Open access peer-reviewed chapter

Actively Q-switched Thulium Lasers

By Jan K. Jabczynski, Lukasz Gorajek, Waldemar Zendzian, Jacek Kwiatkowski, Helena Jelinkova, Jan Sulc and Michal Nemec

Published: February 1st 2010

DOI: 10.5772/7948

Downloaded: 3678

1. Introduction

The near and mid infrared range of optical spectrum (1500 – 5000 nm) has attracted great attention over the last decades, mainly because of a numerous set of absorption / emission lines being “finger prints” of specific chemical and biological compounds (see e.g. (Sorokina & Vodopyanov, 2003)). One of the most reliable techniques for stand alone detection and identification of such agents is laser spectroscopy, for which the coherent, highly monochromatic, tuneable laser sources are required. Research on mid infrared laser sources destined for long range detection is one of the most active areas of solid state photonics nowadays (see e.g. (Godard, 2007) (Mirov et al., 2007) etc.) (Schellhorn, et al., 2007) (Eichhorn, 2008)). One of the necessary requirements for such application is high spatial coherence of laser output beam (parameter M2 near 1). Among the most perspective types of lasers operating in a mid infrared range (above 2.2 μm-wavelength) are quantum cascade lasers, Cr2+:AIIBVI lasers and optical parametric generators. For shorter wavelengths laser diodes and erbium (1600 – 1700 nm), thulium (1800 - 2000 nm), holmium (2050-2200 nm) solid state lasers realised in bulk/crystalline/ or fibre technology are available. The main properties differentiating such groups of lasers are peak power and pulse energy. It has to be pointed out, that for such a wavelength range, damage thresholds of optical elements are severely decreased, comparing to 1-μm wavelength, because of the presence of water vapour and OH groups, having a wide absorption peak just in this wavelength range. The physics of laser action in semiconductor lasers prohibits the high peak power and high energy operation. Moreover, the high CW power 1D or 2D laser diodes stacks characterise low spatial coherence and high beam volume, thus they can be used mainly as optical pumps for other lasers, e.g. holmium or erbium ones.

For short infrared range (< 2 μm wavelength) the Tm or Ho–doped fibre lasers sources operating in a CW regime seem to be the most perspective choice (Gapontsev et al., 2007) (McComb et al., 2009). The pulsed operation of fibre lasers, with energies of tens to hundreds of microJoules, can be realized applying Q-switching technique (Eichhorn & Jackson, 2008) (Eichhorn & Jackson, 2009) or gain-switched method. The best result of 2-μm Q-switched Tm:fibre lasers from the point of view of pulse energy (0.6 mJ for 10 Hz of rep. rate) were obtained (Barnes & De Young, 2009). Mid infrared fibre lasers suffer from lack of good quality active glasses and problems with high peak power / high energy operation for longer wavelengths. However the promising result namely 10 W at 2.78-μm-wavelength has been demonstrated recently in the ZBLAN fibre laser (Zhu & Jain, 2007).

Solid state lasers based on bulk crystalline gain media offer much higher peak powers and pulse energies compared to fibre ones. For the shortest wavelengths (1600-1700 nm) the best configuration is an erbium doped crystalline laser pumped by erbium fibre laser (Clarkson et al., 2006) or directly by laser diode (Setzler et al., 2005) (Kudryashov et al., 2009), (Eichhorn, 2008). For 1800-2000 nm wavelength range the thulium doped crystalline laser pumped by laser diodes seems to be the best option (Honea et al.,1997) (Budni et al., 2000), (Dergachev et al., 2002) (So et al, 2006), (Schellhorn, 2008), (Schellhorn et al., 2009). Intensive research has been devoted to thulium doped gain media (see e.g. (Huber et al.,1988) (Payne et al., 1992) (Lisiecki et al.,2006)) and methods of Q-switching. Passive Q-switching by means of holmium or chromium doped saturable absorbers as well as special types of quantum dots structures (Gaponenko et al., 2008) were examined, however simple, active Q-switching by means of acousto-optic modulators seems to be the better choice because of matured technology, very low insertion losses and relatively high damage thresholds.

The aim of this work was the theoretical analysis of such laser types and its experimental verification for one type of gain medium namely thulium doped yttrium, lithium fluoride (Tm:YLF).

2. Theoretical analysis of actively Q-switched thulium lasers

2.1. Model of quasi- three -level laser for CW pumping

Figure 1.

Scheme of energetic levels of Tm3+ gain medium.

The following analysis can be applied to any quasi-three-level laser for which the lower laser levels are partly occupied at room temperature (see e.g. (Beach, 1996) (Bourdet, 2000) (Bourdet, 2001) (Lim & Izawa, 2002)). Typical configuration of Tm3+ lasers levels (see Figure 1) consists of at least three manifolds : 3H6 - pumping and laser lower levels manifold, 3H4 – pumping, upper levels manifold and 3F4 - laser upper level manifold. The pumping process between 3H6 3H4. corresponds to wavelength ~ 790 nm which is avaiable for typical AlGaAs laser diodes. Excitation of upper laser levels 3F4 is a result of an efficent cross-relaxation process 3H4 + 3H6 2 x 3F4. In the following analysis we assumed, that this two-stage pumping process is characterised by the quantum efficiency equal to 2. Further, we will consider only relaxation/excitation processes (typical for quasi-III-level lasers) between two manifolds 3H6 - lower pump/laser manifold and 3F4 - upper pump/laser manifold. The analysis given in this paper will be followed by the model developed by (Bourdet, 2000).

Primarily, let us define processes of pumping between lower pumping level of number Np,lower – and the upper pumping level of number Np,upper (Np,lower Np,upper). Similarly, the laser transition has to be defined between the pair of levels Nl,upper and Nl,lower (Nl,upper Nl,lower). It was assumed, that it is valid plane wave approximation and both pump and laser beams have the same radius W and area Am=Ap=πW2/2. For such assumptions the analytical formulae describing the quasi-three-level laser can be derived (see details (Bourdet, 2000)).

Figure 2.

Scheme of pumping and laser action in the Bourdet’s model.

The final expression for relative laser output intensity I las in dependence on incident relative pump intensity I p and cavity and gain medium parameters is the following:


where: L – rod length, R m,l, R OC - rear and output mirror reflectivity at laser wavelength, R m,p - rod reflectivity at pump wavelength. The function Γ (corresponding to the transmission of pump beam for laser action) is given by:




N 0 – concentration of active ions, σp, σl – absorption/emission cross sections at pump/emission wavelengths, respectively, f N – Boltzmann‘s occupation factor of N–th level. To calculate the final output laser power P out and the incident pump power P p the relative intensities I las, I p have to be multiplied by the mode/pump area Am =Ap =A=πW2/2 and emission/ absorption saturation densities I sat,l, I sat,p as follows:




τu- life time of upper laser level, νp=c/λp, νl=c/λl – pump / laser frequencies, λp, λl- pump laser wavelengths, c- light speed, h –Planck constant.

Let us summarise the main properties of the quasi-three-level laser:

strong dependence on temperature via Boltzmann’s occupation factors f N occuring in all formulae

occurrence of additional, reabsorption losses per roundtrip defined by:


minimal pump power required for achieving gain medium transparency:


Moreover, in contrast to the typical case of a four-level laser, the absorption efficiency is different in laser and non-laser conditions. As a result of laser transition the occupations of upper and lower laser level are “clamped“ to those at threshold and are dependent only on coupling conditions, losses etc.

For the case of laser action (above threshold) the absorption efficiency is given by:


As a rule, η abs,las is higher compared to non-laser conditions and does not depend on pump power.

In the case of non-lasing conditions the main effect of the diminishing of absorption efficiency consists in saturated absorption. Therefore, the absorption efficiency can be defined in two alternative ways:


where LambertW(z) denotes LambertW function (see e.g. (Barry et al, 2000), (Grace, et al, 2001), (Jabczyński et al, 2003)) defined as follows:


Figure 3.

Absorption efficiency vs. relative pump power; non lasing – continuous curve, lasing R oc=0.5 dotted curve, lasing R oc=0.01 – dash-dot curve.

An alternative way to determine absorption efficiency in non-laser conditions is to find a numerical solution for the pump transmission function Γ of the following equation:


and substituting the obtained value of Γ to formula (8). The results of absorption efficiency calculation for non-laser and laser conditions are shown in Figure 5.

Below threshold absorption efficiency decreases with pump intensity. In a laser condition above threshold, absorption efficiency does not depend on pump power and it can even jump to higher values depending on output coupler reflectivity as was shown in Figure 5. In our case of an actively Q-switched laser the non-lasing condition has to be assumed during the pumping process.

2.1.1 Optimisation of laser parameters

Analysing the formula (1), it is quite easy to find the condition for the optimum length of gain medium. Please note, that the small signal gain (assuming R m,p = 0) can be defined as follows:


Thus, assuming constant I p, R oc, R m,p, N o and temperature, after differentiating (12) with respect to L, the final formula on optimal crystal length can be found:


The example of calculation of optimal crystal length dependent on pump intensity is shown in Figure 6.

Figure 4.

Optimal crystal length vs. relative pump intensity for different output coupler reflectivities R oc, R m,l=0.99.

Please note, that output power for a given pump intensity depends also on output coupler reflectivity and cavity losses. The typical characteristics of output power intensity vs. pump power intensity are shown in Figure 7.

As was shown in Figure 6, 7, to obtain the higher output power with increased pump power density the gain medium length and out-coupling losses have to be increased. Please note that threshold pump power is also the function of gain medium length via reabsorption losses.

In the process of optimisation of quasi-three-level laser parameters, the starting point is the available pump power. We have to find the best combination of pump area, output coupler transmission, gain medium length to obtain the maximum output power. Further, the cavity design (curvature of mirrors, distances) should satisfy the best mode matching condition i.e. the fundamental laser mode area has to be comparable to the pump area to minimize the aperture/absorption losses occurring in an un-pumped region. The above presented formulae can give only preliminary indications, all these rules have to be verified experimentally.

It should be noted, that with increase in pump power density, the temperature of the rod increases, causing an increase in reabsorption losses and additional cavity losses as a result of stress induced aberrations. Thus, it is a trade of between requirements for efficient pumping and thermal limitations of a quasi-three-level laser. In practice, output power of such a laser is limited by thermo-optic effects and thermal fracture (see e.g. (So et al, 2006)), so the proper choice of pump geometry, size and dopant level of gain medium is fundamental to mitigate these effects.

Figure 5.

Output intensity vs. pump intensity.

2.2. The thermo-optic limitations of thulium lasers

For lasers operating in a free running regime the maximum pump power with respect to fracture limit is determined by the doping level and mechanical toughness of the crystal (see e.g. (Koechner, 1996), (Chen, 1999), (So et al, 2006)). Much below fracture limit the operating parameters of any type of diode pumped lasers are governed by the temperature increase inside the gain medium. The temperature profile induced by absorption of a focused pumping beam inside the gain medium of a quasi-three-level laser manifests by means the following effects:

changes in absorption efficiency and available net inversion,

reabsorption losses due to temperature dependent occupations of lower laser level,

paraxial thermal lensing,

higher order thermal aberration,

stress induced birefringence and depolarisation losses

thermal fracture for higher heat loads.

According to the model derived for end pumped lasers (Chen, 1999) the maximum absorbed pump power is given by:


where:η h – heat conversion efficiency, αabs – absorption coefficient, R T – thermal shock parameter defined, as follows:


where : σmax,fracture – fracture limit stress, E – Young’s modulus, K c- thermal conductivity, αT – linear thermal expansion coefficient.

Assuming top-hat distribution of the pump beam, maximum temperature increase on the z- distance on the axis of the laser rod is given by (Chen, 1999):


where : a – rod radius, Wp,0 – radius of pump beam in the waist, zw – waist distance to the rod facet, zp – Rayleigh range of pump beam, P abs- absorbed pump power. To obtain average temperature in the rod, ΔTmax(z) has to be integrated along the rod.

Maximal thermally induced stress inside the rod occurs on rod facet (z=0). Assuming a linear thermal elasticity model, the maximum stress can be estimated by the following formulae:


For top-hat heat source distribution inside the cylindrical rod we have a parabolic profile of temperature resulting in optical path difference of a parabolic shape. In the framework of a paraxial thermal lensing model, the thermo-optic optical power induced inside the rod is given by:

Absoprtion peak wavelength [nm]785795792801
absorption coeff . α abs [ cm -1] @1%Tm1.050.9 /0.80. 367
Refractive index n1.811.92 9/1.9431.4 7 /1.4 4 81.98/2.16
Temperature dispersion dn/d dT[10-6/K]7.39.7-4.4/-28.5/3.9
thermal expansion coefficient α T [10 -6 /K ]7.510.813.34.4/11.4
thermal conductivity K c [W/m/K]13117.211
Young modu l us E [GPa]3102208577
fracture stress σ max,fracture [kG/mm 2]161 644
Thermal shock parameter R T [W/cm]
βr [mm 2 /W/m]1.171.960.471.71
fr [mm] @ I h =1 W/mm 285.450.8212.858.5

Table 1.

Mechanical and optical parameters of 4 typical Tm doped gain media.

Figure 6.

Maximal stress vs. absorbed pump power for 4 Tm crystals; Wp,0=0.5mm.

Figure 7.

Thermo-optic power vs. absorbed pump power for 4 Tm crystals; Wp,0=0.5mm.


where: β T – thermal lensing parameter, I h – heat power density defined as follows:


where: ν- Poisson‘s ration, Ap – averaged pump area, n – refractive index, dn/dΤ − temperature dispersion of refractive index.

To help in the choice of a proper gain medium for the thulium laser, the mechanical and optical parameters of four Tm-doped media were collected in Table 1.

We have calculated the maximum stress and thermo-optical power vs. absorbed pump power for these 4 gain media (see Figure 8, 9 respectively).

2.3. Model of actively Q-switched Tm laser

2.3.1. Degnan’s analytical model

To analyse the regime of active, periodic Q-switching we can modify the classical models of Q-switching (see e.g. (Degnan, 1989), (Koechner, 1996), (Eichhorn, 2008)). The model of rate equations for a quasi-three-level laser is defined by two functions: Φ – relative intensity of the laser field, and X - modified relative occupation (further called inversion) of the upper laser level:

X = XuflE20

where f l –relative occupation of the lower laser level defined by the formula (3).

The set of rate equations consist of two first order differential equations with respect to relative time τ= ct/2L cav as follows:


where: L cav – length of cavity, τrel,u =cτu/2L cav – relative upper level lifetime, I p – relative pump density,


η abs- absorption efficiency, ρon,off – losses of active Q-switch, different in pumping and pulsing intervals,


The pumping process is periodic with a repetition rate of frep =1/trep. In pumping time ton ≈ trep, losses of q-switch ρqsw,high have to be sufficiently high to prevent laser oscillation. In a short interval of duration toff<< ton, trep the cavity losses are small and the pulse starts to build up.

For the steady state (after a few initial pulses) the initial inversion Xi before the pulse and final inversion Xf tend to values defined only by pump density, cavity parameters and the repetition period.

We can define threshold inversion for low losses of Q-switch as follows:


To obtain effective Q-switching, pump intensity and duration should be sufficiently high to achieve initial inversion Xin a much higher value than Xthr :


In pumping time the laser intensity disappears (Φ = 0) and the second equation can be solved analytically, assuming, that absorption efficiency does not change during pumping and other non-linear processes (up-conversion, amplified spontaneous emission) can be neglected. The formula for inversion is the following:


where: X– inversion achieved for time τ >>τrel,u defined as follows:


X(0) = Xf – inversion at the starting point of pumping corresponding to the final inversion after pulse generation. The examples of temporal dependence of inversion for different repetition rates are shown in Figure 10.

Figure 8.

Changes in inversion vs. time for different repetition periods.

During the pulse build up interval the pumping and relaxation components can be neglected in a second rate equation. Thus, we can find the analytical solution of rate equations in the form of a transcendent equation on initial and final inversions Xi, Xf:


Using (27), initial inversion can be written as:


To determine the initial inversion including the cross-relaxation and up-conversion processes the more complicated model of a quasi-three-level laser (Rustad & Stenersen, 1996) can be used.

The pulse duration, pulse energy, and peak power can be determined knowing the initial and final inversions. The conditions of optimisation of an actively Q-switched laser were found (Degnan, 1989). Let us introduce the un-dimensional parameter z defined as follows:


The optimal reflectivity R OC,opt of the output coupler can be determined as follows:


where ρpas – passive cavity losses defined as follows:


Let us notice, that R OC,opt depends on the pump density and repetition period.

For optimal out-coupling losses the formulae on pulse duration t pulse, extraction efficiency η extr and output energy E out are the following:




Such an elegant, simple analytical model can give mainly qualitative information about the properties of the Q-switched laser. It should be underlined the role of parameter z equal to the ratio of small signal gain to passive losses. The quality of laser output is proportional to parameter z which could be determined for any type of laser (including high repetition rate Q-switched fibre lasers as well). The short pulses and high peak powers, evidencing effective Q-switching, occur for z > 10.

However, comparing Degnan’s analytical model with experiments, quite large differences can be found especially for high pumping rate and long repetition periods. It should be noted, that in this model all non-linear processes are neglected, whose role is growing with increase in inversion. Moreover, with an increase in heat load the several temperature dependent processes (thermally induced aberration, stress, lowering of gain etc.) significantly diminish the performance of the laser.

2.3.2. Numerical modelling of an actively Q-switched Tm:YLF laser.

Comparing results of theoretical analysis with experiments on the Q-switched Tm:YLF laser, it was found, that it is necessary to improve the model adding the thermo-optic and cavity effects. Therefore, we have developed a numerical model (Gorajek, et al, 2009) introducing additional losses γ add (T) occurring as a result of the absorption of laser mode wings on unpumped regions of a quasi-three-level medium. In the particular case of our oscillator, the laser scheme for “cold” cavity is nearly half confocal (g 1=1, g 2 = 0.5) for vanished thermal lensing). With increase in negative thermal lensing (typical for Tm:YLF crystal) the mode size at the crystal increases until reaching the stability limit of the cavity (g 1 ~ 2, g 2 =0.5). However, also, even out of stability range, the spatially limited mode is formed due to diffraction on the gain diaphragm induced by the pumping beam, which could be treated as a kind of “imaginary” lens (Grace, et al, 2001) (Jabczyński et al, 2003). Such a laser mode has a “gaussian” like profile and much higher diffraction losses which depend (via temperature increase) on average pump power. To determine the maximal, average temperature in rod and thermal lensing power the analytical formulae (16), (18), (19) were applied. For calculation of the additional losses γ add (Τ) the numerical procedure proposed in (Jabczyński et al, 2003) was used. The results of the calculation of average temperature and pump dependent losses for two cases: quasi-CW pumping (duty factor 10% ) and CW pumping are shown in Figure 11

Figure 9.

Average temperature inside rod, pump dependent losses vs. pump rate: CW pumping.

The numerical procedure prepared for analysis of giant pulse formation was divided into two stages. In the first one, before switching off the high Q-switch losses, the internal flux vanishes and only the second equation is numerically solved. Moreover additional non-linear effects causing a drop in inversion can be added. After switching off the Q-switch, the threshold condition is tested and the set of both equations is solved for the giant pulse evolution calculation.

The main difference in analysis of Q-switching in a quasi-three level laser (compared to the four level scheme) consists on the effect of temperature on the available parameters of the giant pulse. Because of the increase in temperature with pump power, the inversion and additional losses significantly influence on the available peak power and pulse duration (see Figure 12-13).

Figure 10.

Average output power, peak power vs. pump rate: CW pumping.

Figure 11.

Pulse duration vs. pump rate; CW pumping continuous curve, pumping duty cycle 10%– dashed curve.

The all above presented effects give the result, that giant pulse is generated for a considerable level of losses dependent on effective average heat power dissipated in the gain medium. Such effects were observed in experiments (see p.3.3 and p.3.4) and we have shown in Figure 11-13 the results of simulation qualitatively explaining the experiment.

3. Experiments

3.1. Laser head scheme

We have designed the laser head of a diode pumped Tm:YLF laser shown in Figure 14 destined for tuneable and Q-switched operation (Jabczyński, et al., 2007) (Jabczyński, et al., 2009). The fibre coupled diode of 30-W output power emitting at a 0.792 μm wavelength was deployed as a pump source.

Figure 12.

Optical scheme of a Tm:YLF laser: FCB- fiber coupled laser diode of 30 W, RM- rear flat mirror, OC- output coupler, Tm:YLF- gain crystal, AOM- acousto-optic Q-switch.

The pump beam after passing through a reimaging optic (of 1.5 x magnification) forms inside the gain medium the caustics of waist diameter approximately 0.6 mm and induces a near 60 K increase in temperature for the maximum incident pump power of 26 W.

The uncoated, with 3.5%. doping of thulium YLF rods of 8 and 10 mm size wrapped with indium foil were tested as gain media. The crystals were mounted in a copper heat-sink maintaining 293 K temperature of coolant. The diode wavelength was tuned via the control of thermo-electric cooler voltage to maximise the absorbed pump power, however not higher than 65% absorption efficiency for an 8-mm long rod and 80% for a 10-mm crystal were obtained in the best cases of CW pumping without lasing (see Figure 15).

3.2. Free running and tunablity characterisation

As the output couplers we have used mirrors of a 0.3 and 0.5 m radii of curvature and 10%, 15%, 20% and 30% transmission at a 1.9-μm wavelength. The energetic characteristics in quasi-CW pumping in dependence on absorbed pump power were presented in Figure 16.

Above 7-W power with nearly 30% slope efficiency with respect to incident pump power were demonstrated for the best case of quasi-CW pumping for a short, 70-mm resonator. Nearly 5 W were obtained for CW pumping in a short cavity and above 3 W for an elongated 220-mm cavity.

Figure 13.

Absorption efficiency in non-lasing conditions vs. incident pump density for two Tm:YLF rods.

Figure 14.

Output power vs. pump power for quasi-CW pumping (10% duty cycle, 10Hz, 10ms pump duration).

The spectrum of generation was centred at 1908 nm with FWHM of approximately 6 nm (see Figure 17) for the oscillator without deploying Lyot’s filter. In the next step of experiments the cavity was elongated to 220 mm to deploy the Lyot’s filter (consisting of 2 quartz plates of 0.92 and 1.84 mm thickness, respectively) and an active Q-switch.

Figure 15.

Spectra of spontaneous emission and free-running of a Tm:YLF laser with 10%- transmission of OC.

Figure 16.

Spectra of spontaneous emission and tuning of Tm:YLF laser by means of Lyot’s filter.

The experiments of tuning were carried out firstly in a free-running regime. The tuning range of 1845-1935 nm was demonstrated for 37o – 47o angle of rotation with respect to the fast axis of quartz plates (see Figure 18). The linewidth was less than 1 nm. For the Q-switching regime the contrast of a deployed birefringent filter was too low to prevent oscillation on the strongest 1908-nm line. In the last part of characterisation in a free-running regime, we have measured the beam profiles in far field in the focal plane of a 500-focal length lens. The divergence angle was about 4.3 mrad and an estimated parameter M2< 1.3 for high 20-W incident pump power.

3.3. Q-switching experiments for low duty cycle pumping

For Q-switching we have used a water cooled acousto-optic modulator made of 45-mm long fused silica, operating at a radio frequency of 40.7 MHz with a maximum power of 25 W. In fact, that was the largest element of laser head which determined its size. It was shown in separate experiments that for maximum RF power of the acousto-optic modulator the diffraction efficiency was higher than 80%, diffraction angle was about 7 mrad and the falling edge, i.e. switch off time was about 100 ns.

In the first part of the Q-switching experiments we have estimated the maximum available output energy in free-running for which the acousto-optic modulator can hold off oscillations for a switch on state of RF power. It should be noted that we have used a 220-mm long cavity with Lyot’s filter inside introducing additional insertion losses. The laser output was horizontally polarized (perpendicularly to the c-axis of YLF crystal).

Figure 17.

Available output energy vs. incident pump energy in free running for the state of effective operation of the active Q-switch

As was shown in Figure 19, for the best case the output energy of 40 mJ (for incident pump energy of 400 mJ) was the upper limit of efficient operation of the Q-switch. However, the real limit of output energy was far lower, because of the damage threshold of the Tm:YLF crystal facet. It was shown, that the output energy above 10 mJ corresponding approximately to 1.5 – 2 GW/cm2 of intracavity power density constitutes the upper limit of available pulse energy for the safe operation in a Q-switching regime in the case of our laser head. Thus, we can conclude that a much smaller Q-switch without water cooling will be satisfactory for our purposes.

The results of measurements of pulse duration and peak power for a low duty cycle of 10% (10 Hz of PRF and 10 ms pump duration) were shown in Figure 20. The shortest pulse of 22-ns duration (see Figure 21) and 10.5 mJ energy corresponding to 0.45 MW of peak power were demonstrated for the best case of stable output below the risk of damages to laser elements.

Figure 18.

Pulse duration, peak power vs. pump energy for Q-switching in a low 10% duty cycle pumping regime.

Figure 19.

Oscillogram of the giant pulse of 10.5 mJ of energy.

3.4. Q-switching experiments for CW pumping

For the CW pumping regime the maximum pump power was constituted due to the thermal lensing limit. Because of negative thermal dispersion of Tm:YLF the cavity achieves stability limit for nearly 20-W of incident pump power.

The results of the Q-switching experiments were shown in Figure 22, 23, and collected in Table 2. Nearly 20% slope efficiency with respect to absorbed pump energy was obtained for high repetition frequency. The experimental results were in agreement with the numerical model presented in p. 2.3.2

Figure 20.

Output energy vs. absorbed pump energy for different repetition periods.

f rep [Hz]d.f.P avg [W]E p [mJ]? p [ns]P p [kW]

Table 2.

Results of Q-switching experiments; frep – pulse repetition frequency, d.f. – duty cycle factor, Pavg – average output power, Ep – pulse energy, τp – pulse duration, Pp – peak power.

The comparable pulse energies of 10 mJ (last two rows of Table 2) were achieved for both cases of pumping. The much longer pulse duration for a case of CW pumping was caused by the combined effect of an increase in reabsorption and additional diffraction loss (see p. 2.3.2). Please note, that maximum available pulse energy was limited in both cases by reaching the damage thresholds of the rod facet or rear mirror.

Figure 21.

Output peak power vs. absorbed pump power for different repetition periods.

4. Conclusions

The analytical models of quasi-three-level lasers operating in free running and Q-switching regimes were presented. In both cases appropriate formulae enabling the optimization of such lasers were given and analysed. The numerical model of a quasi-three-level laser operating in a Q-switching regime including additional pump dependent losses, was elaborated to explain the properties of the developed actively Q-switched laser. The main difference in analysis of Q-switching in a quasi-three-level laser (compared to a four-level laser) consists of the effect of temperature on giant pulse parameters. Because of increase in temperature with pump power, the net inversion, additional reabsorption and diffraction losses significantly influence available pulse energy, peak power and pulse duration. The all above mentioned effects result in the fact, that giant pulse is generated for a considerable level of losses dependent on effective average heat power dissipated in the gain medium. The results of numerical modelling were confirmed in the experiments.

To compare models with experiments we have presented the results of investigations of an efficient Tm:YLF laser end-pumped by 30-W fiber coupled laser diode bar. The incident pump density exceeded above 5 times the saturation pump density, thus the drawbacks of the quasi-three-level scheme have been mitigated. We have obtained the best output characteristics (slope and maximum power) for out-coupling losses of 20% evidencing the high roundtrip gain for maximum pump power. Above 7-W of output power for incident 26-W pump power in free running regime was achieved in the best case for a short 70-mm cavity. Above 3 W of output power was demonstrated for CW pumping for an elongated 220-mm cavity. The divergence angle was about 4.3 mrad and estimated parameter M2< 1.3. To improve the output characteristics in a free running regime, the optimisation of pump size in the gain medium, application of a longer rod and optimised cavity design should be applied.

For the free-running and Q-switching regimes the output spectrum was centred at 1908-nm with linewidth less than 6 nm. For tuning the Lyot’s filter consisting of 2 quartz plates was deployed. The tuning range of 1845-1935 nm with less than 1-nm linewidth was demonstrated for the free-running regime. For the Q-switching regime the contrast of a deployed birefringent filter was too low to prevent oscillation on the strongest 1908-nm linewidth.

In the experiments on active Q-switching by means of an acousto-optic modulator, up to 10-mJ output energy was demonstrated. Output energy was limited by damage of the laser elements. Nearly 0.5 MW peak power with pulse durations of 22 ns was achieved for a 10-Hz repetition rate with 10% duty cycle of the pumping regime. The 1.7-W of average power with 12 kW peak power and 1000 Hz repetition rate was demonstrated for the CW pumping regime. The developed laser could constitute the basis for development of the tunable, Q-switched laser source operating at a 2-μm wavelength. Moreover, it could be used as a pump source for Ho:YAG and Cr:ZnSe lasers operating in a gain switching regime for the longer ( > 2 μm) wavelengths.


This work was supported by the Polish Ministry of Science and Higher Education under projects 0T00A00330, NN515 423033, NN515 414834, NN515 345036.

© 2010 The Author(s). Licensee IntechOpen. This chapter is distributed under the terms of the Creative Commons Attribution-NonCommercial-ShareAlike-3.0 License, which permits use, distribution and reproduction for non-commercial purposes, provided the original is properly cited and derivative works building on this content are distributed under the same license.

How to cite and reference

Link to this chapter Copy to clipboard

Cite this chapter Copy to clipboard

Jan K. Jabczynski, Lukasz Gorajek, Waldemar Zendzian, Jacek Kwiatkowski, Helena Jelinkova, Jan Sulc and Michal Nemec (February 1st 2010). Actively Q-switched Thulium Lasers, Advances in Solid State Lasers Development and Applications, Mikhail Grishin, IntechOpen, DOI: 10.5772/7948. Available from:

chapter statistics

3678total chapter downloads

More statistics for editors and authors

Login to your personal dashboard for more detailed statistics on your publications.

Access personal reporting

Related Content

This Book

Next chapter

Efficient Intracavity Beam Combining of Multiple Lasers in a Composite Cavity

By Ming Lei

Related Book

First chapter

Gaseous Scanning Electron Microscope (GSEM): Applications and Improvement

By Lahcen Khouchaf

We are IntechOpen, the world's leading publisher of Open Access books. Built by scientists, for scientists. Our readership spans scientists, professors, researchers, librarians, and students, as well as business professionals. We share our knowledge and peer-reveiwed research papers with libraries, scientific and engineering societies, and also work with corporate R&D departments and government entities.

More About Us