1. Introduction
More and more in recent years, investigators in industry and academia are taming the structural and electronic properties of conjugated polymer-based nanowires (NWs) and nanotubes (NTs) that display an impressive applicative potential from bio-environmental sensing and energy harvesting to ultra-low power electronic devices and high density memories. Today, the methods used to synthesize conjugated polymer (CP) NWs span from scanning probe lithography [Lim & Mirkin (2002)] and mechanical stretching [He et al. (2001)] to electrospinning [Reneker (2000)] and templated electrochemical [Jerôme & Jerôme (1998), Martin (1994, 1996)] and wetting procedures [Massuyeau (2009)].
Intriguingly, while CPs present vast technological opportunities and can be easily combined to inorganic materials, hybrid metal-CP NWs have been scarcely studied [Gence (2007); Hernandez (2004), Park (2004)]. They can be advantageously produced by high-throughput template strategies that offer a very good control over the composition and spatial distribution of the different NW segments [Duvail (2008), Liang (2002)]. Nevertheless, the use of single hybrid metal-CP NWs in real applications asks for properly identifying their intrinsic behavior. First, this exigency stems from the obvious requirement of tuning their specific properties in post-synthesis and post-assembly technological steps [Jang (2006), Tran et al. (2009), Yoon et al. (2007)]. Second, the unique opto-electronic properties of single hybrid metal-CP NWs are expected to be closely linked to their intricate architecture and to emerge more exquisitely than those of pure CP NWs [Aleshin (2004), Cao (2008), Duvail (2007)].
The aim of this chapter is not to give a complete overview of the literature addressing CP NWs; the focus is on state-of-the-art techniques for synthesizing, characterizing and integrating hybrid metal-CP NWs. We first present the fabrication of well-shaped and mechanically robust hybrid metal-CP NWs and in the next section we describe the morphology and the microstructure of the resulting NWs. Several advanced techniques such as Raman spectroscopy and electron spin resonance, that enhance our ability to harness promising properties of CP-based NWs, are also presented and discussed. The following section includes research efforts to decrypt electronic properties of CP-based NWs and hybrid metal-CP NWs. Methods for contacting single NWs are reviewed and critically compared. The subsequent section introduces microdevices specially designed for the correlated characterization of single CP-based NWs. The last section refers to the integration and the potential applications of CP-based NWs.
2. Fabrication by the template method
We first address the major issues for preparing well-shaped and mechanically robust hybrid metal-CP NWs and elaborate on a highly reproducible route based upon an all-electrochemical template-based strategy [Reynes & Demoustier-Champagne (2005)].
2.1 Template synthesis
The synthesis of NWs can be achieved by several techniques that can be regrouped into two main families, depending if there are based or not on the use of a template. The template-free method is relatively simple and inexpensive but its control over the morphology and diameter of the NWs is poor compared to the template method [Nalwa (2006), Wan (2008)]. The template method is very efficient for achieving a controlled growth of NWs: the shape, size and orientation of the produced structures are precisely defined by the template [Duvail (2008)]. It allows the synthesis of complex multi-segmented NWs, core-multishell, and coaxial NW structures [Hurst (2006), Kovtyukhova (2004), Lorcy (2009)]. The most used templates are membranes made of ion track-etched polycarbonate (PC) and porous anodic aluminium oxide (AAO); yet, other materials such as Si or polymethylmethacrylate (PMMA) can be used as templates. Typical PC templates [available, for example, at www.it4ip.be] have a mean pore diameter ranging from 30 to 200 nm, pore densities ranging from 108 to 109 pores.cm−2 and thicknesses around 20
Among the large variety of CPs, three representative species have been included in this chapter: poly[3,4-ethylene-dioxythiophene] (PEDOT), polypyrrole (PPy), and polyaniline (PANI). These CPs are by far the most extensively studied as they exhibit remarkable properties such as environmental stability, interesting redox behavior and the ability to exhibit high electrical conductivities [Sadki (2000)]. While the polymerization of these CPs can be performed by both chemical and electrochemical reactions, the electrochemical polymerization is well adapted for the synthesis within templates. Furthermore, multi-segmented NWs [e.g. combining CP segments with noble (Au, Pt) or transition (Ni, Co metal blocks] can be easily produced using an all-electrochemical process, just by changing the plating solution and adapting the parameters of the deposition of each segment [Callegari (2009), Chung (2005)].
A crucial point of the electrochemical synthesis of the CPs within a template is that, depending on the synthesis parameters, NWs or NTs can be obtained [Cho & Lee (2008),
Xiao (2007)][see Fig. 1(b)]. While CP NTs could be interesting for different applications such as energy storage or drug release, NWs are needed for obtaining hybrid multi-segmented NWs with good metal-CP electrical interfaces. As revealed in the sequel, the determination of the exact geometry of metal-CP interfaces requires correlated scanning electron microscopy (SEM) and transmission electron microscopy (TEM) investigations.
The mechanism behind the two possible geometrical configurations is still matter of debate. For explaining the growth of nanotubes inside a template, it has been proposed by Martin and coworkers [Martin (1994, 1996)] that solvophobic and electrostatic interactions between CPs and the template occur within the pores of the template, favouring thus the tubular geometry [see Fig. 1(b)]. A recent study [Xiao (2007)] has shown that the morphological transition between the two configurations can be explained by a mechanism based on monomer diffusion and reaction kinetics. Roughly, as exemplified in Fig. 1(c)., a slow polymerization reaction performed in presence of a sufficient monomer supply leads to the formation of NWs, while a faster reaction associated to an insufficient supply of monomer produces preferentially produces NTs.
2.2. Pure PEDOT and hybrid tri-segmented Au-PPy-Au NWs
Here, we briefly present the synthesis of pure PEDOT NWs and detail the fabrication of hybrid metal-CP NWs, taking the case of a tri-segmented Au-PPy-Au NW. Specifically, the 3,4-ethylenedioxythiophene (EDOT) monomer was provided by Bayer AG and used as received. The polymerization bath was an aqueous solution, previously developed by Sakmeche and coworkers [Sakmeche (1996)], containing 0.07
A schematic view of tri-segmented NW synthesized by an all-electrochemical method is given in the Fig. 2.(a). The synthesis is performed by three sequential electrodepositions. The first step consists in the electrodeposition of a gold segment by cyclic voltammetry (CV). A cyanide free solution containing 0.1
Remarkably, the resulting metal-PPy-metal NWs are characterized by two morphologically different metal-PPy interfaces as revealed by TEM observations and schematized in the insets of the Fig. 2.(a).The metal-onto-PPy interface is mechanically more robust than the PPy-onto-metal interface thanks to a higher adhesion surface. Several strategies have been envisaged to improve the mechanical strength of these interfaces. First, we optimized electrochemical parameters for the growth of the Au-onto-PPy interface by systematically investigating the effects of the potential sweep rate and the monomer concentration on its mechanical strength [Gence (2007)]. Concerning the bottom PPy-onto-Au interface, as its morphology cannot be modified just by playing on electrodeposition parameters, its mechanical strength could be enhanced by increasing the adhesion between the two different materials. Among the different possible strategies, we first investigated the use of self-assembled alkylthiol monolayers (SAMs) onto gold [Lahav (2006)]. We used 11-mercaptoundecanoic and 3-mercaptopropionic acids. The SAM is inserted between the gold and the PPy segment to create an electrostatic bond between the negatively charged carboxylate groups of the chemisorbed monolayer and the positively charged growing polycation as shown in the Fig. 3.(a).On top of the 11-mercaptoundecanoic acid SAM no CP growth has been observed. This is probably due to the presence of long aliphatic chains that passivated the Au segments. Unfortunately, even if the CP growth occurred on the thinner chemisorbed SAM (3-mercaptopropionic acid), no qualitative improvement of the mechanical strength has been detected upon this chemical modification of the interface. Nevertheless, the modification of interfaces by the use of SAMs is essential for the synthesis of hybrid transition metal-CP NWs.
2.3. Hybrid NWs with transition metals
The synthesis of bi- and tri-segmented NWs including transition metals is now described. Bi-segmented, transition metal-onto-CP NWs can be easily elaborated by changing the electrochemical bath. While reducing the metal ions on top of the CP segment, the CP cannot be dissolved. Yet, it can be reduced, thus exhibiting a lower doped level state. The reverse sequence, i.e. the electropolymerization of usual CPs on transition metals, including Ni and Co, is less straightforward to achieve. Indeed, the oxidation potentials of these metals are much lower than the one of conjugated monomers and thus, dissolution of the metal occurs before electropolymerization begins. Figure 3.(c)gives typical chronoamperograms for the electrodeposition of Co and Ni segments. The length of the
transition metal segments can be easily controlled by the electrodeposition time: the growth rates for Ni and Co, observed for 110 nm diameter NWs, are 0.5 and 0.7
Towards preparing hybrid transition metal-CP NWs, a major problem to overcome is to suppress or limit the metal re-dissolution at the oxidative potential required for the electrodeposition of the CP. It is therefore necessary to find synthesis conditions that will strongly passivate the metal without impeding electropolymerization. Our approach consists in the use of a SAM. The 3-(Pyrrol-1-yl) propanoic acid has been chosen due to its facile synthesis and because it contains two end-functional groups, a carboxylate group at one extremity and a pyrrole group at the other end, that can specifically interact with the Ni substrate and the growing CP, respectively [see Fig. 3.(b)]. Prior to the electrodeposition of the CP, the SAM is deposited by immersion of the PC template containing the Ni segment in a 3-(Pyrrol-1-yl) propanoic acid solution for more than 18 hours. The CP segment (PPy or PEDOT) could be then synthesized by CV using standard electrodeposition parameters. Typical cyclic voltammograms recorded during the deposition of the second, (PPy or PEDOT) segments on top of the first grown Ni segments modified by SAMs are given in Fig. 3.(d).In order to fabricate tri-segmented nanowires, a third metallic block can be synthesized on top of the CP segment, by CV (e.g. Au) or by chronoamperommetry (e.g. Co). Following this procedure, 100-nmdiameter Ni-(PPy or PEDOT)-Au and Ni-(PPy or PEDOT)-Co NWs have been successfully synthesized. The inset to the Fig. 3.(d) gives an example of a 100-nm-diameter Ni-PEDOT-Au NW as observed by TEM: the first grown Ni segment is clearly distinguishable. Despite the use of the 3-(Pyrrol-1-yl) propanoic acid SAM, the percentage of unbroken NWs containing transition metal segments remains low compared to the tri-segmented NWs containing only noble metals.
3. Structural characterization
In this section, we present the morphology of several classes of CP NWs, including pure PEDOT NWs and hybrid metal-CP NWs, as studied by SEM, TEM, atomic force microscopy (AFM), Fourier transform Raman spectroscopy and electron spin resonance (ESR).
The morphology of PEDOT NWs is captured in SEM and AFM images reported in Fig. 4.(a, c, d) and Fig. 4.(b), respectively. Once the PC membrane has been removed, PEDOT - as well as other CP NWs - tend to cluster into bundles because of their long length and flexibility. This behavior is reinforced by the NW anchoring on the bottom metallic electrodes (see below). This is an important point to take into account for the integration of CP NWs into devices as well-separated NWs or NTs can be required for high-sensitivity applications. The unambiguous discrimination between NW bundles and large diameter NWs can be easily obtained via AFM studies; the AFM image Fig. 4.(b) reveals five closely-packed PEDOT NWs. In this case, the diameter is determined from the height shift to avoid the convolution by the tip which has to be considered when measuring the lateral size. Finally, a SEM study is not sufficient to determine whether NWs or NTs have been fabricated for given synthesis conditions. As an example, a TEM investigation has shown that the template electropolymerization of PEDOT under the conditions described above results in the
fabrication of PEDOT NWs, while the opened top-ends of the synthesized nano-objects, observed by SEM [Fig. 4.(b)], suggest NTs. In the case of hybrid metal-CP NWs, the metal and CP segments are unambiguously distinguishable by SEM and TEM without any particular contrasting treatment. For example, in a classic SEM picture, tri-segmented metal-(PPy or PEDOT)-metal NWs appear composed of a dark polymer segment inserted between two bright metal segments. In TEM micrographs (Figs. 5 and 6), the polymer block appears more transparent than the metallic segments, due to its lower electronic density.
Figure 6 presents TEM images of tri- and tetra-segmented metal-CP NWs. As displayed in the two insets of Fig. 6.(a), the fabricated Au-PPy-Au NWs have two morphologically different Au-PPy interfaces. In terms of mechanical robustness, the PPy-onto-Au [referred as (1)] interface is smoother and more fragile than the Au [referred as (3)]-onto-PPy interface. Figure 6.(b) illustrates typical Au-PEDOT-PPy-Au NWs. During the synthesis, for enhancing the overall mechanical robustness of the NWs, the deposition sequence was determined according to careful observations on the shape and strength of the different Au-CP interfaces. The PEDOT block was first deposited on the Au segment, as the strong chemical bond between Au-S compensates for the weakness of the flat interface. The PPy block was then electrodeposited onto the PEDOT segment, the strength of the metal-onto-PPy interface being ensured by its meniscus shape. The inset to Fig. 6.(b) gives a magnified view of the PPy-onto-PEDOT heterojunction. It appears that the PEDOT segment shrank more than the PPy segment during the solvent evaporation in a sampling process.
Another unique characterization tool for CP-based NWs is Fourier transform Raman spectroscopy. In the past, the influence of the diameter (35, 75, 100 and 150 nm) on the PEDOT structure was studied on electrodeposited NWs at +0.80 V. All spectra were recorded with an excitation line at 676 nm after dissolution of the membrane [Fig. 7.(a)]. The bands located at 1424 cm−1 and at 1495 cm−1 are attributed, respectively, to the symmetric and antisymmetric C=C vibrations of the thiophene rings. Interestingly, the intensity ratio
to the same EDOT mass. A quantitative analysis of the Lorentzian-like peaks (directly proportional to the spin density) has been carried out. Subsequently, these results have been correlated to the doping level of the NWs estimated from XPS data [Duvail (2004)], revealing that the bipolarons are the dominant charge carriers in these NWs and their contribution increases when the diameter decreases. This conclusion corroborates Raman studies and suggests a strong molecular and supermolecular improvement when the NW diameter decreases.
4. Electrical properties
In this section, we review different techniques for contacting NWs grown by the template method and compare their limitations and advantages. The electrical characterization can be performed in a vertical configuration with multiple NWs contained within the template or in a planar configuration, with NWs freed from the template and dispersed on a substrate.
4.1 Vertical contacting techniques
The vertical configuration is quite convenient and has been frequently employed those last years for the electrical and thermal characterization of NWs [Duvail (2002), Heremans (2002, 2003), Gence (2008), Lorcy (2009)] as it is very fast and requires no complex processing of the sample to be measured. Figure 8.(a)gives an optical micrograph of a PC template mounted on a sample holder and electrically contacted immediately after the electrochemical synthesis. The NWs enclosed within the template are mechanically supported by the PC membrane and are protected from the effect of both oxygen and ambient humidity [Chtanko (2004)]. However, four main drawbacks arise from this method. First, the exact number of connected NWs is not known. An estimation of the number of connected NWs can be made from the porosity of the template and the surface of the electrical contact. The typical values of porosity and hand-made contact surface are 109 pores/cm2 and 5 × 10−4 cm2. Assuming that all pores are filled, this results in a typical number of connected NWs of about 5 × 105. Among this huge number of NWs, by taking into account the calibration of the synthesis parameters, one expects a wide distribution of the physico-chemical characteristics. This distribution results in an averaging effect on the electrical measurements and contributes in masking the intrinsic properties of single NWs. Second, the length of each segment can differ quite significantly between different NWs prepared in the same PC membrane. As the diameter can differ slightly (10 - 20%) from one NW to the other, the intrinsic conductivity (calculated by using the geometrical parameters) can vary by a factor of 2. Third, the resulting two-contact geometry can not avoid the contact resistance to be included in the measurements, in contrast to the four-contact geometry. Fourth, the measurement of multiple NWs contained within a template does not allow any interaction of the NWs with the environment or with any chemical, electrical or physical agent. For all the above reasons, the use of NWs freed from the template is the best choice for the characterization of their intrinsic properties. For application-oriented purposes, the integration of NWs with microelectromechanical systems or electronic devices is required and the NWs have to be precisely aligned and positioned onto microfabricated contacts. Fortunately, various techniques have been specifically developed for the assembly of single NWs onto electrodes [Cao (2008)] and many others are under close scrutiny.
4.2. Planar contacting techniques
For planar contacting techniques, the NWs have to be gently freed from their matrix and the first step consists in the removal of the working electrode from the back of the templates. Generally, the working electrode is made of a few hundred nm Au layer that can be etched with iodine solutions. The PC templates are easily dissolved in dichloromethane, while AAO templates require typically NaOH solutions. The techniques used for contacting single NWs in planar configurations [see Fig. 9.(a)] can be divided in: (i) bottom-contact methods (where NWs are deposited on top of predefined electrodes) and (ii) top-contact methods (where the electrodes are deposited on top of the NWs). In both cases, the substrate includes a high quality insulating layer (
The main advantage of the top-contact approach is to allow chemical and physical cleaning of NW-electrode interface which is not possible for bottom-contacted NWs. Indeed, in the bottom-contact approach, once the NW is deposited onto the electrodes and after the solvent has dried, some PC residues, previously dissolved in the solution are left on the substrate. These residues, when present at the NW-electrodes interfaces, can alter dramatically the electrical contact between the deposited NW and the electrodes in a non reproducible way and cannot be controlled by any treatment. On the other hand, in the framework of the top-contact approach, the NW-electrodes interfaces can be rinsed in pure solvent repetitively for many hours. Another possibility is to use a short cleaning oxygen plasma before the deposition of the electrodes (Au or Pt) for lift-off processing. Nevertheless, the main drawbacks of the direct writing techniques are the likely modification of the intrinsic doping of the NWs (e.g. dedoping associated to EBID manipulation and additional doping during FIB integration). Specifically, for the bottom-contact approach, the expected physisorption of the CP NWs on the metal electrodes can induce a significant contact resistance to inject charge current with a possibly non-ohmic behaviour. The opposite case is met for FIB top-contacts. The ion implantation, although it is reduced by careful choice of experimental parameters, results quite systematically in ohmic contacts. As a consequence, the Pt lines deposited by FIB have to be separated by typically 2
4.3. Electrical properties of pure PEDOT NWs
The motivation for measuring isolated NWs instead of arrays of NWs comes from the opportunity to determine unambiguously the conductivity
Figure 10.(a) gives the diameter dependence of
4.4. Electrical properties of hybrid tri-segmented NWs
We next present electrical transport data for hybrid Au-PPy-Au NWs. The current-voltage
Several experimental studies have shown that the Mott variable-range-hopping (VRH) regime is an appropriate model of charge transport in CP NWs as it is well-known for bulk CPs [Aguilar-Hernández & Potje-Kamloth (1999), Park (2004), Bufon (2005)]. In this model, the charge transport is due to thermally activated tunneling among states that are localized in a constant density of states [Mott & Davis (1979)]. In the VRH model, the resistance follows the relation
The peculiarity of the
4.5. Tunable electronic behavior of hybrid metal-CP NWs
Hybrid metal-CP NWs are attractive candidates for nanodiodes and transistors [Pinto (2003), Park (2004), Merlo & Frisbie (2004), Pinto (2009)] as well as photonic [Guo (2008), Camposeo (2009)] and electrochromic devices [Cho & Lee (2008)]. This high applicative potential comes from the fact that they make profit from intrinsic properties of CPs (low-cost, flexibility, environmental stability, high biocompatibility) concomitantly with other properties stemming from their low-dimensionality (large surface-to-volume ratio and enhanced properties compared to bulk materials). In particular, the literature data show clearly the current interest towards the engineering of novel CP-based NW devices with tunable electronic properties. We present here a new class of tetra-segmented Au-PEDOT-PPy-Au NWs able to switch their electrical characteristics in function of the redox state of the two CP blocks. To illustrate the principle, we use a chemical treatment performed by immersing the samples in a 0.5
Figures 12.(a) and 12.(c) give schematic view of tri-segmented (Au-PEDOT-Au) and tetra-segmented (Au-PEDOT-PPy-Au) NWs, respectively. The
the blue curve corresponds to the as-synthesized NW, the red curve has been obtained after
Similarly to Au-PEDOT-Au NWs, we performed the same experiment with Au-PEDOT-PPy-Au NWs. Remarkably, after the chemical treatment, tetra-segmented NWs exhibit a highly nonlinear
5. Correlated characterization
The correlation of multiple analyses performed on the same, well-defined multi-segmented NWs could lead to a deeper understanding of their structure-function relationships. The aim of this section is to present microdevices specially designed for the correlated characterization of single hybrid metal-CP NWs but it could obviously be applied to other class of hybrid NWs such as hybrid inorganic NWs [Wang (2004)]. We address here the NWs assemblies with membrane-based micro-electromechanical systems. While structural analysis are performed by combining SEM, TEM and AFM microscopies, the microstructure and the elemental composition are investigated by selected area electron diffraction (SAED) and energy dispersive X-ray spectroscopy (EDS) measurements.
5.1. Platforms for correlated characterization
We have used Si micromachining techniques for batch-producing devices based on
5.2. Correlated analysis of hybrid tetra-segmented NWs
A better demonstration of the correlated characterization is offered by hybrid metal-CP NWs. A TEM picture of a Au-PEDOT-PPy-Au NW deposited on top of a
The panel (b) to Fig. 14 gives SAED patterns taken at four different positions on the device. While the SAED obtained through the
low PPy doping ratio generally observed in Au-PPy-Au NW [Gence (2007)]. More important, the data suggest that the Au-PEDOT and PPy-Au interfaces are not equivalent in terms of electrical conductivities. The Au-PPy interface presents a conductance roughly 30 times smaller than the Au-PEDOT interface. Therefore, electrical data analysis of hybrid metal-CP NWs requires utmost care: normally, the conductivities of the metallic segments and the associated metal-CP interfaces are much larger than the conductivities of the CP segments and the interfaces between two CPs. This, obviously, is not always the case. By illustrating this electrical dissymmetry of the metal-CP interfaces, the
6. Integration and applications
The successful assembly of CP-based NWs into hierarchical structures is a key step necessary towards commercially attractive materials and devices. An illustrative example, sorted out from emerging niche applications, is molecular thermoelectricity. Innovative, low-cost thermoelectric converters, combining CPs and metals, could open new vistas in the
search for inexpensive sources of energy. Clearly, the level of integration depends on the envisaged applications; CP-based NWs, processed in mass quantities, are often incorporated in functional layers and they not require complex integration schemes. On one hand, CP designed as functional low-dimensional coatings of NWs or NTs [Lorcy (2009)] are following an easy way towards applications in life sciences (e.g. bio or chemical sensors). On the other hand, CP-based NWs used in electronic devices (e.g. flexible memory devices or thermoelectric converters), have to be integrated into a specific area of the device where physical, chemical or electrical interactions with the environment are permitted. This integration means that NWs have to be manipulated individually and placed on specific sites. Many techniques based on the use of the electric or magnetic field, fluidic flow or chemical assembly have been proposed for addressing the integration of template synthesized NWs. Interestingly, this integration can be achieved by combining classical top-down and template methods. Precisely, it consists in synthesizing the NWs directly on the final device, where they are requested. In this respect, recent work has demonstrated that PANI NWs can be polymerized within PMMA templates [Yunus et al. (2009); Vlad (2009)] in both planar and vertical architectures.
Figure 16.(a) is a schematic view of a PMMA template defined on top of four Pt electrodes for planar NW integration. Here the template is created by EBL from a 500 nm thick PMMA layer; trenches are typically 200 nm wide and about 10
In many cases, the bottom-up approach based on pure chemistry principles fails to reach extended, technologically relevant lengths for functional hybrid assemblies. On the contrary, hierarchical strategies employing standard Si manufacturing allow the achievement of a full superstructural control over the 3D spatial positioning of different self-assembled NWs for developing new artificial nanostructures. In this respect, femtomol-resolved polymerization of aniline on nano-engineered Pt reactors allows nano- and microscale device integration with single NW patterning and growth resolution. Figure 16.(d) offers a schematic view of a cross bar architecture for vertical integration of single PANI NWs as active elements [Vlad (2009)]. The inset displays a highly ordered array of PANI NWs with diameter modulations. The multiplexing feature included in these systems could be exploited for the controlled switching of individual NWs, while the peculiar morphology of the NWs could be adapted to plasmonics and photonics purposes.
A unique opportunity for macroscale self-assembly is offered by the structural engineering of CP-based NWs [Pokroy (2009)]. In a seminal paper, Park and co-workers, by controlling the dissolution of the template, created robust self-assembled mesoscopic metal-CP amphiphiles in which the segregated inorganic hydrophilic segments (Au), connected to the hydrophobic soft segments of the NWs (PPy), display unusual architectures such as bundles, tubes, and sheets [Park (2004)]. In fact, new and versatile functionalities of such hybrid architectures can be achieved easily by chemical treatment such as reversible acid-base doping-dedoping or redox reactions [He (2003); Chiou (2007), Vlad (2009)]. Another way to reach useful functionalities for CP-based NWs is to modify the CP segments by metallic nanoparticles. The figure 17.(a)gives a TEM image of a PEDOT NW functionalized by Au nanoparticles: the Au clusters are chemisorbed onto the PEDOT NW surface due to the presence of S atoms. Such modified NWs could be useful for biosensors applications [Tseng (2005)]. Furthermore, functionalities of CP architectures can be targeted by taking advantage of the peculiar morphology of the constituents. For instance, the axial modulation of aligned PANI NWs can be exploited to fabricate in a single step, self-aligned 3D arrays of vertically stacked Au nanorings (see Fig. 17.(b)).
7. Perspectives
Hybrid metal-CP NWs are promising high-tech materials - as they exhibit enhanced performances compared to their bulk counterparts [Hernandez (2004)] and are of direct interest for developing novel multifunctional systems for convergent micro-nano-bio-technology applications. Among many remaining challenges, we can mention 1) novel methodologies to fabricate highly-ordered architectures - for example, combining electroless and electrochemical depositions with self-assembly; 2) characterization strategies at nanoscale of hybrid NW based superstructures as demanded by molecular electronics, spintronics, plasmonics and photonics; 3) the use of CPs adaptive features for controlled
switching of device properties - at nanoscale - in the presence of external stimuli; 4) protocols for the manipulation of recognition properties of the constitutive segments towards engineering hybrid materials containing biomolecules like DNA or DNA/protein conjugates.
We are convinced that the greatest potential of electroactive CP-based NWs, by virtue of their responsiveness to magnetic, thermal and optical stimuli, is in interfacing the macroscopic world to the human physiological environment. Clearly, integrated hybrid metal- CP NWs into electrical impedance measurement platforms could prove highly beneficial in eliciting desired cellular responses with respect to biomolecules, including chemotaxis processes [Bagorda & Parent (2008)]. Relying on polypyrrole for exemplification, nanostructured 2D and 3D architectures with tunable electronic conductivity could be at the heart of interactive scaffolds that can be employed in tissue regeneration. As PPy has been extensively evaluated for various life science applications, encompassing amperometric biosensors, enzyme-based multicomponent electrodes in analyte detection systems [Li & Lin (2007)], or integrated DNA and peptide arrays on Si chips [Mailley et al. (2005)], there are now great prospects for the use of PPy-based NWs in high-tech applications, like enantiomeric sensoring and chiral molecules separation [Huang et al. (2008)] or biocompatible nanoactuators [Lee (2008); Lim (2008)].
In conclusion, we believe that the challenges proposed here will bring new developments in the engineering of hybrid metal-CP NWs, together with the understanding of the mechanisms underlying a rational use of their molecular functions. In all likelihood, the combined efforts of engineers, chemists, and physicists will lead to breakthroughs in the development of artificial molecular recognition biosensor systems and opto-electronic applications.
Acknowledgments
We acknowledge the help of Drs. S. Faniel, A. Vlad and S. Cuénot. This work was partially supported by the Belgian FRS – FNRS, NANOMOL and TINTIN projects - Communauté Française de Belgique and the NANOTIC – Feeling and NANOTIC – Cite projects of the Belgian Walloon Region and the CNano Project.
References
- 1.
Aguilar-Hernández J. Potje-Kamloth K. 1999 Optical and electrical characterization of a conducting polypyrrole composite prepared by in situ electropolymerization,1 1735 1742 . - 2.
Aleshin A. N. et al. 2004 One-dimensional transport in polymer nanofibers, 93(19): 196601. - 3.
Bagorda A. Parent C. A. 2008 Eukaryotic chemotaxis at a glance,121 16 2621 2624 . - 4.
Bearden J. A. Burr A. F. 1967 Reevaluation of x-ray atomic energy levels,39 1 125 142 . - 5.
Bufon B. et al. 2005 Relationship between chain length, disorder, and resistivity in polypyrrole films,109 41 19191 19199 . - 6.
Callegari V. et al. 2009 Electrochemically template-grown multi-segmented gold-conducting polymer nanowires with tunable electronic behavior,21 18 4241 4247 . - 7.
Camposeo A. et al. 2009 Laser emission from electrospun polymer nanofibers, Small5 5 562 566 . - 8.
Cao Y. et al. 2008 Electrical transport and chemical sensing properties of individual conducting polymer nanowires,8 12 4653 4658 . - 9.
Chiou N. et R. al 2007 Growth and alignment of polyaniline nanofibres with superhydrophobic, superhydrophilic and other properties, Nature2 6 354 357 . - 10.
Cho S. I. Lee S. B. 2008 Fast electrochemistry of conductive polymer nanotubes: Synthesis, mechanism, and application,41 6 699 707 . - 11.
Chtanko N. et al. 2004 Etched single-ion-track templates for single nanowire synthesis, 108(28): 9950. - 12.
Chung H. et J. al 2005 Cobalt-polypyrrole-cobalt nanowire field-effect transistors, 86(21): 213113. - 13.
Dong L. et al. 2005 Dielectrophoretic manipulation and electrical characterization of gold nanowires,16 1500 1505 . - 14.
Duvail J. L. et al. 2002 Charge carrier transport in organic semiconductors, 131: 123. - 15.
Duvail J. L. et al. 2004 Effects of the confined synthesis on conjugated polymer transport properties,108 48 18552 18556 . - 16.
Duvail J. L. et al. 2007 Tuning electrical properties of conjugated polymer nanowires with the diameter, 90(10): 102114. - 17.
Duvail J. L. et al. 2008 Physical properties of magnetic metallic nanowires and conjugated polymer nanowires and nanotubes,5 6 838 850 . - 18.
Gence L. et al. 2007 Structural and electrical characterization of hybrid metal-polypyrrole nanowires, 76(11): 115415. - 19.
Gence L. et al. 2008 Size related transport mechanisms in hybrid metal-polymer nanowires,205 6 1447 1450 . - 20.
Guo Y. et al. 2008 Light-controlled organic/inorganic p-n junction nanowires, 130: 9198. - 21.
He H. X. 2003 Discrete conductance switching in conducting polymer wires, 68(4): 045302. - 22.
He H. X. Li C. Z. Tao N. J. 2001 Conductance of polymer nanowires fabricated by a combined electrodeposition and mechanical break junction method,78 6 811 813 . - 23.
Heremans J. P. et al. 2002 Thermoelectric power of bismuth nanocomposites, 88(21): 216801. - 24.
Heremans J. P. et al. 2003 Resistance, magnetoresistance, and thermopower of zinc nanowire composites, 91(7): 076804. - 25.
Hernandez R. M. et al. 2004 Template fabrication of protein-functionalized gold-polypyrrole-gold segmented nanowires, 16(18): 3431. - 26.
Huang J. Wei Z. Chen J. 2008 Molecular imprinted polypyrrole nanowires for chiral amino acid recognition,134 2 573 578 . - 27.
Hurst S. J. et al. 2006 Multisegmented one-dimensional nanorods prepared by hard template synthetic methods,45 17 2672 2692 . - 28.
Jang J. 2006 Conducting polymer nanomaterials and their applications,199 189 259 . - 29.
Jerôme C. Jerôme R. 1998 Electrochemical synthesis of polypyrrole nanowires, 37(18): 2488. - 30.
Kovtyukhova N. et al. 2004 Coaxially gated in-wire thin-film transistors made by template assembly, 126(40): 12738. - 31.
Lahav A. et al. 2006 Core-shell and segmented polymer-metal composite nanostructures, 6(9): 2166. - 32.
Lee J. I. et al. 2008 Highly aligned ultrahigh density arrays of conducting polymer nanorods using block copolymer templates, 8(8): 1530. - 33.
Li J. Lin X. 2007 Glucose biosensor based on immobilization of glucose oxidase in poly(o-aminophenol) film on polypyrrole-Pt nanocomposite modified glassy carbon electrode,22 12 2898 2905 . - 34.
Liang L. et al. 2002 Highly diastereo- and enantioselective intramolecular amidation of saturated C-H bonds catalyzed by ruthenium porphyrins, 41(18): 3465. - 35.
Lieber C. M. Wang Z. L. 2007 Functional nanowires, 32(3): 99. - 36.
Lim J. H. Mirkin C. A. 2002 Electrostatically driven dip-pen nanolithography of conducting polymers,14 20 1474 1477 . - 37.
Lim J. K. et al. 2008 Actuation of self-assembled two-component rodlike nanostructures, 8(12): 4441. - 38.
Long Y. et al. 2005 Electronic transport in single polyaniline and polypyrrole microtubes, 71(16): 165412. - 39.
Lorcy J. M. et al. 2009 Coaxial nickel/poly(p-phenylene vinylene) nanowires as luminescent building blocks manipulated magnetically, 20(40): 405601. - 40.
Mailley P. Roget A. Livache T. 2005 Conducting polymers for DNA sensors and DNA chips: from fabrication to molecular detection, Persp. In Bioanalysis1 297 330 . - 41.
Martin C. R. 1994 Nanomaterials: A membrane-based synthetic approach, Science266 5193 1961 1966 . - 42.
Martin C. R. 1996 Membrane-based synthesis of nanomaterials, 8(8): 1739. - 43.
Massuyeau F. et al. 2009 Elaboration of conjugated polymer nanowires and nanotubes for tunable photoluminescence properties, 20(15): 155701. - 44.
Merlo J. A. Frisbie C. D. 2004 Field effect transport and trapping in regioregular polythiophene nanofibers, 108:19169. - 45.
Mott N. F. Davis E. A. 1979 , Clarendon Press, Oxford. - 46.
Nalwa H. S. (ed 2006 , American Scientific Publishers. - 47.
Park S. et al. 2004 Hybrid organic-inorganic, rod-shaped nanoresistors and diodes, 126: 11772. - 48.
Pinto N. J. et al. 2003 Electrospun polyaniline/polyethylene oxide nanofiber field-effect transistor,83 20 4244 4246 . - 49.
Pinto N. J. et al. 2009 Rectifying junctions of tin oxide and poly(3 -hexylthiophene) nanofibers fabricated via electrospinning, 94(8): 083504. - 50.
Pokroy B. et al. 2009 Self-organization of a mesoscale bristle into ordered, hierarchical helical assemblies,323 5911 237 240 . - 51.
Reneker D. H. et al. 2000 Bending instability of electrically charged liquid jets of polymer solutions in electrospinning,87 9 4531 4547 . - 52.
Reynes O. Demoustier-Champagne S. 2005 Template electrochemical growth of polypyrrole and gold-polypyrrole-gold nanowire arrays, 152(9): D130 -D135. - 53.
Sadki S. et al. 2000 The mechanisms of pyrrole electropolymerization, 29: 283. - 54.
Sakmeche N. et al. 1996 Anionic micelles: a new aqueous medium for electropolymerization of poly(3,4-ethylenedioxythiophene) films on Pt electrodes,2723 2724 . - 55.
Shen J. et al. 2006 Electrical properties of a single electrochemically template-synthesized polypyrrole nanowire, 88(25): 253106. - 56.
Smith P. A. et al. 2000 Electric-field assisted assembly and alignment of metallic nanowires,77 9 1399 1401 . - 57.
Tran H. D. Li D. Kaner R. B. 2009 One-dimensional conducting polymer nanostructures: Bulk synthesis and applications21 1 1 13 . - 58.
Tseng R. J. et al. 2005 Polyaniline nanofiber/gold nanoparticle nonvolatile memory, 5(6): 1077. - 59.
Vlad A. et al. 2009 Highly ordered conjugated polymer nanoarchitectures with three-dimensional structural control,9 8 2838 2843 . - 60.
Wan M. 2008 A template-free method towards conducting polymer nanostructures, Advanced Materials20 15 2926 2932 . - 61.
Wang J. G. et al. 2004 Microstructure and interdiffusion of template-synthesized Au/Sn/Au junction nanowires, 4(7): 1313. - 62.
Wang Y. et al. 2007 Individually addressable crystalline conducting polymer nanowires in a microelectrode sensor array, 18(42): 424021. - 63.
Xiao R. et al. 2007 Controlled electrochemical synthesis of conductive polymer nanotube structures,9 3 40 50 . - 64.
Yoon C. O. et al. 1994 Transport near the metal-insulator transition: Ppy doped with PF6,49 16 10851 10863 . - 65.
Yoon H. Hong J. Y. Jang J. 2007 Charge-transport behavior in shape-controlled poly(3,4-ethylenedioxythiophene) nanomaterials: Intrinsic and extrinsic factors,3 10 1774 1783 . - 66.
Yunus S. Attout A. Bertrand P. 2009 Controlled aniline polymerization strategies for polyaniline micro- and nano self-assembling into practical electronic devices, 25(3): 1851.