnO nanowires results in the reduction of P3HT. This is well supported by GI-XRD, XPS and FTIR studies (Saxena et al., 2007). The authors also observed decrease in the P3HT conductivity after ZnO doping suggesting that its hole carrier concentation drops when ZnO donates electrons. This interaction may be used to tailor the response of polymers to different stimuli, opening up the possilibity of tunable polymer-based conductivity sensors. For example, the authors have demonstrated that highly reduced P3HT resulting from ZnO doping, has enhanced sensitivity to NO2 because this chemical can easily pick up electrons from P3HT to get adsorbed as NO- 2 ions. They have obtained room temparature sensors that can detect NO2 in the 0 – 10 ppm range with very high selectivity. In contrast, the sensitivity of ZnO-doped P3HT to a reducing H2S is weakened because it is difficult to further reduce the P3HT.
6. Conclusion
As separate materials, polymers and ZnO are already considered to be important technologically. They have found several commercial applications in optoelectronics and sensors. Despite that, research activities involving these materials are still in full swing. For example, there is a lot of effort in developing high efficient polymeric solar cells and light emitting diodes. One of the big challenges in this area is long term stability. For ZnO, most of its expected applications, such as UV light emitters, spin functional devices, chemical sensors, surface acoustic wave devices and transparent conductors, are still in the laboratory level. This is mainly because ZnO is prone to material defects that it becomes very difficult to obtain reproducible device performance and reliability. Clearly, there is still a considerable work to be done with ZnO alone, but it is worthwhile to broaden its potential as a technological material. In this manuscript, a more unique role of ZnO, which is as a dopant to polymers, has been presented. This is an area of research, which is just beginning to be explored. Relevant publications are still limited but they report some intriguing observations that may have novel optoelectronic and sensor applications. The interaction of ZnO with polymers may provide ways of obtaining unique or enhanced optical and electronic properties in polymer nanocomposites. Thus, by doping polymers with ZnO, new applications may be realized without losing the benefits offered by polymers in terms of processing, scalability and mechanical flexibility.
References
- 1.
Albert K. Lewis N. Schauer C. Sotzing G. Stitzel S. Vaid T. Walt D. 2000 Cross-reactive chemical sensor arrays . ,100 7 (June 2000)2595 2626 ,1520-6890 - 2.
Aleshin A. Shcherbakov I. Alexandrova E. Lebedev E. 2008 Effect of electric field on the photoluminescence of polymer-inorganic nanoparticle composites.146 3-4 , (April 2008) 161- 165,0038-1098 - 3.
Aleshin A. Alexandrova E. Shcherbakov I. 2009 Hybrid active layers from a conjugated polymer and inorganic nanoparticles for organic light emitting devices with emission colour tuned by electric field . ,42 10 (May 2009) 105108,1361-6463 - 4.
Arshak K. Moore E. Lyons G. Harris F. Clifford S. 2004 A review of gas sensors employed in electronic nose applications . ,24 2 (April 2004)181 198 ,0260-2288 - 5.
Beek W. Wienk M. Janssen R. 2006 Hybrid solar cells from regioregular polythiophene and ZnO nanoparticles . ,16 8 (May 2006)1112 1116 ,1616-3028 - 6.
Bennett G. Greenbaum S. Owens F. 2009 NMR and Raman spectroscopic characterization of single walled carbon nanotube composites of polybutadiene .24 7 (July 2009)2215 2220 ,0884-2914 - 7.
Blom P. de Jong M. van Munster M. 1997 Electric-field and temperature dependence of the hole mobility in poly(p- phenylene vinylene).55 2 (January 1997) 656-659,1538-4489 - 8.
Brabec C. Shaheen S. Winder C. Sariciftci N. 2002 Effect of LiF/metal electrodes on the performance of plastic solar cells . ,80 7 (February 2002)1288 1290 ,1077-3118 - 9.
Cheng B. Shi W. Russell-Tanner J. Zhang L. Samulski E. 2006 Synthesis of variable-aspect-ratio, single-crystalline ZnO nanostructures. ,45 3 (January 2006)1208 14 ,0020-1669 - 10.
Chiang C. Druy M. Gau S. Heeger A. Louis E.. MacDiarmid A. Shirakawa H. 1978 Synthesis of highly conducting films of derivatives of polyacetylene, (CH)x.100 3 (February 1978) 1013- 1015,1520-5126 - 11.
Chirvase D. Parisi J. Hummelen J. Dyakonov V. 2004 Influence of nanomorphology on the photovoltaic action of polymer-fullerene composites . ,15 9 (August 2004)1317 1323 ,1361-6528 - 12.
Dijken A. Meulenkamp E. Vanmaekelbergh D. Meijerink A. 2000 The kinetics of the radiative and nonradiative processes in nanocrystalline ZnO particles upon photoexcitation . ,104 8 (February 2000)1715 1723 ,1520-6106 - 13.
Guadarrama A. Fernandez J. Iniguez M. Souto J. de Saja J. 2000 Array of conducting polymer sensors for the characterisation of wines .411 1-2 , (May 2000)193 200 ,0003-2670 - 14.
Huang M. Mao S. Feick H. Yan H. Wu Y. Kind H. Weber E. Russo R. Yang P. 2001 Room-temperature ultraviolet nanowire nanolasers . ,292 5523 (June 2001) 1897- 1899,1095-9203 - 15.
Kim J. Ingrosso C. Fakhfouri V. Striccoli M. Agostiano A. Curri M. Brugger J. 2009 Inkjet-printed multicolor arrays of highly luminescent nanocrystal-based nanocomposites . ,5 9 (February 2009)1051 1057 ,1613-6829 - 16.
Kim D. Yang J. Hong J. 2009 Ferromagnetism induced by Zn vacancy defect and lattice distortion in ZnO . ,106 1 (July 2009) 013908,1089-7550 - 17.
Koji N. Tomonori Y. Kenji I. Fumio S. 1999 Properties and structure of poly(vinyl alcohol)/silica composites.74 1 (October 1999) 133- 138,1097-4628 - 18.
Konenkamp R. Word R. Schlegel C. 2004 Vertical nanowire light emitting-diode. ,85 24 (December 2004) 6004- 6006,1077-3118 - 19.
Koster L. Mihailletchi V. Blom P. 2006 Ultimate efficiency of polymer/fullerene bulk heterojunction solar cells. ,88 9 (March 2006) 093511,1077-3118 - 20.
Li Z. Xiong Y. Xie Y. 2003 Selected-control synthesis of ZnO nanowires and nanorods via a PEG-assisted route. ,42 24 (October 2003)8105 9 ,0020-1669 - 21.
Liu B. Zeng C. 2004 Room temperature solution synthesis of monodispersed single-crystalline ZnO nanorods and derived hierarchical nanostructures.20 10 (April 2004) 4196- 4204,0743-7463 - 22.
Ma W. Yang C. Gong X. Lee K. Heeger A. 2005 Thermally stable, efficient polymer solar cells with nanoscale control of the interpenetrating network.15 10 (October 2005) 1617-1622,1616-3028 - 23.
Meulenkamp E. 1998 Synthesis and Growth of ZnO nanoparticles.102 29 (June 1998) 5566- 5572,1520-6106 - 24.
Morteani A. Ho P. Friend R. Silva C. 2005 Electric field-induced transition from heterojunction to bulk charge recombination in bilayer polymer light-emitting diodes . ,86 16 (May 2005) 163501,1077-3118 - 25.
Mukherjee A. Thakur A. Takashima W. Kaneto K. 2007 Minimization of contact resistance between metal and polymer by surface doping . ,40 6 (March 2007)1789 1793 ,1361-6463 - 26.
Musikhin S. Bakueva L. Sargent E. Shik A. 2002 Luminescent properties and electronic structure of conjugated polymer-dielectric nanocrystal composites . ,91 10 (May 2002)6679 6683 ,1089-7550 - 27.
Norton D. Heo Y. Ivill M. Ip K. Pearton S. Chisholm M. Steiner T. 2004 ZnO: growth, doping & processing .7 6 (June 2004)34 40 ,1369-7021 - 28.
Olson D. Shaheen S. Collins R. Ginley D. 2007 The effect of atmosphere and ZnO morphology on the performance of hybrid poly(3-hexylthiophene)/ZnO nanofiber photovoltaic devices.111 44 (October 2007) 16670- 16678,1932-7455 - 29.
Roy S. Basu S. 2002 Improved zinc oxide film for gas sensor applications .25 6 (November 2002)513 516 ,0250-4707 - 30.
Saxena V. Aswal D. Kaur M. Koiry S. Gupta S. Yakhmi J. Kshirsagar R. Deshpande S. 2007 Enhanced NO2 selectivity of hybrid poly(3-hexylthiophene): ZnO-nanowire thin films.90 No. 4, (February 2007) 043516,1077-3118 - 31.
Shalish I. Temkin H. Narayanamurti V. 2004 Size-dependent surface luminescence in ZnO nanowires . ,69 24 (June 2004) 245401,1538-4489 - 32.
Shan W. Walukiewicz W. Ager J. III. Yu K. Yuan H. Xin H. Cantwell G. Song J. 2005 Nature of room-temperature photoluminescence in ZnO . ,86 19 (May 2005) 191911,1077-3118 - 33.
Sharma A. Hotchkiss P. Marder S. Kippelen B. 2009 Tailoring the work function of indium tin oxide electrodes in electrophosphorescent organic light-emitting diodes . ,105 8 (April 2009) 084507,1089-7550 - 34.
Sui X. Shao C. Liu Y. 2005 White-light emission of polyvinyl alcohol/ZnO hybrid nanofibers prepared by electrospinning . ,87 11 (September 2005) 113115,1077-3118 - 35.
Sun D. Sue H-J. Miyatake N. 2008 Optical properties of ZnO quantum dots in epoxy with controlled dispersion . ,112 41 (September 2008)16002 16010 ,1932-7455 - 36.
Sze S. 2007 , John Wiley & Sons, Inc.978-0-471-14323-9 , Hoboken NJ USA - 37.
Ton-That C. Phillips M. Nguyen T-P. 2008 Blue shift in the luminescence spectra of MEH-PPV films containing ZnO nanoparticles . ,128 12 (July 2008)2031 2034 . - 38.
Ton-That C. Phillips M. Foley M. Moody S. Stampfl A. 2008 Surface electronic properties of ZnO nanoparticles . ,92 26 (July 2008) 261916,1077-3118 - 39.
Umeda J. Sakamoto W. Yogo T. 2009 Synthesis and field-responsive properties of SrTiO3 nanoparticle/polymer hybrid . ,24 7 (July 2009)2221 2228 ,0884-2914 - 40.
Wang Q. Pflugl C. Andress W. Ham D. Capasso F. 2008 Gigahertz surface acoustic wave generation on ZnO thin films deposited by radio frequency magnetron sputtering on III-V semiconductor substrates .26 6 (November 2008)1848 1851 ,1520-8567 - 41.
Winey K. Vaia R. 2007 Polymer nanocomposites . ,32 4 (April 2007)314 322 ,0883-7694 - 42.
Xu Z-X. Roy V. Stallinga P. Muccini M. Toffanin S. Xiang H-F. Che C-M. 2007 Nanocomposite field effect transistors based on zinc oxide/polymer blends . ,90 22 (June 2007) 223509,1077-3118 - 43.
Zhang T. Xu Z. Qian L. Tao D. Teng F. Xu X. 2006 Influence of ZnO nanorod on the luminescent and electrical properties of fluorescent dye-doped polymer nanocomposite . ,29 2 (November 2006)216 219 ,0925-3467